KR20180019855A - Method for manufacturing concrete block - Google Patents

Method for manufacturing concrete block Download PDF

Info

Publication number
KR20180019855A
KR20180019855A KR1020160104067A KR20160104067A KR20180019855A KR 20180019855 A KR20180019855 A KR 20180019855A KR 1020160104067 A KR1020160104067 A KR 1020160104067A KR 20160104067 A KR20160104067 A KR 20160104067A KR 20180019855 A KR20180019855 A KR 20180019855A
Authority
KR
South Korea
Prior art keywords
mold
molding block
primary
block
natural stone
Prior art date
Application number
KR1020160104067A
Other languages
Korean (ko)
Other versions
KR101910945B1 (en
Inventor
김한울
Original Assignee
김한울
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김한울 filed Critical 김한울
Priority to KR1020160104067A priority Critical patent/KR101910945B1/en
Publication of KR20180019855A publication Critical patent/KR20180019855A/en
Application granted granted Critical
Publication of KR101910945B1 publication Critical patent/KR101910945B1/en

Abstract

The present invention relates to a method for manufacturing a concrete block having a natural stone color and, more specifically, relates to a method for manufacturing a concrete block, wherein after a primary molding block is cured with steam to realize a natural stone color on a surface a concrete retaining wall block surface, on the front decoration portion of the primary molding block, a natural stone color portion of a secondary molding block that has been cured by a dry type curing method by heat rays embedded in a secondary mold is formed. Moreover, the natural stone color portion of the secondary molding block is not discolored or bleached, and a natural stone color can be displayed to be appropriate for a surrounding environment. Therefore, various senses of beauty can be provided, and various natural stone colors fitted to a local environment are provided to realize appearance of a retaining wall with various design.

Description

자연석 색상을 갖는 콘크리트 블록의 제조방법{METHOD FOR MANUFACTURING CONCRETE BLOCK}TECHNICAL FIELD [0001] The present invention relates to a method of manufacturing a concrete block having a natural stone color,

본 발명은 자연석 색상을 갖는 콘크리트 블록의 제조방법에 관한 것으로서, 보다 상세하게는 콘크리트 옹벽블록 표면에 자연석 색상을 구현할 수 있도록 1차 성형블록을 증기로 양생시킨 다음 위 1차 성형블록 전면 장식부에는 2차 금형몰드 내부에 내장된 열선에 의한 건식 양생 방식으로 양생 완료되는 2차 성형블록의 자연석 색상부를 형성시키되, 위 2차 성형블록의 자연석 색상부는 변색이나 탈색이 발생하지 않고, 주변환경에 적합하도록 자연석의 색상을 표출할 수 있게 함으로써 다양한 미감을 표현할 수 있고 옹벽의 외관을 다양한 디자인으로 구현할 수 있는 현지환경 조성에 맞는 다양한 자연석 색상에 가까운 콘크리트 블록의 제조방법에 관한 것이다.The present invention relates to a method of manufacturing a concrete block having a natural stone color. More specifically, the present invention relates to a method of manufacturing a concrete block having a natural stone color, The natural stone color part of the secondary molding block cured by the dry curing method by the hot wire built in the secondary mold mold is formed, and the natural stone color part of the above secondary molding block does not cause discoloration or discoloration, and is suitable for the surrounding environment The present invention relates to a method of manufacturing a concrete block close to a variety of natural stone colors suitable for forming a local environment capable of expressing a variety of aesthetic feelings and expressing the appearance of the retaining wall with various designs.

일반적으로, 도로건설, 주택단지 조성, 사면보호, 수로 및 제방공사 등의 각종 토목공사의 시행과정에는 성토지 또는 절개지에 토사의 유실로 인한 붕괴를 방지하기 위하여 콘크리트 옹벽블록을 시공하게 된다.In general, concrete construction retaining wall blocks are installed in order to prevent collapse due to the loss of soil on castle land or cutout site in the construction process of road construction, housing complex, slope protection, waterway and embankment construction.

콘크리트 옹벽블록은 다양한 시공방법에 의해 시행되고 있으나, 성토지에서는 블록의 후면에 연결된 지오그리드와 같은 보강재가 뒤채움 토사에 의해 받는 하중으로 블록의 횡방향 변위를 억제하도록 시공하는 옹벽 시공방법을 널리 적용하고 있고, 절개지에서는 콘크리트 옹벽블록과 앵커볼트를 이용한 옹벽 시공방법을 널리 적용하고 있다.Concrete retaining wall blocks are implemented by various construction methods. However, in the case of castle land, a retaining wall construction method is widely applied in which a reinforcing material such as geogrid connected to the back of a block is subjected to the load received by the backfill soil to suppress the lateral displacement of the block And the retaining wall construction method using the concrete retaining wall block and the anchor bolt is widely applied in the cutout.

그리고, 전술한 바와 같은 옹벽의 시공시에는 옹벽블록을 이용하게 되는데, 이러한 옹벽블록은 골재와 물, 시멘트를 적절한 혼합비로 혼합한 몰탈을 이용하여 성형, 양생하는 방식으로 제조하게 되므로 축조된 옹벽블록은 콘크리트 질감이 그대로 노출됨에 따라 외관이 불량하고 미감이 저하되는 단점을 갖고 있다.When the retaining wall is constructed as described above, a retaining wall block is used. Since the retaining wall block is manufactured by molding and curing using aggregates, water and cement mixed with an appropriate mixing ratio, Has a disadvantage in that the appearance of the concrete is exposed and the beauty of the concrete is deteriorated.

