Claims (5)
산가용성 금속판을 산수용액을 용제로하여 엣칭(etching)하는 공지의 방법에 있어서, 시계뒷판등의 금속판에 감광액처리, 건조후 무늬 및 문자도안 필름을 부착하고 자외선 조사하여 문자를 인쇄한 다음 필름제거후 연상하여 약 200℃로 열처리한 다음 자연건조시켜 염화제이철용액에 7-14분간 엣칭시켜, 물세척, 가성소오다탈지, 물세척, 초음파세척 순으로 실시한 후 금도금시켜 다시 세척 및 건조후 길드페인트 도포하여 페인트용해액종이에 금속판을 문질러 길드페인트를 제거시켜 30-50℃의 금용해액에 문자이외의 금도금을 박리시키고, 음각문자부의 페인트를 제거하여 환제품을 얻게되는 금속판의 무늬 및 문자에 색도금 형성방법.In a known method of etching an acid-soluble metal plate with a solvent of an acid solution, a photoresist treatment is applied to a metal plate such as a watch back plate, a pattern and a film after drying, and ultraviolet rays are irradiated to print a character and then the film is removed. After associating, heat-treat it at about 200 ℃, dry it naturally, and etch it in ferric chloride solution for 7-14 minutes, then wash it with water, caustic soda, water wash, ultrasonic wash, gold-plated, wash and dry again, and then guild paint. Remove the guild paint by rubbing the metal plate on the paint dissolving paper and peeling the gold plating other than the letter from the gold solution at 30-50 ℃, and removing the paint of the intaglio letter. Color plating method.
제1항에 있어서, 금속판에 감광액처리 및 건조후 무늬 및 문자도안된 실크인쇄지를 부착하여 자외선 조사하여 문자인쇄한 다음 실크인쇄지를 제거후 현상하여 약 200℃로 열처리하여 자연건조시켜 염화제이철 용액에 7-14분간 에칭시키는 방법으로 무늬 및 문자를 형성시켜 금속판의 무늬 및 문자에 색도금 형성방법.The method of claim 1, after the photoresist treatment and drying on the metal plate, the printed silk printing paper with the pattern and text is attached, and then printed by ultraviolet irradiation, and then removed after the silk printing paper is developed and heat-treated at about 200 ° C. Forming a pattern and a character by etching for 7-14 minutes to form a color plating on the pattern and the character of the metal plate.
제1항에 있어서, 금속판에 감광액처리 및 건조후 무늬 및 문자도안된 패드인쇄지를 부착하여 자외선 조사하여 문자인쇄한 실크인쇄지를 제거하고 약 200℃로 열처리하여 자연건조시켜 염화제이철 용액에 7-14분간 에칭시키는 방법으로 무늬 및 문자를 형성시켜 금속판의 무늬 및 문자에 색도금 형성방법.The method of claim 1, wherein after the photoresist is treated and dried on a metal plate, a pad printing paper with a pattern and a letter pattern is attached to the metal plate to remove ultraviolet printed silk printing paper, and heat-treated at about 200 ° C. to dry naturally. A method of forming a color plate on a metal plate pattern and letters by forming patterns and letters by etching for a minute.
제1항에 있어서, 금속판에 흑도금(검정색)한후 레이저로 무늬 및 문자를 도안하여 염화제이철용액에 7-14분간 엣칭후 다시 흑도금하여 길드페인트로 도포하여 페인트용해액 종이에 문질러 길드페인트를 제거시켜 30-50℃의 용해액에 문자이외의 흑도금을 박리시키고, 음각문자부의 페인트를 제거하므로써 흑색문자가 형성된 제품을 얻게된 금속판의 무늬 및 문자에 색도금 형성방법.The method of claim 1, after black-plating (black) on the metal plate and the pattern and the character with a laser, etched in ferric chloride solution for 7-14 minutes, then black-plated and coated with guild paint to remove the guild paint by rubbing on the paint solution paper A method of forming a color plate on a metal plate pattern and characters obtained by peeling black plating other than characters in a solution of 30-50 ° C. and removing the paint of the intaglio characters.
제4항에 있어서, 금속판에 금도금한 후 레이저로 무늬 및 문자를 도안하여 염화제이철용액에 7-14분간 엣칭후 다시 금도금하여 길드페인트로 도포한 후 페인트용해액 종이에 금속판을 문질러 길드페인트를 제거시켜 30-50℃의 용해액에 문자이외의 금도금을 박리시키고, 음각문자부의 페인트를 제거하므로써 금도금문자가 형성된 제품을 얻게된 금속판의 무늬 및 문자에 색도금 형성방법.The method of claim 4, after the gold plated on the metal plate and the pattern and letters with a laser, etched in a ferric chloride solution for 7-14 minutes and then gold-plated and coated with a guild paint to remove the guild paint by rubbing the metal plate on the paint solution paper Method of forming a color plating on the metal plate pattern and characters obtained by peeling gold plating other than letters in the solution of 30-50 ℃, and removing the paint of the intaglio letters.
※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.※ Note: The disclosure is based on the initial application.