KR20180063997A - self-cleaning olefin sheet and its manufacturing method - Google Patents

self-cleaning olefin sheet and its manufacturing method Download PDF

Info

Publication number
KR20180063997A
KR20180063997A KR1020160164052A KR20160164052A KR20180063997A KR 20180063997 A KR20180063997 A KR 20180063997A KR 1020160164052 A KR1020160164052 A KR 1020160164052A KR 20160164052 A KR20160164052 A KR 20160164052A KR 20180063997 A KR20180063997 A KR 20180063997A
Authority
KR
South Korea
Prior art keywords
layer
olefin film
primer layer
film
olefin
Prior art date
Application number
KR1020160164052A
Other languages
Korean (ko)
Other versions
KR101889615B1 (en
Inventor
김응서
박병래
Original Assignee
김응서
박병래
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김응서, 박병래 filed Critical 김응서
Priority to KR1020160164052A priority Critical patent/KR101889615B1/en
Publication of KR20180063997A publication Critical patent/KR20180063997A/en
Application granted granted Critical
Publication of KR101889615B1 publication Critical patent/KR101889615B1/en

Abstract

The present invention provides a decoration sheet which is usable as an outer covering material rarely polluted even in a state of being exposed to external environment, and which is easily cleaned by rainwater even though polluted. To achieve the purpose, the present invention comprises: an olefin film (1); a PP primer layer (2) formed on a bottom surface of the olefin film (1); an adhesive (3) formed on an upper surface of the olefin film (1); a printed layer (4) formed on the adhesive (3); a transparent olefin film (5) formed on the printed layer (4); a base primer layer (6) base-processed on an upper surface of the transparent olefin film (5); and a finishing primer layer (6) finish-processed on the base primer layer (6).

Description

셀프 클리닝 기능의 올레핀시트 및 그 제조 방법{self-cleaning olefin sheet and its manufacturing method}BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a self-cleaning olefin sheet,

본 발명은 친환경 올레핀 필름재질(CPP)에 특수코팅 처리를 하여, 기존에 사용되고 있는 각종 표면재의 단점을 보강한 것으로, 내오염성이 우수하고 자가세척이 가능하여 실외매연이나 얼룩현상 등이 없으며, 특히 자가 세척이 가능하여 항상 청결한 제품상태를 유지 가능한 셀프클리닝 기능을 갖는 올레핀시트에 관한 것이다.The present invention provides a special coating process for an environmentally friendly olefinic film material (CPP) to reinforce the disadvantages of various surface materials conventionally used, and is excellent in stain resistance and can be self-cleaned, To an olefin sheet having a self-cleaning function capable of self-cleaning and always maintaining a clean product state.

[문헌 1][Document 1]

올레핀 데코레이션 시트 및 그의 제조방법(olefin decoration sheet and its manufacturing method)Olefin decoration sheet and its manufacturing method (olefin decoration sheet and its manufacturing method)

출원인 : 김응서 출원번호 : 10-2013-0065688(출원일자 : 2013.06.10)Applicant: Kim, Eosung Application number: 10-2013-0065688 (filing date: 2013.06.10)

등록번호 : 10-1490666(등록일자 : 2015.01.31)Registration number: 10-1490666 (Registration date: 2015.01.31)

종래의 데코레이션 시트 등은 실내,외 외장 피복재로 많이 사용되고 있다.Conventional decoration sheets and the like are widely used as interior and exterior covering materials.

그러나 특히 실외에 사용되는 각종 외장 피복 데코레이션 재료는 외부환경에 노출되어, 심하게 오염되게 되며 오염이 되는 경우 청소하기가 어려워 외관상 매우 좋지 않을 뿐만 아니라 빈번한 청소로 인해 유지 관리비가 많이 소요되고 심한 경우 내장재 까지 손상이 오게된다.However, various exterior decoration materials used especially for outdoor use are exposed to the external environment and become very polluted. In case of pollution, it is difficult to clean. It is not very good in appearance, and maintenance maintenance cost is high due to frequent cleaning. Damage comes.

따라서 데코레이션시트는 실내 또는 각종 생활용품의 외장 피복재로 사용에 한정되며, 각종 건축물의 건물 외벽 등과 같은 외장 피복재로는 잘 사용하지 않고 있다.Therefore, the decoration sheet is limited to use as an exterior covering material for indoor or various household goods, and is not used as an exterior covering material such as a building outer wall of various buildings.

본 발명은 상기한 점을 감안하여 발명한 것으로, 외부 환경에 노출된 상태에서도 오염이 잘 생기지 않고 오염이 있어도 빗물에 쉽게 세척되는 외장 피복재로도 사용 가능한 데코레이션 시트를 제공함에 본 발명의 목적이 있다.The present invention has been made in view of the above-mentioned problems, and it is an object of the present invention to provide a decoration sheet which can be used as an exterior covering material which is easily washed in rainwater even if it is not contaminated even when exposed to external environment .

