KR20160056081A - Anti-flammable Coating Composition of expansion for Protecting Metal Surface - Google Patents
Anti-flammable Coating Composition of expansion for Protecting Metal Surface Download PDFInfo
- Publication number
- KR20160056081A KR20160056081A KR1020140156022A KR20140156022A KR20160056081A KR 20160056081 A KR20160056081 A KR 20160056081A KR 1020140156022 A KR1020140156022 A KR 1020140156022A KR 20140156022 A KR20140156022 A KR 20140156022A KR 20160056081 A KR20160056081 A KR 20160056081A
- Authority
- KR
- South Korea
- Prior art keywords
- coating composition
- weight
- parts
- flame
- retardant coating
- Prior art date
Abstract
Description
본 발명은 금속표면 보호용 팽창성 방염 도료 조성물에 관한 것이다.
The present invention relates to an expandable flame retardant coating composition for metal surface protection.
금속재 등은 화재 시에 급격히 녹아서 물성을 상실하게 되어 건물 붕괴의 원인을 제공하기 때문에 화재 시 금속재 등을 보호하기 위한 방염 및 내열 코팅 기술의 개발이 필요하다. 미국특허 제3658662호에는 알루미늄 판의 표면을 규산염 화합물을 사용하여 내화성을 부여하는 기술이 공지되어 있지만, 여전히 충분한 방염 특성을 제공하지 못하는 단점이 있다.Metal materials and the like are rapidly melted at the time of fire and lose their physical properties and provide the cause of the collapse of the building. Therefore, it is necessary to develop flame retardant and heat resistant coating technology for protecting metal materials in case of fire. U.S. Patent No. 3658662 discloses a technique for imparting fire resistance by using a silicate compound on the surface of an aluminum plate, but it still has a disadvantage in that it does not provide sufficient flame resistance.
따라서 보다 높은 열에서도 견딜 수 있는 방염 금속 등과 같이 재료 표면의 내화성을 높이기 위한 방염 및 내열 코팅 기술의 개발이 여전히 필요하다.
Therefore, it is still necessary to develop a flame-retardant and heat-resistant coating technique for improving the fire resistance of the material surface, such as flame-retardant metal which can withstand even higher heat.
본 발명의 목적은 기존의 기술보다 개선된 금속표면 보호용 팽창성 방염 도료 조성물을 제공하는 것이다.It is an object of the present invention to provide an expandable flame retardant coating composition for metal surface protection that is improved over existing techniques.
본 발명의 또 다른 목적은 방염성과 함께 방수성 및 방식성을 갖는 금속 등의 표면 층을 보호하는 금속표면 보호용 팽창성 방염 도료 조성물을 제공하는 것이다.
Another object of the present invention is to provide an intumescent coating composition for metal surface protection that protects surface layers of metals and the like having flame resistance and water repellency and anticorrosion properties.
본 발명은 예컨대 금속 표면에 코팅 층을 형성함으로써, 방염 특성을 갖는 도료 조성물에 관한 것이다.The present invention relates to a coating composition having flame resistance properties, for example, by forming a coating layer on a metal surface.
본 발명의 일 양태로서, 상기 도료 조성물은 규산나트륨 및 팽창성 유리를 함유하는 수용성 도료 조성물일 수 있다. 상기 팽창성 유리는 저융점 고팽창성 유리인 것이 보다 바람직하며, 예컨대 붕규산계 저용점 유리를 예시할 수 있다.In one embodiment of the present invention, the coating composition may be a water-soluble coating composition containing sodium silicate and an expandable glass. The above-mentioned inflatable glass is more preferably a low-melting-point high-expansion glass, and for example, a borosilicate-based low-melting glass can be exemplified.
본 발명의 또 다른 양태는 상기 수용성 도료 조성물에 아민계 실란 및 에폭시계 실란을 포함시킴으로써 금속 등의 재료 표면에 단단히 고착할 수 있는 수용성 도료 조성물을 제공할 수 있다. 실란계 화합물을 포함한 도료 조성물로 코팅 후 열처리하여 경화하면 더욱 단단히 금속 표면에 고착되도록 할 수 있다.Another embodiment of the present invention can provide a water-soluble paint composition capable of firmly adhering to the surface of a material such as a metal by including amine silane and epoxy silane in the water-soluble paint composition. When the coating composition is coated with a coating composition containing a silane compound and then cured by heat treatment, it can be more firmly fixed to the surface of the metal.