이에 따라, 최근에는 콘크리트 옹벽블록의 제조과정에서 안료를 혼합하여 특성 색상을 갖도록 제작된 칼라 옹벽블록이 옹벽의 시공에 이용되고 있다.Accordingly, in recent years, a color retaining wall block, which is manufactured to have a characteristic color by mixing pigments in the process of manufacturing a concrete retaining wall block, is used for construction of a retaining wall.

이러한 칼라 옹벽블록으로는, 대한민국 공개특허공보 공개번호 제10-2009-0083661호에 나타난 바와 같이 블록 본체의 전면에 암반돌출부를 구비하되, 이 암반돌출부의 표면에는 자연석과 유사한 색상을 갖는 페인트를 도포한 도포층이 더 형성된 "옹벽축조용 블록"이 개시되어 있다.As such a collar retaining wall block, as shown in Korean Patent Laid-Open Publication No. 10-2009-0083661, a block body is provided with a rock protrusion on the front surface of the block body, and a paint having a color similar to a natural stone is applied to the surface of the rock protrusion Quot; block for building a retaining wall "in which one coating layer is further formed.

그리고, 대한민국 공개특허공보 공개번호 제10-2007-0008286호에 나타난 바와 같은 옹벽 블록은 후면 지지대, 적어도 하나의 중공, 대칭으로 형성된 한 쌍의And, the retaining wall block as shown in Korean Patent Laid-Open Publication No. 10-2007-0008286 includes a back support, at least one hollow, a pair of symmetrically formed

핀 홀 및 전면을 포함하되, 전면에 콘크리트 및 색채 성분의 혼합물이 도포되어 있는 "색채 전면을 가진 옹벽블록"이 개시되어 있다.Discloses a "retaining wall block having a color front surface ", including a pin hole and a front surface, on which a mixture of concrete and color components is applied.

하지만, 전술한 종래의 칼라 옹벽블록은 블록 본체의 전면에 도료나 안료가 도포된 것으로서 열화로 인해 색상이 변색될 뿐만 아니라 다양한 기상조건에 노출되므로 일정 기간이 경과 되면 자연히 탈색되므로 미관이 불량해지는 한계점을 갖고 있다. 또한, 도료나 안료는 납과 같은 중금속을 함유하고 있으므로 토양오염을 유발시키는 단점이 있다.However, since the conventional color retaining wall block described above is coated with paints or pigments on the whole surface of the block body, it is not only discolored due to deterioration but also exposed to various weather conditions. Therefore, when a certain period of time elapses, Lt; / RTI > In addition, paints and pigments have the disadvantage of causing soil contamination because they contain heavy metals such as lead.

그 외에도 대한민국 등록특허공보 등록번호 제10-0531180호에 나타난 바와 같이 전면에 자연석을 돌출, 형성하고, 양측에 사다리꼴 형상의 요부를 갖는 사각형상의 판 블록을 형성하고, 이 판 블록 두개가 서로 마주보도록 결합용 앵글로 연결하여 옹벽블록을 구성하는 "표면에 자연석이 매입된 판 블록을 이용한 조립식 옹벽블록 및 그 제조방법"이 개시되어 있다.In addition, as shown in Korean Patent Registration No. 10-0531180, a natural stone is protruded and formed on the front surface, a rectangular plate block having trapezoidal concave portions is formed on both sides thereof, and two plate blocks are opposed to each other A constructional retaining wall block using a plate block embedded with a natural stone on its surface and a method for manufacturing the retaining wall block by connecting with a joining angle "is disclosed.

이러한, 옹벽블록에 의하면 자연석에 의한 자연미를 구현할 수 있지만, 자연석의 가공 공정을 필요로 하고, 별도의 조립공정이 요구될 뿐만 아니라 구조가 복잡하여 생산원가와 시공비가 증가하는 문제점을 갖는다.Such a retaining wall block can realize a natural beauty due to a natural stone, but it requires a manufacturing process of a natural stone, requires a separate assembling process, and has a complicated structure, thereby increasing the production cost and the construction cost.

그리고, 자연석을 그대로 이용하는 것이므로 표현할 수 있는 색상과 미감이 한정되어 다채로운 색상을 표현할 수 없고, 옹벽의 외관을 다양한 디자인으로 구현할 수 없는 한계점이 있다.In addition, since natural stones are used as they are, there are limitations in that they can not express colorful colors due to limited color and aesthetics that can be expressed, and can not realize the appearance of the retaining wall with various designs.

