KR20170018527A - Expansibility fireproof-board - Google Patents
Expansibility fireproof-board Download PDFInfo
- Publication number
- KR20170018527A KR20170018527A KR1020150112276A KR20150112276A KR20170018527A KR 20170018527 A KR20170018527 A KR 20170018527A KR 1020150112276 A KR1020150112276 A KR 1020150112276A KR 20150112276 A KR20150112276 A KR 20150112276A KR 20170018527 A KR20170018527 A KR 20170018527A
- Authority
- KR
- South Korea
- Prior art keywords
- foam layer
- weight
- core
- expanded
- board
- Prior art date
Abstract
Description
The present invention relates to an inflated refractory board in which a first reinforcing material consisting of an expanded foam layer expanding on heating on both sides of a porous core material and a first reinforcing material composed of mica or silica paper are stacked in order, To an inflatable refractory board having an excellent heat transfer blocking ability and a thin thickness when heated at 180 DEG C or lower
In general, a heat insulating material is a material for covering the outside of a portion to be kept at a constant temperature and reducing the heat loss or heat input to the outside. It is a material having a temperature of 100 ° C or less, It is divided into a heat insulating material of 500-1,100 ℃ and a refractory insulating material of 1,100 ℃ or higher. It is made porous so as to reduce the thermal conductivity and various kinds .
One example is a foamed polystyrene insulation material obtained by adding a flame retardant and a foaming agent to a styrene resin raw material, dissolving and mixing it in an extruder, and a polystyrene insulation material, which is a foamed polystyrene insulation foam obtained by foaming a polystyrene resin with a
In addition, glass-based minerals such as silica sand, limestone, feldspar, and soda ash are the main raw materials, and the air layer sealed between the glass fibers is a heat insulating layer. In addition to thermal insulation, it has excellent nonflammability, sound absorption, There is a possibility that the heat insulating property by the glass surface is lowered.
In addition, it is an insulation material made of ore raw material such as blast furnace slag and basalt. Physical properties and characteristics are plate-like foamed polyethylene insulation which is roughly the same as glass surface and cooled by extrusion foaming after blending foam agent and flame retardant into polyethylene resin.
In addition, there is a polyurethane foam insulation of an organic foam (closed cell structure) in which a polyol, a polyisocyanate and a blowing agent, and an additive for flame retardancy are main raw materials and a polyurethane foam is foamed and formed, Is a wormlike mineral which is fired at 1,000 ℃ and has excellent insulation of insulation, insulation, fireproofing, soundproofing, and prevention of dew condensation.
In addition, perlite insulator composed of small spherical particles of light spherical shape having internal micropores which is calcined and expanded by calcining the volcanic stannous tin at 900 to 1,200 ° C., and a phenolic resin is foamed and hardened , Which is widely used as insulation material for home, factory, and interior.
Although these insulation materials are adhered to the concrete wall by adhesives or separate fastening means to obtain the thermal insulation effect of the room, they may have a secondary fire damage due to the temperature rise on the back surface of the place where the fire occurs in case of fire have. In addition, there is a problem that the thickness of the heat insulating material is increased in order to improve the heat insulating effect, thereby taking up a considerable volume.
[Prior Art Literature]
[Patent Literature]
Patent Document 1: Korean Patent Laid-Open Publication No. 10-2013-0126712
Patent Document 2: Korean Patent Registration No. 10-0610059
The present invention relates to a flame retardant which is applied to a soft porous core material used in a hard material such as a steel frame to provide a flame retardant which is excellent in fire resistance, heat insulation, light weight and sound absorption, I want to provide a refractory board.
According to an aspect of the present invention, there is provided an inflated refractory board in which an expanded foam layer and a first reinforcing material are stacked in order on both sides of a porous core material, the inflated foam layer being made of PVAc (polyvinyl acetate) resin,
15 to 45% by weight of a carbon fiber-extracted carbon tissue, which is expanded to 40 to 350 times at 100 to 850 DEG C,
10 to 40% by weight of one kind of flame retardant mixed with ammonium polyphosphate alone or with ammonium polyphosphate, melamine and pentaerythritol,
1 to 10% by weight of one kind of filler selected from zinc oxide, titanium dioxide and molybdenum oxide,
1 to 25% by weight of one solvent selected from water, an alcohol and an organic solvent; and
(CMC), Attapulgite, hydroxypropylmethylcellulose (HPMC), hydroxyethylcellulose (HEC), ethylhydroxyethylcellulose (EHEC), organoclay, bentonite, fumed And 0.1 to 3% by weight of at least one viscosity modifier selected from silica and starch.
