KR20180057969A - 이차전지용 전해액 및 이를 포함하는 이차전지 - Google Patents
이차전지용 전해액 및 이를 포함하는 이차전지 Download PDFInfo
- Publication number
- KR20180057969A KR20180057969A KR1020160156512A KR20160156512A KR20180057969A KR 20180057969 A KR20180057969 A KR 20180057969A KR 1020160156512 A KR1020160156512 A KR 1020160156512A KR 20160156512 A KR20160156512 A KR 20160156512A KR 20180057969 A KR20180057969 A KR 20180057969A
- Authority
- KR
- South Korea
- Prior art keywords
- carbonate
- secondary battery
- lithium
- electrolyte
- formula
- Prior art date
Abstract
본 발명은 글리옥살 설페이트와 디플루오로 인산염을 포함하는 이차전지용 전해액 및 이를 포함하는 이차전지에 관한 것으로, 상기 이차전지는 고온 저장 시 출력 특성 및 용량 특성이 우수하고 개선된 고온 수명 특성을 나타낸다.
Description
본 발명은 글리옥살 설페이트와 디플루오로인산염을 포함하는 이차전지용 전해액 및 이를 포함하는 이차전지에 관한 것으로, 상기 이차전지는 고온 저장 시 출력 특성 및 용량 특성이 우수하고, 개선된 고온 수명 특성을 나타낸다.
모바일 기기에 대한 기술 개발과 수요가 증가함에 따라 에너지원으로서의 이차전지에 대해 수요가 급격히 증가하고 있다. 이차전지 중에서도 높은 에너지 밀도, 우수한 수명 특성 및 자기 방전율이 낮은 리튬이차전지가 상용화되어 널리 사용되고 있다.
최근에는 환경문제에 대한 관심이 커짐에 따라 대기오염의 주요 원인의 하나인 가솔린 차량, 디젤 차량 등 화석연료를 사용하는 차량을 대체할 수 있는 전기자동차, 하이브리드 전기자동차 등에 대한 연구가 많이 진행되고 있다. 이러한 전기자동차, 하이브리드 전기자동차 등의 동력원으로는 높은 에너지 밀도, 높은 방전 전압 및 출력 안정성의 리튬이차전지를 사용하는 연구가 활발히 진행되고 있으며, 일부 상용화되어 있다.
이러한 리튬 이차전지는 리튬 이온을 흡장 및 방출하는 탄소재 등의 음극, 리튬 함유 산화물 등으로 된 양극 및 혼합 유기용매에 리튬염이 적당량 용해된 비수계 전해액으로 구성되어 있다. 상기 비수계 전해액의 출력 안정성 향상을 위해 첨가하는 다수의 첨가제와 전해액 조성물 기술이 공지되어 있다. 또한, 양극과 음극에 양질의 피막(solid electrolyte interface)을 형성하여 이차전지의 용량 보존 특성을 개선하는 다수의 첨가제와 전해액 조성물 기술이 공지되어 있다.
예컨대, 일본 등록특허 제 3439085 호는 플루오로인산리튬 또는 디플루오로인산리튬을 포함하는 이차전지용 첨가제를 개시하고 있다. 상기 등록특허는 플루오로인산리튬 또는 디플루오로인산리튬 첨가제가 리튬과 반응하여 양극 및 음극의 계면에 양질의 피막을 형성하고 그 피막이 충전 상태의 활물질과 유기용매와의 직접접촉을 억제하여 비수계 전해액의 분해를 억제하는 효과를 개시하고 있다. 또한, 상기 등록특허는 상술한 효과로 인해 이차전지의 충전 후 일정 기간 동안 보존하였을 때 전지의 자기방전을 억제하여 보존 특성이 향상됨을 개시하고 있다.
그러나, 플루오로인산리튬 또는 디플루오로인산리튬은 이차전지의 저장특성 및 수명특성을 어느 정도 개선할 수 있으나, 고온에서 전지의 장기 저장 또는 수명 특성은 부족함이 있었다. 또한, 상기 등록특허는 플루오로인산리튬 또는 디플루오로인산리튬을 포함하는 이차전지의 고출력 특성이 개선됨을 개시하고 있지 않다.
