KR20220071009A - Metal-like flooring material and method for preparing the same - Google Patents
Metal-like flooring material and method for preparing the same Download PDFInfo
- Publication number
- KR20220071009A KR20220071009A KR1020200158171A KR20200158171A KR20220071009A KR 20220071009 A KR20220071009 A KR 20220071009A KR 1020200158171 A KR1020200158171 A KR 1020200158171A KR 20200158171 A KR20200158171 A KR 20200158171A KR 20220071009 A KR20220071009 A KR 20220071009A
- Authority
- KR
- South Korea
- Prior art keywords
- layer
- film layer
- pearl
- flooring material
- flooring
- Prior art date
Abstract
Description
본 발명은 자연스러운 금속 질감을 가지는 금속 질감 바닥재로서, 기재층, 투명 펄 필름층, 인쇄층 및 표면필름층을 포함하는 금속 질감 바닥재에 관한 것이다.The present invention relates to a metal textured flooring material having a natural metal texture, the metal textured flooring including a base layer, a transparent pearl film layer, a printing layer, and a surface film layer.
최근 조색기술의 발달과 함께 제품에 대한 소비자의 색감과 미감에 대한 수준이 향상됨에 따라, 소비자의 요구를 만족시킬 수 있는 다양한 미감이 구현된 디자인 제품이 출시되고 있다.With the recent development of color matching technology, as consumers' level of color and aesthetics for products have improved, design products with various aesthetic senses that can satisfy consumers' needs are being released.
그 중, 디자인적 요소에 큰 영향을 받는 벽지, 바닥재, 천장마감재 등과 같은 같은 내장재에 대한 소비자의 관심과 요구가 증가하고 있는 실정이다.Among them, consumer interest and demand for interior materials such as wallpaper, flooring, and ceiling finishing materials, which are greatly affected by design factors, are increasing.
한편, 바닥재의 경우, 디자인적 요소만이 아니라, 사용자가 직접 밟거나 물건을 거치하는 등의 실질적인 마찰과 사용이 동반되므로, 바닥재로서의 요구 기능을 만족하면서도, 미감을 향상시켜야 하는 제한이 있었다. On the other hand, in the case of a flooring material, not only a design element, but also practical friction and use such as directly stepping on by a user or placing an object, there is a limitation in that it is necessary to improve the aesthetics while satisfying the required function as a flooring material.
이에, 나무 질감 바닥재, 금속 질감 바닥재, 대리석 질감 바닥재와 같이, 실제 소재는 수지를 이용한 바닥재층으로 구성하고 이의 표면에 자연스러운 디자인의 패턴과 색감을 부여함으로써, 바닥재의 미감을 향상시키면서도 바닥재로서 요구되는 내구성, 내충격성, 내스크래치성 등의 물성을 만족하도록 구성하였다.Accordingly, such as wood texture flooring, metal texture flooring, and marble texture flooring, the actual material consists of a flooring layer using a resin and gives a pattern and color of a natural design to the surface thereof, thereby improving the aesthetics of the flooring while improving the flooring required as a flooring material. It was constructed to satisfy physical properties such as durability, impact resistance, and scratch resistance.
금속 질감 바닥재의 경우에는, 더욱 자연스러운 금속 질감을 구현하기 위해, 금속 파우더, 금속 펄과 같은 소재를 인쇄하여 자연스러운 금속 질감의 바닥재를 제조하고자 하였으나, 금속 파우더나 금속 펄과 같은 소재는 인쇄층에 일정량 이상으로 사용되는 경우, 이웃한 층과의 접착력을 저하시켜 층간 박리가 발생되는 문제가 있었다.In the case of metal texture flooring, in order to realize a more natural metal texture, it was attempted to manufacture a natural metal textured flooring material by printing materials such as metal powder and metal pearl. When used as described above, there was a problem in that the adhesive force with the adjacent layer was lowered, so that delamination between the layers occurred.
대한민국 등록특허 제0467227호는 합성수지 타일 바닥재에 있어서, 인쇄층에 금속 펄을 포함하여 금속 질감을 형성하는 타일 바닥재의 구성만을 개시하고 있고, 더욱 자연스러운 금속 질감을 형성하기 위해, 금속 펄의 사용량을 증가시키면서도 바닥재의 내구성을 확보하기 위한 해결과제 및 이의 해결방법에 대해서는 구체적으로 개시하고 있지 않다.Republic of Korea Patent No. 0467227 discloses only the composition of a tile flooring material that forms a metallic texture by including metallic pearls in the printed layer in a synthetic resin tile flooring material, and increases the amount of metallic pearls used to form a more natural metallic texture It does not specifically disclose a solution for securing the durability of the flooring while making the flooring material and a method for solving the same.
한편, 바닥재 상부면에서 균일한 광택효과와 반사효과를 가지는 경우에는 자연스러운 금속 질감을 구현하기 어렵고, 인위적인 시각효과를 주어 바닥재의 미감을 오히려 저하시키는 문제가 있다. 이는 일반적으로 금속이 빛이 비추는 방향에 따라 영역을 달리하여 반사효과를 가지기 때문에, 자연스러운 금속 질감을 구현하기 위해서는 바닥재 표면에서 광택효과와 반사효과를 표면 영역에 따라 다르게 구성하는 것이 필요하다.On the other hand, when the upper surface of the flooring has a uniform glossy effect and a reflective effect, it is difficult to realize a natural metal texture, and there is a problem in that the aesthetics of the flooring is rather deteriorated by giving an artificial visual effect. In general, since metal has a reflective effect by changing the region according to the direction in which light shines, it is necessary to configure the gloss effect and the reflective effect differently on the surface of the flooring material according to the surface area in order to realize a natural metal texture.
이와 관련하여, 대한민국 등록실용신안 제0299621호는 난반사 효과가 우수한 동조입체질감의 바닥재에 관한 것으로서, 하부발포층, 유리섬유매트와 PVC 수지를 포함하는 유리섬유매트 함침층, 상부발포층, 펄시트층, 억제인쇄층 및 투명층이 순차로 적층된 구조의 동조입체질감의 바닥재에 관해서 개시하고 있으나, 바닥재의 표면에서 보다 자연스러운 금속 질감을 구현하기 위해 영역에 따라 다른 반사효과와 광택효과를 나타내도록 하는 기술에 대해서는 개시되어 있지 않다.In this regard, Republic of Korea Registered Utility Model No. 0299621 relates to a flooring material having a synchronous three-dimensional texture with excellent diffuse reflection effect. Although it discloses a flooring material with a three-dimensional texture in which a layer, a suppression printing layer, and a transparent layer are sequentially stacked, a different reflective effect and a gloss effect depending on the area to realize a more natural metallic texture on the surface of the flooring material. The technique is not disclosed.
