KR20180132647A - 흑연 함유 물품 - Google Patents

흑연 함유 물품 Download PDF

Info

Publication number
KR20180132647A
KR20180132647A KR1020187027386A KR20187027386A KR20180132647A KR 20180132647 A KR20180132647 A KR 20180132647A KR 1020187027386 A KR1020187027386 A KR 1020187027386A KR 20187027386 A KR20187027386 A KR 20187027386A KR 20180132647 A KR20180132647 A KR 20180132647A
Authority
KR
South Korea
Prior art keywords
graphite
article
cooking
layer
intermediate layer
Prior art date
Application number
KR1020187027386A
Other languages
English (en)
Other versions
KR102319252B1 (ko
Inventor
존 사우더드
라이언 웨인
토머스 웨버
Original Assignee
네오그라프 솔루션즈, 엘엘씨
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 네오그라프 솔루션즈, 엘엘씨 filed Critical 네오그라프 솔루션즈, 엘엘씨
Publication of KR20180132647A publication Critical patent/KR20180132647A/ko
Application granted granted Critical
Publication of KR102319252B1 publication Critical patent/KR102319252B1/ko

Abstract

조리기구 및 다른 가열 물품이 본 명세서에 포함된다. 물품은 조리기구의 하부 표면을 형성하는 기판을 가질 수 있다. 물품은 또한 흑연 중간 층 및 중간 층 위에 배치되는 조리/가열 표면을 가질 수 있다. 흑연 층은 다음 특성 중 하나 이상을 가질 수 있다; (1) 적어도 0.64 g/cm3의 밀도; (2) 주위 조건에서 물에 2.5 시간 침지 후 30 중량% 미만의 물 흡수(water pick-up); (3) 횡방향에서보다 기계 방향에서 적어도 25% 더 높은 테이버 강성도(Taber stiffness); 및 (4) 350 ppm 미만의 황 함량, 및 이들의 조합.

Description

흑연 함유 물품
본 개시는 조리 또는 가열 장치에 사용되는 물품 분야, 및 흑연의 중간 층을 포함하는 조리기구 물품 또는 실험 기구와 같은 특정 예에 관한 것이다.
조리기구의 종래 기술 유형은 다음을 포함한다: (1) 유도 조리를 위해 설계된 고 페라이트 스테인리스강 조성물; (2) 전도성 가열을 위해 설계된 일반 스테인리스강; (3) 유도 조리를 위해 고 페라이트 스테인리스강으로 코팅 또는 피복된 금속; 및 (4) 유리 또는 세라믹 조리기구.
본 명세서에 개시된 실시예는 조리기구뿐만 아니라 물체를 가열하기 위해 사용될 수 있는 다른 물품을 포함한다. 하나의 실시예에서, 물품은 조리기구의 하부 표면을 포함하는 기판을 가질 수 있다. 조리기구는 또한 흑연 중간 층 및 중간 층 위에 배치되는 조리 표면을 가질 수도 있다. 바람직하게는, 흑연 층은 다음 특성 중 하나 이상을 가질 수 있다: (1) 적어도 0.64 g/cm3의 밀도; (2) 주위 조건(ambient condition)에서 물에 2.5 시간 침지 후 30 중량% 미만의 물 흡수(water pick-up); (3) "횡방향"에서보다 "기계 방향"에서 적어도 25% 더 높은 테이버 강성도(Taber stiffness); 및 (4) 400 ppm 미만의 황 함량. 선택적으로는, 흑연은 이러한 특성의 임의의 조합을 가질 수 있다.
상기 일반적인 설명과 다음의 상세한 설명은 둘 다 본 발명의 실시예를 제공하며, 청구된 바와 같은 본 발명의 본질 및 특성을 이해하기 위한 개요 또는 구조를 제공하기 위한 것임을 알아야 한다. 첨부 도면은 본 발명의 추가적인 이해를 제공하기 위해 포함되고, 본 명세서에 통합되어 그 일부를 구성한다. 도면은 본 발명의 다양한 실시예를 도시하고, 상기 상세한 설명과 함께 본 발명의 원리 및 작동을 기술하는 역할을 한다.
도 1a는 가열하기 위해 사용될 수 있는 명세서에 개시된 흑연 물품의 실시예를 도시하고;
도 1b는 본 명세서에 개시된 와이어 메쉬를 갖는 흑연 물품의 또 다른 실시예를 도시한다.