본 발명의 또 다른 양태는 상기 수용성 도료 조성물에 방연제 및 발수제 중에서 선택된 하나 또는 두 성분을 더 포함시킴으로써, 방수 기능과 연기 발생 억제 기능을 부여할 수 있는 도료 조성물을 제공할 수 있다.Another embodiment of the present invention can provide a coating composition capable of imparting a waterproof function and a smoke generation inhibiting function by further including one or two components selected from a flame retardant and a water repellent in the water-soluble paint composition.
본 발명의 또 다른 양태는 상기 양태들에서 아크릴계 첨가제, 예컨대 수성에멀젼계를 더 추가시킴으로써, 치밀하게 박막을 형성하는 효과가 부여된 도료 조성물을 제공할 수 있다.Another embodiment of the present invention can provide a coating composition having the effect of forming a dense thin film by further adding an acrylic additive such as an aqueous emulsion system in the above embodiments.
본 발명의 상기 도료 조성물에서 각 성분의 조성비는 당업자라면 목적에 맞게 크게 제한되지 않는 것으로, 필요에 의해 적절히 조절될 수 있다.The composition ratio of each component in the coating composition of the present invention is not particularly limited so far as it is suitable for a person skilled in the art, and can be appropriately adjusted if necessary.
본 발명의 하나의 예를 들면, 상기 규산나트륨 100 중량부에 대하여 팽창성 저융점 유리 0.5 내지 100 중량부 및 물 10 내지 300 중량부를 포함하는 도료 조성물일 수 있다.One example of the present invention may be a coating composition comprising 0.5 to 100 parts by weight of an expandable low melting point glass and 10 to 300 parts by weight of water based on 100 parts by weight of the sodium silicate.
본 발명의 또 다른 예로, 상기 규산나트륨 100 중량부에 대하여 팽창성 저융점 유리 0.5 내지 100 중량부, 물 10 내지 300 중량부, 아민계 실란 0.1 내지 10 중량부, 및 에폭시계 실란 0.1 내지 10 중량부를 포함하는 도료 조성물일 수 있다.In another embodiment of the present invention, 0.5 to 100 parts by weight of an expandable low-melting glass, 10 to 300 parts by weight of water, 0.1 to 10 parts by weight of an amine series silane and 0.1 to 10 parts by weight of an epoxy series silane are added to 100 parts by weight of the sodium silicate. ≪ / RTI >
본 발명의 또 다른 예로, 상기 예의 경우를 연결시킬 경우 각 예컨대 10 내지 50 중량부의 고형분을 가지는 아크릴계 에멀젼 0.5 내지 10 중량부를 더 포함하는 도료 조성물일 수 있다.Another example of the present invention is a coating composition comprising 0.5 to 10 parts by weight of an acrylic emulsion having a solid content of 10 to 50 parts by weight, for example, when the above examples are connected.
본 발명의 또 다른 예로, 상기 예들에서 방연제로서 다공성 무기산화물 등의 세라믹을 0.1 내지 10 중량부 더 포함하는 도료 조성물일 수 있다.As another example of the present invention, in the above examples, a coating composition comprising 0.1 to 10 parts by weight of a ceramic such as a porous inorganic oxide may be used as a flame retardant.
또한 본 발명의 또 다른 예를 든다면, 상기 다양한 예들에서 발수제, 점도조절제 및 고형화방지제 등의 첨가제 0.1 내지 10 중량부를 더 포함하는 도료 조성물일 수 있다.
Another example of the present invention may be a coating composition comprising 0.1 to 10 parts by weight of an additive such as a water repellent agent, a viscosity controlling agent and an anti-settling agent in the various examples.
