KR910005042B1 - Method making a design of a pearl - Google Patents
Method making a design of a pearl Download PDFInfo
- Publication number
- KR910005042B1 KR910005042B1 KR1019860005245A KR860005245A KR910005042B1 KR 910005042 B1 KR910005042 B1 KR 910005042B1 KR 1019860005245 A KR1019860005245 A KR 1019860005245A KR 860005245 A KR860005245 A KR 860005245A KR 910005042 B1 KR910005042 B1 KR 910005042B1
- Authority
- KR
- South Korea
- Prior art keywords
- pearl
- resin
- foil
- squeegee
- pattern
- Prior art date
Abstract
Description
본 발명은 액상 진주박을 불포화 폴리 에스테르 수지에 혼입한 진주박 혼입 수지로 천연 진주와 같은 아름다운 진주 광택이 나타날 수 있도록한 불포화 폴리 에스테르 수지에 의한 진주 무늬 형성 방법에 관한 것이다.The present invention relates to a method of forming a pearl pattern by an unsaturated polyester resin in which a pearlescent resin mixture incorporating a liquid pearl foil into an unsaturated polyester resin can exhibit a beautiful pearl luster like natural pearls.
종래 천연의 진주 자재 무늬 가구가 있었으나 이것은 진주 자개를 일일이 세공으로 작업한 후 장식해서 제조하여야 했으므로 그 재료비는 물론 수공비가 많이 소요될 뿐 아니라 많은 작업 시간과 인력이 소모되어 대량 생산을 할 수 없었고 제품 가격이 고가인 결점이 있었으며 다른 일례로서 자개 가구를 이용한 무늬판의 가공 방법이 있었으나 이것도 자개설이나 자개 가루를 살포해야 하므로 도료와의 혼합 상태가 불균일하고 살포된 자개 재료위에 도료를 다시 수회 재도층시키므로 자개 재료의 노출도가 불충분하여 광택도가 물량하므로 천연 자개와 같은 광택을 얻을 수 없었고 정밀도나 작업성이 불량하여 많은 손질을 요하는 등의 단점이 있었는데 이와 같은 제반 문제점을 해결 하였다는 특허공고 번호 80-1073호의 가구용 진주박 자개무늬지의 제조 방법은 감광지로 된 기지위에 액상 진주박 투명 랙커, 신나, 실리콘, 오일 및 MIBK로 조성된 진주박 도료(백색 또는 은색)로 도층하고 그위에 황색, 적색 또는 이와 유사한 색의 안료와 진주박 도료로 조성된 착색제로 줄무늬를 착색한 후 40℃내외의 온도로 30-60분간 가열 건조하며 PVC계 수지를 전색제로 하는 흑색 인쇄 잉크로 장식 무늬를 인쇄하고 건조 후 호마이카 약 1-2mm 정도의 두께로 도층한 위에 실리콘 수지계 필름을 깔고 로울러로 가압하는 것으로서, 이 방법은 액상 진주박, 투명랙커, 신나, 실리콘 오일 및 MIBK로 조성된 진주박 도료층, 그 위에 줄무늬를 교대로 착색하는 착색제층에서 투명 랙커 수지성분과 호마이카 수지가 서로 다른 수지이므로 도층된 두 층의 강도 차이 또는 불친화성과 호마이카 경화시 7-10%의 체적의 수축으로 인하여 호마이카층의 균열이나 박리가 발생하고 작업과정에서 유기 용제나 진주박 등이 직접 외부로 노출된 상태에서 작업하기 때문에 일정 온도와 시간을 맞추어야 하며 위생상에도 해로운 결점이 있었다.Previously, there was a natural pearl-patterned furniture, but this was required to be manufactured after the mother-of-pearl was worked by handwork. Therefore, not only the material cost but also the manual cost were high. There was this expensive defect, and another example was the method of processing the pattern plate using the mother-of-pearl furniture, but this also required the mother-of-pearl and the mother-of-pearl to be sprayed, resulting in uneven mixing with the paint and re-painting the paint on the mother-of-pearl. Because of insufficient exposure of the mother-of-pearl material, the gloss content was insufficient, so it was impossible to obtain gloss like natural mother-of-pearl, and there was a disadvantage of requiring a lot of care due to poor precision and workability. Of pearl leaf mother of pearl pattern paper for the furniture of 80-1073 The method consists of coating a pearlescent paint (white or silver) composed of liquid pearl foil transparent racker, thinner, silicone, oil and MIBK on a base of photosensitive paper, on top of which pigments and pearlescent paints of yellow, red or similar color. After coloring the stripes with a colorant composition, heat-dried for 30-60 minutes at a temperature of about 40 ℃, print a decorative pattern with a black printing ink with a PVC-based resin as a colorant, and after drying, to a thickness of about 1-2mm Applying a silicone resin film on the coating layer and pressing with a roller, this method is transparent in a pearlescent paint layer composed of liquid pearl foil, transparent lacquer, thinner, silicone oil and MIBK, and a colorant layer for alternately coloring stripes thereon. Since the racker resin component and the Homica resin are different resins, due to the difference in strength or incompatibility between the two layers layered and the shrinkage of the volume of 7-10% during Homica curing Matchueoya a predetermined temperature and time, because the operation in which the cracking or peeling of the mica layer occurs, and the like organic solvent or pearl foil directly exposed to the outside in a work process and conditions were the defects detrimental to the health.
