KR20160008299A - Method for protecting an urgent stamping out livestock landfill - Google Patents
Method for protecting an urgent stamping out livestock landfill Download PDFInfo
- Publication number
- KR20160008299A KR20160008299A KR1020140088273A KR20140088273A KR20160008299A KR 20160008299 A KR20160008299 A KR 20160008299A KR 1020140088273 A KR1020140088273 A KR 1020140088273A KR 20140088273 A KR20140088273 A KR 20140088273A KR 20160008299 A KR20160008299 A KR 20160008299A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- buried
- composition
- soil
- absorbent
- Prior art date
Abstract
Description
본 발명은 긴급 살처분 가축 매몰공법에 관한 것이다. 보다 상세하게는, 본 발명은 강 알칼리 성분의 흡수성 고화재 조성물을 가축매몰시 사용하여 유기물인 사체가 분해되면서 발생하는 슬러지 및 침출수를 흡수하고 알칼리에 의한 병원균의 살균을 유도하는 친환경적인 살처분 가축 매몰공법에 관한 것이다.The present invention relates to a livestock burial method for emergency disposal. More particularly, the present invention relates to an environmentally friendly livestock cattle that absorbs sludge and leachate generated by the decomposition of organic matter, and induces sterilization of pathogens caused by alkali, It relates to buried construction method.
최근 급속하게 그 발병이 늘고 있는 추세인 고병원성 가금 인플루엔자(A I)는 닭과 오리 등 가금류에 발생하는 바이러스성 급성 전염병으로 사람에게의 전염도 보고되고 있는 제 1종 가축전염병이며, 구제역은 소, 돼지, 염소 등과 같이 발굽이 둘로 갈라진 우제류 동물에서 발생하는 바이러스 성 급성 전염병으로 고병원성 가금 인플루엔자(A I)와 같이 제1종 가축전염병으로 지정되어 있다. 이와 같은 주요한 가축전염병이 발생할 경우 정부당국에서는 전염병의 급속한 전파를 방지하기 위하여 전염병 발생지역 및 그 인근의 동종 가축을 살처분하여 매몰하는 방법을 채택하고 있으며, 이와 관련된 대표적인 법률은 가축전염병 예방법이고 동법 시행규칙 별표5에 소각 또는 매몰기준이 규정되어 있다. (AI) is a viral acute infectious disease caused by poultry such as chickens and ducks. It is a type 1 livestock infectious disease that is reported to be transmitted to humans. , And chlorine, and is designated as a type 1 livestock infectious disease, such as the highly pathogenic poultry influenza (AI). If such a major livestock epidemic occurs, the government authorities have adopted a method of disposing and burping the same kind of livestock in the area where the epidemic disease occurred and to prevent the rapid spread of the epidemic, and the representative law related to this is the livestock epidemic prevention law, Enforcement regulations Annex 5 specifies the criteria for incineration or burial.
매몰규정에 의한 매몰방법을 단계별로 살펴보면, 매몰 구덩이를 파는 단계; 구덩이의 바닥과 벽면을 이중비닐 등 불 침투성 재료로 덮는 단계; 바닥 비닐로부터 1m 높이 이상의 흙과 5㎝이상의 생석회를 투입하고 생석회 위에 40㎝이상으로 흙을 덮은 후 2m 높이 이하로 사체를 투입하는 단계; 및 사체를 흙으로 40㎝이상 덮은 다음 5㎝ 두께 이상으로 생석회를 뿌린 후 지표면 까지 흙으로 복토를 하고 지표면에서 1.5m 이상 성토를 한 후 생석회를 마지막으로 도포하는 단계로 구성되어 있다. The burial method according to the burial regulation will be described step by step. Covering the bottom and the wall surface of the pit with an impermeable material such as double vinyl; A step of putting soil of at least 1 m in height and quicklime of at least 5 cm from the bottom vinyl, covering the soil with 40 cm or more on the burnt lime, And cover the dead body with more than 40 cm of soil, then spray the quicklime to more than 5 cm thickness, cover with earth to the surface of the earth, cover with 1.5 m or more on the surface, and finally apply the quicklime.
