KR20200022837A - Toothpaste composition having photocatalyst - Google Patents

Toothpaste composition having photocatalyst Download PDF

Info

Publication number
KR20200022837A
KR20200022837A KR1020180098959A KR20180098959A KR20200022837A KR 20200022837 A KR20200022837 A KR 20200022837A KR 1020180098959 A KR1020180098959 A KR 1020180098959A KR 20180098959 A KR20180098959 A KR 20180098959A KR 20200022837 A KR20200022837 A KR 20200022837A
Authority
KR
South Korea
Prior art keywords
photocatalyst
tio
toothpaste composition
minutes
toothpaste
Prior art date
Application number
KR1020180098959A
Other languages
Korean (ko)
Other versions
KR102132705B1 (en
Inventor
김병하
홍창익
Original Assignee
주식회사 디네이쳐
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 디네이쳐 filed Critical 주식회사 디네이쳐
Priority to KR1020180098959A priority Critical patent/KR102132705B1/en
Publication of KR20200022837A publication Critical patent/KR20200022837A/en
Application granted granted Critical
Publication of KR102132705B1 publication Critical patent/KR102132705B1/en

Abstract

Disclosed is a toothpaste composition containing photocatalyst. According to an embodiment of the present invention, the toothpaste composition containing photocatalyst including a TiO_2 photocatalyst, a pH dependent colorant and a binder. Therefore, the toothpaste composition containing photocatalyst can derive tooth whitening effects, and maximizes antibacterial effects through light irradiation during storage of a toothbrush by more tightly binding the photocatalyst onto the toothbrush. In addition, by containing a colorant that changes color depending on pH, visualization is possible to minimize the impact on gums and teeth by allowing a user to brush teeth in an optimal brushing environment, and wounds and inflammation in the oral cavity can be prevented by containing chitosan and alginic acid for the prevention of oral diseases.

Description

광촉매제 함유 치약 조성물{TOOTHPASTE COMPOSITION HAVING PHOTOCATALYST}Photocatalyst-containing toothpaste composition {TOOTHPASTE COMPOSITION HAVING PHOTOCATALYST}

본 발명은 광촉매 함유 치약 조성물에 관한 것으로, 보다 상세하게는 광촉매를 포함하여 치아 미백 및 칫솔 항균 효과를 얻을 수 있으며 잇몸의 환경을 시각화할 수 있고 치주염을 예방할 수 있는 광촉매제 함유 치약 조성물에 관한 것이다.The present invention relates to a photocatalyst-containing toothpaste composition, and more particularly, to a photocatalyst-containing toothpaste composition including a photocatalyst, which can obtain tooth whitening and toothbrush antibacterial effects, visualize the environment of the gums, and prevent periodontitis. .

일반적으로 치아 변색 요인은 외인성 변색과 내인성 변색으로 분류할 수 있다. 이중 외인성 치아 변색은 음식물 찌꺼기나 니코틴, 커피, 홍차 등이 치아표면에 침착하거나 치면상의 치석이나 연성 침착물이 색소성분에 의해 염색됨에 의해서 발생할 수 있으며, 내인성 치아 변색은 치아가 신경을 잃거나 테트라사이클린계 항생제를 과다 복용하는 경우 노화현상을 그 원인으로 언급할 수 있다. 그러나, 사람들은 미용이나 다른 여러 가지 이유로 인하여 하얀 치아를 원해왔고, 1960년대 말에 처음으로 표준화된 치아 미백 방법이 치과에서 행해진 후에 여러 가지 치아 미백 방법이 개발되고 발전되어 왔다.Generally, tooth discoloration factors can be classified into exogenous discoloration and endogenous discoloration. Exogenous tooth discoloration may be caused by food deposits, nicotine, coffee, tea, etc. deposited on the tooth surface, or tartar or soft deposits on the tooth surface by pigmentation. Endogenous tooth discoloration is caused by tooth loss or tetra Overdose of cyclin antibiotics may be cited as the cause of aging. However, people have desired white teeth for cosmetic or other reasons, and various tooth whitening methods have been developed and developed since the first standardized tooth whitening method was performed at the dentist in the late 1960s.

치아의 변색에 의한 영향은 미용적인 측면 이외에는 별다른 악영향이 없기 때문에 근래에 이르기까지도 치아 미백의 중요성 및 시급성은 상대적으로 평가 절하되어 왔다. 사회가 발달하고 국민들의 생활 수준이 높아짐에 따라, 이전에는 기능 중심의 치과 치료가 행해졌던 것에 비해 최근에는 심미적 치료의 중요성이 대두되고 있다. 특히, 치아의 삭제나 기계적인 이동(교정)을 동반하지 않고 비교적 용이한 방법으로 피시술자 스스로 만족할 만한 결과를 얻을 수 있는 치아 미백술에 대한 관심과 수요가 증가하고 있다.Since the effect of discoloration of teeth has no adverse effects other than cosmetics, the importance and urgency of tooth whitening has been relatively deteriorated until recently. As society develops and the standard of living of the people rises, the importance of aesthetic treatment is emerging in recent years, compared to the function-oriented dental treatment. In particular, there is a growing interest and demand for teeth whitening that can achieve satisfactory results by the operator himself in a relatively easy way without the removal of teeth or mechanical movement (correction).

또한, 양치질을 통해서 구강의 청결이 유지되지 않으면, 치아에 치태(Dental Plaque)가 생기고, 치태는 점차 석회화되어 치아 표면에 치석(Dental Calculus)을 만들게 된다. 이러한 치태(Dental Plaque)와 치석(Dental Calculus)은 구강 내 세균을 증식시켜 치주염(Gingivitis), 치은염(Periodontitis) 등의 잇몸질환을 일으키고, 구취도 발생시킨다. 최근 고령화 등의 문제로 치주질환 환자가 급격히 증가하고 있으나, 이러한 치주질환의 경우 올바른 양치질과 적절한 치약 제품을 통하여 예방이 가능하나, 이러한 예방을 위한 양치법 등에 대한 사용자의 인식이 부족한 실정이다.In addition, if the oral cavity is not maintained through brushing the teeth, dental plaque is generated in the teeth, and the plaque is gradually calcified to form dental calculus on the tooth surface. Dental plaque and dental calculus multiply bacteria in the oral cavity causing gum disease such as gingivitis and gingivitis, and also cause bad breath. Recently, the periodontal disease patients are rapidly increasing due to aging problems, but such periodontal disease can be prevented through correct tooth brushing and proper toothpaste products, but the user's awareness of such a method for preventing toothpaste is insufficient.

뿐만 아니라, 양치질 후에 칫솔을 보관하는 과정에서 일반적으로 칫솔모 1mm2당 약 500만 마리 이상의 세균이 검출되는 등, 칫솔 자체에 세균 번식으로 인한 위생이 문제되고 있다.In addition, in the process of storing the toothbrush after brushing the teeth, the hygiene due to the breeding of bacteria in the toothbrush itself, such as about 5 million bacteria per 1 mm 2 of the brush head is generally detected.

따라서,이러한 문제를 해결하기 위한 치약 조성물에 대한 연구가 지속적으로 다각적으로 진행되고 있다.Therefore, researches on toothpaste compositions for solving these problems continue to be diversified.

특허문헌 1: 대한민국 공개특허공보 제10-2004-0021954호Patent Document 1: Republic of Korea Patent Publication No. 10-2004-0021954

본 발명의 실시예들은 광촉매를 포함하는 치약 조성물을 통하여 치아의 미백 및 칫솔의 항균 효과를 극대화할 수 있는 치약 조성물을 제공하고자 한다.Embodiments of the present invention to provide a toothpaste composition that can maximize the antibacterial effect of the tooth whitening and toothbrush through the toothpaste composition comprising a photocatalyst.

또한, 최적의 양치 환경에서 양치질하여 잇몸 및 치아의 충격을 최소화할 수 있도록 시각화가 가능한 치약 조성물을 제공하고자 한다.In addition, to provide a toothpaste composition that can be visualized to minimize the impact of the gums and teeth by brushing in an optimal brushing environment.

