KR20190099599A - Gel type cosmetic composition - Google Patents
Gel type cosmetic composition Download PDFInfo
- Publication number
- KR20190099599A KR20190099599A KR1020180019227A KR20180019227A KR20190099599A KR 20190099599 A KR20190099599 A KR 20190099599A KR 1020180019227 A KR1020180019227 A KR 1020180019227A KR 20180019227 A KR20180019227 A KR 20180019227A KR 20190099599 A KR20190099599 A KR 20190099599A
- Authority
- KR
- South Korea
- Prior art keywords
- cosmetic composition
- gel cosmetic
- present
- powder
- gel
- Prior art date
Abstract
Description
본 발명은 젤 타입의 화장료 조성물로, 건조 후 분말화 됨으로써 유분을 효율적으로 흡수할 수 있는 화장료 조성물에 관한 것이다.The present invention relates to a cosmetic composition of the gel type, which can be efficiently absorbed oil by being powdered after drying.
베이비 파우더는 주로 소아가 이용하는 것으로, 소아 피부의 땀띠나 짓무름을 예방하기 위하여 피부에 도포하는 것이 일반적이며, 이에 따라 베이비 파우더는 피부의 유분을 효율적으로 흡수하면서도, 보송보송한 촉감을 유지하는 것이 바람직 하다.Baby powder is mainly used by children, and it is generally applied to the skin in order to prevent sweat or rash of pediatric skin. Therefore, it is desirable that baby powder effectively absorbs skin oil and maintains a soft touch. Do.
이를 위하여 종래 베이비 파우더는 탈크를 함유하여 피부의 유분을 흡수하는 것이 통상적이었다. 그러나 많은 종류의 탈크에서 석면이 검출되어, 탈크를 포함하는 베이비 파우더의 위험성이 널리 알려지게 된다. 석면은 침상의 입자로, 폐로 흡입되는 경우 침상 구조가 지속적으로 폐를 자극함으로써 심각한 질병을 유발할 수 있으며, 이에 따라 대다수의 국가에서 석면의 사용을 금지하고 있는 추세이다. 이에, 석면을 함유하지 않은 탈크가 제조 및 판매되고 있으나, 소비자의 불신을 극복하기에는 어려운 실정이다. To this end, conventional baby powders typically contain talc to absorb oil from the skin. However, asbestos is detected in many types of talc, and the danger of baby powder containing talc becomes widely known. Asbestos is a needle-like particle, and if inhaled into the lungs, the needle structure may continuously irritate the lungs, causing serious diseases, and as a result, most countries have banned the use of asbestos. Thus, talc containing no asbestos is manufactured and sold, but it is difficult to overcome consumer distrust.
이에, 탈크의 대체품으로 옥수수 전분을 함유하는 베이비 파우더가 개발되어 판매되고 있으나, 탈크에 비하여 옥수수전분의 흡유도가 낮아, 유분을 흡수함으로써 보송보송한 촉감을 유지하고 땀띠나 짓무름을 예방하는 효과가 탈크에 비하여 낮은 문제점이 있으며, 옥수수 전분을 이용하는 경우에도 여전히 분말상의 제형으로 도포 시 소아의 폐에 흡입될 수 있는 문제점이 있다. As a substitute for talc, baby powder containing corn starch has been developed and sold. However, the absorption of corn starch is lower than that of talc, and it absorbs oil to keep the skin soft and prevent sweat and sores. There is a lower problem than talc, and even when using corn starch there is a problem that can be inhaled in the lungs of children when applied in a powdery formulation.
이에, 높은 흡유도를 가져 피부의 짓무름을 예방하면서도, 폐에 흡입되지 않는 화장료 조성물의 개발이 필요한 실정이다.Thus, while having a high oil absorption to prevent skin sores, it is necessary to develop a cosmetic composition that is not inhaled into the lungs.
본 발명의 목적은 젤 타입으로 도포되어 분말의 흡입을 예방할 수 있는 화장료 조성물을 제공하는 것이다.An object of the present invention is to provide a cosmetic composition that can be applied in a gel type to prevent inhalation of the powder.
본 발명의 다른 목적은 건조 후 분말화되어 보송보송한 감촉을 유지할 수 있는 화장료 조성물을 제공하는 것이다. Another object of the present invention is to provide a cosmetic composition that can be powdered after drying to maintain a smooth texture.
본 발명의 또 다른 목적은 중공 다공성 실리카를 포함하여 유분 흡수력이 우수한 화장료 조성물을 제공하는 것이다.Still another object of the present invention is to provide a cosmetic composition having excellent oil absorption, including hollow porous silica.
본 발명에 의한 젤 화장료 조성물은 Gel cosmetic composition according to the present invention
공극 부피가 0.1 내지 1.2 ㎖/g인 중공 다공성 실리카 분말 및 산화아연 입자를 포함하며, 건조 후 분말화 되어 유분을 흡수한다. Hollow porous silica powder and zinc oxide particles having a pore volume of 0.1 to 1.2 ml / g, and powdered after drying to absorb the oil.
본 발명의 일 실시예에 의한 젤 화장료 조성물에서 상기 중공 다공성 실리카는 평균 입경이 1 내지 15 ㎛이며, 전체 부피 중 중공 부피가 85% 이상일 수 있다. In the gel cosmetic composition according to an embodiment of the present invention, the hollow porous silica has an average particle diameter of 1 to 15 μm, and a hollow volume of the total volume may be 85% or more.
본 발명의 일 실시예에 의한 젤 화장료 조성물에서 상기 중공 다공성 실리카의 쉘은 직경이 0.05 내지 25 ㎚인 기공을 포함하는 다공성 쉘일 수 있다. In the gel cosmetic composition according to an embodiment of the present invention, the shell of the hollow porous silica may be a porous shell including pores having a diameter of 0.05 to 25 nm.
본 발명의 일 실시예에 의한 젤 화장료 조성물에서 상기 젤 화장료 조성물은 중공 다공성 실리카를 10 내지 50 중량% 포함할 수 있다. In the gel cosmetic composition according to an embodiment of the present invention, the gel cosmetic composition may include 10 to 50% by weight of hollow porous silica.