또한 본 발명은 하도프라이머층(6)을 형성하기 위한 용제를 제외한 모든 소재의 성분이 친환경 소재이어서 인체에 무해한 시트를 제공함에 본 발명의 목적이 있다. 그 외 추가적인 목적은 이하, 발명의 상세한 설명에서 상술한다.Further, the present invention has an object of providing a sheet which is harmless to the human body because all the ingredients of the material except the solvent for forming the undercoat primer layer 6 are eco-friendly materials. Further and further objects are described below in detail in the description of the invention.

상기 본 발명의 목적을 해결하기 위한 본 발명의 주요 구성은, 올레핀필름(1)과, 상기 올레핀필름(1) 저면에 형성시키는 PP프라이머층(2)과, 상기 올레핀필름(1) 상면에 형성시키는 접착제(3)와, 접착제(3) 상에 형성시키는 인쇄층(4)과, 인쇄층(4) 상에 형성시키는 투명올레핀필름(5)과, 투명올레핀필름(5)상면에 하도 처리한 하도프라이머층(6)과, 하도프라이머층(6)에 상도 처리한 상도처리층(7)을 포함하는 것을 특징으로하며, 상기 접착제는 레트로치용 접착제인 것을 특징으로 하며, 상기 하도프라이머층(6)의 재료는 1액형을 사용하며, 도막두께는 3-5마이크론이며, 상도처리층(7)은 2액형을 사용하며, 도막두께는 5-10마이크론 두께인 것을 특징으로 하며, 상기 하도프라이머층(6)의 하도코팅이 성분은 디메틸포름아미드, 톨루올, 이소프로필알콜, 메칠에칠케톤, 사이크론 헥산 중량 비율로 이루어지는 것을 특징으로 하며, 상기 하도프라이머층(6)의 성분은 디메칠포름아미드 20, 톨루올 15, 이소프로필알콜 20, 메칠에칠케톤 25, 사이크론 헥산 20 중량 비율로 이루어지는 것을 특징으로 하며, 상기 상도처리층(7)의 코팅은 주제:경화제 비율이 2:1 이며, 주제 성분은 실란 트리메톡시 비닐계, 헥사메틸렌 글리콜, 이소프로필 알코올, 디 수소산화물의 구성으로 이루어지며, 경화제는 폴리우레탄레진을 포함하는 것을 특징으로 하며, 상기 상도처리층(7)의 코팅은 주제 성분은 실란 트리메톡시 비닐계 60, 헥사메틸렌 글리콜 20, 이소프로필 알코올 10, 디 수소산화물 10의 중량비 구성으로 이루어지며, 경화제는 폴리우레탄 레진 40과 물 60 중량비로 이루어지는 것을 특징으로 한다(1), a PP primer layer (2) formed on the bottom surface of the olefin film (1), and a protective layer (2) formed on the top surface of the olefin film (4) formed on the adhesive (3), a transparent olefin film (5) formed on the printing layer (4), and a transparent olefin film Characterized in that the primer layer (6) comprises an undercoat primer layer (6) and a top coat layer (7) top-treated on the undercoat primer layer (6), characterized in that the adhesive is a retrograde adhesive, ) Is one-component type, the film thickness is 3-5 microns, the upper treatment layer 7 is a two-component type, and the film thickness is 5-10 microns. The lower primer layer (6) This component can be dissolved in an organic solvent such as dimethylformamide, toluol, isopropyl alcohol, And cyclohexane weight ratio. The component of the undercoat primer layer (6) is preferably selected from the group consisting of Dimethylformamide 20, Tolylol 15, Isopropyl Alcohol 20, Methyl Ethyl Chuckketone 25, Cyclohexane 20 weight ratio Wherein the coating of the top treatment layer (7) comprises a base: a hardener ratio of 2: 1, and a base component is a composition of silane trimethoxyvinyl series, hexamethylene glycol, isopropyl alcohol, dihydrogen oxide , And the curing agent comprises a polyurethane resin. The coating of the top treatment layer (7) includes a silane trimethoxyvinyl series 60, hexamethylene glycol 20, isopropyl alcohol 10, dihydrogen Oxide 10, and the curing agent is composed of polyurethane resin 40 and water 60 at a weight ratio