또한, 구강 내 상처 및 염증을 예방할 수 있는 치약 조성물을 제공하고자 한다.In addition, to provide a toothpaste composition that can prevent oral wounds and inflammation.

본 발명의 일 실시예에 따른 광촉매 함유 치약 조성물은, TiO2 광촉매, pH 의존형 발색제, 바인더 및 용제를 포함한다.The photocatalyst-containing toothpaste composition according to the embodiment of the present invention includes a TiO 2 photocatalyst, a pH-dependent color developer, a binder, and a solvent.

또한, 본 발명의 일 실시예에 따르면, 상기 TiO2 광촉매는 TiO2를 분말 형태로 포함하며, TiO2는 150um 내지 250um의 직경을 가질 수 있다.In addition, according to an embodiment of the present invention, the TiO 2 photocatalyst includes TiO 2 in powder form, and TiO 2 may have a diameter of 150 μm to 250 μm.

또한, 본 발명의 일 실시예에 따르면, 상기 pH 의존형 발색제는 Laccaic acid B를 포함할 수 있다.In addition, according to one embodiment of the present invention, the pH-dependent color developer may include Laccaic acid B.

또한, 본 발명의 일 실시예에 따르면, 상기 바인더는 HPC-L, HPC-H, HPC-ELF, HPC-HF, Polyox, Povidon K-30 MW, Povidon K-85/95, Kollidon VA64, pharmacote 645, pharmacote 615, pharmacote 603, Polyvinyl alcohol로 이루어진 그룹에서 선택된 어느 하나 이상을 포함할 수 있다.In addition, according to an embodiment of the present invention, the binder is HPC-L, HPC-H, HPC-ELF, HPC-HF, Polyox, Povidon K-30 MW, Povidon K-85 / 95, Kollidon VA64, pharmacote 645 It may include any one or more selected from the group consisting of pharmacote 615, pharmacote 603, polyvinyl alcohol.

또한, 본 발명의 일 실시예에 따르면, 소듐 알기네이트(sodium alginate), 키토산 염산염(Chitosan Hydrochloride), HPMC K100M 및 소듐 카복시메틸 셀룰로오스(sodium carboxymethyl cellulose)로 이루어진 그룹에서 선택된 어느 하나 이상을 포함하는 점도 조절제를 더 포함할 수 있다.In addition, according to an embodiment of the present invention, the viscosity including any one or more selected from the group consisting of sodium alginate, chitosan hydrochloride, HPMC K100M and sodium carboxymethyl cellulose It may further comprise a regulator.

또한, 본 발명의 일 실시예에 따르면, 상기 점도 조절제는 소듐 알기네이트 및 키토산 염산염을 포함할 수 있다.In addition, according to one embodiment of the present invention, the viscosity modifier may include sodium alginate and chitosan hydrochloride.

또한, 본 발명의 일 실시예에 따르면, 상기 TiO2 광촉매 100중량부, 상기 pH 의존형 발색제 450 내지 500중량부, 상기 바인더 20 내지 300중량부 및 상기 용제 1,500 내지 2,200중량부를 포함할 수 있다.In addition, according to one embodiment of the present invention, the TiO 2 photocatalyst may include 100 parts by weight, 450 to 500 parts by weight of the pH-dependent color developer, 20 to 300 parts by weight of the binder, and 1,500 to 2,200 parts by weight of the solvent.

본 발명의 실시예들은 광촉매를 포함하는 치약 조성물을 통하여 치아의 미백 효과를 달성하고, 칫솔에 광촉매를 보다 강하게 바인딩시켜 칫솔의 보관 과정에서 광조사를 통한 항균 효과를 극대화할 수 있다.Embodiments of the present invention can achieve a whitening effect of the tooth through the toothpaste composition comprising a photocatalyst, and bind the photocatalyst to the toothbrush more strongly to maximize the antibacterial effect through light irradiation in the storage process of the toothbrush.

또한, 본 발명의 실시예들에 따른 치약 조성물은 pH에 따라 색상이 변화하는 발색제를 포함하여 최적의 양치 환경에서 양치질하여 잇몸 및 치아의 충격을 최소화할 수 있도록 시각화가 가능하다.In addition, the toothpaste composition according to the embodiments of the present invention can be visualized to minimize the impact of the gums and teeth by brushing in an optimal toothbrushing environment including a color changing agent that changes color depending on the pH.

또한, 본 발명의 실시예들에 따른 치약 조성물은 구강 질환 예방을 위한 키토산 및 알긴산을 더 포함하여 구강 내 상처 및 염증을 예방할 수 있다.In addition, the toothpaste composition according to the embodiments of the present invention may further include chitosan and alginic acid for the prevention of oral diseases to prevent oral wounds and inflammation.

도 1은 본 발명의 실시예에 따른 치약 조성물의 TiO2의 활성 및 미백 효과를 확인하기 위한 실험 결과를 나타내는 사진이다.
도 2는 발명의 실시예에 따른 치약 조성물의 미백 효과를 확인하기 위한 실험 결과를 나타내는 사진이다.
도 3은 본 발명의 실시예에 따른 치약 조성물의 구강내 환경을 시각화하는지 여부를 확인하기 위한 실험 결과를 나타내는 사진이다.
1 is a photograph showing the experimental results for confirming the activity and whitening effect of TiO 2 of the toothpaste composition according to an embodiment of the present invention.
Figure 2 is a photograph showing the experimental results for confirming the whitening effect of the toothpaste composition according to an embodiment of the invention.
3 is a photograph showing an experimental result for confirming whether or not to visualize the oral environment of the toothpaste composition according to an embodiment of the present invention.

이하에서는 본 발명의 이해를 돕기 위하여 실시예를 들어 상세하게 설명하기로 한다. 다만, 하기의 실시예는 본 발명의 내용을 예시하는 것일 뿐, 본 발명의 범위가 하기 실시예에 한정되는 것은 아니다. 본 발명의 실시예는 당업계에서 평균적인 지식을 가진 자에게 본 발명을 보다 완전하게 설명하기 위해 제공되는 것이다. 본 발명은 여기서 제시한 실시예만으로 한정되지 않고 다른 형태로 구체화될 수도 있다.Hereinafter will be described in detail with reference to Examples to help the understanding of the present invention. However, the following examples are merely to illustrate the content of the present invention, the scope of the present invention is not limited to the following examples. The embodiments of the present invention are provided to more completely explain the present invention to those skilled in the art. The invention is not limited to the examples presented herein but may be embodied in other forms.

본 발명은 치약 조성물에 관한 것으로서, 보다 상세하게는 광촉매 함유 치약 조성물에 관한 것이다. 본 발명의 치약 조성물은, TiO2 광촉매, pH 의존형 발색제, 바인더 및 용제를 포함한다.The present invention relates to a toothpaste composition, and more particularly to a photocatalyst-containing toothpaste composition. The dentifrice composition of the present invention, a TiO 2 photocatalyst, pH-dependent coloring agents, binders and solvents.

광촉매는 일반적으로 광화학 반응을 촉진시키는 물질을 말하며, 예를 들어, TiO2 광촉매를 사용할 수 있다. 이산화타이타늄(TiO2)은 자외선이 조사되면 물과 반응하여 활성 산소를 유도하며 활성 산소는 세균 등의 유해물질, 예를 들어, 칫솔모의 세균 등을 산화 분해하거나 치아의 치태 내지 치석, 그리고 치아에 침착된 색소 성분을 산화 분해시킬 수 있다.The photocatalyst generally refers to a substance that promotes a photochemical reaction, and for example, a TiO 2 photocatalyst may be used. When titanium dioxide (TiO 2 ) is irradiated with UV light, it reacts with water to induce free radicals, and free radicals oxidatively decompose harmful substances such as bacteria, for example, bacteria in brush heads, or in dental plaque, tartar, and teeth. The deposited pigment component can be oxidatively decomposed.