본 발명의 일 실시예에 의한 젤 화장료 조성물에서 상기 젤 화장료 조성물은 친수성 고분자 점증제를 더 포함할 수 있다. In the gel cosmetic composition according to an embodiment of the present invention, the gel cosmetic composition may further include a hydrophilic polymer thickener.
본 발명의 일 실시예에 의한 젤 화장료 조성물에서 상기 젤 화장료 조성물은 상기 친수성 고분자 점증제를 0.05 내지 7 중량% 포함할 수 있다. In the gel cosmetic composition according to an embodiment of the present invention, the gel cosmetic composition may include 0.05 to 7% by weight of the hydrophilic polymer thickener.
본 발명의 일 실시예에 의한 젤 화장료 조성물에서 상기 젤 화장료 조성물은 옥수수 전분을 더 포함할 수 있다. In the gel cosmetic composition according to an embodiment of the present invention, the gel cosmetic composition may further include corn starch.
본 발명의 일 실시예에 의한 젤 화장료 조성물에서 상기 젤 화장료 조성물은 건조 후 파우더의 평균 직경이 1000 ㎛이하일 수 있다. In the gel cosmetic composition according to an embodiment of the present invention, the gel cosmetic composition may have an average diameter of less than 1000 ㎛ powder after drying.
본 발명의 일 실시예에 의한 젤 화장료 조성물에서 상기 젤 화장료 조성물은 젤 화장료 조성물의 건조 후 분말을 기준으로, In the gel cosmetic composition according to an embodiment of the present invention, the gel cosmetic composition is based on the powder after drying the gel cosmetic composition,
상기 젤 화장료 조성물의 건조 후 분말 100 g 당 80 ㎖ 이상의 유분을 흡수할 수 있다. After drying the gel cosmetic composition may absorb more than 80 ml of oil per 100 g of powder.
본 발명의 일 실시예에 의한 젤 화장료 조성물에서 상기 젤 화장료 조성물은 유분 흡수용일 수 있다.In the gel cosmetic composition according to an embodiment of the present invention, the gel cosmetic composition may be for oil absorption.
본 발명은 중공 다공성 실리카 및 산화아연을 포함하여 도포 시에는 젤타입으로 도포되나, 건조 후에 분말화 됨으로써 유분 흡수력이 우수하여 종래 베이비 파우더의 효과를 도모하면서도 분말의 흡입을 예방할 수 있는 장점이 있다.The present invention is applied in a gel type at the time of application, including hollow porous silica and zinc oxide, it is powdered after drying has an advantage of excellent oil absorption ability to prevent the inhalation of the powder while promoting the effect of the conventional baby powder.
도 1은 본 발명의 실시예 및 비교예에 의한 화장료 조성물의 건조 전후 제형을 육안으로 관찰하여 도시한 것이다.1 is a visual observation of the formulation before and after drying the cosmetic composition according to the Examples and Comparative Examples of the present invention.
이하 본 발명에 따른 젤 화장료 조성물에 대해 상세히 설명한다. 이때, 사용되는 기술 용어 및 과학 용어에 있어서 다른 정의가 없다면, 이 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 통상적으로 이해하고 있는 의미를 가지며, 하기의 설명에서 본 발명의 요지를 불필요하게 흐릴 수 있는 공지 기능 및 구성에 대한 설명은 생략한다. Hereinafter, the gel cosmetic composition according to the present invention will be described in detail. In this case, unless there is another definition in the technical terms and scientific terms used, it has the meaning that is commonly understood by those of ordinary skill in the art, unnecessarily obscure the subject matter of the present invention in the following description Description of known functions and configurations that may be omitted.
본 발명은 공극 부피가 0.1 내지 1.2 ㎖/g인 중공 다공성 실리카 분말 및 산화아연 입자를 포함하며, The present invention comprises a hollow porous silica powder and zinc oxide particles having a pore volume of 0.1 to 1.2 ml / g,
건조 후 분말화 되는 젤 화장료 조성물에 관한 것이다. It relates to a gel cosmetic composition to be powdered after drying.
본 발명에 의한 젤 화장료 조성물은 젤타입으로 도포된 후, 수 분 내에 분말화됨으로써 도포 시 발생할 수 있는 분말의 흡입을 예방하면서도, 중공 다공성 실리카 분말에 의하여 높은 흡유도를 나타냄으로써 보송보송한 촉감을 유지할 수 있는 장점이 있다. The gel cosmetic composition according to the present invention is applied in a gel type, and then powdered within minutes to prevent inhalation of the powder that may occur during application, while exhibiting a high oil absorption by the hollow porous silica powder, thereby providing a soft touch. There is an advantage to maintain.
종래 베이비 파우더는 도포 시 가루날림이 발생하여 폐로 흡입될 수 있는 문제점이 있다. 특히 탈크가 주성분인 베이비 파우더의 경우 석면을 포함할 수 있어, 소아의 신체에 악영향을 미칠 수 있는 문제가 있다. Conventional baby powders have a problem that they may be sucked into the lungs due to powder blowing during application. In particular, talc is a main ingredient of the baby powder may include asbestos, there is a problem that may adversely affect the body of the child.
이를 극복하기 위하여 파우더리한 감촉을 갖는 크림 또는 젤 타입의 베이비 파우더 대체품이 개발되고 있으나, 대부분의 경우 파우더와 유사한 감촉만을 나타낼 뿐, 건조 후에도 꾸덕한 식감을 가져 유분의 효율적인 흡수가 어려운 문제점이 있었다. In order to overcome this problem, a cream or gel-type baby powder substitute having a powdery texture has been developed. However, in most cases, only a powder-like texture is exhibited, and there is a problem that efficient absorption of oil is difficult due to a solid texture even after drying.
이에 본 출원인은 도포 시에는 젤 또는 크림타입으로 가루 날림을 예방하면서도, 건조 후 분말화되어 유분을 흡수할 수 있는 화장료 조성물의 제형에 대해 장간 연구를 수행하였다. Accordingly, the present applicant conducted a long-term study on the formulation of the cosmetic composition that can be absorbed oil after drying, while preventing powder blowing in a gel or cream type when applied.
