KR950032670A - 차체패널재용 알루미늄 합금판 및 그 제조방법 - Google Patents

차체패널재용 알루미늄 합금판 및 그 제조방법 Download PDF

Info

Publication number
KR950032670A
KR950032670A KR1019940010192A KR19940010192A KR950032670A KR 950032670 A KR950032670 A KR 950032670A KR 1019940010192 A KR1019940010192 A KR 1019940010192A KR 19940010192 A KR19940010192 A KR 19940010192A KR 950032670 A KR950032670 A KR 950032670A
Authority
KR
South Korea
Prior art keywords
aluminum alloy
less
alloy plate
body panel
content
Prior art date
Application number
KR1019940010192A
Other languages
English (en)
Other versions
KR100209208B1 (ko
Inventor
테쯔시 하부
미노루 하야시
요이치로 벳키
Original Assignee
토모마쯔 켕고
후루카와덴기코교 카부시키가이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 토모마쯔 켕고, 후루카와덴기코교 카부시키가이샤 filed Critical 토모마쯔 켕고
Priority to KR1019940010192A priority Critical patent/KR100209208B1/ko
Publication of KR950032670A publication Critical patent/KR950032670A/ko
Application granted granted Critical
Publication of KR100209208B1 publication Critical patent/KR100209208B1/ko

Abstract

Mg 함량이 4∼10wt%이고, Fe, Mn, Cr, Ti 및 Zr 함량은 하기식 Ⅰ
0.4wt%≤f≤1.5wt% ……… (Ⅰ)
(식중, f=〔Fe〕+1.1〔Mn〕+1.1〔Cr〕+3〔Ti〕+3〔Zr〕이고, 〔Fe〕,〔Mn〕,〔Cr〕,〔Ti〕 및 〔Zr〕은 각각 Fe, Mn, Cr, Ti 및 Zr의 중량%함량을 나타낸다)을 만족시키는 값 f로 한정되며, 잔부가 Aℓ로 이루어진 용융알루미늄합금을 주조하여 잉고트를 얻고; 잉고트를 열간압연처리한 후 다음식 Ⅱ
-ℓog(f-0.2)+8≤G≤-60ℓog(f-0.2)+50 ……… (Ⅱ)
를 만족하는 냉간압연을 R로 냉간압연처리하여 압연판을 얻고; 압연판을 승온속도 100℃/분 이상으로 하여 온도를 450-550℃로 높여 그 온도에서 300초 이하로 유지하여 최종 에닐링처리하고; 압연판을 냉각을 100℃/분 이상으로 냉각처리하여 알루미늄 합금판을 얻는 공정으로 이루어진 차체패털재용 알루미늄 합금판의 제조방법.

Description

차체패널재용 알루미늄 합금판 및 그 제조방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 알루미늄합금 내 Fe 당량과 냉간압연을 간의 관계를 도시하는 그래프.

Claims (9)

  1. Mg 함량이 4∼10wt%, Fe, Mn, Cr, Ti 및 Zr 함량은 하기식 Ⅰ
    0.4wt%≤f≤1.5wt% ……… (Ⅰ)
    (식중, f=〔Fe〕+1.1〔Mn〕+1.1〔Cr〕+3〔Ti〕+3〔Zr〕이고, 〔Fe〕,〔Mn〕,〔Cr〕,〔Ti〕 및 〔Zr〕은 각각 Fe, Mn, Cr, Ti 및 Zr의 중량%함량을 나타낸다)을 만족시키는 값 f로 한정되며, 잔부가 Aℓ로 이루어진 용융알루미늄합금을 주조하여 잉고트를 얻고; 잉고트를 열간압연처리한 후 다음식
    ℓog(f-0.2)+8 ≤R≤- 60ℓog(f-0.2)+50 ……… (Ⅱ)
    를 만족하는 냉간압연을 R로 냉간압연처리하여 압연판을 얻고; 압연판을 승온속도 100℃/분 이상으로 하여 온도를 450~550℃로 높여 그 온도에서 300초 이하로 유지하여 최종 에닐링처리하고; 압연판을 냉각을 100℃/분 이상으로 냉각처리하여 알루미늄 합금판을 얻는 공정으로 이루어진 차체패털재용 알루미늄 합금판의 제조방법.
  2. 제1항에 있어서, 상기 열간압연처리후의 압연판을 냉각압연공정의 중간에서 프로세스에닐링처리하는 것을 특징으로 하는 차체패널재용 알루미늄합금판의 제조방법.
  3. 제1항에 있어서, 상기 알루미늄 합금은 Cu를 0.5wt%이하 함유하는 것을 특징으로 하는 차체패널재용 알루미늄합금판의 제조방법.
  4. 제1항에 있어서, 상기 알루미늄 합금은 Fe를 1.0wt%이하, Mn을 1.0wt%, Cr을 0.3wt%이하, Ti를 0.2%이하, Zr을 0.3%이하로 함유하는 것을 특징으로 하는 차체패널재용 알루미늄합금판의 제조방법.
  5. 제1항에 있어서, 상기 알루미늄 합금은 Si를 0.5wt%이하로 함유하는 것을 특징으로 하는 알루미늄 합금판의 제조방법.
  6. Mg함량이 4∼10wt%, Fe, Mn, Cr, Ti 및 Zr 함량은 다음식 Ⅰ
    0.4wt%≤f≤1.5wt% ……… (Ⅰ)
    (식중, f=〔Fe〕+1.1〔Mn〕+1.1〔Cr〕+3〔Ti〕+3〔Zr〕이고, 〔Fe〕,〔Mn〕,〔Cr〕,〔Ti〕 및 〔Zr〕은 각각 Fe, Mn, Cr, Ti 및 Zr의 중량%함량을 나타낸다)을 만족시키는 값 f로 한정되며, 잔부가 Aℓ로 이루어진 입경 20~80㎛의 차체패널재용 알루미늄 합금판.
  7. 제6항에 있어서, 상기 알루미늄 합금은 Cu를 0.5%이하 함유하는 것을 특징으로 하는 차체패널재용 알루미늄 합금판.
  8. 제6항에 있어서, 상기 알루미늄 합금은 Fe를 1.0wt%이하, Mn을 1.0wt%이하, Cr을 0.3wt%이하, Ti를 0.2%이하, Zr을 0.3%이하로 함유하는 것을 특징으로 하는 차체패널재용 알루미늄합금판.
  9. 제6항에 있어서, 상기 알루미늄 합금은 Si를 0.5wt%이하로 함유하는 것을 특징으로 하는 차체패널재용 알루미늄합금판.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019940010192A 1994-05-10 1994-05-10 차체패널재용 알루미늄합금판 및 그 제조방법 KR100209208B1 (ko)