도 2는 도 1a의 실시예에 표준 조리기구의 내용물을 가열하기 위해 사용되는 표준 조리기구가 조합된 사시도이고,
도 3은 조리기구 안의 도 1a의 실시예를 나타내는 내부도이고,
도 4는 본 명세서에 기술된 또 다른 실시예의 부분 단면도이고,
도 5는 본 명세서에 기술된 추가적인 실시예의 부분 단면도이고,
도 6은 조리에 사용될 수 있는 유도 가열을 도시하는 본 명세서에 개시된 실시예의 개략도이고,
도 7a는 표(표 IIa)이고, 도 7b는 표(표 IIb)로, 두 표는 본 명세서에 개시된 흑연 물품의 실시예에 대한 비등하기까지 걸리는 시간 조건을 나타낸다.
본 명세서에 개시된 하나의 실시예는 조리기구 물품을 포함한다. 조리기구 물품은 조리기구의 하부 표면을 포함하는 기판을 가질 수 있다. 조리기구는 흑연 층을 포함하는 중간 층 및 증간 층 위에 배치되는 조리 표면을 더 포함한다. 흑연 층은 압축된 박리 흑연 입자의 시트, 흑연화 중합체 또는 그들의 조합 중 적어도 하나를 포함할 수 있다. 선택적으로는, 중간 층은 이들의 임의의 조합으로 복수의 흑연 시트를 포함할 수 있다.
흑연 층은 다음의 특성 중 하나 이상을 가질 수 있다: (1) 최소 0.64 g/cm3, 최대 2.25 g/cm3의 밀도(이 사이의 임의의 밀도를 포함함); (2) 주위 조건에서 물에 2.5 시간 침지 후 30 중량% 미만, 바람직하게는 28 중량% 미만의 물 흡수; (3) "횡방향"에서보다 "기계 방향"에서 적어도 25%, 바람직하게는 적어도 30% 더 높은 테이버 강성도; 및 (4) 375 ppm 미만, 바람직하게는 250 ppm 미만 및 보다 바람직하게는 200 ppm 미만의 황 함량. 레코(Leco) S-144DR이 샘플의 황 함량을 측정하는데 사용될 수 있다. 레코 S-144DR는 주어진 샘플의 총 황 함량을 분석하기 위한 시스템이다. 이것의 최저 검출 한계치는 대략 50 ppm이다. 테이버 강성도를 측정하기 위한 장비는 미국 뉴욕주 노스 토나완다에 소재하는 테이버 인더스티리스로부터 구할 수 있다. 물 흡수는 특정 조건하에서 물에 침지 전후 흑연 층의 무게의 변화를 측정함으로써 결정될 수 있다.
특정 실시예에서, 흑연 물품은 열을 발생시키는 방식으로 적어도 15 KHz의 주파수에 의해 전달되는 충분한 전력으로 생성되는 인가 자기장에 성공적으로 결합(couple)하도록 하는 유효량의 자기 감수성 물질을 포함한다. 하나의 실시예에서 최대 약 50 KHz, 가능하게는 최대 70 KHz이다. 충분한 흑연 양의 한 예는 적어도 7 마이크로미터의 두께를 가지는 흑연 층이다. 적어도 하나의 예시적인 실시예에서, 두께의 상한은 약 5 mm일 수 있다. 조리에 사용되는 최대 주파수의 예는 100 KHz 이하이다.
추가적인 실시예에서, 중간 층의 흑연 층은 적어도 7 제곱인치(7-in2)를 포함하는 표면적을 가진다. 전형적으로는, 흑연 층은 1 제곱미터(1 m2)를 초과하는 표면적을 갖지 않을 것이다. 흑연 층에 대한 특정 풋 프린트(foot print) 크기의 예는 전형적으로 5 인치(5") 내지 12 인치(12") 직경의 팬에 대해 각각 78 내지 452 제곱인치(in2)다. 일부 특정 예는 300 내지 390 제곱인치(in2) 범위의 풋 프린트를 갖는 흑연 층을 포함한다.
또 다른 실시예에서, 흑연 층은 직경이 3 인치 내지 12 인치(3" 내지 12")인 흑연 디스크로부터 함께 압축된 단일 물품의 형태일 수 있다. 물품은 둘 내지 열 개(2 내지 10)의 압축된 박리 흑연 입자 층으로 형성될 수 있다. 각각의 흑연 층의 예시적인 두께는 0.85 g/cm3의 예시적인 밀도에서 5 밀(mil)일 수 있다.
하나의 특정 실시예에서, 흑연 중간 층은 반자성체로서 기능할 수 있고, 이는 도입된 인가 자기장의 반대 유도장을 발생시키는 자기 감수성을 나타낸다.
다른 특정 실시예에서, 흑연 중간 층은 인가된 자기장의 상호 작용을 변경시키고, 그에 의해 특정 열 반응을 조정하는 수단을 제공하는 구리, 알루미늄, 은, 철(강으로도 알려짐) 및 그 합금의 금속 필름과 같은 다른 박층에 접촉하게 배치될 수 있다. 임의의 특정 금속 필름의 두께는 약 5 마이크로미터 내지 약 0.5 mm(500 마이크로미터)일 수 있다.