따라서, 이차전지의 고온 특성을 현저히 개선하면서 동시에 고출력 특성을 만족시킬 수 있는 전해액의 연구개발이 필요하게 되었다.
이에, 본 발명의 목적은 이차전지의 음극에 보다 치밀한 피막을 형성시키는 첨가제를 포함하여 이차전지의 고온 저장시 출력 특성 및 용량 특성이 우수하고, 동시에 고온 수명 특성을 개선할 수 있는 이차전지용 전해액 및 이를 포함하는 이차전지를 제공하는 것이다.
상기 목적을 달성하기 위해 본 발명은
카보네이트계 용매;
리튬염;
하기 화학식 1의 화합물; 및
디플루오로인산리튬(LiPO2F2)을 포함하는, 이차전지용 전해액을 제공한다:
또한, 본 발명은 상기 이차전지용 전해액을 포함하는 이차전지를 제공한다.
본 발명의 이차전지용 전해액은 이차전지의 양극 및 음극에 안정적인 피막을 형성시켜 이차전지의 고온 저장시 출력 특성 및 용량 특성을 향상시키고, 동시에 전지의 고온 수명 특성을 개선하는 효과가 있다.
이하, 본 발명을 상세히 설명한다.
본 발명의 이차전지용 전해액은 카보네이트계 용매; 리튬염; 하기 화학식 1의 화합물; 및 디플루오로인산리튬(LiPO2F2)을 포함한다:
[화학식 1]
상기 화학식 1의 화합물은 공지의 화합물(CAS No. 496-45-7)로서, 바이사이클로-글리옥살 설페이트(bicyclo-glyoxal sulfate), 글리옥살 설페이트(glyoxal sulfate), 또는 3a,6a-디하이드로-[1,3,2]디옥사티올로[4,5-d][1,3,2]디옥사티올 2,2,5,5-테트라옥사이드(3a,6a-dihydro-[1,3,2]dioxathiolo[4,5-d][1,3,2]dioxathiole 2,2,5,5-tetraoxide) 등의 명칭으로 불리며, 시중에서 구매할 수 있다. 또한 상기 화학식 1의 화합물은 예를 들어, 1,1,2,2-테트라클로로에탄을 출발물질로 하여 발연 황산 등과 반응시키는 공지의 합성법으로 제조될 수 있다(미국 등록특허 제1,999,995호 및 미국 등록특허 제2,415,397호 참조).
또한, 디플루오로인산리튬(CAS No. 845910-47-6)은 공지의 화합물로서 시중에서 구매하거나 공지의 합성법으로 제조될 수 있다.
상기 전해액은 총 중량 대비 0.1 내지 10 중량%의 상기 화학식 1의 화합물 및 0.05 내지 10 중량%의 디플루오로인산리튬을 포함할 수 있다. 구체적으로, 상기 전해액은 총 중량 대비 0.1 내지 8 중량%, 0.2 내지 5 중량%, 또는 0.5 내지 3 중량%의 상기 화학식 1의 화합물; 및 0.05 내지 8 중량%, 0.1 내지 5 중량%, 또는 0.2 내지 2 중량%의 디플루오로인산리튬을 포함할 수 있다. 상기 함량 범위 내의 양으로 화학식 1의 화합물을 포함할 경우, 본 발명의 전해액을 포함하는 이차전지의 고온환경에서의 저항증가를 억제하는 효과 및 상온 초기 저항의 과도한 향상이 방지되는 효과가 있다. 또한, 상기 함량 범위 내의 양으로 디플루오로인산리튬을 포함할 경우, 상기 이차전지의 전극 표면이 적절한 두께로 코팅되며, 이차전지의 저항 증가를 방지할 수 있다.