한국 등록특허 10-1482859Korean Patent No. 10-1482859

본 발명은 콘크리트와의 결합력이 우수하면서도 내약품성, 내구성이 보강될 뿐만 아니라 시멘트 콘크리트 블록 전면부의 백화현상을 방지하고 자외선에 의한 탈색, 변색이 일어나지 않으며, 색상 및 외관이 미려하고 주변환경에 적합하도록 자연석의 색상을 표출할 수 있게 함으로써 외관과 질감을 장기간 유지할 수 있도록 구성되며 녹지 조성과 주변 환경에 맞는 색상을 구현할 수 있는 자연석 색상을 갖는 콘크리트 블록의 제조방법을 제공하는데 그 목적이 있다.The present invention is to provide a cement concrete block which is excellent in the bonding strength with concrete, and is resistant to chemical resistance and durability, and also prevents bleaching of the front portion of cement concrete block, does not discolor due to ultraviolet rays, does not cause discoloration, It is an object of the present invention to provide a method of manufacturing a concrete block having a natural stone color which is capable of maintaining the appearance and texture for a long period of time by allowing the color of the natural stone to be expressed,

본 발명의 목적을 달성하기 위하여 콘크리트 옹벽블록 표면에 자연석 색상을 구현할 수 있도록 1차 금형몰드에 의해 성형된 1차 성형블록을 증기 양생시킨 후, 위 1차 성형블록을 2차 금형몰드로 내부에 투입시켜 자연석 색상부를 표현할 수 있는 2차 몰탈이 위 1차 성형블록의 표면에 도포됨과 함께 2차 성형블록에 형성된 열선에 의한 건식 건조방식으로 2차 성형블록의 자연석 색상부로 형성시킬 수 있다. In order to achieve the object of the present invention, a primary molding block molded by a primary mold mold is vapor-cured so as to realize a color of a natural stone on the surface of a concrete retaining wall block, and then the upper primary molding block is filled with a secondary mold mold A secondary mortar capable of expressing the color of a natural stone can be applied to the surface of the primary molding block and formed into a natural stone color portion of the secondary molding block by a dry drying method using a hot wire formed in the secondary molding block.

따라서, 양생 완료된 위 2차 성형블록의 표면에 형성된 자연석 색상부는 변색이나 탈색이 발생하지 않고, 주변환경에 적합하도록 칼라의 색상을 표출할 수 있게 함으로써 다양한 미감을 표현할 수 있고 옹벽의 외관을 다양한 디자인으로 구현할 수 있는 자연석 색상을 갖는 콘크리트 블록의 제조방법에 관한 것이다.Therefore, the color of the natural stone formed on the surface of the cured secondary molding block is not colored or discolored, and it is possible to express the color of the color so as to be suitable for the surrounding environment, so that various aesthetics can be expressed. To a method of manufacturing a concrete block having a natural stone color.

본 발명은 콘크리트와의 결합력이 우수하면서도 내약품성, 내구성이 보강될 뿐만 아니라 시멘트 콘크리트 블럭 전면부의 백화현상을 방지하고 자외선에 의한 탈색, 변색이 일어나지 않으며, 색상 및 외관이 미려하고 고품격을 지닌 자연석과 같은 외관과 질감을 장기간 유지할 수 있는 효과가 있다.The present invention relates to a cement concrete block which is excellent in bonding strength with concrete, and which is resistant to chemical resistance and durability, as well as preventing whitening of the front face of a cement concrete block, discoloration and discoloration caused by ultraviolet rays, The same appearance and texture can be maintained for a long period of time.

도 1는 본 발명의 1차 금형몰드에 1차 몰탈이 채워지면서 동시에 진동으로 성형하는 상태를 나타낸 사시도.
도 2는 본 발명의 1차 금형몰드에 진동 성형된 제품에 파렛트가 들어오는 상태를 나타낸 사시도.
도 3은 진동 성형된 1차 금형몰드를 180°회전시키는 상태를 나타낸 사시도.
도 4는 1차 금형몰드에서 1차 성형블록을 분리시키는 상태를 나타낸 사시도.
도 5는 1차 성형블록을 증기로 양생시키는 상태를 나타낸 사시도.
도 6은 2차 금형몰드를 형성시킨 후, 2차 몰탈이 채워진 상태를 나타낸 정면도.
도 7은 2차 금형몰드 내부에 1차 성형블록을 끼우는 상태를 나타낸 정면도.
도 8은 2차 금형몰드 내부에 채워진 2차 몰탈이 2차 성형블록 표면에 흡수되고 열선에 의해 수분이 건조되면서 양생되어 코팅되는 상태를 나타낸 정면도.
도 9는 2차 금형몰드 내부에 분리되어진 상태의 2차 성형블록을 나타낸 사시도. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a perspective view showing a state in which a primary molten metal is filled in a primary mold of the present invention and is simultaneously molded by vibration.
Fig. 2 is a perspective view showing a state in which a pallet enters a product which is vibration-molded in a primary mold of the present invention; Fig.
3 is a perspective view showing a state in which the vibration-molded primary mold mold is rotated by 180 °.
4 is a perspective view showing a state in which a primary molding block is separated from a primary mold.
5 is a perspective view showing a state in which the primary molding block is cured by vapor.
6 is a front view showing a state in which the secondary mortar is filled after the secondary mold is formed.
7 is a front view showing a state in which the primary molding block is sandwiched in the mold of the secondary mold.
8 is a front view showing a state in which a secondary mortar filled in the mold of the secondary mold is absorbed by the surface of the secondary molding block and is cured while moisture is dried by hot wire.
9 is a perspective view showing a secondary molding block in a state of being separated inside the mold of the secondary mold.

아래에서는 첨부한 도면을 참조하여 본 발명이 속하는 기술분야에서 통상의 지식을 가진자가 용이하게 실시할 수 있도록 본 발명의 실시예를 설명한다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, embodiments of the present invention will be described with reference to the accompanying drawings.

그러나, 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다.The present invention may, however, be embodied in many different forms and should not be construed as limited to the embodiments set forth herein.