본 발명에 따른 제조방법적 특징은, 올레핀필름(1)과 투명올레핀필름(5)을 준비하고, 투명올레핀필름(5)저면에는 인쇄기를 이용하여 인쇄를 실시하여 인쇄층(4)을 형성하고, 올레핀필름(1)상면과 투명올레핀필름(5)저면을 접착제(3)를 이용하여 합지 및 드라이 작업을 행한 후, 인쇄기를 이용하여 올레핀필름(1) 저면에 PP프라이머층(2)을 처리한 후, 투명올레핀(5) 상면에 코타기에서 콤마 코팅으로 하도처리작업을 행하여 하도프라이머층(6)을 형성하고, 추가로 상도처리하여 상도처리층(7)을 형성하는 것을 특징으로 하며, 상기 하도프라이머층(6) 형성 작업 온도 조건은 섭씨 70-80도 이며, 상도처리층(7) 형성은, 섭씨 130-140도 온도와 코팅 속도 2-3m/분 인 것을 특징으로 한다.The manufacturing method according to the present invention is characterized in that an olefin film (1) and a transparent olefin film (5) are prepared, and printing is performed on the bottom surface of the transparent olefin film (5) , The upper surface of the olefin film 1 and the lower surface of the transparent olefin film 5 were laminated and dried using the adhesive 3 and then the PP primer layer 2 was treated on the bottom surface of the olefin film 1 using a printing machine , The upper surface of the transparent olefin (5) is subjected to a priming treatment with a comma coating to form a primer layer (6), and the upper treatment layer (7) is formed by further topping treatment. The working temperature condition for forming the under primer layer 6 is 70-80 degrees Celsius, and the top coat layer 7 is formed at a temperature of 130-140 degrees Celsius and a coating speed of 2-3 m / min.

본 발명에 의하면, 하도 및 상도의 표면 코팅제 코팅에 의해 내오염성이 우수하고, 먼지나 매연 등에 오염이 쉽게 되지 않고 빗물에 의한 얼룩 발생 현상이 없이 청결한 상태를 유지 가능한 장점이 있어 청소 비용을 크게 절감한다.According to the present invention, it is possible to maintain a clean state without stain caused by rainwater because the stain resistance is excellent by the coating of the surface coating agent on the lower and upper surfaces, do.

또한 천연나무의 질감이나 원하는 색상을 항상 유지 가능하여 내후성도 우수하다. 내후성은 평균 5-10년(Quv B타입에서 테스트 1200시간) 유지 가능하다.It is also excellent in weather resistance because it can always maintain the desired color and texture of natural wood. The weatherability can be maintained on average 5-10 years (1200 hours in Quv B type).

또한 본 발명에 의하면 제품의 수축이 없어 동조(엠보무늬와 인쇄무늬가 동일함) 엠보작업이 가능하고 투톤효과가 가능하며 사용 재료의 특성상 화재시 다이옥신이나 유해가스 발생이 없다.According to the present invention, since there is no shrinkage of the product, the embossing operation (the emboss pattern and the print pattern are the same) is possible and the two-tone effect is possible. Due to the nature of the material used, there is no dioxin or harmful gas generated in the fire.

본 발명에 의하면 건물의 알루미늄, 철판, 복합판넬 샌드위치 판넬 등 건물 내외장재의 내,외부 인테리어 시공에 사용 가능하다.According to the present invention, it can be used for interior and exterior interior construction of building interior and exterior materials such as aluminum, steel plate, and composite panel sandwich panel of a building.

특히 콘테이너 하우스나 컨테이너 차량 외면용으로 사용 가능하다. 그 외 기존의 표면재로 사용하는 전부분에 사용 가능하다. 예를 들어 가구, 창틀, 도어 문짝용도 사용 가능하다.Especially, it can be used for exterior of container houses and container cars. It can be used for all other parts used as conventional surface material. For example, it can be used for furniture, window frames, door doors.

또한 본 발명에 따른 시트재료 성분에는 염소기가 없어 주거용 아파트 내부 거실, 가구재, 사무실 병원, 식당 학교 교실 등에서 친환경적으로 사용 가능하다.Further, the sheet material component according to the present invention has no chlorine group and can be eco-friendly in a living room, a furniture, an office, a school room, and the like of a residential apartment.

도 1 은 본 발명의 시트 구성을 설명하기 위한 도면
도 2 는 본 발명의 제조 방법을 설명하기 위한 도면.BRIEF DESCRIPTION OF DRAWINGS FIG. 1 is a view for explaining a sheet configuration of the present invention;
2 is a view for explaining the production method of the present invention.

이하, 본 발명을 첨부 도면과 함께 추가로 상술한다.Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.

도 1 은 본 발명을 설명하기 위한 예시 단면 설명도이다.1 is an explanatory cross-sectional explanatory view for explaining the present invention.

예시한 바와 같이, 본 발명은, 올레핀필름(1) 저면에 PP프라이머층(2)을 처리하고, 상층에는 접착제(3)를 도포하고, 인쇄층(4), 투명올레핀필름(5) 상면에 하도프라이머 처리한 하도프라이머층(6), 상도처리한 상도처리층(7), 엠보를 형성한 엠보층(8)이 순차 형성된다. 올레핀필름(1)은 바람직하기로는 유백올레핀필름을 사용한다.As shown in the figure, the present invention is characterized in that the PP primer layer 2 is applied to the bottom of the olefin film 1, the adhesive 3 is applied to the upper layer, A primer layer 6 which has undergone a primer treatment, an upper treatment layer 7 which has been subjected to a top treatment, and an emboss layer 8 on which an emboss is formed are sequentially formed. The olefin film (1) preferably employs a milky white olefin film.