연구 결과, 공극 부피가 0.1 내지 1.2 ㎖/g인 중공 다공성 실리카 분말; 및 산화아연 입자;를 혼합하여 젤 화장료 조성물로 제조하는 경우, 건조 후 분말화되어 유분을 흡수하면서도, 젤 타입으로 가루날림을 방지하고 도포가 용이한 장점이 있다. As a result, hollow porous silica powder having a pore volume of 0.1 to 1.2 ml / g; And zinc oxide particles; when mixed to prepare a gel cosmetic composition, while drying to absorb the oil while being powdered, there is an advantage of preventing the powder to fly in a gel type and easy application.
본 발명에서 중공 다공성 실리카라 함은, 내부에 중공을 포함하며, 외부 쉘이 기공을 포함하는 다공성의 실리카 입자를 의미한다. Hollow porous silica in the present invention means a porous silica particle including a hollow inside, the outer shell includes pores.
본 발명의 일 실시예에 의한 젤 화장료 조성물에서 중공 다공성 실리카는 평균 입경이 1 내지 15 ㎛, 구체적으로 2 내지 10 ㎛이며, 전체 부피중 중공 부피 가 85% 이상, 구체적으로는 85 내지 97%일 수 있다. 본 발명의 일 실시예에 의한 젤 화장료 조성물은 상술한 범위의 중공 다공성 실리카를 포함함으로써 유분을 다량 흡수하여 보송보송한 촉감을 유지할 수 있다. 본 발명의 일 실시예에 의한 젤 화장료 조성물은 공극 부피가 0.1 내지 1.2 ㎖/g이며, 전체 부피 중 중공 부피가 85% 이상인 중공 다공성 실리카 입자 및 산화 아연을 포함함으로써, 본 발명의 일 실시예에 의한 젤 화장료 조성물의 건조 후 분말을 기준으로, 상기 젤 화장료 조성물의 건조 후 분말 100 g 당 80 ㎖ 이상, 구체적으로는 80 내지 150 ㎖의 유분을 흡수할 수 있다. 이때, 유분 흡수도의 측정은 분말에 오일을 천천히 적가하면서 분말이 크림상이 되는 시점에 투입된 오일 양을 기준으로 한다. 이는 통상적으로 이용되는 베이비 파우더 분말 대비 흡유도가 150% 이상, 더욱 구체적으로는 200 내지 300 % 이상 높은 수치로, 본 발명의 일 실시예에 의한 젤 화장료 조성물의 건조에 의해 생성되는 분말상의 흡유도가 현저히 높음을 확인할 수 있다. 이는 중공 다공성 실리카 및 산화아연 입자를 동시에 포함함으로써 나타날 수 있는 상승효과로, 이에 따라 젤 화장료 조성물의 건조로 형성되는 분말상의 입자를 기준으로, 본 발명의 일 실시예에 의한 젤 화장료 조성물이 통상의 베이비 파우더보다 소량 도포되더라도 유분을 흡수하여 땀띠 또는 짓무름 등의 피부 문제를 예방할 수 있음을 의미한다.In the gel cosmetic composition according to an embodiment of the present invention, the hollow porous silica has an average particle diameter of 1 to 15 μm, specifically 2 to 10 μm, and a hollow volume of 85% or more, specifically 85 to 97% of the total volume. Can be. Gel cosmetic composition according to an embodiment of the present invention by containing the hollow porous silica in the above-described range can be absorbed in a large amount of oil to maintain a soft touch. Gel cosmetic composition according to an embodiment of the present invention has a void volume of 0.1 to 1.2 ml / g, and comprises hollow porous silica particles and zinc oxide having a hollow volume of 85% or more of the total volume, according to an embodiment of the present invention Based on the powder after drying the gel cosmetic composition, the gel cosmetic composition may absorb 80 ml or more, specifically, 80 to 150 ml of oil per 100 g of the powder. In this case, the measurement of oil absorption is based on the amount of oil added at the time when the powder becomes a cream while slowly dropping oil into the powder. This is a value of 150% or more, more specifically, 200 to 300% or more higher than the commonly used baby powder powder, the oil absorption of the powder form produced by the drying of the gel cosmetic composition according to an embodiment of the present invention. It can be seen that is significantly higher. This is a synergistic effect that can be seen by simultaneously including the hollow porous silica and zinc oxide particles, according to the powdery particles formed by drying of the gel cosmetic composition, the gel cosmetic composition according to an embodiment of the present invention is conventional Even if a small amount is applied than baby powder, it means that it can absorb oil and prevent skin problems such as sweat or soreness.
또한, 본 발명의 일 실시예에 의한 중공 다공성 실리카의 쉘은 직경이 0.05 내지 25 ㎚, 더욱 구체적으로는 1 내지 15 ㎚의 기공을 포함할 수 있다. 상술한 범위에서 유분을 용이하게 흡수하면서도 다른 조성과의 용이하게 혼합되어 젤 화장료 조성물 내에서 분산성이 우수한 장점이 있다. In addition, the shell of the hollow porous silica according to an embodiment of the present invention may include pores having a diameter of 0.05 to 25 nm, more specifically 1 to 15 nm. While easily absorbing the oil in the above-described range is easily mixed with other compositions has the advantage of excellent dispersibility in the gel cosmetic composition.
본 발명의 일 실시예에 의한 젤 화장료 조성물은 중공 다공성 실리카를 10 내지 50 중량%, 좋게는 15 내지 35 중량% 포함할 수 있다. 상술한 범위에서 건조에 지나치게 많은 시간이 소요되는 문제를 예방하면서도, 젤타입의 사용감으로 넓은 면적에 도포가 용이한 장점이 있다. Gel cosmetic composition according to an embodiment of the present invention may comprise 10 to 50% by weight, preferably 15 to 35% by weight of the hollow porous silica. While preventing the problem of taking too much time for drying in the above-described range, there is an advantage in that it is easy to apply to a large area with the feeling of gel type.