본 발명은 종래의 이러한 단점을 해소하고 불포화 폴리 에스테르 수지를 이용한 특수한 아름다운 진주 광택을 지닌 진주 무늬 장식판을 제조하기 위한 것으로서 본 발명을 공정별로 상세히 설명하면 다음과 같다.The present invention is to solve the above disadvantages of the prior art and to prepare a pearl pattern decorative plate having a special beautiful pearl luster using an unsaturated polyester resin will be described in detail the present invention by the process as follows.
[제1공정(지당 화이트 혼입 수지의 도포 공정)][1st process (coating process of per white fat mixed resin)]
칩보드로 된 기판위에 백색 안료인 지당 화이트를 혼입한 불포화 폴리 에스테르 수지를 일정한 두께로 균일하게 도포하여 기판 자체의 색소나 얼룩 등을 차폐시킨 후 건조시켜서 220번 정도의 사포로 건조시킨 차폐층을 고루 문질러 표면을 연마한다.On the chipboard substrate, an unsaturated polyester resin mixed with white sugar, which is a white pigment, is uniformly applied to a certain thickness to shield pigments or stains of the substrate itself, and then dried and dried with a sandpaper of about 220 times. Rub evenly to polish the surface.
[제2공정(액상 진주박 혼입 수지 도포 공정)][2nd process (liquid pearl foil mixed resin coating process)]
기판 600㎠당 작업장의 온도와 목적하는 무늬의 종류에 따른 적량의 경화제를 첨가한 100cc의 불포화 폴리 에스테르 수지에 5cc내외의 비율로 액상 진주박을 혼입하여서된 진주박 혼입 수지를 제1공정의 차폐층 위에 도포한 다음 셀로판 필름이나 데트론 필름을 그 위에 덮어 로울러로 적절히 가압하면서 밀어 주어 기포를 없애는 탈포를 겸하면서 차폐층의 전면에 진주박 혼입 수지가 일정한 두께로 균일하게 도포되게 한다.Shielding the pearl foil mixing resin prepared by mixing liquid pearl foil at a rate of about 5 cc to 100 cc of unsaturated polyester resin to which an appropriate amount of curing agent is added according to the type of the desired pattern and the type of the desired pattern per 600 cm 2 of substrate After coating on the layer, the cellophane film or detron film is covered on it and pushed with a roller while appropriately pressed to serve as a defoaming to remove air bubbles, and the pearl foil mixed resin is uniformly applied to the entire surface of the shielding layer at a uniform thickness.