본 발명의 발명자들은 수많은 실험과 반복을 거듭한 끝에, 자연스러운 금속 질감을 구현하여 심미감을 향상시키면서도, 바닥재 층의 박리가 일어나지 않아 우수한 내구성을 확보할 수 있는 금속 질감 바닥재 및 이의 제조방법을 완성하기에 이으렀다.The inventors of the present invention, after numerous experiments and repetitions, realize a natural metal texture to improve aesthetics, and to complete a metal texture flooring material that can ensure excellent durability without peeling of the floor material layer and a method for manufacturing the same followed
본 발명은 금속 질감 바닥재에 관한 것으로서, 자연스러운 금속 질감을 구현하기 위해 메탈릭 펄의 사용량을 증가시키면서도 바닥재의 박리를 방지할 수 있는 신규한 금속 질감 바닥재 및 이의 제조방법을 제공하는 것을 목적으로 한다.The present invention relates to a metal textured flooring, and an object of the present invention is to provide a novel metal textured flooring that can prevent peeling of the flooring while increasing the amount of metallic pearl used to realize a natural metal texture, and a method for manufacturing the same.
본 발명은 바닥재의 표면에서 영역에 따라 광택효과와 반사효과가 상이하게 나타나 더욱 자연스러운 금속 질감이 구현된 금속 질감 바닥재 및 이의 제조방법을 제공하는 것을 목적으로 한다.An object of the present invention is to provide a metal textured flooring material in which a more natural metal texture is realized by showing different gloss effects and reflection effects depending on regions on the surface of the flooring material, and a method for manufacturing the same.
상기와 같은 과제를 해결하기 위한, 본 발명에 따른 금속 질감 바닥재는, 기재층, 투명 펄 필름층, 인쇄층 및 표면필름층을 포함하고, 상기 투명 펄 필름층은 펄 안료를 포함한다. In order to solve the above problems, the metal textured flooring material according to the present invention includes a base layer, a transparent pearl film layer, a printing layer, and a surface film layer, and the transparent pearl film layer includes a pearl pigment.
본 발명에 있어서, 상기 투명 펄 필름층은 상기 투명 펄 필름층의 전체 중량을 기준으로 펄 안료를 0.5 내지 5 중량%로 포함할 수 있다.In the present invention, the transparent pearl film layer may include a pearl pigment in an amount of 0.5 to 5% by weight based on the total weight of the transparent pearl film layer.
본 발명에 있어서, 상기 투명 펄 필름층은 두께가 0.05 내지 0.4 mm일 수 있다.In the present invention, the transparent pearl film layer may have a thickness of 0.05 to 0.4 mm.
본 발명에 있어서, 상기 투명 펄 필름층은 PVC 수지 및 메탈릭 펄 안료를 포함할 수 있다.In the present invention, the transparent pearl film layer may include a PVC resin and a metallic pearl pigment.
본 발명에 있어서, 상기 금속 질감 바닥재는 상기 투명 펄 필름층과 상기 인쇄층 사이에 은폐잉크층을 더 포함할 수 있다.In the present invention, the metal texture flooring material may further include a hiding ink layer between the transparent pearl film layer and the printing layer.
보다 상세하게는, 상기 은폐잉크층은 이산화티탄, 산화아연 및 탄석으로 이루어진 군에서 선택된 하나 이상을 포함할 수 있다.More specifically, the hiding ink layer may include one or more selected from the group consisting of titanium dioxide, zinc oxide, and carbon dioxide.
본 발명에 있어서, 상기 금속 질감 바닥재는 가시광선 영역의 빛 반사율이 40 내지 80 %일 수 있다.In the present invention, the metal texture flooring material may have a light reflectance of 40 to 80% in a visible ray region.
본 발명에 따른 금속 질감 바닥재의 제조방법은, a) 기재층의 표면에 투명 펄 필름층을 형성하는 단계, b) 상기 a) 단계에서 형성된 상기 투명 펄 필름층의 표면에 인쇄층을 형성하는 단계 및 c) 상기 b) 단계에서 형성된 인쇄층의 표면에 표면필름층을 형성하는 단계를 포함한다.The method of manufacturing a metal textured flooring material according to the present invention comprises the steps of: a) forming a transparent pearl film layer on the surface of a base layer; b) forming a printed layer on the surface of the transparent pearl film layer formed in step a) and c) forming a surface film layer on the surface of the printed layer formed in step b).
보다 상세하게는, 상기 a) 단계 후, 상기 b) 단계 전에 은폐잉크층을 형성하는 단계를 더 포함할 수 있다.More specifically, after step a), the method may further include forming a hiding ink layer before step b).
본 발명은 기존의 금속 질감 바닥재보다 메탈릭 펄 함량을 증가시킬 수 있어 보다 향상된 금속 질감 효과를 가진다.The present invention can increase the metallic pearl content than the conventional metallic texture flooring material, so that it has a more improved metallic texture effect.
본 발명은 메탈릭 펄의 함량을 기존기술보다 과량으로 포함하면서도, 바닥재층이 상호 분리되는 문제, 즉, 메탈릭 펄이 인쇄되는 인쇄층에서의 박리가 방지되어 바닥재의 내구성이 우수한 효과를 가진다.The present invention has an excellent effect of durability of the flooring material by preventing the problem of separation of the flooring layers from each other, that is, peeling from the printed layer on which the metallic pearls are printed, while including an excessive amount of metallic pearls compared to the conventional technology.
본 발명에 따른 금속 질감 바닥재는 은폐잉크층과 색조잉크를 포함하는 인쇄층에 의해 영역에 따라 바닥재 표면에서 메탈릭 펄의 광택효과, 반사효과가 상이하게 나타나 보다 자연스러운 금속 질감을 나타내는 효과를 가진다.The metallic texture flooring material according to the present invention has the effect of showing a more natural metallic texture because the gloss effect and the reflection effect of the metallic pearl are different on the surface of the flooring material depending on the area by the printing layer including the hiding ink layer and the color ink.
본 발명은 또한, 인쇄공정, 합지공정 등의 기존 기술과 유사한 과정으로 공정을 수행함에 따라 추가 설비를 구비할 필요없이 기존의 설비를 그대로 이용할 수 있는 금속 질감 바닥재의 제조방법을 제공한다.The present invention also provides a method for manufacturing a metal texture flooring material that can use existing equipment as it is without the need for additional equipment as the process is performed in a process similar to the existing technology, such as a printing process and a laminating process.
도 1은 본 발명의 일 실시예에 따른 금속 질감 바닥재의 구조를 나타낸 모식도이다;
도 2는 본 발명의 일 실시예에 따른 금속 질감 바닥재의 사진이다;
도 3은 본 발명의 또 따른 실시예에 따른 금속 질감 바닥재의 사진이다;
도 4는 본 발명의 또 다른 실시예에 따른 금속 질감 바닥재의 사진이다.1 is a schematic diagram showing the structure of a metal textured flooring according to an embodiment of the present invention;
2 is a photograph of a metal textured flooring according to an embodiment of the present invention;
3 is a photograph of a metal textured flooring material according to another embodiment of the present invention;
4 is a photograph of a metal textured flooring material according to another embodiment of the present invention.
이하, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 각 구성을 보다 상세히 설명하나, 이는 하나의 예시에 불과할 뿐, 본 발명의 권리범위가 다음 내용에 의해 제한되지 아니한다.Hereinafter, each configuration of the present invention will be described in more detail so that those of ordinary skill in the art to which the present invention pertains can easily carry out, but this is only an example, and the scope of the present invention is defined by the following contents Not limited.