본 발명의 일 실시예에 의한 젤 화장료 조성물은 산화아연 입자를 포함한다. 본 발명의 일 실시예에 의한 젤 화장료 조성물은 상술한 바와 같이 공극 부피가 0.1 내지 1.2 ㎖/g인 중공 다공성 실리카 분말 및 산화아연 입자를 포함함으로써 도포 후 분말 제형으로 변화되어 분말의 흡입을 예방하면서도 유분을 흡수하여 땀띠 또는 짓무름 등을 예방할 수 있다. 구체적으로, 본 발명의 산화아연 입자는 통상적으로 화장료에 이용되는 것인 경우 제한 없이 이용이 가능하나, 구체적이고 비한정적인 일 예로 평균입경이 10 내지 2000 ㎚일 수 있으나, 본 발명이 이에 제한되는 것은 아니다. Gel cosmetic composition according to an embodiment of the present invention comprises zinc oxide particles. Gel cosmetic composition according to an embodiment of the present invention is a porous porous silica powder and zinc oxide particles having a pore volume of 0.1 to 1.2 ㎖ / g as described above is changed to a powder formulation after application to prevent inhalation of the powder Absorb oil to prevent sweat or sores. Specifically, the zinc oxide particles of the present invention may be used without limitation in the case where they are commonly used in cosmetics, but one or more specific and non-limiting examples may have an average particle diameter of 10 to 2000 nm, but the present invention is limited thereto. It is not.
본 발명의 일 실시예에 의한 젤 화장료 조성물은 산화아연 입자를 1 내지 20 중량%, 더욱 구체적으로는 2 내지 15 중량% 포함할 수 있다. 상술한 범위에서 중공 다공성 실리카와 균일한 분산을 도모하면서도, 도포 시 젤 제형을 유지할 수 있다. Gel cosmetic composition according to an embodiment of the present invention may contain 1 to 20% by weight, more specifically 2 to 15% by weight of zinc oxide particles. While achieving a uniform dispersion with the hollow porous silica in the above range, it is possible to maintain the gel formulation during application.
더욱 좋게는, 본 발명의 일 실시예에 의한 젤 화장료 조성물은 상술한 중량 범위를 만족하면서도, 중공 다공성 입자 : 산화아연 입자를 1:0.1 내지 0.8 중량% 포함할 수 있다. 본 발명의 일 실시예에 의한 젤 화장료 조성물이 중공 다공성 입자 및 산화아연 입자를 상술한 범위에서 건조 후 미세한 크기의 분말을 형성하면서도, 건조로 생성되는 입자가 판상 또는 침상으로 형성되어, 피부자극을 유발하는 문제점을 예방할 수 있다. More preferably, the gel cosmetic composition according to one embodiment of the present invention may satisfy the above-described weight range, but may include 1: 0.1 to 0.8 wt% of hollow porous particles: zinc oxide particles. While the gel cosmetic composition according to an embodiment of the present invention forms a powder having a fine size after drying the porous porous particles and the zinc oxide particles in the above-described range, the particles produced by drying are formed in a plate shape or needle shape, and skin irritation is achieved. It can prevent causing problems.
상술한 바와 같이 본 발명에 의한 젤 화장료 조성물은 건조 후 분말화되어 유분을 흡수할 수 있다. 즉, 본 발명의 일 실시예에 의한 젤 화장료 조성물은 기타 다른 크림 또는 젤 제형의 베이비 파우더 대체품과 달리, 분말화되어 유분을 흡수할 수 있다. 구체적으로, 종래 시판중인 베이비 파우더 대체용 크림 또는 젤은 베이비 파우더와 촉감만 유사하게 제조된 것일 뿐, 건조 후에도 분말화되지 않고, 크림 또는 버터와 유사한 제형을 나타냄으로써, 피부에서 분비되는 유분 및 땀 등의 흡수가 어려운 문제점이 있으며, 이에 따라 베이비 파우더의 본래 목적을 수행하기 어려운 문제점이 있다. 그러나 본 발명의 일 실시예에 의한 젤 화장료 조성물은 건조 후 분말화됨으로써 유분 및 땀을 효율적으로 흡수할 수 있는 장점이 있다. As described above, the gel cosmetic composition according to the present invention may be powdered after drying to absorb oil. That is, the gel cosmetic composition according to one embodiment of the present invention may be powdered to absorb oil, unlike other baby powder substitutes of other cream or gel formulations. Specifically, commercially available baby powder replacement creams or gels are only manufactured similarly to baby powders, and are not powdered even after drying, and exhibit a cream or butter-like formulation, thereby releasing oil and sweat secreted from the skin. There is a problem that is difficult to absorb, such as, there is a problem difficult to perform the original purpose of the baby powder. However, the gel cosmetic composition according to an embodiment of the present invention has an advantage of efficiently absorbing oil and sweat by being powdered after drying.
나아가, 본 발명의 일 실시예에 의한 젤 화장료 조성물은 건조 후 파우더의 평균 직경이 1000 ㎛ 이하, 더욱 구체적으로는 10 내지 900 ㎛일 수 있다. 즉, 본 발명의 일 실시예에 의한 젤 화장료 조성물은 건조 후 지나치게 뭉쳐진 입자상으로 생성되지 않으며, 미세한 분말형태로 피부에 도포되어 분말상의 베이비 파우더와 같이 유분 및 땀 등을 흡수할 수 있다. 이러한 관점에서 본 발명의 일 실시예에 의한 젤 화장료 조성물은 유분 흡수용으로 이용될 수 있으나, 본 발명이 이에 제한되는 것은 아니다. 아울러, 본 발명의 일 실시예에 의한 젤 화장료 조성물의 건조 후 직경이 상술한 범위 내로 포함됨으로써, 지나치게 미세한 입자의 생성으로 인한 가루날림 및 입자에 의한 피부 자극을 예방하면서도, 효율적으로 유분의 흡수가 가능하다. Furthermore, the gel cosmetic composition according to one embodiment of the present invention may have an average diameter of the powder after drying of 1000 μm or less, more specifically 10 to 900 μm. That is, the gel cosmetic composition according to an embodiment of the present invention is not produced in the form of too much agglomerated particles after drying, and is applied to the skin in the form of fine powder to absorb oil, sweat, etc., like a powdery baby powder. In this regard, the gel cosmetic composition according to one embodiment of the present invention may be used for oil absorption, but the present invention is not limited thereto. In addition, since the diameter after drying of the gel cosmetic composition according to an embodiment of the present invention is included in the above-described range, while preventing the stimulation of the powder caused by the generation of too fine particles and skin irritation by the particles, the absorption of oil efficiently It is possible.
