KR20200017111A - Method for producing hair dye - Google Patents

Abstract

The present invention relates to a manufacturing method for a bento mineral mud aqueous solution for manufacturing a hypoallergenic hair dye, and a manufacturing method for a hair dye thereby. The disclosed manufacturing method for a bento mineral mud aqueous solution for manufacturing a hypoallergenic hair dye comprises: a pozzolan powder manufacturing step of sintering and crushing pozzolan trass and acquiring pozzolan powder; an ocher water manufacturing step of, after completion of the pozzolan powder manufacturing step, mixing the pozzolan powder in clean water, stirring and maturing the same to acquire supernatant ocher water; a green mud powder manufacturing step of sintering and grinding green mud bentonite to acquire green mud powder; a pearl powder manufacturing step of sintering and grinding pearls to acquire pearl powder; a mud aqueous solution manufacturing step of acquiring a mud aqueous solution by mixing the green mud powder and the pearl powder which are acquired in the green mud powder manufacturing step and the pearl powder manufacturing step, respectively, into the ocher water which is acquired in the ocher water manufacturing step, stirring, maturing, and drying the mixture; and a Bento fine mud aqueous solution manufacturing step of filtering the mud aqueous solution acquired in the mud aqueous solution manufacturing step for refining the same. The present invention can improve health of user′s hair and scalp.

Description

Method for preparing aqueous solution of bento mineral mud for the preparation of hypo-allergic hair dye and method for producing hair dye thereby {Method for producing hair dye}

The present invention relates to a method for preparing a bento mineral mud solution and a method for preparing a hair dye according to the present invention. The present invention relates to a method for preparing a bento mineral mud aqueous solution for producing a hypoallergenic hair dye having excellent water washing ability, excellent color development, various colors, and long lasting power, and a method for preparing the hair dye.

Hair dyes are used to artificially change the color of hair, and in recent years have been used as a means of expressing the appearance more attractive beyond the dyeing of white hair or swordfish. Hair dyes are called henna or chamomile by Egyptians about 4,000 years ago. Various hair dyes have been developed since the hair was dyed using dyes derived from plants.

These hair dyes are classified into permanent hair dyes, semi-permanent hair dyes, temporary hair dyes and other hair dyes depending on the persistence of the dyed color.

Permanent hair dyes are commonly referred to as oxidative hair dyes. Oxidized hair dyes use a oxidizing dye to color by dye oxidation. Oxidized hair dyes are usually of the first type, but are generally the first agent. It consists of an oxidizing agent which is a second agent.

The first agent contains an oxidative dye precursor and a coupler as a dye for coloring, and an alkali agent such as ammonia and monoethanolamine which causes the oxidation reaction by swelling the hair and promoting decomposition of hydrogen peroxide.

In addition, chelates are used for the purpose of controlling the oxidation reaction of the dye using a reducing agent or an antioxidant, and for blocking the metal ions. In addition, hair conditioning agents and fragrances, such as polyalcohols, surfactants or cationic polymers, are included.

In addition, the hydrogen peroxide contained in the oxidant, the second agent, decomposes the melanin of the hair to brighten the background color of the hair and promote the oxidation reaction of the dye.

Semi-permanent hair dyes are the principle of dyeing hair using acid dyes or basic dyes which are non-oxidizing dyes. These dyes do not undergo an oxidative polymerization reaction and are colored in themselves and are attached to the hair by ionic bonds with amino acids of the hair to dye the hair. I can't go up to the floor.

Temporary hair dye is a pigment or pearl is attached to the surface of the hair using a film forming agent to temporarily impart a coloring effect to the hair.

Other hair dyes include hair dyes using natural vegetable dyes such as henna, indigo or chamomile, or metallic hair dyes which dye hair by oxidation of silver nitrate and lead acetate.

Oxidative hair dyes are generally colored by oxidative polymerization reaction between dyes contained in the first agent by mixing the first agent and the second agent, and the melanin pigment in the hair is decomposed by hydrogen peroxide in the second agent. By bleaching the hair, the background color of the hair is brightened to produce a more vivid color.

However, since oxidative hair dyes are dyed by oxidative polymerization inside the hair, they not only lose the gloss and gloss of the hair, but also cause severe damage to the hair. There is a problem that skin irritation occurs.

