KR20080082315A - Black plastic film for lamination having non-iridescence and lustrous property, and method for manufacturing the same - Google Patents
Black plastic film for lamination having non-iridescence and lustrous property, and method for manufacturing the same Download PDFInfo
- Publication number
- KR20080082315A KR20080082315A KR1020070023025A KR20070023025A KR20080082315A KR 20080082315 A KR20080082315 A KR 20080082315A KR 1020070023025 A KR1020070023025 A KR 1020070023025A KR 20070023025 A KR20070023025 A KR 20070023025A KR 20080082315 A KR20080082315 A KR 20080082315A
- Authority
- KR
- South Korea
- Prior art keywords
- plastic film
- iridescence
- layer
- black
- film
- Prior art date
Abstract
Description
도 1 내지 도 4는 본 발명의 바람직한 실시예에 따른 라미네이션용 무 변색 유광 흑색 플라스틱 필름의 단면을 나타낸 구성도이다.1 to 4 is a block diagram showing a cross section of a colorless glossy black plastic film for lamination according to a preferred embodiment of the present invention.
<도면의 주요부분에 대한 부호의 설명><Description of the code | symbol about the principal part of drawing>
1 : 라미네이션용 무 변색 유광 흑색 플라스틱 필름1: Colorless Glossy Black Plastic Film for Lamination
10 : 투명 플라스틱필름(층) 11 : 광 경화형 수지층10: transparent plastic film (layer) 11: photo-curable resin layer
12, 15 : 인쇄층 13 : 흑색 필름(층)12, 15: printed layer 13: black film (layer)
14 : 접착제층14: adhesive layer
본 발명은 라미네이션용 무 변색(non-iridescence) 유광 흑색 플라스틱 필름 및 그의 제조방법에 관한 것이다. 좀 더 상세하게는 투명 플라스틱 필름을 중심으로 그 표면 측에는 광 경화형 수지 층이 형성되고, 그 이면 측에는 인쇄층 및 흑색필름층을 포함하는 라미네이션용 플라스틱 흑색 필름에 있어서, 상기 광 경화형 수지층이 무 변색(non-iridescence) 유광층인 것을 특징으로 한다. The present invention relates to a non-iridescence glossy black plastic film for lamination and a method of manufacturing the same. In more detail, a photocurable resin layer is formed on the surface side of the transparent plastic film, and the photocurable resin layer is discolored in the plastic black film for lamination including a printing layer and a black film layer on the back side thereof. (non-iridescence) It is characterized in that it is a glossy layer.
본 발명에 따른 상기 라미네이션용 무 변색(non-iridescence) 유광 흑색 플라스틱 필름은 가전제품의 외장재, 건물 내부 및 외부 인테리어 그리고 가구의 표면 장식용 마감재 등으로 사용하기에 적합하다. 특히, 본 발명에 따른 상기 라미네이션용 무 변색 유광 흑색 플라스틱 필름은 금속판(또는 금속 면)에 적합한 것으로서 금속면에 합지, 사용함으로써 패턴 효과를 극대화 할 수 있다. The non-iridescence glossy black plastic film for lamination according to the present invention is suitable for use as exterior materials for home appliances, interior and exterior interiors of buildings, and surface decorative finishes for furniture. In particular, the non-chromic glossy black plastic film for lamination according to the present invention is suitable for a metal plate (or metal surface) can be laminated on the metal surface and used to maximize the pattern effect.