기본적으로 광촉매라 함은 광이 제공되어야 제 역할을 할 수 있는 것으로, 위 광촉매는 자연적으로 존재하는 자연광 중 자외선에 의하여 촉매 역할을 어느 정도 할 수 있을 뿐만 아니라, 치약 조성물이 사용되는 환경, 예를 들어 자외선을 조사할 수 있는 칫솔 및 칫솔모와 함께 사용되는 경우에는 그 효과를 극대화할 수 있다.Basically, photocatalyst means that light can be provided to play a role, and the photocatalyst can not only act as a catalyst by ultraviolet rays among natural light existing naturally, but also an environment in which toothpaste compositions are used. For example, when used in conjunction with the toothbrush and bristles that can irradiate ultraviolet rays can maximize the effect.

TiO2 광촉매는 TiO2를 분말 형태로 포함하며, TiO2는 150um 내지 250um의 직경을 가지는 것을 사용할 수 있다.The TiO 2 photocatalyst includes TiO 2 in powder form, and TiO 2 may be used having a diameter of 150 μm to 250 μm.

TiO2 광촉매는 최적의 미백 효과 및 항균 효과를 달성하고, 인체에 무해한 수준의 안전성 확보 및 계면 활성제 및 보존제의 사용을 최소화하하기 위하여 150um 내지 250um의 직경을 가지는 것을 사용할 수 있다.TiO 2 photocatalyst may be used having a diameter of 150um to 250um to achieve the optimal whitening and antimicrobial effect, to minimize the use of surfactants and preservatives and to ensure a level of safety harmless to the human body.

TiO2 광촉매의 직경이 150um 미만인 경우에는 입자가 너무 작아 피부 투과 가능한 사이즈로서 양치 후 인체로 흡수될 확률이 증가하여 안전성 확보에 문제가 있고, TiO2 광촉매의 직경이 250um를 초과하는 경우에는 입자가 커서 함량 대비 전체 표면적이 감소하여 일반적인 양치 시간 등 양치 환경에서 항균 등을 위한 충분한 활성산소를 만들어내기 어려워 충분한 항균 효과를 얻기 어려운 문제점이 있다.If the diameter of the TiO 2 photocatalyst is less than 150 μm, the particle size is too small to penetrate the skin, and thus the probability of absorption into the human body after brushing increases, which is a problem in securing safety. When the diameter of the TiO 2 photocatalyst exceeds 250 μm, Since the total surface area is reduced compared to the cursor content, it is difficult to produce sufficient active oxygen for antibacterial in the fern environment, such as general fern time, it is difficult to obtain a sufficient antibacterial effect.

일반적으로 양치는 식사 후 어느정도 시간이 지난 후 하여야 잇몸 및 치아의 충격을 최소화할 수 있다. 구강 내 환경은 시간에 따라 변화가 나타나며, 식사 전후로 pH의 변화가 심하며, 예를 들어, 식사를 마친 직후에는 섭취한 음식으로 인하여 입안의 pH가 낮아 바로 양치질을 하게 되면 칫솔모가 치아 및 잇몸의 외부벽(에나멜)을 긁어내어 치아의 건강에 매우 좋지 않다. 특히 양치 전에 탄산수 또는 맥주 등을 마셨을 경우에는 더욱 치명적일 수 있다. 즉, 양치질은 최적의 양치 환경에서 진행되어야 잇몸 및 치아의 건강을 유지할 수 있다. 그러나, 구강 내 환경의 모니터링은 용이하지 않으므로 이를 시각적으로 표현하여 사용자에게 양치 환경을 알려 줄 필요성이 있다.In general, brushing teeth after a certain amount of time to minimize the impact of the gums and teeth. The oral environment changes with time, and the pH changes significantly before and after a meal.For example, immediately after a meal, when the toothbrush is brushed due to low pH in the mouth due to the ingested food, the bristles are external to the teeth and gums. Scraping off the wall (enamel) is very bad for the health of your teeth. Especially if you drank carbonated water or beer before brushing your teeth, it can be more lethal. That is, brushing teeth can be maintained in the optimal brushing environment to maintain the health of the gums and teeth. However, since the monitoring of the oral environment is not easy, there is a need to inform the user of the brushing environment by visually expressing it.

따라서, 본 발명의 치약 조성물은 pH 의존형 발색제를 포함한다. 예를 들어, pH 의존형 발색제는 Laccaic acid B를 포함할 수 있다. 치약 조성물은 pH에 따라 색상이 변화하는 발색제를 포함하여 최적의 양치 환경에서 양치질하여 잇몸 및 치아의 충격을 최소화할 수 있게 된다. 예를 들어, 상기 Laccaic acid B는 pH 3에서는 옅은 오렌지색을 띄고 pH 6이상에서는 보라색을 띈다.Accordingly, the toothpaste composition of the present invention comprises a pH dependent color developer. For example, the pH dependent color developer may include Laccaic acid B. Toothpaste compositions include a coloring agent that changes color depending on pH, so as to brush in an optimal toothbrushing environment to minimize the impact of gums and teeth. For example, the Laccaic acid B is pale orange at pH 3 and purple at pH 6 and above.

따라서, 본 발명의 치약 조성물은 pH 의존형 발색제를 포함함에 따라 양치시 구강 내 pH 환경을 시각적으로 나타내어 줄 수 있어 사용자의 반복적인 사용에 따라 적절한 양치 시점을 알려줄 수 있다. 뿐만 아니라, pH 의존형 발색제는 치아의 치태를 염색하여 치태의 위치를 더 상세하게 알려줄 수 있어 치태의 제거를 통한 치석의 형성을 억제할 수 있는 효과가 있다.Therefore, the toothpaste composition of the present invention can visually represent the pH environment in the oral cavity when brushing, as it includes a pH-dependent colorant, so as to indicate a proper brushing time according to the repeated use of the user. In addition, the pH-dependent color developer can stain the plaque of the tooth can tell the location of the plaque in more detail has the effect of inhibiting the formation of plaque through the removal of plaque.

본 발명의 치약 조성물은 칫솔모에 TiO2 광촉매를 바인딩시키기 위한 바인더를 포함한다. 예를 들어, 바인더는 HPC-L, HPC-H, HPC-ELF, HPC-HF, Polyox, Povidon K-30 MW, Povidon K-85/95, Kollidon VA64, pharmacote 645, pharmacote 615, pharmacote 603, Polyvinyl alcohol로 이루어진 그룹에서 선택된 어느 하나 이상을 포함할 수 있다.The toothpaste composition of the present invention comprises a binder for binding the TiO 2 photocatalyst to the bristles. For example, the binder may be HPC-L, HPC-H, HPC-ELF, HPC-HF, Polyox, Povidon K-30 MW, Povidon K-85 / 95, Kollidon VA64, pharmacote 645, pharmacote 615, pharmacote 603, Polyvinyl It may contain any one or more selected from the group consisting of alcohols.

기존의 치약 조성물에는 본 발명에서 목적하는 TiO2 광촉매를 칫솔모에 바인딩시키는 것이 요구되지 않으며 기타 칫솔모에 바인딩 시킬 구성이 없으므로 일반적으로 바인더를 포함하지 않는다. 특히, 본 천연 광촉매 기술을 이용한 구강관리시스템에서는 마이크로화된 TiO2 광촉매를 치솔모(광모)에 선택적으로 바인딩하고 유지하는 것은 양치 시간/환경에서 광촉매를 통해 활성 산소를 생성하기 위해서는 필수적인 기술이다.Existing toothpaste composition does not require binding of the TiO 2 photocatalyst desired in the present invention to the bristles and does not generally include a binder since there is no configuration to bind to other bristles. In particular, in the oral care system using the natural photocatalyst technology, selectively binding and maintaining the micronized TiO 2 photocatalyst to the bristles (bristle) is an essential technique for generating active oxygen through the photocatalyst at the time of brushing / environment.