올레핀필름(1)저면에 PP프라이머층(2)을 형성시키는 이유는 접착성을 좋게 하기 위한 것이다. PP 성분은 철판이나 목재, 플라스틱재 등등 어느 곳에나 접착성이 양호하게 나타난다.The reason for forming the PP primer layer 2 on the bottom surface of the olefin film 1 is to improve adhesion. The PP component exhibits good adhesion to steel plate, wood, plastic, and so on.

상기 올레핀필름(1)상면에 도포하는 접착제(3)는 레트로치용 접착제를 사용한다. 그 이유는 고온에서도 사용하여도 접착불량이 없이 가능하기 때문이다. 본 발명에서 접착 사용시 사용 온도는 섭씨 160-170도이다. 그러나 일반 접착제를 사용하면 내열성이 낮아, 즉, 섭씨 100-110도 정도에서만 사용되므로 접착 불량이 발생한다. 투명올레핀필름(5)저면에 인쇄층(4)은 인쇄 형상을 더욱 돋보이게 하고 인쇄면을 보호하고 입체감을 주는 등의 여러 역할을 한다. 상기 층으로 이루어지는 시트는 두께가 예를 들어, 약 0.15-0.2mm 로 이루어진다.The adhesive (3) to be applied on the upper surface of the olefin film (1) uses an adhesive for retrograde bonding. The reason is that even if used at a high temperature, it is possible to carry out the bonding without defective. In the present invention, the temperature at which the adhesive is used is 160-170 degrees centigrade. However, when a general adhesive is used, the heat resistance is low. That is, since it is used only at about 100-110 degrees Celsius, adhesion failure occurs. The printed layer 4 on the bottom surface of the transparent olefin film 5 plays various roles such as enhancing the printing form, protecting the printed surface, and giving a three-dimensional effect. The layered sheet has a thickness of, for example, about 0.15-0.2 mm.

인쇄층의 잉크는 내후성이 좋은 잉크를 사용하는 것이 바람직하다. 즉. 그 성분은 내후성이 우수한 우레탄 아크릴계 수지에 산화 방지제와 UV 첨가제를 첨가한 잉크를 사용하고 사용안료도 8등급을 사용한다.The ink of the print layer preferably uses ink having good weather resistance. In other words. The ingredients used are urethane acrylic resins with excellent weatherability, inks containing antioxidants and UV additives, and grade 8 grades of used pigments.

상기 본 발명에 따른 시트의 제조 방법의 순서는 아래와 같다.The procedure of the method for producing a sheet according to the present invention is as follows.

먼저 도 2 에서 보듯이, 올레핀필름(1)과 투명올레핀필름(5)을 준비하고, 투명올레핀필름(5)저면에는 인쇄기를 이용하여 원하는 무늬 등으로 인쇄를 실시하여 인쇄층(4)을 형성한다. 그리고 올레핀필름(1)상면과 투명올레핀필름(5)저면을 접착제(3)를 이용하여 합지 및 드라이 작업을 행한 후, 인쇄기를 이용하여 올레핀필름(1) 저면에 PP프라이머층(2)을 처리하되, 인쇄기를 이용하여 처리한다.2, an olefin film 1 and a transparent olefin film 5 are prepared and printed on a bottom surface of the transparent olefin film 5 with a desired pattern using a printing machine to form a print layer 4 do. The upper surface of the olefin film 1 and the lower surface of the transparent olefin film 5 were subjected to a laminating and drying operation using an adhesive 3 and then the PP primer layer 2 was treated on the bottom surface of the olefin film 1 using a printing machine However, it is processed using a printing machine.

인쇄기를 이용한 저면 프라이머가 완성된 시트는 투명올레핀(5) 상면에 코타기에서 하도처리작업을 행하여 하도프라이머층(6)을 형성하고 그에 추가로 상도처리하여 상도처리층(7)을 형성하고, 최종 요철면을 만드는 엠보작업을 행하여 엠보층(8)을 부여하여 제품을 출고한다. 제품출고시, 엠보층(8) 형성은 생략할 수도 있다.In the sheet in which the bottom primer using the printing machine is completed, a primer layer 6 is formed on the upper surface of the transparent olefin 5 in the cortex, and further, the top coat layer 7 is formed by top- An embossing operation for forming a final uneven surface is performed, and the emboss layer 8 is provided to leave the product. Formation of the embossed layer 8 may be omitted at the time of product release.

