KR20160043441A - plaster composition for construction and manufacturing method thereof - Google Patents

plaster composition for construction and manufacturing method thereof Download PDF

Info

Publication number
KR20160043441A
KR20160043441A KR1020140137826A KR20140137826A KR20160043441A KR 20160043441 A KR20160043441 A KR 20160043441A KR 1020140137826 A KR1020140137826 A KR 1020140137826A KR 20140137826 A KR20140137826 A KR 20140137826A KR 20160043441 A KR20160043441 A KR 20160043441A
Authority
KR
South Korea
Prior art keywords
salt
weight
parts
mixed
binder
Prior art date
Application number
KR1020140137826A
Other languages
Korean (ko)
Other versions
KR101706344B1 (en
Inventor
고계석
Original Assignee
고계석
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 고계석 filed Critical 고계석
Priority to KR1020140137826A priority Critical patent/KR101706344B1/en
Publication of KR20160043441A publication Critical patent/KR20160043441A/en
Application granted granted Critical
Publication of KR101706344B1 publication Critical patent/KR101706344B1/en

Abstract

The present invention relates to a plaster composition comprising bay salt as a main component for construction, and a manufacturing method thereof. More particularly, the present invention relates to a plaster composition which comprises bay salt as a main component and a fermented mixture material as a binder, and to a manufacturing method thereof, wherein the fermented mixture material is prepared by mixing and fermenting aloe and kelp. The plaster composition comprising bay salt as a main component is prepared by mixing 10 to 50 parts by weight of a binder in 100 parts by weight of bay salt, wherein the binder is a fermented mixture material prepared by mixing and fermenting aloe and kelp.

Description

천일염을 주성분으로 하는 건축용 미장 조성물과 이의 제조방법{plaster composition for construction and manufacturing method thereof}BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a plaster composition for architectural use,

본 발명은 천일염을 주성분으로 하는 건축용 미장 조성물과 이의 제조방법에 관한 것으로서, 더욱 상세하게는 천일염염을 주성분으로 하고 알로에와 다시마를 혼합하여 발효시킨 혼합발효물을 바인더로 한 건축용 미장 조성물과 이의 제조방법에 관한 것이다. More particularly, the present invention relates to a composition for architectural use, which comprises a mixed fermented product obtained by fermenting aloe and kelp by mixing a salt of chalcone salt as a main component and a preparation thereof ≪ / RTI >

최근 각종 시멘트를 주원료로 사용하는 건축문화와 아름다운 실내장식을 이루기 위해 화공약품으로 가공된 건축 내외장재는 시간이 지남에 따라 각종유해물질과 새집증후군을 유발하고 있음이 알려지고 있다. Recently, it has been known that architectural interior and exterior materials processed with chemical agents in order to achieve architectural culture and beautiful interior decoration using various cements as main materials cause various harmful substances and sick house syndrome over time.

특히 시멘트는 재활용이 되지 않으며 시멘트의 유해물질은 인체에 치명적인 위해를 줄 수 있으며, 포름알데히드, 니켈, 라돈, 크롬 등의 중금속이 포함되어 있으며 특히 크롬은 호흡기가 아닌 인체의 피부에 직접 파고들어 피부암 등의 질환을 일으키며 가장 치명적인 위해를 줄 수 있는 중금속임이 밝혀지고 있다. 그로 인하여 환경친화적인 건축물 구축재, 내외장재가 요구되고 있다. In particular, cement is not recycled, and harmful substances in cement can cause fatal injuries to the human body. It contains heavy metals such as formaldehyde, nickel, radon and chromium. In particular, chromium penetrates directly into the skin of the body, And it is found that it is the heavy metal that can give the most fatal damage. As a result, environment-friendly building materials and interior and exterior materials are required.

자연의 질감(느낌)을 줄 수 있는 재료 중 목재는 자원의 고갈로 인하여 양질의 자재를 대량으로 구입하기 어려우며, 그로 인하여 목재 공급의 한계를 합성수지재 제품으로 제작하여 인위적인 분위기를 연출하고 있는 실정이다. 그리고 석재는 자연 파괴의 한계로 개발을 제한하여 수요 충족을 만족시키지 못해 수입에 의존하고 있다. 따라서 친환경 건축자재인 황토가 주목받고 있다. Among the materials that can give the natural texture (feel), it is difficult to purchase a large quantity of high quality materials due to depletion of resources, and therefore the artificial atmosphere is produced by making the limit of the supply of wood as a synthetic resin product . And stone is limited by natural destruction and is dependent on import because it can not satisfy the demand by limiting the development. Hwangto, an eco-friendly building material, is attracting attention.

