MD797Z

MD797Z - Method for producing the identification tag on a metal carrier

Info

Publication number: MD797Z
Application number: MDS20130219A
Authority: MD
Inventors: Владимир ШКИЛЁВ; Анатолий ПАРАМОНОВ; Александр КОВАЛЬ; Василе АГАФИЙ
Original assignee: Институт Прикладной Физики Академии Наук Молдовы
Priority date: 2013-12-27
Filing date: 2013-12-27
Publication date: 2015-02-28
Also published as: MD797Y

Abstract

The invention relates to the field of information technologies and is intended for identification of material objects, particularly for producing the identification tag on a metal carrier.The method for producing the identification tag on a metal carrier consists in that it is carried out a single electrospark discharge between a high-voltage electrode and a carrier, consisting of a metal sheet with a transparent dielectric film coating on one surface. The carrier is placed in a grounded closed electrode. Thereafter, it is selected a sector with the most informative image, obtained as a result of electrical discharge, on which is applied a digital code and a virtual information grid.

Description

Invenţia se referă la domeniul tehnologiilor informaţionale şi este destinată pentru identificarea resurselor materiale, în special pentru obţinerea marcajului de identificare pe un purtător metalic. The invention relates to the field of information technologies and is intended for identifying material resources, in particular for obtaining an identification mark on a metal carrier.

Este cunoscut un procedeu de identificare, care include imprimarea unui număr de identificare pe obiectul electroconductor, aplicarea mecanică pe obiect a unei grile informaţionale de coordonate, urmată de o descărcare electrică punctiformă între obiect şi electrodul vibrant, care se deplasează arbitrar în sistemul de coordonate al grilei. Imaginea obţinută a grilei se scanează şi se păstrează în memoria calculatorului, iar identificarea obiectului se realizează prin compararea numărului de identificare şi a imaginii grilei cu cele înregistrate anterior [1]. An identification process is known, which includes printing an identification number on the electroconductive object, mechanically applying an informational coordinate grid to the object, followed by a point-like electrical discharge between the object and the vibrating electrode, which moves arbitrarily in the coordinate system of the grid. The obtained image of the grid is scanned and stored in the computer memory, and the identification of the object is achieved by comparing the identification number and the grid image with those previously recorded [1].

Dezavantajul acestui procedeu constă în aceea că este puţin sigur şi are un randament mic din cauza procesului îndelungat de obţinere a marcajului de identificare. The disadvantage of this process is that it is not very reliable and has a low yield due to the long process of obtaining the identification mark.

Cea mai apropiată soluţie este un procedeu de identificare a obiectului electroconductor, în care procedeul de obţinere a marcajului de identificare constă în aceea că pe obiect se imprimă un număr de identificare, pe care se aplică o grilă informaţională de coordonate, pe care se aplică o imagine nereproductibilă prin descărcări electrice punctiforme între obiect şi un electrod, executat din nanocompozite ale pulberilor ultradisperse de metal, instalat cu interstiţiu deasupra grilei informaţionale. După aceasta grila cu imaginea nereproductibilă obţinută se înregistrează într-o bază de date electronică, totodată conform legii numerelor aleatorii pe imaginea nereproductibilă se selectează cel puţin un semn, coordonatele căruia pe grila informaţională şi caracteristica lui spectrală se înregistrează într-o bază de date electronică independentă. Identificarea obiectului se realizează în două etape [2]. The closest solution is a method of identifying an electroconductive object, in which the method of obtaining the identification mark consists in printing an identification number on the object, on which an information grid of coordinates is applied, on which an unreproducible image is applied by point electrical discharges between the object and an electrode, made of nanocomposites of ultradisperse metal powders, installed with a gap above the information grid. After this, the grid with the obtained unreproducible image is registered in an electronic database, at the same time, according to the law of random numbers, at least one sign is selected on the unreproducible image, the coordinates of which on the information grid and its spectral characteristic are registered in an independent electronic database. Object identification is carried out in two stages [2].

Dezavantajele acestui procedeu constau în necesitatea aparatelor spectrale costisitoare, eficienţa joasă, necesitatea de a efectua mai multe descărcări electrice şi imposibilitatea de a majora productivitatea procesului. Petele punctiforme de la descărcările electrice posedă o saturaţie informaţională joasă. Toate dezavantajele au loc din cauza utilizării descărcării electrice prin scântei, care poate să creeze numai dimensiuni limitate ale petelor şi nu poate crea desene rămuroase, care ar poseda o saturaţie informaţională maximă. The disadvantages of this method are the need for expensive spectral devices, low efficiency, the need to perform several electric discharges, and the impossibility of increasing the productivity of the process. Point-like spots from electric discharges have a low information saturation. All disadvantages occur due to the use of electric discharge through sparks, which can create only limited sizes of spots and cannot create branched patterns, which would have a maximum information saturation.