상도처리층(7) 및 하도프라이머층(6) 코팅 처리작업은 여러 방법으로도 행할 수 있다.The coating treatment of the upper treatment layer 7 and the lower primer layer 6 can also be carried out by various methods.

예를 들어, 콤마코팅, 그라비아 방법, 나이프코팅, 스프레이코팅, 다이랙트롤코팅 방법 등 많은 방법을 실시하여 본 결과 콤마코팅이 제품 품질상 가장 우수하고 양산 가능한 결과로 나타났다.For example, many methods such as comma coating, gravure coating, knife coating, spray coating, and die rack coating have been performed. As a result, the comma coating has been found to be the best product quality and mass production.

즉, 콤마 코팅으로 하는 이유는 도포량을 크게 하기 위한 것과 균일한 도포를 위한 것이다. 콤마코팅은 30-40 마이크론 이상의 두께까지 도포 가능한 장점과 도포량이 일정하게 이루어질 수 있는 장점이 있다. 다른 코팅방법으로는 원하는 물성과 두께로 제조가 어렵다.That is, the reason for the comma coating is to increase the coating amount and to apply uniform coating. The comma coating has the advantage that it can be applied up to a thickness of 30-40 microns or more and the coating amount can be made constant. Other coating methods are difficult to manufacture with desired properties and thicknesses.

예를들어, 메쉬롤을 사용하는 일반 그라비아코팅 방법은 도포량이 적어 원하는 물성을 얻을 수 없다. 그리고 다이렉트롤 코팅방법은 고무롤과 처리제의 점도에 의해 롤자국이 발생되어 원하는 제품의 품질 수준을 가져올 수 없다.For example, a general gravure coating method using a mesh roll can not obtain desired physical properties because of a small amount of coating. And the direct roll coating method can not produce the quality level of the desired product due to the roll marks due to the viscosity of the rubber roll and the treating agent.

스프레이코팅방법은 점도가 묽은 것으로 여러 차례 처리하면 어느 정도 요구하는 물성을 얻을 수 있으나 로스(손실)가 심하고 작업이 힘들고 번거롭고 시간이 오래 걸리고 주위환경이 지저분하여 바람직하지 못하다. 마이크로코팅방법은, 제품 코팅시 제품의 표면이 매우 양호하나 도포량이 적고 표면 엠보 형성이 없는 정교한 제품에만 적합하다는 제한성을 갖는다.The spray coating method can obtain desired physical properties by treating it several times with a diluted viscosity, but the loss (loss) is severe, the work is troublesome, cumbersome, takes a long time, and the surrounding environment is dirty. The microcoating method has the limitation that the surface of the product is very good at the time of coating the product but is suitable only for a sophisticated product having a small amount of application and no surface emboss formation.

상기한 하도프라이머층(6) 형성시키는 이유는 표면장력을 높여주어 후속작업인 상도처리시 부착력을 좋게 하기 위한 것이다. 이 하도프라이머층(6)을 형성시키지 않으면 부착력에 문제가 있어 제품이 이루어질 수 없다. 하도프라이머층(6) 형성 작업 온도 조건은 섭씨 70-80도 일때 그리고 라인에서의 주행속도20m/분 일 경우에 가장 우수한 결과로 나타낸다.The reason why the undercoat primer layer 6 is formed is to increase the surface tension and to improve the adhesion force in the subsequent operation, that is, the top coat treatment. If the undercoat primer layer 6 is not formed, there is a problem in adhesion and the product can not be formed. The work temperature conditions for forming the undercoat primer layer (6) are the best when the temperature is 70-80 degrees Celsius and the running speed is 20m / min on the line.

상기 온도 조건 이상이면 하도프라이머층(6)에 물과 같이 흐름이 생기거나 주름층이 형성되며 상기 온도 이하 조건에서는 접착력이 떨어진다. 주행속도는 상기 속도 이상이면 균일한 표면처리층 형성이 어렵고 상기 속도 이하면 생산력이 떨어진다.If the temperature is higher than the above-mentioned temperature condition, the lower primer layer 6 may flow like water or a crease layer may be formed. If the running speed is higher than the above-mentioned speed, it is difficult to form a uniform surface treatment layer, and if the speed is lower than this speed, the productivity is lowered.

상도처리층(7) 형성은, 섭씨 130-140도 온도와 속도 2-3m/분 으로 하도프라이머층(6) 형성시키는 처리속도 보다는 늦으며 온도도 다소 높은 편이다. 이 온도와 속도 조건은 매우 중요하다. 속도가 빠르면 상도처리층(7) 형성이 잘 이루어지지 못하고 불량 발생이 많다.The upper treatment layer 7 is formed at a temperature of 130-140 degrees Celsius and at a speed of 2-3 m / min, which is later than the treatment rate for forming the lower primer layer 6, and the temperature is somewhat higher. This temperature and speed condition is very important. If the speed is high, the top coat layer 7 is not formed well and many defects occur.