황토는 여러 가지 효능을 가지며, 대표적으로 원적외선 방출과 습도 조절 능력 그리고 정화능력을 들 수 있다. 황토의 원적외선은 인체의 신진대사를 원활히 하여 혈액순환에 효과가 좋고 살균 효과와 독성 제거 능력이 뛰어나며 유해 물질을 중화시키는데 탁월하고 황토의 특유에 벌집 구조체로 정화능력 또한 뛰어나 오염된 호수의 녹조현상이나 바다의 기름 유출 때 바다와 강 및 호수를 정화하는 최고의 자연 치료제로 그 효능이 인정되고 있다.Horticulture has various effects, such as far-infrared emission, humidity control ability and purification ability. The far-infrared rays of Hwangto are excellent for the blood circulation by facilitating the metabolism of the human body, excellent in disinfecting effect and toxic removal ability, excellent in neutralizing harmful substances, and excellent in purification ability by honeycomb structure specific to loess, It is recognized as the best natural remedy to cleanse the sea, rivers and lakes when sea oil spills out.

이러한 황토의 우수한 효능을 바탕으로 황토를 주성분으로 하는 황토 모르타르가 건축용 미장재로 널리 사용되고 있다. Based on the excellent efficacy of the loess, the loess mortar containing loess as the main ingredient is widely used as a building finishing material.

최근에는 황토 모르타르의 기능성을 높이기 위해 다양한 첨가제를 첨가하고 있다. 대한민국 공개특허 제 10-2012-0043186호에는 내균열성이 우수한 황토몰탈 조성물이 개시되어 있다. In recent years, various additives have been added to improve the functionality of the mortar. Korean Patent Laid-Open No. 10-2012-0043186 discloses an ocher mortar composition excellent in crack resistance.

상기 황토몰탈 조성물은 황토분말 28~33중량%, 규사 48~53 중량%, 세라믹 8~13중량%, 탄산칼슘 4~6중량%, 생석회 4~6중량%, 천연소금 1~2중량%를 교반/혼합하여 구성된다. The loess mortar composition comprises 28 to 33 wt% of loess powder, 48 to 53 wt% of silica, 8 to 13 wt% of ceramic, 4 to 6 wt% of calcium carbonate, 4 to 6 wt% of burnt lime and 1 to 2 wt% Followed by stirring / mixing.

상기 황토몰탈 조성물은 황토와 규사를 주성분으로하고, 기능성을 위해 세라믹과 천연소금이 소량 첨가된다. 첨가되는 소금은 습도조절, 탈취, 원적외선 방사 등의 기능을 갖는다.The above-described loess mortar composition contains loess and silica as a main component, and ceramic and natural salt are added in small amounts for the sake of functionality. The added salt has functions such as humidity control, deodorization, and far-infrared radiation.

하지만, 종래의 모르타르는 위와 같은 소금의 유익한 기능성에도 불구하고 극히 소량으로만 첨가되는 실정이어서 소금의 효과를 기대하기가 어렵다. 이는 소금을 다량으로 첨가하는 경우 바인더 역할을 하는 황토의 함량이 낮아져 점착성이 저하되어 모르타르의 제 기능을 발휘할 수 없기 때문이다. However, the conventional mortar is added only in a very small amount in spite of the beneficial function of the above-mentioned salt, and it is difficult to expect the effect of the salt. This is because when the salt is added in a large amount, the content of the yellow clay which acts as a binder is lowered and the adhesiveness is lowered, so that the function of the mortar can not be exhibited.

대한민국 공개특허 제 10-2012-0043186호: 내균열성이 우수한 황토몰탈 조성물Korean Patent Laid-Open No. 10-2012-0043186: Yellow loam mortar composition excellent in crack resistance

본 발명은 상기의 문제점을 개선하고자 창출된 것으로서, 알로에와 다시마를 혼합하여 발효시킨 혼합발효물을 바인더로 사용하여 천일염의 함량을 크게 증대시킨 건축용 미장 조성물과 이의 제조방법을 제공하는 데 그 목적이 있다. The present invention has been made to overcome the above problems, and it is an object of the present invention to provide a plaster composition for architectural use and a method for manufacturing the same, wherein a content of the sun salt is greatly increased by using a mixed fermented product obtained by fermenting aloe and kelp have.

