KR890013809A - 초전도 세라믹의 제조방법 및 그 생성물 - Google Patents
초전도 세라믹의 제조방법 및 그 생성물 Download PDFInfo
- Publication number
- KR890013809A KR890013809A KR1019880011677A KR880011677A KR890013809A KR 890013809 A KR890013809 A KR 890013809A KR 1019880011677 A KR1019880011677 A KR 1019880011677A KR 880011677 A KR880011677 A KR 880011677A KR 890013809 A KR890013809 A KR 890013809A
- Authority
- KR
- South Korea
- Prior art keywords
- metal
- precipitate
- carbonate
- quaternary ammonium
- hydroxide
- Prior art date
Abstract
내용 없음.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (23)
- L.M.A.O. 금속산화물의 초전도 조성물에 있어서, 상기 조성물은 이물질(extraneous materials)이 없도록 구성함을 특징으로한 상기 조성물, 상기 L은 적어도 하나의 3가금속, 상기 M은 적어도 하나의 2가금속, 상기 A는 적어도 하나의 다가금속이고, 상기 L.M.A는 초전도체에서 소정의 원자비로 구성되어 있음.
- 제1항에 있어서, 상기 L은 Y, 상기 M은 Ba, 상기 A는 Cu로서, 각각 1:2:3의 원자비로 구성함을 특징으로하는 상기 조성물.
- 제1항에 있어서, 상기 L은 스칸듐과 이트륨을 포함하여 희토류족중에서 적어도 하나의 금속이고 ; 상기 M은 Ba, Be, Mg, Ca 및 Sr그룹중 적어도 하나의 금속이고 ; 상기 A는 Cu, Ag 및 Au그룹중 적어도 하나의 금속이며 ; 0는 산소인 상기 조성물.
- 제3항에 있어서, (a) 상기의 소정의 원자비로 성분 L, M, 및 A를 가진 L, M, 및 A의 용해염 용액을 제조하고 ; (b) 제4급암모늄 카보네이트 용액을 제조하며 ; 물푸울(water pool)에 상기 L.M.A. 용해염용액과 제4급암모늄 카보네이트를 넣고 동시에 교반하면서 혼합시켜 화학양론적인 공침전물(co-precipitate)을 생성하고 ; (d) 상기 공침전물을 회수하여 ; (e) 상기 공침전물을 소성시키는 공정으로 구성하는 방법에 의해 얻어진 생성물임을 특징으로 하는 상기 조성물.
- 제4항에 있어서, 상기 소성은 건조된 공침전물을 약 850-1050℃의 온도로 가열하여 ; 그 온도를 약 4-8시간동안 유지하고 ; 약 5-12시간에 걸쳐서 약 실온 내지 250℃의 범위의 온도에서 선냉각(linearly cooling)시켜 얻어짐을 특징으로한 상기 조성물.
- L.M.A 카보네이트와 제4급 암모늄염을 균질분산시켜 구성함을 특징으로 하는 수용성 슬러리(Aqueous slurry). 상기 L은 적어도 하나의 3가금속, 상기 M은 적어도 하나의 2가금속, 상기 A는 적어도 하나의 다가금속임.,
- 제6항에 있어서, 상기 L은 스칸듐 및 이트륨을 포함하여 희토류족중 적어도 하나의 금속이고 ; 상기 M은 Ba, Be, Mg, Ca, 및 Sr그룹중 적어도 하나의 금속이며 ; 상기 A는 Cu, Ag 및 Au그룹중 적어도 하나의 금속임을 특징으로한 상기 수용성 슬러리.
- 제6항에 있어서, 상기 L.M.A.는 Y, Ba, Cu로서 원자비 1:2:3을 구성함을 특징으로한 상기 수용성 슬러리.
- 제8항에 있어서, ⅰ) 상기 L.M.A.의 카보네이트 약 0.5-75wt％ ; ⅱ) 제4급 암모늄 카티온 약 0.1-75wt％ ; ⅲ) 상기 L.M.A.카보네이트와 화학량론적으로 당량인 출발 L.M.A.염의 잔류아니온(anions) ; ⅳ) 나머지 물로 구성함을 특징으로한 상기 수용성 슬러리.
- 초전도 L.M.A.O.금속산화물로 하소시켜 변형하는데 적합한 유기물이 없는 조성물에 있어서, 상기 조성물은 (a) 소정의 원자비의 성분 L, M, A를 가진 L, M, A용해염 용액을 제조하고 ; (b) 제4급암모늄 카보네이트용액을 제조하여 ; (c) 상기 L, M, A용해염용액과 제4급암모늄 카보네이트용액을 물푸올(water pool)에서 동시에 교반하면서 혼합시켜 화학양론적인 공침전물을 생성하며 ; (d) 상기 공침전물을 회수하고 ; (e) 분해 또는 휘발시키기에 충분한 온도로 상기 건조된 공침전물을 가열시켜 제4급 암모늄과 니트레이트를 잔류시키고 상기 공침전물의 카보네이트를 산화물로 부분전환시킴을 특징으로 하는 공정으로 얻어진 생성물임을 특징으로 한 상기 조성물. 상기 L은 적어도 하나의 3가금속, 상기 M은 적어도 하나의 2가금속, A는 적어도 하나의 다가금속이다. 상기 L, M, A는 주어진 원자비로 구성되어 있음.
