KR890005127B1 - 구리기본합금 - Google Patents

구리기본합금 Download PDF

Info

Publication number
KR890005127B1
KR890005127B1 KR8201777A KR820001777A KR890005127B1 KR 890005127 B1 KR890005127 B1 KR 890005127B1 KR 8201777 A KR8201777 A KR 8201777A KR 820001777 A KR820001777 A KR 820001777A KR 890005127 B1 KR890005127 B1 KR 890005127B1
Authority
KR
South Korea
Prior art keywords
nickel
copper
coins
discoloration
gold
Prior art date
Application number
KR8201777A
Other languages
English (en)
Other versions
KR830010216A (ko
Inventor
브루노 프린츠 독크톨
만프레드 베록켈 독크톨
귄터 루돌프 독크톨
울리히 히프너 독크톨
쬐베 후우고
Original Assignee
에드가 린데르만, 울리히 예켈
파우데엠 니킬-테크놀로지 아크치엔게젤샤후트
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=6130663&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=KR890005127(B1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by 에드가 린데르만, 울리히 예켈, 파우데엠 니킬-테크놀로지 아크치엔게젤샤후트 filed Critical 에드가 린데르만, 울리히 예켈
Publication of KR830010216A publication Critical patent/KR830010216A/ko
Application granted granted Critical
Publication of KR890005127B1 publication Critical patent/KR890005127B1/ko

Abstract

내용 없음.