[제3공정(진주 무늬 형성 공정)][3rd process (Pearl pattern forming process)]
제2공정이 끝난 뒤 진주박 혼입 수지가 겔화하기 시작하면 셀로판 필름을 진주박 혼입 수지층에 밀착시킨채로 일정한 방향으로 이동시켜 로울러로 밀어 주었을 때 자연적으로 발생했던 얼룩 무늬를 없애주고 우레탄 고무재질의 스퀴이지를 셀로판 필름상에 대고 일정한 방향으로 밀어 주어 진주박 혼입 수지가 스퀴이지가 밀어 주는 방향으로 이동하면서 진주박 입자가 일정하게 규칙적으로 배열되게 하여 미려하고 아름다운 진주 광택을 지닌 유선형 무늬가 나타나도록 하고 진주막 혼입 수지층의 경화된 후 셀로판 필름을 벗겨내어 진주 무늬 장식판을 완성시킨다.After the end of the second process, the pearl foil mixture resin begins to gel, and the cellophane film moves in a fixed direction while being in close contact with the pearl foil mixture resin layer to remove the stains that occurred naturally when pushed to the rollers. Press the squeegee on the cellophane film and push it in a certain direction so that the pearl foil mixing resin moves in the direction that the squeegee pushes so that the pearl foil particles are regularly arranged so that a streamlined pattern with beautiful and beautiful pearl luster appears. After the hardening of the nacre mixed resin layer, the cellophane film is peeled off to complete the pearl-patterned decorative plate.
본 발명은 이상과 같은 3개 공정에 의해 이루어지며 이상과 같이 구성된 본 발명의 작용 효과를 상술하면 다음과 같다.The present invention is made by the three steps as described above and the operation and effect of the present invention configured as described above are as follows.
지당 화이트는 백색 안료이며 이를 혼입한 불포화 폴리 에스테르 수지를 칩보드로된 기판위에 일정한 두께로 균일하게 도포하여 기판 자체의 색소나 얼룩 등을 차폐시킴으로써 그 위에 도포되는 진주박 혼입 수지에 의한 진주 무늬가 선명하게 나타나게 됨은 물론, 만일 진주 무늬가 형성되도록 하기 위해 스퀴이지로 밀어줄 때 진주박 혼입 수지가 기판상의 다른 곳보다 얇은 곳이 생긴다 하더라도 진주박이 많이 모인곳은 좀 더 진한색의 유선형 무늬가 형성되면서 진주박의 은백색과 차폐층의 백색 안료인 지당 화이트의 색상이 서로 어울리기 때문에 이 경우에는 보기 좋게 조화를 이루게 된다.White sugar is white pigment and pearl pattern by pearl foil mixed resin applied on it by shielding pigments or stains of substrate itself by uniformly applying unsaturated polyester resin mixed with uniform thickness on chipboard. Not only will it appear clearer, but if the pearlescent mixture is thinner than other parts on the substrate when it is pushed into the squeegee to form a pearly pattern, the darker streamlined pattern will be formed where much of the pearlescent is gathered. In this case, the silver white of pearl foil and the white color of Jidang, which is the white pigment of the shielding layer, are in harmony with each other.
이와 같은 차폐층을 사포로 문질러 그 표면을 연마 해주어야만 그 위에 도층되는 진주박 혼입 수지층과의 결합 강도가 높아져 차폐층으로부터 진주박 혼입 수지의 박리나 균열 등이 일어나지 않게 되는데 너무 지나치게 굵은 사포로 표면을 연마하게 되면 차폐층의 표면에 울퉁불퉁하게 요철이 심하여 진주박 혼입 수지층의 두께가 균일하게 되지 않으므로 깨끗하고 선명한 진주 광택 무늬를 형성할 수가 없고 너무 고운 사포를 사용하면 작업 능률이 저하되어 220번 전후의 사포로 연마하는 것이 가장 알맞다.Rubbing such a shielding layer with sandpaper should polish the surface, so that the bonding strength with the pearl foil-containing resin layer layered thereon becomes high, so that peeling or cracking of the pearl-oil-containing resin from the shielding layer does not occur. When the surface is polished, the surface of the shielding layer is unevenly rough, so the thickness of the pearl foil mixed resin layer is not uniform, so that it is impossible to form a clean and clear pearlescent pattern. It is best to grind with sandpaper before and after burning.