상기 카보네이트계 용매는 상기 리튬염, 상기 화학식 1의 화합물 및 디플루오로인산리튬에 대한 용해도가 높은 것이 바람직하다. 구체적으로, 상기 카보네이트계 용매는 디에틸 카보네이트(diethyl carbonate; DEC), 에틸메틸 카보네이트(ethylmethyl carbonate; EMC), 디메틸 카보네이트(dimethyl carbonate; DMC), 디프로필 카보네이트(dipropyl carbonate; DPC), 메틸프로필 카보네이트(methylpropyl carbonate; MPC), 에틸프로필 카보네이트(ethylpropyl carbonate; EPC), 에틸렌 카보네이트(ethylene carbonate; EC), 프로필렌 카보네이트(propylene carbonate; PC), 부틸렌 카보네이트(butylene carbonate; BC), 프로필 프로피오네이트(propyl propionate; PP) 및 플루오로에틸렌 카보네이트(fluoroethylene carbonate; FEC)로 이루어진 군으로부터 선택된 1종 이상일 수 있다. 보다 구체적으로, 상기 전해액은 카보네이트계 용매로서 디에틸 카보네이트(DEC), 에틸메틸 카보네이트(EMC), 디메틸 카보네이트(DMC), 디프로필 카보네이트(DPC), 메틸프로필 카보네이트(MPC) 및 에틸프로필 카보네이트(EPC)로 이루어진 군으로부터 선택된 1종 이상의 제1 카보네이트계 용매(선형 카보네이트); 및 에틸렌 카보네이트(EC), 프로필렌 카보네이트(PC), 부틸렌 카보네이트(BC), 프로필 프로피오네이트(PP) 및 플루오로에틸렌 카보네이트(FEC)로 이루어진 군으로부터 선택된 1종 이상의 제2 카보네이트계 용매(선형 또는 환형 카보네이트)를 포함할 수 있다.
상기 카보네이트계 용매는 탈수된 것을 사용할 수 있으며, 구체적으로, 카보네이트계 용매는 30 중량ppm 이하의 수분을 포함할 수 있다.
상기 리튬염은 이차전지용 전해액에 통상 사용되는 것이라면 특별히 한정하지 않는다. 구체적으로, 상기 리튬염은 LiPF6, LiBF4, LiBF6, LiSbF6, LiAsF6, LiClO4, LiSO3CF3, LiN(CF3SO2)2, LiN(C2F5SO2)2, LiN(SO2F)2 및 LiC(CF3SO2)3로 이루어진 군으로부터 선택된 1종 이상일 수 있다.
상기 전해액은 상기 카보네이트계 용매 1 리터를 기준으로 0.05 내지 5.0 몰의 리튬염을 포함할 수 있다. 구체적으로, 상기 전해액은 상기 카보네이트계 용매 1 리터를 기준으로 0.1 내지 5.0 몰, 0.1 내지 3.0 몰, 0.1 내지 2.5 몰, 0.5 내지 3.0 몰 또는 0.5 내지 2.5 몰의 리튬염을 포함할 수 있다. 상기 범위 내의 함량으로 리튬염을 포함할 경우, 전해액의 이온 전도도가 적절하게 확보되며, 첨가한 리튬염의 농도대비 수득할 수 있는 전해액의 이온 전도도 향상 효과가 높아 경제적이다.
본 발명에 따른 이차전지용 전해액은 카보네이트계 용매, 리튬염, 상기 화학식 1로 표시되는 글리옥살 설페이트 및 디플루오로인산리튬을 단순히 혼합하고 교반함으로서 제조될 수 있다.
본 발명의 이차전지용 전해액은 이차전지의 제조에 사용될 경우, 넓은 온도 범위에서 이차전지의 계면 저항을 낮추고 저항의 증가를 억제함으로써 전지의 출력 특성, 용량 보존 특성, 및 수명 특성을 개선할 수 있다.
본 발명은 상기 이차전지용 전해액을 포함하는 이차전지를 제공한다. 구체적으로, 상기 이차전지는 양극 활물질을 포함하는 양극; 음극 활물질을 포함하는 음극; 상기 양극과 음극 사이에 배치되는 분리막; 및 상기 이차전지용 전해액을 포함할 수 있다.