본 발명에 따른 금속 질감 바닥재는 기재층, 투명 펄 필름층, 인쇄층 및 표면필름층을 포함하고, 각 층은 바닥면으로부터 순차로 적층된 구조를 가지며 상기 투명 펄 필름층은 펄 안료를 포함한다.The metal textured flooring according to the present invention includes a base layer, a transparent pearl film layer, a printing layer, and a surface film layer, each layer has a structure sequentially stacked from the bottom surface, and the transparent pearl film layer includes a pearl pigment .
본 발명은 기존의 금속 질감 바닥재에 있어서, 금속 질감 효과를 향상시키기 위해 인쇄층에 메탈릭 펄의 사용량을 증가시키는 것이 필요하였으나, 인쇄층에 메탈릭 펄의 사용량이 증가하는 경우에는, 인쇄층과 인접한 층과의 접착력이 저하됨에 따라, 인쇄층의 상부층과 하부층이 서로 분리되는 문제가 있었다.In the present invention, in the existing metal textured flooring, it was necessary to increase the amount of metallic pearl used in the printed layer in order to improve the metal texture effect. As the adhesive strength with the lower layer decreased, there was a problem in that the upper layer and the lower layer of the printed layer were separated from each other.
본 발명은 메탈릭 펄의 사용량을 증가시키면서도 인쇄층의 부착력이 저하되는 문제를 해결하기 위한 발명으로서, 본 발명에서는 인쇄층의 하부에 메탈릭 펄을 포함하는 투명 펄 시트를 도입하여 메탈릭 펄 인쇄층에 메탈릭 펄을 사용하여 인쇄한 것과 동일한 효과를 가지면서도 메탈릭 펄의 사용량을 증가시켜 더욱 향상된 금속 질감 효과 부여한 것을 특징으로 한다.The present invention is an invention for solving a problem that the adhesion of the printed layer decreases while increasing the amount of metallic pearl used. It is characterized in that it has the same effect as printed using pearls, but has a more improved metallic texture effect by increasing the amount of metallic pearls used.
도 1은 본 발명의 일 실시예에 따른 금속 질감 바닥재의 구조를 나타낸 모식도이다.1 is a schematic diagram showing the structure of a metal textured flooring according to an embodiment of the present invention.
도 1을 참고하면, 바닥면으로부터 기재층(Base층), 투명 펄 필름층(메탈 펄 필름), 고은폐 백색 잉크층, 인쇄층 및 표면의 투명필름층으로 구성된 금속 질감 바닥재가 개시되어 있다.Referring to FIG. 1, a metal textured flooring composed of a base layer (Base layer), a transparent pearl film layer (metal pearl film), a high hiding white ink layer, a printing layer, and a transparent film layer on the surface from the bottom surface is disclosed.
이는 하나의 예시로서, 필요에 따라 고은폐 백색 잉크층을 포함하지 않거나 포함하도록 구성함으로써 보다 자연스러운 금속 질감을 구현할 수도 있다.This is an example, and a more natural metal texture may be implemented by configuring it to include or not include a high hiding white ink layer if necessary.
이하, 구성을 보다 상세히 설명한다.Hereinafter, the configuration will be described in more detail.
투명 펄 필름층transparent pearl film layer
본 발명에 따른 금속 질감 바닥재는, 기존의 바닥재와 대비하여, 펼 안료를 포함하는 투명 펄 필름층을 포함하는 것을 특징으로 한다.The metal textured flooring according to the present invention is characterized in that it includes a transparent pearl film layer including a spreading pigment, as compared to a conventional flooring material.
상기 투명 펄 필름층은 기재층의 상부에 위치하고, 인쇄층의 하부에 위치하여, 투명 펄 필름층의 상부에 목적하는 디자인으로 금속 효과를 부여하기 위한 인쇄층을 형성한다.The transparent pearl film layer is located above the base layer and below the printed layer to form a printed layer for imparting a metallic effect in a desired design on the transparent pearl film layer.
구체적으로, 상기 투명 펄 필름층은 해당 필름층의 전체 중량으로 기준으로 펄 안료를 0.5 내지 5 중량%로 포함하는 것을 특징으로 한다. 바람직하게는, 0.65 중량% 이상으로 포함할 수 있다.Specifically, the transparent pearl film layer is characterized in that it contains 0.5 to 5% by weight of the pearl pigment based on the total weight of the film layer. Preferably, it may be included in an amount of 0.65% by weight or more.
상기 함량보다 소량으로 포함하는 경우에는, 기존의 금속 질감 바닥재와 대비하여 금속 질감 효과 차이가 미미한 문제가 있고, 상기 함량보다 과량으로 포함하는 경우에는, 상기 투명 펄 필름층을 형성하기 위한 혼합 조성물의 점도가 증가하여, 필름 형태로 구현하기 어렵거나, 다른 층과의 부착력이 저하되는 문제가 있을 수 있다.When included in a smaller amount than the above content, there is a slight problem in the difference in metal texture effect compared to the existing metal texture flooring material. As the viscosity increases, it may be difficult to implement in the form of a film, or there may be a problem in that adhesion with other layers is reduced.
한편, 상기 투명 펄 필름층의 두께는 0.05 내지 0.4 mm일 수 있다. 바람직하게는, 0.1 내지 0.3 mm일 수 있다. 상기 두께 범위로 구성함으로써, 바닥재 내에 추가 층을 부가함에 따른 문제점인 컬링 등의 밸런스가 저하되는 문제점을 최소화하면서도 펄에 의한 디자인 효과를 구현할 수 있다. Meanwhile, the thickness of the transparent pearl film layer may be 0.05 to 0.4 mm. Preferably, it may be 0.1 to 0.3 mm. By configuring the thickness range, it is possible to realize the design effect by the pearl while minimizing the problem of balance deterioration, such as curling, which is a problem caused by adding an additional layer in the flooring.
상기 두께보다 얇은 경우에는, 펄 안료가 투명 펄 필름층에 균일하게 분산되기 어려운 문제점이 있고, 펄 안료의 사용량 대비 금속 질감 효과 차이가 크지 않은 문제가 있을 수 있다.When the thickness is thinner than the above thickness, there may be a problem in that it is difficult for the pearl pigment to be uniformly dispersed in the transparent pearl film layer, and there may be a problem in that the difference in the metal texture effect is not large compared to the amount of the pearl pigment used.
상기 두께보다 두꺼운 경우에는, 바닥재의 일반 두께 규격을 맞추기 위해 기재층의 두께가 상대적으로 얇아짐에 따라, 바닥재의 지지성능이 저하되어 바닥재 자체의 품질저하를 유발할 수 있는 문제가 있을 수 있다.If it is thicker than the thickness, as the thickness of the base layer becomes relatively thin in order to meet the general thickness specification of the flooring material, the supporting performance of the flooring material is lowered, and there may be a problem that may cause deterioration of the quality of the flooring material itself.