본 발명의 도료 조성물을 이용한 코팅 층 형성 방법은 크게 제한되지 않지만, 예를 들면,The method of forming the coating layer using the coating composition of the present invention is not particularly limited, but, for example,
S1) 규산나트륨, 팽창성 유리, 아민계실란 및 에폭시계 실란을 포함하는 금속 표면 보호용 내염성 방염 도료 조성물을 금속재료의 표면에 코팅하는 단계; 및S1) coating a surface of a metal material with a flame-retardant flame retardant coating composition for metal surface protection comprising sodium silicate, expandable glass, amine-based silane and epoxy silane; And
S2) 상기 코팅 면을 건조 및 경화하는 단계;S2) drying and curing the coated surface;
를 포함하는 금속표면 보호용 도료 조성물을 이용한 금속표면 방염 코팅 층 형성 방법일 수 있다.A method of forming a metal surface flame-retardant coating layer using the metal surface protective coating composition.
또한 본 발명의 일 실시예에 있어서, 상기 S1) 및 S2) 단계를 2회 또는 그 이상 반복하는 단계를 거쳐 코팅 층의 두께를 조절하여 형성할 수 있는 금속표면 보호용 도료 조성물을 이용한 금속표면 방염 코팅 층 형성 방법일 수 있다.Also, in one embodiment of the present invention, the metal surface flame-retardant coating using the coating composition for metal surface protection, which can be formed by adjusting the thickness of the coating layer through repeating steps S1) and S2) Layer forming method.
또한 본 발명의 일 실시예에 있어서, 상기 S1) 단계에서 상기 금속표면을 물과 세제로 세정하고, 이어서 상기 표면을 도료 조성물로 코팅하는 것을 포함하는 금속표면 보호용 도료 조성물을 이용한 금속표면 방염 코팅 층 형성 방법일 수 있다.In an embodiment of the present invention, the metal surface flame-retardant coating layer may be formed by using the metal surface protective coating composition comprising cleaning the metal surface with water and a detergent in step S1), and then coating the surface with a coating composition. Lt; / RTI >
본 발명의 도료 조성물을 이용한 코팅 층 형성 방법은 금속 등의 표면에 상기 도료 조성물을 함침 또는 코팅한 후 건조하여 제조할 수 있으며, 건조 및 경화는 -10 내지 40℃ 가열한 후 건조 또는 경화하여 코팅하는 것을 포함하는 금속표면 보호용 도료 조성물을 이용한 금속표면 방염 코팅 층 형성 방법일 수 있다.The coating layer forming method using the coating composition of the present invention can be prepared by impregnating or coating the coating composition on the surface of a metal or the like, followed by drying. The drying and curing are performed by heating or drying at -10 to 40 캜, And a method for forming a metal surface flame-retardant coating layer using the metal surface protective coating composition.
또한 코팅 과정 또는 함침 과정에서 코팅 층은 균열 등의 결함이 발생할 수 있으므로, 1회 이상의 코팅, 건조 또는 경화 단계를 가질 수 있다. 하지만 이에 한정되는 것은 아니다.Also, the coating layer may have cracks or other defects during the coating process or the impregnation process, and thus may have one or more coating, drying or curing steps. However, the present invention is not limited thereto.
본 발명의 일 실시예에 있어서, 도료 조성물은 상기와 같은 균열을 방지하기 위하여 규산나튜륨 100 중량부에 대하여 고분자 물질 1 내지 30 중량부를 더 포함할 수 있다. 이 때 상기 고분자 물질은 딱히 제한되지 않으며, 상세하게는 코팅 후 건조하였을 때 더 이상 물에 용해되지 않는 성분이라면 제한되지 않는다. In one embodiment of the present invention, the coating composition may further comprise 1 to 30 parts by weight of a polymeric material based on 100 parts by weight of natrium silicate to prevent the cracks. In this case, the polymer material is not particularly limited, and is not particularly limited as long as it is a component that is no longer soluble in water when dried after coating.