다른 특정 실시예에서, 흑연 중간 층은 그 안에 매립된 하나 이상의 와이어 메쉬를 포함할 수 있다. 와이어 메쉬로 적합한 물질을 알루미늄, 황동, 컬럼븀, 구리, 금, 인코넬, 니켈, 니켈 합금, 인광체, 청동, 백금, 은, 스테인리스강, 저탄소강, 탄탈룸, 티타늄, 아연, 지르코늄, 폴리에테르에테르 케톤(PEEK), PTFE, PFA, ECTFE, 폴리프로필렌, 폴리에틸렌, PET(예를 들어, 듀폰(Dupont)의 등록 상표인 마일라(Mylar)®, 이에 한정되지 않음) 및 그의 조합물을 포함할 수 있다. 흑연 중간 층 내에 메쉬를 포함하는 것은 흑연이 다른 물품에 도입하기 위한 3-D 형상으로 용이하게 성형될 수 있게 한다.
흑연은 조리기구 제조에 보통 사용되는 강자성 물질과 비교하여 상당히 다른 열 특성, 밀도 및 자성 특성을 가진다. 흑연을 이용하는 조리기구는 (1) 경량, (2) 열 반응, 및 (3) 열적으로 균일한 조리 중 하나 이상의 이점을 가질 수 있다. 이러한 이점은 모든 표면 조리 기술(예를 들어, 가스, 종래 전기, 적외선 및 유도 쿡탑)에서 잘 작동할 수 있다. 아래 표 1의 특성 차이를 참고하라.
물질 면내 열 전도율(W/mK) 밀도(g/cm3) CTE 선형(10-6·K-3) 비열용량(J/Kg·K) 몰 열용량(J/mol·K) 부피 비열용량 실질적인 자기 감수성
흑연 300-2000 0.64-2.27 0.5 0.71 0.0085 0.0192 예
구리 385 8.96 17 0.39 0.0244 7.9022 특별 상황
알루미늄 205 2.70 23.1 0.90 0.0243 2.3651 아니오
스테인리스강(1810) 16-21 7.99 17.3 0.50 0.0277 7.9900 아니오
강(고 페라이트 강) 50 7.87 11.8 0.44 0.0246 6.9768 예
유리 0.8 2.4-2.8 0.33 0.84 0.0505 4.5515 아니오
본 명세서에 기술된 실시예에 관련하여 흑연의 열 성능에 대한 다른 중요 특성은 몰 열용량과 부피 비열용량을 포함한다. 이러한 특성은 특정 물질이 얼마나 빨리 열을 얻고 방출하는지에 대한 좋은 지표가 될 수 있어서, 흑연의 열 반응 이점을 나타낸다.
흑연의 대안적인 유형은 이소몰딩(isomolded)된 흑연, 압출 흑연, 흑연 폼(foam), 몰딩된 흑연 또는 그의 조합 중 적어도 하나를 포함할 수 있다.
선택적으로는, 조리기구 물품은 기판과 중간 층 사이에 배치되는 단열 재료를 더 포함할 수 있다. 조리기구에 선택적으로 포함될 수 있는 단열 재료는 에어로젤, 유리-울, 섬유 유리, 탄소 섬유, 탄소 폼, 고온 플라스틱 또는 세라믹 단열재, 및/또는 그래핀을 포함한다.
기판은 유도에 의해 조리하기에 불충분한 양의 강자성 물질을 포함할 수 있다. 대안적으로는, 기판은 비자성 물질을 포함할 수 있다. 본 개시의 목적상, 비자성 물질은 조리/가열에 충분한 주목할 만한 열 반응을 발생시키는 방식으로 인가된 자기장에 반응하지 않는 물질이다. 물질은 그로부터 제조되는 물품이 표준 온도 및 압력의 주어진 초기 조건에서 분당 2℃ 미만의 열 상승을 발생시키는 경우 조리 또는 가열 목적상 비자성으로 간주될 수 있다.
또 다른 실시예에서, 기판은 약 75 W/mK 미만의 수직 방향(through plane) 열 전도율을 가질 수 있다. 이러한 물질의 비제한적인 예에는 저 페라이트 스테인리스강, 유리(예를 들어, 붕규산 유리), 세라믹, 플라스틱, 코르크, 나무 또는 상기 자기장에 노출 시 그의 자기 특성상 각각의 열 안정성 한계(즉, 녹는점 또는 분해 온도)에 의해 상기 임계치 초과의 에너지를 생성하지 않는 기타 물질이 포함된다. 이 실시예들은 함께 또는 개별적으로 실시될 수 있다. 더 높은 열 전도율을 갖는 물질이 요구될 경우, 옵션에는 알루미늄, 구리, 은, 및/또는 기타 금속 및 그의 합금이 포함될 수 있다.