종래의 라미네이션용 유광 흑색 플라스틱필름은 일반적으로 보는 각도에 따라 무지개 빛깔(iridescence)이 나타나는 외관에 변색(iridescence)현상이 일어난다. 즉, 보는 각도에 따라서 무지개 빛깔 또는 진주 빛깔(iridescence)이 나타난다. 이는 이면 필름층을 흑색필름으로 구성할 경우, 투명 플라스틱필름의 고유 굴절률과 가공 시 이축 연신으로 발생하는 이방성(anisotropic), 헤이즈(Haze) 등으로 인하여 투명플라스틱필름 자체에서 무지개 빛깔(iridescence)이 발생되고, 또한 표면 코팅수지(자외선 또는 열 경화형 수지)의 고유 굴절률이나 그 가공조건 등으로 인하여 외관에 무지개 빛깔(iridescence)이 발생하는 것으로 알려져 있다. The conventional glossy black plastic film for lamination generally causes discoloration (iridescence) on the appearance of iridescence depending on the viewing angle. That is, iridescence or iridescence appears depending on the viewing angle. When the back film layer is composed of a black film, iridescence occurs in the transparent plastic film due to the intrinsic refractive index of the transparent plastic film and the anisotropic and haze generated by biaxial stretching during processing. In addition, due to the intrinsic refractive index of the surface coating resin (ultraviolet ray or thermosetting resin), processing conditions, and the like, it is known that iridescence occurs in appearance.
이론적으로는 투명 플라스틱필름과 그에 적층되는 각 층의 플라스틱 재료의 굴절률을 일치시킴으로써 무지개 빛깔(iridescence)이 발생되는 문제점의 해결이 가능하다(non-iridescence)고 하나, 각 층(Layer) 별 가공 시 발생하는 무지개 빛 깔(iridescence) 발생 문제로 인해 굴절률 일치를 통하여 무 변색(non-iridescence) 유광 흑색 플라스틱 필름으로 제작이 용이하지 않다. Theoretically, it is possible to solve the problem that iridescence occurs by matching the refractive index of the transparent plastic film and the plastic material of each layer laminated thereon (non-iridescence). Due to the problem of iridescence that occurs, it is not easy to produce non-iridescence glossy black plastic film through refractive index matching.
또한 위와 같은 각 층의 굴절률을 일치시키는 방법으로는 사용 가능한 수지의 한정성으로 인하여 가공물성(Bending성), 표면측 광 경화형수지층(H/Coating)의 부착력 및 표면경도(Hardness) 등의 물성 충족에 어려운 점이 여전히 남아있게 된다. In addition, the method of matching the refractive index of each layer as described above, due to the limited properties of the resin can be used (Bending properties), adhesion properties of the surface-side photo-curable resin layer (H / Coating) and physical properties (Hardness), etc. Difficulties still remain.
본 발명은 상기와 같은 종래 기술에서 나타나는 문제점을 해결하기 위한 것으로서, 투명 플라스틱필름의 헤이즈(Haze)를 조정함으로써 무지개 빛깔(iridescence)이 발생되는 문제점을 해결한 무 변색(non-iridescence) 유광 흑색 플라스틱 필름을 제공하려는 것이다. The present invention is to solve the problems appearing in the prior art as described above, non-iridescence glossy black plastic that solves the problem that the iridescence occurs by adjusting the haze (Haze) of the transparent plastic film To provide the film.
또한, 본 발명은 표면층을 형성하는 광 경화형 아크릴계 수지 조성물의 Solid contents를 조절 제어함으로써 무지개 빛깔(iridescence)이 발생되는 문제점을 해결한 무 변색(non-iridescence) 유광 흑색 플라스틱 필름을 제공하려는 것이다.In addition, the present invention is to provide a non-iridescence glossy black plastic film that solves the problem that iridescence occurs by controlling and controlling the solid contents of the photocurable acrylic resin composition forming the surface layer.
본 발명의 다른 목적은 표면층인 광 경화형 수지층을 150 내지 250메쉬(Mesh) 롤(Roll)을 이용하여 코팅(Coating)함으로써 무지개 빛깔(iridescence)이 발생되는 문제점을 해결한 무 변색(non-iridescence) 유광 흑색 플라스틱 필름을 제공하려는 것이다. Another object of the present invention is a non-iridescence that solves the problem that iridescence occurs by coating a photocurable resin layer, which is a surface layer, using 150 to 250 mesh rolls. ) To provide a glossy black plastic film.
