KR970000733B1 - Pattern coating method of hardboard - Google Patents
Pattern coating method of hardboardInfo
- Publication number
- KR970000733B1 KR970000733B1 KR1019930015435A KR930015435A KR970000733B1 KR 970000733 B1 KR970000733 B1 KR 970000733B1 KR 1019930015435 A KR1019930015435 A KR 1019930015435A KR 930015435 A KR930015435 A KR 930015435A KR 970000733 B1 KR970000733 B1 KR 970000733B1
- Authority
- KR
- South Korea
- Prior art keywords
- paint
- pattern
- intaglio
- layer
- coating
- Prior art date
Abstract
Description
제1도는 본 발명 실시중 하도공정 예시도.Figure 1 is an exemplary diagram of the undercoating process in the practice of the present invention.
제2도는 본 발명 실시중 양각부 도장공정 예시도.Figure 2 is an illustration of the embossed coating process during the implementation of the present invention.
제3도는 본 발명 실시중 음각부 도장공정초기단계 예시도.Figure 3 is an illustration of the initial step of the engraving process during the present invention.
제4도는 본 발명 실시중 음각부 도장공정마무리단계 예시도.Figure 4 is an illustration of the finishing process of the engraved part coating process during the present invention.
제5도는 본 발명 실시중 최종마무리단계 예시도.Figure 5 is an illustration of the final finishing step in the practice of the present invention.
* 도면의 주요부분에 대한 부호의 설명* Explanation of symbols for main parts of the drawings
21 : 음각부도장층 30 : 하도도장층21: engraved coating layer 30: undercoat coating layer
41 : 양각부도장층41: embossed coating layer
본 발명은 주로 건물내장재, 문짝등으로 사용되는 건재용 하드보드에 이색무늬 도장방법에 관한 것이다.The present invention relates to a dichroic pattern coating method on a hard board for building materials mainly used as building interior materials, doors and the like.
일반적으로 건물내장재, 문짝등은 주로 목재를 이용하였으나 최근 원가절감을 위하여 하드보드가 건재로 이용되고 있다.Generally, building interior materials and doors are mainly made of wood, but hard boards have recently been used as building materials for cost reduction.
이와 같은 하드보드는 재질이 엷고(약 5mm), 흡습성이 강하므로 표면도장이 어려워 단일색상만을 도장하여 이용되고 있는 실정이다. 따라서 장식을 요하는 건물내장재, 문짝으로서의 장식적 효과가 미흡한 문제점이 있었다.Such hard boards are thin (about 5 mm) and have high hygroscopic properties, which makes it difficult to coat the surface. Therefore, there is a problem that the decorative effect as a building interior materials, doors that require decoration.
본 고안에서는 이상과 같은 종래의 문제점을 해결하기 위하여 하드보드에 표현하고자 하는 무늬모양을 음각으로 압인하여 그 표면에 하도공정, 양각부, 도장공정, 음각부 도장공정을 거쳐 표면에 이색무늬모양으로 장식된 표면을 얻고자 한다.In the present invention, in order to solve the conventional problems as described above, the pattern shape to be expressed on the hard board is engraved in an intaglio, and the surface is subjected to a subcontracting process, an embossed part, a painting process, and an intaglio part painting process to form a dichroic pattern on the surface. We want to get a decorated surface.
본 발명을 공정별로 상세히 설명하면 다음과 같아.The present invention will be described in detail by process as follows.
[제1공정][Step 1]
하드보드 표면에 표현하고자 하는 무늬모양을 음각으로 압인 또는 조각한다. 압인방법은 무늬모양이 조각된 압인로울러로 압인할 수 있으며 무늬모양이 특별한 경우는 인위적으로 조각할 수 있다.Stamp or sculpt the pattern you want to express on the hard board surface. The stamping method can be stamped with a patterned engraved roller, and if the pattern is special, it can be engraved artificially.
이상과 같이 음각무늬모양이 형성된 표면은 연마포로 연마하여 표면을 도장하기 좋은 상태로 정리한다.The surface in which the intaglio pattern is formed as described above is polished with a polishing cloth to arrange the surface in a good state for coating.