KR, A, 10-2008-0060480, (2008.07.02)

The present invention is to solve the above problems, to minimize the irritation of the hair and scalp by the hair dye, there is no damage to the hair and scalp after dyeing, flushing ability, excellent color development, can express a variety of colors and long lasting It is an object of the present invention to provide a method for preparing a bento mineral mud solution for producing a hypo-allergic hair dye having a hair dye, and a method for preparing the hair dye.

According to the technical idea of the present invention for achieving the above object, the pozzolanic powder manufacturing step of firing and pulverizing pozzolanic volcanic soil to obtain a pozzolanic powder, and after mixing the pozzolanic powder manufacturing step by mixing in a purified water, stirring and ripening Jijangsu manufacturing step to obtain a, green mud powder manufacturing step of firing and pulverizing green mud bentonite to obtain a green mud powder, pearl powder manufacturing step of obtaining pearl powder by firing and pulverizing pearl, and jijisu obtained in the manufacturing step In the green mud powder manufacturing step and the pearl powder manufacturing step, the green mud powder and pearl powder, respectively, are mixed, stirred and dried to obtain a mud aqueous solution, and a mud aqueous solution obtained in the mud aqueous solution manufacturing step is added to the net. Ben to refine It is achieved by a method for producing a bento mineral mud aqueous solution for the preparation of a hypo-allergenic hair dye, characterized in that it comprises a step of preparing a solution of soil fine mud.

Here, the pozzolanic powder manufacturing step is to bake the pozzolanic volcanic soil at 1100 ℃ to 1300 ℃ in a hot gas furnace, it is preferable to obtain a pozzolanic powder of 300 mesh to 350 mesh using a mill.

In addition, the Jijangsu manufacturing step is to mix the pozzolane powder obtained in the purified water and pozzolane powder manufacturing step in a weight ratio of 9: 1, and stirred for 20 hours to 28 hours in a stirrer and aged for 24 hours to obtain a supernatant water using a filtration filter desirable.

In addition, in the green mud powder manufacturing step, the green mud bentonite of 300 mesh to 350 mesh is calcined at 1000 ° C. to 1200 ° C. in a hot gas furnace, and 500 mill green powder is obtained using a grinder.

In addition, in the pearl powder manufacturing step, the pearl is calcined at 500 ° C. to 700 ° C. in a hot gas furnace, and a pearl powder of 300 mesh to 350 mesh is obtained by using a grinder.

In addition, the mud aqueous solution manufacturing step is a mixture of Jijangsu, green mud powder, pearl powder obtained in each of the Jijisu manufacturing step, green mud powder manufacturing step, pearl powder manufacturing step in a weight ratio of 84: 15: 1 in a high-speed mixer 10 It is preferable to stir at high speed for 14 to 14 hours and then to dry for 24 hours in a aging dryer.

In addition, the high-speed mixer is preferably a ceramic mixer ball is added to stir the Jijisu, green mud powder, pearl powder at high speed.

In addition, the bento fine mud aqueous solution manufacturing step may be used to refine the mud aqueous solution using a mesh of 500 mesh.

On the other hand, in another technical idea of the present invention for achieving the above object, the pozzolanic powder manufacturing step of obtaining a pozzolanic powder by firing and pulverizing pozzolanic volcanic soil, and after mixing and stirring and maturing in the purified water after the pozzolane powder manufacturing step Jijangsu manufacturing step of obtaining the jijangsu of the supernatant, greenmud powder manufacturing step of firing and grinding green mud bentonite to obtain green mud powder, pearl powder manufacturing step of firing and grinding pearl to obtain pearl powder, and the jijisu manufacturing step The mud aqueous solution obtained by mixing the green mud powder and the pearl powder obtained in the green mud powder manufacturing step and the pearl powder manufacturing step, and then aging and drying to obtain a mud aqueous solution, and the mud aqueous solution obtained in the mud aqueous solution manufacturing step. Filter out meshes Of bentonite fine mud aqueous solution it is achieved by a method of manufacturing a hair dye comprising a stirring step of stirring a mixture of the fine bentonite mud aqueous solution produced by the production steps to the dye.