본 발명의 일 실시예에 의한 젤 화장료 조성물은 젤형의 화장료 조성물 형성을 위하여 점증제를 더 포함할 수 있다. 좋게는, 본 발명의 일 실시예에 의한 젤 화장료 조성물은 친수성 고분자 점증제를 이용할 수 있다. 친수성 고분자 증점제를 이용하는 경우 건조 후 더욱 보송보송한 식감을 나타내면서도 건조후 후감이 끈적해지는 문제를 예방할 수 있다. 구체적으로, 본 발명에서 친수성 고분자 증점제는 잔탄검, 구아검, 로커스트빈검, 아라비아검, 트래거캔스, 카라야검 및 가티검에서 선택되는 하나 또는 둘 이상일 수 있으나, 본 발명이 이에 제한되는 것은 아니다. Gel cosmetic composition according to an embodiment of the present invention may further include a thickening agent for forming a cosmetic composition of the gel type. Preferably, the gel cosmetic composition according to one embodiment of the present invention may use a hydrophilic polymer thickener. In the case of using a hydrophilic polymer thickener, it may prevent the problem that the aftertaste becomes sticky after drying while showing a smoother texture after drying. Specifically, the hydrophilic polymer thickener in the present invention may be one or two or more selected from xanthan gum, guar gum, locust bean gum, gum arabic, tragacanth, karaya gum and gatti gum, but the present invention is not limited thereto.
본 발명의 일 실시예에 의한 젤 화장료 조성물에 포함되는 친수성 고분자 점증제의 함량은, 젤 화장료 제형을 형성하기 위한 범위에서는 제한없이 포함할 수 있다. 구체적이고 비한정적인 일 예로 본 발명의 일 실시예에 의한 젤 화장료 조성물은 상기 친수성 고분자 점증제를 0.05 내지 7 중량%, 좋게는 0.1 내지 5 중량%를 포함할 수 있다. The content of the hydrophilic polymer thickener included in the gel cosmetic composition according to an embodiment of the present invention may be included without limitation in the range for forming the gel cosmetic formulation. As a specific and non-limiting example, the gel cosmetic composition according to one embodiment of the present invention may include 0.05 to 7% by weight, preferably 0.1 to 5% by weight of the hydrophilic polymer thickener.
본 발명의 일 실시예에 의한 젤 화장료 조성물은 옥수수 전분을 더 포함할 수 있다. 본 발명의 일 실시예에 의한 젤 화장료 조성물이 옥수수 전분을 더 포함하는 경우, 건조 후 분말의 촉감을 더욱 향상시킬 수 있는 장점이 있다. 본 발명의 일 실시예에 의한 젤 화장료 조성물은 젤 제형을 유지할 수 있는 범위 한에서 옥수수 전분을 포함할 수 있으며, 본 발명이 이에 제한되는 것은 아니다. 좋게는 본 발명의 일 실시예에 의한 젤 화장료 조성물은 옥수수 전분을 1 내지 10 중량%, 더욱 구체적으로는 2 내지 8 중량% 포함할 수 있으나 본 발명이 이에 제한되는 것은 아니다. Gel cosmetic composition according to an embodiment of the present invention may further comprise corn starch. When the gel cosmetic composition according to an embodiment of the present invention further comprises corn starch, there is an advantage of further improving the feel of the powder after drying. Gel cosmetic composition according to an embodiment of the present invention may include corn starch as long as it can maintain the gel formulation, the present invention is not limited thereto. Preferably the gel cosmetic composition according to an embodiment of the present invention may include 1 to 10% by weight, more specifically 2 to 8% by weight of corn starch, but the present invention is not limited thereto.
본 발명의 일 실시예에 의한 젤 화장료 조성물은 통상적으로 화장료에 이용되는 입자상 물질을 더 포함할 수 있다. 구체적이고 비한정적인 일 예로, 본 발명의 일 실시예에 의한 젤 화장료 조성물은 옥수수 전분 이외의 전분, 이산화티탄, 칼슘스테아레이트, 제올라이트, 탄산마그네슘, 마이카, 운모, 활석, 규산바륨 및 나일론 파우다 등에서 선택되는 하나 또는 둘 이상의 입자를 포함할 수 있으나, 통상의 화장료 조성물에 이용되는 분말인 경우 제한 없이 이용이 가능하다. 구체적으로 본 발명의 일 실시예에 의한 젤 화장료 조성물은 상술한 입자상 물질을 0.05 내지 5 중량% 포함할 수 있으나, 본 발명이 이에 제한되는 것은 아니다.Gel cosmetic composition according to an embodiment of the present invention may further include a particulate material commonly used in cosmetics. As a specific and non-limiting example, the gel cosmetic composition according to an embodiment of the present invention is a starch other than corn starch, titanium dioxide, calcium stearate, zeolite, magnesium carbonate, mica, mica, talc, barium silicate and nylon powder It may include one or two or more particles selected, but may be used without limitation in the case of powder used in a conventional cosmetic composition. Specifically, the gel cosmetic composition according to one embodiment of the present invention may include 0.05 to 5% by weight of the above-mentioned particulate matter, but the present invention is not limited thereto.