그리고, 도면에서 본 발명을 명확하게 설명하기 위해서 설명과 관계없는 부분은 생략하였으며, 명세서 전체를 통하여 유사한 부분에 대해서는 유사한 도면 부호를 붙였다.In order to clearly illustrate the present invention, parts not related to the description are omitted, and like parts are denoted by similar reference numerals throughout the specification.

명세서 전체에서, 어떤 부분이 어떤 구성요소를 포함한다고 할 때 이는 특별히 반대되는 기재가 없는 한 다른 구성요소를 제어하는 것이 아니라 다른 구성요소를 더 포함할 수 있는 것을 의미한다.Throughout the specification, when an element comprises a constituent element, it means that it can include other constituents, rather than controlling other elements, unless specifically stated otherwise.

먼저, 본 발명은 콘크리트와의 결합력이 우수하면서도 내약품성, 내구성이 보강될 뿐만 아니라, 시멘트 콘크리트 블록 전면부의 백화현상을 방지하고 자외선에 의한 탈색, 변색이 일어나지 않으며, 색상 및 외관이 미려하고 주변환경에 적합하도록 자연석의 색상을 다양하게 표출할 수 있게 함으로써 외관과 질감을 장기간 유지 시킬 수 있다.First of all, the present invention provides a cement concrete block which is excellent in bonding strength with concrete, and which is resistant to chemical resistance and durability, prevents bleaching of the front portion of a cement concrete block, does not discolor due to ultraviolet rays, does not discolor, So that the appearance and texture can be maintained for a long period of time.

그리고, 콘크리트 옹벽블록 표면에 자연석 색상을 구현할 수 있도록 1차 금형몰드(10)에 의해 성형된 1차 성형블록(11)을 증기 양생시킨 후, 위 1차 성형블록(11)을 2차 금형몰드(20)로 내부에 고정시켜 자연석 색상부(30)를 표현할 수 있는 구성이다.The primary molding block 11 formed by the primary mold mold 10 is vapor-cured so that the color of the natural stone can be realized on the surface of the concrete retaining wall block. Then, the upper primary molding block 11 is placed in the secondary mold mold (20) to fix the natural stone color part (30).

이때, 2차 금형몰드(20) 내부에 투입되는 2차 몰탈(23)이 위 1차 성형블록(11)의 전면 장식부(13)에 도포됨과 함께 2차 금형몰드(20) 내부에 내장된 열선(21)에 의한 건식 건조방식으로 2차 성형블록(24)으로 형성시킬 수 있다. At this time, the secondary mortar 23 injected into the secondary mold mold 20 is applied to the front decorating portion 13 of the upper primary molding block 11, and the secondary mortar 23 is embedded in the secondary mold mold 20 It is possible to form the secondary molding block 24 by a dry drying method using the hot wire 21.

여기서, 2차 금형몰드(20)는 열전도성이 양호한 섬유강화복합재 FRP(Fiber Reinforced Plastics) 또는 알루미늄 재질로 형성된다.Here, the secondary mold mold 20 is formed of fiber reinforced plastics (FRP) or aluminum material having good thermal conductivity.

따라서, 양생 완료된 위 2차 성형블록(24)의 표면에 형성된 자연석 색상부(30)는 변색이나 탈색이 발생하지 않고, 주변환경에 적합하도록 칼라의 색상을 표출할 수 있게 함으로써 다양한 미감을 표현할 수 있고 옹벽의 외관을 다양한 디자인으로 구현할 수 있다.Therefore, the natural stone hue 30 formed on the surface of the cured secondary molding block 24, which has been cured, is capable of expressing the color of the color so as not to discolor or discolor, And the appearance of the retaining wall can be realized with various designs.

도 1는 본 발명의 1차 금형몰드에 1차 몰탈이 채워지면서 동시에 진동으로 성형하는 상태를 나타낸 사시도이다.1 is a perspective view showing a state in which a primary molten metal is filled in a primary metal mold of the present invention and is simultaneously molded by vibration.

여기서, 1차 금형몰드(10) 내부에 채워지는 1차 몰탈(12)이 채워진 후, 제품 파렛트(14)가 장착된 구성이다.Here, the primary mold 12 is filled with the primary mortar 12, and then the product pallet 14 is mounted.

그리고, 도 2는 본 발명의 1차 금형몰드에 진동 성형된 제품에 파렛트가 조립되어 가압되는 상태를 나타낸 사시도.2 is a perspective view showing a state in which a pallet is assembled and pressed on a product subjected to vibration molding in a mold of a primary mold of the present invention.

여기서, 1차 금형몰드(10) 내부에 채워진 1차 몰탈(12)은 제품 파렛트(14)의 진동가압 작용과 1차 금형몰드(10)의 진동에 의해 1차 성형블록(11)의 형상을 잡아주게 되는 구성이다.The primary molding 12 filled in the primary mold mold 10 has a shape of the primary molding block 11 formed by the vibration pressing action of the product pallet 14 and the vibration of the primary mold mold 10 It is the configuration to be held.

한편, 도 3은 진동 성형된 1차 금형몰드를 파렛트와 클램프(미도시됨)를 이용하여 고정시킨 다음 180°회전시키는 상태를 나타낸 사시도이며, 도 4는 1차 금형몰드에서 1차 성형블록을 클램프(미도시됨)를 풀고 파렛트를 분리시키는 상태를 나타낸 사시도이다.FIG. 3 is a perspective view showing a state in which the vibration-molded primary mold mold is fixed by using a pallet and a clamp (not shown) and then rotated by 180.degree. FIG. 4 is a cross- Fig. 3 is a perspective view showing a state in which a clamp (not shown) is released and the pallet is separated.