In addition, the stirring step is preferably stirred by mixing 5 to 8 parts by weight of the bento fine mud aqueous solution obtained in the bento fine mud aqueous solution manufacturing step with respect to 100 parts by weight of the dye.

According to the present invention, a method for preparing a bento mineral mud solution for producing a hypo-allergic hair dye and a method for preparing the hair dye according to the present invention include mud solution in the dye to relieve the irritant properties of the dye, thereby stimulating hair and scalp when the dye is used. It is possible to minimize the damage of the hair and scalp after dyeing, to wash the water, excellent color development, and to express a variety of colors, it is possible to prepare a hair dye having a long lasting hair and scalp improvement function.

In particular, the mud aqueous solution is applied to the hair and scalp with the dye and then dried to adsorb the harmful substances (inflammatory or bacterial inflammatory) of the hair and scalp, thereby improving the health of the hair and scalp.

1 is a flow chart illustrating a method for preparing a bento mineral mud aqueous solution and a method for preparing a hair dye for the preparation of a hypoallergenic hair dye according to the present invention.

The terms or words used in this specification and claims should not be construed as being limited to the common or dictionary meanings, and the inventors can appropriately define the concept of terms in order to explain their invention in the best way. Based on the principle, it should be interpreted as meaning and concept corresponding to the technical idea of the present invention.

Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings.

1 is a flow chart showing a method for producing a bento mineral mud aqueous solution for preparing a hypoallergenic hair dye according to the present invention and a method for preparing a hair dye.

Referring to the drawings, the manufacturing method of the hair dye according to the present invention, pozolan powder manufacturing step (S10), Jijangsu manufacturing step (S20), green mud powder manufacturing step (S30), pearl powder manufacturing step (S40), mud Aqueous solution manufacturing step (S50), Bento fine mud aqueous solution manufacturing step (S60), the stirring step (S70) consists of.

In other words, the pozzolanic powder manufacturing step (S10) is to obtain a pozzolanic powder by firing and pulverizing the pozzolanic volcanic soil, and then firing the pozzolanic volcanic soil at 1100 ° C. to 1300 ° C. in a hot gas furnace and using a grinder to form pozzolane of 300 mesh to 350 mesh. Powder is produced.

Pozzolanic volcanic soil not only has water vein, harmful electromagnetic wave shielding, antibacterial and mold removal effect, but also contains abundant germanium (Ge) and emits far infrared rays, which is excellent for hair and skin beauty.

Jijosoo manufacturing step (S20) is a pozzolanic powder manufacturing step (S10) after mixing in the purified water, stirring and aging to obtain the jijangsu of the supernatant, the pozzolanic powder obtained in the purified water and pozzolane powder manufacturing step () in a 9: 1 weight ratio Mixing and stirring in a stirrer for 20 to 28 hours and aged for 24 hours to prepare a supernatant water using a filtration filter. Jijisu prepared through such Jijisu manufacturing step (S20) is rich in minerals.

The green mud powder manufacturing step (S30) is to obtain green mud powder by firing and pulverizing green mud bentonite, and firing green mud bentonite of 300 mesh to 350 mesh at 1000 ° C. to 1200 ° C. in a hot gas furnace, using a grinder. 500 mesh green mud powder will be made.

Green mud bentonite is used in cosmetics and beauty packs and has excellent effects on skin waste removal, skin regeneration, blemishes, freckles, acne, blemishes, keratin and atopic dermatitis.

Pearl powder manufacturing step (S40) is to obtain the pearl powder by calcining and grinding the pearl, the pearl is calcined at 500 ℃ to 700 ℃ in a hot gas furnace and to prepare a pearl powder of 300 mesh to 350 mesh using a grinder.

Mud aqueous solution manufacturing step (S50) is a mixture of green mud powder and pearl powder obtained in the green mud powder manufacturing step (S30) and pearl powder manufacturing step (S40) to the jijangsu obtained in the Jijangsu manufacturing step (S20), and then stirred and aged By obtaining a mud aqueous solution by drying, the weight of 84: 15: 1 jijisu, green mud powder, pearl powder respectively obtained in Jijisu manufacturing step (S20), green mud powder manufacturing step (S30), pearl powder manufacturing step (S40). The mixture is mixed at a high speed for 10 to 14 hours in a high speed mixer and then aged for 24 hours in a drying dryer to prepare a mud aqueous solution.

