KR20130076356A - Interior films expressing metallic appearance and method of manufacturing where of - Google Patents

Interior films expressing metallic appearance and method of manufacturing where of Download PDF

Info

Publication number
KR20130076356A
KR20130076356A KR1020110144914A KR20110144914A KR20130076356A KR 20130076356 A KR20130076356 A KR 20130076356A KR 1020110144914 A KR1020110144914 A KR 1020110144914A KR 20110144914 A KR20110144914 A KR 20110144914A KR 20130076356 A KR20130076356 A KR 20130076356A
Authority
KR
South Korea
Prior art keywords
layer
film
pattern
thin film
metal
Prior art date
Application number
KR1020110144914A
Other languages
Korean (ko)
Other versions
KR101439590B1 (en
Inventor
하정은
남재광
이민호
신준범
Original Assignee
(주)엘지하우시스
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)엘지하우시스 filed Critical (주)엘지하우시스
Priority to KR1020110144914A priority Critical patent/KR101439590B1/en
Publication of KR20130076356A publication Critical patent/KR20130076356A/en
Application granted granted Critical
Publication of KR101439590B1 publication Critical patent/KR101439590B1/en

Abstract

PURPOSE: An interior film for implementing metallic appearance effect and a manufacturing method thereof are provided to implement metallic feel of various colors desired by consumers, as maintaining unique color and luminance of metallic appearance. CONSTITUTION: An interior film includes a base film (10), a pattern layer (20) and a metallic thin film layer (30). The pattern layer includes a cubic concave-convex pattern on the base film. The metallic thin film layer is formed on the pattern layer. According to a method for manufacturing the interior film, the base film is prepared. The pattern layer including the cubic concave-convex pattern is formed on the base film. The metallic thin film layer is formed on the pattern layer.

Description

금속외관 효과를 구현하는 인테리어 필름 및 그의 제조방법{INTERIOR FILMS EXPRESSING METALLIC APPEARANCE AND METHOD OF MANUFACTURING WHERE OF}BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an interior film,

본 발명은 금속 외관 효과를 구현하는 인테리어 필름 및 그의 제조방법에 관한 것으로 가전제품 및 다양한 분야의 금속 대체 용도 등에 적용이 가능하다.
The present invention relates to an interior film for realizing a metallic appearance effect and a method of manufacturing the same, and is applicable to household appliances and metal substitute applications in various fields.

금속외관에 대한 수요가 많음에도 불구하고 효과의 구현 및 가격, 물성 등의 제한 때문에 그 적용 사례가 많지 않다. 이에 필름상에서 금속외관 효과를 구현 하고자 하는 욕구가 늘고 있다. 현재 금속질감의 필름은 가격이 비싼 알루미늄 및 SUS 대체 용도로 철판 등에 사용되고 있으나 금속의 무게, 부식 등의 문제는 계속 야기되고 있는 실정이며 그 효과의 구현에 제한이 있다.
Despite the high demand for metal appearance, there are not many applications because of the implementation of the effect and the limitation of price and physical properties. Therefore, there is an increasing need to realize the metallic appearance effect on the film. Currently, metal-textured films are used for expensive aluminum and SUS alternatives for steel plates, but the problems of metal weight and corrosion are still being caused, and the implementation of such effects is limited.

대한민국 공개공보 제10-2006-0078530호에도 헤어라인 무늬가 형성된 PET필름과, 상기 헤어라인 무늬의 하부에 순차적으로 프라이머층과 알루미늄 증착층, 우레탄 접착제층, 열가소성 수지층으로 이루어지는 금속효과를 내는 고광택 시트에 대해서 기재하고 있기는 하나, 합성수지 필름과 금속증착막의 접착력을 증가시키기 위함만 개시하고 있을 뿐, 실제적으로 금속외관을 효과적으로 나타내는 인테리어 필름의 구조에 대해서는 나타나 있지 않다. Korean Patent Laid-Open Publication No. 10-2006-0078530 also discloses a PET film having a hairline pattern formed thereon, and a high gloss coating layer having a metallic effect comprising a primer layer, an aluminum deposition layer, a urethane adhesive layer and a thermoplastic resin layer sequentially below the hairline pattern Sheets are disclosed, but only to increase the adhesive force between the synthetic resin film and the metal vapor deposition film, but the structure of the interior film which effectively exhibits the metal appearance is not shown.

또한, 일반 금속층 및 기재필름을 포함하는 인테리어 필름의 경우 금속의 종류 및 두께에 따라 그 특성이 변하며, 그 컬러의 구현에 제한이 있어, 단순한 색상의 구현은 소비자의 심미적 욕구를 충족시키기에는 미흡하다. 또한, 내구성이 충족되지 않아 녹이나 부식으로부터 자유롭지 못하다.
In addition, in the case of an interior film including a general metal layer and a base film, the characteristics of the interior film vary depending on the kind and thickness of the metal, and the implementation of the color is limited, so that implementation of a simple color is insufficient to satisfy a consumer's aesthetic desire . Also, the durability is not satisfied and it is not free from rust and corrosion.

본 발명의 목적은 다양한 컬러 및 고휘도의 금속 질감 구현을 가능하게 하는 인테리어 필름을 제공하는 것이다.It is an object of the present invention to provide an interior film which enables the implementation of various color and high brightness metallic textures.

본 발명의 또 다른 목적은 헤어라인 구현이 다양하며, 금속 컬러 및 내구성 제어가 가능한 인테리어 필름의 제조방법을 제공하는 것이다.
It is still another object of the present invention to provide a method of manufacturing an interior film having various hair line implementations and capable of controlling metal color and durability.

상기 목적을 달성하기 위해, 기재필름 및 상기 기재필름 상에 입체적인 요철무늬를 포함하는 패턴층을 포함하고 상기 패턴층 상에 금속박막층을 포함하는 것을 특징으로 하는 인테리어 필름을 제공한다.
In order to achieve the above object, the present invention provides an interior film comprising a substrate film and a pattern layer including a three-dimensional concavo-convex pattern on the substrate film, and a metal thin film layer on the pattern layer.

또한 본 발명의 또 다른 목적을 달성하기 위하여, 기재필름을 마련하는 단계; 상기 기재필름 상에 입체적인 요철무늬를 포함하는 패턴층을 형성하는 단계; 상기 패턴층 상에 금속박막층을 형성하는 단계를 포함하는 것을 특징으로 하는 인테리어 필름의 제조방법을 제공한다.
According to another aspect of the present invention, there is provided a method of manufacturing a semiconductor device, Forming a pattern layer including a three-dimensional concave-convex pattern on the base film; And forming a metal thin film layer on the pattern layer.

본 발명의 인테리어 필름은 금속 질감 특유의 컬러 및 휘도감을 살리면서 소비자가 원하는 다양한 컬러의 금속 질감 구현이 가능하다. 또한, 내구성 부여를 통해 부식으로부터 자유로울 수 있다.The interior film of the present invention can realize a metal texture of various colors desired by consumers while taking advantage of color and brightness characteristic unique to the metal texture. In addition, it can be free from corrosion through durability.

또한 본 발명의 인테리어 필름의 제조방법을 통하여 헤어라인 효과가 부여된 패턴층을 포함함으로써 고급스러운 외관을 표현할 수 있는 인테리어 필름을 제공할 수 있다.
Also, the interior film of the present invention can provide a high quality appearance by including a pattern layer imparted with a hairline effect through the method of manufacturing an interior film of the present invention.