또한 본 발명의 일 실시예에 있어서, 상기 물을 유기용제로 대체하여 코팅 용액을 제조하는 방법을 포함할 수 있다. 상기 유기용제는 통상적으로 비수용성의 상기 고분자 물질을 용해할 수 있다.Also, in one embodiment of the present invention, a method of preparing a coating solution by replacing the water with an organic solvent may be included. The organic solvent can dissolve the non-water-soluble polymer material.
본 발명의 일 실시예에 있어서, 상기 아민계 실란 화합물은 분자량이 20 내지 2000의 수용성 성분 또는 유용성 성분을 모두 사용될 수 있으며, 예를 들면, 3-아미노프로필트리알콕시실란(3-aminopropyl trialkoxysilane) 등의 다양한 것이 있으므로 이에 한정되지 않으며, 당업자에게는 통상적으로 잘 알려져 있으므로 더 이상의 기재는 생략한다.In one embodiment of the present invention, the amine-based silane compound may be a water-soluble or oil-soluble component having a molecular weight of 20 to 2000, for example, 3-aminopropyl trialkoxysilane There is no limitation to this, and it is well known to those skilled in the art that further description will be omitted.
본 발명의 일 실시예에 있어서, 에폭시 실란 화합물은 하나 이상의 에폭시기를 가지는 실란 화합물이라면 제한되지 않지만, 상기 에폭시기는 상기 아미노기와 결합하여 가교되는 성질을 가지기도 하므로, 코팅 층을 더욱 단단히 잡아주는 역할을 한다. 본 발명의 에폭시계 실란 화합물은 분자량이 50 내지 5000의 것이라면 제한하지 않지만, 예를 들면, 2-(3,4-에폭시시클로헥실)에틸트리메틸실란(2 - (3,4-epoxycyclohexyl) ethyl trimethylsilane), 3-글리시딜프로필메틸디메톡시실란(3-glycidyl methyl dimethoxy silane) 등의 다양한 것이 있으므로 더 이상의 기재를 생략한다.In one embodiment of the present invention, the epoxy silane compound is not limited as long as it is a silane compound having at least one epoxy group, but since the epoxy group has a property of binding with the amino group and bridging with the amino group, do. The epoxy silane compound of the present invention is not limited as long as it has a molecular weight of 50 to 5000. For example, 2- (3,4-epoxycyclohexyl) ethyl trimethylsilane, 2- (3,4-epoxycyclohexyl) , 3-glycidyl methyl dimethoxy silane, and the like, so that further description is omitted.
본 발명의 일 실시예에 있어서, 상기 팽창성 저융점 유리는 크게 제한되지 않지만, 예를 들면, 5%의 붕소 화합물이 있으며, 구체적으로는 입경이 0.1 내지 10 의 크기의 붕규산 유리 등이 있으며, 이러한 물질은 가열에 의해 팽창하는 특징이 있어 우수한 방염 특성을 유지하는 역할을 한다.In one embodiment of the present invention, the inflatable low-melting glass is not particularly limited, but for example, there is a boron compound of 5%, specifically borosilicate glass having a particle size of 0.1 to 10, The material has a characteristic of expanding by heating and plays a role of maintaining an excellent flame retarding property.
본 발명의 일 실시예에 있어서, 아크릴에멀젼은 수성이나 유성 모두 사용 가능하며, 이는 코팅 용액이 수용성인지 유용성인지의 여부에 따라서 결정하여 사용할 수 있다.In one embodiment of the present invention, the acrylic emulsion can be used both aqueous and oily, and can be used depending on whether the coating solution is water-soluble or usable.
본 발명의 일 실시예에 있어서, 방연제로는 다공성 금속산화물로서, 예컨대 아연보레이트, 아연스타네이트, 수화알루미늄 및 기타 MgO, Al2O3 및 제올라이트 등의 각종 다공성 세라믹을 예시할 수 있다.In one embodiment of the present invention, examples of the flame retardant include various porous ceramics such as zinc borate, zinc stannate, aluminum hydrate and other MgO, Al 2 O 3 and zeolite as porous metal oxides.