Description

구리기본합금
제1도는 DIN 6164에 따른 색 삼각관계의 일부를 나타낸 것임.
본 발명은 변색에 대한 높은 저항성과 금색을 가져야 하는 동전 또는 그와 유사한 것들을 제조하는데 사용하기 위한 물질로서, 4-6%의 니켈, 4-6%의 알루미늄, 제조시 불가피하게 존재하는 불순물과 잔분의 구리로 구성된 구리기본합금에 관한 것이다.
최근 수년동안 전세계적으로 파급되고 있고 여러국가의 국력면에서 다른 인플레이션 경향, 및 자동판매기의 급증으로인해 가치가 높은 동전을 필요로 하게되었다. 예를들어, 독일에서는 한동안 10 마르크짜리 동전의 도입을 고려해 보았었다. 현존하는 대부분의 화폐 제도상, 무게와 부피가 크면 다루기가 어려울 뿐만 아니라 상당량의 금속을 필요로하기 때문에, 가장 가치가 큰 현존 동전과의 구별을 위해 더큰 동전을 제공하는것을 실용화 될수 없을 것이다. 게다가, 동전으로 사용될 수 있는 금속 값이 상승함으로써 동전의 액면가와 금속 값사이의 차이가 감소될 것이다. 이러한 이유 때문에, 관계 당국에서는, 가치가 더 높고, 가장 가치가 큰 현존 동전과 색이 다르고 그것보다 더 작은 새로운 동전을 발행할 것을 고려하고 있다 금색은 가치가 높은 것으로 인정되며 통상 사용되고 있는 대부분의 동전(가치가 큰것)이 은색이기 때문에, 금색은 상기 목적에 특히 바람직하다.
금색을 갖는 동전 물질은 잘 알려져 있으며, 그들 일부는 이미 사용되고 있다. 그들은, 거의 예외없이, 25%의 아연, 또는 20% 아연 및 1% 니켈, 또는 5-6%의 알루미늄 및 2% 니켈, 또는 2% 알루미늄 및 6%니켈을 함유하는 구리 기본 합금으로 구성되어 있다. 그러나, 이들 모든 물질은 사용시 비교적 빨리 본래의 밝은 색을 잃고 갈색을 띠는 단점을 갖고 있다. 이러한 단점은 가치가 적은 동전에서는 허용되는 것이지만 매우 가치가 높은 동전이 사용 즉시 퇴색되는 것을 허용할 수 없는 것이다. 이러한 이유 때문에, 은색물질(특히, 니켈 또는 니켈 함량이 많은 합금)이 가치가 높은 동전에 쓰여져 왔다.
동전 또는 그와 유사한 것들을 만들기 위해 사용될 수 있고 주조, 아연 및 스탬핑(stamping)공정에 의해 가공될 수 있으며, 변색에 대한 저항성이 커서 본래의 금색을 가능한한 오래동안 유지할 수 있는 금색의 물질을 제공하는 것이 바람직하다.
상기한 목적은, 동전을 제조하는데 사용되는 물질이 4-6%의 니켈, 4-6의 알루미늄, 잔분 구리와 제조시 불가피하게 존재하는 불순물을 함유하는 구리기본 합금일 경우 달성될수 있다는 것을 의외로 알아냈다. 바람직하게 구리합금이 0.5-1.8%의 철 및/또는 0.3-1.5%의 망간도 함유한다. 또한, 구리 합금은 변색에 저항성을 증진시키기 위해서 0.5-0.30%의 규소를 함유할 수 있다.
또한 구리기본합금은 다른 금속(양호하기로는 니켈)의 핵심층을 갖는 동전들을 제조하기위한 피복물질로서 사용될 수 있다.
변색에 대한 실험을 하기위해, 스템프되거나 스템프되지 않은 형태로 5%의 니켈, 5%의 알루미륨, 1,2%의 철과 0.8%의 망간을 함유하는 구리 기본합금으로부터 제조되어 스탬프된 블랭크(blank)동전을 다음과 같이 예비처리하였다 : 색을 선명하게 하는(bright)산세척, 수세, 광택제로 처리, 예비세척하지 않고 라이스 그릿(rice grit)에서 건조, 윤활제를 첨가하지 않은채 임의로 스탬핑.
상기 예비처리는, 실제로 사용되는 상태에서 스탬프되거나 스탬프되지 않는 동전 블랭크에 대한 변색저항을 실험하기 위해 필요하다. 변색 실험전에 모든 지문을 제거하기 위해 동전 블랭크에서 그리스(grease)를 제거하였다.
다음의 서로 다른 조건에서 실험을 실시하였다 :
A : 부식 시험용 실험실에서 실온에 노출.동전을 손가락과 접촉시켜 매일 뒤집음.
B : 부식 시험용 실험실에서 실온에 노출.
C : 10% NaCl 용액위에서 실온에서 노출.
D : 80% 상대습도와 실온에 노출.
E : 부식시험용 실험실에서 45-50℃에 노출.
F : 100% 상대습도와 실온에 노출.
20일 동안 실험한 후, 샘플을 채취하고, 주어진 조건하에서 실험된 동전을 육안으로 검사하여 선결된 시스템에 따라 1에서 부터 5까지 등급을 매겼다. 등급 1은 변색 저항이 매우 높은 것을 뜻하고, 등급 5는 변색 저항이 매우 낮아 표면이 심하게 변색된 것을 뜻한다.
전술했던 공지의 구리 기본 합금 (샘플 1-4)으로 부터 제조된 동전을 유사하게 예비 처리한후 실험 하였다.
그 결과를 표 1에 나타냈다.
[표 1]
Figure kpo00001
샘플 1-4의 등급은 총 19 내지 24이었다.
본 발명에 따라 사용될 구리기본 합금으로 제조된 샘플5에 대한 총 등급 15는 훨씬 낮은 것이다. 이것은, 상기 합금이, 변색저항에 관한한, 동전물질로서 종래 사용된 모든 구리 기본 합금보다 분명히 우수하다는 것을 나타내는 것이다.
금색은, 스펙트럼 반사 측정에 의해 DIN 6164에 따른 색표(色表)의 좌표와 DIN 5033에 따른 색도(色度) 좌표를 결정하므로써 확인 되었다. DIN 6164에 따른 색표의 색도 좌표 T : S : D의 형태로 실험된 구리합금에 대한 색상 T, 채도 S와 어둠값 D를 표 2에 나타냈다 :
[표 2]
Figure kpo00002
첨부한 도면 제1도에서, DIN에 따른 금색(△), 상기 구리기본 동전 합금의 금색(샘플 1-4=X)과 본 발명에 따른 합금의 금색(●)을 기입하였다.
합금 CuNi5Al5Fe 1.2Mn 0.8은 DIN 금색 채도와 조금만 다를 뿐이고 색상은 황금색과 녹황색의 금색 사이에 있기 때문에 합금 CuNi6AI2보다 채도가 우수한 것이 명백하다.
4-6%의 니켈과 4-6%의 알루미늄을 함유하는 본 발명에 따른 구리 합금은 니켈의 핵심을 갖는 적충된 동전 블랭크를 제조하는데 매우 적당하다. 이러한 물질은 자동판매기의 남용을 방지하는 블랭크를 천공하는데 이용될 수 있는 고철은 쉽게 재 사용될 수 있다.

Claims (2)

  1. 변색에 대한 높은 저항성을 가져야 하는 금색의 동전등을 제조하는데 사용되는 물질로서, 4-6%의 니켈, 4-6%의 알루미늄, 0.5-1.8%의 철 및 0.3-1.5% 망간, 잔분의 구리와 제조시 불가피하게 존재하는 불순물을 함유하는 구리기본합금.
  2. 변색에 대한 높은 저항성을 가져야 하는 금색의 동전등을 제조하는데 사용되는 물질로서, 4-6%의 니켈, 4-6%의 알루미늄, 0.5-1.8%의 철, 0.3-1.5%의 망간, 0.05-0.30%의 규소 및 잔분의 구리와 제조시 불가피하게 존재하는 불순물을 함유하는 구리기본합금.
KR8201777A 1981-04-23 1982-04-22 구리기본합금 KR890005127B1 (ko)