CN109555289A - One kind is imitative to inlay flower wood floors and preparation method thereof - Google Patents
One kind is imitative to inlay flower wood floors and preparation method thereof Download PDFInfo
- Publication number
- CN109555289A CN109555289A CN201910048054.8A CN201910048054A CN109555289A CN 109555289 A CN109555289 A CN 109555289A CN 201910048054 A CN201910048054 A CN 201910048054A CN 109555289 A CN109555289 A CN 109555289A
- Authority
- CN
- China
- Prior art keywords
- roller
- wooden substrate
- pattern
- screen
- wooden
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to ground pavement field of material technology, are related to a kind of imitate and inlay flower wood floors, including wooden substrate and are attached to the transparent surface protective layer with wear-resisting scratch-resisting wiping performance on wooden substrate, and 200~600 μm of thickness;It is provided with decoration figure layer between the wooden substrate and transparent surface protective layer, is that pattern lattice are printed on wooden substrate surface as carrier leaching using dyestuff through multiple silk-screen to form.The invention also discloses the imitative preparation methods for inlaying flower wood floors, including by pattern fragmentation, are divided into pattern lattice, and roller A, B, C etc. is made in correspondence;Then by prepared dye-coating in the surface of roller A, B, C etc., when wooden substrate translation passes sequentially through below corresponding roller, the pattern lattice silk-screen in roller is in wooden substrate surface;Finally in decoration figure layer top finishing laminated coating, being formed, there is wear-resisting scratch-resisting to wipe performance transparency sealer.Dyestuff leaching is printed on wood surface using silk-screen by the present invention, does not cover timber texture itself.
Description
Technical field
The invention belongs to ground pavement field of material technology, are related to timber floor, more particularly to a kind of imitative inlay spends wood floors
And preparation method thereof.
Background technique
As consumption demand upgrades, consumer is higher and higher to the appearance requirement of pavement.Common wood floor surface
Though there is the natural grain of wood, color tends to be unified, shows slightly dull.Parquet is different from texture using different wooden kind of the colors,
It is spliced into changeable pattern and moulding, to have different decorative effects.The mainstream parquet floor of existing market is divided into two classes:
One kind is to be spliced by several independent solid wood blocks or other materials, such as stone material, jade by equilateral and supplementary angle principle
Regular geometric shape constitutes solid wood parquets unit floor, such as CN201521135977.0;In addition a kind of, then by it is several several
Independent wood skin or other materials are spliced into decoration wood skin or paste substrate, constitute solid wood layer spellingization unit such as leather, plastics
Floor, such as CN200810212180.4.
Such parquet floor can make wood floor decoration effect get a promotion, but be easy to be limited by spliced materials, decoration effect
Fruit is not only limited, and pattern, the uncontrollability of color are larger, it is difficult to meet the needs of consumer personalization.
Currently there are effect floor is spent using the imitative edge of mode of printing production, since printing process uses UV oil
Ink, pigment form a thick layer in floor surface and decorate figure layer.Since figure layer is thicker, wood floors table has been covered substantially
The grain of wood in face affects the expressive force of solid wooden floor board itself, also difficult to meet the needs of consumer personalization.
Summary of the invention
In view of the above-mentioned deficiencies in the prior art, the object of the present invention is to provide one kind to have imitative edge floral pattern table
Face, and controllable the having of color pattern color change is imitated and inlays flower effect wood floors.
One kind is imitative to inlay flower effect wood floors, including wooden substrate and being attached on wooden substrate, there is wear-resisting scratch-resisting to wipe
The transparent surface protective layer of performance, 200~600 μm of thickness, preferably 400 μm;It is protected in the wooden substrate and transparent surface
It is provided with decoration figure layer between layer, is that pattern lattice are printed on wooden substrate surface as carrier leaching using dyestuff through multiple silk-screen to form.
In the more excellent disclosed example of the present invention, 8~18mm of the wooden substrate thickness, including but not limited to independent body solid wood baseplate,
Or it is bonded by wood substrate layer and wooden dash board, wherein the wood substrate layer includes but is not limited to particieboard, multilayer glue
Plywood, fiberboard, preferably multi-plywood, the wooden dash board are the plates of solid wood of 0.2~4mm of thickness, and preferred thickness is
The Oak veneer of 0.6mm or so.