상기의 목적을 달성하기 위한 본 발명의 천일염을 주성분으로 하는 건축용 미장 조성물은 천일염 100중량부에 대하여 천연 바인더 10 내지 50중량부를 혼합하여 조성되며, 상기 바인더는 알로에와 다시마를 혼합하여 발효시킨 혼합발효물인 것을 특징으로 한다. In order to accomplish the above object, the present invention provides a composition for architectural use, the main component being a mixture of 100 parts by weight of sun-salt and 10-50 parts by weight of a natural binder. The binder is mixed fermented by mixing aloe and kelp Water.

상기 천일염은 결정 또는 입자 형태로 상기 바인더 중에 분산되어 있는 것을 특징으로 한다. And the silver salt is dispersed in the binder in the form of crystals or particles.

황토 또는 숯을 더 혼합하여 조성된 것을 특징으로 한다. And further comprises loess or charcoal.

상기 혼합발효물은 유자 또는 탱자를 더 혼합하여 발효시킨 것을 특징으로 한다. The mixed fermented product is characterized in that citron or tangerine is further mixed and fermented.

그리고 상기의 목적을 달성하기 위한 본 발명의 천일염을 주성분으로 하는 건축용 미장 조성물의 제조방법은 알로에와 다시마를 혼합한 후 발효시켜 혼합발효물을 수득하는 혼합발효물준비단계와; 천일염 100중량부에 대하여 상기 혼합발효물 10 내지 50중량부를 혼합하는 혼합단계;를 포함하는 것을 특징으로 한다. In order to accomplish the above object, the present invention provides a method for preparing a composition for architectural use based on a salt of sunflower, comprising: preparing a mixed fermented product by mixing aloe and kelp and then fermenting the mixed fermented product; And mixing 10 to 50 parts by weight of the mixed fermentation product with 100 parts by weight of the salt.

상기 천일염은 열을 가해 구운 후 분쇄한 입자인 것을 특징으로 한다. The salt of the present invention is characterized in that it is pulverized by heating and baking.

상술한 바와 같이 본 발명에 의하면 알로에와 다시마를 혼합하여 발효시킨 혼합발효물을 바인더로 사용함으로써 천일염을 주성분으로 한 건축용 미장 조성물을 제공할 수 있다. As described above, according to the present invention, it is possible to provide a plaster composition for architectural use based on a sun-salt by using a mixed fermented product obtained by fermenting aloe and kelp as a binder.

본 발명의 건축용 미장 조성물은 천연의 재료만을 이용하므로 인체나 주거환경에 해롭지 않을뿐더러 천일염과 천연 바인더가 갖는 다양한 기능에 의해 주거환경을 개선시킨다. Since the architectural laundry composition of the present invention uses only natural materials, it is not harmful to the human body or the residential environment, and also improves the residential environment by various functions of sun-dried salt and natural binder.

도 1은 본 발명의 일 실시 예에 따른 건축용 미장 조성물의 모습을 나타낸 사진이고,
도 2는 본 발명의 다른 실시 예에 따른 건축용 미장 조성물의 모습을 나타낸 사진이고,
도 3은 도 1 및 도 2의 건축용 미장 조성물을 벽면에 발랐을 때의 모습을 나타낸 사진이다. BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a photograph showing a composition of a building plaster according to an embodiment of the present invention,
FIG. 2 is a photograph showing the appearance of a building plaster composition according to another embodiment of the present invention,
FIG. 3 is a photograph showing a state in which the plaster composition for architectural use of FIGS. 1 and 2 is applied on a wall surface.

이하, 첨부된 도면을 참조하면서 본 발명의 바람직한 실시 예에 따른 건축용 미장 조성물과 이의 제조방법에 대하여 구체적으로 설명한다. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will now be described more fully with reference to the accompanying drawings, in which preferred embodiments of the present invention are shown.