[제2공정][Step 2]
본 공정은 하도공정으로서 도1과 같이 음각무늬모양(20)이 압인된 하드보드표면에 투명도료를 도포한 하도도장층(30)을 약 4시간정도 자연건조후 연마포로 표면을 연마하여 도장하기 좋은 상태로 정리한다.This process is the undercoat process, as shown in FIG. 1, after the natural coating of the undercoat layer 30 coated with a transparent paint on the hard board surface of which the engraved pattern 20 is pressed for about 4 hours, the surface is polished and coated with an abrasive cloth. Clean up in good condition.
이때 연마포는 180-200메쉬를 사용하며 연마는 2회정도 실시하는 것이 좋다.At this time, the polishing cloth is used 180-200 mesh and polishing should be performed twice.
이 공정은 다음에 도장될 양각과 음각도장도료의 흡습을 방지하여 색상변화를 방지하고 도료의 도포상태가 양호하도록 하는 바탕이 된다.This process is the basis for preventing the color change and the good coating state of the paint by preventing the moisture absorption of the embossed and engraved paint to be coated next.
[제3공정][Step 3]
본 공정은 음각무늬모양(20)을 제외한 부분, 즉 양각에 해당하는 부분의 도장공정으로서 도 2와 같이 상기 공정에서 형성한 하도도장층(30)상에 양각부(40) 도색을 위한 도료를 스프레이방법으로 도장하여 양각부도장층(41)을 형성하고 이를 8-12시간 자연건조한 다음 연마포로 연마하여 도장면을 정리한다.This process is a coating process of the portion except the intaglio pattern 20, that is, the portion corresponding to the embossing, the paint for painting the embossed portion 40 on the undercoat layer 30 formed in the process as shown in FIG. Painting by spraying method to form an embossed coating layer 41, which is naturally dried for 8-12 hours and then polished with a polishing cloth to clean the painted surface.
이때 사용되는 도료는 2액형 우레탄수지도료로서 도료와 경화제가 2:1로 배합한 것을 사용한다.At this time, the coating material used is a two-component urethane resin coating material, which contains a 2: 1 paint and a curing agent.
[제4공정][Step 4]
본 공정은 음각무늬모양 도장공정으로서 도 3과 같이 상기 공정에서의 양각부도장층(41)과는 다른 색상의 음각도장도료를 스프레이 방법으로 도장하여 음각부도장층(21)을 형성한 다음 건조하여 도 4와 같이 양각부(40)표면에 도포된 음각도장도료를 연마제거하여 상기 공정에서 도장한 양각부도장층(41)의 색상을 노출시키고, 음각부도장층(21)은 음각부(20)에만 남도록 한다.This process is an intaglio pattern coating process, as shown in Fig. 3, the intaglio coating layer of the color different from the embossed portion coating layer 41 in the process by spraying method to form the intaglio portion coating layer 21 and then dried 4 to expose the color of the embossed coating layer 41 coated in the above process by polishing and removing the intaglio coating applied to the surface of the embossed portion 40, as shown in FIG. Only).
이때 연마포는 220-320메쉬를 사용하는 것이 좋다.In this case, it is preferable to use a 220-320 mesh for the polishing cloth.
[제5공정][Step 5]
본 공정은 통상의 마무리 공정으로서 도 5와 같이 양각, 음각의 도장층(21)(41)이 보호되도록 유광 또는 무광으로 투명코팅도료(50)를 도포하여 완제품을 얻는다.This process is a conventional finishing process, as shown in Fig. 5 to obtain a finished product by applying a transparent coating paint 50 in a glossy or matte so as to protect the embossed, intaglio coating layers (21, 41).
이상과 같이 도장된 하드보드는 표면의 무늬모양이 이색으로 도장되어 장식적 효과가 높고, 수요자의 다양한 기호에 대응할 수 있는 고품질의 장식판재로 이용되는 효과가 있다.The hard board coated as described above has a high decorative effect because the pattern of the surface is painted in a different color, it is used as a high-quality decorative plate material that can respond to various preferences of the consumer.
Claims (1)