KR970006415A - 티타늄 디옥사이드 안료 - Google Patents
티타늄 디옥사이드 안료 Download PDFInfo
- Publication number
- KR970006415A KR970006415A KR1019960028284A KR19960028284A KR970006415A KR 970006415 A KR970006415 A KR 970006415A KR 1019960028284 A KR1019960028284 A KR 1019960028284A KR 19960028284 A KR19960028284 A KR 19960028284A KR 970006415 A KR970006415 A KR 970006415A
- Authority
- KR
- South Korea
- Prior art keywords
- titanium dioxide
- aluminum
- pigment
- amount
- reagent
- Prior art date
Abstract
1. 청구범위에 기재된 발명이 속한 기술분야
본 발명은 경량의 고착성이 향상된 티타늄 디옥사이드에 관한 것으로서, 특히 라미네이트에서 사용되기 위한 티타늄 디옥사이드에 관한 것이다.
2. 발명이 해결하려고 하는 기술적 과제
본 발명의 목적은 알루미늄 포스페이트의 응집성 코팅제로 티타늄 디옥사이드 입자를 코팅시킴에 의하여 회색으로 변색되는 문제점에 대한 해결책을 제공하는 것이다.
3. 발명의 해결방법의 요지
농축된 인산과 알루미늄 혹은 알루미늄 화합물을 상승된 온도하에서 반응시킴에 의하여 형성된 시약과 티타늄 디옥사이드의 현탁물을 혼합시키고 pH값이 적어도 3.5가 될때까지 알칼리 화합물을 첨가하는 공정을 포함하는 티타늄 디옥사이드 안료의 제조방법이다. 본 발명의 제조방법에 의해 제조될 수 있는 새로운 안료는 티타늄 디옥사이드를 함유하며, 그 입자가 알루미늄(Al) 대 인(P)의 몰비가 1.8 : 1~1 : 1.4인 알루미늄 포스페이트의 포면 코팅제로 코팅되어 있다.
4. 발명의 중요한 용도
본 발명에 따라 제조된 안료는 페이퍼 라미네이트의 제조시 사용될 수 있다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (18)
- 농축된 인산과 알루미늄 혹은 알루미늄 화합물을 상승된 온도하에서 반응시킴에 의하여 형성된 시약과 티타늄 디옥사이드의 현탁물을 혼합시키고 pH값이 적어도 3.5가 될때까지 알칼리 화합물을 첨가하는 것을 특징으로 하는 티타늄 디옥사이드의 제조방법.
- 제1항에 있어서, 시약은 알루미늄(Al) 대 인(p)의 몰비가 1 : 2~1 : 5인 량으로 알루미늄 또는 알루미늄 화합물 및 인산을 반응시킴에 의하여 형성되는 것을 특징으로 하는 제조방법.
- 제1항에 있어서, 농축 인산은 30~100℃의 온도범위에서 알루미늄 또는 알루미늄 화합물과 반응되는 것을 특징으로 하는 제조방법.
- 제1항에 있어서, 사용된 시약의 량은 TiO2에 대하여 Al2O3로서 계산되어진 2~6중량%에 상당하는 알루미늄의 량을 함유하는 티타늄 디옥사이드 입자들을 형성하기에 충분한 것임을 특징으로 하는 제조방법.
- 제1항에 있어서, 사용된 시약의 량은 TiO2에 대하여 P2O5로서 계산되어진 2~12중량%에 상당하는 인의 량을 함유하는 티타늄 디옥사이드 입자들을 형성하기에 충분한 것임을 특징으로 하는 제조방법.
- 제1항에 있어서, 농축된 인산은 H3PO4로서 계산된 산70~80중량%을 함유하는 것을 특징으로 하는 제조방법.
- 제1항에 있어서, 시약은 티타늄 디옥사이드의 현탁물과 혼합시키기전에 리터당 Al2O390~120그램당량의 농도로 희석시키는 것을 특징으로 하는 제조방법.
- 제1항에 있어서, 티타늄 디옥사이드의 현탁물의 농도는 리터당 TiO2200~400그램인 것을 특징으로 하는 제조방법.
- 제1항에 있어서, 티타늄 디옥사이드는 시약과 혼합되기전 제분공정을 거치는 것을 특징으로 하는 제조방법.
- 제1항에 있어서, 분산제는 티타늄 디옥사이드의 현탁물내에 함유되는 것을 특징으로 하는 제조방법.
- 제1항에 있어서, 알칼리성 화합물은 리터당 250~250그램 범위인 농도를 갖는 수산화나트륨의 수용액인 것을 특징으로 하는 제조방법.
- 제1항에 있어서, 알칼리성 화합물은 리터당 Al2O350~120그램 당량의 농도를 갖는 수용액중의 부식성 알루민산 나트륨인 것을 특징으로 하는 제조방법.
- 티타늄 디옥사이드 안료의 제조방법에 있어서, ⒜ 50~70℃의 온도하에서 알루미늄(Al) 대 인(P)의 몰비가 1 : 2~1 : 5인 수산화 알루미늄 및 농축 인산을 반응시키는 공정과, ⒝ 투명한 온도가 얻어질때까지 상기 온도하에서 반응 혼합물을 유지시키는 공정과, ⒞ 상기 결과로 얻어진 투명한 용액을 희석시키는 공정, ⒟ 건조된 티타늄 디옥사이드의 중량을 기준으로 하여, Al2O3로서 계산되어진 알루미늄 포스페이트 시약 2~6중량%를 함유하는 혼합물이 주어지도록 제분된 티타늄 디옥사이드의 분산물에 일정량의 희석 용액을 첨가하는 공정과, ⒠ 상기 결과로 얻어진 혼합물의 pH가 적어도 5가 될때까지 시간 간격을 두고 수산화나트륨을 첨가하는 공정, 및 ⒡ 상기 결과로 얻어진 코팅된 안료를 여과하는 공정을 포함하는 것을 특징으로 하는 티타늄 옥사이드 안료의 제조방법.
- 제1 내지 13항에 있어서, 상화제는 안료가 건조되기전 코팅된 안료와 함께 혼합되는 것을 특징으로 하는 제조방법.
- 제14항에 있어서, 산화제는 건조된 티타늄 디옥사이드 중량을 기준으로 0.5~1.0중량%의 량으로 첨가되는 질산칼륨인 것을 특징으로 하는 제조방법.
- 알루미늄(Al) 대 인(P)의 몰비가 1.8 : 1~1 : 4인 알루미늄 포스페이트의 표면 코팅제로 입자들이, 코팅된 것을 특징으로 하는 티타늄 디옥사이드 안료.
- 제16항에 있어서, 알루미늄 포스페이트는 TiO2에 대하여 Al2O3로서 계산되어진 2~6중량%에 상당하는 량으로 함유되는 것을 특징으로 하는 티타늄 디옥사이드 안료.
- 제16항 또는 17항에 있어서, 알루미늄 포스페이트는 TiO2에 대하여 P2O3로서 계산되어진 2~12중량%에 상당하는 량으로 함유되는 것을 특징으로 하는 티타늄 디옥사이드 안료.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.