상기 양극은 리튬 이온을 가역적으로 흡장 및 탈리할 수 있는 양극 활물질을 포함한다. 상기 양극 활물질은 코발트, 망간 및 니켈로 이루어진 군으로부터 선택된 1 종 이상의 금속; 및 리튬을 포함하는 복합 금속 산화물을 포함할 수 있다. 금속 사이의 고용율은 다양하게 이루어질 수 있으며, 상기 양극 활물질은 상술한 금속 외에 Mg, Al, K, Na, Ca, Si, Ti, Sn, V, Ge, Ga, B, As, Zr, Cr, Fe, Sr 및 희토류 원소로 이루어진 군에서 선택되는 1종 이상의 원소를 더 포함할 수 있다.
상기 음극은 리튬 이온을 흡장 및 탈리할 수 있는 음극 활물질을 포함한다. 상기 음극 활물질은 결정질 또는 비정질의 탄소, 또는 탄소 복합체의 탄소계 음극 활물질(열적으로 분해된 탄소, 코크, 흑연); 연소된 유기 중합체 화합물; 탄소 섬유; 산화 주석 화합물; 리튬 금속; 또는 리튬 합금을 포함할 수 있다. 예를 들어, 상기 비정질 탄소로는 하드 카본, 코크스, 1500 ℃ 이하에서 소성한 메조카본 마이크로비드(mesocarbon microbead; MCMB), 메조페이스 피치계 탄소 섬유(mesophase pitch-based carbon fiber; MPCF) 등을 들 수 있다. 상기 결정질 탄소는 흑연계 재료일 수 있으며, 예를 들어, 천연흑연, 인조흑연, 흑연화 코크스, 흑연화 MCMB, 흑연화 MPCF 등을 들 수 있다. 상기 리튬 합금 중 리튬과 합금을 이루는 다른 원소는 알루미늄, 아연, 비스무스, 카드뮴, 안티몬, 실리콘, 납, 주석, 갈륨 또는 인듐일 수 있다.
상기 분리막은 양극과 음극 사이의 직접적인 접촉으로 인한 단락을 방지하기 위한 것으로, 예를 들어, 폴리올레핀, 폴리프로필렌, 폴리에틸렌 등의 고분자막 또는 이들의 다중막; 미세다공성 필름; 직포; 및 부직포 등을 들 수 있다. 상기 분리막은 단면 혹은 양면에 금속 산화물 등이 코팅된 것일 수 있다.
이하, 구체적인 실시예 및 비교예를 통하여 본 발명을 더욱 상세히 설명한다. 하기 실시예는 본 발명을 보다 구체적으로 설명하기 위한 것으로서, 본 발명이 하기 실시예에 의해 한정되는 것은 아니다.
[
실시예
]
이하의 실시예 및 비교예에서 사용되는 화학식 1의 화합물 및 디플루오로인산리튬(LiPO2F2)(화학식 2)은 모두 공지의 화합물로서, 이들의 구조식, 화학명 및 CAS No.는 아래와 같다:
(1) 화학식 1의 화합물: 글리옥살 설페이트, glyoxal sulfate, CAS No. 496-45-7.
[화학식 1]
(2) 디플루오로인산리튬: Difluorophosphate Lithium, CAS No. 845910-47-6.
[화학식 2]
제조예
1.
글리옥살
설페이트의
제조
상기 화학식 1의 화합물은 다음과 같은 공지의 합성법에 따라 제조될 수 있다.