위의 실시예가 적합한 조리기구의 예에는 베이킹 팬, 냄비, 프라이팬, 취반기, 그릴, 팝콘 제조기, 커피 포트, 찻주전자, 커피 머그잔, 소테 팬 및 수프 접시가 포함된다. 조리기구는 대류, 전도, 적외선 또는 유도 가열에 사용될 수 있다. 본 명세서에 개시된 개념은 또한 오븐용 쿡탑 또는 레인지 탑 스토브와 같은 조리 표면에 적용할 수도 있다. 이러한 실시예에서, 흑연 층은 하부 층과 상부 표면 사이의 중간 층일 것이다. 상부 표면은 조리해야 할 액체 또는 음식과 접촉하는 실질적인 표면이 아니라 가열해야 할 물품에 열-전달 층으로 기능할 수 있다.
조리기구의 특정 실시예에서, 기판은 흑연 중간 층을 지지하기 위한 구조물(structrual architecture)을 포함한다. 구조물은 자기장에 노출 시 조리에 적합한 열 반응을 생성하기에 불충분한 양의 자기 감수성 물질을 포함하고, 그에 따라 자기장은 구조물을 통과한다. 중간 층 내의 흑연은 자기장에 노출 시 유효량의 자기 감수성을 가진다. 자기 감수성은 조리기구의 조리 표면에 전도되는 열을 발생시킴으로써, 조리기구로부터 음식 또는 조리하거나 가열시켜야 할 기타 물질에 열을 전달한다.
조리기구에서 선택적인 단열 재료는 다양한 방식으로 이용될 수 있는데, 예를 들어 측벽을 갖는 조리구에 관해서는 단열 재료는 측벽 전체에 균일하게 배치될 수 있다. 또 다른 선택적인 실시예로, 단열 재료는 중간 층 아래에 균일하게 또는 중간 층 아래에 불균일하게 배치될 수 있다. 추가의 선택적인 실시예에서, 단열 재료는 중간 층의 두께를 따라 연장될 수 있다.
본 명세서에 개시된 조리기구의 실시예는 알루미늄, 및/또는 저 페라이트 스테인리스강 또는 앞서 언급한 자기장에 노출 시 그의 자기 특성 때문에 상기 임계치 이상의 열을 생성하지 않는 기타 금속 또는 합금 안에 매립된 전술한 흑연을 포함한다. 이 실시예는 특히 적어도 다음 유형의 조리기구에 적용된다: 비등 보조 플레이트, 조리기구 어댑터, 확산판, 보온 수프 그릇, 음식 서빙 도구, 취반기, 팝콘 제조기, 유도 그릴 가열 요소, 유도 레인지 가열 요소, 유도 커피 포트, 유도 찻주전자, 유도 이용가능 커피 머그잔 및 유도 이용가능 음식 저장 용기뿐만 아니라 위에서 언급한 조리기구의 유형.
본 명세서에서 개시된 조리기구의 또 다른 실시예는 상기 자기장에의 노출을 통한 열의 발생을 가능하게 하기 위한 붕규산 유리, 알루미노규산염 유리, 산화물 유리, 유리 세라믹, 또는 그 외에 고온 유리 또는 세라믹 재료 안에 매립된 앞서 언급한 흑연을 포함한다. 이 실시예는 또한 위의 문단에 기술된 상기 유형의 조리기구에 적용 가능하다. 적어도 상기 유형의 조리기구에 적용 가능한 추가의 실시예는 자기장에의 노출을 통해 열의 발생을 가능하게 하기 위한, 고밀도 또는 저밀도 폴리에틸렌(HDPE 또는 LDPE), 기타 고온 플라스틱, 또는 고온 플라스틱 복합체(예를 들어 흑연 섬유 복합체) 내에 매립된 앞서 언급한 흑연을 포함한다.
본 명세서에 개시된 흑연은 하기의 유리한 재료 특성의 독특한 조합을 가질 수 있다: (1) 자기장과의 결합(coupling), (2) 열 확산, (3) 요구되는 열 용량(즉, 열을 빠르게 얻고 방출하는 것), 및 (4) (경량 물품을 촉진하는) 다른 잠재적 재료에 비해 낮은 밀도.