본 발명의 일 실시예에 의한 젤 화장료 조성물은 보습제를 더 포함할 수 있다. 이때 보습제는 통상적으로 화장료에 이용되는 보습제인 경우 제한없이 이용이 가능하다. 이때 보습제는 다가 알코올 또는 오일상일 수 있으나 본 발명이 이에 제한되는 것은 아니다. 구체적이고 비한정적인 일 예로 다가알콜의 경우 글리세린, 프로필렌글리콜, 디프로필렌 글리콜, 부틸렌글리콜, 펜틸렌글리콜, 폴리에틸렌글리콜, 솔비톨, 프로판디올, 헥산디올, 옥탄디올 및 에틸 헥산디올에서 선택되는 하나 또는 둘 이상일 수 있으며, 오일의 경우 스쿠알란(squalane), 폴리부텐(Polybutene), 폴리이소부텐(Polyisobutene), 폴리데센(Polydecene) 및 하이드로제네이티드 폴리데센(Hydrogenated Polydecene) 등에서 선택되는 탄화수소계 오일; 세틸알코올, 스테아릴알코올, 베헤닐알코올, 2-옥틸도데칸올 및 이소세틸알코올 등에서 선택되는 고급 지방산계 오일; 이소프로필 미리스테이트, 이소프로필 팔미테이트, 세틸 헥사노에이트, 세틸 에틸헥사노에이트, C12~C15알킬 벤조에이트, 디카프릴릴 카보네이트, 펜타에리스리틸 테트라에틸헥사노에이트, 펜타에리스리틸 테트라이소스테아레이트, 디이소스테아릴 말레이트, 디카프릴릴 카보네이트 등에서 선택되는 에스테르계 오일; 및 카프릴릭/카프릭 트리글리세라이드(caprylic/capric triglyceride) 등에서 선택되는 글리세라이드계 오일; 등일 수 있으나, 본 발명이 이에 제한되는 것은 아니다. Gel cosmetic composition according to an embodiment of the present invention may further include a moisturizing agent. At this time, the moisturizer can be used without limitation in the case of a moisturizer that is commonly used in cosmetics. At this time, the humectant may be a polyhydric alcohol or an oil phase, but the present invention is not limited thereto. Specific and non-limiting examples of the polyhydric alcohol is one selected from glycerin, propylene glycol, dipropylene glycol, butylene glycol, pentylene glycol, polyethylene glycol, sorbitol, propanediol, hexanediol, octanediol and ethyl hexanediol or It may be two or more, in the case of oil, hydrocarbon oils selected from squalane (poly), polybutene (Polybutene), polyisobutene (Polyisobutene), polydecene (Polydecene) and hydrogenated polydecene (Hydrogenated Polydecene); Higher fatty acid oils selected from cetyl alcohol, stearyl alcohol, behenyl alcohol, 2-octyldodecanol and isocetyl alcohol; Isopropyl myristate, isopropyl palmitate, cetyl hexanoate, cetyl ethylhexanoate, C 12 to C 15 alkyl benzoate, dicaprylyl carbonate, pentaerythritol tetraethylhexanoate, pentaerythryl tetraisosteaa Ester oils selected from elate, diisostearyl maleate, dicaprylyl carbonate, and the like; And glyceride oils selected from caprylic / capric triglycerides and the like; Etc., but the present invention is not limited thereto.
본 발명의 일 실시예에 의한 젤 화장료 조성물은 상술한 보습제를 0.05 내지 5 중량% 포함할 수 있으나, 본 발명이 이에 제한되는 것은 아니다. Gel cosmetic composition according to an embodiment of the present invention may include 0.05 to 5% by weight of the moisturizer described above, but the present invention is not limited thereto.
본 발명의 일 실시예에 의한 젤 화장료 조성물은 계면활성제를 더 포함할 수 있다. 구체적으로이고 비한정적인 일 예로 계면활성제는 소르비탄모노올레에이트, 소르비탄모노이소스테아레이트, 소르비탄모노라우레이트, 소르비탄모노팔미테이트, 소르비탄모노스테아레이트, 소르비탄세스퀴올레에이트, 소르비탄트리올레에이트 또는 펜타-2-에틸헥실산디글리세롤소르비탄 등과 같은 소르비탄 지방산 에스테르류; 글리세릴 팔미토스테아레이트, 글리세릴 스테아레이트, 글리세릴 올레이트 또는 글리세릴 미리스테이트 등과 같은 글리세릴계 지방산 에스테르류; 폴리글리세릴-3-디폴리히드록시스테아레이트, 폴리글리세릴-3-디이소스테아레이트, 폴리글리세릴-2-테트라이소스테아레이트, 폴리글리세릴-2-트리이소스테아레이트 또는 폴리글리세릴-4-이소스테아레이트 등과 같은 폴리글리세릴계 계면활성제; 폴리옥시에틸렌-소르비탄모노올레에이트, 폴리옥시에틸렌-소르비탄모노스테아레이트, 또는 폴리옥시에틸렌-소르비탄테트라올레에이트 등과 같은 폴리옥시에틸렌(polyoxyethylene)-소르비탄 지방산 에스테르류; 폴리소르베이트 60, 폴리소르베이트 80 또는 폴리소르베이트 20), 폴리옥시에틸렌-소르비트 지방산 에스테르류(폴리옥시에틸렌-소르비트모노라우레이트, 폴리옥시에틸렌-소르비트모노올레에이트, 폴리옥시에틸렌-소르비트펜타올레에이트, 또는 폴리옥시에틸렌-소르비트모노스테아레이트 등과 같은 폴리소르베이트류, 폴리옥시에틸렌-글리세린모노스테아레이트, 폴리옥시에틸렌-글리세린모노이소스테아레이트, 또는 폴리옥시에틸렌-글리세린트리이소스테아레이트 등과 같은 폴리옥시에틸렌-글리세린 지방산에스테르류; 폴리옥시에틸렌-디스테아레이트, 폴리옥시에틸렌-모노디올레에이트, 또는 디스테아린산 에틸렌글리콜 등과 같은 폴리옥시에틸렌-지방산 에스테르류; 폴리옥시에틸렌-라우릴에테르, 폴리옥시에틸렌-올레일에테르, 폴리옥시에틸렌-세틸에테르(세테아레스-16, 세테아레스-17, 세테아레스-18, 세테아레스-20, 세테아레스-22, 또는 세테아레스-23 등), 폴리옥시에틸렌-스테아릴에테르, 폴리옥시에틸렌-베헤닐에테르, 폴리옥시에틸렌-2-옥틸도데실에테르, 또는 폴리옥시에틸렌-콜레스탄올에테르 등과 같은 폴리옥시에틸렌-알킬에스테르류;일 수 있으나 이에 제한되는 것은 아니다. 구체적으로, 본 발명의 일 실시예에 의한 젤 화장료 조성물은 상술한 계면활성제를 0.05 내지 5 중량% 포함할 수 있으나, 본 발명이 이에 제한되는 것은 아니다. Gel cosmetic composition according to an embodiment of the present invention may further include a surfactant. Specific and non-limiting examples of surfactants include sorbitan monooleate, sorbitan monoisostearate, sorbitan monolaurate, sorbitan monopalmitate, sorbitan monostearate, sorbitan sesquioleate, sorbent Sorbitan fatty acid esters such as non-triglyceride or penta-2-ethylhexyl diglycerol sorbitan; Glyceryl fatty acid esters such as glyceryl palmitostearate, glyceryl stearate, glyceryl oleate or glyceryl myristate; Polyglyceryl-3-dipolyhydroxystearate, polyglyceryl-3-diisostearate, polyglyceryl-2-tetraisostearate, polyglyceryl-2-triisostearate or polyglyceryl- Polyglyceryl surfactants such as 4-isostearate and the like; Polyoxyethylene-sorbitan fatty acid esters such as polyoxyethylene-sorbitan monooleate, polyoxyethylene-sorbitan monostearate, polyoxyethylene-sorbitan tetraoleate and the like; Polysorbate 60, polysorbate 80 or polysorbate 20), polyoxyethylene-sorbitan fatty acid esters (polyoxyethylene-sorbitan monolaurate, polyoxyethylene-sorbitol monooleate, polyoxyethylene- Polysorbates such as sorbitol pentaoleate or polyoxyethylene-sorbitol monostearate, polyoxyethylene-glycerin monostearate, polyoxyethylene-glycerine monoisostearate, or polyoxyethylene-glycerine triiso Polyoxyethylene-glycerin fatty acid esters such as stearate and the like, polyoxyethylene-fatty acid esters such as polyoxyethylene-distearate, polyoxyethylene-monodioleate, ethylene glycol distearic acid and the like; polyoxyethylene-lauryl Ether, polyoxyethylene-oleyl ether, polyoxyethyl Cetyl ether (such as ceteareth-16, ceteareth-17, ceteareth-18, ceteareth-20, ceteareth-22, or ceteareth-23, etc.), polyoxyethylene-stearyl ether, polyoxyethylene-be Polyoxyethylene-alkyl esters such as heyl ether, polyoxyethylene-2-octyldodecyl ether, polyoxyethylene-cholestanol ether, etc .; but are not limited thereto. Gel cosmetic composition according to the example may include 0.05 to 5% by weight of the above-described surfactant, but the present invention is not limited thereto.