위와 같은 목적을 달성하기 위한 본 발명에서는 투명 플라스틱 필름을 중심으로 그 표면 측에는 광 경화형 수지 층이, 그 이면 측에는 인쇄층 및 흑색필름층이 포함된 라미네이션용 플라스틱 흑색 필름에 있어서, 상기 광 경화형 수지층이 무 변색(non-iridescence) 유광층인 것을 특징으로 하는 라미네이션용 무 변색(non-iridescence) 유광 흑색 플라스틱 필름과 그 제조방법이 개시된다. In the present invention for achieving the above object, a photocurable resin layer on the surface side of the transparent plastic film, the printing layer and a black film layer on the back side thereof in the plastic black film for lamination, the photocurable resin layer Disclosed are a non-iridescence glossy black plastic film for lamination characterized in that it is a non-iridescence glossy layer and a manufacturing method thereof.
본 발명에 따른 상기 라미네이션용 무 변색(non-iridescence) 유광 흑색 플라스틱 필름은 투명 플라스틱 필름을 중심으로 그 표면 측에는 광 경화형 수지 층이, 그 이면 측에는 인쇄층 및 흑색필름층이 기본 구성으로 포함된다. The non-iridescence glossy black plastic film for lamination according to the present invention includes a photocurable resin layer on the surface side of the transparent plastic film, and a printing layer and a black film layer on the back side thereof as basic configurations.
상기 투명 플라스틱 필름과 흑색필름층 사이에는 접착제층이 개재될 수 있고, 상기 인쇄층은 투명 플라스틱 필름의 양면에 형성될 수도 있다.An adhesive layer may be interposed between the transparent plastic film and the black film layer, and the printing layer may be formed on both sides of the transparent plastic film.
본 발명에 따른 상기 라미네이션용 무 변색(non-iridescence) 유광 흑색 플라스틱 필름을 iridescence 효과에 취약한 단색, 특히 블랙(Black) 류에 적용 시, 경면효과와 Non-iridescence 효과에 따라 High Glossy 효과의 구현이 가능하며, 종래의 iridescence 효과가 가미된 단색 유광, 특히 유광 블랙(Black) 제품에 비해 한층 고급스런 외관효과를 얻을 수 있다. When the non-iridescence glossy black plastic film for lamination according to the present invention is applied to a monochromatic, in particular, black, which is vulnerable to the iridescence effect, the implementation of the High Glossy effect according to the mirror effect and the non-iridescence effect is achieved. It is possible to obtain a more elegant appearance effect than the monochromatic gloss, especially gloss black products, to which the conventional iridescence effect is added.
본 발명에 따른 라미네이션용 무 변색(non-iridescence) 유광 흑색 플라스틱 필름의 상기 투명 플라스틱 필름은 폴리에틸렌텔레프탈레이트(Polyethylene terephthalate;PET), 폴리에스테르( Polyester), 폴리에틸렌(PE), 폴리프로필 렌(PP) 등의 소재로 된 필름이 바람직하고, 특히, 압축, 카렌다, T-Die 등 통상적인 공법으로 제조 가능하고, 두께가 얇고 균일성이 있으며, 투명도가 높고 가공 물성이 뛰어난 피이티(Polyethylene Terephthalate ; PET) 필름이 바람직하다. 본 발명에서 투명 플라스틱 필름의 투명도(Haze)는 1% 내지 10% 수준이 바람직하며 1% 미만일 경우에는 투명 필름 자체의 iridescence 효과를 제어하기가 어렵고 10%를 초과하는 경우에는 인쇄 후 흑색(흑색)감이 떨어지게 된다. The transparent plastic film of the non-iridescence glossy black plastic film for lamination according to the present invention is polyethylene terephthalate (PET), polyester (polyester), polyethylene (PE), polypropylene (PP) Films made of such materials are preferred, and in particular, PET, which can be manufactured by conventional methods such as compression, calendar, and T-Die, has a thin thickness, uniformity, high transparency, and excellent processing properties, and PET (Polyethylene Terephthalate; PET). ) Film is preferred. In the present invention, the transparency (Haze) of the transparent plastic film (Haze) is preferably 1% to 10% level is less than 1%, it is difficult to control the iridescence effect of the transparent film itself, if it exceeds 10% black after printing (black) The feeling will fall.