본 명세서에 개시된 개념을 도면에 따라 추가로 예시하고 설명한다. 이제 도 1a을 참조하면, 가열에 사용될 수 있는 본 명세서에 개시된 흑연 물품의 실시예가 일반적으로 10'으로 도시되어 있다. 흑연 물품(10')은 내부 흑연 섹션(12)을 포함할 수 있다. 섹션(12)은 임의의 원하는 형상일 수 있다. 바람직하게는, 섹션(12)은 적어도 7 마이크로미터의 두께를 가진다. 섹션(12)은 상술한 흑연 유형 중 어느 하나 또는 그의 조합으로 구성될 수 있다. 테두리 부분(trim piece)(14)은 섹션(12)을 둘러쌀 수 있다. 테두리 부분(14)은 바람직하게는 자기장과 충분히 결합하지 않는 임의의 재료로 제조될 수 있다. 또한, 테두리 부분(14)은 유리, 플라스틱, 또는 세라믹을 포함하나 이에 제한되지 않는 임의의 단열 재료로 구성될 수 있다.
이제 도 1b를 참조하면, 흑연 물품의 또 다른 실시예가 일반적으로 10"으로 도시되어 있다. 흑연 물품(10")은 상술한 바와 같은 내부 흑연 섹션(12)을 포함하고, 그 안에는 와이어 메쉬(13)가 매립되어 있다. 와이어 메쉬(13)는 상술한 바와 같은 재료로 형성된다. 동일한 재료로 형성되거나 다른 재료로 형성될 수 있는 하나 초과의 와이어 메쉬(13)가 포함될 수 있다는 점을 이해해야 한다. 흑연 섹션(12) 내에 메쉬(13)를 포함하는 것은 흑연 섹션이 다른 물품에 도입하기 위한 3-D 형상으로 용이하게 성형될 수 있게 한다. 테두리 부분(14)은 상술한 바와 같이 섹션(12)을 둘러쌀 수 있다.
흑연 물품들(10' 및 10")은 일반적으로 흑연 물품(10)으로 지칭될 수 있다.
도 2에 도시된 바와 같이, 팬(pan)(20)이 팬 내부의 물질을 가열하기 위한 물품(10)의 상부에 위치할 수 있다. 흑연 물품(10)은 팬(20)에 열을 가하기 위해서 유도-가열 표면 또는 저항 가열 표면(미도시) 상에 위치할 수 있다. 흑연 물품(10)은 도 2에 도시된 바와 같이 팬(20) 아래에 위치하여 팬(20) 안의 내용물을 가열할 수 있거나, 또는 물품(10)은 도 3에 도시된 바와 같이 팬(20) 안에 위치하여 팬(20)의 내용물을 가열할 수 있다.
도 4는 본 명세서에 기술된 또 다른 실시예의 부분 단면도이다. 도 4에 도시된 것은 냄비(40)로서, 조리 표면(42) 및 흑연 중간 층(44) 및 기판(46)을 포함한다. 도시된 바와 같이, 조리 표면(42) 및 기판(46)은 금속, 유리, 세라믹 또는 기타 선택 재료로 구성될 수 있으나, 상술된 실시예 중 임의의 것이 팬(40)에 적용될 수도 있다. 동일하게는, 중간 층에 관한 위의 설명 또한 중간 층(44)에도 적용된다. 도 5에 도시된 바와 같이, 이 개념은 또한 유사하게 조리 표면(52), 중간 층(54) 및 기판(56)을 포함하는 포트(50)에 적용될 수도 있다.
도 6은 일반적으로 60으로 도시되는 조리에 사용될 수 있는 유도 가열 조립체를 도시하는 본 명세서에 개시된 실시예의 개략도이다. 유도 가열 조립체(60)는 유도 호브(induction hob)(62)를 포함한다. 유도 호브(62)에 전기의 인가는 일반적으로 15 KHz 초과의 주파수를 갖는 자기장을 발생시킨다.
또한, 도 6에서, 가열 요소(64)는 외측 케이싱(66)을 포함할 수 있다. 케이싱(66)은 가열 요소(64)의 다른 구성 성분들을 둘러쌀 수 있다. 가열 요소(64)는 유도 호브(62)에 인접한 단열 재료(67)를 포함할 수 있다. 가열 요소(64)는 유도 호브(62)와는 반대쪽에서 상의 단열 재료(67)에 인접하는 흑연 층(68)을 더 포함할 수 있다. 바람직하게는, 흑연 층(68)은 호브(62)에 의해 생성되는 자기장에 노출 시 그의 자기 감수성이 효과적으로 결합해서 열을 발생시키기에 충분한 두께를 포함한다.