본 발명의 일 실시예에 있어서, 발수제는 지방산 알코올로서 C12 내지 C30의 지방산 알코올이나, 폴리실록산 등의 것을 사용할 수 있으며, 이 분야에 공지된 것이라면 제한되지 않는다.In one embodiment of the present invention, the water-repellent agent may be a fatty acid alcohol of C12 to C30, a polysiloxane or the like as the fatty alcohol, and is not limited as long as it is known in the art.
본 발명의 일 실시예에 있어서, 고화방지제는 이 기술분야에 채택되는 것이라면 제한되지 않는다. 예컨대 지방산금속염, 폴리덱스트로즈(Polydextrose) 및 덱스트린(Dextrin) 등의 화합물이 사용될 수 있지만 이에 한정되는 것은 아니다.
In one embodiment of the present invention, the anti-static agent is not limited as long as it is adopted in this technical field. For example, compounds such as fatty acid metal salts, polydextrose, and dextrin may be used, but are not limited thereto.
본 발명의 도료 조성물을 금속 등의 표면에 코팅하여 코팅 층을 형성하면 불 및 열로부터의 영향을 최소화하여 표면을 보호할 수 있으며, 건축 등의 자재에 사용하면 방염 특성을 갖는 건축 자재로 활용할 수 있는 장점이 있다.When the coating composition of the present invention is coated on the surface of a metal or the like to form a coating layer, the surface can be protected by minimizing the influence from fire and heat. When used for materials such as construction, There is an advantage.
또한 본 발명의 도료 조성물은 방염 및 내열 특성과 함께 방수성 및 방식성을 갖는 장점이 있다.
Further, the coating composition of the present invention is advantageous in that it has water repellency and anticorrosion properties together with flame retardancy and heat resistance.
이하 첨부한 도면들을 참조하여 본 발명의 금속표면 보호용 팽창성 방염 도료 조성물을 상세히 설명한다. 다음에 소개되는 도면들은 당업자에게 본 발명의 사상이 충분히 전달될 수 있도록 하기 위해 예로서 제공되는 것이다. 따라서 본 발명은 이하 제시되는 도면들에 한정되지 않고 다른 형태로 구체화될 수도 있으며, 이하 제시되는 도면들은 본 발명의 사상을 명확히 하기 위해 과장되어 도시될 수 있다. 이때, 사용되는 기술 용어 및 과학 용어에 있어서 다른 정의가 없다면, 이 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 통상적으로 이해하고 있는 의미를 가지며, 하기의 설명 및 첨부 도면에서 본 발명의 요지를 불필요하게 흐릴 수 있는 공지 기능 및 구성에 대한 설명은 생략한다.
Hereinafter, the present invention will be described in detail with reference to the accompanying drawings. The following drawings are provided by way of example so that those skilled in the art can fully understand the spirit of the present invention. Therefore, the present invention is not limited to the following drawings, but may be embodied in other forms, and the drawings presented below may be exaggerated in order to clarify the spirit of the present invention. Hereinafter, the technical and scientific terms used herein will be understood by those skilled in the art without departing from the scope of the present invention. Descriptions of known functions and configurations that may be unnecessarily blurred are omitted.
이하, 실시예 및 실험적으로 입증하기 위한 결과에 대하여 자세히 설명한다.
Hereinafter, examples and experimental results will be described in detail.
(실시예 1)(Example 1)
규산나트륨(고형분 35%)의 수용액 100 중량부, 입경 3 ㎛의 붕규산계 저용점 유리 5 중량부, 3-글리시딜프로필메틸디메톡시실란 5 중량부, 3-아미노프로필트리알콕시실란 5 중량부를 혼합하고 1시간 동안 교반하여 도료 조성물을 제조하였다.100 parts by weight of an aqueous solution of sodium silicate (solid content 35%), 5 parts by weight of a borosilicate low-melting point glass having a particle diameter of 3 占 퐉, 5 parts by weight of 3-glycidylpropylmethyldimethoxysilane and 5 parts by weight of 3-aminopropyltrialkoxysilane And the mixture was stirred for 1 hour to prepare a coating composition.