상기 바인더들은 TiO2 광촉매를 칫솔모에 일정 시간 동안 강하게 부착시켜 양치질 후에도 칫솔모에 일부 잔여량이 남아있어 칫솔의 보관 중에도 항균 효과를 나타낸다.The binders strongly adhere TiO 2 photocatalyst to the bristles for a certain period of time, so that some residual amount remains on the bristles even after brushing, thus exhibiting antibacterial effect even during storage of the toothbrush.

본 발명에 있어서, TiO2 광촉매를 칫솔모에 일정 시간 이상 붙게 하기 위하여는 고점도의 폴리머가 필요하며, 고점도를 가지는 바인더로 점도가 낮아진 후에도 여전히 칫솔모와의 바인딩 효과를 유지할 수 있는 셀룰로오스계열의 폴리머를 사용하는 것이 바람직하다. 셀룰로오스계열의 폴리머는 높은 분자량을 지니므로 이를 바인더로 사용하여 고점도를 유지할 수 있으며, 이에 TiO2 광촉매가 칫솔모에 일정 시간 이상 부착되어 있을 수 있다.In the present invention, in order to adhere the TiO 2 photocatalyst to the bristles for a predetermined time, a polymer having a high viscosity is required, and a cellulose-based polymer that can maintain the binding effect with the bristles is still used even after the viscosity is reduced with a binder having a high viscosity. It is desirable to. Since the cellulose-based polymer has a high molecular weight, it may be used as a binder to maintain high viscosity, and thus TiO 2 photocatalyst may be attached to the bristles for a predetermined time.

본 발명의 치약 조성물은 상기 TiO2 광촉매 100중량부, 상기 pH 의존형 발색제 450 내지 500중량부, 상기 바인더 20 내지 300중량부 및 상기 용제 1,500 내지 2,200중량부를 포함한다.Toothpaste composition of the present invention comprises 100 parts by weight of the TiO 2 photocatalyst, 450 to 500 parts by weight of the pH-dependent color developer, 20 to 300 parts by weight of the binder and 1,500 to 2,200 parts by weight of the solvent.

상기 pH 의존형 발색제의 함량이 상기 TiO2 광촉매 100중량부에 대하여, 450중량부 미만인 경우 변색 효과가 두드러지지 않아 육안으로 관찰이 어려우며 치태까지 착색시키기 어려운 문제점이 있고, 500중량부 초과하여 첨가하더라도 그 효과가 미미하다.When the content of the pH-dependent color developer is less than 450 parts by weight based on 100 parts by weight of the TiO 2 photocatalyst, the discoloration effect is not noticeable, so it is difficult to visually observe and difficult to color until plaque, and even if added in excess of 500 parts by weight The effect is minimal.

상기 바인더의 함량이 상기 TiO2 광촉매 100중량부에 대하여, 20중량부 미만인 경우 충분한 바인딩 효과를 나타내기 어렵고, 제조 공정 중에 하이드로겔 형성이 어려워 TiO2 광촉매와의 충분한 분산이 어렵다. 또한, 상기 바인더의 함량이 300중량부 초과인 경우 제조 공정 중에 겔화되지 않고 서로 엉겨 붙게 되어 유동성을 확보할 수 없는 문제점이 있다.When the content of the binder is less than 20 parts by weight based on 100 parts by weight of the TiO 2 photocatalyst, it is difficult to exhibit a sufficient binding effect, and it is difficult to form a hydrogel during the manufacturing process, so that sufficient dispersion with the TiO 2 photocatalyst is difficult. In addition, when the content of the binder is more than 300 parts by weight, there is a problem in that the fluidity is not secured due to entanglement with each other without gelation during the manufacturing process.

상기 용제의 함량은 상기 TiO2 광촉매 100중량부에 대하여, 1,500 내지 2,200중량부의 범위로 포함하는 것이 바람직하다. 상기 용제는 정제수를 사용할 수 있으며, TiO2 광촉매, 바인더와 혼합하여 적정 점도를 가지는 하이드로겔을 제조하기 위한 것이다.The content of the solvent is preferably included in the range of 1,500 to 2,200 parts by weight based on 100 parts by weight of the TiO 2 photocatalyst. The solvent may be purified water, and mixed with a TiO 2 photocatalyst and a binder to prepare a hydrogel having an appropriate viscosity.

상기 TiO2 광촉매는 대체로 함량의 증가로 미백 및 항균 효과가 증가하나, 그 농도가 너무 높으면 촉매 반응이 더디게 일어나 양치 중 충분한 활성산소를 만들어 낼 수 없으며, 너무 낮으면 촉매 반응이 일어나지 않게 되어 미백 효과 및 항균 효과를 얻을 수 없다.The TiO 2 photocatalyst generally increases the whitening and antibacterial effect due to the increase in the content, but if the concentration is too high, the catalytic reaction is slow to produce sufficient free radicals in the fern, and if the concentration is too low, the catalytic reaction does not occur. And antibacterial effect is not obtained.

본 발명의 치약 조성물은 점도 조절제를 더 포함하며, 상기 점도 조절제는 예를 들어, 소듐 알기네이트(sodium alginate), 키토산 염산염(Chitosan Hydrochloride), HPMC K100M 및 소듐 카복시메틸 셀룰로오스(sodium carboxymethyl cellulose)로 이루어진 그룹에서 선택된 어느 하나 이상을 포함할 수 있다.The toothpaste composition of the present invention further comprises a viscosity modifier, the viscosity modifier is composed of, for example, sodium alginate, chitosan hydrochloride, HPMC K100M and sodium carboxymethyl cellulose It may include any one or more selected from the group.

알긴산(Alginic acid)은 소듐 알기네이트(sodium alginate)의 형태로 제공될 수 있다. 소듐 알기네이트는 유기용매에 용해되지 않으며, 물에서 서서히 용해되어 점성을 가지는 콜로이드 용액(colloidal solution)을 형성한다. 소듐 알기네이트는 pH 3 미만의 산성용액에 녹지 않으며 침전되고, pH 3~7에서 약 20~200cps의 점도를 나타내고, pH 4에서 약 100cps의 점도를 가진다. 알긴산염은 약 pH 3에서부터 서서히 용해되기 시작하고, pH 5에서부터 강하게 용해된다.Alginic acid may be provided in the form of sodium alginate. Sodium alginate is not soluble in organic solvents, but is slowly dissolved in water to form a viscous colloidal solution. Sodium alginate does not dissolve in acidic solutions below pH 3 and precipitates, exhibits a viscosity of about 20-200 cps at pH 3-7 and a viscosity of about 100 cps at pH 4. Alginate begins to dissolve slowly from about pH 3 and strongly dissolves from pH 5.

키토산(chitosan)은 하기 화학식 1의 기본 구조식을 가진다.Chitosan has a basic structural formula of Chemical Formula 1 below.

Figure pat00001
[화학식 1]
Figure pat00001
[Formula 1]

키토산(chitosan)은 키토산 염산염(Chitosan Hydrochloride)의 형태로 제공될 수 있다. 키토산 염산염은 물에 약간 용해되기는 하나 에탄올에 쉽게 용해되며, 또한 희석된 유기산 용액에 쉽게 용해되고, pH 6.5 이상의 중성 또는 약 알칼리성 용액에는 거의 용해되지 않는다. 키토산의 용해도는 용액의 이온강도가 높을수록 염석 효과에 따라 용해도가 낮아지며, 낮은 pH에서는 점도가 높으나 pH가 높아질수록 점도가 낮아지게 된다. 키토산은 약 pH 4에서부터 서서히 용해되기 시작하고, pH 6에서부터 강하게 용해된다. 특히, 키토산은 생분해성(biodegradable)한 물질로 인체에 무해하다.Chitosan may be provided in the form of Chitosan Hydrochloride. Chitosan hydrochloride, although slightly soluble in water, is easily soluble in ethanol, is also readily soluble in dilute organic acid solutions and hardly soluble in neutral or slightly alkaline solutions above pH 6.5. The solubility of chitosan is lower in solubility according to the salting effect as the ionic strength of the solution is higher. The viscosity is higher at low pH, but is lower as the pH is higher. Chitosan begins to dissolve slowly from about pH 4 and strongly dissolves from pH 6. In particular, chitosan is a biodegradable substance that is harmless to humans.