Further, the core material may include a first core material and a second core material, and may further include an expanded foam layer between the first core material and the second core material.
And the expanded foam layer between the first core and the second core includes a flame retardant composed only of ammonium polyphosphate.
And the expansion foam layer between the first core and the second core includes a first expanded foam layer and a second expanded foam layer and further comprises a first reinforcing material between the first expanded foam layer and the second expanded foam layer .
And the expanded foam layer between the first core and the second core includes a first expanded foam layer and a second expanded foam layer and further includes a second reinforcing material between the first expanded foam layer and the second expanded foam layer .
The core material may be a porous board selected from expanded vermiculite board made of mineral fiber or inorganic, pearlite board, or flyish board.
The first reinforcing material may be a sheet or a film made of mica or silica paper.
The second stiffener may be any one selected from a styrofoam panel, a urethane foam panel, a paper honeycomb, a nonwoven fabric, or a polyester suction plate.
The inflatable refractory board of the present invention has the advantage of having a reduced load and a thin thickness in the case of a non-proof fire wall, and also has an advantageous effect of increasing the internal effective use area.
The inflated refractory board of the present invention expands the inflated foam layer during a fire to form a thick flame retardant pad layer on both sides of the core to block the air flow and fundamentally block the flame propagation to the inside of the heat insulator, So that the generation of smoke and noxious gas is remarkably reduced to minimize the harmfulness of the heat insulating material caused by the fire, thereby reducing the damage to the human body and the environment.
Further, the inflatable refractory board of the present invention is advantageous in that it is lighter than conventional gypsum board or refractory board, is easy to be processed, has a simple installation process, and has a low installation cost.
1 is a cross-sectional view of an inflatable refractory board according to an embodiment of the present invention.
2 is a cross-sectional view of an inflatable refractory board according to another embodiment of the present invention.
3 is a cross-section of an inflatable refractory board according to another embodiment of the present invention.
4 is a cross-sectional view of an inflatable refractory board according to another embodiment of the present invention.
5 is a view showing the construction and materials used in the refractory performance test of the inflatable refractory board (FIG. 3) according to another embodiment of the present invention.
Figure 6 is a partial detail view of an inflatable refractory board (
FIG. 7 is a view showing a temperature measurement position of a test body used in the refractory performance test of the inflatable refractory board (
8 is a graph showing heating temperature curves of an inflatable refractory board (
9 is a table of heating temperature results and a time-temperature area table of an inflatable refractory board (
10 is a result of measuring the temperature of the back surface rising of the inflatable refractory board (
11 is a photograph of a heating surface before and after heating of an inflatable refractory board (
Fig. 12 is a photograph of a back surface of the inflatable refractory board (
FIG. 13 is a view showing temperature measurement positions of the expandable fireproof board test specimen of FIGS. 1, 2 and 4 according to another embodiment of the present invention.
FIG. 14 is a result of measuring the temperature of the back surface of the inflatable refractory board (FIG. 1) according to another embodiment of the present invention.
15 is a result of measuring the temperature of the back surface of the inflatable refractory board (FIG. 2) according to another embodiment of the present invention.
16 is a result of measuring the temperature of the back surface of the inflatable refractory board (FIG. 4) according to another embodiment of the present invention.
Hereinafter, the inflatable refractory board of the present invention will be described in detail. It is to be understood, however, that the invention is not limited to the disclosed embodiments, but is capable of many modifications and alternatives, all of which fall within the scope of the claims as defined by the claims. It is obvious that it can be done.