그리고 상기 도료 조성물을 두께 1 mm 주철 표면에 코팅한 후, 코팅 층을 200℃에서 20 분 동안 건조하였다. 그 다음 5 시간 동안 상온에서 경화하였다. 적정 두께에 도달할 때까지 코팅 및 경화를 한 번 더 반복하여 주철에 코팅 층을 형성하였다. 상기 주철의 표면 상태는 매우 균일하고 매끄러웠다.The coating composition was coated on a 1 mm thick cast iron surface and then the coating layer was dried at 200 ° C for 20 minutes. And then cured at room temperature for 5 hours. The coating and curing were repeated one more time until a suitable thickness was reached to form a coating layer on the cast iron. The surface state of the cast iron was very uniform and smooth.
(실시예 2)(Example 2)
실시예 1에서 중량평균분자량 23000의 폴리디메틸실록산(Polydimethylsiloxane) 3 중량부를 투입한 것을 제외하고는 동일하게 실시하였다.Except that 3 parts by weight of polydimethylsiloxane having a weight average molecular weight of 23,000 was added in Example 1.
(비교예 1)(Comparative Example 1)
상기 규산나트륨 및 상기 팽창성 유리를 혼합하지 않은 것을 제외하고, 실시예 1과 동일하게 실시하였다.
The same operation as in Example 1 was carried out except that the sodium silicate and the inflatable glass were not mixed.
<실험 및 분석 결과><Experiments and Analysis Results>
1. 실험방법1. Experimental Method
실시예 1, 실시예 2, 및 비교예 1에 따라 제조된 주철 표면을 950℃에서 2 시간 동안 토치램프를 이용하여 열에 노출시켰다. 노출이 끝나고 바로 30 초 후에 상기 주철 뒷면의 온도를 측정하였다.(평가방법 : KOFEIS1001)
The cast iron surface prepared according to Example 1, Example 2, and Comparative Example 1 was exposed to heat using a torch lamp at 950 캜 for 2 hours. The temperature of the rear surface of the cast iron was measured 30 seconds after the end of exposure. (Evaluation method: KOFEIS1001)
2. 분석 결과2. Analysis results
실시예 1에 따른 도료 조성물로 코팅된 주철 표면의 코팅 층은 0.09 mm이였으며, 노출이 끝나고 바로 30 초 후의 상기 주철 뒷면의 온도는 약 60℃로 측정되었다.The coating layer on the cast iron surface coated with the coating composition according to Example 1 was 0.09 mm, and the temperature of the rear surface of the cast iron after 30 seconds from the end of exposure was measured to be about 60 캜.
실시예 2에 따른 도료 조성물로 코팅된 주철 표면의 코팅 층은 0.10 mm이였으며, 노출이 끝나고 바로 30 초 후의 상기 주철 뒷면의 온도는 약 55℃로 측정되었다.The coating layer on the surface of the cast iron coated with the coating composition according to Example 2 was 0.10 mm and the temperature of the rear surface of the cast iron after 30 seconds from the end of exposure was measured to be about 55 캜.
비교예 1에 따른 도료 조성물로 코팅된 주철 표면의 코팅 층은 0.08 mm이였으며, 노출이 끝나고 바로 30 초 후의 상기 주철 뒷면의 온도는 약 900℃ 이상으로 측정이 어려울 정도였다.
The coating layer on the surface of the cast iron coated with the coating composition of Comparative Example 1 was 0.08 mm and the temperature of the back surface of the cast iron after 30 seconds after the exposure was about 900 ° C or more was difficult to measure.
이상과 같이 본 발명에서는 특정된 사항들과 한정된 실시예 및 도면에 의해 설명되었으나 이는 본 발명의 보다 전반적인 이해를 돕기 위해서 제공된 것일 뿐, 본 발명은 상기의 실시예에 한정되는 것은 아니며, 본 발명이 속하는 분야에서 통상의 지식을 가진 자라면 이러한 기재로부터 다양한 수정 및 변형이 가능하다. While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed embodiments, but, on the contrary, Those skilled in the art will recognize that many modifications and variations are possible in light of the above teachings.