In the more excellent disclosed example of the present invention, the transparent surface protective layer with a thickness of 5~50 μm of laminated coating by constituting, institute
Stating coating is electron beam (EBC) or the UV photocuring cross-linked polymer as the main component with acrylate functional resins, described third
Olefin(e) acid rouge functional resins cross-linked polymer has the solidification temperature higher than room temperature.
Further, the coating also includes abrasion resistant particles material, and the abrasion resistant particles are including but not limited to aluminium oxide pellet, carbon
SiClx pellet, content are about the 0.5%~10% of cross-linked polymeric amount of substance.
Further, the coating also may include azo dyes, and content is about the 0~3% of cross-linked polymeric amount of substance.
Further, the dyestuff is the aqueous complex dyestuff of different colours.
Further, it is possible to add colorant or pigment in the dyestuff, assign the decoration figure layer different decorations
Effect.For example, oxidation chlorination bismuth pearlescent pigment, daylight fluorescent pigment, phosphorescent pigment etc..
A further object of the invention is to disclose the above-mentioned imitative preparation method for inlaying flower effect wood floors, including such as
Lower step:
Step 1. is divided into pattern lattice A, B, C etc. according to the rule of color gradient in mapping software, by pattern fragmentation,
The pattern lattice of segmentation are produced on screen cloth, and with pattern lattice reference numeral, roller A, B, C etc. is made;
Step 2. by prepared dye-coating in the surface of roller A, B, C etc., when wooden substrate translation pass sequentially through it is corresponding
Roller below when, by the pattern lattice silk-screen in roller in wooden substrate surface;Through multiple silk-screen, by all pattern lattice silk-screens
It is dry into infrared baking oven after wooden substrate surface constitutes complete pattern;In the drying process, some dyes immerse wooden base
Plate surface forms the decoration figure layer;
Poly- 3. are walked in decoration figure layer top finishing laminated coating, being formed, there is wear-resisting scratch-resisting to wipe performance transparency sealer.
In the more excellent disclosed example of the present invention, each roller corresponds to a kind of dye formulation, pattern lattice and roller pair in step 1
It should number A, B, C etc.;The pattern lattice are made of in roller fine and closely woven mesh.
Further, the mesh material includes but is not limited to fabric, wire mesh.
In the more excellent disclosed example of the present invention, the dyestuff in step 2 according to formulation ratio is sufficiently stirred and filters before use, institute
Roller is stated to be made of screen cloths more than 250 mesh.
The mobility and silk-screen performance that dyestuff can be improved in this way, are able to maintain the dyestuff in silk-screen printing process adequately
Mobility and transfer performance;After guaranteeing the wooden substrate printing, wooden substrate picture on surface lattice sharpness of border, no wire drawing unrest line
Phenomenon.
In the more excellent disclosed example of the present invention, used between different rollers in step 2 in production line, at least one position conduct
True edge.
In the more excellent disclosed example of the present invention, in step 2 on mobile wooden substrate, by the difference on wooden substrate after silk-screen
The position of pattern lattice relative to each other is compared, and adjusts roller position along true edge in production process, to reduce pattern
Deviation between lattice.Be also based on the wooden substrate before silk-screen and measure, wooden substrate after silk-screen into
Row measurement, predicts the offset between different pattern lattice, adjusts roller position along the true edge.
Without the auxiliary device outside production line increment, alignment of the prevention between screen printing pattern lattice is corrected during production
Mistake or deviation.
In the more excellent disclosed example of the present invention, step 3, which applies, is decorated with the cross-linking agent polymerization as the main component of acrylate functional resins
Sealer is formed, it is dry using rubber roller coating, intaglio plate coating etc., then by electron beam (EBC) solidification or UV light.
Beneficial effect
The present invention is printed on wooden substrate surface by carrier leaching of complex dyestuff by way of silk-screen, by pattern, and is covered with
Bright sealer is formed with imitative inlay and spends effect wood floors.Dyestuff leaching is printed on wood surface, forms decoration layer, and not
Timber texture itself is covered, the expressive force of product is enhanced.
Detailed description of the invention
The layer structure schematic diagram of 1 product of Fig. 1 embodiment;
The layer structure schematic diagram of 2 product of Fig. 2 embodiment;
Fig. 3 is the pattern lattice schematic diagram after decorating figure layer pattern and decomposing;
Wherein, the title of each component is respectively as follows: 1, wooden substrate, 2, transparent surface protective layer, 3, decoration figure layer, 31, pattern,
32, pattern lattice A, 33, pattern lattice B, 34, pattern lattice C, 4, wooden dash board, 5, wood substrate layer.