이제 도 7a 및 도 7b를 참조하면, 본 명세서에 기술된 흑연 물품의 다양한 실시예에 대한 비등 시간 정보를 나타내는 표 IIa 및 IIb가 제공된다. 1 내지 5 개의 층을 갖는 실시예에서, 350 ppm 미만의 황 함량을 갖는 압축 팽창 천연 흑연을 분석하였다. 또한, 1 내지 6 개의 층을 갖는 합성 흑연을 분석하였다. 표 IIa 및 IIb는 이들 실시예의 흑연 층의 유효 개수에 대한 비등하기까지 걸리는 시간을 나타냈다.
본 명세서에 개시된 조리기구 실시예는 또한, 액체, 기체, 또는 고체의 급속 가열이 요망되는 실험 기구("lab ware") 또는 산업 공정 장비에 적용될 수도 있다. 적합한 액체의 예는 물에서 합성 또는 유기 중합체까지 다양할 수 있다. 조리기구 외부에 적용될 수 있는 물품의 예는 앞서 언급한 기판, 앞서 언급한 흑연 층 및 흑연 층 위에 배치되는 상부 표면을 포함할 수 있다. 적용 가능한 물품의 비제한적인 예로는 비커, 플라스크 등이 포함된다. 조리기구 실시예와 동일하게 이들 실시예에서도 흑연 층은 작업편(work piece)(고체 및/또는 액체)과 접촉하는 실험 기구의 작업 표면과 열을 교류하는 중간 층이 될 것이다. 선택적으로는, 단열 층이 실험 기구의 작업 표면에 반대쪽에서 흑연 층에 인접하여 포함될 수 있다.
특정 중요 실시예는 유리 및/또는 세라믹 층 사이에 낀 흑연 중간 층을 갖는 물품을 포함할 수 있다. 선택적으로는, 이 실시예는 단열 층을 포함할 수 있다. 바람직하게는, 단열 층은 가열되거나 조리되는 작업편에 열전달을 촉진하는 위치에서 흑연 층에 인접하게 위치할 수 있다. 이러한 위치의 예는 흑연 층의 가장자리를 따르고/거나 유도 호브에 가장 가까운 흑연 층의 표면을 포함할 수 있다. 하나의 실시예에서, 단열재는 단일 방향으로 열의 전달을 단리 및 유도함으로써 원하는 열 효과의 방향에서 열전달 효율을 최적화하고 하나 이상의 원하지 않은 방향에서의 열전달을 차폐하는 기능을 한다.
산업 분야 실시예의 경우, 흑연은 고온 압착을 위한 압반을 형성할 수 있다. 이러한 흑연 압반은 압착할 작업편에 적용될 수 있다. 흑연은 작업편과 열 교류한다. 또한 유도 호브는 압반과 교류하며 자기장을 생성하는 데 사용되어, 작업편을 고온 압착하기 위한 열을 발생시킨다. 압반을 위한 적절한 유형의 흑연은 가요성 흑연의 라미네이트(수지 함침, 비-수지 함침 및 그의 임의의 조합), 이소몰딩된 흑연, 몰딩된 흑연 또는 압출 흑연, 또는 유도 반응 원료로 사용될 수 있는 다른 기타 적절한 등급의 구조적 흑연을 포함한다. 이 공정은 평면뿐만 아니라 비평면 물품을 제조하는 데 사용될 수 있다. 원하는 경우, 각각의 압반은 자체 유도 호브를 가질 수 있다.
본 명세서에 개시된 또 다른 실시예는 상부 기판과 하부 기판의 사이에 배치된 압축된 박리 흑연 입자, 흑연화 중합체 또는 이들의 조합 중 하나의 흑연 시트를 포함한다. 단열재는 흑연 시트와 하부 기판 사이에 위치할 수 있다. 상부 기판, 흑연 시트, 단열 층 및 하부 기판의 조립체는 유도 가열되는 것이 바람직할 수 있는 임의의 유형의 물품에 도입될 수 있다. 바람직하게는, 하부 기판은 유도 코일에 더 가깝게 배치되고, 조립체의 상부 기판은 가열시킬 작업편에 가장 가깝다. 대안적인 실시예에서, 원한다면, 흑연 시트는 열을 발생시키기 위해 자기장과 결합하기 쉬운 또 다른 물질로 대체될 수 있다. 또한, 하부 기판은 열을 발생시키기 위해 자기장과 결합하기 쉬운 물질이 아니라는 점을 제외하면 임의의 특정 물질에 제한되지 않는다. 이 실시예에서, 흑연 시트는 표준 물질부터 위에서 언급한 유형의 흑연까지 다양할 수 있다.