또한 본 발명의 사상은 설명된 실시예에 국한되어 정해져서는 안 되며, 후술하는 특허청구범위뿐 아니라 이 특허청구범위와 균등하거나 등가적 변형이 있는 모든 것들은 본 발명 사상의 범주에 속한다고 할 것이다.It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory and are intended to provide further explanation of the invention as claimed.
Claims (10)
상기 방염 도료 조성물은 방연제 및 발수제 중에서 선택된 하나 또는 두 성분을 더 포함하는 방염 도료 조성물.The method according to claim 1,
Wherein the flame retardant coating composition further comprises one or two components selected from flame retardants and water repellents.
상기 방염 도료 조성물은 수성에멀젼계를 더 포함하는 방염 도료 조성물.The method according to claim 1,
Wherein the flame retardant coating composition further comprises an aqueous emulsion system.
상기 방염 도료 조성물은 수성에멀젼계를 더 포함하는 방염 도료 조성물.3. The method of claim 2,
Wherein the flame retardant coating composition further comprises an aqueous emulsion system.
상기 방염 도료 조성물은 점도조절제, 고화방지제, 및 발수제에서 선택되는 하나 또는 둘 이상의 성분을 더 포함하는 방염 도료 조성물.The method according to any one of claims 1 to 4,
Wherein the flame retardant coating composition further comprises one or two or more components selected from a viscosity adjusting agent, an antifoaming agent, and a water repellent agent.
상기 방염 도료 조성물은 상기 규산나트륨 100 중량부에 대하여, 팽창성 유리 0.5 내지 100 중량부, 용매 10 내지 300 중량부, 아민계 실란 0.1 내지 10 중량부, 에폭시계 실란 0.1 내지 10 중량부, 고형분 10 내지 50 중량부를 포함하는 아크릴계 에멀젼 0.5 내지 10 중량부, 방연제 0.1 내지 10 중량부, 발수제 0.1 내지 10 중량부, 점도조절제 0.1 내지 10 중량부, 및 고형화방지제 0.1 내지 10 중량부에서 선택되는 하나 또는 둘 이상의 성분을 포함하는 방염 도료 조성물.6. The method of claim 5,
Wherein the flame-retardant coating composition contains 0.5 to 100 parts by weight of an expandable glass, 10 to 300 parts by weight of a solvent, 0.1 to 10 parts by weight of an amine-based silane, 0.1 to 10 parts by weight of an epoxy-based silane, 0.5 to 10 parts by weight of an acrylic emulsion containing 50 to 50 parts by weight of an antistatic agent, 0.1 to 10 parts by weight of a flameproof agent, 0.1 to 10 parts by weight of a water repellent agent, 0.1 to 10 parts by weight of a viscosity modifier, and 0.1 to 10 parts by weight of an anti- Wherein the composition comprises the above components.
S2) 상기 코팅 면을 건조 및 경화하는 단계;
를 포함하는 금속표면 방염 코팅 층 형성 방법.S1) coating a surface of a metal material with a flame-retardant flame retardant coating composition for metal surface protection comprising sodium silicate, expandable glass, amine-based silane and epoxy silane; And
S2) drying and curing the coated surface;
Wherein the flame-retardant coating layer is formed on the metal surface.
상기 S1) 및 S2) 단계를 2회 또는 그 이상 반복하는 단계를 포함하는 금속표면 방염 코팅 층 형성 방법.8. The method of claim 7,
And repeating the steps S1) and S2) two or more times.
상기 금속표면을 물과 세제로 세정하고, 이어서 상기 표면을 방염 도료 조성물로 코팅하는 것을 포함하는 금속표면 방염 코팅 층 형성 방법. 8. The method of claim 7,
Cleaning the metal surface with water and a detergent, and then coating the surface with a flame retardant coating composition.
상기 건조 및 경화는 -10 내지 40℃의 온도에서 수행되는 것을 포함하는 금속표면 방염 코팅 층 형성 방법.8. The method of claim 7,
Wherein the drying and curing is carried out at a temperature of -10 to < RTI ID = 0.0 > 40 C. < / RTI >