At this time, the aging dryer is dried at about 70 ~ 80 ℃ mud aqueous solution for 24 hours, thereby removing the bacteria in the mud aqueous solution.

In addition, the high speed mixer of the mud aqueous solution manufacturing step (S50) is a ceramic mixer ball is added to agitate jijisu, green mud powder, pearl powder at high speed, preferably the ceramic mixer ball using a size of about 10mm in diameter Ceramic mixer balls, Ji-soo, green mud powder, and pearl powder collide with each other to finely molecularize.

Bento fine mud aqueous solution manufacturing step (S60) is to finely filter the mud aqueous solution obtained in the mud aqueous solution manufacturing step (S50) to the net, Bento fine mud aqueous solution manufacturing step (S60) using a mesh of 500 mesh finely mud aqueous solution Let's go. The 500-mesh mesh can filter the ceramic mixer balls fed into the high speed mixer to obtain an aqueous bento fine mud solution.

When the bento fine mud aqueous solution is prepared as described above, a dyeing agent is prepared through a denomination step (S70), and the dyeing agent is prepared by mixing the dye with the bento fine mud aqueous solution obtained in the bento fine mud aqueous solution preparation step (S60). , Hypotonic hair dye having a hair and scalp improvement function through a denomination step (S70) of mixing the bento fine mud aqueous solution obtained in the preparation step (S60) of about 5 to 8 parts by weight to 100 parts by weight of the dyeing agent. It can manufacture.

According to the method for preparing a bento mineral mud solution and the method for preparing the hair dye according to the above-described hypoallergenic hair dye, the mud solution is contained in the dye to relieve the irritant properties of the hair dye and hair and scalp when using the dye. It can minimize the damage of hair and scalp after dyeing by minimizing irritation, and can produce hair dye having the ability to improve hair and scalp with long-lasting power, good washing ability, excellent color development, and various colors. .

In particular, the mud aqueous solution is applied to the hair and scalp with the dye and then dried to adsorb the harmful substances (inflammatory or bacterial inflammatory) of the hair and scalp, thereby improving the health of the hair and scalp.

Meanwhile, the present invention is not limited to the above-described embodiments, but may be modified and modified without departing from the scope of the present invention, and such modifications and variations should be regarded as belonging to the technical spirit of the present invention. .

Claims (4)

Pozzolanic powder manufacturing step of firing and pulverizing pozzolanic volcanic soil to obtain pozzolanic powder;
Jijosoo manufacturing step of mixing the purified water after the pozzolane powder manufacturing step to obtain a jijangsu of the supernatant by stirring and aging;
Green mud powder manufacturing step of firing and grinding green mud bentonite to obtain green mud powder;
Pearl powder manufacturing step of firing and pulverizing pearl to obtain pearl powder;
A mud aqueous solution manufacturing step of mixing the green mud powder and the pearl powder obtained in the green mud powder manufacturing step and the pearl powder manufacturing step with the jijangsu obtained in the jijisu manufacturing step, followed by aging and drying to obtain an aqueous mud solution; And
Bento mineral mud aqueous solution manufacturing method for producing a hypo-allergenic hair dye, characterized in that it comprises ;;
The method according to claim 1,
The pozzolane powder manufacturing step
The pozzolanic volcanic soil is calcined at 1100 ° C. to 1300 ° C. in a hot gas furnace, and a pozzolane powder of 300 mesh to 350 mesh is obtained by using a grinder to produce a bento mineral mud aqueous solution for preparing a hypoallergenic hair dye.
The method according to claim 1,
The Jijangsu manufacturing step
Preparation of the hypoallergenic hair dye characterized by mixing the pozzolane powder obtained in the purified water and pozzolane powder manufacturing step in a weight ratio of 9: 1, stirring for 20 to 28 hours in a stirrer and aging for 24 hours to obtain a supernatant water using a filtration filter. Bento mineral mud aqueous solution preparation method for.
Method for producing a hair dye comprising a; stirring step of mixing and stirring the dye in the aqueous solution of bento fine mud prepared by claims 1 to 3.