도 1은 본 발명의 금속박막층을 포함하는 인테리어 필름을 나타낸 것이다.
도 2는 본 발명의 펄코팅층을 포함하는 인테리어 필름을 나타낸 것이다.
도 3은 본 발명의 일실시예에 따른 인테리어 필름을 나타낸 것이다.
도 4 및 도 5는 본 발명의 또다른 실시예에 따른 인테리어 필름을 나타낸 것이다.
도 6은 본 발명의 인테리어 필름의 제조방법을 개략적으로 나타낸 것이다.Fig. 1 shows an interior film including the metal thin film layer of the present invention.
Fig. 2 shows an interior film comprising the perl coating layer of the present invention.
3 shows an interior film according to an embodiment of the present invention.
4 and 5 show an interior film according to another embodiment of the present invention.
Fig. 6 schematically shows a method for producing an interior film of the present invention.

본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 첨부되는 도면과 함께 상세하게 후술되어 있는 실시예들을 참조하면 명확해질 것이다. 그러나 본 발명은 이하에서 개시되는 실시예에 한정되는 것이 아니라 서로 다른 다양한 형태로 구형된 것이며, 단지 본 실시예들은 본 발명의 개시가 완전하도록 하며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이며, 본 발명의 청구항의 범주에 의해 정의될 뿐이다. 명세서 전체에 걸쳐 동일 참조 부호는 동일 구성요소를 지칭한다.
BRIEF DESCRIPTION OF THE DRAWINGS The advantages and features of the present invention, and the manner of achieving them, will be apparent from and elucidated with reference to the embodiments described hereinafter in conjunction with the accompanying drawings. However, it should be understood that the present invention is not limited to the disclosed embodiments, but is variously modified in various forms, and it is to be understood that these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the invention to those skilled in the art. And is merely defined by the scope of the claims of the present invention. Like reference numerals refer to like elements throughout the specification.

이하, 첨부도면을 참조하여 본 발명을 상세히 설명한다.
Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.

인테리어 필름Interior film

먼저 본 발명에 따른 금속외관 효과를 구현하는 인테리어 필름에 대한 살펴보면 다음과 같다.
First, an interior film for realizing the metallic appearance effect according to the present invention will be described as follows.

도 1은 참고하면, 금속외관 효과를 구현하는 인테리어 필름을 나타낸 것으로서, 위로부터 기재필름(10), 패턴층(20), 금속박막층(30)으로 구성된다.
Referring to FIG. 1, an interior film for realizing a metallic appearance effect is composed of a base film 10, a pattern layer 20, and a metal thin film layer 30 from above.

본 발명에서 사용되는 기재필름(10)은 바람직하게는 폴리에스테르, 염화비닐수지, 폴리프로필렌, 폴리에틸렌, 폴리아크릴레이트 등의 플라스틱 필름을 사용할 수 있다. 특히, 얇고(0.02∼0.2mm) 균일성 및 투명도가 우수한 폴리에틸렌테레프탈레이트 필름(PET)을 사용하면 패턴층의 요철무늬 효과와 금속이나 펄 효과를 더욱 선명하게 높일 수 있다.
The base film (10) used in the present invention is preferably a plastic film such as polyester, vinyl chloride resin, polypropylene, polyethylene, polyacrylate and the like. In particular, the use of a polyethylene terephthalate film (PET) which is thin (0.02 to 0.2 mm) and excellent in uniformity and transparency can improve the irregular pattern effect of the pattern layer and the metal or pearl effect more clearly.

본 발명의 인테리어 필름은 전술한 기재필름(10) 상에 형성되고, 입체적인 요철무늬를 포함하는 패턴층(20)을 포함한다. 상기 패턴층(20)은 자외선 경화형 수지층에 요철무늬를 부여한 층으로 본 발명의 경우, 입체적인 요철무늬를 통해 금속박막층의 난반사 효과의 구현이 가능하게 해준다.
The interior film of the present invention is formed on the above-described base film 10 and includes a pattern layer 20 including a three-dimensional concave-convex pattern. The pattern layer 20 is a layer provided with a concave-convex pattern on an ultraviolet curable resin layer. In the case of the present invention, it is possible to realize a diffused reflection effect of a metal thin film layer through a three-dimensional irregular pattern.

본 발명의 패턴층(20)이 포함하는 자외선 경화형 수지층은 폴리우레탄, 폴리아크릴레이트 등의 올리고머와 모노머, 광개시제, 기타 물성을 보완해주는 첨가제로 구성된 자외선 경화형 수지조성물로 형성할 수 있으며, 상기 자외선 경화형 수지조성물은 엠보싱 롤과 같은 금형에 형성된 무늬와 동일한 무늬를 형성시키기 위해서는 용제를 첨가하지 않은 수지 조성물(고형분 100%)을 사용하는 것이 바람직하다. 상기 자외선 경화형 수지층은 그 위에 형성되는 요철무늬의 두께를 고려하여 형성하는 것이 바람직하다.
The ultraviolet curable resin layer included in the pattern layer 20 of the present invention may be formed of an ultraviolet curing resin composition composed of an oligomer such as polyurethane, polyacrylate and the like, and an additive to complement a monomer, a photoinitiator and other physical properties. In the curable resin composition, it is preferable to use a resin composition (solid content: 100%) in which a solvent is not added in order to form the same pattern as a pattern formed on a mold such as an embossing roll. The ultraviolet curable resin layer is preferably formed in consideration of the thickness of the concavo-convex pattern formed thereon.

자외선 경화형 수지조성물은 엠보싱 롤과 같은 금형에서 필름을 이형시킬때 이형력을 좋게 하기 위해서는 금속과 부착력이 없을수록 유리하고, 표면장력이 낮을수록 유리하다. 그러나 본 발명의 인테리어 필름은 패턴층(20) 상에 금속박막층을 포함하고 있는바, 상기 인테리어 필름 제품의 부착을 유지할 수 있고, 금형에서의 이형이 가능한 수준의 범위로 이형력을 유지하는 것이 바람직하다. The ultraviolet ray hardening type resin composition is advantageous as it has no adherence to metal in order to improve releasing force when a film is released from a mold such as an embossing roll, and the lower the surface tension is, the more advantageous it is. However, since the interior film of the present invention includes a metal thin film layer on the pattern layer 20, it is preferable to keep the adhesion of the interior film product and to maintain the releasing force within a range of possible mold release in the mold Do.

아울러, 상기 자외선 경화형 수지 조성물의 표면 경도를 올리려면 경화된 수지의 가교가 많을수록 경도가 강해지므로 상기 자외선 경화형 수지조성물를 구성하는 모노머를 다관능기를 사용해야 하나, 관능기의 수가 많아질수록 치수안정성, 신율, 굴곡성은 나빠지고, 굴곡 성형시 Crack등의 문제가 발생할 수 있으므로 적정한 관능기의 모노머를 사용해야 한다.
Further, in order to increase the surface hardness of the ultraviolet ray hardening type resin composition, the hardness becomes stronger as the hardening of the hardening resin increases, so that the monomers constituting the ultraviolet ray hardening type resin composition must use a multifunctional group. However, as the number of functional groups increases, Flexibility is deteriorated and problems such as cracks may occur during bending molding, so proper monomer of functional group should be used.