상기 온도 조건 이상이면 상도처리층(7)에 변형이 온다. 통상적으로 PVC 재질은 섭씨 130도 이상이면 수축에 의해 작업이 불가능하다. 그러나 본 발명에서는 올레핀 재질의 필름 원단을 사용하므로, 130-140도 범위의 온도에서도 변형이 없다. 상기 온도 이하면 표면의 균일성과 접합성이 좋치 못하다. 또한 상기 속도 이상이면 상도처리층(7) 형성에 손상이 오거나 균일하지 못하며, 상기 속도 이하면 생산성이 떨어진다. 그리고 상기 조건들을 충족하지 못하며 건조 후 요구되는 물성을 얻을 수 없었다.If the temperature condition is exceeded, deformation occurs in the top treatment layer 7. Normally PVC material is impossible to work by contraction if it is over 130 degrees Celsius. However, in the present invention, since the film material of olefin is used, there is no deformation even in the temperature range of 130-140 degrees. If the temperature is lower than the above range, the uniformity of the surface and the bonding property are not good. If the speed is higher than the above-mentioned speed, the formation of the upper treatment layer 7 may be damaged or uneven. If the speed is lower than this speed, the productivity is lowered. And the above conditions were not satisfied and the required physical properties after drying could not be obtained.

하도프라이머층(6)의 재료는 1액형을 사용하며, 도막두께는 3-5마이크론으로 함이 바람직하며 상도처리층(7)은 2액형을 사용하며, 도막두께는 5-10마이크론 두께가 되도록 함이 바람직하다. 최소한 상기 두께 범위 이하면 원하는 물성을 나타내지 못한다.The primer layer 6 is made of a one-component type, and the thickness of the primer layer 6 is preferably 3-5 microns. The top coat layer 7 is a two-component primer, and the thickness of the primer layer 6 is 5-10 microns. . And if it is at least the above-mentioned thickness range, it can not exhibit desired properties.

하도프라이머층(6)의 하도코팅은 속히 건조되는 형태이며, 함량 성분은 디메틸포름아미드 20, 톨루올 15, 이소프로필알콜 20, 메칠에칠케톤 25, 사이크론헥산 20 중량 비율로 이루어진다. 상기 성분들의 범위를 준다면 아래 위로 약 20% 범위로 변경하여 혼합 비율의 조절이 가능하다. 예를들어 디메틸포름아미드 20 라면, 16-24 정도의 범위를 줄 수 있다. 이러한 범위라면 물성상 큰 변화는 없다.The undercoat of the undercoat primer layer 6 is rapidly dried, and the content component is composed of dimethylformamide 20, toluol 15, isopropyl alcohol 20, methyl ethyl ketone 25, and cicron hexane 20 weight ratio. If the range of the above components is given, the mixing ratio can be adjusted by changing the range from about 20% to about 20%. For example, in the case of dimethylformamide 20, a range of about 16-24 can be given. In this range, there is no significant change in physical properties.

상도처리층(7)의 코팅 성분은 인체에 무해한 성분으로 이루어지는 바, 주제:경화제 비율이 2:1 이며, 가사시간(포트라이프(POT LIFE)라고 하며, 2액형 제품을 사용시 주제와 경화제를 혼합하여 사용 가능한시간, 즉 혼합 후에는 점차 굳어지므로 작업 할 수 있는 시간을 말함)이 1시간 30분 정도로 짧다.The coating composition of the top coat treatment layer 7 is composed of a harmless component to the human body. The main subject is a hardener ratio of 2: 1, and the pot life (POT LIFE) Which means the time available for use, that is, the time that can be worked since the mixture is hardened gradually) is as short as 1 hour and 30 minutes.

주제와 경화제의 비율이 상기 보다 현저히 달라지면 처리제의 도막이 깨어지고 제품 표면에 경화가 되지 않아 부착에 문제가 발생하며 제품을 감을 경우, 처리제가 이면에 전이되며 원하는 물성을 가져올 수 없다.If the ratio of the base material and the hardener is significantly different from the above, the coating film of the treatment agent is broken and the surface of the product is not hardened, thereby causing adhesion problems. When the product is wound, the treatment agent is transferred to the back surface,

주제 성분은 실란 트리메톡시 비닐계 60, 헥사메틸렌 글리콜 20, 이소프로필 알코올 10, 디 수소산화물 10의 중량비 구성으로 이루어진다. 경화제는 성분이 폴리우레탄레진 40과 물 60 중량비로 이루어진다. 상기 비율이 최적이다. 그러나 상기 범위 역시 각 성분의 포함 함량이 아래 위로 약 20% 정도 범위를 주어도 물성상 큰 차이는 없다.The main component is composed of silane trimethoxyvinyl series 60, hexamethylene glycol 20, isopropyl alcohol 10, and dihydrogen oxide 10 in a weight ratio. The hardener is composed of polyurethane resin 40 and water 60 parts by weight. The above ratio is optimal. However, even if the content of each component is in the range of about 20%, there is not much difference in the physical properties.

