KR880003028A - 알루미늄의 내식성 피복 조성물 - Google Patents
알루미늄의 내식성 피복 조성물 Download PDFInfo
- Publication number
- KR880003028A KR880003028A KR870009495A KR870009495A KR880003028A KR 880003028 A KR880003028 A KR 880003028A KR 870009495 A KR870009495 A KR 870009495A KR 870009495 A KR870009495 A KR 870009495A KR 880003028 A KR880003028 A KR 880003028A
- Authority
- KR
- South Korea
- Prior art keywords
- alkali metal
- permanganate
- aluminum
- borax
- weight
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (25)
- 알루미늄 및 알루미늄 합금용 알칼리 금속 과망간산염 피복 조성물에 있어서, 염기성 PH를 구비하고 : 필수 성분으로써, 알칼리 금속 과망간산염과, 그리고, 알칼리 금속 염화물, 알칼리 금속 사중붕산염, 알칼리 금속 메타붕산염, 벤조산, 알칼리 금속 벤조산염, 알칼리 금속 탄산염, 알칼리 금속 사중 및 메타붕산염의 혼합물로부터 선택된 적어도 하나의 화합물과, 그리고, 필요하다면, 규산나트륨, 인산 칼륨, 알칼리 금속 질산염, 또는 그들의 혼합물을 갖고 있는 것을 특징으로 하는 알루미늄 및 아루미늄 합금용 알칼리 금속 과망간산염 피복 조성물.
- 제1항에 있어서, 과망간산염은 과망간산 칼륨이고, 필수 성분 중의 하나는 염화 나트륨 또는 염화 리튬인 것을 특징으로 하는 알루미늄 및 알루미늄 합금용 알칼리 금속 과망간산염 피복 조성물.
- 제1항 또는 제2항에 있어서, 필수 성분중의 하나는 알카리 금속 사중붕산염, 알칼리 금속 메타붕산염, 벤조산, 알칼리 금속 벤조산염, 알칼리 금속 탄산염, 알칼리 금속 사중 및 메타붕산염의 혼합물로부터 선택된 화합물인 것을 특징으로 하는 알루미늄 및 알루미늄 합금용 알칼리 금속 과망간산염 피복 조성물.
- 제3항에 있어서, 필수 성분중의 하나는 사중붕산 나트륨, 메타붕산나트륨 및 그들의 혼합물로부터 선택된 것을 특징으로 하는 알루미늄 및 알루미늄 합금용 알칼리 금속 과망간산염 피복 조성물.
- 제3항에 있어서, 알칼리 금속 인산염을 포함하고 있는 것을 특징으로 하는 알루미늄 합금용 알칼리 금속 과망간산염 피복 조성물.
- 제3항에 있어서, 7내지 12.5의 범위에서 pH를 갖고 있는 수용성 과망간산염 용액인 것을 특징으로 하는 알루미늄 및 알루미늄 합금용 알칼리 금속 과망간산염 피복 조성물.
- 제6항에 있어서, pH는 9 내지 10의 범위에 있는 것을 특징으로 하는 알루미늄 및 알루미늄 합금용 알칼리 금속과망간산염 피복 조성물.
- 제1항에 있어서, 필수 성분으로써, 과망간산 칼륨, 사중붕산 나트륨, 그리고 염화 나트륨 또는 염화 리튬을 함유하고 있는 것을 특징으로 하는 알루미늄 및 알루미늄 합금용 알칼리 금속 과망간산염 피복 조성물.
- 제5항에 있어서, 필수 성분으로써 과망간산 칼륨, 염화 나트륨 또는 염화 리튬, 알칼리 금속 인산염을 함유하고 있는 것을 특징으로 하는 알루미늄 합금용 알칼리 금속 과망간산염 피복 조성물.
- 제1항에 있어서, 필수 성분으로써, 과망간산 칼륨, 염화 나트륨 또는 염화 리튬을 함유하고 있는 것을 특징으로 하는 알루미늄 및 알루미늄 합금용 알칼리 금속 과망간산염 피복 조성물.