Problema pe care o rezolvă invenţia este majorarea productivităţii şi obţinerea imaginii individuale cu o saturaţie informaţională maximă. The problem that the invention solves is increasing productivity and obtaining an individual image with maximum information saturation.

Procedeul, conform invenţiei, înlătură dezavantajele menţionate mai sus prin aceea că se efectuează o descărcare electrică unică între un electrod de tensiune înaltă şi un purtător, format dintr-o foaie metalică cu o acoperire dielectrică peliculară transparentă pe o suprafaţă. Purtătorul este amplasat cu marginile într-un electrod închis legat la pământ şi cu suprafaţa metalică îndreptată spre electrodul de tensiune înaltă. După aceasta se selectează un sector cu cea mai informativă imagine, obţinută în urma descărcării electrice, pe care se aplică un cod numeric şi o grilă informaţională virtuală. The method according to the invention eliminates the above-mentioned disadvantages by performing a single electric discharge between a high-voltage electrode and a carrier, formed by a metal sheet with a transparent film dielectric coating on one surface. The carrier is placed with its edges in a closed electrode connected to the ground and with the metal surface facing the high-voltage electrode. After that, a sector with the most informative image, obtained as a result of the electric discharge, is selected, on which a numerical code and a virtual information grid are applied.

Totodată, poate fi selectat un sector cu o imagine, obţinută la expunerea la lumină în urma descărcării electrice, pe care se aplică un cod numeric şi o grilă informaţională virtuală. At the same time, a sector can be selected with an image, obtained upon exposure to light following an electrical discharge, on which a numerical code and a virtual information grid are applied.

Rezultatul tehnic constă în sporirea productivităţii de confecţionare a marcajului de identificare şi obţinerea unei imagini individuale cu saturaţie informaţională, formată din mai multe desene rămuroase, care posedă o saturaţie informaţională maximă. The technical result consists in increasing the productivity of making the identification mark and obtaining an individual image with information saturation, consisting of several branched drawings, which possess maximum information saturation.

Invenţia se explică prin desenele din fig. 1-5, care reprezintă: The invention is explained by the drawings in Fig. 1-5, which represent:

- fig. 1, schema instalaţiei pentru realizarea procedeului de obţinere a marcajului de identificare pe un purtător metalic; - Fig. 1, diagram of the installation for carrying out the process of obtaining the identification mark on a metal carrier;

- fig. 2-4, vederi ale purtătorilor metalici cu imagini individuale; - Fig. 2-4, views of the metal carriers with individual images;

- fig. 5, vederea purtătorului metalic cu sectoare ale marcajelor de identificare. - Fig. 5, view of the metal carrier with sectors of the identification marks.

În fig. 1 este prezentată schematic instalaţia, care permite de a realiza procedeul: 1 - sticlă, 2 - acoperire dielectrică peliculară transparentă, 3 - foaie metalică, 4 - electrod închis, 5 - electrod de tensiune înaltă, 6 - sursă de tensiune înaltă, 7 - condensator de descărcare de tensiune înaltă. Fig. 1 shows a schematic diagram of the installation that allows the process to be carried out: 1 - glass, 2 - transparent film dielectric coating, 3 - metal sheet, 4 - closed electrode, 5 - high voltage electrode, 6 - high voltage source, 7 - high voltage discharge capacitor.

Procedeul de obţinere a marcajului de identificare pe un purtător metalic constă în aceea că se efectuează o descărcare electrică unică între un electrod de tensiune înaltă 5 şi un purtător, format dintr-o foaie metalică 3 cu o acoperire dielectrică peliculară transparentă 2 pe o suprafaţă. Purtătorul este amplasat cu marginile într-un electrod închis 4 legat la pământ şi cu suprafaţa metalică 3 îndreptată spre electrodul de tensiune înaltă. După aceasta se selectează un sector cu cea mai informativă imagine, obţinută în urma descărcării electrice, pe care se aplică un cod numeric şi o grilă informaţională virtuală. Totodată, poate fi selectat un sector cu o imagine, obţinută la expunerea la lumină în urma descărcării electrice, pe care se aplică un cod numeric şi o grilă informaţională virtuală. The method of obtaining the identification mark on a metal carrier consists in performing a single electric discharge between a high-voltage electrode 5 and a carrier, formed by a metal sheet 3 with a transparent film dielectric coating 2 on one surface. The carrier is placed with its edges in a closed electrode 4 connected to the ground and with the metal surface 3 facing the high-voltage electrode. After this, a sector with the most informative image, obtained as a result of the electric discharge, is selected, on which a numerical code and a virtual information grid are applied. At the same time, a sector with an image, obtained upon exposure to light as a result of the electric discharge, can be selected, on which a numerical code and a virtual information grid are applied.