양이온을 띄는 키토산은 상기 바인더와 함께 보조적으로 바인딩 효과를 더욱 촉진시키며 TiO2와 칫솔모에 순간적으로 붙어 활성 산소를 생산하게 되며, 이 양이온성 폴리머는 세균들의 치태(biofilm) 형성을 저해시킬 수 있다.The cationic chitosan, together with the binder, further promotes the binding effect and instantaneously attaches to TiO 2 and bristles to produce free radicals, and this cationic polymer can inhibit the formation of bacteria's biofilm.

HPMC는 하기 화학식 2의 기본 구조식을 가진다.HPMC has a basic structural formula of formula (2).

Figure pat00002
[화학식 2]
Figure pat00002
[Formula 2]

HPMC는 HPMC K100M 일 수 있다.HPMC may be HPMC K100M.

HPMC K100M은 파우더 형태로 공급되어 찬물에서 서서히 용해되며 점성의 콜로이드를 형성한다. HPMC K100M은 하이드록시프로필 메틸셀룰로스(hydroxypropyl methylcellulose, HPMC) 계열이므로 분자량(Grade)별로 다양한 점도를 가지고 있으며, 2% (w/v) 수용액에서 약 100,000 mpas의 점도를 가진다.HPMC K100M is supplied in powder form and slowly dissolves in cold water to form viscous colloids. Since HPMC K100M is a hydroxypropyl methylcellulose (HPMC) series, it has various viscosities according to molecular weight (Grade), and has a viscosity of about 100,000 mpas in 2% (w / v) aqueous solution.

CMC(carboxymethyl cellulose)는 하기 화학식 3의 기본 구조식을 가진다.CMC (carboxymethyl cellulose) has a basic structural formula of the following formula (3).

Figure pat00003
[화학식 3]
Figure pat00003
[Formula 3]

CMC는 소듐 카복시메틸 셀룰로오스(sodium carboxymethyl cellulose)의 파우더 형태로 제공될 수 있다. 소듐 카복시메틸 셀룰로오스는 치약 등 점도 조절제, 습윤제 그리고 안정화제 등의 용도로 널리 사용된다. CMC는 약 1.2% w/v 수성 분산액에서 pH 6~8을 나타내며, 첨가시 하이드로콜로이드(hydrocolloid)를 형성하고, 치약 조성물에 점탄성을 부여한다.CMC may be provided in the form of a powder of sodium carboxymethyl cellulose. Sodium carboxymethyl cellulose is widely used for applications such as viscosity modifiers, wetting agents and stabilizers such as toothpaste. CMC exhibits a pH of 6-8 in about 1.2% w / v aqueous dispersion, forms hydrocolloids upon addition and imparts viscoelasticity to the toothpaste composition.

바람직하게는, 상기 치약 조성물에 포함되는 점도 조절제는 소듐 알기네이트 및 키토산 염산염을 포함하여 사용될 수 있다.Preferably, the viscosity modifier included in the dentifrice composition may be used including sodium alginate and chitosan hydrochloride.

구강 질환의 예방을 위하여는 구강 내 상처를 치유 및 회복시키는 것이 가장 중요하며, 소듐 알기네이트 및 키토산 염산염의 조합은 구강 내 상처 및 염증을 예방 및 치유할 수 있는 성분 조합이다. For the prevention of oral diseases, it is most important to heal and repair the oral wounds, and the combination of sodium alginate and chitosan hydrochloride is a combination of ingredients that can prevent and heal oral wounds and inflammation.

소듐 알기네이트 및 키토산 염산염은 1:1 내지 1:10의 중량 비율로 혼합되어 사용될 수 있다.Sodium alginate and chitosan hydrochloride can be mixed and used in a weight ratio of 1: 1 to 1:10.

소듐 알기네이트는 구강 내 잇몸의 상처에 피막을 형성하는 역할을 한다. 소듐 알기네이트는 상처 주변 혈관에 침투하여 점성도를 증가시키고 상처 주변의 피브린과 용이하게 결합하여 상처 주변에 섬유상 입자를 형성하여 지혈을 할 수 있다. 소듐 알기네이트는 다가 음이온성 중합체로 분자량이 클수록 점성도가 증가하며 따라서 분자량과 그 효과는 정비례한다. 예를 들어, 소듐 알기네이트의 분자량은 100~1,000kDa일 수 있다.Sodium alginate serves to form a coating on the wound of the gum in the oral cavity. Sodium alginate penetrates the blood vessels around the wound to increase its viscosity and easily binds to fibrin around the wound, forming fibrous particles around the wound for hemostasis. Sodium alginate is a polyvalent anionic polymer, the higher the molecular weight, the higher the viscosity and thus the molecular weight and its effect are directly proportional. For example, the molecular weight of sodium alginate may be 100-1,000 kDa.

키토산 염산염은 구강 내 잇몸의 상처에 따른 세균 증식을 억제하는 정균(bacteriostatic) 작용을 한다. 또한, 키토산 염산염은 세균 표면의 소수성을 감소시켜 치아의 법랑질(에나멜)의 부착을 감소시킬 수 있어 치태 형성을 저해할 뿐만 아니라, 잇몸 상처의 재생, 항균 활성의 효과가 있으며, 생분해성이라는 장점이 있다(Journal of Oral Biosciences 59 (2017) 205-210). 키토산 염산염은 다가 양이온성 중합체로 분자량이 전하 운반력에 영향을 미치므로 분자량과 그 효과는 정비례한다. 예를 들어, 키토산 염산염의 분자량은 100~2,000kDa일 수 있다.Chitosan hydrochloride has a bacteriostatic action that inhibits bacterial growth due to wounds of the gums in the oral cavity. In addition, chitosan hydrochloride can reduce the hydrophobicity of the bacterial surface, thereby reducing the adhesion of enamel (enamel) of the tooth, which not only inhibits plaque formation, but also has the effect of regenerating gum wounds, antibacterial activity, and biodegradability. (Journal of Oral Biosciences 59 (2017) 205-210). Chitosan hydrochloride is a polyvalent cationic polymer, whose molecular weight affects the charge-carrying capacity, so the molecular weight and its effects are directly proportional. For example, the molecular weight of chitosan hydrochloride may be 100-2,000 kDa.

본 발명의 치약 조성물은 상기 성분들 뿐만 아니라 연마제, 기포제, 습윤제, 감미제, 착향제, 불화물, 안정화제 등 치약의 목적을 달성하기 위한 기타 성분들을 적절히 혼합하여 제조될 수 있다.The toothpaste composition of the present invention may be prepared by appropriately mixing not only the above ingredients but also other ingredients for achieving the purpose of the toothpaste such as abrasives, foaming agents, wetting agents, sweeteners, flavoring agents, fluorides, stabilizers and the like.

이하, 본 발명의 치약 조성물에 관한 실시예를 통하여 보다 상세히 설명하도록 한다.Hereinafter, the embodiment of the toothpaste composition of the present invention will be described in more detail.

실시예Example

본 발명의 실시예에 따른 치약 조성물은 하기 표 1 및 표 2에 따라 각 성분들을 혼합하여 제조하였다. 치약 조성물은 2개의 층으로 분리하여 제조하였다.Toothpaste composition according to an embodiment of the present invention was prepared by mixing each component according to Table 1 and Table 2. Toothpaste compositions were prepared separately in two layers.

첫번째 층은 TiO2 광촉매를 함유하는 층으로 하기 표 1의 성분에 따라 제조하였으며, TiO2 분말을 바인더와 적량의 용제와 혼합하여 하이드로겔을 제조하여 혼합기(Ultrasonic Homogenizer)에서 TiO2를 충분히 분산시켰다. 추가로 점증제를 넣어 교반 후 기포를 제거하여 TiO2를 포함하는 첫번째 층을 제조하였다.The first layer was a layer containing TiO 2 photocatalyst, which was prepared according to the components shown in Table 1 below, and TiO 2 powder was mixed with a binder and an appropriate amount of solvent to prepare a hydrogel, thereby sufficiently dispersing TiO 2 in a mixer (Ultrasonic Homogenizer). . Further adding a thickener to remove the bubbles after stirring to prepare a first layer containing TiO 2 .