본 발명의 일 실시 예에 따른 건축용 미장 조성물은 천일염과 바인더를 함유한다. 가령, 천일염 100중량부에 대하여 바인더 10 내지 50중량부를 혼합하여 조성될 수 있다. A plaster composition for architectural use according to an embodiment of the present invention contains a silver salt and a binder. For example, 10 to 50 parts by weight of the binder may be mixed with 100 parts by weight of the salt of the sun.

천일염은 바닷물을 햇볕과 바람으로 수분을 증발시켜 염전에서 얻은 소금으로서, 염전에서 얻은 결정 형태 그대로 사용할 수 있다. 바람직하게, 천일염에 함유된 불순물을 태워서 제거하기 위해 천일염을 열을 가해 고온으로 구워서 사용한다. 가령, 천일염을 400 내지 800℃에서 4 내지 10시간 정도 구워 유기 불순물을 제거하고, 결정 내부에 함유된 수분을 증발시킨다. 이와 같이 굽는 과정을 통해 천일염의 색상을 더욱 하얗게 만들 수 있다. 또한, 천일염의 원적외선 방사량을 높일 수 있는 장점을 갖는다. Sun-salt is a salt obtained by evaporating water from sea water by sunshine and wind, and can be used as a crystal form obtained from a salt bath. Preferably, the sun-salt is heated and baked at a high temperature to remove impurities contained in the sun-salt. For example, the salt is baked at 400 to 800 ° C for about 4 to 10 hours to remove organic impurities and evaporate water contained in the crystals. In this way, the color of the sun salt can be whitened through the baking process. It also has the advantage of increasing the far-infrared radiation dose of sun-salt.

구운 천일염은 분쇄하여 일정한 크기의 입자 형태로 이용한다. 예를 들어 100 내지 400메쉬 입도 크기로 분쇄할 수 있다. Grilled sun-dried salt is crushed and used in the form of regular sized particles. For example, 100 to 400 mesh size.

바인더는 천일염 100중량부에 대하여 10 내지 50중량부를 혼합한다. 본 발명의 건축용 미장 조성물이 천일염과 바인더로 조성된 경우 천일염의 함량은 50 내지 90중량% 이상이다. 이와 같이 본 발명은 천일염이 주성분이다. The binder is mixed with 10 to 50 parts by weight per 100 parts by weight of the salt of the sun. When the architectural plaster composition of the present invention is composed of a silver salt and a binder, the content of the silver salt is 50 to 90% by weight or more. As described above, the present invention is mainly composed of silver salt.

바인더는 천일염의 입자들을 결합시키는 역할을 하는 것으로서, 본 발명에서는 천연의 재료를 가공하여 얻은 천연 바인더를 이용한다. The binder serves to bind the particles of the sun-salt, and in the present invention, a natural binder obtained by processing a natural material is used.

본 발명에 적용될 수 있는 바인더의 일 예로 알로에와 다시마를 혼합하여 발효시킨 혼합발효물이다. 이러한 혼합발효물은 밀가루 풀과 같이 페이스트(paste) 형태로 얻어진다. An example of a binder applicable to the present invention is a mixed fermented product obtained by mixing aloe and kelp. These mixed fermented products are obtained in the form of a paste such as wheat flour paste.

알로에와 다시마는 끈끈한 점액상 물질을 함유하고 있다. 따라서 알로에와 다시마를 발효시켜 얻는 페이스트 형태의 혼합발효물은 바인더로서 충분한 결합력을 갖는다. Aloe and kelp contain a sticky liquid substance. Therefore, the paste - type mixed fermented product obtained by fermenting aloe and kelp has a sufficient binding force as a binder.

그리고 혼합발효물은 바인더로서 기능 외에도 항균이나 방향 효과 기능을 더하기 위해 유자 또는 탱자를 더 혼합하여 발효시켜 얻을 수 있다. 즉, 알로에와 다시마에 유자 또는 탱자를 혼합한 후 발효시켜 얻는다. 유자와 탱자는 열매를 이용한다. The mixed fermented product can be obtained by fermenting a mixture of citron or tangerine in order to add antibacterial or directional function in addition to function as a binder. That is, aloe and kelp are mixed with citron or tangerine and fermented. Citron and tangerine use fruit.