상기 자외선 경화형 수지조성물를 구성하는 광개시제는 통상적인 것으로서 예를 들면, Irgacure184와 같은 광개시제를 사용할 수 있고, Tinuvin400과 같은 광안정제를 병용할 수 있다.
The photoinitiator constituting the ultraviolet-curable resin composition is conventional one, for example, a photoinitiator such as Irgacure 184 can be used, and a light stabilizer such as Tinuvin 400 can be used in combination.

본 발명의 패턴층(20)은 상기 자외선 경화형 수지층에 요철무늬를 부여한 층으로 상기 패턴층(20)은 헤어라인 패턴을 포함할 수 있다.
The pattern layer 20 of the present invention is a layer to which a concave-convex pattern is imparted to the ultraviolet curable resin layer, and the pattern layer 20 may include a hairline pattern.

종래의 헤어라인층은 기재인 플라스틱 필름의 길이 방향과 평행한 일방향 헤어라인이 전부였기 때문에, 필름의 금속 표면에 근접한 질감을 구현하기에는 한계를 가지고 있는 것에 반해, 본 발명의 패턴층(20)은 상기 자외선 경화층에 기존 일방향 헤어라인 패턴만이 아닌 다양한 형상의 헤어라인 패턴을 구현할 수 있다.
Since the conventional hairline layer has all the one-directional hair lines parallel to the longitudinal direction of the plastic film as the substrate, the pattern layer 20 of the present invention has a limit to realize a texture close to the metal surface of the film, The hairline pattern of various shapes other than the existing unidirectional hairline pattern can be implemented in the ultraviolet ray hardening layer.

본 발명에서 구현이 가능한 헤어라인 패턴의 예로는 필름 길이 방향에 대해 수직 방향으로 형성된 헤어라인, 다방향 헤어라인, 무방향 헤어라인 및 원형 헤어라인의 일종 또는 이종 이상의 조합을 들 수 있다. 본 발명에서는 이와 같은 다양한 형상의 패턴을 구현함으로써, 기존 금속 소재의 필름과 대등한 금속 질감을 나타내는 인테리어 필름을 제공할 수 있다.
Examples of the hair line pattern that can be implemented in the present invention include a hair line formed in a direction perpendicular to the longitudinal direction of the film, a multi-directional hair line, a non-directional hair line, and a circular hair line. In the present invention, it is possible to provide an interior film exhibiting a metal texture comparable to a film of a conventional metal material by implementing the patterns of various shapes as described above.

상기 다방향 헤어라인은 단방향 헤어라인이 기재필름 상에서 여러 방향으로 무늬를 구현하고 있는 패턴을 의미한다. 상기 단방향 헤어라인은 그 깊이와 폭이 매우 가는 선이 상기 기재필름 상에서 단방향(기재 필름의 길이방향, 폭방향 또는 기타 방향)으로 무늬를 형성하고 있는 패턴을 의미한다. 즉, 상기 다방향 헤어라인이란 하나 이상의 단방향 헤어라인의 복합 패턴을 의미하고, 이 때 각 헤어라인의 형성 방향은 동일하거나 상이할 수 있다.
The multi-directional hair line refers to a pattern in which a unidirectional hair line implements patterns in various directions on a base film. The unidirectional hair line means a pattern in which a very thin line having a depth and a width form a pattern in a unidirectional direction (longitudinal direction, width direction, or other direction of the base film) on the base film. That is, the multi-directional hairline refers to a composite pattern of one or more unidirectional hair lines, wherein the direction of formation of each hairline may be the same or different.

또한, 상기 무방향 헤어라인은 직선 형상의 헤어라인이 아닌 곡선 형상의 헤어라인에 의해 무늬가 구현된 패턴을 의미하여, 상기 헤어라인은 파형, 타원 형상일 수 있다. 아울리 상기 원형 헤어라인은 가는 스크래치가 원형을 이루는 패턴으로서, 형성되는 원의 크기의 목적하는 효과에 따라 다양하게 구현될 수 있다.
In addition, the non-directional hair line refers to a pattern in which a pattern is implemented by a curved hair line, not a linear hair line, and the hair line may have a waveform or an elliptical shape. The circular hair line is a pattern in which a thin scratch is a circular pattern, and can be variously implemented according to a desired effect of the size of a circle to be formed.

본 발명의 헤어라인은 원하는 형태의 외관에 따라 패턴층(20)의 두께 및 요철무늬의 깊이를 조절할 수 있다. 보다 구체적으로, 헤어라인 패턴의 입체감을 살리고자 하는 경우, 미려한 헤어라인의 외관을 얻고자 하는 경우 깊이를 선택하여 헤어라인을 형성시킬 수 있다.
The hair line of the present invention can control the thickness of the pattern layer 20 and the depth of the concave / convex pattern depending on the appearance of the desired shape. More specifically, in order to obtain a three-dimensional effect of the hair line pattern, it is possible to form a hair line by selecting the depth when the appearance of a beautiful hair line is desired.

본 발명의 인테리어 필름에서는 또한, 보다 금속과 유사한 질감을 구현하기 위하여, 금속 색감을 표현하기 위한 금속박막층(30)을 입체적인 요철무늬를 포함하는 패턴층 상에 포함할 수 있다. In the interior film of the present invention, the metal thin film layer 30 for expressing the metal color tone may be included on the pattern layer including the three-dimensional uneven pattern so as to realize a more metal-like texture.

본 발명의 금속박막층(30)은 단층 또는 다층의 금속이 증착될 수 있다. 특히 본 발명의 인테리어 필름은 다층의 금속이 증착된 금속박막층을 포함함으로써, 증착막 제어를 통해 다양한 컬러감 및 금속 특유의 휘도감으로 필름에 금속질감을 부여할 수 있다.
The metal thin film layer 30 of the present invention can be deposited with a single layer or a multilayer metal. In particular, since the interior film of the present invention includes a metal thin film layer on which a plurality of metal layers are deposited, the metal texture can be imparted to the film with various color sensations and unique metal feel through the control of the deposition film.

금속박막층(30)은 단일의 금속박막층으로 구성될 수도 있으나, 단일 금속 박막층으로 금속질감을 구현하는 경우, 금속의 종류 및 두께에 따라 그 특성이 변하며, 상기 단일 금속 박막층(30)이 너무 얇으면 금속성이 떨어지거나 색이 어두워져 본연의 금속 색상과는 차이가 있으며, 상기 단일 금속 박막층이 너무 두꺼우면 금속층의 부착성이 떨어져 막이 박리되거나 최종 제품의 내구성을 내기가 어려운 문제가 있었다.
The metal thin film layer 30 may be composed of a single metal thin film layer. However, when the metal thin film layer is formed of a single metal thin film layer, its characteristics vary depending on the kind and thickness of the metal. If the single metal thin film layer 30 is too thin There is a problem in that the metallic layer is deteriorated and the color becomes dark to be different from the original metal color. If the single metal thin film layer is too thick, the adhesion of the metal layer is deteriorated and the film is peeled off or the durability of the final product is difficult to be obtained.

그러므로, 다층의 금속이 증착된 금속박막층을 포함하는 것도 가능하다. 이로 인하여, 증착률 및 컬러 제어를 통해 일반 단일 금속 박막층을 포함하는 인테리어 필름 대비 고급스러운 외관을 지녀 금속 외관 효과를 나타낼 수 있으며, 다양한 컬러 및 고휘도의 금속 질감 구현이 가능하다. Therefore, it is also possible that the multi-layered metal includes the deposited metal thin film layer. Accordingly, the metal film can have a metallic appearance due to its high quality appearance compared to an interior film including a general single metal thin film layer through deposition rate and color control, and it is possible to realize various color and high brightness metallic texture.