나아가 본 발명의 일 실시예에 의한 젤 화장료 조성물은 1,2-헥산디올 및 메칠 파라벤 등의 방부제를 0.01 내지 3 중량% 더 포함할 수 있으나, 본 발명이 이에 제한되는 것은 아니다. Furthermore, the gel cosmetic composition according to one embodiment of the present invention may further include 0.01 to 3 wt% of preservatives such as 1,2-hexanediol and methyl paraben, but the present invention is not limited thereto.
본 발명의 일 실시예에 의한 젤 화장료 조성물은 젤 제형을 형성하기 위한 관점에서 정제수를 포함할 수 있으며, 다시 말해 본 발명의 일 실시예에 의한 젤 화장료 조성물은 수성 젤 화장료 조성물일 수 있다. The gel cosmetic composition according to an embodiment of the present invention may include purified water from the viewpoint of forming a gel formulation, that is, the gel cosmetic composition according to an embodiment of the present invention may be an aqueous gel cosmetic composition.
본 발명의 일 실시예에 의한 젤 화장료 조성물은 상술한 함량의 고형 성분 외에, 잔량의 정제수를 포함할 수 있으며, 좋게는, 본 발명의 일 실시예에 의한 젤 화장료 조성물은 정제수를 30 내지 60 중량%, 더욱 구체적으로는 30 내지 50 중량% 포함할 수 있으나 본 발명이 이에 제한되는 것은 아니다. 상술한 범위에서 도포가 용이하면서도, 수분 내에 분말화되어 빠른 속도로 유분을 흡수할 수 있는 장점이 있다. Gel cosmetic composition according to an embodiment of the present invention may include a residual amount of purified water in addition to the solid component of the above-described content, preferably, the gel cosmetic composition according to an embodiment of the present invention 30 to 60 weight of purified water %, More specifically, may include 30 to 50% by weight, but the present invention is not limited thereto. While easy to apply in the above-described range, there is an advantage in that it can be powdered in water to absorb oil at a high speed.
이하 본 발명을 실시예에 의해 구체적으로 설명한다. 아래에서 설명하는 실시예는 발명의 이해를 돕기 위한 것일 뿐, 본 발명이 실시예에 한정되지 않는다.Hereinafter, the present invention will be described in detail by way of examples. The embodiments described below are merely to aid the understanding of the invention, and the present invention is not limited to the embodiments.
[실시예 1]Example 1
중공 다공성 실리카 분말의 제조Preparation of Hollow Porous Silica Powder
30 중량% 농도의 규산소다 3500 g과 정제수 2000 g을 균일하게 혼합하여 규산소다 용액을 제조하였으며, 등유 5000 g과 Sorbitan mono stearate(Koremul SF-80, 한농화성) 50 g을 혼합하여 계면활성제 용액을 제조하였다. A sodium silicate solution was prepared by uniformly mixing 3500 g of sodium silicate and 2000 g of purified water at a concentration of 30 wt%, and a surfactant solution was prepared by mixing 5000 g of kerosene and 50 g of Sorbitan mono stearate (Koremul SF-80). Prepared.
호모믹서를 3500 rpm으로 회전하면서 규산소다 용액 : 계면활성제 용액을 2:1의 속도로 호모믹서에 혼합하여 에멀젼을 제조하였다. 여기에 14 중량%의 탄산 암모늄 용액 3600 g을 천천히 혼합하여 구형 미립자가 혼합된 슬러리를 수득하였다. 이를 원심분리기를 통하여 물을 분리하고, 세척하여 중공 다공성 실리카 분말을 수득하였다. An emulsion was prepared by mixing a sodium silicate solution: surfactant solution at a 2: 1 speed with a homomixer rotating at 3500 rpm. Here, 3600 g of 14% by weight of ammonium carbonate solution was slowly mixed to obtain a slurry in which spherical fine particles were mixed. The water was separated through a centrifuge and washed to obtain a hollow porous silica powder.
수득된 중공 다공성 실리카 공극 부피가 0.5 ㎖/g이며, 평균입경이 4 ㎛이고, 표면 공극이 10 ㎚인 중공 다공성 실리카 분말을 제조하였다. The hollow porous silica powder having the obtained porous porous silica pore volume of 0.5 ml / g, an average particle diameter of 4 m and a surface pore of 10 nm was prepared.