천일염과 바인더는 교반기를 이용하여 골고루 혼합한다. 이를 통해 천일염이 입자 형태로 바인더 중에 균일하게 분산된 건축용 미장 조성물을 수득할 수 있다. 이러한 건축용 미장 조성물은 천일염 색상에 의해 백색을 갖는다. The salt and the binder are mixed evenly using an agitator. Whereby a sunscreen composition can be obtained which is uniformly dispersed in the binder in the form of particles of sun-salt. Such architectural plaster compositions have a white color by the sun salt color.

한편, 본 발명의 다른 실시 예로 천일염과 바인더에 천연 안료를 더 혼합하여 조성할 수 있다. 가령, 천일염 100중량부에 대하여 바인더 10 내지 50중량부, 천연 안료 5 내지 25중량부를 혼합하여 조성할 수 있다. In another embodiment of the present invention, a natural pigment may be further mixed with the sun-salt and the binder. For example, 10 to 50 parts by weight of a binder and 5 to 25 parts by weight of a natural pigment may be mixed with 100 parts by weight of a salt of the sun.

천연 안료로 황토 또는 숯을 이용한다. 황토와 숯은 분말 형태로 이용한다. 황토를 첨가한 건축용 미장 조성물의 색상은 적색을 갖는다. 그리고 숯을 첨가한 건축용 미장 조성물의 색상은 흑색을 갖는다. 황토와 숯의 함량에 따라 건축용 미장 조성물의 색상 농도를 조절할 수 있다. It uses loess or charcoal as a natural pigment. Ocher and charcoal are used in powder form. The color of the architectural pasty composition added with loess has a red color. The color of the decorative plaster composition added with charcoal is black. Depending on the content of the loess and charcoal, the color concentration of the building plaster composition can be controlled.

이하, 상술한 건축용 미장 조성물의 제조방법에 대하여 설명한다. Hereinafter, a method for manufacturing the above-mentioned building plaster composition will be described.

먼저, 바인더인 혼합발효물을 준비한다. 이를 위해 알로에와 다시마를 혼합한다. 알로에 100중량부에 대하여 다시마 50 내지 150중량부를 혼합할 수 있다. 알로에와 다시마는 생것 그대로를 재료로 이용하거나 건조분말을 재료로 이용할 수 있다. First, a mixed fermentation product as a binder is prepared. To do this, mix aloe and kelp. 50 to 150 parts by weight of sea tangle may be mixed with 100 parts by weight of aloe. Aloe and kelp can be either raw raw materials or dry powder.

알로에와 다시마를 혼합한 혼합재료 100중량부에 대하여 물 20 내지 60중량부, 설탕 40 내지 100중량부를 혼합한 후 항아리에 투입하고 20 내지 40℃에서 1 내지 5개월 동안 발효시킨다. 발효 후 체로 걸러내어 고형 잔사가 제거된 혼합발효물을 얻을 수 있다. 이와 같이 얻어진 혼합발효물은 끈끈한 점액상 물질을 함유하한 페이스트(paste) 형태를 갖는다. 20 to 60 parts by weight of water and 40 to 100 parts by weight of sugar are mixed with 100 parts by weight of a mixed material of aloe and kelp, and the mixture is put into a jar and fermented at 20 to 40 DEG C for 1 to 5 months. After the fermentation, the mixture is sieved to obtain a mixed fermented product in which the solid residue is removed. The thus obtained mixed fermented product has a paste form in which it contains a sticky point liquid substance.

상기의 발효과정은 균주가 자연적으로 접종되어 발효될 수 있다. 또한, 특정의 발효균주를 인위적으로 접종하여 발효시킬 수 있다. 접종시 발효균주로 사카로미세스 속 균주를 이용할 수 있다. 사카로미세스 속 균주로 사카로미세스 루시(Saccharomyces rouxii), 사카로미세스 세레비시아에(Saccharomyces cereviciae), 사카로미세스 오비폴미스(Saccharomyces oviformis), 사카로미세스 스테이네리(Saccharomyces steineri) 등을 들 수 있다. 발효균주는 혼합재료 100중량부에 대하여 0.05 내지 0.5중량부를 접종할 수 있다. The above-mentioned fermentation process can be fermented by inoculation of the strain naturally. In addition, specific fermentation strains can be artificially inoculated and fermented. Saccharomyces spp. Can be used as a fermenting bacteria mainly for inoculation. Saccharomyces sp. Strain Saccharomyces sp. the rouxii), Mrs. Celebi Asia as Saccharomyces (Saccharomyces cereviciae), Miss Mrs. Paul Ob as Saccharomyces (Saccharomyces oviformis), MRS stay Neri as Saccharomyces (Saccharomyces steineri ) and the like. The fermenting bacteria may be inoculated in an amount of 0.05 to 0.5 parts by weight based on 100 parts by weight of the mixed material.