성분ingredient 실시예1Example 1 실시예2Example 2 실시예3Example 3 실시예4Example 4 실시예5Example 5 실시예6Example 6 TiO2 (200um)TiO 2 (200um) 1.5g1.5 g 1.5g1.5 g 1.5g1.5 g 1.5g1.5 g 1.5g1.5 g 1.5g1.5 g Laccaic acid BLaccaic acid B 7.0g7.0 g 7.0g7.0 g 7.0g7.0 g 7.0g7.0 g 7.0g7.0 g 7.0g7.0 g HPMC(K100M)HPMC (K100M) 0.6g0.6g -- -- -- -- -- Polyox(LEO NF)Polyox (LEO NF) -- 0.3g0.3 g -- -- -- -- HPC-HFHPC-HF -- -- 0.9g0.9 g 0.6g0.6g -- 0.6g0.6g Povidone 90FPovidone 90F -- -- 3.0g3.0 g -- 3.0g3.0 g 3.0g3.0 g Sodium carboxymethyl celluloseSodium carboxymethyl cellulose -- -- -- -- 0.6g0.6g -- Hydrated silicon dioxideHydrated silicon dioxide -- -- 1.0g1.0 g -- 6.0g6.0 g 1.0g1.0 g Chitosan HydrochlorideChitosan Hydrochloride -- -- -- -- -- 0.3g0.3 g sodium alginatesodium alginate -- -- -- -- -- 0.2g0.2 g 정제수Purified water 30.0g30.0 g 30.0g30.0 g 30.0g30.0 g 30.0g30.0 g 30.0g30.0 g 30.0g30.0 g

첫번째 층을 보조하는 치약 보조층으로서 두번째 층을 제조하였으며, 두번째 층은 하기 표 2의 성분에 따라 제조하였으며, 계면활성제 등 기타 추가적인 첨가제를 적량의 용제에 넣고 교반하고, 점증제를 첨가하여 기포를 제거하고 첫번째 층과 유사한 점도로 제조하였다.A second layer was prepared as a toothpaste auxiliary layer to assist the first layer, and the second layer was prepared according to the ingredients shown in Table 2 below. Removed and made to a viscosity similar to the first layer.

성분ingredient 함량content Sodium lauryl sulfateSodium lauryl sulfate 2.0g2.0 g Sodium carboxymethyl celluloseSodium carboxymethyl cellulose 0.9g0.9 g Hydrated silicon dioxideHydrated silicon dioxide 9.0g9.0 g D-Sorbitol solutionD-Sorbitol solution 60.0g60.0 g Polyethylen glycol 1500Polyethylen glycol 1500 1.5g1.5 g xylitolxylitol 4.0g4.0g Saccharin Sodium HydrateSaccharin Sodium Hydrate 0.7g0.7 g Ascorbic acidAscorbic acid 0.5g0.5g Citric Acid HydrateCitric acid hydrate 0.1g0.1g L-MentholL-Menthol 0.2g0.2 g Citrus Flavo HF-60052Citrus Flavo HF-60052 0.1g0.1g 정제수Purified water 30.0g30.0 g

즉, 본 발명의 실시예에 따른 치약 조성물은 2개의 층으로 분리하여 제조한 후, 2개의 층을 동시에 치약 튜브에 충진하였다.That is, the toothpaste composition according to the embodiment of the present invention was prepared by separating the two layers, and the two layers were simultaneously filled in the toothpaste tube.

비교예Comparative example

비교예에 따른 치약 조성물은 상기 실시예와 동일하게 2개의 층으로 분리하여 제조하였다. 실시예의 첫번째 층에 대응되는 비교예의 첫번째 층은 하기 표 3에 따라 각 성분들을 혼합하여 제조하였다. 두번째 층은 상기 실시예와 동일하게 상기 표 2에 따라 제조하였다.Toothpaste composition according to a comparative example was prepared by separating into two layers in the same manner as in the above example. The first layer of the comparative example corresponding to the first layer of the example was prepared by mixing the respective components according to Table 3 below. The second layer was prepared according to Table 2, in the same manner as in the above example.

성분ingredient 비교예1Comparative Example 1 비교예2Comparative Example 2 TiO2 TiO 2 -- 200nm, 1.5g200 nm, 1.5 g Laccaic acid BLaccaic acid B -- 7.0g7.0 g Povidone 30FPovidone 30F -- -- Sodium carboxymethyl celluloseSodium carboxymethyl cellulose 0.6g0.6g 0.6g0.6g Hydrated silicon dioxideHydrated silicon dioxide 6.0g6.0 g 6.0g6.0 g 정제수Purified water 30.0g30.0 g 30.0g30.0 g

이후, 비교예에 따른 치약 조성물은 2개의 층으로 분리하여 제조한 후, 2개의 층을 동시에 치약 튜브에 충진하였다.Thereafter, the toothpaste composition according to the comparative example was prepared by separating the two layers, and the two layers were simultaneously filled in the toothpaste tube.

실험예Experimental Example

실험예Experimental Example 1 One

본 발명의 실시예 및 비교예에 따른 치약 조성물들의 항균 효과 및 미백 효과를 확인하기 위하여 메틸렌블루환원 시험법에 따라 광촉매의 효과를 실험하였다. 실시예 1~6, 비교예 1에 따라 제조된 치약 조성물을 아래 활성 산소 방출 실험 및 미백 실험의 조건에 따라 수행하였다.In order to confirm the antibacterial and whitening effects of the toothpaste compositions according to the examples and comparative examples of the present invention, the effect of the photocatalyst was tested according to the methylene blue reduction test method. Toothpaste compositions prepared according to Examples 1 to 6 and Comparative Example 1 were performed according to the conditions of the following active oxygen release experiment and whitening experiment.

1. 활성산소 방출 실험1. Active Oxygen Release Experiment

반응조건: MB(1mg/40mL) 용액에 치약(100mg/100mL) 희석액을 혼합하여, 380nm 광원에 3분간 노출하고 활성산소를 측정하기 위해 자외선 분광광도계를 이용하여 흡광도(380nm)의 변화를 측정하였다.Reaction condition: Toothpaste (100 mg / 100 mL) diluent was mixed with MB (1 mg / 40 mL) solution, exposed to a 380 nm light source for 3 minutes, and the change in absorbance (380 nm) was measured using an ultraviolet spectrophotometer to measure the active oxygen. .

2. 미백 실험2. Whitening Experiment

일반적으로 메틸렌블루환원 시험법은 활성산소를 측정하는 시험법이나, 미백을 테스트하기 위하여 여기서 메틸렌블루 용액을 저농도로 희석하였으며, 메틸렌블루는 여기서 색소로 사용되었으며 활성산소 측정시 반응 조건 보다 치약을 더 희석하여 측정하였다.In general, methylene blue reduction test is a test method for measuring free radicals, but to test whitening, methylene blue solution was diluted to a low concentration, methylene blue was used as a pigment here, and toothpaste was more than reaction conditions when measuring free radicals. Measured by dilution.

반응조건: MB(1mg/100mL) 용액에 치약(100mg/10mL) 희석액을 혼합하여, 365nm 광원에 3분간 노출하고 자외선 분광광도계를 이용하여 흡광도(380nm)를 측정하였다.Reaction conditions: Toothpaste (100 mg / 10 mL) diluent was mixed with MB (1 mg / 100 mL) solution, exposed to a 365 nm light source for 3 minutes, and absorbance (380 nm) was measured using an ultraviolet spectrophotometer.