The present invention is an expandable refractory board in which an expandable foam layer and a first reinforcing material which are expanded on heating on both sides of a porous core material are laminated in order. The expanded foam layer used in the present invention is coated and manufactured with a thickness of 0.1 to 2 mm and is made of PVAc (polyvinyl acetate) resin, EVA (ethylene vinyl acetate) resin, acrylic resin, PU (polyurethane) resin, 10 to 40% by weight of one liquid binder selected from resins,
15 to 45% by weight of a carbon fiber-extracted carbon tissue, which is expanded to 40 to 350 times at 100 to 850 DEG C,
10 to 40% by weight of one kind of flame retardant mixed with ammonium polyphosphate alone or with ammonium polyphosphate, melamine and pentaerythritol,
1 to 10% by weight of one kind of filler selected from zinc oxide, titanium dioxide and molybdenum oxide,
1 to 25% by weight of one solvent selected from water, an alcohol and an organic solvent; and
(CMC), Attapulgite, hydroxypropylmethylcellulose (HPMC), hydroxyethylcellulose (HEC), ethylhydroxyethylcellulose (EHEC), organoclay, bentonite, fumed And 0.1 to 3% by weight of at least one viscosity modifier selected from silica and starch.
The liquid binder of the expanded foam layer has a main function of flame retardancy and influences the strength maintenance and moldability of the product. When the addition amount is less than 10% by weight, the moldability of the product is poor. When the addition amount is more than 40% by weight, It is preferable to add it in the range of 10 to 40% by weight, since it affects the strength maintenance of the product.
The graphite of the expanded foam layer prevents flame propagation when a fire occurs to protect the refractory board and reduce the emission of harmful gases. When the content is less than 15 wt%, the flame retardancy is poor. When the content is more than 45 wt%, the flame retardant effect is excellent It is preferable to add it in the range of 15 to 45% by weight since it affects cost rise and product molding.
The flame retardant of the expanded foam layer affects the strength and viscosity of the product in addition to the main function of flame retardancy. When the content is less than 10% by weight, the strength of the molded product is decreased. When the content is more than 40% , It is preferable to add it within the range of 10 to 40% by weight.
The flame retardant used in the present invention may be one of ammonium polyphosphate alone or mixed with ammonium polyphosphate, melamine and pentaerythritol. Ammonium polyphosphate (APP) has been applied to a hard material such as a conventional steel or sheet, but the present invention is characterized in that it can be used for a porous soft core such as a mineral fiber board. The pentaerythritol may be mono, di, or tripentaerythritol.
The flame retardant of the expanded foam layer may be used in a weight ratio of 1: 1 to 2: 1 relative to the graphite to enhance the binding force of the graphite expanded due to heating, thereby preventing the expanded graphite from flowing down. Preferably 1.5: 1. In particular, the ammonium polyphosphate further includes melamine and / or pentaerythritol to further strengthen the bonding force of the graphite expanded by heating to prevent the expansion material from flowing down.
The filling agent of the expanded foam layer is used for the purpose of increasing the volume and controlling the expansion rate. When the addition amount is 1% by weight or less, the expansion foaming speed is remarkably slow. When 10% by weight or more is added, the expansion speed is fast. And it is difficult to prevent the disappearance, so it is preferable to add in the range of 1 to 10% by weight.
The viscosity modifier of the expanded foam layer affects the strength and viscosity maintenance of the product. When added in an amount of 0.1 wt% or less, the strength of the molded product is lowered. When the added amount is 3 wt% or more, It is preferably added within the range of 0.1 to 3% by weight.
The porous core used in the present invention is any porous board selected from expanded vermiculite board, pearlite board or fly ash board made of mineral fiber or inorganic, and is lighter than gypsum board and has excellent heat insulation, fire resistance, light weight and sound absorption , The thickness is at least about 15 mm, the density is at least about 220 kg / m 3 , the thermal conductivity is about 0.065 w / mk or less, the bending strength is about 250 N, the moisture resistance is about 90% The noise reduction factor is NRC 0.4-0.6, depending on the pattern and thickness) and the light reflectance is greater than about 85%. In addition, the porous core material does not contain asbestos and formaldehyde and is low in toxicity.