- 제1항에 있어서, (a) 붕산-5H2O 중량으로 0.05% 내지 9% 및 KMnO4중량으로 0.2% 내지 6.3% (b) 알칼리 금속 벤조산염 중량으로 0.5% 내지 44% 및 KMnO4중량으로 0.2%내지 6.3% (c) 탄산 나트륨 중량으로 0.05% 내지 31.5% 및 KMnO4중량으로 0.2% 내지 6.3% (d) NaCl 또는 LiCl 중량으로 0.5 내지 10% 및 KMnO4중량으로 0.2% 내지 6.3% (e) 붕사-5H2O 중량으로 0.05% 내지 9%, KMnO4중량으로 0.2% 내지 6.3% 및 NaCl 또는 LiCl 중량으로 0.05% 내지 10% (f) 알칼리 금속 벤조산염 0.05% 내지 44%, KMnO4중량으로 0.2% 중량으로 6.3% 및 중량으로 0.05% 내지 10% (g) 탄산 나트륨 중량으로 0.5% 내지 31.5%, KMnO4중량으로 0.2% 내지 6.3% 및 또는 LiCl 중량으로 0.5% 내지 10% 필수 성분으로써, 상기(a) 내지 (g)중의 하나를 함유하고 있는 것을 특징으로 하는 알루미늄 및 알루미늄 합금용 알칼리 금속 과망간산염 피복 조성물.
- 제1항에 있어서, 모든 백분비(%)는 중량 백분비이고, (a) 붕사-5H2O 0.1%, KMnO40.2% NaCl 0.1% : (b) 붕사-5H2O 0.5%, KMnO41.0% NaCl 0.5% : (c) KMnO44.0% NaCl 0.1% : (d) KMnO40.2% NaCl 5.0% : (e) KMnO41.0% NaCl 3.0%, K2(HPO4) 0.5% : (f) 붕사-5H2O 1.0%, KMnO40.2% : (g) 붕사-5H2O 0.05%, KMnO43.0% : (h) 붕사-5H2O 9.0%, KMnO44.0% : (i) 붕사-5H2O 1.0%, KMnO41.0% : (j) 벤조산 나트륨 1.0%, KMnO41.0% : (k) Na2CO31.0%, KMnO41.0% (l) 붕사-5H2O 3.0%, KMnO43.0% : 필수 성분으로써 상기(a) 내지(l)을 함유하고 있는 조성물로 구성되어 있는 그룹으로부터 선택된 것을 특징으로 하는 알루미늄 및 알루미늄 합금용 알칼리 금속 과망간산염 피복 조성물.
- 보호 피복으로 알루미늄 및 알루미늄 합금을 보호하는 방법에 있어서, 필수 성분으로써, 알칼리 금속 과망간산염과, 그리고 알칼리 금속 염화물, 알칼리 금속 사중붕산염, 알칼리 금속 메타붕산염, 알칼리 금속 탄산염, 벤조산, 알칼리 금속 벤조산염, 알칼리 그속 메타 및 사중붕산염의 혼합물로부터 선택된 화합물을 구비하고, 7 내지 12.5 이하의 범위에서 pH를 갖고 염기수용성 용액을 세척된 알루미늄과 접촉시키고 : 그 알루미늄 상에 전환 피복을 형성하고 : 그 알루미늄으로부터 어떤 과도한 피복 용액을 제거하는 것을 구비하고 있는 것을 특징으로 하는 보호 피복으로 알루미늄 합금을 보호 하는 방법.
- 제13항에 있어서, 알루미늄 및 알루미늄 합금은 수산화 나트륨, 불화수소산, 붕사, 황산, 질산, 알칼리 질산염과, 그리고, 유기산, 알코올, 알킬페놀 또는 아민의 폴리옥시에틸렌 또는 폴리옥시프로필렌 유도체로부터 선택된 비이온 비간섭 활성제로 세척되는 것을 특징으로 하는 보호 피복으로 알루미늄 및 알루미늄 합금을 보호하는 방법.