본 발명의 인테리어 필름이 다층의 금속이 증착된 금속박막층을 포함하는 경우, 상기 금속박막층의 두께는 nm단위로, 완제품의 사용용도에 따라 그 특징을 달리 하여 제조할 수 있는바, 상기 금속박막층에 대한 두께의 제한이 없다.
When the interior film of the present invention includes a metal thin film layer on which a multilayered metal is deposited, the thickness of the metal thin film layer can be manufactured in a unit of nm in accordance with the intended use of the finished product. There is no limitation on the thickness.

이 때 상기 금속박막층(30)은 금속질감을 부여하는 층으로 미려하고 독특한 색상을 부여할 목적으로 적용되며, 상기 금속박막층(30)은 알루미늄, 스테인리스, 스틸, 구리, 금, 은, 니켈, 크롬 또는 코발트 등을 1종 또는 2종 이상 포함할 수 있으나, 구현하고자 하는 금속 질감 효과에 따라 다양하게 변형될 수 있다.
The metal thin film layer 30 may be formed of a metal such as aluminum, stainless steel, steel, copper, gold, silver, nickel, chromium Or cobalt, but they can be variously modified depending on the metal texture effect to be implemented.

아울러, 상기 금속박막층(30)은 상기 패턴층(20)의 패턴의 이미지를 부각시키고 금속 특유의 질감을 느낄 수 있도록 하는 효과 이외에도, 상기 패턴층(20)의 이미지가 보는 각도에 따라서 다양한 색상으로 보일 수 있도록 한다. 상기 패턴층(20)을 통과하여 금속박막층(30)의 표면에서 반사되는 빛의 파장이 입사되는 빛의 파장에 따라 변화되기 때문이다.
In addition to the effect of enhancing the image of the pattern of the pattern layer 20 and allowing the metal layer 30 to feel the unique texture of the metal layer 30, So that it can be seen. The wavelength of light reflected from the surface of the metal thin film layer 30 after passing through the pattern layer 20 changes according to the wavelength of the incident light.

본 발명에 따른 금속박막층 대신에 펄코팅층을 포함하는 인테리어 필름 또한 제공하는바, 도 2를 참고하면, 펄코팅층을 포함하는 인테리어 필름을 나타낸 것으로서, 위로부터 기재필름(10), 패턴층(20), 펄코팅층(31)으로 구성된다.
2, an interior film including a perl coating layer is shown. The interior film includes a base film 10, a pattern layer 20, , And a pearl coating layer (31).

상기 펄코팅층(31)은 상기 패턴층(20)에 특정무늬가 인쇄되지 않았을 때 어떤 형상의 무늬를 인쇄하여 심미감을 향상시키거나, 그렇지 않으면 펄(Pearl) 효과를 내는 코팅층을 형성시켜 인테리어 효과를 극대화시키기 위한 층이다. 펄 코팅층(31)이 패턴층(20)상에 위치하고, 기재필름(10)이 최종 인테리어 필름의 상층에 위치함에 따라 상기 펄 코팅층(31)이 어느 정도 은폐력을 주면서 패턴층의 난반사 효과를 상기 기재필름(10)에 반사시킬 수 있다. 펄 코팅층(31)의 은폐효과는 원하는 외관 효과에 따라 조절이 가능하며, 이때에는 거울효과를 나타내는 미러펄 또는 알루미늄 페이스트 등을 사용할 수 있다.
The pearl coating layer 31 may be formed by forming a coating layer on the pattern layer 20 to improve the aesthetic sensation or to produce a pearl effect when the pattern layer 20 is not printed with a specific pattern, It is a layer to maximize. The perfluororescent effect of the pattern layer is imparted to the substrate 30 while the perl coating layer 31 is placed on the pattern layer 20 and the base film 10 is positioned on the upper layer of the final interior film, It can be reflected to the film 10. The concealing effect of the perl coating layer 31 can be adjusted according to a desired appearance effect. In this case, a mirror pearl or aluminum paste showing a mirror effect can be used.

아울러, 펄코팅층(31)에 사용되는 펄 물질은 천연진주, 염기성 탄산염, 옥시염화 비스머스 (bismuth oxychloride), 산화티탄/마이카계 등이 있지만, 기계적 강도나 화학적 안정성, 내광(후)성, 경제성, 안정성 등을 고려하여 산화티탄/마이카계를 사용하는 것이 바람직하다.The pearl material used in the perl coating layer 31 is natural pearls, basic carbonates, bismuth oxychloride, titanium oxide / mica, etc. However, the pearl material used in the perl coating layer 31 has mechanical strength, chemical stability, , It is preferable to use a titanium oxide / mica system in consideration of stability and the like.

상기 산화티탄/마이카계 펄 안료의 구체적인 예로는 마이카 아이런 옥사이드, 마이카 아이런 옥사이드 티타늄 디옥사이드, 마이카 티타늄 디옥사이드 페릭 페로 시아나이드, 마이카 티타늄 디옥사이드 아이런 옥사이드 카민, 마이카 티타늄 디옥사이드 카민 및 마이카 티타늄 디옥사이드 크로늄 옥사이드 중에서 선택된 1종 이상을 언급할 수 있다.
Specific examples of the titanium oxide / mica based pearl pigment include, for example, mica iron oxide, mica iron oxide titanium dioxide, mica titanium dioxide ferric ferrocyanide, mica titanium dioxide iron oxide camine, mica titanium dioxide camphor and mica titanium dioxide chromium oxide One or more species may be mentioned.

본 발명의 인테리어 필름은 패턴층상에 접착제층 및 착색플라스틱필름이 차례로 적층된 것을 특징으로 한다. 도 3을 참고하면, 위로부터 기재층(10), 패턴층(20), 금속박막층(30), 접착제층(40), 착색플라스틱필름(50)으로 구성된다.
The interior film of the present invention is characterized in that an adhesive layer and a colored plastic film are sequentially stacked on a pattern layer. 3, the base layer 10, the pattern layer 20, the metal thin film layer 30, the adhesive layer 40, and the colored plastic film 50 are formed from above.

상기 금속박막층(30) 또는 펄코팅층(31) 위에 형성되는 접착제층(40)은 폴리우레탄 혹은 폴리에스테르 등의 접착제를 사용하여 콤마 코팅법으로 5∼10㎛ 두께로 도포하여 형성할 수 있고, 불투명층으로 형성함으로써 보다 선명한 입체감을 연출시킬수 있다. 경우에 따라 마이크로그라비아 코팅법으로 상기 접착제층(40)의 도포가 가능하다. 본 발명에서 상기 접착층을 불투명층으로 형성할 경우에는 상기 접착제에 안료가 첨가될 수 있다.
The adhesive layer 40 formed on the metal thin film layer 30 or the pearl coating layer 31 may be formed by applying an adhesive such as polyurethane or polyester to a thickness of 5 to 10 μm by a comma coating method, Layer, it is possible to produce a clearer three-dimensional effect. In some cases, the adhesive layer 40 can be applied by microgravure coating. In the present invention, when the adhesive layer is formed of an opaque layer, a pigment may be added to the adhesive.