이에 따른 실험 결과는 하기 표 4와 같으며, 이를 도 1의 사진을 통하여 색상의 변화를 명확히 알 수 있다.The experimental results are shown in Table 4 below, and the change in color can be clearly seen through the photograph of FIG. 1.

미백 실험Whitening experiment 활성산소 방출 실험Free radical release experiment 광노출Light exposure 광차단Light blocking 광노출Light exposure 광차단Light blocking 실시예1Example 1 0.17650.1765 0.57860.5786 1.14821.1482 0.79320.7932 실시예2Example 2 0.16080.1608 0.60110.6011 1.16431.1643 0.88470.8847 실시예3Example 3 0.19840.1984 0.62740.6274 1.12401.1240 0.86790.8679 실시예4Example 4 0.18220.1822 0.60150.6015 1.15081.1508 0.81270.8127 실시예5Example 5 0.16880.1688 0.66070.6607 1.17041.1704 0.89440.8944 실시예6Example 6 0.18750.1875 0.63440.6344 1.15401.1540 0.88350.8835 비교예1Comparative Example 1 0.13010.1301 0.13240.1324 1.77341.7734 0.86170.8617

도 1의 상측의 사진은 비교예1에 따른 치약 조성물이고, 하측의 사진은 실시예1에 따른 치약 조성물이다. 좌측의 2개는 광원에 노출, 우측의 2개는 광원을 차단한 결과를 나타내는 것이다. 비교예1의 경우 TiO2가 미포함이므로 광원에 노출 또는 차단시 메틸렌블루의 분해가 일어나지 않음을 색상 변화가 없는 것으로 알 수 있다. 실시예1의 경우 TiO2가 포함이므로 광원의 차단시 메틸렌블루가 분해되지 않아 파란색을 띄나, 광원에 노출시 메틸렌블루가 분해되어 흰색을 띄는 것을 알 수 있다. 이에 따라, TiO2를 포함하는 본 발명의 실시예의 경우 광촉매가 충분한 미백 효과를 가지는 것을 확인할 수 있다.1 is a photo of the toothpaste composition according to Comparative Example 1, the lower photo is a toothpaste composition according to Example 1. Two on the left show the result of exposure to the light source, and two on the right show the result of blocking the light source. In Comparative Example 1, since TiO 2 is not included, it can be seen that there is no color change when methylene blue does not occur when exposed to or blocked by a light source. In Example 1, since TiO 2 is included, methylene blue does not decompose when the light source is blocked, but appears blue. Accordingly, in the case of the embodiment of the present invention containing TiO 2 it can be seen that the photocatalyst has a sufficient whitening effect.

표 4를 참조하면, 미백 실험 결과, TiO2를 포함하지 않는 비교예1의 경우에는 광을 조사하는 경우라도 광촉매에 의한 메틸렌블루의 색상 변화가 없어 광을 조사하거나 미조사하는 경우에 있어서 흡광도에 큰 차이가 없으나, 실시예들의 경우 광을 조사한 경우 흡광도가 현저히 줄어들어 미백 효과가 있음을 확인할 수 있었다.Referring to Table 4, as a result of the whitening experiment, in the case of Comparative Example 1, which does not contain TiO 2 , even when light is irradiated, there is no change in the color of methylene blue due to the photocatalyst, and thus the absorbance is obtained when light is irradiated or not irradiated. Although there is no big difference, in the case of the embodiment of the irradiation with light it was confirmed that the absorbance is significantly reduced whitening effect.

표 4에서, 활성산소 방출 실험은 미백 실험과 달리 고농도의 메틸렌블루로 진행되어, 광촉매에 의한 활성산소 증가에 따른 흡광도를 측정하였으며, 활성산소 증가시 흡광도 값은 낮은 값을 가진다. TiO2를 포함하지 않는 비교예1의 경우에는 광노출시 흡광도 값이 약 1.7정도로 높게 나타나나 TiO2를 포함하는 실시예들의 경우 약 1.1 정도로 낮은 값을 가짐을 알 수 있다.In Table 4, unlike the whitening experiment, the active oxygen release experiment proceeded to a high concentration of methylene blue, and measured the absorbance according to the increase of the active oxygen by the photocatalyst, and the absorbance value at the increase of the active oxygen has a low value. In the case of Comparative Example 1 that does not contain TiO 2 and it can be seen to have a lower value as about 1.1, if the embodiments shown to the light upon exposure to high absorbance values at about 1.7 and including TiO 2.

실험예Experimental Example 2 2

TiO2 광촉매의 바인딩 효과를 확인하기 위하여 칫솔모에 치약을 바른 후 일정 조건에 따른 실험시 TiO2 용출량을 측정하여 바인딩 효과를 확인하기 위한 실험을 진행하였다.To confirm the binding effect of TiO 2 photocatalyst, toothpaste was applied to the bristles, and the experiment was carried out to determine the binding effect by measuring the amount of TiO 2 elution during the experiment according to a predetermined condition.

실시예 1~6, 비교예 1, 2에 따라 제조된 치약 조성물을 동일한 칫솔 6개의 칫솔모에 각각 0.6g 씩 바른 후, 400ml 증류수가 담긴 비이커에 담근 후 180rpm으로 교반하였다. 시간대 별로 각 용액을 종이필터하고 세척하여 건조한 후 용출된 TiO2의 량을 마이크로 저울을 이용하여 측정하였다. 이에 따라 측정된 TiO2의 양은 첨가된 전체 TiO2의 양 대비하여 표현하였으며, 하기 표 5에 나타낸 바와 같다.0.6 g of the toothpaste compositions prepared according to Examples 1 to 6 and Comparative Examples 1 and 2 were respectively applied to six bristles of the same toothbrush, and then immersed in a beaker containing 400 ml of distilled water and stirred at 180 rpm. Each solution was time-filtered, washed with paper, dried and the amount of TiO 2 eluted was measured using a micro balance. Accordingly, compared to the amount it was represented by the amount of added TiO 2 the total of the measured TiO 2, as shown in Table 5 below.

용출된 TiO2의 양(%)% Of eluted TiO 2 실시예1Example 1 10분10 minutes 30분30 minutes 45분45 minutes 60분60 minutes 15.2515.25 25.4225.42 35.2435.24 49.7849.78 실시예2Example 2 10분10 minutes 30분30 minutes 45분45 minutes 60분60 minutes 12.2612.26 19.4419.44 48.9748.97 96.5596.55 실시예3Example 3 10분10 minutes 30분30 minutes 45분45 minutes 60분60 minutes 20.2620.26 34.4834.48 58.0058.00 98.2798.27 실시예4Example 4 10분10 minutes 30분30 minutes 45분45 minutes 60분60 minutes 21.5421.54 35.5435.54 56.5256.52 97.1597.15 실시예5Example 5 10분10 minutes 30분30 minutes 45분45 minutes 60분60 minutes 20.2120.21 34.5634.56 65.1265.12 98.7298.72 실시예6Example 6 10분10 minutes 30분30 minutes 45분45 minutes 60분60 minutes 18.5418.54 32.2532.25 55.2055.20 99.5899.58 비교예1Comparative Example 1 10분10 minutes 30분30 minutes 45분45 minutes 60분60 minutes 35.435.4 86.2486.24 97.2297.22 98.2698.26 비교예2(non-binder)Comparative Example 2 (non-binder) 10분10 minutes 30분30 minutes 45분45 minutes 60분60 minutes 37.8737.87 89.4789.47 97.2297.22 98.2698.26

표 5를 참조하면, 비교예들에 따른 치약 조성물들은 용출 실험 시작 후 약 10분 경과 후 전체 TiO2함량의 30% 이상이 용출되고 30분 경과시 85% 이상이 용출되었으나, 본 발명의 실시예들에 따른 치약 조성물들은 대부분 용출 실험 시작 후 약 10분 경과 후 전체 TiO2함량의 약 20% 내외로 용출되어 광촉매인 TiO2가 칫솔모에 부착된 후 용이하게 용출되지 않고 바인더와 함께 충분한 시간동안 부착되어 있는 것을 알 수 있다.Referring to Table 5, the toothpaste compositions according to the comparative examples were eluted at least 30% of the total TiO 2 content after about 10 minutes after the start of the dissolution experiment, and more than 85% after 30 minutes was eluted, Example of the present invention Most toothpaste compositions were eluted to about 20% of the total TiO 2 content after about 10 minutes after the start of the dissolution experiment, so that the photocatalyst TiO 2 was attached to the bristles and was not easily eluted. It can be seen that.