여기서, 1차 금형몰드(10)를 통하여 1차 성형블록(11)은 2차 성형블록의 문양에 가깝게 완성될 수 있으며, 위 1차 성형블록(11)의 표면에는 전면 장식부(13)가 1차 형성되는 구성이다.Here, the primary molding block 11 can be completed close to the pattern of the secondary molding block through the primary mold mold 10, and the front decorating portion 13 is formed on the surface of the upper primary molding block 11 And is formed in a primary form.

이와 같은 방법으로 완성된 1차 성형블록(11)은 증기 양생방식으로 몰탈이 건조될 수 있다.The primary molding block 11 thus completed can be dried in a vapor curing manner.

즉, 도 5와 같이 1차 성형블록(11)이 완성될 수 있다.That is, the primary molding block 11 can be completed as shown in FIG.

한편, 도 6은 2차 금형몰드(20)이며, 2차 몰탈이 채워진 상태를 나타낸 정면도이다.On the other hand, Fig. 6 is a front view showing a state in which the secondary mold is filled with the secondary mold.

여기서, 2차 금형몰드(20)는 열전도성이 양호한 섬유강화복합재 FRP(Fiber Reinforced Plastics) 또는 알루미늄 재질이며 그 내부에는 열선(21)과 돌출부 금형 성형부(22)가 형성되고, 1차 성형블록(11)의 투입과 분리가 용이하도록 라운드 형상의 출구(25)가 형성된다. Here, the secondary mold mold 20 is made of fiber reinforced plastic (FRP) or aluminum material having a good thermal conductivity, in which a heat ray 21 and a protruding mold forming section 22 are formed, Shaped outlet 25 is formed to facilitate the introduction and separation of the outlet 11.

여기서, 작업자는 2차 금형몰드(20) 내부에 박리제를 도포하고 2차 몰탈(23)을 투입시키게 된다.Here, the worker applies a releasing agent to the interior of the secondary mold 20 and inserts the secondary mortar 23 therein.

그리고, 도 7은 2차 금형몰드(20) 내부에 1차 성형블록(11)을 끼우는 상태를 나타낸 정면도이다.7 is a front view showing a state in which the primary molding block 11 is sandwiched in the mold 20 of the secondary mold.

한편, 도 8은 2차 금형몰드(20) 내부에 채워진 2차 몰탈(23)이 1차 성형블록 (11) 전면 장식부(13)에 흡수되는 상태이다.8 shows a state in which the secondary mortar 23 filled in the secondary mold 20 is absorbed by the front decoration 13 of the primary molding block 11.

이때, 약간의 2차 몰탈(23) 부분은 1차 성형블록(11)의 자중과 진동자(미도시됨)에 의해 압축이 되어 넘치면서 1차 성형블록(11)의 테두리 상측까지 도달할 수 있으며, 이는 후 공정에서 제거되는 구성이다.At this time, a part of the secondary mortar 23 may reach the upper edge of the primary molding block 11 while being compressed by the weight of the primary molding block 11 and the vibrator (not shown) This is a configuration that is removed in the post-process.

여기서, 위 2차 금형몰드(20) 내부에 채워진 2차 몰탈(23)이 1차 성형블록(11) 전면장식부(13)에 흡수되고 조직을 치밀하게 하기 위하여 진동자(미도시됨)를 이용하여 1분간 진동을 실행후, 정지시킬 수 있다.Here, a secondary mortar 23 filled in the upper secondary mold 20 is absorbed by the front decorating part 13 and a vibrator (not shown) is used to tighten the texture After the vibration is performed for 1 minute, it can be stopped.

또한, 2차 금형몰드(20) 내부에 형성된 열선(21)이 가열 작동하게 되면서 2차 몰탈의 충전과 함께 수분을 건조시키는 구성이다.In addition, the heating wire 21 formed in the mold 20 of the secondary mold is heated to dry the water together with the secondary mortar.

여기서, 열선(21)의 온도 60 ~ 65℃ 정도까지 상승하게 되고 작업 시간은 30분정도이며, 중앙제어부를 통한 컨트롤박스(미도시됨)에 의해 자동제어 될 수 있다.Here, the temperature of the hot wire 21 is raised to about 60 to 65 DEG C, and the operation time is about 30 minutes, and can be automatically controlled by a control box (not shown) through the central control unit.

따라서, 종래의 레미콘을 이용한 습식 몰탈을 이용한 작업 방식과 비교하였을 때 작업을 시간을 크게 단축시킬 수 있는 것이다.Therefore, when compared with a conventional wet concrete using a mortar, the time required for the operation can be greatly shortened.

그리고, 도 9는 2차 금형몰드(20) 내부에서 2차 성형블록(24)이 분리되어진 상태를 나타낸 사시도이다.9 is a perspective view showing a state in which the secondary molding block 24 is separated from the inside of the secondary mold mold 20. As shown in FIG.

여기서, 2차 성형블록(24)의 표면에는 2차 몰탈(23)이 건조되어진 상태의 자연석 색상부(30)가 형성되어 있다.Here, on the surface of the secondary molding block 24, a natural stone color part 30 in a state where the secondary mortar 23 is dried is formed.