상기 착색 플라스틱필름(50)은 금속박막층(30) 또는 펄코팅층(31)을 보호하고, 내후성과 내구성을 더욱 보완하기 위한 구성으로서 그 재질은 특별히 한정되지는 않지만 폴리에스테르 필름, 폴리염화비닐, 또는 폴리에스테르/폴리염화 비닐 복합필름이나 폴리에스테르/폴리프로필렌, 폴리에스테르/폴리에틸렌 등의 복합필름이 바람직하며, 특히 폴리에스테르를 함유하는 필름이 바람직하다. 상기 착색 플라스틱필름(50)은 그 두께가 특별히 한정되지는 않지만 0.05~0.3mm의 것을 사용하는 것이 바람직하고, 염화비닐의 경우, 레진의 중합도가 800∼1300정도의 염화비닐 수지에 가소제를 15∼25부, 안정제를 2∼4부, 다양한 색상을 부여하기 위하여 유기 및 무기안료, 금속색상을 부여하기 위한 알루미늄, Mica Pearl 등을 첨가하여 생산된 착색필름을 적용하는 것이 바람직하다.
The colored plastic film 50 protects the metal thin film layer 30 or the pearl coating layer 31 and further improves weather resistance and durability. The material is not particularly limited, but a polyester film, a polyvinyl chloride film, A composite film of a polyester / polyvinyl chloride composite film or a polyester / polypropylene film or a polyester / polyethylene film is preferable, and a film containing a polyester is particularly preferable. Although the thickness of the colored plastic film 50 is not particularly limited, it is preferably 0.05 to 0.3 mm. In the case of vinyl chloride, the vinyl chloride resin having a polymerization degree of resin of about 800 to 1300, 25 parts by weight of a stabilizer, 2 to 4 parts by weight of a stabilizer, and organic and inorganic pigments for imparting various colors, aluminum for imparting metallic color, Mica Pearl, and the like.

본 발명에 따른 금속박막층(30)을 포함하는 인테리어 필름은 상기 접착제층(40)에 80∼150℃의 열을 가하여 라미네이션롤로 상기 착색 플라스틱필름(50)을 합판시켜 제조할 수 있고, 이를 철판, 목재, 건물 벽체 등에 접착제를 도포하여 접착시킴으로써 가전제품 외장재 및 건물 내부 및 외부 그리고 가구 등의 장식용 마감재로 적용이 가능하다.
The interior film including the metal thin film layer 30 according to the present invention can be manufactured by applying heat to the adhesive layer 40 at a temperature of 80 to 150 캜 and laminating the colored plastic film 50 with a lamination roll, It can be applied to exterior materials for household appliances, interior and exterior of buildings, and decorative finishing materials such as furniture by applying adhesives to wood and building walls.

도 4를 참조하면, 본 발명의 금속박막층(30)을 표면에 산화방지층(40)을 추가로 포함할 수 있다. 상기 산화방지층(40)이 추가됨으로써 금속의 부식을 막을 수 있고, 시간이 경과하여도 금속느낌을 그대로 살려주며 특유의 휘도감을 발휘하여 금속 질감을 나타낼 수 있다. 보다 구체적으로는 산화방지층은 SiO2, TiO2, AlO3 등의 금속산화물을 포함할 수 있으며, 금속박막층에 영향을 줄 수 있는 수분을 차단하여, 금속의 산화방지 또는 표면 물성을 강화할 수 있다.
Referring to FIG. 4, the metal thin film layer 30 of the present invention may further include an antioxidant layer 40 on its surface. By the addition of the antioxidant layer 40, the corrosion of the metal can be prevented, and the metal feel can be maintained even after a lapse of time. More specifically, the antioxidant layer may include a metal oxide such as SiO 2 , TiO 2 , AlO 3, or the like, and may block moisture that may affect the metal thin film layer, thereby preventing oxidation of the metal or enhancing surface properties.

본 발명의 인테리어 필름은 기재필름(10)을 보호하기 위하여 기재필름(10) 상부에 하드코팅층(70)을 포함할 수 있는바, 상기 하드코팅층(70)과 상기 기재필름(10) 사이에 제 1 프라이머층(81)을 추가로 포함하는 것을 특징으로 한다 The interior film of the present invention may include a hard coating layer 70 on the base film 10 to protect the base film 10 and may include a hard coating layer 70 between the hard coating layer 70 and the base film 10 1 < / RTI > primer layer < RTI ID = 0.0 >

또한 상기 기재필름(10)과 상기 패턴층(20) 사이에 제 2프라이머층(82)을 추가로 포함할 수 있다.
Further, a second primer layer 82 may be additionally provided between the base film 10 and the pattern layer 20.

도 5를 참고하면, 본 발명의 인테리어 필름은 위로부터 하드코팅층(70), 제 1프라이머층(81), 기재필름(10), 제 2프라이머층(82), 패턴층(20), 금속층(30), 접착제층(40), 착색플라스틱필름(50)을 포함할 수 있다.
5, the interior film of the present invention comprises a hard coating layer 70, a first primer layer 81, a base film 10, a second primer layer 82, a pattern layer 20, a metal layer 30, an adhesive layer 40, and a colored plastic film 50.

상기 하드코팅층(70)은 자외선 경화형 수지를 사용한 것으로 기재필름(10)에 스크래치가 발생되는 것을 방지하기 위한 목적으로 형성되는 것으로, 바람직하게는 마이크로 그라이바(Micro Gravure) 코팅을 이용하여 형성한다.The hard coating layer 70 is formed by using an ultraviolet curable resin and is formed for the purpose of preventing scratches on the base film 10, and is preferably formed using a micro gravure coating.

이 때, 상기 하드 코팅층(70)은 아크릴계, 우레탄계, 에폭시계 및 실록산계 폴리머 재질 중 1종 이상을 사용할 수 있고, 또한 올리고머(oligomer)와 같은 자외선 경화 수지를 사용할 수 있다. 또한, 상기 하드 코팅층(70)은 강도 향상 및 기계적 물성의 보완을 위하여 실리카(silica)계의 필러를 더 포함할 수도 있다.At this time, the hard coating layer 70 may use at least one of acrylic, urethane, epoxy, and siloxane polymer materials, and an ultraviolet curable resin such as an oligomer may be used. In addition, the hard coating layer 70 may further include a silica-based filler to improve strength and mechanical properties.

이때, 상기 하드 코팅층(70)은 1~5㎛의 두께로 형성하는 것이 좋다. 만약, 하드 코팅층(70)의 두께가 1㎛ 미만일 경우에는 스크래치 방지 효과가 미미할 수 있고, 반대로 하드 코팅층(70)의 두께가 5㎛를 초과할 경우에는 필요 이상의 두께로 형성되는 데 따른 생산 비용의 상승 문제가 발생할 수 있다.
At this time, it is preferable that the hard coat layer 70 is formed to a thickness of 1 to 5 탆. If the thickness of the hard coating layer 70 is less than 1 占 퐉, the effect of preventing scratches may be insufficient. On the other hand, if the thickness of the hard coating layer 70 exceeds 5 占 퐉, Rising problems can occur.