- 제14항에 있어서, 과망간산염 용액의 pH는 9 내지 10의 범위에 있는 것을 특징으로 하는 보호 피복으로 알루미늄 및 알루미늄 합금을 보호하는 방법.
- 제14항 또는 제15항에 있어서, 과망간산염 용액은 알칼리 금속 인산염도 또한 함유하고 있는 것을 특징으로 하는 보호 피복으로 알루미늄 및 알루미늄 합금을 보호하는 방법.
- 제14항에 있어서, 모든 백분율(%)은 중량 배분율이고, (a) 알칼리 금속 과망간산염 0.2% 내지 6.3%, 알칼리 금속 염화물 0.05% 내지 10.0%, 그리고 잔부는 물 : (b) 알칼리 금속 과망간산염 0.2% 내지 6.3%, 알칼리 금속 붕산염 및 그들의 수화물 0.05%내지 9%, 알칼리 금속 염화물 0.05% 내지 10.0%, 그리고 잔부는 물 : (c) 알칼리 금속 과망간산염 0.2% 내지 6.3%, 알칼리 금속 붕산염 및 그들의 수화물 0.05%내지 9%, 알칼리 금속 인산염 0.1% 내지 1%, 그리고 잔부는 물 : (d) 알칼리 금속 과망간산염 0.2% 내지 6.3%, 알칼리 금속 붕산염 및 그들의 수화물, 0.05%내지 9%, 그리고 잔부는 물 : (e) 알칼리 금속 과망간산염 0.2% 내지 6.3%, 알칼리 금속 벤조산염 0.05% 내지 44%, 그리고 잔부는 물 : (f) 알칼리 금속 과망간산염 0.2% 내지 6.3%, 알칼리 금속 벤조산염 0.05% 내지 44%, 그리고 잔부는 물 : (g) 알칼리 금속 과망간산염 0.2% 내지 6.3%, 알칼리 금속 탄산염 0.05% 내지 31.5%, 그리고 잔부는 물 : (h) 알칼리 금속 과망간산염 0.2% 내지 6.3%, 알칼리 금속 탄산염 0.05% 내지 31.5%, 그리고 잔부는 물 : (i) 알칼리 금속 과망간산염 0.2% 내지 6.3%, 알칼리 금속 염화물 0.05% 내지 10% 알칼리 금속 탄산염 0.05 내지 31.5%, 그리고 잔부는 물 : (j) 붕사-5H2O 1.0%, KMnO43.0%, 물 96.05% : (k) 붕사-5H2O 5.0, KMnO43.0%, 물 96.05% : (l) 붕사-5H2O 9.0%, KMnO44.0%, 물 87.0% : (m) 붕사-5H2O 1.0%, KMnO41.0%, 물 98.0% : (n) 벤조산 나트륨 1.0%, KMnO41.0%, 물 98.0% : (o) Na2CO31.0%, KMnO41.0%, 물 98.0% : (p) 붕사-5H2O 1.0%, KMnO43.0%, 물 96.0% : 과망간산염 용액은 상기 (a) 내지 (p)로부터 선택되는 것을 특징으로 하는 보호 피복으로 알루미늄 및 알루미늄 합금을 보호하는 방법.