한편, 혼합발효물의 다른 예로 알로에 100중량부에 대하여 다시마 50 내지 150중량부, 유자 또는 탱자 10 내지 50중량부를 혼합한 후 발효시켜 얻는다. 발효방법은 상술한 바와 동일하다. 유자와 탱자는 생것 그대로 또는 건조시켜 분쇄한 건조분말을 재료로 이용할 수 있다. On the other hand, as another example of the mixed fermented product, 50 to 150 parts by weight of kelp, 10 to 50 parts by weight of citron or tangerine are mixed with 100 parts by weight of aloe, and then fermented. The fermentation method is the same as described above. Citron and tangerine can be used as a raw material or as a dry powder which is dried and pulverized.

바인더인 혼합발효물이 준비되면 천일염과 혼합한다. When the mixed fermented material as the binder is prepared, it is mixed with the salt of the sun.

천일염은 상술한 바와 같이 열을 가해 고온으로 구운 후 분쇄하여 입자 형태로 이용할 수 있다. As described above, the sun-salt can be used in the form of particles by burning at high temperature after applying heat.

100 내지 400메쉬 입도 크기로 분쇄된 천일염 100중량부에 대하여 혼합발효물 10 내지 50중량부를 혼합하여 건축용 미장 조성물을 제조한다. 혼합시 교반기를 이용하여 골고루 혼합하는 것이 바람직하다. 10 to 50 parts by weight of the mixed fermentation product is mixed with 100 parts by weight of the sun-dried salt which has been pulverized to have a particle size of 100 to 400 mesh to prepare a composition for architectural use. It is preferable to mix them evenly using an agitator.

이하, 실시 예를 통하여 본 발명에 대해 설명하고자 한다. 다만, 하기의 실시 예는 본 발명을 구체적으로 설명하기 위한 것으로, 본 발명의 범위를 하기의 실시 예로 한정하는 것은 아니다.Hereinafter, the present invention will be described by way of examples. However, the following examples are intended to illustrate the present invention in detail, and the scope of the present invention is not limited to the following examples.

(실시예 1)(Example 1)

알로에 건조분말과 다시마 건조분말을 동일 중량비로 혼합한 혼합재료 100중량부에 대하여 물 40중량부, 설탕 70중량부를 혼합한 후 항아리에 투입하고 30℃에서 3개월 동안 자연발효시켰다. 발효 후 체로 걸러내어 고형 잔사가 제거된 혼합발효물을 얻었다. 40 parts by weight of water and 70 parts by weight of sugar were mixed with 100 parts by weight of a mixed material obtained by mixing aloe dry powder and kelp dry powder at the same weight ratio, and the mixture was put into a jar and spontaneously fermented at 30 캜 for 3 months. After fermentation, the mixture was sieved to obtain a mixed fermented product in which the solid residue was removed.

한편, 천일염을 600℃에서 8시간 동안 구운 다음 200메쉬 입도 크기로 분쇄하였다. On the other hand, the solar salt was baked at 600 DEG C for 8 hours and then pulverized into 200 mesh size.

그리고 분쇄된 천일염 100중량부에 대하여 혼합발효물 30중량부를 첨가하고 교반기를 이용하여 골고루 혼합하여 백색의 건축용 미장 조성물을 제조하였다. Then, 30 parts by weight of the mixed fermentation product was added to 100 parts by weight of the ground sun-salt, and the mixture was evenly mixed using an agitator to prepare a white building composition.

(실시예 2)(Example 2)

천일염 100중량부에 대하여 혼합발효물 30중량부, 황토 분말 15중량부를 첨가하고 교반기를 이용하여 골고루 혼합하여 붉은 색의 건축용 미장 조성물을 제조하였다. 천일염과 혼합발효물은 상기 실시예 1에 사용된 것과 동일하다. 30 parts by weight of the mixed fermentation product and 15 parts by weight of the loess powder were added to 100 parts by weight of the salt of the sun to be mixed evenly using an agitator to prepare a red architectural plaster composition. The salt and mixed fermented product were the same as those used in Example 1 above.