상기 제 1프라이머층(81)은 하드코팅층(70)과 기재필름(10)사이에 위치하는바 상기 하드코팅층(70)과 상기 기재필름(10)의 부착력을 증대시키는 역할을 한다. 상기 제 2프라이머층(82)은 기재필름(10)과 패턴층(20) 사이에 위치하는바 상기 기재필름(10)과 상기 패턴층(20)의 부착력을 증대시키기 위함이다. 이 때, 제 1프라이머층(81) 또는 제 2프라이머층(82)의 목적을 달성할 수 있는 범위내에서, 그 두께는 특별히 제한되지 않는다.
The first primer layer 81 is positioned between the hard coating layer 70 and the base film 10 and functions to increase the adhesion between the hard coating layer 70 and the base film 10. The second primer layer 82 is positioned between the base film 10 and the pattern layer 20 in order to increase adhesion between the base film 10 and the pattern layer 20. In this case, the thickness of the first primer layer 81 or the second primer layer 82 is not particularly limited within a range that can achieve the object.

인테리어 필름 제조방법 How to make interior film

도 6은 본 발명의 인테리어 필름의 제조방법을 단계별로 나타낸 것으로, 기재필름을 마련하는 단계(S10), 상기 기재필름 상에 입체적인 요철무늬를 포함하는 패턴층을 형성하는 단계(S20), 상기 패턴층 상에 금속박막층을 형성하는 단계(S30)를 포함할 수 있다.
FIG. 6 is a view showing a step of manufacturing the interior film according to the present invention. FIG. 6 is a view showing a step (S10) of preparing a base film, a step S20 of forming a pattern layer including three- And forming a metal thin film layer on the layer (S30).

상기 기재필름을 마련하는 단계(S10)는 기재필름(10)의 표면을 UV 코팅 하는 단계를 포함함으로써 내스크래치성과 필름 경도를 증가시킬 수 있다. 상기 UV코팅이란 자외선 조사에 의해 단시간에 경화되는 도료를 이용하여 피도물을 코팅하는 방법으로서 일반 우레탄 도료에 비하여 경도, 내화학성, 내부식성 등이 강하다. 이에 의해, 기재필름(10)의 내스크래치성을 높이고 필름의 경도를 증가시킬 수 있다.
Step S10 of providing the base film may include UV coating the surface of the base film 10 to increase scratch resistance and film hardness. The UV coating is a method of coating a substrate using a coating which is cured in a short time by irradiation with ultraviolet rays, which is stronger in hardness, chemical resistance and corrosion resistance than a general urethane coating. As a result, the scratch resistance of the base film 10 can be enhanced and the hardness of the film can be increased.

상기 패턴층을 형성하는 단계(S20)는 상기 패턴층(20)에 헤어라인 패턴을 구현하는 단계를 포함하는 것을 특징으로 한다. The step of forming the pattern layer (S20) includes the step of embodying a hair line pattern on the pattern layer (20).

상기 패턴층(20)에 헤어라인 패턴을 구현하는 단계는 요철무늬를 포함하는 Hard Roll과 UV램프 사이에 자외선 경화형 수지를 주입함과 동시에 UV램프를 가동시켜 1차로 가경화하는 단계를 포함한다. 상기 Hard Roll은 금속소재의 Roll로써, 금속재질의 금형롤에 헤어라인 또는 패턴등의 무늬를 형성시킨 것으로 볼 수 있다. 그 후 별개의 UV램프에 의한 2차 경화를 통하여 요철무늬를 포함하는 완전한 패턴층을 형성할 수 있다.
The step of embodying a hair line pattern in the pattern layer 20 includes injecting an ultraviolet curable resin between a hard roll including a concavo-convex pattern and a UV lamp, and simultaneously activating the UV lamp. The Hard Roll is a roll of metal material, and it can be seen that a pattern such as a hair line or a pattern is formed on a metal mold roll. Then, a complete pattern layer including the concave-convex pattern can be formed through secondary curing by a separate UV lamp.

상기 요철무늬를 포함하는 Hard Roll에는 헤어라인 무늬가 형성되어 있어 본 발명이 목적하는 헤어라인 패턴을 포함하는 패턴층을 포함할 수 있다. 이 때, 상기 Hard Roll과 UV램프 사이에 주입된 자외선 경화형 수지는 전술한 자외선 경화형 수지 조성물을 포함한다.
The hard roll including the concavo-convex pattern may include a pattern layer having a hairline pattern and including a desired hairline pattern of the present invention. At this time, the ultraviolet curable resin injected between the hard roll and the UV lamp includes the ultraviolet curable resin composition described above.

종래에는 입체무늬를 구현하기 위하여 기재필름을 사포롤을 통화시킴으로써, 상기 사포롤에 의한 긁힘을 이용하여 세로방향의 헤어라인 패턴을 구현하였는바, 이 때 사포롤은 표면이 거칠게 가공된 사포를 롤에 감아 기재필름을 긁는 역할을 하였다. Conventionally, in order to realize a three-dimensional pattern, the base film is contacted with a sandpaper so that a scratching by the sandpaper roll is used to realize a hairline pattern in the longitudinal direction. In this case, the sandpaper, To thereby scratch the substrate film.

그러나, 이에 반해 본 발명은 기재필름을 가로선이 구현된 Hard Roll을 통과시킴으로써, 상기 기재필름과 Hard Roll 사이에 자외선 경화형 수지를 주입하여, 상기 자외선 경화형 수지가 가로 라인을 형성할 수 있게 한다. 이로 인하여, 상기 Hard Roll에 어떠한 입체무늬가 새겨져 있는 지에 따라 헤어라인의 길이를 조절 할 수 있으며, 종래의 세로 헤어라인 뿐 아니라 가로 헤어라인의 구현이 가능하다.
On the other hand, in the present invention, the base film is passed through a hard roll having a horizontal line, so that an ultraviolet curable resin is injected between the base film and the hard roll so that the ultraviolet curable resin can form a horizontal line. Accordingly, it is possible to adjust the length of the hair line according to whether a solid pattern is engraved on the hard roll, and a vertical hair line as well as a conventional vertical hair line can be realized.

상기와 같이 제조된 패턴층(20)상에 금속박막층을 형성하는 단계(S30)는 상기 패턴층(20) 표면에 알루미늄, 스테인리스 스틸, 구리, 금, 은, 니켈, 크롬 및 코발트로 이루어진 군으로부터 선택된 하나 이상을 포함하는 금속을 단층 또는 다층으로 증착하여 형성하는 것을 특징으로 한다. The step S30 of forming the metal thin film layer on the pattern layer 20 as described above may be performed by forming a metal thin film layer on the pattern layer 20 from the group consisting of aluminum, And a metal containing at least one selected is deposited and formed as a single layer or a multilayer.

금속박막층(30)을 형성하는 방법은 특별히 한정되지 않으며, 예를 들면, 전술한 금속 소재를 사용한 진공열 증착 공법 또는 스퍼터링 공법으로 형성할 수 있으며, 이 때 상기 공법의 조건은 특별히 한정되지 않는다. 상기 금속박막층의 두께 및 광투과율 또한 특별히 한정되지 않으며, 목적하는 효과에 따라 적절히 선택되면 된다. 아울러, 금속박막층을 다층으로 형성하는 경우, 증착율 또는 은폐율을 조절할 수 있으나, 완제품 사용 용도에 따라 그 특징을 달리하여 제조할 수 있는바, 특별히 한정하지 않는다.
The method for forming the metal thin film layer 30 is not particularly limited and can be formed, for example, by a vacuum thermal evaporation method or a sputtering method using the above-described metal material, and the conditions of the method are not particularly limited. The thickness and the light transmittance of the metal thin film layer are not particularly limited and may be appropriately selected according to the desired effect. In addition, when the metal thin film layer is formed in multiple layers, the deposition rate or the concealment ratio can be controlled, but the material can be manufactured by different characteristics depending on the use of the final product, and is not particularly limited.

