KR850700261A - 바나듐 첨가제로서 화학적으로 제조한 v₂o₃을 사용하는 공구강의 제조공정 - Google Patents
바나듐 첨가제로서 화학적으로 제조한 v₂o₃을 사용하는 공구강의 제조공정Info
- Publication number
- KR850700261A KR850700261A KR1019850700296A KR850700296A KR850700261A KR 850700261 A KR850700261 A KR 850700261A KR 1019850700296 A KR1019850700296 A KR 1019850700296A KR 850700296 A KR850700296 A KR 850700296A KR 850700261 A KR850700261 A KR 850700261A
- Authority
- KR
- South Korea
- Prior art keywords
- sub
- molten steel
- sio
- cao
- silicon
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
첨부한 도면에서 제1도는 본 발명에 따른 바나듐첨가제로서 사용된 화학적으로 제조한 V2O3을 100X배 확대한 현미경사진.
Claims (6)
- (a) 약 0.35중량%이상의 탄소함량을 갖고, 약 0.15 내지 약 3.0중량%의 실리콘을 함유하는 용융강 및 SiO2에 대한 CaO의 중량비가 1 또는 1보다 큰 비율로 CaO 및 SiO2를 함유하고, 용융강을 피복시키는 슬래그를 형성하고; 및 (b) 용융강속에 약 0.4 내지 약 5.0중량%의 바나듐을 함유하는 강을 제조하기 위해 상기 탄소 및 실리콘과 화학양론적으로 반응할 수 있는 양이상으로, 필수적으로 화학적으로 제조되고 실질적으로 순수한 V2O3로 구성되는 바나듐 첨가제를 용융강속에 가함을 특징으로 하는 공구강의 제조공정.
- 제1항에 있어서, 슬래그에서 SiO2에 대한 CaO의 중량비가 2와 같거나 또는 2이상임을 특징으로 하는 공정.
- 제1항에 있어서, 슬래그는 탄화칼슘, 실리콘철 및 실리코망간으로 구성되는 그룹으로부터 선택된 재료의 부가에 의하여 환원됨을 특징으로 하는 공정.
- 제1항에 있어서, 용융강은 약 0.10wt.%이하의 알루미늄을 함유함을 특징으로 하는 공정.
- 제1항에 있어서, 화학적으로 제조되고 실질적으로 순수한 V2O3는 약 80000cm2/cm3이상의 표면적을 갖음을 특징으로 하는 공정.
- 제1항에 있어서, 화학적으로 제조되고 실질적으로 순수한 V2O3는 약 70 내지 77 1b/cu.ft의 부피밀도를 갖도록 분쇄됨을 특징으로 하는 공정.※참고사항:최초출원 내용에 의하여 공개하는 것임.