상기한 상도처리층(7)의 주제와 경화제의 비율과 각 성분의 구성 범위에서 상하 20% 이상의 범위로 크게 벗어나면, 처리제의 도막이 깨어지고 제품 표면에 경화가 되지 않아 부착에 문제가 발생하며 제품을 감을 경우, 처리제가 이면에 전이되며 원하는 물성을 가져올 수 없다.If the ratio of the main component of the top treatment layer 7 to the curing agent and the composition range of each component are largely deviated to the upper and lower limits of 20% or more, the coating film of the treating agent is broken and the surface of the product is not hardened, , The treating agent is transferred to the back surface and can not bring desired physical properties.

상기한 하도프라이머층(6)과 상도처리층(7)을 구성하는 성분은 시트를 접거나 말았을 때 깨짐을 방지하지 위해 모두 연질 계통의 수지를 사용하였으며 아울러 내구성이 보강되도록 한 성분들의 조합이다. 그리고 상도처리층(7)을 형성하는 실리카 계열의 성분은 오염에 대한 저항성이 매우 큰 특성을 가지고 있어 본 발명의 목적을 달성할 수 있는 것이다.The components constituting the undercoat primer layer 6 and the top coat layer 7 are a combination of components which are made of soft resin and are reinforced with durability to prevent cracking when the sheet is folded or rolled . And the silica-based components forming the top treatment layer 7 have a very high resistance to contamination, so that the object of the present invention can be achieved.

본 발명의 시트 제품은 2년에 가까운 장기간에 걸쳐 7차례의 실험을 통하여 원하는 물성을 얻었으며, 4차례 이상의 실제 생산 라인 작업을 통하여 요구 물성을 얻을 수 있었다. 7차례의 완제품의 물성테스트는 미래화학에 의뢰하여 행하였다. 그 테스트 결과는 참고로 아래와 같이 첨부한다.The sheet product of the present invention obtained desired physical properties through seven experiments over a long period of nearly two years, and required physical properties were obtained through four or more actual production line operations. The test of the physical properties of the finished products was carried out on the basis of the future chemistry. The test results are attached as follows for reference.

Figure pat00001
Figure pat00001

Figure pat00002
Figure pat00002

Figure pat00003
Figure pat00003

Figure pat00004
Figure pat00004

Figure pat00005
Figure pat00005

Figure pat00006
Figure pat00006

Figure pat00007
Figure pat00007

1. 올레핀필름 2. pp프라이머층
3. 접착제 4. 인쇄층
5. 투명올레핀필름 6. 하도프라이머층
7. 상도처리층 8. 엠보층1. olefin film 2. pp primer layer
3. Adhesive 4. Printing layer
5. Transparent olefin film 6. Primer layer
7. Top treatment layer 8. Emboss layer

Claims (9)