자기장을 유도하기 위해 압축된 박리 흑연 입자("CPEG")의 덩어리를 사용하기 위한 일부 바람직한 실시예에 관해서는, 독립된 예시적인 특성의 예는 적어도 300 ㎛의 두께를 갖는 흑연 덩어리를 포함할 수 있다. CPEG의 적합한 덩어리 두께는 약 1.5 mm(1500 ㎛) 이하로 확인되었다. 300 ㎛ 내지 1500 ㎛의 모든 두께가 본 명세서에 개시된 바와 같이 고려된다. 바람직하게는, CPEG 덩어리는 1.22 g/cc 초과의 밀도를 가진다. 자기장을 유도하기 위한 흑연 층 평면에 관해서는, CPEG 덩어리에서 층 평면의 예시적인 수는 적어도 425,000이다. 그래핀의 층 평면의 상한 개수의 예는 최대 약 3,000,000이다. 본 명세서에서는 425,000 내지 3,000,000의 모든 흑연 층 평면 개수가 고려되지만, 그래핀 층 평면의 하나의 바람직한 범위는 100,000 내지 180,000이다.
흑연화 중합체 실시예에 관해서는, 바람직한 두께는 적어도 45 ㎛이다. 흑연화 중합체의 덩어리 두께의 상한은 300 ㎛ 이하이고, 본 명세서에서는 45 내지 300 ㎛의 모든 두께가 고려된다. 흑연화 중합체 덩어리에서 그래핀 층 평면의 바람직한 개수는 적어도 100,000을 포함한다. 비제한적인 상한의 예는 600,000 미만일 수 있다. 흑연화 중합체의 덩어리에 대한 그래핀 층 평면의 바람직한 범위는 250,000 내지 600,000을 포함할 수 있다. 흑연화 중합체 덩어리에 대한 또 다른 독립적인 특성은 전기 전도도를 포함할 수 있다. 실시예에서, 바람직한 평면 내 전기 전도도는 적어도 16000 S/cm이다. 평면 내 전기 전도도에 대한 비제한적인 예시적인 상한은 최대 20000 S/cm일 수 있다.
본 명세서에서 고려되는 추가의 실시예는 복합체 매트릭스를 형성하는 것을 포함하며, 이에 의해 자기장에 충분히 유도 결합하여 충분한 양의 열을 발생시키기에 적합한 전구체를 제조하기 위한 다양한 형태의 세라믹 전구체 및/또는 유리 전구체 재료에 흑연 분말을 도입할 수 있으므로, 복합체를 유도 가열 분야에 사용할 수 있다. 이 실시예의 이점은 복합체 매트릭스가 임의의 원하는 형태로 더 변형될 수 있다는 점이다. 마찬가지로, 복합체 매트릭스는 임의의 원하는 물품에 도입될 수 있다.
본 명세서에 개시된 각각의 실시예는 다음 이점 중 적어도 하나를 제공할 수 있다; (1) 평면 내 열 전도율의 증가; (2) 균일한 열전달; (3) 고온점(hot spot) 제거; (4) 시간 경과에 따른 치수 변화 감소; (5) 조리기구의 뒤틀림 감소; (6) (특정 유형의 조리기구의 반복된 사용과 관련된 수분 및 산소에 노출로 인한) 조리기구의 얼룩 감소; (7) (산이 풍부한 음식과 특정 유형의 조리기구의 표면의 반응과 관련된) 조리기구의 변색 감소; (8) 유도 조리 동안의 진동 감소 및 그에 의해 발생하는 소음의 제거; (9) 조리기구 상의 코팅은 더 긴 수명을 보임; (10) 비용 절감; (11) 무게 감소; (12) 유도 조리를 위한 고 페라이트 기재 스테인리스강의 불가피한 사용의 제거; (13) 단순한 구조; 및 (14) 가열 및/또는 냉각 중 열 조절에 있어서 향상된 정밀도(resolution)를 갖는 조리기구.
다양한 실시예는 이들의 임의의 조합으로 실시될 수 있다.
이 출원에서 인용된 모든 특허 및 간행물은 그 전체가 참조로 포함된다.
본 발명이 이와 같이 설명되었지만, 여러 방식으로 변경될 수 있음은 명백할 것이다. 위 명세서를 읽고 이해한 후 통상의 기줄자에게 수정 및 변경이 생각날 것이다. 본 발명은 첨부된 청구범위 또는 그 균등물의 범위 내에 있는 한에서는 이러한 모든 수정 및 변경을 포함하는 것으로 해석되어야 한다.

Claims (24)

  1. 조리기구 물품으로서,
    조리기구의 하부 표면을 포함하는 기판;
    350 ppm 미만의 황 함량을 갖는 흑연 층을 포함하는 중간 층; 및
    중간 층 위에 배치되는 조리 표면을 포함하는 조리기구 물품.
  2. 제1항에 있어서, 흑연은 적어도 0.64 g/cm3의 밀도를 가지는 조리기구.