상기 투명 펄 필름층에 포함되는 펄 안료는, 바람직하게는, 메탈릭 펄 안료를 사용할 수 있다.The pearl pigment contained in the transparent pearl film layer may preferably be a metallic pearl pigment.
보다 상세하게는, 상기 메탈릭 펄 안료는 골드 펄 안료(Gold pearl pigment), 실버 펄 안료(Silver pearl pigment), 코퍼 펄 안료(Copper pearl pigment), 크롬 펄 안료(Chrome pearl pigment), 황동 펄 안료(Brass pearl pigment) 및 이의 혼합물로 이루어진 군에서 선택된 하나일 수 있다.More specifically, the metallic pearl pigment is a gold pearl pigment (Gold pearl pigment), silver pearl pigment (Silver pearl pigment), copper pearl pigment (Copper pearl pigment), chrome pearl pigment (Chrome pearl pigment), brass pearl pigment ( It may be one selected from the group consisting of brass pearl pigment) and mixtures thereof.
상기 메탈릭 펄 안료는 목표하는 효과에 따라 적절히 메탈릭 펄 안료 혼합물을 포함하도록 구성할 수 있다.The metallic pearl pigment may be appropriately configured to include a metallic pearl pigment mixture according to a desired effect.
한편, 상기 투명 펄 필름층은 펄 안료 외에 PVC 수지를 포함한다. PVC 수지는 내구성이 우수하고, 필름 형태로 가공하기 용이한 장점을 가지며, 투명 필름층으로 구성하기에 용이한 바, PVC 수지를 이용하여 상기 투명 펄 필름층을 제조한다.Meanwhile, the transparent pearl film layer includes a PVC resin in addition to the pearl pigment. The PVC resin has excellent durability, has the advantage of being easy to process in a film form, and is easy to configure as a transparent film layer, so the transparent pearl film layer is prepared using the PVC resin.
상기 투명 펄 필름층은 필요에 따라, 가소제, 가공조제 등의 다양한 첨가제를 더 포함할 수 있다. 이는 해당 투명 펄 필름층의 물성을 조절하기 위해 필요에 따라 적절히 첨가될 수 있다.The transparent pearl film layer may further include various additives such as a plasticizer and a processing aid, if necessary. It may be appropriately added as necessary to control the physical properties of the transparent pearl film layer.
도 2는 본 발명의 일 실시예에 다른 금속 질감 바닥재의 사진으로서, 도 2는 기재층, 투명 펄 필름층, 인쇄층 및 표면보호층으로 이루어진 바닥재의 사진이다.2 is a photograph of a metal textured flooring material according to an embodiment of the present invention.
종래기술의 금속 질감 바닥재에 비해 투명 펄 필름층에 메탈릭 펄 안료를 포함하도록 구성함으로써, 금속 질감 효과가 더욱 향상된 효과를 가지면서도, 바닥재의 내구성이 양호 내지 우수한 특성을 가진다.By configuring the transparent pearl film layer to include a metallic pearl pigment compared to the metal textured flooring material of the prior art, the metal texture effect is further improved, and the durability of the flooring material is good to excellent.
기재층base layer
상기 기재층은 바닥재로 기능할 수 있도록 하기 위한 것이며, 이의 상단에 위치하는 투명 펄 필름층, 인쇄층 등을 지지하는 역할을 한다.The base layer is to function as a flooring material, and serves to support a transparent pearl film layer, a printing layer, etc. located on the upper end thereof.
상기 기재층은 상부층을 지지하고, 바닥재로 기능할 수 있는 것이면 특별히 제한되지 않고 사용이 가능하고, 바닥재의 형태와 특성에 따라 다르게 구성할 수 있다.The base layer supports the upper layer and can be used without particular limitation as long as it can function as a flooring material, and may be configured differently depending on the shape and characteristics of the flooring material.
바닥재는 시트형, 소위 장판이라고 불리우는 형태의 바닥재가 있으며, 타일형 바닥재가 있으며, 본 발명에서는 바닥재의 종류에 따라 다양한 기재층을 사용할 수 있다.There are sheet-type flooring materials, so-called flooring materials, and tile-type flooring materials. In the present invention, various substrate layers can be used depending on the type of flooring material.
상기 기재층은 구체적으로, PET 수지, PVC 수지, 아크릴 수지, 우레탄 수지 등으로 이루어진 군에서 선택된 하나 이상의 수지를 포함할 수 있고, 바람직하게는, PET 수지를 포함하도록 구성될 수 있다.Specifically, the base layer may include one or more resins selected from the group consisting of PET resin, PVC resin, acrylic resin, urethane resin, and the like, and preferably, may be configured to include PET resin.
상기 기재층의 두께는 특별히 제한되지 않고 바닥재로서 기본적으로 요구되는 특성을 만족하는 것이면 사용이 가능하다.The thickness of the base layer is not particularly limited and can be used as long as it satisfies the basic properties required as a flooring material.
인쇄층print layer
상기 투명 펄 필름의 상부에는 인쇄층이 형성된다. 상기 인쇄층은 바닥재에 컬러감과 디자인을 주어 심미감을 부여하기 위한 것으로서, 다양한 컬러잉크를 일정한 패턴으로 또는 전면에 인쇄할 수 있다.A printed layer is formed on the transparent pearl film. The printing layer is for giving an aesthetic feeling by giving a color and a design to the flooring material, and various color inks can be printed in a predetermined pattern or on the entire surface.
상기 인쇄층의 인쇄방법은 특별히 방법이 제한되지 않고 다양한 방법을 사용할 수 있으나, 보다 상세하게는, 상기 컬러잉크는 그라비아 인쇄방식을 이용하여 도수 인쇄할 수 있다. 상기 컬러잉크는, CMYK 잉크를 이용하여, 다양한 색감을 구현할 수 있다.The printing method of the printing layer is not particularly limited and various methods may be used, but in more detail, the color ink may be repeatedly printed using a gravure printing method. The color ink may implement various colors by using CMYK ink.
종래기술에서는 바닥재의 표면에서의 금속 질감을 구현하기 위해, 펄 안료를 인쇄층에 포함시켜 인쇄함으로써, 금속 질감을 부여하였으나, 이는 펄 안료, 특히, 메탈릭 펄 안료의 사용량이 과다한 경우에, 인쇄층의 상부층과 하부층의 부착력이 떨어지게 되고, 이는 바닥재의 내구성을 저하시키는 문제를 유발하였다.In the prior art, in order to implement a metallic texture on the surface of the flooring material, a metallic texture was imparted by printing by including a pearl pigment in the printing layer. The adhesion of the upper and lower layers of the flooring decreased, which caused a problem of lowering the durability of the flooring material.
그러나, 본 발명에서는 바닥재에 금속 질감을 부여하기 위한 메탈릭 펄 안료를 투명 펄 인쇄층에 포함하도록 구성함으로써 인쇄층에 펄 안료를 포함하지 않거나, 기존에 바닥재의 내구성을 확보하기 위한 제한적인 양만을 사용하더라도 금속 질감 효과가 보다 향상된 효과를 달성할 수 있게 하였다.However, in the present invention, by configuring the transparent pearl printing layer to include a metallic pearl pigment for imparting a metallic texture to the flooring material, the printing layer does not contain a pearl pigment, or only a limited amount is used to ensure the durability of the existing flooring material Even so, the metal texture effect made it possible to achieve a more improved effect.