여기서, 자연석 색상부(30)를 이루는 2차 몰탈(23)의 조성물은 가는모래 50중량%, 석분 13중량%, 시멘트 35중량%, 무기안료 2중량%로 구성되며 물의 구성비는 골재의 습윤상태에 따라 적정한 슬럼프를 유지하여 작업에 용이할 수 있도록 가감하며 필요에 따라서 혼화제를 사용하게 된다.The composition of the secondary mortar 23 constituting the natural stone hue 30 is composed of 50% by weight of fine sand, 13% by weight of stoneware, 35% by weight of cement and 2% by weight of inorganic pigment. To maintain the proper slump and to facilitate the work, and the admixture is used if necessary.

이상과 같이 본 발명은 콘크리트 옹벽블록 표면에 자연석 색상을 구현할 수 있도록 1차 성형블록(11)을 증기로 양생시킨 다음 위 1차 성형블록(11) 전면 장식부(l3)에는 열선(21)에 의한 건식 방식으로 양생 완료되는 2차 성형블록(24)의 자연석 색상부(30)를 형성시킬 수 있다.As described above, according to the present invention, the primary molding block 11 is cured by steam so that the color of the natural stone can be realized on the surface of the concrete retaining wall block. Then, the front decorating part 13 of the primary molding block 11 is heated It is possible to form the natural stone hue 30 of the secondary molding block 24 which is cured by the dry method of the present invention.

또한, 위 2차 성형블록(24)의 자연석 색상부(30)는 변색이나 탈색이 발생하지 않고, 주변환경에 적합하도록 자연석의 색상을 표출할 수 있게 함으로써 다양한 미감을 표현할 수 있고 옹벽의 외관을 다양한 디자인으로 구현할 수 있는 다양한 주변 환경에 맞는 색상을 표현할 수 있다.In addition, the natural stone color portion 30 of the upper secondary molding block 24 can display various colors without causing discoloration or discoloration, and can display the color of the natural stone so as to be suitable for the surrounding environment. It is able to express the color suitable for various environment that can be implemented with various designs.

즉, 1차 금형몰드(10)에 의해 성형된 1차 성형블록(11)을 증기 양생시킨 후, 위 1차 성형블록(11)을 2차 금형몰드(20)로 내부에 투입시켜 자연석 색상부(30)를 표현할 수 있는 2차 몰탈(23)이 위 1차 성형블록(11)의 표면에 도포됨과 함께 2차 성형블록(24)에 형성된 열선(21)에 의한 건식 양생 건조방식으로 2차 성형블록(24)의 자연석 색상부(30)로 형성시킬 수 있다. That is, after the primary molding block 11 molded by the primary mold mold 10 is vapor-cured, the upper primary molding block 11 is inserted into the interior of the natural stone color block 20 by the secondary mold mold 20, The secondary mortar 23 capable of expressing the secondary molding block 30 is applied to the surface of the upper primary molding block 11 and the second secondary molding block 23 is coated with the second secondary molding block 11 by the dry curing drying method using the hot wire 21 formed in the secondary molding block 24. [ It is possible to form the natural stone color part 30 of the molding block 24.

따라서, 양생 완료된 위 2차 성형블록(24)의 표면에 형성된 자연석 색상부(30)는 변색이나 탈색이 발생하지 않고, 주변환경과 사용자의 요구에 적합하도록 칼라의 색상을 표출할 수 있게 함으로써 다양한 미감을 표현할 수 있고 옹벽의 외관을 다양한 디자인으로 구현할 수 있다.Therefore, the natural stone color part 30 formed on the surface of the cured secondary molding block 24, which has been cured, can display the color of the color so as not to discolor or discolor, It can express aesthetic sense and it can realize the appearance of retaining wall with various designs.

한편, 본 발명은 다음과 같은 단계를 통하여 작업이 이루어진다.Meanwhile, the present invention is accomplished through the following steps.

1차 금형몰드에 1차 몰탈이 채워지는 단계;와,Filling the primary mold with a primary mortar;

위 1차 금형몰드 내부에 채워지는 1차 몰탈이 채워진 후, 진동 가압되면서 충전되는 단계;와,A first molten metal filled in the mold is filled with the molten metal while being vibrated,

위 1차 금형몰드에 제품 파렛트가 조립되어 가압되는 단계;와,A step of assembling and pressing the product pallet onto the first mold,

위 1차 금형몰드 내부에 채워진 1차 몰탈은 제품 파렛트의 가압 작용과 1차 금형몰드의 진동에 의해 1차 성형블록의 형상을 잡아주는 단계;와,A step of holding the shape of the primary molding block by the pressing action of the product pallet and the vibration of the primary mold mold,

위 진동, 가압 성형된 1차 금형몰드를 180°회전시킨 다음 1차 금형몰드에서 1차 성형블록을 분리시키는 단계;와,A step of rotating the primary mold mold by 180 ° and separating the primary molding block from the primary mold mold;

위 1차 금형몰드를 통하여 1차 성형블록은 완성될 수 있으며, 위 1차 성형블록의 표면에는 전면 장식부가 형성되는 단계;와,The primary molding block can be completed through the primary mold mold, a front decoration part is formed on the surface of the primary molding block,