실험예Experimental Example 3 3

치약 조성물의 미백 효과를 확인하기 위하여 소의 치아를 홍차에 12시간 동안 담궈 착색시키고, 치아의 일부에 테이핑을 하고 주변에 실시예 1에 따른 치약을 전체적으로 도포하였다. 이후, 365nm 광원에 6시간 노출시킨 후 테이프를 제거한 후 육안으로 미백 효과를 관찰하였다. 이에 따른 결과는 도 2와 같다. 치약 조성물을 바른 곳의 색상이 테이핑한 곳의 색상과 확연히 차이가 있음을 알 수 있었다.To confirm the whitening effect of the toothpaste composition, the cow's teeth were dipped in black tea for 12 hours, colored, taped on a portion of the teeth, and the toothpaste according to Example 1 was applied to the whole. Thereafter, after exposure to 365nm light source for 6 hours, the tape was removed and the whitening effect was observed by naked eye. The result is as shown in FIG. It was found that the color of the place where the toothpaste composition was applied was significantly different from the color of the place where the tape was applied.

실험예Experimental Example 4 4

치약 조성물의 치아의 양치 환경을 확인하기 위하여, 소의 치아를 대상으로 실험을 진행하였다. 소의 치아를 물로 헹군 후, 실시예4에 따른 치약 조성물을 이용하여 양치를 5분간 진행하고 치아의 염색 상태를 확인하였다. 이와 달리 소의 치아를 음식물에 약 30분간 담가 두었다가 물로 헹군 후, 실시예4에 따른 치약 조성물을 이용하여 양치를 5분간 진행하고 치아의 염색 상태를 확인하였다. 이에 따른 결과는 도 3과 같으며, 우측이 음식물에 소의 치아를 담근 실험 결과를 나타낸다.In order to check the tooth environment of the tooth of the toothpaste composition, the experiment was conducted on the bovine teeth. After rinsing the cow's teeth with water, the toothpaste composition according to Example 4 was used for 5 minutes to check the staining state of the teeth. On the contrary, after soaking the cow's teeth in food for about 30 minutes and rinsing with water, using the toothpaste composition according to Example 4 proceeds to brushing for 5 minutes to check the staining state of the teeth. The result is the same as in Figure 3, the right side shows the results of experiments soaking the teeth of the cow in food.

따라서, 본 발명의 광촉매 함유 치약 조성물에 따르면, 치아의 미백 효과를 달성하고, 칫솔에 광촉매를 보다 강하게 바인딩시켜 칫솔의 보관 과정에서 광조사를 통한 항균 효과를 극대화할 수 있으며, pH에 따라 색상이 변화하는 발색제를 포함하여 최적의 양치 환경에서 양치질하여 잇몸 및 치아의 충격을 최소화할 수 있도록 시각화가 가능하다. 또한, 본 발명의 실시예들에 따른 치약 조성물은 구강 질환 예방을 위한 키토산 및 알긴산을 더 포함하여 구강 내 상처 및 염증을 예방할 수 있다.Therefore, according to the photocatalyst-containing toothpaste composition of the present invention, the whitening effect of the tooth is achieved, the photocatalyst is more strongly bound to the toothbrush, thereby maximizing the antibacterial effect through light irradiation in the storage process of the toothbrush, and the color according to the pH. It can be visualized to minimize the impact of gums and teeth by brushing in the optimal brushing environment, including changing colorants. In addition, the toothpaste composition according to the embodiments of the present invention may further include chitosan and alginic acid for the prevention of oral diseases to prevent oral wounds and inflammation.

상술한 바에 있어서, 본 발명의 예시적인 실시예들을 설명하였지만, 본 발명은 이에 한정되지 않으며 해당 기술 분야에서 통상의 지식을 가진 자라면 다음에 기재하는 특허청구범위의 개념과 범위를 벗어나지 않는 범위 내에서 다양한 변경 및 변형이 가능함을 이해할 수 있을 것이다.As described above, the exemplary embodiments of the present invention have been described, but the present invention is not limited thereto, and a person skilled in the art does not depart from the concept and scope of the following claims. It will be understood that various changes and modifications are possible in the following.

Claims (7)

TiO2 광촉매;
pH 의존형 발색제;
바인더; 및
용제를 포함하는 광촉매 함유 치약 조성물.
TiO 2 photocatalyst;
pH dependent coloring agents;
bookbinder; And
Photocatalyst-containing toothpaste composition comprising a solvent.
제1항에 있어서,
상기 TiO2 광촉매는 TiO2를 분말 형태로 포함하며, TiO2는 150nm 내지 250um의 직경을 가지는 것을 특징으로 하는 광촉매 함유 치약 조성물.
The method of claim 1,
The TiO 2 photocatalyst comprises TiO 2 in powder form, and TiO 2 has a diameter of 150 nm to 250 μm.
제1항에 있어서,
상기 pH 의존형 발색제는 Laccaic acid B를 포함하는 것을 특징으로 하는 광촉매 함유 치약 조성물.
The method of claim 1,
The pH-dependent color developing agent is a photocatalyst-containing toothpaste composition, characterized in that it comprises Laccaic acid B.
제1항에 있어서,
상기 바인더는 HPC-L, HPC-H, HPC-ELF, HPC-HF, Polyox, Povidon K-30 MW, Povidon K-85/95, Kollidon VA64, pharmacote 645, pharmacote 615, pharmacote 603, Polyvinyl alcohol로 이루어진 그룹에서 선택된 어느 하나 이상을 포함하는 광촉매 함유 치약 조성물.
The method of claim 1,
The binder consists of HPC-L, HPC-H, HPC-ELF, HPC-HF, Polyox, Povidon K-30 MW, Povidon K-85 / 95, Kollidon VA64, pharmacote 645, pharmacote 615, pharmacote 603, Polyvinyl alcohol Photocatalyst-containing toothpaste composition comprising any one or more selected from the group.
제1항에 있어서,
소듐 알기네이트(sodium alginate), 키토산 염산염(Chitosan Hydrochloride), HPMC K100M 및 소듐 카복시메틸 셀룰로오스(sodium carboxymethyl cellulose)로 이루어진 그룹에서 선택된 어느 하나 이상을 포함하는 점도 조절제를 더 포함하는 것을 특징으로 하는 광촉매 함유 치약 조성물.
The method of claim 1,
Photocatalyst containing, characterized in that it further comprises a viscosity modifier comprising any one or more selected from the group consisting of sodium alginate, chitosan hydrochloride, HPMC K100M and sodium carboxymethyl cellulose Toothpaste Composition.
제5항에 있어서,
상기 점도 조절제는 소듐 알기네이트 및 키토산 염산염를 포함하는 것을 특징으로 하는 광촉매 함유 치약 조성물.
The method of claim 5,
Wherein said viscosity modifier comprises sodium alginate and chitosan hydrochloride.
제1항에 있어서,
상기 TiO2 광촉매 100중량부;
상기 pH 의존형 발색제 450 내지 500중량부;
상기 바인더 20 내지 300중량부; 및
상기 용제 1,500 내지 2,200중량부를 포함하는 것을 특징으로 하는 광촉매 함유 치약 조성물.
The method of claim 1,
100 parts by weight of the TiO 2 photocatalyst;
450 to 500 parts by weight of the pH dependent color developer;
20 to 300 parts by weight of the binder; And
A photocatalyst-containing toothpaste composition comprising 1,500 to 2,200 parts by weight of the solvent.
KR1020180098959A 2018-08-24 2018-08-24 Toothpaste composition having photocatalyst KR102132705B1 (en)