따라서, 본 발명에 따른 인쇄층은, 컬러잉크 뿐만 아니라, 필요에 따라서는 추가 펄 안료를 포함하도록 인쇄층을 형성할 수 있으며, 특히, 메탈릭 펄 안료를 포함도록 인쇄할 수도 있다.Accordingly, the printing layer according to the present invention may form a printing layer to include additional pearl pigments as necessary as well as color ink, and in particular, may be printed to include metallic pearl pigments.
다만, 상기 인쇄층에 포함되는 펄 안료의 함량은 바닥재를 구성하는 층의 박리를 방지하도록 제한적인 함량으로 사용되는 것이 바람직하다.However, the content of the pearl pigment included in the printing layer is preferably used in a limited amount to prevent peeling of the layers constituting the flooring material.
예를 들면, 상기 투명 펄 인쇄층 외에, 인쇄층에 펄 안료를 포함하여 인쇄하는 경우에는, 인쇄층의 전체 중량을 기준으로 펄 안료를 5 중량% 이하로 포함하도록 구성할 수 있다.For example, when the printing layer includes a pearl pigment in addition to the transparent pearl printing layer, the pearl pigment may be included in an amount of 5 wt % or less based on the total weight of the printing layer.
한편, 상기 인쇄층을 형성하기 위한 인쇄잉크 조성액은 아크릴계 수지 및 컬러잉크를 포함한다.On the other hand, the printing ink composition solution for forming the printing layer includes an acrylic resin and color ink.
아크릴계 수지를 포함하도록 구성함으로써, 인쇄층의 접착력을 우수하게 유지할 수 있도록 구성된다.By configuring it to contain an acrylic resin, it is configured to be able to maintain excellent adhesion of the printing layer.
상술한 바와 같이, 인쇄층의 펄 안료의 함량이 상기 함량을 초과하는 경우에는, 인쇄층의 박리로 인하여 바닥재의 내구성이 저하되는 문제가 있다.As described above, when the content of the pearl pigment in the print layer exceeds the content, there is a problem in that durability of the flooring material is deteriorated due to peeling of the print layer.
상기 인쇄층은 상기 투명 펄 필름층의 펄 안료에 더하여, 이의 상부에 다양한 컬러잉크로 도색함으로써 녹이 슨 금속을 표현하거나, 사용감 등의 자연스러운 흠집이나 변색을 유발하여 보다 자연스러운 금속 질감을 표현할 수 있다.In addition to the pearl pigment of the transparent pearl film layer, the printed layer expresses rusted metal by painting with various color inks on top of it, or by causing natural scratches or discoloration such as feeling of use, a more natural metal texture can be expressed.
도 4는 본 발명의 또 다른 실시예에 따른 금속 질감 바닥재의 사진으로서, 기재층, 투명 펄 필름층, 인쇄층 및 표면보호층을 포함하되, 인쇄층에 어두운 색상의 컬러잉크를 사용함으로써, 금속의 녹슨 효과를 자연스럽게 구현하였음을 확인할 수 있다.4 is a photograph of a metal textured flooring material according to another embodiment of the present invention, including a base layer, a transparent pearl film layer, a printing layer and a surface protection layer, but by using a dark color ink in the printing layer, the metal It can be seen that the rusty effect of the
이와 같이, 투명 펄 필름층을 포함함과 동시에 이의 상부에 위치하는 인쇄층에서 다양한 색상을 활용함으로써 보다 자연스러운 금속 질감을 구현할 수도 있다.In this way, a more natural metal texture may be realized by using various colors in the printing layer positioned above the transparent pearl film layer and at the same time.
은폐잉크층Concealing Ink Layer
본 발명에 따른 금속 질감 바닥재는 기재층, 투명 펄 필름층, 인쇄층 및 표면보호층을 포함하되, 상기 투명 펄 필름층과 상기 인쇄층 사이에 은폐잉크층을 더 포함할 수 있다.The metal textured flooring according to the present invention includes a base layer, a transparent pearl film layer, a printing layer, and a surface protection layer, and may further include a hiding ink layer between the transparent pearl film layer and the printing layer.
상기 은폐잉크층은 하부층의 이미지나 색상이 상부로 노출되는 것을 방지하는 은폐형 백색 안료를 사용하여, 은폐형 백색 안료의 분산 및 농도를 조절함으로써 금속 질감을 보다 자연스럽게 구현하도록 구성된다.The concealing ink layer is configured to realize a metallic texture more naturally by controlling the dispersion and concentration of the concealing type white pigment by using a concealing type white pigment that prevents the image or color of the lower layer from being exposed to the upper side.
상기 은폐잉크층은 은폐력을 가지는 안료, 잉크 성분이라면 특별히 제한되지 않고 사용이 가능하고, 예를 들면, 이산화티탄, 산화아연, 탄석으로 이루어진 군에서 선택된 하나 이상을 포함할 수 있고, 바람직하게는, 이산화티탄을 포함할 수 있다.The hiding ink layer is not particularly limited as long as it is a pigment or ink component having a hiding power, and can be used, for example, it may include one or more selected from the group consisting of titanium dioxide, zinc oxide, and carbon stone, preferably, Titanium dioxide may be included.
또한, 상기 은폐잉크층에는 은폐력을 가지는 폴리머 수지를 사용하여 형성하는 것도 가능하다. 예를 들면, MEK계 미디엄 수지, PVC계 미디엄 수지 등을 사용할 수 있다. 다만, 이는 하나의 예시에 불과할 뿐, 본 발명의 목적 및 효과를 만족하는 범위 내에서 다양한 구성을 활용할 수 있다.In addition, it is also possible to form the hiding ink layer using a polymer resin having a hiding power. For example, MEK-based medium resin, PVC-based medium resin, or the like can be used. However, this is only an example, and various configurations may be used within the range that satisfies the object and effect of the present invention.
상기 은폐잉크층은 20 ㎛(마이크로미터) 이하의 두께로 포함될 수 있고, 바람직하게는, 10 ㎛(마이크로미터) 이하의 두께로 포함될 수 있으며, 5 ㎛(마이크로미터) 이하의 두께로 포함될 수 있다.The hiding ink layer may be included in a thickness of 20 μm (micrometer) or less, preferably, it may be included in a thickness of 10 μm (micrometer) or less, and may be included in a thickness of 5 μm (micrometer) or less. .
상기 두께보다 두꺼운 경우에는, 은폐잉크층의 하부에 위치한 투명 펄 필름층의 펄 안료가 바닥재 표면에서 쉽게 관찰되지 않아 금속 질감 효과가 저하되는 문제가 있을 수 있다.If it is thicker than the thickness, the pearl pigment of the transparent pearl film layer located below the hiding ink layer is not easily observed on the surface of the flooring material, so there may be a problem in that the metal texture effect is deteriorated.