이상과 같이 연마된 기판의 차폐층 위에 진주박 혼입 수지를 도포할 때는 기판 600㎠당 불포화 폴리 에스테르 수지 100cc에 5cc내외의 액상 진주박을 혼입한 도료량이 가장 알맞으며 만일 그보다 적으면 기판 전체를 골고루 덮는데 부족하게 되고 그 보다 많으면 생산 원가의 상승뿐만 아니라 진주 광택 무늬 형성을 위해 스퀴이지를 셀로판 필름상에 대고 동일 방향으로 밀어줄 때 초과된 진주박 혼입 수지의 량은 기판밖으로 흘러 내리기 때문에 불필요하게 진주박 혼입 수지가 소모된다. 또한 불포화 폴리 에스테르 수지에 혼합하는 액상 진주박이 지나치게 많으면 불포화 폴리에스테르 수지와 잘 섞이지 않고 혼합 과정에서 무수한 기포가 발생하게 되므로 진주박 혼입 수지의 도포 때 탈포가 어려워지고 진주 무늬가 양호하게 형성될 수 없으며 너무 적으면 충분한 진주 무늬 광택을 나타낼 수 없게 된다.When applying the pearl foil mixed resin on the shielding layer of the polished substrate as described above, 100cc of unsaturated polyester resin per 600cm2 of the substrate mixed with liquid pearl foil of about 5cc is most suitable. If it is insufficient to cover, and more than that, the amount of excess pearl foil mixed resin is unnecessarily flowed out of the substrate when the squeegee is pushed on the cellophane film in the same direction not only to increase the production cost but also to form a pearlescent pattern. Pearl foil mixing resin is consumed. In addition, if there are too many liquid pearl foil mixed with the unsaturated polyester resin, it does not mix well with the unsaturated polyester resin and numerous bubbles are generated during the mixing process, so that defoaming becomes difficult and the pearl pattern cannot be formed well when the pearl foil mixed resin is applied. Too little can result in insufficient pearlescent luster.
진주박은 길이에 비교하여 두께가 대단히 얇은 물고기 비늘 형상인 선편상 결정의 연염으로써 불포화 폴리 에스테르 수지에 혼합하여 기판위에 도포를 한 상태에서는 그 결정이 일정하게 배열되지 않고 사방으로 불규칙하게 난립되 있어 흰색과 연회색빛 얼룩만 나타날 따름이나 수지가 겔화가 되기 시작할 때 진주박 혼입 수지층에 셀로판 필름을 덮어 진주박 혼입 수지층과 밀착되게 한 후 셀로판 필름을 일정한 방향으로 이동시켜 주면 셀로판 필름 아래에 도층된 진주박 혼입 수지중에 함유된 진주박 입자들이 어느 정도 셀로판 필름의 이동 방향으로 규칙적으로 일정하게 배열되면서 연회색 얼룩이 사라지게 되며 시간이 지나 진주박 혼입 수지층 위에 셀로판 필름이 접착되어 팽팽하게 잡아주고 있는 셀로판 필름틀의 무게로 기판의 가장자리 부근의 수지가 얇아 가운데 부분보다 먼저 겔화되어 셀로판 필름을 움직이기 어려우면 셀로판 필름위에 우레탄 고무 재질로된 스퀴이지를 대어 밀착시켜서 적당한 압력을 가하면서 동일 방향으로 스퀴이지로 밀어주면 진주박 혼입 수지가 필름 아래에서 스퀴이지의 이동 방향으로 유동하면서 진주박 혼입 수지속에 혼입되 있는 진주박 입자가 그 스퀴이지의 이동 방향으로 규칙적으로 일정하게 배열하게 되어 미려한 진주 무늬 광택을 나타내는 유선형 무늬가 형성된다.Pearl foil is a salt of linear scale crystals in the shape of fish scales that is very thin compared to its length. When mixed with unsaturated polyester resin and coated on a substrate, the crystals are not uniformly arranged but irregularly scattered in all directions. When only the light gray stain appears, or when the resin starts to gel, cover the cellophane film with the pearl foil mixed resin layer to be in close contact with the pearl foil mixed resin layer, and then move the cellophane film in a certain direction. The pearlescent particles contained in the pearlescent mixed resin are regularly arranged to a certain extent in the direction of movement of the cellophane film, so that the light gray stain disappears, and the cellophane film is firmly held by the cellophane film adhered to the pearlescent mixed resin layer over time. Edge part of the substrate under the weight of the frame If the resin is thin and gelled before the center part, making it difficult to move the cellophane film. Touch the squeegee made of urethane rubber on the cellophane film and push it to the squeegee in the same direction while applying the appropriate pressure. The pearl foil particles mixed in the pearl foil mixing resin while flowing in the direction of movement of the squeegee from below are regularly arranged regularly in the direction of movement of the squeegee to form a streamlined pattern showing a beautiful pearlescent luster.