도시하지 않았지만, 상기와 같이 제조된 금속박막층 표면에 산화방지층을 형성하는 단계를 추가로 포함할 수 있다. 산화방지층은 주로 하부의 금속박막층의 산화를 방지하는 역할을 하는바, 접착제층의 적층을 보다 용이하게 하고 금속층의 부식을 장기간 방지하게 위해 구비되는 것이다.
Although not shown, a step of forming an antioxidant layer on the surface of the metal thin film layer may be further included. The antioxidant layer serves mainly to prevent the oxidation of the metal thin film layer on the lower side, and is provided for facilitating the laminating of the adhesive layer and for preventing the corrosion of the metal layer for a long time.

한편, 패턴층(20)상에 펄코팅층을 형성하는 단계(S30)는 콤마코팅 또는 마이크로그라비아 코팅방법으로 상기 패턴층(20)상부에 도포하는 것을 포함할 수 있다.
On the other hand, the step (S30) of forming the perl coating layer on the pattern layer 20 may include coating the top of the pattern layer 20 with a comma coating method or a microgravure coating method.

아울러, 도시하지는 않았지만, 본 발명의 인테리어 필름의 제조방법에 있어서, 상기 패턴층(20) 상에 접착제층 및 착색플라스틱필름을 형성하는 단계를 더 포함하는 것을 특징으로 할 수 있다.In addition, although not shown, the method of manufacturing an interior film of the present invention may further include forming an adhesive layer and a colored plastic film on the pattern layer 20.

또한, 상기 하드코팅층과 상기 기재필름 사이에 제 1프라이머층을 형성하는 단계 또는 상기 기재필름과 상기 패턴층 사이에 제2프라이머층을 형성하는 단계를 추가로 포함할 수 있는바, 그라비아 코팅법에 의해 도포함이 바람직하다. 이 때 각층에 대한 특징은 전술한 바와 같다.
The method may further include forming a first primer layer between the hard coating layer and the base film or forming a second primer layer between the base film and the pattern layer, . The characteristics of each layer are as described above.

이하, 본 발명의 바람직한 실시예를 통해 본 발명의 구성 및 작용을 더욱 상세히 설명하기로 한다. 다만 이는 본 발명의 바람직한 예시로 제시된 것이며 어떠한 의미로도 이에 의해 본 발명이 제한되는 것으로 해석될 수는 없다.
Hereinafter, the configuration and operation of the present invention will be described in more detail with reference to preferred embodiments of the present invention. It is to be understood, however, that the same is by way of illustration and example only and is not to be construed as limiting the invention in any way.

실시예1Example 1

헤이즈도가 6%, 빛투과율 92%이상, 광택도 160%이고 두께가 30㎛인 고투명 PET필름 표면에, 에폭시아크릴레이트(SKUCBEbecryl 3700) 47중량%, 펜타에리쓰리톨 트리아크릴레이트 20중량%, 트리메틸올프로판트리아크릴레이트 15중량%, 1,6-핵산디올디아크릴레이트 12중량%, 광개시제(시바-가이기 D1173) 5중량% 및 레벨링제(SK-UCB Ebecryl350) 1중량%로 구성된 자외선 경화형 조성물을 UV램프와 헤어라인 무늬가 형성되어 있는 Hard Roll 사이에 주입함과 동시에 UV램프를 1차 경화하였다. 그 후 1차 경화된 상기 자외선 경화성 수지층을 별도의 UV램프로 2차 경화하여 헤어라인 패턴을 포함하는 패턴층을 형성하였다. 이를 충분히 건조한 후, 10-4Torr 1420℃에서 진공증착하여 400Å의 두께를 가지는 알루미늄이 증착되어 있는 금속박막층을 형성하였다47% by weight of an epoxy acrylate (SKUCBEbecryl 3700), 20% by weight of pentaerythritol triacrylate, and 20% by weight of an epoxy acrylate were coated on the surface of a highly transparent PET film having a haze of 6%, a light transmittance of 92% (UV-curing type) composed of 15% by weight of trimethylolpropane triacrylate, 12% by weight of 1,6-nucleic acid diol diacrylate, 5% by weight of a photoinitiator (Ciba-Geigy D1173) and a leveling agent The composition was injected between a UV lamp and a hard roll having a hairline pattern, and the UV lamp was first cured. Thereafter, the ultraviolet ray hardening resin layer that was first cured was secondarily cured by a separate UV lamp to form a pattern layer including a hair line pattern. After sufficiently dried, the aluminum thin film layer was vacuum deposited at 10 -4 Torr at 1420 ° C to form a metal thin film layer on which aluminum having a thickness of 400 Å was deposited

그 후, 상기 금속박막층 상부에 Si를 스퍼터링(Sputtering)시키면서, 산소를 주입하여 SiO2의 금속산화물로 구성된 산화방지층을 형성하였다.
Thereafter, oxygen was injected into the upper part of the metal thin film layer while sputtering Si to form an oxidation preventing layer composed of a metal oxide of SiO 2 .

실시예2Example 2

산화방지층을 포함하지 않은 것을 제외하고는 상기 실시예1과 동일하게 제조한다. 이 때, 상기 실시예1의 PET필름 상부에 아크릴계 폴리머 재질을 함유하는 자외선 경화형 수지를 마이크로 그라비아 코팅을 이용하여 3㎛의 하드코팅층을 형성하였다. An antioxidant layer was prepared in the same manner as in Example 1, except that the antioxidant layer was not included. At this time, a hard coat layer of 3 占 퐉 was formed on the PET film of Example 1 using a microgravure coating of an ultraviolet curable resin containing an acrylic polymer material.

또한, 폴리에스테르 접착제를 콤마 코팅법으로 10㎛ 두께로 도포하여 상기 실시예1의 알루미늄이 증착되어 있는 금속박막층 상부에 접착제층을 형성하였다. 이 때 상기 접착제층에 100℃의 열을 가하여 라미네이션롤로 폴리에스테르 필름을 합판시켜 본 발명의 인테리어 필름을 제조하였다.Further, a polyester adhesive was applied by a comma coating method to a thickness of 10 mu m to form an adhesive layer on the metal thin film layer on which the aluminum of Example 1 was deposited. At this time, heat of 100 占 폚 was applied to the adhesive layer, and the polyester film was laminated with a lamination roll to prepare an interior film of the present invention.

실시예3Example 3

상기 실시예2와 동일하게 제조하는바, 상기 실시예2의 하드코팅층과 PET필름 사이에 제1프라이머층을 포함하는바, 상기 PET층 상부에 그라비아 코팅법을 이용하여 2㎛ 두께의 제1프라이머층을 도포하였다. 또한, 상기 PET필름과 실시예2의 패턴층 사이에 제 2프라이머층을 추가로 포함할 수 있다. 이 때, 상기 제 2프라이머층은 패턴층 상부에 그라비아 코팅법을 이용하여 2㎛ 두께로 형성되었다.
The first primer layer was formed between the hard coat layer and the PET film of Example 2. The first primer layer was formed on the PET layer by a gravure coating method and then a first primer Layer. In addition, a second primer layer may be additionally provided between the PET film and the pattern layer of Example 2. At this time, the second primer layer was formed to a thickness of 2 mu m on the pattern layer using a gravure coating method.