2차 금형몰드 내부에 박리제를 도포 후 가는모래 50중량%, 석분 13중량%, 시멘트 35중량%, 무기안료 2중량%를 물과 믹싱시켜 형성되는 2차 몰탈을 채우는 단계;와,Filling the secondary mold with a releasing agent, filling a secondary mortar formed by mixing 50 wt% of fine sand, 13 wt% of fine particles, 35 wt% of cement and 2 wt% of inorganic pigment with water,

위 2차 금형몰드 내부에 1차 성형블록을 끼우는 단계;와,A step of sandwiching the primary molding block inside the mold of the secondary mold,

위 2차 금형몰드 내부에 채워진 2차 몰탈이 1차 성형블록 전면 장식부에 흡수되면서 진동으로 조직을 조밀하게하는 단계;와,A step of densifying the tissue by vibrating while the secondary mortar filled in the mold of the secondary mold is absorbed by the front decorating part of the primary molding block,

위 2차 금형몰드 내부에 형성된 열선이 작동하게 되면서 2차 몰탈의 양생과함께 수분을 건조시키는 단계;와,Drying the moisture together with the curing of the secondary mortar while the hot wire formed inside the upper secondary mold mold operates,

위 2차 금형몰드 내부에서 2차 성형블록이 분리되는 단계;와,Separating the secondary molding block from the inside of the secondary mold mold;

위 2차 성형블록의 표면에는 2차 몰탈이 건조되어진 상태의 자연석 색상부가 형성되는 단계로 이루어진다.And forming a natural stone color part in a state where the secondary mortar is dried on the surface of the secondary molding block.

따라서, 본 발명은 콘크리트와의 결합력이 우수하면서도 내약품성, 내구성이 보강될 뿐만 아니라 시멘트 콘크리트 블럭 전면부의 백화현상을 방지하고 자외선에 의한 탈색, 변색이 일어나지 않으며, 색상 및 외관이 미려하고 고품격을 지닌 자연석과 같은 외관과 질감을 장기간 유지할 수 있는 효과가 있다.Accordingly, it is an object of the present invention to provide a cement concrete block which is excellent in bonding strength with concrete, and is resistant to chemical resistance and durability as well as preventing whitening of the front surface of a cement concrete block and preventing discoloration and discoloration due to ultraviolet rays, It has the effect of maintaining appearance and texture like natural stone for a long time.

전술한 본 발명의 설명은 예시를 위한 것이며, 본 발명이 속하는 기술분야의 통상의 지식을 가진자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 쉽게 변형이 가능하다는 것을 이해할 수 있을 것이다.It will be understood by those skilled in the art that the foregoing description of the present invention is for illustrative purposes only and that those of ordinary skill in the art can readily understand that various changes and modifications may be made without departing from the spirit or essential characteristics of the present invention. will be.

그러므로 이상에서 설명한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다.It is therefore to be understood that the above-described embodiments are illustrative in all aspects and not restrictive.

예를 들어 단일형으로 설명되어 있는 각 구성요소는 분산되어 실시될 수도 있으며, 마찬가지로 분산된 것으로 설명되어 있는 구성요소들도 결합된 형태로 실시될 수 있다.For example, each component described as a single entity may be distributed and implemented, and components described as being distributed may be implemented in a combined manner.

본 발명의 범위는 상세한 설명보다는 후술하는 특허청구범위에 의하여 나타내어지며 청구범위의 의미 및 범위 그리고 균등 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.The scope of the present invention is defined by the appended claims rather than the detailed description, and all changes or modifications derived from the meaning and scope of the claims and the equivalents are to be construed as being included in the scope of the present invention.

10. 1차 금형몰드
11. 1차 성형블록
12. 1차 몰탈
13. 전면 장식부
14. 제품 파렛트
20. 2차 금형몰드
21. 열선
22. 돌출부 성형부
23. 2차 몰탈
24. 2차 성형블록
25. 라운드형 출구
30. 자연석 색상부10. Primary mold mold
11. Primary forming block
12. Primary mortar
13. Front decorative part
14. Product pallet
20. Second Mold Mold
21. Heat line
22. Projection forming part
23. Second mortar
24. Secondary forming block
25. Round type exit
30. Natural stone color part

Claims (3)