스퀴이지는 목재나 철재로된 손잡이의 한쪽 끝에 셀로판 필름면과 평행하도록 우레탄 고무를 길게 부착시킨 것으로서 스퀴이지에 형성된 우레탄 고무는 단단하고 질긴 합성 고무이며 이 고무의 경도는 필름 아래에 도층된 진주박 혼입 수지를 필름위에서 압력을 적당히 가하면서 밀어 주어 유동시키는데 적합하고 스퀴이지로 밀어줄 때 우레탄 고무가 쉽사리 마모되지 않는 재질이므로 장시간 사용에 적합하게 된다.Squeegee is a long stick of urethane rubber that is parallel to the surface of a cellophane film at one end of a wooden or steel handle. Urethane rubber formed on the squeegee is a hard, tough synthetic rubber whose hardness is the pearl foil layered under the film. It is suitable to push the mixed resin with moderate pressure on the film, and it is suitable for long time use because urethane rubber is not easily worn when it is pushed with squeegee.
인용 발명에서와 같은 목재에 박은 못머리로 교란 연마하는 방법에 있어서는 못과 못의 간격이 일정하고 너무 넓으면 안되기 때문에 무늬가 항상 거의 동일한 것을 얻을 수밖에 없었지만 본 발명의 스퀴이지는 크기 즉 셀로판 필름에 횡으로 접하는 면적에 따라 스퀴이지가 작을 때는 가는 선들로 이루어진 진주 무늬를 형성하고 클 때에는 크고 대담하게 물결치는 것과 같은 유선형의 무늬를 형성할 수가 있다.In the method of perturbing and polishing with nail heads embedded in wood as in the cited invention, since the distance between the nails and nails should be constant and too wide, the pattern was always almost the same, but the squeegee of the present invention had a size, that is, a cellophane film. When the squeegee is small, it forms a pearl pattern of thin lines, and when it is large, it can form a streamlined pattern such as large and bold waves.
만약 기판위에 진주박 혼입 수지를 도포하고 인용 발명에서 공지된 것과 같이 필름을 덮지 않은 상태에서 나무에 박은 못머리로 도포층을 휘저어서 교란시키면 교란되고 있는 순간에는 못머리가 지나간 자국 부근의 진주박 입자들이 떠올라 진주 광택을 나타내지만 곧 진주박 혼입수지가 골고루 퍼져서 못자국이 없어지고 진주 광택이 사라지게 되고 진주박 혼입 수지가 겔화된 상태에서는 상기 기구인 나무에 박은 못머리를 사용하게 되면 진주박 혼입 수지가 뭉쳐서 몰려 다니게 되어 작업이 어렵게 된다. 그러나, 본 발명에서는 셀로판 필름으로 진주박 혼입 수지를 덮고 셀로판 필름위에서 스퀴이지로 셀로판 필름 아래에 도포되어 있는 진주박 혼입 수지를 일정한 방향으로 밀어주면 진주박 혼입 수지가 일정한 방향으로 유동되기 때문에 겔화된 수지가 뭉쳐서 몰려 다니는 일 없이 필름과 같은 평활한 면을 얻을 수가 있을며 또한 경화제와 수지의 불안전한 혼합 상태 및 작업 온도에 따른 적량의 경화제 보다 적은량을 섞으므로서 판상에서 시차를 두고 먼저 겔화된 수지가 스퀴이지 조작 때 셀로판 밑의 한쪽으로 몰린다 하더라도 스퀴이지로 계속 밀어주면 진주 입자를 더 많이 함유한 먼저 경화된 수지층과 더 적게 함유한 나중에 경화된 수지층이 평활한 셀로판 필름을 따라 마치 나무결과 같은 모양의 진주 무늬를 얻을 수 있고 스퀴이지로 밀어 주는 작업 때 직접 스퀴이지가 진주박 혼입 수지에 접하지 않고 셀로판 필름위에 밀착시켜 밀어 주는 작업이므로 유기 용제나 진주박 등의 해로운 물질로 인한 작업 환경상의 문제가 없게 된다.If you apply a pearlescent resin mixed resin onto a substrate and stir the coating layer with nail nails embedded in wood without covering the film as is known in the cited invention, the pearl foil in the vicinity of the marks where the nail hair has passed is disturbed. Particles float to give pearl luster, but soon pearl pearl mixing resin spreads evenly, and nail marks disappear and pearl luster disappears. The resin will stick together and make it difficult. However, in the present invention, if the pearl foil mixture resin is covered with a cellophane film and the pearl foil mixture resin applied under the cellophane film with a squeegee on the cellophane film is pushed in a certain direction, the pearlescent mixture resin flows in a constant direction and gelated. It is possible to obtain a smooth surface like a film without clumping the resin and also to gel the resin first with a time difference on the plate by mixing less than an appropriate amount of the curing agent according to the unstable mixing state of the curing agent and the resin and the working temperature. If the squeegee is driven to one side under the cellophane during the squeegee operation, it will continue to be pushed into the squeegee so that the first hardened resin layer containing more pearl particles and the later hardened resin layer along the smooth cellophane film appear as if A pearl pattern of the same shape can be obtained and push it with a squeegee Since the operations that directly squeezing not without contact with the foil pearls mixed into the resin when working slide adhered on the cellophane film is no problem in working environment due to the harmful substances such as organic solvent or pearl foil.