실시예 1과 실시예 2의 건축용 미장 조성물의 모습을 도 1 및 도 2에 각각 나타내었다. Figs. 1 and 2 show the appearance of the building plaster compositions of Examples 1 and 2, respectively.

도 1 및 도 2를 참조하면, 실시예 1의 건축용 미장 조성물은 백색을 띠고, 실시예 2의 건축용 미장 조성물은 황토에 의해 붉은 색을 띠고 있다. 1 and 2, the composition for architectural use of Example 1 is white, and the composition for architectural use of Example 2 is red by yellow clay.

그리고 실시예 1과 실시예 2의 건축용 미장 조성물을 벽면에 발랐을 때의 모습을 도 3에 나타내었다. 본 발명의 건축용 미장 조성물은 천일염을 주성분으로 하면서 높은 결합력을 가져 건축용 미장재로 충분히 이용될 수 있음을 확인하였다. Fig. 3 shows the appearance when the architectural plaster compositions of Examples 1 and 2 were applied to a wall. It was confirmed that the architectural plaster composition of the present invention can be sufficiently used as a plaster for architectural purposes because it has a high bonding force while the main component is mannitol.

이상, 본 발명은 일 실시 예를 참고로 설명되었으나 이는 예시적인 것에 불과하며, 당해 기술분야에서 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 실시 예가 가능하다는 점을 이해할 것이다. 따라서 본 발명의 진정한 보호 범위는 첨부된 청구범위에 의해서만 정해져야 할 것이다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be clearly understood that the same is by way of illustration and example only and is not to be taken by way of limitation. Accordingly, the true scope of protection of the present invention should be determined only by the appended claims.

Claims (6)

천일염 100중량부에 대하여 천연 바인더 10 내지 50중량부를 혼합하여 조성되며,
상기 바인더는 알로에와 다시마를 혼합하여 발효시킨 혼합발효물인 것을 특징으로 하는 천일염을 주성분으로 하는 건축용 미장 조성물.10 to 50 parts by weight of a natural binder is blended with 100 parts by weight of a salt of austenite,
Wherein the binder is a mixed fermented product obtained by mixing aloe and kelp and fermenting the same. 제 1항에 있어서, 상기 천일염은 입자 형태로 상기 바인더 중에 분산되어 있는 것을 특징으로 하는 천일염을 주성분으로 하는 건축용 미장 조성물.The architectural paste composition according to claim 1, wherein the salt is dispersed in the binder in the form of particles. 제 1항에 있어서, 황토 또는 숯을 더 혼합하여 조성한 것을 특징으로 하는 천일염을 주성분으로 하는 건축용 미장 조성물.The architectural paste composition according to claim 1, wherein the composition is a mixture of loess or charcoal. 제 1항에 있어서, 상기 혼합발효물은 유자 또는 탱자를 더 혼합하여 발효시킨 것을 특징으로 하는 천일염을 주성분으로 하는 건축용 미장 조성물.The composition for architectural use according to claim 1, wherein the mixed fermented product is fermented by further mixing citron or tangerine. 알로에와 다시마를 혼합한 후 발효시켜 혼합발효물을 수득하는 혼합발효물준비단계와;
천일염 100중량부에 대하여 상기 혼합발효물 10 내지 50중량부를 혼합하는 혼합단계;를 포함하는 것을 특징으로 하는 천일염을 주성분으로 하는 건축용 미장 조성물의 제조방법. Preparing a mixed fermented product by mixing aloe and kelp and then fermenting to obtain a mixed fermented product;
And mixing 10 to 50 parts by weight of the mixed fermentation product with 100 parts by weight of the salt of sunflower. 제 5항에 있어서, 상기 천일염은 열을 가해 구운 후 분쇄한 입자인 것을 특징으로 하는 천일염을 주성분으로 하는 건축용 미장 조성물의 제조방법.
[Claim 6] The method according to claim 5, wherein the salt of the salt is ground particles after being heated and pulverized.
KR1020140137826A 2014-10-13 2014-10-13 plaster composition for construction and manufacturing method thereof KR101706344B1 (en)