먼저, 60 ℃의 오일 배쓰에 1,000 mL의 3구 플라스크와 컨덴서를 장착하였다. 상기 3구 플라스크에 1,1,2,2-테트라클로로에탄 70 g을 넣고 온도를 60 ℃로 안정화시킨 후, 황산(60 % fuming grade) 320 g을 투입하여 반응을 개시하였다. 반응액은 초기에 투명 내지 연한 갈색의 점성을 나타내었으며, 반응 개시로부터 4 시간 경과 후에 결정성 고체가 생성되었다. 오일 배쓰를 상온으로 식히고 추가 3 시간 동안 저속 교반하였다. 이후 5~7 ℃의 냉수 배쓰로 교체하고 추가 2 시간 동안 저속 교반하였다. 결정성 고체의 추가 생성이 없을 때 반응을 종결시켰다. 수득한 슬러리 용액을 여과기로 고액 분리한 후, 20 Torr 하에서 12 시간 동안 진공 건조하였다. 그 결과 상기 화학식 1로 표시되는 글리옥살 설페이트 72.8 g을 수득하였다(수율: 84.4%).
실시예
1. 전해질 용액의 제조
에틸렌 카보네이트(EC), 에틸메틸 카보네이트(EMC) 및 디에틸 카보네이트(DEC)를 20 : 40 : 40의 부피비로 혼합하여 혼합액을 제조하고, 상기 혼합액에 LiPF6을 1 몰/ℓ의 농도로 용해하고, 전해액 총 중량에 대하여 1 중량%의 상기 화학식 1로 표시되는 글리옥살 설페이트 및 1 중량%의 디플루오로인산리튬을 첨가하고 혼합하여, 이차전지용 전해액(전해질 용액)을 제조하였다.
실시예
2.
상기 화학식 1로 표시되는 글리옥살 설페이트를 2 중량%의 함량 및 디플루오로인산리튬을 1 중량%의 함량으로 첨가한 것을 제외하고는, 실시예 1과 동일한 방법으로 전해액을 제조하였다.
비교예
1.
디플루오로인산리튬을 첨가하지 않는 것을 제외하고는, 실시예 1과 동일한 방법으로 전해액을 제조하였다.
비교예
2.
디플루오로인산리튬을 첨가하지 않는 것을 제외하고는, 실시예 2와 동일한 방법으로 전해액을 제조하였다.
비교예
3.
상기 화학식 1로 표시되는 글리옥살 설페이트를 첨가하지 않는 것을 제외하고는, 실시예 1과 동일한 방법으로 전해액을 제조하였다.
비교예
4.
상기 화학식 1로 표시되는 글리옥살 설페이트 및 디플루오로인산리튬을 첨가하지 않는 것을 제외하고는, 실시예 1과 동일한 방법으로 전해액을 제조하였다.
실험예
1. 리튬 이차전지의 고온 저장 시 출력 특성
양극 활물질인 LiNi1 /3Co1 /3Mn1 /3을 사용한 양극재와 음극 활물질인 인조흑연과 천연흑연을 1:1 중량비로 사용한 음극재를 사용하여 통상의 방법으로 1.4 Ah 파우치 전지를 조립하고, 상기 실시예 1 및 2, 및 비교예 1 내지 4의 전해액을 각각 6.5 g씩 주입하여 이차전지를 완성하였다. 상기 전지 화성 공정을 통해 얻은 1.4 Ah 파우치 전지를 25 ℃에서 만충전 대비 60 % 충전 상태 전압을 유지한 채 3 C(쿨롱)으로 10 초간 방전시키고, 이때 발생하는 전압차를 PNE-0506 충방전기(제조사: (주)PNE 솔루션)로 측정하고, 이로부터 초기 저항을 계산하였다.
또한, 상기 전지를 만충전 후, 60 ℃ 고온 오븐에서 6주 동안 저장하고 6주 경과 후의 저항을 상기와 동일한 방법으로 측정하여 표 1에 나타냈다.