이상과 같은 방법으로 생산된 진주 무늬 장식판은 그대로 상품화할 수 있으며 이 장식판상에 공지의 스크린 인쇄에 의하여 적절한 무늬를 인쇄하여 진주 무늬 장식판을 제작할 수도 있다.The pearl-patterned decorative plate produced by the above method can be commercialized as it is, and by printing a suitable pattern on the decorative plate by known screen printing, it is also possible to produce a pearl-patterned decorative plate.
본 발명의 실시예를 상술하면 다음과 같다.An embodiment of the present invention will be described in detail as follows.
[실시예]EXAMPLE
(1) 600㎠의 칩보드를 기판으로 하고 그 위에 지당 화이트를 혼입한 불포화 폴리 에스테르 수지를 균일하게 도포하여 기판의 색소나 얼룩 등을 차폐시키고 수지 경화 후에 220번 사포로 연마한다.(1) A 600 cm2 chipboard is used as a substrate, and an unsaturated polyester resin mixed with white sugar is uniformly applied to shield pigments, stains, and the like from the substrate, and polished with sandpaper 220 after curing of the resin.
(2) 은백색 액상 진주박 5cc를 도료용 불포화 폴리 에스테르 수지 100cc에 혼합하여서된 진주박 혼입 수지를 상기 도포층 위에 부은 다음 셀로판 필름으로 덮고 로울러로 밀어서 진주박 혼입 수지내의 기포를 탈포 시키면서 진주박 혼입 수지가 전면에 골고루 퍼지게 한다.(2) Pearl foil mixed resin was mixed by pouring 5 cc of silver white liquid pearl foil into 100 cc of unsaturated polyester resin for coating, poured over the coating layer, covered with a cellophane film, and then pushed into a roller to deflate bubbles in the pearl mixed resin. Allow the resin to spread evenly over the front.
(3) 진주박 혼입 수지가 겔화하기 시작할 때 진주박 혼입 수지층에 밀착시킨 셀로판 필름을 일정한 방향으로 이동시켜 진주박 혼입 수지를 유동시켜서 진주박 혼입 수지에 나타난 연회색 빛 얼룩을 제거하며 겔화가 더욱 진행되어 셀로판 필름이 잘 움직이지 않게 되었을 때 셀로판 필름 위에 우레탄 고무 스퀴이지를 밀착시켜 일정한 방향으로 밀어 주어서 셀로판 필름 아래의 진주박 혼입 수지를 유동시키면 진주박 혼입 수지층의 진주박 입자가 그 유동 방향으로 일정하게 배열하면서 진주광택을 나타내게 되고 진주박 혼입수지의 경화 후 셀로판 필름을 벗기니까 진주 무늬 광택이 형성된 장식판을 완성하게 되었다.(3) When the pearl leaf mixture resin starts to gel, the cellophane film adhered to the pearl leaf mixture resin layer is moved in a certain direction to flow the pearl leaf mixture resin to remove the light gray light stain on the pearl leaf mixture resin, and the gelation is further performed. When the cellophane film does not move well, the urethane rubber squeegee is pressed against the cellophane film and pushed in a certain direction to flow the pearlescent resin mixed under the cellophane film. The pearlescent gloss was exhibited by constantly arranging and peeling off the cellophane film after curing of the pearl leaf mixed resin to complete a decorative plate on which pearlescent luster was formed.
Claims (1)