본 발명에서 투명 플라스틱 필름의 두께는 12미크론미터(㎛) 내지 50미크론미터(㎛) 범위의 것이 바람직하다. 투명 플라스틱 필름의 두께가 12㎛ 미만일 경우에는 투명 플라스틱필름에 컬(Curl)이 발생하여 인쇄 작업에 악영향을 미칠 수 있고 50㎛를 초과할 경우에는 불투명성이 높아져 흑색질감을 살리기가 어려울 수 있다. In the present invention, the thickness of the transparent plastic film is preferably in the range of 12 microns (µm) to 50 microns (µm). If the thickness of the transparent plastic film is less than 12㎛ curl may occur on the transparent plastic film (Curl) may adversely affect the print job, if it exceeds 50㎛ it may be difficult to save the black texture due to the high opacity.
본 발명에 따른 라미네이션용 무 변색(non-iridescence) 유광 흑색 플라스틱 필름의 무 변색(non-iridescence) 유광층인 상기 광 경화형 수지층은 물성제어가 용이하고 범용 굴절률을 갖는 우레탄 아크릴레이트(urethane acrylate), 에폭시 아크릴레이트(epoxy acrylate), 폴리에스테르아크릴레이트(polyester acrylate) 등의 올리고머(oligomer)와 이소보르닐 아크릴레이트(Isobornyl acrylate), 비닐피로리디논(Vinyl pyrrolidinone)과 같은 모노머(monomer), Irgacure184와 같은 통상적인 광개시제, 등으로 이루어지는 자외선 경화형 수지 조성물로 형성된다. 본 발명에 따른 상기 자외선 경화형 수지조성물은 통상적인 Tinuvin400과 같은 통상적인 광안정제와 기타 물성보완을 위한 통상적인 첨가제가 첨가될 수 있다. The photo-curable resin layer, which is a non-iridescence glossy layer of a non-iridescence glossy black plastic film for lamination according to the present invention, is easy to control properties and has a general refractive index urethane acrylate. , Oligomers such as epoxy acrylate and polyester acrylate, monomers such as isobornyl acrylate and vinyl pyrrolidinone, Irgacure184 It is formed of the ultraviolet curable resin composition which consists of conventional photoinitiators, such as these. In the ultraviolet curable resin composition according to the present invention, conventional light stabilizers such as conventional Tinuvin400 and other additives for supplementing physical properties may be added.
상기 자외선 경화형 수지 조성물은 상기 올리고머의 고형분 함량(Solid Contents)은 50중량퍼센트(%) 내지 80중량퍼센트(%) 범위가 바람직하다.In the ultraviolet curable resin composition, solid content (Solid Contents) of the oligomer is preferably in the range of 50% by weight (%) to 80% by weight (%).
또한 경화된 수지의 가교가 많을수록 경도가 강해지므로 모노머를 다관능기를 사용하는 것이 바람직하나, 관능기가 높을수록 치수안정성, 신율, 굴곡성이 나빠지므로 적정한 관능기의 모노머의 선택이 필요하다. 이러한 모노머로서 예를 들면, 이소보르닐 아크릴레이트(Isobornyl acrylate), 비닐피로리디논(Vinyl pyrrolidinone)과 같은 모노머를 들 수 있다.In addition, the more crosslinking of the cured resin, the stronger the hardness, it is preferable to use a polyfunctional monomer, but the higher the functional group, the worse the dimensional stability, elongation, bendability, it is necessary to select the monomer of the appropriate functional group. Examples of such monomers include monomers such as isobornyl acrylate and vinyl pyrrolidinone.
상기 무 변색(non-iridescence) 유광층인 광 경화형 수지층은 닢 코타(Nip Coater), 바 코타(Bar Coater) 등 통상적인 다양한 방법을 사용하여 형성할 수 있으나, 글래뷰어(Gravure) 코팅 방법이 더 적합하며, 150 내지 250메쉬(Mesh) 롤(Roll)을 이용하여 코팅(Coating)하는 것이 바람직하다. 150Mesh 미만에서는 코팅 효과의 섬세도가 떨어지게 되어 코팅의 균일도가 불안정해지고 250Mesh를 초과하는 경우에는 원단 상태에 조그만 흠집이 발생하여도 코팅액이 도포되지 않는 문제점이 발생하게 된다. The photo-curable resin layer, which is a non-iridescence gloss layer, may be formed using various conventional methods such as Nip Coater and Bar Coater. However, a Gravure coating method may be used. More suitable, it is preferable to coat using 150 to 250 mesh rolls. If the 150Mesh is less than the fineness of the coating effect is unstable coating uniformity and if the 250Mesh exceeds 250Mesh occurs a problem that the coating liquid is not applied even if a small scratch on the fabric state.