올레핀필름(1)과,
상기 올레핀필름(1) 저면에 형성시키는 PP프라이머층(2)과,
상기 올레핀필름(1) 상면에 형성시키는 접착제(3)와,
접착제(3) 상에 형성시키는 인쇄층(4)과,
인쇄층(4) 상에 형성시키는 투명올레핀필름(5)과,
투명올레핀필름(5)상면에 하도 처리한 하도프라이머층(6)과,
하도프라이머층(6)에 상도 처리한 상도처리층(7)을 포함하는 것을 특징으로 하는 셀프 클리닝 기능의 올레핀시트The olefin film (1)
A PP primer layer 2 formed on the bottom surface of the olefin film 1,
An adhesive 3 formed on the upper surface of the olefin film 1,
A printed layer 4 formed on the adhesive 3,
A transparent olefin film 5 formed on the printing layer 4,
A primer layer (6) primed on the upper surface of the transparent olefin film (5)
Characterized in that it comprises an upper treatment layer (7) top-treated to a lower primer layer (6) 제 1 항에 있어서,
상기 접착제는 레트로치용 접착제인 것을 특징으로 하는 셀프 클리닝 기능의 올레핀시트.The method according to claim 1,
The olefin sheet of self-cleaning function, wherein the adhesive is a retrograde adhesive. 제 1 항에 있어서,
상기 하도프라이머층(6)의 재료는 1액형을 사용하며, 도막두께는 3-5마이크론이며,
상도처리층(7)은 2액형을 사용하며, 도막두께는 5-10마이크론 두께인 것을 특징으로 하는 셀프 클리닝 기능의 올레핀시트.The method according to claim 1,
The lower primer layer 6 is made of one-component type, the film thickness is 3-5 microns,
Characterized in that the top coat treatment layer (7) is of a two-part type and has a film thickness of 5-10 microns. 제 1 항에 있어서,
상기 하도프라이머층(6)의 하도코팅이 성분은 디메틸포름아미드, 톨루올, 이소프로필알콜, 메칠에칠케톤, 사이크론 헥산 중량 비율로 이루어지는 것을 특징으로 하는 셀프 클리닝 기능의 올레핀시트The method according to claim 1,
Characterized in that the undercoat layer of the undercoat primer layer (6) comprises a self-cleaning functional olefinic sheet (1), characterized in that the component is composed of dimethylformamide, toluol, isopropyl alcohol, methyl ethyl ketone, 제 3 항에 있어서,
상기 하도프라이머층(6)의 성분은 디메틸포름아미드 20, 톨루올 15, 이소프로필알콜 20, 메칠에칠케톤 25, 사이크론 헥산 20 중량 비율로 이루어지는 것을 특징으로 하는 셀프 크리닝 기능의 올레핀시트The method of claim 3,
Characterized in that the components of the undercoat primer layer (6) are composed of dimethylformamide (20), toluol (15), isopropyl alcohol (20), methyl ethyl ketone (25) and cicron hexane (20) 제 1 항에 있어서,
상기 상도처리층(7)의 코팅은 주제:경화제 비율이 2:1 이며,
주제 성분은 실란 트리메톡시 비닐계, 헥사메틸렌 글리콜, 이소프로필 알코올, 디 수소산화물의 구성으로 이루어지며, 경화제는 폴리우레탄레진을 포함하는 것을 특징으로 하는 셀프 크리닝 기능의 올레핀시트The method according to claim 1,
The coating of the top treatment layer (7) has a main: hardener ratio of 2: 1,
Characterized in that the main component is composed of silane trimethoxyvinyl type, hexamethylene glycol, isopropyl alcohol, dihydrogen oxide, and the curing agent comprises a polyurethane resin. The self-cleaning olefin sheet 제 6 항에 있어서,
상기 상기 상도처리층(7)의 코팅은 주제 성분은 실란 트리메톡시 비닐계 60, 헥사메틸렌 글리콜 20, 이소프로필 알코올 10, 디 수소산화물 10의 중량비 구성으로 이루어지며, 경화제는 폴리우레탄 레진 40과 물 60 중량비로 이루어지는 것을 특징으로 하는 셀프 크리닝 기능의 올레핀시트.The method according to claim 6,
The coating of the top treatment layer (7) is composed of a silane trimethoxyvinyl series 60, hexamethylene glycol 20, isopropyl alcohol 10, and dihydrogen oxide 10 in a weight ratio ratio, and the curing agent is a polyurethane resin 40 Water and 60 parts by weight of water. 올레핀필름(1)과 투명올레핀필름(5)을 준비하고,
투명올레핀필름(5)에는 인쇄기를 이용하여 인쇄를 실시하여 인쇄층(4)을 형성하고,
올레핀필름(1)과 투명올레핀필름(5)을 접착제(3)를 이용하여 합지 및 드라이 작업을 행한 후,
인쇄기를 이용하여 올레핀필름(1) 저면에 PP프라이머층(2)을 처리한 후,
후속작업으로 투명올레핀필름(5) 상면에 코타기에서 콤마 코팅으로 하도처리작업을 행하여 하도프라이머층(6)을 형성하고,
추가로 상도처리하여 상도처리층(7)을 형성하는 것을 특징으로 하는 셀프 크리닝 기능의 올레핀시트 제조방법.An olefin film (1) and a transparent olefin film (5) were prepared,
The transparent olefin film 5 is printed using a printing machine to form the printing layer 4,
After the olefin film (1) and the transparent olefin film (5) were laminated and dried using the adhesive (3)
After the PP primer layer 2 was treated on the bottom surface of the olefin film 1 by using a printing machine,
As a subsequent work, a primer layer 6 is formed by subjecting the transparent olefin film 5 to a priming treatment with a comma coating on the top surface thereof,
Wherein the top treatment layer (7) is formed by further topping the top coat layer (7). 제 8 항에 있어서,
상기 하도프라이머층(6) 형성 작업 온도 조건은 섭씨 70-80도 이며,
상도처리층(7) 형성은, 섭씨 130-140도 온도와 코팅 속도 2-3m/분 인 것을 특징으로 하는 셀프 클리닝 기능의 올레핀시트 제조방법.9. The method of claim 8,
The work temperature condition for forming the undercoat primer layer 6 is 70-80 degrees Celsius,
Wherein the top coat layer (7) is formed at a temperature of 130-140 DEG C and a coating speed of 2-3 m / min.
KR1020160164052A 2016-12-05 2016-12-05 self-cleaning olefin sheet KR101889615B1 (en)