KR850007813A - 반고체 금속슬러리 형성용 β상 동기본합금 및 그 제조방법 - Google Patents
반고체 금속슬러리 형성용 β상 동기본합금 및 그 제조방법 Download PDFInfo
- Publication number
- KR850007813A KR850007813A KR1019850002425A KR850002425A KR850007813A KR 850007813 A KR850007813 A KR 850007813A KR 1019850002425 A KR1019850002425 A KR 1019850002425A KR 850002425 A KR850002425 A KR 850002425A KR 850007813 A KR850007813 A KR 850007813A
- Authority
- KR
- South Korea
- Prior art keywords
- alloy
- semi
- forming
- solid metal
- phase synchronous
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (20)
- 반고체 금속슬러리 형성용으로 적합하며 자신보다 저용융점을 갖는 매트릭스내에 수용된 이산입자를 갖는 미소조직을 포함하는 β상이 주인 동기본합금에 있어서, 상기 합금은 9 내지 10.5%량의 알루미늄, 적어도 10중량%의 니켈 및 잔부는 거의 구리로 된 것을 특징으로 하는 반고체 금속슬러리 형성용 β상 동기본합금.
- 제1항에 있어서, 상기 합금은 칠주조하며 주조중에 교반할 필요없이 바라는 미소조직을 형성하기에 적합한 것으로서, 9 내지 10중량%의 알루미늄, 10 내지 12중량% 니켈 및 잔부는 거의 구리로 된 것을 특징으로 하는 반고체 금속슬러리 형성용 β상 동기본합금.
- 제2항에 있어서, 상기 합금은 틱소단조된 상태인 것을 특징으로 하는 반고체 금속슬러리 형성용 β상 동기본합금.
- 제3항에 있어서, 상기 합금은 시효경화처리된 상태인 것을 특징으로 하는 반고체 금속슬러리 형성용 β상 동기본합금.
- 제3항에 있어서, 상기 합금은 용체화처리 및 시효경화처리된 상태인 것을 특징으로 하는 반고체 금속슬러리 형성용 β상 동기본합금.
- 제3항에 있어서, 이산입자는 β상을 포함하고, 매트릭스는 α+β공정상을 포함하는 것을 특징으로 하는 반고체 금속슬러리 형성용 β상 동기본합금.
- 제1항에 있어서, 상기 슬러리는 응고시 매트릭스를 포함하며 액상의 체적분율이 10 내지 30%에 달하는 것을 특징으로 하는 반고체 금속슬러리 형성용 β상 동기본합금.
- 제1항에 있어서, 상기 합금은 카트리지 케이스와 같은 벽이 얇고 연신된 부재의 제조용으로 적합한 것을 특징으로 하는 반고체 금속슬러리 형성용 β상 동기본합금.
- 반고체 금속슬러리 형성용으로 적합한 β상이 주인 동기본합금에 있어서, 상기 합금은 자신보다 저용융점을 갖는 매트릭스내에 수용된 이산입자를 포함하는 미소조직을 가지며, 그 조성은 9 내지 10.5중량% 의 알루미늄, 니켈과 철의 총량이 적어도 10중량%을 유지하면서 3 내지 7중량%의 니켈 및 3 내지 7중량%의 철, 그리고 잔부는 거의 구리인 것을 특징으로 하는 반고체 금속슬러리 형성용 β상 동기본합금.
- 제9항에 있어서, 상기 합금은 칠주조하며 주조중에 교반할 필요없이 바라는 미소조직을 형성하기에 적합한 것으로서, 그 조성이 9 내지 10중량%의 알루미늄, 니켈과 철의 총량이 10 내지 12중량%를 유지하면서 4 내지 6중량%의 니켈 및 4 내지 6중량%의 철, 그리고 잔부는 거의 구리인 것을 특징으로 하는 반고체 금속슬러리 형성용 β상 동기본합금.
- 제10항에 있어서, 상기 합금은 틱소단조된 상태인 것을 특징으로 하는 반고체 금속슬러리 형성용 β상 동기본합금.
- 제11항에 있어서, 상기 합금은 시효경화처리된 상태인 것을 특징으로 하는 반고체 금속슬러리 형성용 β상 동기본합금.
- 제11항에 있어서, 상기 합금은 용체와처리 및 시효경화처리된 상태인 것을 특징으로 하는 반고체 금속슬러리 형성용 β상 동기본합금.
- 제11항에 있어서, 이산입자는 β상을 포함하고, 매트릭스는 α+β공정상을 포함하는 것을 특징으로 하는 반고체 금속슬러리 형성용 상 동기본합금.
- 제9항에 있어서, 상기 슬러리는 응고시 매트릭스를 포함하며 액상의 체적분율이 10 내지 30%에 달하는 것을 특징으로 하는 반고체 금속슬러리 형성용 β상 동기본합금.
- 제9항에 있어서, 상기합금은 카트리지 케이스와 같은 벽이 얇고 연신된 부재의 제조용으로 적합한 것을 특징으로 하는 반고체 금속슬러리 형성용 β상 동기본합금.
- 반고체 금속슬러리 상태로 형성하기에 적합한 β상 동기본합금의 제조방법에 있어서, 조성이 9 내지 10.5중량%의 알루미늄, 적어도 10중량%의 니켈 및 잔부는 거의 구리인 합금을 준비하거나, 또는 조성이 9 내지 10.5중량%의 알루미늄, 니켈과 철의 총량이 적어도 10중량%를 유지하면서 3 내지 7중량%의 니켈 및 3 내지 7중량%의 철, 그리고 잔부는 거의 구리인 합금을 준비하고, 완전히 용해된 합금을 주물의 전단면을 통하여 냉각속도가 적어도 10°C/sec를 유지하면서 칠주조하는 것을 특징으로 하는 반고체 금속슬러리 형상용 β상 동기본합금의 제조방법.
- 제17항에 있어서, 합금에 저용융점을 갖는 용융매트릭스내의 이산입자를 포함시키기 위하여 합금을 15분 이내로 반고체상태로 만들 수 있는 온도로 칠주조된 합금을 가열하는 단계를 포함하는 것을 특징으로 하는 반고체 금속슬러리 형성용 β상 동기본합금의 제조방법.
- 제18항에 있어서, 반고체 상태의 합금을 프레스 단조하는 단계를 포함하는 것을 특징으로 하는 반고체 금속슬러리 형성용 β상 동기본합금의 제조방법.
- 제19항에 있어서, 프레스단조 공정은 합금이 가열공정에 의해 반고체 상태인 동안 실시하는 것을 특징으로 하는 반고체 금속슬러리 형성용 β상 동기본합금의 제조방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.