한편, 상기 은폐잉크층은 PVC 수지를 포함할 수 있고, PVC 수지 100 중량부 대비 은폐형 백색 안료를 1 내지 15 중량부로 포함할 수 있다. Meanwhile, the hiding ink layer may include a PVC resin, and may contain 1 to 15 parts by weight of a hiding type white pigment based on 100 parts by weight of the PVC resin.
예를 들면, 이산화티탄 5 내지 10 중량부와 탄석 3 내지 7 중량부를 첨가하여 상기 중량범위 내에서 첨가될 수 있다.For example, 5 to 10 parts by weight of titanium dioxide and 3 to 7 parts by weight of coal may be added within the above weight range.
바람직하게는, 상기 은폐형 백색 안료를 5 내지 10 중량부로 포함할 수 있으며, 이 때, 상기 은폐형 백색 안료는 이산화티탄일 수 있다.Preferably, the hiding-type white pigment may be included in an amount of 5 to 10 parts by weight, and in this case, the hiding-type white pigment may be titanium dioxide.
상기 함량보다 과량으로 첨가되는 경우에는, 투명 펄 필름층의 펄이 관찰되지 않아 금속 질감을 구현하기 어려운 문제점이 있다.When added in excess of the above content, there is a problem in that it is difficult to realize a metallic texture because the pearl of the transparent pearl film layer is not observed.
특히, 상기 은폐잉크층은 바닥재의 표면에서 관찰되는 펄 안료의 반사효과와 광택효과를 영역마다 다르게 구성되도록 함으로써, 보다 자연스러운 금속 질감을 구현하게 하는 효과를 가진다.In particular, the hiding ink layer has the effect of realizing a more natural metal texture by configuring the reflection effect and the gloss effect of the pearl pigment observed on the surface of the flooring material differently for each area.
구체적으로, 상기 투명 펄 필름층에 분산된 펄 안료와 분산된 은폐잉크층의 분산된 은폐형 백색 안료가 어우러져 영역마다 다양한 반사효과와 광택효과를 부여하게 된다.Specifically, the pearl pigment dispersed in the transparent pearl film layer and the concealed white pigment dispersed in the dispersed hiding ink layer are mixed to provide various reflection and gloss effects for each area.
도 3은 본 발명의 또 다른 실시예에 따른 금속 질감 바닥재의 사진으로써, 기재층, 투명 펄 필름층, 은폐잉크층, 인쇄층 및 표면보호층을 포함하는 바닥재의 사진이다.3 is a photograph of a metal textured flooring material according to another embodiment of the present invention, and is a photograph of the flooring material including a base material layer, a transparent pearl film layer, a hiding ink layer, a printing layer, and a surface protection layer.
도 3을 참고하면, 상기 도 1과 대비하여, 바닥재 표면의 다양한 영역에서의 반사효과와 광택효과가 자연스럽게 나타남으로써, 자연스러운 금속 질감이 구현된다. Referring to FIG. 3 , in contrast to FIG. 1 , the reflection effect and the gloss effect in various areas of the surface of the flooring material appear naturally, thereby realizing a natural metallic texture.
표면필름층surface film layer
상기 인쇄층의 표면에는 표면필름층이 적층되는데, 상기 표면필름층은 바닥재의 인쇄층이 손상되지 않고, 미감을 유지하면서도, 바닥재의 투명 펄 필름층과 인쇄층을 투명하게 그대로 관찰할 수 있도록 유지하는 역할을 한다.A surface film layer is laminated on the surface of the print layer, and the surface film layer maintains the transparent pearl film layer and the printed layer of the flooring material so that the printed layer of the flooring material is not damaged and the printed layer is transparently observed while maintaining the aesthetics. plays a role
이에 따라, 상기 표면필름층은 내찰상성을 가지면서도 투명성을 가지는 소재를 사용하는 것이 바람직하다.Accordingly, it is preferable to use a material having transparency while having scratch resistance for the surface film layer.
이의 적층방법은 특별히 제한되지 않고 사용이 가능하며, 상기 표면필름층을 구성하는 혼합물을 블레이드 코팅, 브러쉬 코팅, 스프레이 코팅 등과 같은 다양한 방식에 의해 코팅할 수 있다.The lamination method thereof is not particularly limited and can be used, and the mixture constituting the surface film layer may be coated by various methods such as blade coating, brush coating, spray coating, and the like.
상술한 구성을 포함하는 본 발명에 따른 금속 질감 바닥재는 기존의 금속 질감 바닥재와 대비하여 더욱 자연스러운 금속 질감을 구현할 수 있다.The metal textured flooring according to the present invention including the above-described configuration can implement a more natural metal texture compared to the existing metal textured flooring.
구체적으로, 기존의 제한적인 메탈릭 펄 안료의 사용량에서는 구현할 수 없었던 외관 효과로서, 가시광선 영역의 빛 반사율이 LRV(Light Reflectance Value) 40 내지 80 %인 특징을 가져, 자연스러운 금속 질감을 구현한다. 바람직하게는, 상기 반사율은 바람직하게는, 50 내지 70%일 수 있다.Specifically, as an appearance effect that could not be realized with the conventional limited amount of metallic pearl pigment used, it has a light reflectance value of 40 to 80% LRV (Light Reflectance Value) in the visible region, realizing a natural metallic texture. Preferably, the reflectance may be 50 to 70%.
상기 반사율보다 높은 경우에는, 바닥재에서 반사되는 빛이 관찰자의 입장에서 밝게 느껴지게 되어 자연스러운 금속 질감이 떨어지고, 상기 반사율보다 낮은 경우에는 반사 효과가 미미하여, 금속 자체의 광택에 미치지 못하는 문제가 있어 상기 반사율 범위로 반사함으로써 자연스러운 금속 질감을 구현하게 된다.When the reflectance is higher than the reflectance, the light reflected from the flooring material feels bright from the observer's point of view and the natural metal texture is lowered. By reflecting in a range, a natural metallic texture is realized.
한편, 상기 빛의 반사율이 상기 범위보다 낮은 경우에도 마찬가지로, 금속 자체의 광택효과를 충분히 구현하지 못하게 되어, 금속 질감 효과가 미미한 것으로 인식될 수 있고, 상기 반사율보다 높은 경우에는, 반사효과가 과다하여 인위적인 금속 질감으로 관찰될 수 있는 문제점이 있다.On the other hand, even when the reflectance of the light is lower than the above range, the luster effect of the metal itself cannot be sufficiently realized, and the metal texture effect can be recognized as insignificant. There is a problem that can be observed as an artificial metal texture.
금속 질감 바닥재의 제조방법Manufacturing method of metal texture flooring
본 발명은 또한, 상술한 금속 질감 바닥재의 제조방법을 제공한다.The present invention also provides a method for manufacturing the above-described metal texture flooring.
구체적으로, 본 발명에 따른 금속 질감 바닥재의 제조방법은, a) 기재층의 표면에 투명 펄 필름층을 형성하는 단계, b) 상기 a) 단계에서 형성된 상기 투명 펄 필름층의 표면에 인쇄층을 형성하는 단계 및 c) 상기 b) 단계에서 형성된 인쇄층의 표면에 표면필름층을 형성하는 단계를 포함한다.Specifically, the method for manufacturing a metal textured flooring material according to the present invention comprises the steps of: a) forming a transparent pearl film layer on the surface of a base layer; b) forming a printed layer on the surface of the transparent pearl film layer formed in step a) and c) forming a surface film layer on the surface of the printed layer formed in step b).