Procedeul se realizează în următoarea ordine: între electrodul de înaltă tensiune 5 şi instalaţia principală legată la pământ se instalează purtătorul. Prezenţa acoperirii dielectrice 2 duce la aceea că descărcarea electrică se îndreaptă la electrodul închis 4 legat la pământ, lăsând pe foaia metalică 3 un desen rămuros al imaginii individuale. După aceasta, pe imaginea individuală scanată se aplică grila informaţională virtuală şi i se atribuie un cod numeric sau literal-numeric. Marcajul este gata şi sub aşa aspect se introduce în baza de date. The procedure is carried out in the following order: the carrier is installed between the high-voltage electrode 5 and the main grounded installation. The presence of the dielectric coating 2 leads to the fact that the electric discharge is directed to the closed grounded electrode 4, leaving a branched pattern of the individual image on the metal sheet 3. After that, the virtual information grid is applied to the scanned individual image and a numerical or literal-numeric code is assigned to it. The marking is ready and in this form it is entered into the database.

Exemple de realizare a procedeului. Examples of implementation of the process.

Exemplul 1. Example 1.

S-a utilizat folie de aluminiu cu grosimea de 30 µm, capacitatea condensatorului de descărcare de 47 pF, iar interstiţiul dintre foaia metalică şi electrod de 10 mm. Descărcarea superficială electrică lasă pe foaia metalică un desen rămuros cu saturaţie informativă a imaginii nereproductibile (fig. 2). Aluminum foil with a thickness of 30 µm was used, the discharge capacitor capacity was 47 pF, and the gap between the metal sheet and the electrode was 10 mm. The superficial electrical discharge leaves a branched pattern on the metal sheet with non-reproducible image information saturation (fig. 2).

Exemplul 2. Example 2.

Toţi parametrii procedeului sunt analogici exemplului 1, în afară de capacitatea condensatorului de descărcare mărită de 10 ori, până la 470 pF (fig. 3). All process parameters are analogous to example 1, except for the discharge capacitor capacity increased 10 times, up to 470 pF (fig. 3).

Exemplul 3. Example 3.

Toţi parametrii sunt analogici exemplelor 1 şi 2, în afară de capacitatea condensatorului de descărcare mărită până la 1000 pF (fig. 4). All parameters are analogous to examples 1 and 2, except for the discharge capacitor capacitance increased to 1000 pF (fig. 4).

Exemplul 4. Example 4.

Marcajul este obţinut cu ajutorul câtorva descărcări superficiale cu utilizarea capacităţii condensatorului de 470 pF (fig. 5). Ca bază a marcajelor de identificare, obţinute de la descărcarea superficială (fig. 5), sunt selectate imaginile 1, 2, 4. Imaginea 3 este obţinută la expunerea la lumină în urma descărcării electrice superficiale. The marking is obtained by means of several surface discharges using the capacitor capacity of 470 pF (Fig. 5). As a basis for the identification marks obtained from the surface discharge (Fig. 5), images 1, 2, 4 are selected. Image 3 is obtained upon exposure to light following the surface electric discharge.

Astfel este propus un procedeu nou, mai productiv, de obţinere a marcajului de identificare pe metal, care formează prin descărcare electrică superficială un desen rămuros cu saturaţie informaţională a imaginii individuale. Thus, a new, more productive process is proposed for obtaining identification markings on metal, which forms a branched pattern with information saturation of the individual image through superficial electrical discharge.

1. MD 3389 G2 2007.08.31 1. MD 3389 G2 2007.08.31

2. MD 3950 C2 2009.07.31 2. MD 3950 C2 2009.07.31

Claims

1. Method for obtaining an identification mark on a metal carrier, which consists in performing a single electrical discharge between a high-voltage electrode and a carrier, consisting of a metal sheet with a transparent film dielectric coating on one surface; the carrier is placed with its edges in a closed electrode connected to the ground and with the metal surface facing the high-voltage electrode; after this, a sector with the most informative image, obtained as a result of the electrical discharge, is selected, on which a numerical code and a virtual information grid are applied.

2. Method according to claim 1, wherein a sector with an image obtained upon exposure to light following the electrical discharge is selected.