The first reinforcing material used in the present invention is a heat-resistant refractory material which is a sheet or a film made of mica or silica paper and is excellent in heat insulation, fire resistance, salt resistance, water resistance, scratch resistance, At least about 0.1 mm thick, at least 170 g / m 2 per weight, and the back side is glued with a glass fiber mesh. The first reinforcing material may be composed of mica or silica paper. The mica is excellent in fire resistance at high temperatures, has a flame and heat shielding effect, inhibits burning of the graphite expansion layer at high temperature, For a long time. The mica may be natural or synthetic mica.
The present invention relates to an inflatable refractory board in which a first reinforcing material, which is an expanded foamed layer expanded on heating on both sides of a porous core material and a mica or silica paper, is laminated in order (FIG. 1) And the backside temperature is maintained at 180 DEG C or lower for 30 minutes. Preferably, the inflatable refractory board has a thickness of 17-19 mm and a weight of 6-8 kg / m 2 .
The inflatable refractory board may be manufactured by laminating an expanded foamed layer and a first reinforcing material on one surface of a core material in this order and laminating the expanded foamed layer and the first reinforcing material on the back surface of the core material in this order . After each layer is laminated, it is naturally dried or heated and dried at 100 ° C., and the first stiffener can be adhered using a polyvinyl acetate (PVAc) resin or an ethylene vinyl acetate (EVA) resin adhesive.
Further, the present invention provides an inflatable refractory board further comprising an inflated foam layer between the core of the inflatable refractory board (Fig. 2). Preferably, the inflatable refractory board has a thickness of 35-37 mm and a weight of 13-17 kg / m 2 . By including the expanded foam layer between the core members, the expansion volume at the time of fire can be further increased to lower the temperature rise rate of the back surface of the heating surface. It is preferable to use a flame retardant composed only of ammonium polyphosphate in order to maximize the binding force of the expanded graphite in the expanded foam layer between the core materials.
According to another embodiment of the present invention, the inflatable refractory board may be manufactured by preparing two core materials each having an expanded foamed layer and a first reinforcing material laminated on one surface thereof and bonding the expanded core material to the back surface of each core material with an expanded foamed layer .
The present invention also provides an inflatable refractory board in which the expanded foam layer between the core materials further comprises a first reinforcing material (Fig. 3). The first reinforcing material between the expanded foam layers has an effect of blocking heat transfer to the non-heated surface due to the heat insulating property during heating.
The present invention also provides an inflatable refractory board wherein the expanded foam layer between the core materials further comprises a second reinforcing material (Fig. 4). When the second reinforcing material between the expanded foam layers is any one selected from the group consisting of a styrofoam panel, a urethane foam panel, a paper honeycomb, a nonwoven fabric, and a polyester suction plate, it is melted or carbonized upon heating to provide an expanded space of the expanded foam layer So that the thickness of the refractory board before and after expansion of the expanded foam layer is kept constant.
≪ Evaluation Example 1 &
The fire resistance performance of the inflatable refractory board manufactured according to one embodiment of the present invention was measured by performing a 2-hour refractory test (structural grade: A-2) according to the operational guidelines of the refractory filling structure.
The construction and materials of the test body having the inflatable refractory board of the present invention (Systems 2-A and 2-B of FIG. 3) are shown in the following table (unit: mm).
The refractory performance of the expandable refractory board of the present invention was measured. The test specimen having the expandable refractory board of the present invention was fixed to a vertical heating furnace having a heating area of 3 m X 3 m. The specimen was heated for 2 hours so that the average value of the temperature measured in the thermocouple installed in the furnace matched the standard heating temperature curve according to the detailed operating instructions of the refractory filling structure. During the heating test, the pressure in the heating furnace was adjusted so that the pressure at the top of the test body was 20 Pa or less at a pressure of 0 Pa at a height of 500 mm above the bottom of the test body. Deformation, fracture, and dropout of the test specimen during heating were observed and the scratch resistance of the test specimens such as whether or not the cotton pads were ignited was measured. During the test, a thermocouple was placed on the backside of the specimen to measure the temperature rise on the backside.
The performance criteria of the facility penetration part charging system specified in the Detailed Operation Guidelines of the Refractory Charging Structure are shown in the following table.