Specific embodiment
The following describes the present invention in detail with reference to examples, so that those skilled in the art more fully understand this hair
It is bright, but the invention is not limited to following embodiments.
Embodiment 1
One kind is with imitative edge floral pattern surface, and controllable the having of color pattern color change is imitated and inlay flower effect wood floors, packet
It includes wooden substrate 1 and is attached to the transparent surface protective layer 2 with performances such as wear-resisting scratch-resisting wipings on wooden substrate.Wooden substrate 1
It is decoration figure layer 3 between transparent surface protective layer 2.Pattern lattice are printed on by carrier leaching of dyestuff by way of multiple silk-screen
Wooden substrate surface ultimately forms decoration figure layer 3.
The wooden substrate 1 is to be made of wood substrate layer 5 and wooden dash board 4.The wood substrate layer is multilayer gluing
Plate;The wooden dash board 4 is the Oak veneer with a thickness of 0.6mm.
The transparency sealer 2 is made of laminated coating, and coating is the acrylate of UV light solidifying coating composition
Functional resins cross-linked polymer, the acrylate functional resins cross-linked polymer, which has, is greater than normal temperature cure temperature.It is formed
Transparent surface protective layer 2 gives floor scratch resistance, abrasion performance, water resistance, stain resistance.
Further, transparent surface protective layer thickness is usually 200~600 μm, and preferably 300~600 μm.
Further, the coating includes wear-resisting pellet, and the abrasion resistant particles are aluminium oxide pellet, content about 5%.
Further, the coating includes azo dyes, and content is about 2%.
Further, the dyestuff is the aqueous complex dyestuff of the colors such as red, yellow, black, white.
The above-mentioned imitative preparation method for inlaying flower effect wood floors, includes the following steps:
Step 1. is in mapping software, by the processing of 31 fragmentation of pattern.According to the rule of color gradient, 3 pattern lattice are divided into,
Number pattern lattice A32, pattern lattice B33, pattern lattice C34 respectively, and successively the pattern lattice finished point are produced on screen cloth, it is made
Roller A, roller B, roller C.One roller corresponds to a kind of dye formulation, and roller A corresponds to the corresponding dye of dye formulation A, roller B
Material formula B, roller C correspond to dye formulation C, the pattern lattice are made of in roller fine and closely woven mesh.
Further, the mesh material is fabric, selects roller made of the screen cloth of 300 mesh.
Further, the dye formulation A, dye formulation B, dye formulation C press pattern lattice color, and use is red, yellow, black, white race
The aqueous complex dyestuff of color is deployed.
When 1 continuous translation of step 2. wooden substrate passes through production line, screen printing pattern lattice A32 is provided first and is mentioned thereafter
For pattern lattice B33 matched with pattern lattice A, pattern lattice C34 etc..Including will be by dye formulation A, dye formulation B, dye formulation C
It is respectively coated on corresponding roller A, roller B, on roller C, wooden substrate 1 continues through roller A, roller B, below roller C,
Corresponding pattern lattice A32, pattern lattice B33, pattern lattice C34 silk-screen on wooden substrate 1.By multiple silk-screen, will own
Pattern lattice silk-screen in 1 surface of wooden substrate, pass through infrared drying.In the drying process, some dyes immerse wooden substrate
Surface forms the decoration layer 3.
Further, in order to improve the mobility and silk-screen performance of the dyestuff, make the dyestuff can in silk-screen operation
Keep sufficient mobility and transfer performance.After guaranteeing the wooden substrate printing, the wooden substrate picture on surface lattice boundary
Clearly, no wire drawing unrest line phenomenon.It is filled before use according to the dyestuff of dye formulation A, dye formulation B, dye formulation C proportion
Divide stirring.
Further, in production line, there is a true edge between each roller.
Further, on mobile wooden substrate, by the difference pattern lattice on wooden substrate after silk-screen relative to that
This position is compared, and adjusts roller position along the true edge in production process, to reduce between the pattern lattice
Deviation.It is also based on the measurement carried out on the wooden substrate before silk-screen and wooden base after silk-screen
The offset between different pattern lattice is predicted in the measurement that plate carries out, and adjusts roller position along the true edge.Without in production line
Auxiliary device outside increment.For example in production, this corrects alignment errors or inclined of the prevention between the pattern lattice described in silk-screen for permission
Difference.