본 발명에 따른 라미네이션용 무 변색(non-iridescence) 유광 흑색 플라스틱 필름의 흑색필름층은 중합도가 800∼1300정도의 염화비닐 수지에 가소제를 15∼25부, 안정제를 2∼4부, 흑색감이나 은폐력 확보를 위하여 유기 및 무기안료 등을 첨가하여 생산된 0.05∼0.2mm 두께의 흑색필름을 적용하는 것이 바람직하다. The black film layer of the non-iridescence gloss black plastic film for lamination according to the present invention is 15 to 25 parts of plasticizer, 2 to 4 parts of stabilizer, black color to vinyl chloride resin having a degree of polymerization of about 800 to 1300. In order to secure hiding power, it is preferable to apply a black film having a thickness of 0.05 to 0.2 mm produced by adding organic and inorganic pigments.
본 발명에 따른 라미네이션용 무 변색(non-iridescence) 유광 흑색 플라스틱 필름은 투명 플라스틱 필름 및 광 경화형 수지조성물을 준비하는 단계; 상기 투명 플라스틱 필름의 일 측면에 상기 광 경화형 수지조성물을 150 내지 250메쉬(Mesh) 롤(Roll)을 이용하여 코팅(Coating) 및 경화시켜 광 경화형 수지층을 형성하는 단계; 상기 광 경화형 수지층이 형성된 이면에 인쇄층을 형성하는 단계; 별도로 준비된 흑색필름을 상기 인쇄층에 합판시키는 흑색필름 합판단계;를 포함하는 제조방법에 의해 제조할 수 있다. The non-iridescence glossy black plastic film for lamination according to the present invention comprises the steps of preparing a transparent plastic film and a light curable resin composition; Coating and curing the photocurable resin composition on one side of the transparent plastic film using 150 to 250 mesh rolls to form a photocurable resin layer; Forming a printing layer on a rear surface of the photocurable resin layer; It can be prepared by a manufacturing method comprising a; black film plywood step of plywood separately prepared black film on the printing layer.
상기 인쇄층을 형성한 다음, 접착제층을 형성한 후, 흑색필름 합판할 수도 있다. 상기 접착제층은 폴리우레탄 또는 폴리에스테르 등의 접착제를 인쇄층 또는 흑색필름의 상부에 그라비아 공법으로 1∼5㎛ 정도의 두께로 도포 한 후, 80∼150℃의 열을 가하여 라미네이션 롤로 흑색필름과 합판시킬 수 있다.After the printing layer is formed, the adhesive layer may be formed, followed by black film plywood. The adhesive layer is coated with an adhesive such as polyurethane or polyester on the printing layer or the black film to a thickness of about 1 to 5㎛ by the gravure method, and then applied a heat of 80 ~ 150 ℃ to the black film and plywood with a lamination roll You can.
상기 광 경화형 수지층을 형성하기 전에 먼저 인쇄층을 형성한 다음 그 위에 광 경화형 수지층을 형성함으로써 양면에 인쇄층이 형성된 라미네이션용 무 변색(non-iridescence) 유광 흑색 플라스틱 필름을 제조할 수 있다.Before the photocurable resin layer is formed, a non-iridescence glossy black plastic film for lamination in which a printing layer is formed on both surfaces may be manufactured by first forming a printing layer and then forming a photocurable resin layer thereon.