  3. 제2항에 있어서, 황 함량이 200 ppm 이하인 조리기구.
  4. 제2항에 있어서, 기판과 중간 층 사이에 배치되는 단열재를 더 포함하는 조리기구.
  5. 제2항에 있어서, 중간 층 내의 흑연의 양은 적어도 15 KHz 주파수의 자기장에 노출 시 열을 발생시키기에 충분한 양을 포함하는 조리기구.
  6. 제1항에 있어서, 기판은 유도에 의해 조리하기에 불충분한 양의 강자성 물질을 포함하는 조리기구.
  7. 제1항에 있어서, 흑연 층의 표면적이 적어도 7 제곱인치를 포함하는 조리기구.
  8. 제1항에 있어서, 기판은 약 75 W/m·K 미만의 수직 방향(through plane) 열 전도율을 갖는 조리기구.
  9. 제1항에 있어서, 기판은 중간 층의 흑연을 지지하기 위한 구조물을 포함하고, 구조물은 적어도 15 KHz의 자기장에 노출 시 조리 적용에 효과적으로 결합(couple)될 수 있는 유효량의 물질을 함유하지 않는 조리기구.
  10. 제1항에 있어서, 흑연의 테이버 강성도(Taber stiffness)가 흑연 층의 횡방향에 비해 흑연 층의 기계 방향에서 적어도 30% 더 높은 조리기구.
  11. 제1항에 있어서, 흑연 층의 물 흡수(water pickup)는 주위 압력(ambient pressure)에서 실온의 물에 2.5 시간 침지 후 30 중량% 미만을 포함하는 조리기구.
  12. 제11항에 있어서, 흑연의 테이버 강성도가 흑연 층의 횡방향에 비해 흑연 층의 기계 방향에서 적어도 25% 더 높은 조리기구 물품.
  13. 제1항에 있어서, 흑연 층 안에 매립된 와이어 메쉬를 더 포함하는 조리기구.
  14. 제1항에 있어서, 흑연은 압축된 박리 흑연 입자의 시트, 흑연화 중합체, 및 이들의 조합 중 적어도 하나를 포함하는 조리기구.
  15. 조리기구 물품으로서,
    조리기구의 하부 표면을 포함하는 기판;
    7 마이크로미터 초과의 두께 및 횡방향에서보다 기계 방향에서 적어도 25% 더 높은 테이버 강성도를 갖는 흑연 층을 포함하는 중간 층; 및
    중간 층 위에 배치되는 조리 표면을 포함하는 조리기구 물품.
  16. 조리기구 물품으로서,
    조리기구의 하부 표면을 포함하는 기판;
    7 마이크로미터 초과의 두께 및 주위 조건(ambient condition)에서 물에 2.5 시간 침지 후 30 중량% 미만의 물 흡수를 갖는 흑연 층을 포함하는 중간 층; 및
    중간 층 위에 배치되는 조리 표면을 포함하는 조리기구 물품.
  17. 적어도 하나의 주요 평면 표면을 가지는 흑연 물품으로서, 물품은 기계 방향 및 횡방향을 가지고, 물품의 테이버 강성도가 횡방향에 비해 기계 방향에서 적어도 25% 더 높은 물품.
  18. 제17항에 있어서, 물품의 적어도 하나의 둘레가 50 W/mK 미만의 열 전도율을 가지는 단열 재료로 둘러싸이는 물품.
  19. 물품으로서,
    물품의 하부 표면을 포함하는 기판;
    350 ppm 미만의 황 함량을 갖는 흑연 층을 포함하는 중간 층; 및
    중간 층 위에 배치되는 상부 표면을 포함하는 물품.
  20. 제19항에 있어서, 기판 또는 상부 표면 중 적어도 하나는 75 W/mK 미만의 열 전도율을 가지는 물품.
  21. 제19항에 있어서, 흑연 층 안에 매립된 와이어 메쉬를 더 포함하는 물품.
  22. 제19항에 있어서, 흑연은 압축된 박리 흑연 입자의 시트, 흑연화 중합체, 및 이들의 조합 중 적어도 하나를 포함하는 물품.
  23. 제19항에 있어서, 흑연은 적어도 하나의 주요 평면 표면을 가지고, 흑연은 기계 방향 및 횡방향을 가지고, 흑연의 테이버 강성도가 횡방향에 비해 기계 방향에서 적어도 25% 더 높은 물품.
  24. 제22항에 있어서, 주위 조건에서 물에 2.5 시간 침지 후 30 중량% 미만의 물 흡수를 갖는 물품.
KR1020187027386A 2016-03-31 2017-03-28 흑연 함유 물품 KR102319252B1 (ko)