본 발명에 따른 금속 질감 바닥재에 있어서, 각 구성에 대한 상세한 설명은 상술한 구성에 관한 설명을 참고할 수 있다.In the metal texture flooring material according to the present invention, detailed description of each configuration may refer to the description of the above-described configuration.
한편, 상기 a) 단계 후, 상기 b) 단계 전에 은폐잉크층을 형성하는 단계를 더 포함함으로써, 본 발명의 일 실시예에 따른 은폐잉크층을 추가로 포함하는 바닥재를 제조할 수 있다.On the other hand, by further comprising the step of forming a hiding ink layer before step b) after step a), it is possible to manufacture a flooring material further including a hiding ink layer according to an embodiment of the present invention.
기존의 금속 질감 바닥재의 제조과정의 경우, 기재층 표면에 인쇄층을 형성하고, 펄 안료를 인쇄한 후, 표면보호층을 형성하는 과정을 순차로 거치게 되는데, 본 발명의 경우, 기존의 방법과 유사하되, 기재층 표면에 투명 펄 필름층을 형성하고, 필요에 따라 그 표면에 은폐잉크층을 더 형성하는 단계를 더 포함함으로써 제조될 수 있다.In the case of the existing metal texture flooring manufacturing process, the process of forming a printed layer on the surface of the base layer, printing the pearl pigment, and then forming the surface protection layer is sequentially performed. In the case of the present invention, the conventional method and However, it may be prepared by forming a transparent pearl film layer on the surface of the base layer, and further comprising the step of further forming a hiding ink layer on the surface if necessary.
상기 투명 펄 필름층은 PVC 필름과 동일하게, 롤투롤 공정에서 필름을 언와인딩하여 합지함으로써 기재층의 상부에 적층되도록 도입될 수 있고, 상기 은폐잉크층은 인쇄층을 형성하는 인쇄기술을 이용하여 형성될 수 있다. 예를 들면, 인쇄층을 형성하기 위해 그라비아 인쇄를 이용하는 경우, 은폐잉크를 1도로 구성하여 은폐잉크층을 먼저 형성한 후, 그 표면에 컬러잉크로 그라비아 인쇄하는 과정으로 수행될 수 있다.The transparent pearl film layer can be introduced so as to be laminated on top of the base layer by unwinding and laminating the film in a roll-to-roll process in the same way as the PVC film, and the hiding ink layer uses a printing technology to form a printing layer. can be formed. For example, when gravure printing is used to form the printing layer, the hiding ink layer is first formed by composing the hiding ink in one degree, and then it may be carried out as a process of gravure printing with color ink on the surface.
이와 같이, 본 발명에 따른 금속 질감 바닥재 및 이의 제조방법은 기존 기술과 대비하여 바닥재의 구조 상의 큰 차이가 없고, 제조공정도 크게 상이하지 않다는 점에서, 제조효율성이 높고, 기존의 설비를 그대로 이용하여 제조할 수 있다는 장점을 가진다.As such, the metal texture flooring material and the manufacturing method thereof according to the present invention have high manufacturing efficiency in that there is no significant difference in the structure of the flooring material and the manufacturing process is not significantly different compared to the existing technology, and the existing equipment is used as it is. It has the advantage that it can be manufactured.
[제조예][Production Example]
하기 표 1을 참고하여, 바닥재를 제조하였다.With reference to Table 1 below, flooring was prepared.
(㎛)thickness
(μm)
3도 인쇄
(CMYK-잉크타입 4종)Acrylic resin + color ink,
3rd degree printing
(CMYK-ink type 4 types)
3도 인쇄
(CMYK-잉크타입 4종)
+ 골드펄 1도 인쇄(1 중량%)Acrylic resin + color ink,
3rd degree printing
(CMYK-ink type 4 types)
+ Gold pearl 1 degree printing (1% by weight)
3도 인쇄
(CMYK-잉크타입 4종)
+ 골드펄 1도 인쇄(6 중량%)Acrylic resin + color ink,
3rd degree printing
(CMYK-ink type 4 types)
+ Gold pearl 1 degree printing (6% by weight)
3도 인쇄
(CMYK-잉크타입 4종)Acrylic resin + color ink,
3rd degree printing
(CMYK-ink type 4 types)
(두께)Concealing Ink Layer
(thickness)
[바닥재 물성 평가][Evaluation of flooring properties]
1. 인쇄층과 표면필름층의 박리 강도 측정1. Measurement of peel strength between the printed layer and the surface film layer
바닥재를 폭 2.54 cm(1 inch), 길이 15 cm의 시편으로 제조하고 고속박리기(ChemInstruments社, AR-1000)를 이용하여 투명 펄 필름층과 기재층을 포함하는 기재를 수평 방향의 고속박리기 이동부에 부착하고, 표면필름층은 강도를 측정할 수 있는 센서가 부착된 고정부 집게에 고정한 후 300 cm/min의 속도로 수평 방향으로 이동부를 이동시키면서 표면필름층과 기재층의 양 쪽 부분에 걸리는 강도를 시간별로 측정하고 측정된 박리강도의 평균값을 계산하여 표 2에 나타냈다.The flooring material was prepared as a specimen of 2.54 cm (1 inch) in width and 15 cm in length, and using a high-speed peeler (ChemInstruments, AR-1000), the substrate including the transparent pearl film layer and the substrate layer was subjected to a horizontal high-speed peeling machine. It is attached to the moving part, and the surface film layer is fixed to the tongs of the fixed part with a sensor that can measure the strength, and then moves the moving part in the horizontal direction at a speed of 300 cm/min. The strength applied to the peel strength was measured by time, and the average value of the measured peel strength was calculated and shown in Table 2.
2. 바닥재 표면 물성 평가2. Evaluation of surface properties of flooring materials
바닥재 시편의 표면에 가시광선 영역(400 내지 700 nm)의 빛을 조사한 후, 반사율 측정기(CROMOCON社, CROMOCON LRV METER)를 이용하여 반사율을 측정하였다.After irradiating light in the visible region (400 to 700 nm) on the surface of the flooring specimen, the reflectance was measured using a reflectance meter (CROMOCON, CROMOCON LRV METER).
상기 표 1 및 2를 참고하면, 실시예에 따른 바닥재의 내구성이 가장 우수함을 확인할 수 있다. 즉, 인쇄층과 표면필름층 간의 박리강도가 높게 측정됨에 따라 바닥재가 층 분리없이 유지되어 내구성이 우수한 장점을 가진다.Referring to Tables 1 and 2, it can be seen that the durability of the flooring material according to the embodiment is the best. That is, as the peel strength between the printed layer and the surface film layer is measured to be high, the flooring material is maintained without layer separation, and thus has excellent durability.