본 발명에서 투명도가 높고 가공 물성이 뛰어난 피이티(Polyethylene terephthalate;PET) 필름을 기재필름으로 사용하고 투명도(Haze) 조절과 물성 modify가 용이한 범용 굴절률를 가진 아크릴계수지를 표면층의 기재수지로 사용함으로써 Non-iridescence 외관 구현과 더불어, 가공물성(Bending성), 표면 경도(Hardness) 등의 제품 사용 기본 물성을 충족시킬 수 있음은 물론, 보편화된 가공방법으로 제조할 수 있어 가공 공정을 단순화시킬 수 있다. In the present invention, a non-transparent poly terephthalate (PET) film having high transparency and processing properties is used as a base film, and an acrylic resin having a general refractive index that is easy to control haze and modify physical properties is used as a base resin of the surface layer. In addition to realizing the appearance of -iridescence, it can satisfy the basic properties of products such as bending (bending) and surface hardness (Hardness), and can be manufactured by a generalized processing method, thereby simplifying the processing process.
본 발명에 따른 상기 라미네이션용 무 변색(non-iridescence) 유광 흑색 플라스틱 필름은 철판, 목재, 건물 벽체 등에 접착제를 도포한 다음, 접착시킨 후, 가전제품 외장재, 건물 내부 및 외부 그리고 가구 등의 장식용 마감재로 적용이 가능하다. The non-iridescence gloss black plastic film for lamination according to the present invention is applied to an iron plate, wood, building walls and then glued, and then bonded, decorative finishing materials for home appliances exterior, building interior and exterior and furniture It is possible to apply.
이하, 본 발명의 바람직한 실시예에 따른 라미네이션용 무 변색 유광 흑색 플라스틱 필름의 구성을 첨부한 도면을 참조하여 설명한다.Hereinafter, with reference to the accompanying drawings, the configuration of a colorless glossy black plastic film for lamination according to a preferred embodiment of the present invention.
도 1 내지 도 4는 본 발명의 바람직한 실시예에 따른 라미네이션용 무 변색 유광 흑색 플라스틱 필름(1)의 단면을 나타낸 개략적인 구성도이다. 도 1을 참조하면, 표면층인 광 경화형 수지 층(11)으로부터 투명 플라스틱필름층(10), 인쇄층(12), 흑색필름(13)이 차례로 형성된 적층구조이다. 1 to 4 are schematic configuration diagrams showing a cross section of a colorless, glossy black
도 2는 광 경화형 수지 층(11)으로부터 투명 플라스틱필름층(10), 인쇄층(12), 접착제 층(14) 및 흑색필름(13)이 차례로 형성된 적층구조이다. 2 is a laminated structure in which a transparent
도 3 참조하면, 표면층인 광 경화형 수지 층(11)으로부터 인쇄층(15), 투명 플라스틱필름층(10), 인쇄층(12), 및 흑색필름(13)이 차례로 형성된 적층구조이고, 도 4는 표면층인 광 경화형 수지 층(11)으로부터 인쇄층(15), 투명 플라스틱필름층(10), 인쇄층(12), 접착제층(14) 및 흑색필름(13)이 차례로 형성된 적층구조이다. Referring to FIG. 3, a
본 발명의 상기 라미네이션용 플라스틱 필름(1)은 피착소재에 상기 흑색필름(13)의 이면이 접착되어 합판된다.The lamination
본 발명에 따른 라미네이션용 플라스틱 필름은 Non-iridescence 외관 구현과 더불어, 투명 플라스틱필름의 일면 또는 양면에 다양한 인쇄층을 형성함으로써 의장성이 우수한 블랙(black)질감의 유광 흑색 플라스틱 필름을 제공할 수 있는 효과가 있다. Lamination plastic film according to the present invention can provide a glossy black plastic film having a good texture (black) texture by forming a variety of printed layers on one or both sides of the transparent plastic film in addition to the non-iridescence appearance. It works.
또한, 본 발명은 가공물성(Bending성), 표면 경도(Hardness) 등의 제품 사용 기본 물성을 충족시킬 수 있으며, 보편화된 가공방법을 통하여 가공 공정을 단순화시킬 수 있는 효과가 있다. In addition, the present invention can satisfy the basic physical properties of the product, such as processing properties (Bending properties), surface hardness (Hardness), there is an effect that can simplify the processing process through a generalized processing method.
Claims (13)