| 전해액 중 첨가제의 함량 | DC-IR (mΩ) | ||
| 25 ℃ 초기 | 60 ℃ 6주 후 | ||
| 실시예 1 | 1 중량%의 화학식 1 + 1 중량%의 디플루오로인산리튬 | 35.7 | 41.7 |
| 실시예 2 | 2 중량%의 화학식 1 + 1 중량%의 디플루오로인산리튬 | 39.5 | 40.2 |
| 비교예 1 | 1 중량%의 화학식 1 | 36.1 | 48.6 |
| 비교예 2 | 2 중량%의 화학식 1 | 38.4 | 42.9 |
| 비교예 3 | 1 중량%의 디플루오로인산리튬 | 33.7 | 58.0 |
| 비교예 4 | 첨가제 없음 | 36.1 | 74.6 |
표 1에서 보는 바와 같이, 실시예 1 및 2의 전해액은, 첨가제를 첨가하지 않거나(비교예 4), 한 종류의 첨가제를 사용한 경우(비교예 1 내지 3)와 비교하여, 전지 내부 저항이 낮아졌다. 이는 화학식 1의 화합물 및 디플루오로인산리튬의 조합을 포함하는 전해액을 사용함으로써 전지의 방전 과정에서 전극과 전해질 계면의 낮은 저항 특성으로 인해 전지의 출력 특성이 향상됨을 보여주는 결과이다. 특히, 디플루오로인산리튬만 사용한 비교예 3보다 디플루오로인산리튬과 화학식 1의 화합물을 함께 사용한 실시예 1 및 2가 낮은 저항을 보여 전지의 출력 특성이 향상됨을 확인할 수 있었다.
실험예
2. 리튬 이차전지의 고온 저장 시 용량 특성
상기 실험예 1과 동일한 방법으로 전지 화성공정을 수행하여 이차전지(1.4 Ah 파우치 전지)를 얻은 후, 25 ℃에서 정전류/정전압(CC/CV) 조건에서 4.2 V/140 mA까지 1 C로 충전한 다음, 정전류(CC) 조건에서 3 V까지 1 C로 방전시키며 PNE-0506 충방전기로 초기 방전 용량을 측정하였다.
또한, 상기 전지를 만충전 후, 60 ℃ 고온 오븐에서 6주 동안 저장하고 6주 경과 후의 방전 용량을 상기와 동일한 방법으로 측정하고, 초기 용량 대비 용량 유지율을 계산하여 표 2에 나타냈다.
| 전해액 중 첨가제의 함량 | 60 ℃ 6주 후 용량 유지율 (%) |
|
| 실시예 1 | 1 중량%의 화학식 1 + 1 중량%의 디플루오로인산리튬 | 93 % |
| 실시예 2 | 2 중량%의 화학식 1 + 1 중량%의 디플루오로인산리튬 | 93 % |
| 비교예 1 | 1 중량%의 화학식 1 | 87 % |
| 비교예 2 | 2 중량%의 화학식 1 | 92 % |
| 비교예 3 | 1 중량%의 디플루오로인산리튬 | 78 % |
| 비교예 4 | 첨가제 없음 | 71 % |
표 2에서 보는 바와 같이, 실시예 1 및 2의 전해액은, 첨가제를 첨가하지 않거나(비교예 4), 한 종류의 첨가제를 사용한 경우(비교예 1 내지 3)와 비교하여, 전지 초기 충전량 대비한 고온(60℃) 저장 후의 방전량이 현저히 우수했다. 이는 화학식 1의 화합물 및 디플루오로인산리튬의 조합을 포함하는 전해액을 사용함으로써 전지의 고온 저장 중 발생하는 전기화학적 전극용량 감소가 현저히 줄어들었음을 보여주는 결과이다. 이로써 본 발명의 전해액을 포함하는 이차전지는 고온에서도 안정적인 충방전 용량을 구현함을 확인할 수 있었다.
실험예
3. 리튬 이차전지의 고온 수명 특성
상기 실험예 1과 동일한 방법으로 전지 화성공정을 수행하여 이차전지(1.4 Ah 파우치 전지)를 얻은 후, 45 ℃에서 정전류/정전압(CC/CV) 조건에서 4.2 V/140 mA까지 1 C로 충전한 다음, 정전류(CC) 조건에서 3 V까지 2 C로 방전시키며 PNE-0506 충방전기로 초기 방전 용량을 측정하였다. 이를 500 회 반복 실시하였고, 500 회 반복 후 측정한 방전 용량을 전지의 초기 용량 대비 용량 유지율로 계산하여 표 3에 나타내었다.