젤 Gel 화장료Cosmetics 조성물의 제조 Preparation of the composition
상기에서 제조된 중공 다공성 실리카 분말 15 g, 입경이 5.5 ㎛ 인 산화아연 입자 4 g, 잔탄검 1 g, 옥수수전분 5 g, 베타인 0.1 g, 하이드롤라이즈드히알루로닉애씨드 0.1 g, 양배추싹추출물0.1g, 1,2-헥산디올 0.2 g, 토코페롤 0.1 g 및 10 g의 정제수를 혼합하여 젤 화장료 조성물을 제조하였다. 15 g of the hollow porous silica powder prepared above, 4 g of zinc oxide particles having a particle size of 5.5 μm, xanthan gum 1 g, corn starch 5 g, betaine 0.1 g, hydrolyzed hyaluronic acid 0.1 g, cabbage sprout A gel cosmetic composition was prepared by mixing 0.1 g of extract, 0.2 g of 1,2-hexanediol, 0.1 g of tocopherol, and 10 g of purified water.
[비교예 1]Comparative Example 1
시판중인 ATO N O2 옥시젠 베이비 파우더 크림을 이용하여 실험을 수행하였다.Experiments were performed using commercially available ATO N O2 Oxygen Baby Powder Cream.
[비교예 2]Comparative Example 2
시판중인 ATO NB 파우더 로션을 이용하여 실험을 수행하였다.Experiments were performed using commercially available ATO NB powder lotions.
[비교예 3]Comparative Example 3
수아비스 하이포아 콘파우더 크림을 이용하여 실험을 수행하였다.Experiments were performed using a Suabis hypoa powder powder.
[비교예 4][Comparative Example 4]
존슨즈 베이비 파우더를 이용하여 실험을 수행하였다. Experiments were performed using Johnsons Baby Powder.
건조 후 제형 비교Formulation Comparison After Drying
실시예 1 및 비교예 1 내지 3에 의한 화장료 조성물을 각각 2 g 씩 플라스틱 판 위에 도포한 뒤, 상온에서 10시간 방치한 후, 건조 후 제형을 비교하여 도 1로 나타내었다. 2 g of each of the cosmetic compositions according to Example 1 and Comparative Examples 1 to 3 were applied on a plastic plate, and then left at room temperature for 10 hours, and then compared to the formulations after drying.
도 1을 참고하면, 본 발명의 실시예에 의한 젤 화장료 조성물 만이 분말화되어 유분을 흡수하는 것을 확인할 수 있다. Referring to Figure 1, it can be seen that only the gel cosmetic composition according to an embodiment of the present invention is powdered to absorb the oil.
흡유도Oil absorption 확인 Confirm
실시예 1의 젤 화장료 조성물을 건조시킨 후 분말을 수득하고, 비교예 4의 베이비 파우더를 이용하여 흡유도를 측정하였다. 100 g의 분말을 각각 준비한 뒤, 올리브 오일을 적가하고 균일하게 혼합하면서, 크림 제형이 되는 순간을 기준으로, 중량 차이를 이용하여 흡유도를 측정하였다. Powder was obtained after drying the gel cosmetic composition of Example 1, and the oil absorption was measured using the baby powder of Comparative Example 4. After preparing 100 g of each powder, the oil absorption was measured using the difference in weight, based on the moment when the cream formulation was added dropwise and uniformly mixed with olive oil.
그 결과, 실시예 1의 젤 화장료 조성물을 건조시킨 경우 100 g당 90 ㎖의 유분을 흡수하였으나, 비교예 1의 베이비 파우더는 45 ㎖의 유분을 흡수하였다. As a result, when the gel cosmetic composition of Example 1 was dried, 90 ml of oil per 100 g was absorbed, but the baby powder of Comparative Example 1 absorbed 45 ml of oil.
Claims (10)
건조 후 분말화 되는 젤 화장료 조성물. Zinc oxide particles and hollow porous silica powder having a void volume of 0.1 to 1.2 ml / g,
Gel cosmetic composition to be powdered after drying.
상기 중공 다공성 실리카는 평균 입경이 1 내지 15 ㎛이며,
전체 부피 중 중공 부피가 85% 이상인 젤 화장료 조성물. The method of claim 1,
The hollow porous silica has an average particle diameter of 1 to 15 ㎛,
Gel cosmetic composition having a hollow volume of at least 85% of the total volume.
상기 중공 다공성 실리카의 쉘은 직경이 0.05 내지 25 ㎚인 기공을 포함하는 다공성 쉘인 젤 화장료 조성물. The method of claim 2,
The shell of the hollow porous silica is a gel cosmetic composition is a porous shell containing pores having a diameter of 0.05 to 25 nm.
상기 젤 화장료 조성물은 중공 다공성 실리카를 10 내지 50 중량% 포함하는 젤 화장료 조성물. The method of claim 1,
The gel cosmetic composition is a gel cosmetic composition containing 10 to 50% by weight of a hollow porous silica.
상기 젤 화장료 조성물은 친수성 고분자 점증제를 더 포함하는 젤 화장료 조성물. The method of claim 1,
The gel cosmetic composition is a gel cosmetic composition further comprises a hydrophilic polymer thickener.
상기 젤 화장료 조성물은 상기 친수성 고분자 점증제를 0.05 내지 7 중량% 포함하는 젤 화장료 조성물. The method of claim 5,
The gel cosmetic composition is a gel cosmetic composition containing 0.05 to 7% by weight of the hydrophilic polymer thickener.
상기 젤 화장료 조성물은 옥수수 전분을 더 포함하는 젤 화장료 조성물. The method of claim 1,
The gel cosmetic composition is a gel cosmetic composition further comprises corn starch.
상기 젤 화장료 조성물은 건조 후 파우더의 평균 직경이 1000 ㎛이하인 젤 화장료 조성물. The method of claim 1,
The gel cosmetic composition is a gel cosmetic composition having an average diameter of less than 1000 ㎛ powder after drying.
상기 젤 화장료 조성물은 젤 화장료 조성물의 건조 후 분말을 기준으로,
상기 젤 화장료 조성물의 건조 후 분말 100 g 당 80 ㎖ 이상의 유분을 흡수하는 젤 화장료 조성물. The method of claim 1,
The gel cosmetic composition is based on the powder after drying the gel cosmetic composition,
Gel cosmetic composition that absorbs more than 80 ml of oil per 100 g of powder after drying the gel cosmetic composition.
상기 젤 화장료 조성물은 유분 흡수용인 젤 화장료 조성물. The method of claim 1,
The gel cosmetic composition is a gel cosmetic composition for oil absorption.