Poly- 3. coatings described in wooden substrate top finishing multilayer are walked, being formed on the wooden substrate surface has wear-resisting resist
The performance transparencies sealers such as scraping.
Embodiment 2
One kind is with imitative edge floral pattern surface, and controllable the having of color pattern color change is imitated and inlay flower effect wood floors, packet
It includes wooden substrate 1 and is attached to the transparent surface protective layer 2 with performances such as wear-resisting scratch-resisting wipings on wooden substrate.Wooden substrate 1
It is decoration figure layer 3 between transparent surface protective layer 2.Pattern lattice are printed on by carrier leaching of dyestuff by way of multiple silk-screen
Wooden substrate surface ultimately forms decoration figure layer 3.
The wooden substrate 1 is independent body solid wood solid wood baseplate, and material kind is toothed oak wood.
The transparent surface protective layer 2 is made of laminated coating, and coating is the acrylate official of EBC light solidifying coating composition
It can resin cross-linked polymer.The acrylate functional resins cross-linked polymer, which has, is greater than normal temperature cure temperature.
Further, sealer is with a thickness of 300~600 μm
Further, the coating includes wear-resisting pellet, and the abrasion resistant particles are silicon carbide pellet, and content can about 10%.
Further, the coating includes azo dyes, and content may be about 1.9%.
Further, the dyestuff is red, yellow, black, white race color aqueous complex dyestuff.
The above-mentioned imitative preparation method for inlaying flower effect wood floors, includes the following steps:
Step 1. is in mapping software, by the processing of 31 fragmentation of pattern.According to the rule of color gradient, 3 pattern lattice are divided into,
Number pattern lattice A32, pattern lattice B33, pattern lattice C34 respectively, and successively the pattern lattice of number point are produced on screen cloth, it is made
Roller A, roller B, roller C.One roller corresponds to a kind of dye formulation, i.e. it is corresponding that roller A corresponds to dye formulation A, roller B
Dye formulation B, roller C correspond to dye formulation C, pattern lattice are made of in the roller fine and closely woven mesh.
Further, the mesh material is fabric, selects roller made of the screen cloth of 350 mesh.
Further, the dye formulation A, dye formulation B, dye formulation C press pattern lattice color, and use is red, yellow, black, white race
The aqueous complex dyestuff of color is deployed.
Step 2. makes 1 continuous translation of wooden substrate by production line, provides screen printing pattern lattice A32 first and mentions thereafter
For pattern lattice B33 matched with pattern lattice A, pattern lattice C34 etc..Including will be by dye formulation A, dye formulation B, dye formulation C
It is respectively coated on corresponding roller A, roller B, on roller C, wooden substrate 1 continues through roller A, roller B, below roller C,
Corresponding pattern lattice A32, pattern lattice B33, pattern lattice C34 silk-screen on wooden substrate 1.By multiple silk-screen, will own
Pattern lattice silk-screen in 1 surface of wooden substrate, pass through infrared drying.In the drying process, some dyes immerse wooden substrate
Surface forms the decoration layer 3.
Further, in order to improve the mobility and silk-screen performance of the dyestuff, make the dyestuff can in silk-screen operation
Keep sufficient mobility and transfer performance.After guaranteeing the wooden substrate printing, the wooden substrate picture on surface lattice boundary
Clearly, no wire drawing unrest line phenomenon.It is filled before use according to the dyestuff of dye formulation A, dye formulation B, dye formulation C proportion
Divide stirring.
Further, in production line, there is a true edge between each roller.
Further, on mobile wooden substrate, by the difference pattern lattice on wooden substrate after silk-screen relative to that
This position is compared, and adjusts roller position along the true edge in production process, to reduce between the pattern lattice
Deviation.It is also based on the measurement carried out on the wooden substrate before silk-screen and wooden base after silk-screen
The offset between different pattern lattice is predicted in the measurement that plate carries out, and adjusts roller position along the true edge.Without in production line
Auxiliary device outside increment.The method allows for example producing this alignment mistake of correction prevention between the pattern lattice described in silk-screen
Mistake or deviation.
Poly- 3. coatings described in wooden substrate top finishing multilayer are walked, being formed on the wooden substrate surface has wear-resisting resist
The performance transparencies sealers such as scraping.
It should be noted that the pattern lattice used in description of the invention attached drawing, only illustrate that imitative inlay spends effect wooden
Floor surface pattern is not limited to shown in attached drawing by the preparation on floor.
