LT4235B - Method for a formation of electrical conductive coatings on polycaproamidic films - Google Patents
Method for a formation of electrical conductive coatings on polycaproamidic films Download PDFInfo
- Publication number
- LT4235B LT4235B LT96-004A LT96004A LT4235B LT 4235 B LT4235 B LT 4235B LT 96004 A LT96004 A LT 96004A LT 4235 B LT4235 B LT 4235B
- Authority
- LT
- Lithuania
- Prior art keywords
- solution
- selenium
- coatings
- electrically conductive
- conductive coatings
- Prior art date
Description
Išradimas priskiriamas polimerinių medžiagų savybių modifikavimui, sudarant ant jų paviršiaus elektrai laidžias chalkogenidų dangas, kas Įgalina tokias polimerines medžiagas panaudoti galvaninei metalizacijai ar kaip lanksčius laidininkus.
Žinomas elektrai laidžių sulfidinių dangų ant kai kurių polimerinių medžiagų (poliamido, polistirolo) gavimo būdas, kai polimerinės medžiagos paviršius veikiamas metalų druskų tirpalu, o vėliau - natrio sulfido tirpalu (žiūr. buv. TSRS autor. liud. Nr.l 110819, TPK C 23 C 3/02, 1984).
Šiuo būdu ant polimerinių medžiagų nėra gaunamos pakankamai laidžios elektrai sulridinės dangos.
Artimiausias siūlomam sprendimui yra elektrai laidžių sulfidinių dangų gavimo būdas, kai pradžioje polimerinės medžiagos sierinamos šarminiu sieros tirpalu, nuplaunamos parūgštintu vandeniu ir po to veikiamos vario druskos tirpalu (žiūr. buv. TSRS autor. liud. Nr.895542, TPK B 05 D 5/12, C 23 C 3/02, 1982).
Šiuo būdu gautų sulfidinių dangų ant polimerų varža yra per didelė, kad tokius polimerus būtų galima kokybiškai metalizuoti. Polimerų sierinimui šiame būde naudojamas stipriai šarminis sieros tirpalas, o tai tinka ne visoms medžiagoms. Šiame metode naudojami vario druskos tirpalai nėra stabilūs. Metodai gauti laidžias elektrai vario selenidines dangas nėra žinomi.
Siūlomo išradimo tikslas - gauti laidžias elektrai vario selenidines dangas ant polikaproamido, panaudojant seleno difuzijai į polikaproamidą rūgštų kalio selenotritionato K2SeS2O6 tirpalą, o vario selenidų gavimui - {difundavusio į polikaproamidą seleno sąveiką su vario druskomis.
Tikslas pasiekiamas tuo, kad polikaproamido plėvelė seleninama 0.05+0.1 M parūgštintu kalio selenotritionato tirpalu, džiovinama ir veikiama 0.4M vario druskos su reduktoriumi hidrochinonu, tirpalu.
PAVYZDYS:
Polikaproarnido plėvelės bandiniai veikiami maišomu 50-80oC temperatūros 0,03-0,2M kalio selenotritionato tirpalu parūgštintu ekvivalentiniu druskos rūgšties kiekiu 60-180 minučių, plaunami
2-4s vandeniu ir merkiami į vario druskos su hidrochinonu tirpalą, turintį vienvalenčio vario jonų. Šiuo 60-90°C temperatūros tirpalu seleninti bandiniai veikiami 5-20 minučių, po to 2-4s plaunami vandeniu. Matuojama sausų polikaproamidinės plėvelės bandinių su vario selenidine danga paviršiaus varža. Paviršiaus varžos yra 50-260Ω/ΰ. Duomenys pateikti lentelėje.
lentelė
| Seleninimo agentas | Tirpalo molinė kon- centra- cija | Seleninimo sąlygos | Vario druskos tirpalo sudėtis g· | Veikimo vario druskos tirpalu sąlygos | Pavir- šiaus varža, Ω/Π | ||
| Tem- pera- tūra, °C. | Truk- mė, min. | Tem- pera- tūra, °C. | Truk- mė, min. | ||||
| 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 |
| IŠRADIMAS | |||||||
| K2SeS2O6 | 0.05 | 60 | 180 | Vario sulfato kristalo hidratas - 10, Hidrochinonas - i.o, Vanduo - 100 | 78 | 10 | 554-60 |
| — »1 — | — | 150 | — J’ — | — i»— | 58-65 | ||
| — — | 90 | — J,— | 60-65 |
| 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 |
| —i»— | 60 | -»- | — >1 — | —J'— | 70-75 | ||
| —J»— | 150 | -n- | 60 | 130- 150 | |||
| —i»— | 90 | —— | 60-70 | ||||
| -J»- | 0.03 | —J» — | 78 | 250- 275 | |||
| -M- | 0.05 | 50 | — M — | 150- 180 | |||
| —i»— | 70 | 30 | —J»— | 190- 210 | |||
| 80 | —n— | 240- 260 | |||||
| —n — | 60 | 150 | — n— | 20 | 60-70 | ||
| 5 | 220- 250 | ||||||
| 0.10 | 90 | 10 | 50-55 | ||||
| -»- | —i»— | 120 | —i»— | 55-60 | |||
| 0.20 | 150 | —n— | 65-70 | ||||
| ANALOGAS | |||||||
| Šarminis sieros tirpalas | 2.0 | 90 | 5 | Vario sulfato kristalo hidratas -io, Hidrochinonas - 3, Vanduo - 100 | 70 | l.O | 150- 260 |
Iš lentelės matome, kad naudojant praskiestą ir parūgštintą ekvivalentiniu druskos rūgšties kiekiu kalio selenotritionato tirpalą polikaproamidinės plėvelės bandinių seleninimui, o vėliau juos paveikus vario druskos su hidrochinonu tirpalu, gaunamos selenidinės dangos su mažesnėmis nei analoge paviršiaus varžomis.
Siūlomas išradimas, palyginus jį su jau žinomu, pasižymi tokiais privalumais:
- polikaproamido seleninimui naudojamas mažos koncentracijos kalio selenotritionato rūgštus tirpalas;
-leidžia žymiai sumažinti polikaproamido plėvelės paviršiaus varžą ir panaudoti tokią plėvelę elektrocheminei metalizacijai ar kaip lankstų laidininką.
IŠRADIMO APIBRĖŽTIS
Claims (1)
- IŠRADIMO APIBRĖŽTISElektrai laidžių dangų ant polimerų gavimo būdas, kuriame polimerines medžiagas sierina šarminiame sieros tirpale, nuplauna parūgštintu vandeniu, po to veikia vario druskos tirpalu, besiskiriantis tuo, kad polikaproamido plėvelės paviršiaus varža sumažinama plėvelę seleninant 0.05-e-0.1M kalio selenotritionato rūgščiame tirpale, nuplauna vandeniu ir veikia vario druskos su hidrochinonu tirpalu.