- 제10항에 있어서, 상기 L은 스칸듐 및 이트륨을 포함하여, 희토류족중 적어도 하나의 금속이고 ; 상기 M은 Ba, Be, Mg, Ca 및 Sr그룹중 적어도 하나의 금속이며 ; 상기 A는 Cu, Ag 및 Au그룹중 적어도 하나의 금속이고 ; O는 산소이며 ; 상기 L, M, A의 용해염은 니트레이트임을 특징으로 하는 상기 유기물이 없는 조성물.
- 수용성매체중에서 제4급암모늄 카보네이트의 카보네이트이온과 L, M, A, 금속이온을 반응시켜 각각의 금속카보네이트침전물을 구성하는 슬러리를 생성하고 그 침전물을 회수, 건조시켜 구성함을 특징으로 하는 처리방법. 상기 L은 적어도 하나의 3가금속, 상기 M은 적어도 하나의 2가금속 상기 A는 적어도 하나의 다가금속이며 L, M, A는 초전도체에 있어서 소정의 원자비로 구성되어 있음.
- 제12항에 있어서, 상기 침전물을 건조시킨 다음의 침전물을 분해 또는 휘발시키기에 충분한 온도로 가열시켜 제4급암모늄과 니트레이트를 잔류시키고 상기 공침전물의 카보네이트를 산화물로 부분전환시킴을 특징으로 하는 상기 방법.
- 제13항에 있어서, 상기 L은 스칸듐 및 이트륨을 포함하여, 희토류족중 적어도 하나의 금속이고 ; 상기 M은 Ba, Be, Mg, Ca 및 Sr 그룹중 적어도 하나의 금속이며 ; 상기 A는 Cu, ag 및 Au그룹중 적어도 하나의 금속이고 ; O는 산소인 상기 방법.
- 제12항에 있어서, 상기 L은 스칸듐 및 이트륨을 포함하여, 희토류족중 적어도 하나의 금속이고 ; 상기 M은 Ba, Be, Mg, Ca 및 Sr그룹중 적어도 하나의 금속이며 ; 상기 A는 Cu, ag 및 Au그룹중 적어도 하나의 금속인 상기 방법.
- 제15항에 있어서, 상기 침전물의 전조다음의 침전물을 약 850-1050℃의 초기온도로 하소하며 ; 약 4-8시간동안 그 온도는 유지하고 ; 약 실온 내지 250℃의 범위의 온도에서 약 5-12시간에 걸쳐서 선냉각시킴으로써, 초전도재를 생성시킴을 특징으로한 상기 방법.
- 제15항에 있어서, PH 8.3의 수용성 테트라에틸암모늄 히드록시드용액을 통하여 카본디옥시드를 통과시켜 테트라에틸암모늄카보네이트와 용해카본디옥시드를 생성하여 ; 상기 테트라에틸암모늄 카보네이트를 Y : Ba : Cu의 원자비 1:2:3으로 구성하는 이트륨, 바륨 및 동의 니트레이트수용액에 PH 7.7-8.0에서 첨가시켜 카보네이트로서 상기 Y, Ba, 및 Cu를 침전시키며 ; 상기 침전물을 회수 및 건조하고 ; 상기 건조침전물을 약 950℃에서 하소시켜 그하소생성물을 약 150℃에서 8시간에 걸쳐 냉각시킴을 특징으로 하는 상기 방법.
- 제15항에 있어서, 상기 반응매체의 PH는 공침전시에 약 7.5-12로 유지시킴을 특징으로한 상기 방법.
- 제15항에 있어서, 상기 반응매체의 PH는 공침전시에 약 7.7-8.0으로 유지시킴을 특징으로한 상기 상법.
- 제15항에 있어서, 상기 금속이온은 금속니트레이트로부터 유도시킴을 특징으로한 상기 방법.
- 제15항에 있어서, 상기 제4급 암모늄 카보네이트가 화학양론적으로 생성되고 CO2가 과잉으로 용해될때까지 제4급 암모늄 히드록시드수용액을 통하여 CO2의 기포를 발생시켜 제4급 암모늄 카보네이트를 제조하는 방법에서, 상기 제4급암모늄 히드록시드는 다음식을 가짐을 특징으로 하는 상기 방법.위식에서 R, R′, R″, R″′는 같거나 다른 다음그룹의 멤버이다. ⅰ) 알킬, 즉, 테트라메틸암모늄히드록시드, 테트라에틸암모늄히드록시드, 테트라프로필암모늄히드록시드, 디메틸디에틸암모늄 히드록시드, 시클로 프로필트리메틸암모늄 히드록시드등 ; ⅱ) 방향족, 즉, 페닐트리메틸암모늄히드록시드, 페닐에틸 디메틸암모늄히드록시드, 벤질트리메틸암모늄 히드록시드등 ; ⅲ) 헤테로시클, ⅳ) 두링(ring)멤버가 하나의 링에 결합함으로써 N은 하나의 링멤버, 즉 디메틸피롤리디늄히드록시드, 디메틸피리디늄 히드록시등으로됨.
- 제15항에 있어서, 상기 L.M.A.는 Y, Ba2Cu3이고, 상기 제4급암모늄카보네이트는 테트라메틸암모늄카보네이트 또는 테트라에틸암모늄카보네이트임을 특징으로한 상기 방법.
- 제22항에 있어서, 상기 침전물의 건조다음의 침전물은 약 850-1050℃의 초기온도로 하소시켜 약 4-8시간동안 그 온도로 유지시키고 약 실온 내지 250℃범위의 온도로 약 5-12시간에 걸쳐서 선냉각(linear cooling)시킴으로써 생성함을 특징으로 하는 상기 방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.