- 제1항에 있어서, 필수 성분으로써, 알칼리 금속 과망간산염, 알칼리 금속 규산염과, 그리고, 알칼리 금속 염화물, 알칼리 금속 사중붕산염, 알칼리 금속 메타붕산염, 벤조산, 알칼리 금속 벤조산염, 알칼리 금속 사중 및 메타붕산염의 혼합물로 부터 선택된 화합물을 갖고 있는 것을 특징으로 하는 알루미늄 및 알루미늄 합금용 알칼리 금속 과망간산염 피복 조성물
- 제18항에 있어서, 수용성 과망간산염 용액은 12 내지 14의 범위에서 pH를 갖고 있고, 모든 백분율은 중량 백분율이고, 풀수 성분으로써, KMnO40.2% 내지 6.3%, NaCl 또는 LiCl 0.05% 내지 10%, 수화 규산나트륨 0.1% 내지 35%, NaNO3또는 LiNO30 내지 10%, pH가 11를 초과할 때 부분적으로 또는 전체적으로 메타붕산염으로 전환되는 붕사 0.1 내지 35%를 함유하고 있는 것을 특징으로 하는 알루미늄 및 알루미늄 합금용 과망간산염 피복 조성물.
- 제19항에 있어서, (a) KMnO40.2%, 수화 NaSiO30.1%, 붕사 0.1%, NaCl 0.1% : (b) KMnO43.0%, 수화 NaSiO31.5%, 붕사 0.1%, NaCl 1.0%, LiCl 1.0% : (d) KMnO43.0%, 수화 NaSiO30.5%, 붕사 0.1%, LiCl 1.0%, LiNO31.0% : (e) KMnO43.0%, 붕사 0.1%, LiCl 1.0% : (f) KMnO43.0%, Li2CO30.5 : 필수 성분들은 상기 (a) 내지 (f) 항으로부터 선택되는 것을 특징으로 하는 알루미늄 및 알루미늄 합금용 과망간산염 피복 조성물.
- 제14항에 있어서, 1.0% 이상의 CU를 갖고 있는 알루미늄 합금을 82℃내지 100℃(180℃ 내지 212℃) 사이의 온도에서 물에 침지시켜 알루미늄 합금상에 알루미늄 산화물 피복을 제공하고, 그 다음에, 그 산화물 피복 알루미늄 합금을 청구범위 제19항 또는 제20항의 과망간산염 용액으로 처리하여, 그 과망간산염 처리된 합금을 헹구고, 그 헹군 합금을 알칼리 금속 규산염과 접촉시키고, 그 규산염 처리된 합금을 Ca(OH)2및 알칼리 금속 질산염의 용액으로 헹구고, 그 다음에, 그 합금을 헹구어 보호된 합금으로 회복시키는 것을 특징으로 하는 보호 피복으로 알루미늄 및 알루미늄 합금을 보호하는 방법.
- 제21항에 있어서, 과망간산염 용액은, 필수 성분으로써, 과망간산염 칼륨, 염화 리튬, 질산 리튬, 수화 규산 나트륨, 붕사를 함유하고 있고, 그리고, 알칼리 금속 규산염은 규산 칼륨이고, 그리고, 알칼리 금속 질산염은 질산 리튬인 것을 특징으로 하는 보호 피복으로 알루미늄 및 알루미늄 합금을 보호하는 방법.
- 제14항에 있어서, 4% 이상의 Zn을 갖고 있는 알루미늄 합금을 처음에 세척하여, 그 다음에 제1과망간산염 용액으로 처리하고, 헹구고, 그 다음에 필수 성분으로써 알칼리 금속 과망간산염과 알칼리 금속 탄산염을 함유하고 있는 제2과망간산염 용액으로 처리한 것을 특징으로 하는 보호 피복으로 알루미늄 및 알루미늄 합금을 보호하는 방법.
- 제23항에 있어서, 제1과망간산염 용액은, 필수 성분으로써, 과망간산 칼륨, 알칼리 금속 염화물 및 붕사를 함유하고 있는것을 특징으로 하는 보호 피복으로 알루미늄 및 알루미늄 합금을 보호하는 방법.
- 제23항에 있어서, 상기 알칼리 금속 염화물은 염화 리튬이고, 상기 알칼리 금속 탄산염은 탄산 리튬인 것을 특징으로 하는 보호 피복으로 알루미늄 및 합금을 보호 하는 방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.