No holes or flames were generated on the surface of all the specimens until the end of the test, and flames did not occur on the back of the specimen (FIGS. 11 and 12).
As a result of the backside temperature measurement for the heat resistance measurement of the specimen during the heating test, the maximum rising temperature of the backside is as shown in the following table.
≪ Evaluation Example 2 &
In the same manner as in Evaluation Example 1, each of the expandable fireproof boards (FIGS. 1, 2 and 4) manufactured in accordance with an embodiment of the present invention was subjected to the fire resistance test according to the operating instructions of the fireproof filling structure.
A test specimen (size: 600 mm x 600 mm) equipped with an inflatable refractory board of the present invention was fixed to a heating furnace having a heating area of 600 mm x 600 mm. The average value of the temperature measured in the thermocouple installed in the heating furnace is set to be 30 minutes (expansion reinforcing board in FIG. 1), 120 minutes (in FIG. 1) so that the average value of the temperature measured in the thermocouple installed in the heating furnace meets the standard heating temperature curve according to the KSF- 2) and 120 minutes (the inflatable refractory board of FIG. 4). The backside temperature of the test piece was measured at 8 places in Fig. 13, and the results are shown in Figs. 14, 15 and 16.
Until the end of the test, no holes or flames were generated on the surface of all the specimens, and no flames were generated on the back side of the specimen. In particular, in the case of the system shown in FIG. 4, the temperature rise was the smallest at about 80-100 ° C.
Claims (8)
10 to 40% by weight of at least one liquid binder selected from the group consisting of PVAc (polyvinyl acetate) resin, EVA (ethylene vinyl acetate) resin, acrylic resin, PU (polyurethane) resin, silicone resin,
15 to 45% by weight of a carbon fiber-extracted carbon tissue, which is expanded to 40 to 350 times at 100 to 850 DEG C,
10 to 40% by weight of a flame retardant mixed with ammonium polyphosphate alone or with ammonium polyphosphate, melamine, pentaerythritol,
1 to 10% by weight of one kind of filler selected from zinc oxide, titanium dioxide and molybdenum oxide,
1 to 25% by weight of a solvent selected from water, an alcohol and an organic solvent; and
(CMC), Attapulgite, hydroxypropylmethylcellulose (HPMC), hydroxyethylcellulose (HEC), ethylhydroxyethylcellulose (EHEC), organoclay, bentonite, fumed 0.1 to 3% by weight of at least one viscosity modifier selected from silica and starch.
The expanded foam layer between the first core and the second core
10 to 40% by weight of at least one liquid binder selected from the group consisting of PVAc (polyvinyl acetate) resin, EVA (ethylene vinyl acetate) resin, acrylic resin, PU (polyurethane) resin, silicone resin,
15 to 45% by weight of a carbon fiber-extracted carbon tissue, which is expanded to 40 to 350 times at 100 to 850 DEG C,
10 to 40% by weight of a flame retardant composed of ammonium polyphosphate,
1 to 10% by weight of a filler selected from zinc oxide, titanium dioxide and molybdenum oxide,
1 to 25% by weight of a solvent selected from water, an alcohol and an organic solvent; and
(CMC), Attapulgite, hydroxypropylmethylcellulose (HPMC), hydroxyethylcellulose (HEC), ethylhydroxyethylcellulose (EHEC), organoclay, bentonite, fumed 0.1 to 3% by weight of at least one viscosity modifier selected from silica and starch.
Wherein the expanded foam layer between the first core and the second core includes a first expanded foam layer and a second expanded foam layer and further includes a first reinforcing material between the first expanded foam layer and the second expanded foam layer Inner inflatable board.
Wherein the expanded foamed foam layer between the first core and the second core includes a first expanded foam layer and a second expanded foam layer and further includes a second reinforcing material between the first expanded foam layer and the second expanded foam layer Inner inflatable board.
Wherein the first reinforcing material is a sheet or a film made of mica or silica paper.
Wherein the second reinforcing material is any one selected from the group consisting of a styrofoam panel, a urethane foam panel, a paper honeycomb, a nonwoven fabric, and a polyester suction plate.