이와 대비하여, 비교예 1 내지 2의 경우에는, 인쇄층에 메탈릭 펄 안료를 포함함에 따라, 바닥재의 박리강도가 떨어짐을 확인할 수 있다. 더욱이, 비교예 3의 경우, 인쇄층에 메탈릭 펄 안료를 과량으로 포함함에 따라 인쇄층과 표면필름층의 박리강도가 현저히 낮게 나타남을 확인할 수 있다.In contrast, in Comparative Examples 1 and 2, as the metallic pearl pigment was included in the printed layer, it could be confirmed that the peel strength of the flooring material was decreased. Moreover, in the case of Comparative Example 3, it can be confirmed that the peel strength of the printed layer and the surface film layer is significantly lower as the metallic pearl pigment is included in the printed layer in excess.
한편, 비교예 4의 경우에는, 바닥재의 내구성과 박리강도는 실시예와 유사한 수준이나, 투명 펄 필름층에 포함된 메탈릭 펄 안료의 함량이 현저하게 낮아, 메탈릭 펄 안료의 첨가에 따른 자연스러운 금속 질감을 구현하기 어려운 문제가 있다.On the other hand, in the case of Comparative Example 4, the durability and peeling strength of the flooring material was similar to that of the Example, but the content of the metallic pearl pigment contained in the transparent pearl film layer was remarkably low, and the natural metallic texture due to the addition of the metallic pearl pigment There is a problem that is difficult to implement.
비교예 5의 경우, 투명 펄 필름층의 메탈릭 펄 안료의 함량이 증가함에 따라 투명 펄 필름층을 형성하기 위한 혼합 조성물의 점도가 증가하여 필름층으로 성형하기 어려운 문제가 있었으며, 열과 압력을 가하여 필름 형태로 성형하여 바닥재를 제조하였으나, 하부의 기재층, 상부의 인쇄층과의 부착력이 떨어져 바닥재 자체의 내구성이 현저히 떨어지는 문제가 나타났다. 이는 인쇄층과 표면필름층의 낮은 박리강도 결과값과 일치되는 결과로서, 바닥재를 제조하기에는 부적합함을 알 수 있다.In the case of Comparative Example 5, as the content of the metallic pearl pigment in the transparent pearl film layer increased, the viscosity of the mixed composition for forming the transparent pearl film layer increased, so there was a problem in that it was difficult to form a film layer. Although the flooring material was manufactured by molding in a shape, the adhesion between the lower substrate layer and the upper printed layer was poor, and thus the durability of the flooring material itself was significantly reduced. This is a result consistent with the result of low peel strength of the printed layer and the surface film layer, and it can be seen that it is not suitable for manufacturing a flooring material.
비교예 6의 경우에는, 투명 펄 필름층의 두께가 얇아져, 필름 형태로 가공하는 것이 어려운 문제가 있었으며, 투명 펄 필름층 내의 메탈릭 펄 안료의 분산성이 저하되어, 금속 질감 향상 효과가 미미하였다. In the case of Comparative Example 6, the thickness of the transparent pearl film layer was thin, and there was a problem in that it was difficult to process it into a film form, and the dispersibility of the metallic pearl pigment in the transparent pearl film layer was lowered, and the effect of improving the metal texture was insignificant.
비교예 7의 경우에는, 투명 펄 필름층의 두께가 과도하여, 바닥재 전체 두께가 증가하고, 바닥재층이 평평하게 유지되지 못하고 컬이 형성되는 등, 바닥재의 품질이 저하되는 문제가 있었다.In the case of Comparative Example 7, the thickness of the transparent pearl film layer was excessive, and the overall thickness of the flooring material increased, and there was a problem in that the quality of the flooring material decreased, such as curls were formed without keeping the flooring layer flat.
또한, 비교예 8의 경우에는, 은폐잉크층의 두께가 두꺼워져 하부의 투명 펄 필름층의 메탈릭 펄 안료가 관찰되지 않는 문제가 있었으며, 이에 따라, 금속 질감 효과가 미미하게 나타나는 문제가 있었다.In addition, in the case of Comparative Example 8, there was a problem in that the thickness of the hiding ink layer was thickened and the metallic pearl pigment of the lower transparent pearl film layer was not observed.
Claims (9)
상기 투명 펄 필름층은 펄 안료를 포함하는 금속 질감 바닥재.
Including a base layer, a transparent pearl film layer, a printing layer and a surface film layer,
The transparent pearl film layer is a metal textured flooring comprising a pearl pigment.
상기 투명 펄 필름층은 상기 투명 펄 필름층의 전체 중량을 기준으로 펄 안료를 0.5 내지 5 중량%로 포함하는 금속 질감 바닥재.
According to claim 1,
The transparent pearl film layer is a metal textured flooring material comprising 0.5 to 5% by weight of a pearl pigment based on the total weight of the transparent pearl film layer.
상기 투명 펄 필름층은 두께가 0.05 내지 0.4 mm인 금속 질감 바닥재.
According to claim 1,
The transparent pearl film layer is a metal textured flooring having a thickness of 0.05 to 0.4 mm.
상기 투명 펄 필름층은 PVC 수지 및 메탈릭 펄 안료를 포함하는 금속 질감 바닥재.
According to claim 1,
The transparent pearl film layer is a metal textured flooring material comprising a PVC resin and a metallic pearl pigment.
상기 금속 질감 바닥재는 상기 투명 펄 필름층과 상기 인쇄층 사이에 은폐잉크층을 더 포함하는 금속 질감 바닥재.
According to claim 1,
The metal textured flooring material further comprising a hiding ink layer between the transparent pearl film layer and the printed layer.
상기 은폐잉크층은 이산화티탄, 산화아연 및 탄석으로 이루어진 군에서 선택된 하나 이상을 포함하는 금속 질감 바닥재.
6. The method of claim 5,
The hiding ink layer is a metal texture flooring material comprising at least one selected from the group consisting of titanium dioxide, zinc oxide, and coal.
상기 금속 질감 바닥재는 가시광선 영역의 빛 반사율이 40 내지 80 %인 금속 질감 바닥재.
According to claim 1,
The metal texture flooring material is a metal texture flooring material having a light reflectance of 40 to 80% in the visible region.
a) 기재층의 표면에 투명 펄 필름층을 형성하는 단계;
b) 상기 a) 단계에서 형성된 상기 투명 펄 필름층의 표면에 인쇄층을 형성하는 단계; 및
c) 상기 b) 단계에서 형성된 인쇄층의 표면에 표면필름층을 형성하는 단계;
를 포함하는 금속 질감 바닥재의 제조방법.
As a method for manufacturing the metal texture flooring according to claim 1,
a) forming a transparent pearl film layer on the surface of the base layer;
b) forming a printed layer on the surface of the transparent pearl film layer formed in step a); and
c) forming a surface film layer on the surface of the printed layer formed in step b);
A method of manufacturing a metal textured flooring comprising a.
상기 a) 단계 후, 상기 b) 단계 전에 은폐잉크층을 형성하는 단계를 더 포함하는 금속 질감 바닥재의 제조방법.9. The method of claim 8,
After step a), the method of manufacturing a metal texture flooring further comprising the step of forming a hiding ink layer before step b).