상기와 같이 제조된 인테리어 필름은 다층의 금속이 증착된 금속박막층을 포함함으로써, 금속질감 및 컬러구현에 제한이 있는 단일 금속층을 포함하는 경우에 비해, 금속의 특유 컬러 및 휘도감을 부여하였으며, 산화 방지층을 함께 포함함으로써, 부식으로부터 자유로운 인테리어 필름을 완성할 수 있었다.
The interior film thus produced has a metal thin film layer on which a multi-layered metal is deposited, thereby giving a unique color and brightness of the metal, compared with the case of including a single metal layer with limited metal texture and color implementation, It is possible to complete the interior film free from corrosion.

10 : 기재필름
20 : 패턴층
30 : 금속박막층 31 : 펄 코팅층
40 : 접착제층
50 : 착색플라스틱필름
60 : 산화방지층
70 : 하드코팅층
81 : 제 1 프라이머층 82 : 제 2 프라이머층10: substrate film
20: pattern layer
30: metal thin film layer 31: pearl coating layer
40: adhesive layer
50: colored plastic film
60: antioxidant layer
70: Hard coating layer
81: first primer layer 82: second primer layer

Claims (15)

기재필름 및 상기 기재필름 상에 입체적인 요철무늬를 포함하는 패턴층을 포함하고 상기 패턴층 상에 금속박막층을 포함하는 것을 특징으로 하는 인테리어 필름.
An interior film comprising a base film and a pattern layer including a three-dimensional uneven pattern on the base film and a metal thin film layer on the pattern layer.
제 1항에 있어서,
상기 패턴층 상에 접착제층 및 착색플라스틱필름이 차례로 적층된 것을 특징으로 하는 인테리어 필름.
The method of claim 1,
Wherein an adhesive layer and a colored plastic film are sequentially laminated on the pattern layer.
제 1항에 있어서,
상기 패턴층은 헤어라인 패턴을 포함하는 것을 특징으로 하는 인테리어 필름.
The method of claim 1,
Wherein the pattern layer comprises a hairline pattern.
제 1항에 있어서,
상기 금속박막층은 알루미늄, 스테인리스 스틸, 구리, 금, 은, 니켈, 크롬 및 코발트로 이루어진 군으로부터 선택된 하나 이상을 포함하는 것을 특징으로 하는 인테리어 필름.
The method of claim 1,
The metal thin film layer is an interior film, characterized in that at least one selected from the group consisting of aluminum, stainless steel, copper, gold, silver, nickel, chromium and cobalt.
제 1항에 있어서,
상기 금속박막층은 알루미늄, 스테인리스 스틸, 구리, 금, 은, 니켈, 크롬 및 코발트로 이루어진 군으로부터 선택된 하나 이상을 포함하는 금속을 증착하여 형성하는 것을 특징으로 하는 인테리어 필름.
The method of claim 1,
The metal thin film layer is formed by depositing a metal including at least one selected from the group consisting of aluminum, stainless steel, copper, gold, silver, nickel, chromium and cobalt.
제 1항에 있어서,
상기 금속박막층은 알루미늄, 스테인리스 스틸, 구리, 금, 은, 니켈, 크롬 및 코발트로 이루어진 군으로부터 선택된 2종 이상을 포함하는 다층구조인 것을 특징으로 하는 인테리어 필름.
The method of claim 1,
The metal thin film layer is an interior film, characterized in that the multi-layer structure comprising two or more selected from the group consisting of aluminum, stainless steel, copper, gold, silver, nickel, chromium and cobalt.
제 1항에 있어서,
상기 금속박막층의 표면에 산화방지층을 추가로 포함하는 것을 특징으로 하는 인테리어 필름.
The method of claim 1,
And an antioxidant layer on the surface of the metal thin film layer.
제 1항에 있어서,
상기 기재필름 상부에 하드코팅층을 포함하고,
상기 하드코팅층과 상기 기재필름 사이에 제1프라이머층을 추가로 포함하는 것을 특징으로 하는 인테리어 필름.
The method of claim 1,
A hard coating layer on the base film,
Further comprising a first primer layer between the hard coating layer and the substrate film.
제 1항에 있어서,
상기 기재필름과 상기 패턴층 사이에 제2프라이머층을 추가로 포함하는 것을 특징으로 하는 인테리어 필름.
The method of claim 1,
Further comprising a second primer layer between the base film and the pattern layer.
기재필름을 마련하는 단계;
상기 기재필름 상에 입체적인 요철무늬를 포함하는 패턴층을 형성하는 단계;
상기 패턴층 상에 금속박막층을 형성하는 단계를 포함하는 것을 특징으로 하는 인테리어 필름의 제조방법.
Providing a base film;
Forming a pattern layer including a three-dimensional concave-convex pattern on the base film;
Method of manufacturing an interior film comprising the step of forming a metal thin film layer on the pattern layer.
제 10항에 있어서,
상기 패턴층 상에 접착제층 및 착색플라스틱필름을 형성하는 단계를 더 포함하는 것을 특징으로 하는 인테리어 필름의 제조방법.
The method of claim 10,
And forming an adhesive layer and a colored plastic film on the pattern layer.
제 10항에 있어서,
상기 패턴층을 형성하는 단계는
상기 패턴층에 헤어라인 패턴을 구현하는 단계를 포함하는 것을 특징으로 하는 인테리어 필름의 제조방법.
The method of claim 10,
The step of forming the pattern layer
Method for producing an interior film comprising the step of implementing a hairline pattern on the pattern layer.
제 10항에 있어서,
상기 금속박막층을 형성하는 단계는
상기 패턴층 표면에 알루미늄, 스테인리스 스틸, 구리, 금, 은, 니켈, 크롬 및 코발트로 이루어진 군으로부터 선택된 하나 이상을 포함하는 금속을 증착하여 형성하는 것을 특징으로 하는 인테리어 필름의 제조방법.
The method of claim 10,
Forming the metal thin film layer is
Method of manufacturing an interior film, characterized in that by depositing a metal comprising at least one selected from the group consisting of aluminum, stainless steel, copper, gold, silver, nickel, chromium and cobalt on the surface of the pattern layer.
제 10항에 있어서,
상기 금속박막층을 형성하는 단계는
상기 패턴층 표면에 알루미늄, 스테인리스 스틸, 구리, 금, 은, 니켈, 크롬 및 코발트로 이루어진 군으로부터 선택된 2종 이상을 포함하는 금속을 다층으로 증착하여 형성하는 것을 특징으로 하는 인테리어 필름의 제조방법.
The method of claim 10,
Forming the metal thin film layer is
Method of manufacturing an interior film, characterized in that formed on the surface of the pattern layer by depositing a multilayer of a metal containing at least two selected from the group consisting of aluminum, stainless steel, copper, gold, silver, nickel, chromium and cobalt.
제 10항에 있어서,
상기 금속박막층 표면에 산화방지층을 추가로 형성하는 단계를 포함하는 것을 특징으로 하는 인테리어 필름의 제조방법.The method of claim 10,
And forming an antioxidant layer on the surface of the metal thin film layer.
KR1020110144914A 2011-12-28 2011-12-28 Interior films expressing metallic appearance and method of manufacturing where of KR101439590B1 (en)