| 전해액 중 첨가제의 함량 | 45℃ 수명 500회 후 용량 유지율 (%) |
|
| 실시예 1 | 1 중량%의 화학식 1 + 1 중량%의 디플루오로인산리튬 | 97 % |
| 실시예 2 | 2 중량%의 화학식 1 + 1 중량%의 디플루오로인산리튬 | 96 % |
| 비교예 1 | 1 중량%의 화학식 1 | 86 % |
| 비교예 2 | 2 중량%의 화학식 1 | 90 % |
| 비교예 3 | 1 중량%의 디플루오로인산리튬 | 83 % |
| 비교예 4 | 첨가제 없음 | 6 % |
표 3에서 보는 바와 같이, 실시예 1 및 2의 전해액은, 첨가제를 첨가하지 않거나(비교예 4), 한 종류의 첨가제를 사용한 경우(비교예 1 내지 3)와 비교하여, 고온 수명 특성이 개선되었다. 이는 화학식 1의 화합물 및 디플루오로인산리튬의 조합을 포함하는 전해액을 사용함으로써 전지를 고온에서 연속 사용할 경우 발생하는 부반응이 현저히 감소하는 것을 보여주는 결과이다. 이로써 본 발명의 전해액을 포함하는 이차전지는 고온에서도 안정적인 수명 특성을 구현할 수 있었다.
Claims (7)
- 카보네이트계 용매;
리튬염;
하기 화학식 1의 화합물; 및
디플루오로인산리튬(LiPO2F2)을 포함하는, 이차전지용 전해액:
[화학식 1]
.
- 제1항에 있어서,
상기 카보네이트계 용매가 디에틸 카보네이트(diethyl carbonate), 에틸메틸 카보네이트(ethylmethyl carbonate), 디메틸 카보네이트(dimethyl carbonate), 디프로필 카보네이트(dipropyl carbonate), 메틸프로필 카보네이트(methylpropyl carbonate), 에틸프로필 카보네이트(ethylpropyl carbonate), 에틸렌 카보네이트(ethylene carbonate), 프로필렌 카보네이트(propylene carbonate), 부틸렌 카보네이트(butylene carbonate), 프로필 프로피오네이트(propyl propionate) 및 플루오로에틸렌 카보네이트(fluoroethylene carbonate)로 이루어진 군으로부터 선택된 1종 이상을 포함하는, 이차전지용 전해액.
- 제2항에 있어서,
상기 카보네이트계 용매가
디에틸 카보네이트, 에틸메틸 카보네이트, 디메틸 카보네이트, 디프로필 카보네이트, 메틸프로필 카보네이트 및 에틸프로필 카보네이트로 이루어진 군으로부터 선택된 1종 이상의 제1 카보네이트계 용매, 및
에틸렌 카보네이트, 프로필렌 카보네이트, 부틸렌 카보네이트, 프로필 프로피오네이트 및 플루오로에틸렌 카보네이트로 이루어진 군으로부터 선택된 1종 이상의 제2 카보네이트계 용매를 포함하는, 이차전지용 전해액.
- 제1항에 있어서,
상기 리튬염이 LiPF6, LiBF4, LiBF6, LiSbF6, LiAsF6, LiClO4, LiSO3CF3, LiN(CF3SO2)2, LiN(C2F5SO2)2, LiN(SO2F)2 및 LiC(CF3SO2)3로 이루어진 군으로부터 선택된 1종 이상을 포함하는, 이차전지용 전해액.
- 제1항에 있어서,
상기 전해액이 총 중량 대비 0.1 내지 10 중량%의 상기 화학식 1의 화합물 및 0.05 내지 10 중량%의 디플루오로인산리튬을 포함하는, 이차전지용 전해액.
- 제1항에 있어서,
상기 전해액이 상기 카보네이트계 용매 1 리터를 기준으로 0.05 내지 5.0 몰의 리튬염을 포함하는, 이차전지용 전해액.
- 제1항 내지 제6항 중 어느 한 항에 따른 이차전지용 전해액을 포함하는 이차전지.