The above description is only an embodiment of the present invention, is not intended to limit the scope of the invention, all to utilize this hair
Equivalent structure or equivalent flow shift made by bright specification is applied directly or indirectly in other relevant technical fields,
Similarly it is included within the scope of the present invention.
Claims (10)
1. one kind is imitative to inlay flower effect wood floors, including wooden substrate (1) and it is attached on wooden substrate with wear-resisting scratch-resisting
Wipe the transparent surface protective layer (2) of performance, it is characterised in that: 200~600 μm of thickness of the transparent surface protective layer (2), preferably
400μm;It is provided with decoration figure layer (3) between the wooden substrate (1) and transparent surface protective layer (2), is through multiple silk-screen
Pattern lattice are printed on wooden substrate surface as carrier leaching using dyestuff to form.
Flower effect wood floors are inlayed 2. imitating according to claim 1, it is characterised in that: wooden substrate (1) thickness 8~
18mm, including but not limited to independent body solid wood baseplate, or be bonded by wood substrate layer (5) and wooden dash board (4), wherein institute
Stating wood substrate layer (5) includes but is not limited to particieboard, multi-plywood, fiberboard, preferably multi-plywood, the wooden table
Plate (4) is the plates of solid wood of 0.2~4mm of thickness, and preferred thickness is the Oak veneer of 0.6mm or so.
3. according to claim 1 imitate inlay flower effect wood floors, it is characterised in that: the transparent surface protective layer (2) by
It is constituted with a thickness of 5~50 μm of laminated coatings, the coating is that electron beam C or UV photocuring are with acrylate functional resins
The cross-linked polymer of main ingredient, the acrylate functional resins cross-linked polymer have the solidification temperature higher than room temperature.
Flower effect wood floors are inlayed 4. imitating according to claim 3, it is characterised in that: the coating also includes abrasion resistant particles
Material, for the abrasion resistant particles including but not limited to aluminium oxide pellet, silicon carbide pellet, content is about the 0.5% of cross-linked polymeric amount of substance
~10%.
Flower effect wood floors are inlayed 5. imitating according to claim 3, it is characterised in that: the coating also may include azo dye
Material, content is about the 0~3% of cross-linked polymeric amount of substance;The dyestuff is the aqueous complex dyestuff of different colours.
6. preparing the method imitated as described in claim 1-5 is any and inlay flower effect wood floors, which is characterized in that including walking as follows
It is rapid:
Step 1. is divided into pattern lattice A, B, C etc. according to the rule of color gradient in mapping software, by pattern fragmentation,
The pattern lattice of segmentation are produced on screen cloth, and with pattern lattice reference numeral, roller A, B, C etc. is made;
Step 2. by prepared dye-coating in the surface of roller A, B, C etc., when wooden substrate translation pass sequentially through it is corresponding
Roller below when, by the pattern lattice silk-screen in roller in wooden substrate surface;Through multiple silk-screen, by all pattern lattice silk-screens
It is dry into infrared baking oven after wooden substrate surface constitutes complete pattern;In the drying process, some dyes immerse wooden base
Plate surface forms the decoration figure layer;
Poly- 3. are walked in decoration figure layer top finishing laminated coating, being formed, there is wear-resisting scratch-resisting to wipe performance transparency sealer.
7. imitating the preparation method for inlaying flower effect wood floors according to claim 6, it is characterised in that: each institute in step 1
It states roller and corresponds to a kind of dye formulation, pattern lattice and roller reference numeral A, B, C etc.;The pattern lattice are in roller by fine and closely woven
Mesh is constituted;The mesh material includes but is not limited to fabric, wire mesh.
8. imitating the preparation method for inlaying flower effect wood floors according to claim 6, it is characterised in that: according to matching in step 2
The dyestuff just matched is sufficiently stirred and filters before use, and the roller is made of screen cloths more than 250 mesh.
9. imitating the preparation method for inlaying flower effect wood floors according to claim 6, it is characterised in that: produced in step 2
Line is using between different rollers, at least one position is as true edge.
10. imitating the preparation method for inlaying flower effect wood floors according to claim 6, it is characterised in that: step 3 painting is decorated with third
Olefin(e) acid rouge functional resins cross-linking agent as the main component polymerize to form sealer, using rubber roller coating, intaglio plate coating etc., then
Solidified by electron beam C or UV light is dry.