KR960023195A - Manufacturing method of high tensile alloyed hot dip galvanized steel sheet with excellent workability and corrosion resistance - Google Patents
Manufacturing method of high tensile alloyed hot dip galvanized steel sheet with excellent workability and corrosion resistance Download PDFInfo
- Publication number
- KR960023195A KR960023195A KR1019940032487A KR19940032487A KR960023195A KR 960023195 A KR960023195 A KR 960023195A KR 1019940032487 A KR1019940032487 A KR 1019940032487A KR 19940032487 A KR19940032487 A KR 19940032487A KR 960023195 A KR960023195 A KR 960023195A
- Authority
- KR
- South Korea
- Prior art keywords
- dip galvanized
- steel sheet
- hot
- galvanized steel
- corrosion resistance
- Prior art date
Abstract
본 발명은 통상의 아연도금욕 조성에서 도금 및 공기분사에 의한 부착량 조정을 거쳐 적정 온도에서의 합금과 처리를 실시하므로서 프레스 가공시 내파우더링성이 우수하고 도장 후 내식성이 우수한 합금화 용융아연도금강판을 제조할 수 있는 방법을 제공하고자 함에 그 목적이 있다.The present invention provides an alloyed hot-dip galvanized steel sheet having excellent powdering resistance during press working and excellent corrosion resistance after coating by performing treatment with an alloy at an appropriate temperature by adjusting the adhesion amount by plating and air spraying in a conventional galvanizing bath composition. The purpose is to provide a method which can be manufactured.
본 발명은 티타늄-인 복합첨가 극저탄소강을 소둔하고 용융아연 도금한 후, 합금화 처리하여 합금화 용융아연도금강판을 제조하는 방법에 있어서, 상기 용융아연 도금시 도금부착량이 80∼100g/m2범위가 되도록 용융아연 도금한 후, 500∼540℃ 온도범위에서 합금화 처리하여 가공성 및 내식성이 우수한 합금화 용융아연도금 강판을 제조하는 방법을 제공함을 그 요지로 한다.The present invention is a method for producing an alloyed hot dip galvanized steel sheet by annealing and hot-dip galvanizing titanium-phosphorus composite addition ultra low carbon steel, the coating adhesion amount during the hot-dip galvanizing range 80 ~ 100g / m 2 The present invention is to provide a method for producing an alloyed hot-dip galvanized steel sheet excellent in workability and corrosion resistance after the hot-dip galvanized so as to be alloyed at 500 ~ 540 ℃ temperature range.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음Since this is an open matter, no full text was included.
Claims (1)