KR920000849A - 3차 알코올 존재하에 폴리이소시아네이트 중합 부가법에 의한 다공성 플라스틱의 제조방법 - Google Patents
3차 알코올 존재하에 폴리이소시아네이트 중합 부가법에 의한 다공성 플라스틱의 제조방법 Download PDFInfo
- Publication number
- KR920000849A KR920000849A KR1019910010454A KR910010454A KR920000849A KR 920000849 A KR920000849 A KR 920000849A KR 1019910010454 A KR1019910010454 A KR 1019910010454A KR 910010454 A KR910010454 A KR 910010454A KR 920000849 A KR920000849 A KR 920000849A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- blowing agent
- tertiary alcohol
- tertiary
- process according
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (10)
- 폴리이소시아네이트 중합부가법에 의한 다공성 플라스틱의 제조방법으로서, a)유기 및/또는 변형된 유기 폴리이소시아네이트를, b)알키드 수지를 제외한 최소한 2개의 반응성 수소 원자를 포함한 1개 이상의 고-분자량 화합물, 및 필요하다면, c)저-분자량 사슬 연장제 및/또는 가교결합제와, d)발포제(여기서 사용된 발포제는 최소한 하나의 3차 알코올(di)이다), e)촉매, 및 필요하다며, f)보조제 및 첨가제의 존재하에 반응시키는 다공성 플라스틱의 제조방법.
- 제1항에 있어서, 사용된 발포제(d)가 dj)최소한 하나 이상의 3차 알코올과 dii)물의 혼합물인 것을 특징으로 하는 방법.
- 제1항에 있어서, 사용된 발포제(d)는, 성분(a)내지 (c)의 총중량을 토대로, 0.5 내지 20중량%의 최소한 하나 이상의 3차 알코올(di)인 것을 특징으로 하는 방법.
- 제1항에 있어서, 사용된 발포제(d)가 di)0.5 내지 20중량%의 최소한 하나 이상의 3차 알코올 및 dii)성분(a)내지 (c)의 총중량을 토대로 한 중량%로, 0.05내지 2중량%의 물로 이루어진 혼합물인 것을 특징으로 하는 방법.
- 제1항 내지 제4항중 어느 한 항에 있어서, 사용된 발포제(d)가 3차 부탄올(di)인 것을 특징으로 하는 방법.
- 우레탄-함유 플라스틱으로부터 만들어진 밀집한 주변 영역 및 다공성 코어를 갖는 성형물의 제조방법으로서 a)유기 및/또는 변형된 유기 폴리이소시아네이트를, b)최소한 2개 이상의 반응성 수소 원자를 포함한 최소한 하나 이상의 고-분자량 화합물 및 필요하다면, c)저-분자량 사슬 연장제 및/또는 가교 결합제와, d)발포제(여기서 사용된 발포제(d)는 최소한 1개의 알코올(di)이다), e)촉매 및 필요하다며, f)보조제 및/또는 첨가제의 존재하에 폐쇄된 모올드에서 밀집하게 반응시킴에 의한 제조방법.
- 제6항에 있어서, 사용된 발포제(d)가 성분(a) 내지 (c)의 총 중량을 토대로, 0.5 내지 20중량%의 최소한 하나 이상의 3차 알코올(di)인 것을 특징으로 하는 방법.
- 제6항에 있어서, 사용된 발포제(d)가 di)0.5내지 20중량%의 최소한 하나 이상의 3차 알코올 및 dii)성분(a)내지 (c)의 전체 중량을 토대로 한 중량%로 0.05 내지 2중량%의 물로, 0.05 내지 2중량%의 물로 이루어진 혼합물인 것을 특징으로 하는 방법.
- 제6항 내지 제8항중 어느 한 항에 있어서, 사용된 발포제(d)는 3차 부탄올(di)인 것을 특징으로 하는 방법.
- 제6항에 있어서, 반응은 폐쇄된 모올드에서 2내지 6의 밀집도로 수행되는 것을 특징으로 하는 방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.