콘크리트 옹벽블록 전면 장식부(13)에 자연석 색상을 구현할 수 있도록 증기로 양생되는 1차 성형블록(11)을 형성시키는 1차 금형몰드(10)와,
위 1차 성형블록의 전면 장식부(13)에 2차 몰탈(23)을 코팅시키기 위한 2차 금형몰드(20)가 형성되되,
위 2차 금형몰드(20)는 열전도성이 양호한 섬유강화복합재 FRP(Fiber Reinforced Plastics) 또는 알루미늄 재질이며 그 내부에는 열선(21)과 돌출부 금형 성형부(22)가 형성되고, 1차 성형블록(11)의 투입과 분리가 용이하도록 라운드 형상의 출구(25)가 형성되고,
위 2차 금형몰드(20) 내부에 채워진 2차 몰탈(23)이 1차 성형블록(11) 전면장식부(13)에 흡수되고 조직을 치밀하게 하기 위하여 진동자(미도시됨)를 이용하여 1분간 진동을 실행후, 정지시키고,
건조 작업시간 10분 동안 위 열선(21)의 온도가 60 ~ 65℃ 정도까지 상승, 제어할 수 있도록 중앙제어부를 통한 컨트롤박스(미도시됨)에 의해 자동제어 되는 구성이고,
위 2차 금형몰드(20) 내부에서 2차 성형블록(24)이 분리되면 2차 성형블록(24)의 표면에는 2차 몰탈(23)이 건조되어진 상태의 자연석 색상부(30)가 형성될 수 있도록 구성되는 자연석 색상을 갖는 콘크리트 블록의 제조방법.A primary mold mold 10 for forming a primary molding block 11 which is cured by vapor so as to realize a natural stone color on a concrete retaining wall block front decorative part 13,
A secondary mold mold 20 for coating the secondary mortar 23 on the front decorative part 13 of the primary molding block is formed,
The secondary mold mold 20 is made of fiber reinforced plastic (FRP) or aluminum material having a good thermal conductivity, in which a hot wire 21 and a protruding mold forming part 22 are formed, Shaped outlet 25 is formed for facilitating the insertion and separation of the outlet 11,
A secondary mortar 23 filled in the mold 20 of the secondary mold is absorbed by the front decoration 13 of the primary molding block 11 and a vibrator (not shown) After the minute vibration is executed,
And is automatically controlled by a control box (not shown) through a central control unit so that the temperature of the upper heating line 21 rises to about 60 to 65 ° C for 10 minutes during a drying operation time,
When the secondary molding block 24 is separated from the inside of the secondary mold 20, the natural stone hatch 30 is formed on the surface of the secondary molding block 24 in a state where the secondary mortar 23 is dried The method comprising the steps < RTI ID = 0.0 > of: < / RTI > 제 1항에 있어서,
위 2차 성형블록(24)의 자연석 색상부(30)를 형성시키는 2차 몰탈(23)의 조성물은 가는모래 50중량%, 석분 13중량%, 시멘트 35중량%, 무기안료 2중량%와 작업에 용이하도록 적정한 슬럼프를 갖출 수 있도록 물과 함께 믹싱 되도록 구성하는 것을 특징으로 하는 자연석 색상을 갖는 콘크리트 블록의 제조방법.The method according to claim 1,
The composition of the secondary mortar 23 for forming the natural stone hue 30 of the secondary molding block 24 is composed of 50% by weight of fine sand, 13% by weight of stannum, 35% by weight of cement and 2% Wherein the water is mixed with water so as to have a proper slump so as to be easy to use. 1차 금형몰드에 1차 몰탈이 채워지는 단계;와,
위 1차 금형몰드 내부에 채워지는 1차 몰탈이 채워진 후, 진동 가압되면서 충전되는 단계;와,
위 1차 금형몰드에 제품 파렛트가 조립되어 가압되는 단계;와,
위 1차 금형몰드 내부에 채워진 1차 몰탈은 제품 파렛트의 가압 작용과 1차 금형몰드의 진동에 의해 1차 성형블록의 형상을 잡아주는 단계;와,
위 진동, 가압 성형된 1차 금형몰드를 180°회전시킨 다음 1차 금형몰드에서 1차 성형블록을 분리시키는 단계;와,
위 1차 금형몰드를 통하여 1차 성형블록은 완성될 수 있으며, 위 1차 성형블록의 표면에는 전면 장식부가 형성되는 단계;와,
2차 금형몰드 내부에 박리제를 도포 후 가는모래 50중량%, 석분 13중량%, 시멘트 35중량%, 무기안료 2중량%으로 이루어진 2차 몰탈을 채우는 단계;와,
위 2차 금형몰드 내부에 1차 성형블록을 끼우는 단계;와,
위 2차 금형몰드 내부에 채워진 2차 몰탈이 1차 성형블록 전면 장식부에 흡수되면서 진동으로 조직을 조밀하게하는 단계;와,
위 2차 금형몰드 내부에 형성된 열선이 작동하게 되면서 2차 몰탈의 양생과함께 수분을 건조시키는 단계;와,
위 2차 금형몰드 내부에서 2차 성형블록이 분리되는 단계;와,
위 2차 성형블록의 표면에는 2차 몰탈이 건조되어진 상태의 자연석 색상부가 형성되는 단계로 이루어지는 것을 특징으로 하는 자연석 색상을 갖는 콘크리트 블록의 제조방법.
Filling the primary mold with a primary mortar;
A first molten metal filled in the mold is filled with the molten metal while being vibrated,
A step of assembling and pressing the product pallet onto the first mold,
A step of holding the shape of the primary molding block by the pressing action of the product pallet and the vibration of the primary mold mold,
A step of rotating the primary mold mold by 180 ° and separating the primary molding block from the primary mold mold;
The primary molding block can be completed through the primary mold mold, a front decoration part is formed on the surface of the primary molding block,
Filling the secondary mold with a releasing agent, filling a secondary mortar composed of 50 wt% of fine sand, 13 wt% of abrasive, 35 wt% of cement and 2 wt% of inorganic pigment,
A step of sandwiching the primary molding block inside the mold of the secondary mold,
A step of densifying the tissue by vibrating while the secondary mortar filled in the mold of the secondary mold is absorbed by the front decorating part of the primary molding block,
Drying the moisture together with the curing of the secondary mortar while the hot wire formed inside the upper secondary mold mold operates,
Separating the secondary molding block from the inside of the secondary mold mold;
And forming a natural stone color part in a state where the secondary mortar is dried on the surface of the secondary molding block.
KR1020160104067A 2016-08-17 2016-08-17 Method for manufacturing concrete block KR101910945B1 (en)