또한 사후관리차원으로 사체의 부패에 의한 가스발생에 따른 가스배출관의 설치, 호우 등으로 매몰지가 유실되지 않도록 비닐 등을 덮고 빗물 배수로와 집수로를 설치, 또한 필요한 경우 침출수 배출관 및 저류조의 설치 및 소독 등을 규정하고 있다.In addition, for the purpose of post-management, it is necessary to install a gas discharge pipe due to corruption of the corpse, to cover the vinyl etc. so that the buried land is not lost due to heavy rain, to install the rainwater drainage channel and the water supply channel, and to install and disinfect the drainage pipe and storage tank And so on.
그러나 이러한 규정에 의한 매몰시공에도 불구하고 가축의 사체와 함께 매몰하는 매립재가 흙이 대부분이고 약간의 생석회를 사용하도록 규정되어 있어 사체 슬러지 및 침출수가 발생할 수 밖에 없으며, 우기에 지하수위 변동의 영향이나 지반의 응력에 변화가 있을 경우 방수포가 훼손되는 경우 침출수나 슬러지가 지반으로 유실되어 지하수의 오염, 지표수의 오염 및 인근토양의 오염 등 많은 환경유해요소 가 발생할 수 있다. However, in spite of the above-mentioned regulations, landfills that are buried with the carcass of livestock are largely composed of soot and some lime is required to be used, so that the sludge and leachate are inevitably generated. In the rainy season, If there is a change in the stress of the soil, if the defoamer is damaged, leachate or sludge will be lost to the ground, which may lead to many environmental hazards such as groundwater contamination, surface water contamination and nearby soil contamination.
이러한 문제점을 해결하기 위하여 대한민국 등록특허(10-1085171)와 대한민국 공개특허(10-2012-0138009)에서는 저유동성 콘크리트를 압밀 주입하거나 특수 콘크리트를 숏크리트화 하여 매몰지 지반을 보강하는 방법을 제시하였다. 그러나 이러한 방법도 콘크리트 박스 구조체를 전면적으로 설치하는 것과 같이 매몰지반의 토질역학적 외력을 충분히 감당할 수 있을지 의문이며, 압밀에 의한 주입으로 인근지반이 강화된다 하여도 지하수 및 침출수의 영향으로 액상화 될 수 있다. In order to solve these problems, Korean Patent (10-1085171) and Korea Patent Application (10-2012-0138009) proposed a method of reinforcing a buried ground by consolidating a low fluidity concrete or shotcrete a special concrete. However, this method also doubts whether the soil mechanics external forces of the buried ground can be fully met, such as installing the concrete box structure as a whole, and even if the ground is strengthened by the consolidation, it can be liquefied under the influence of groundwater and leachate .
따라서 보다 근본적인 대책으로 발생되는 동물사체의 슬러지나 침출수를 매몰지 내에서 자체 소화하고, 전염가능성이 있는 병원균을 매몰지 내에서 차폐, 사멸시킬 수 있는 공법의 개발이 시급히 요구되고 있다.Therefore, it is urgently required to develop a method for self-extinguishing sludge or leachate of animal carcass which is generated as a fundamental measure, and to shield and kill infectious pathogens in buried ground.
본 발명은 상술한 문제점을 해결하기 위하여 안출된 것으로서, 기존의 법령에 따른 매몰지침은 준수하되, 대부분의 흙과 아주 일부의 생석회를 가축과 함께 매립하는 매립재로 사용하는 방법을 개선하여 흡수성 고화재 조성물을 가축과 함께 매몰하여 발생되는 동물사체의 슬러지나 침출수를 매몰지 내에서 자체 소화하고, 전염가능성이 있는 병원균을 매몰지 내에서 차폐, 사멸시킬 수 있는 흡수성 고화재를 이용한 살처분 가축 매몰공법을 제공하는 것이다.SUMMARY OF THE INVENTION The present invention has been made in order to solve the above-mentioned problems, and it is an object of the present invention to obviate the burial guide according to the existing laws and regulations and to improve the method of using most of soil and a part of quicklime as a landfill material to be buried with livestock, Sludge and leachate of animal carcasses generated by burial of fire composition with livestock are self-extinguished in buried ground, and the disposable livestock buried with absorbable fire that can shield and kill infectious pathogens in buried ground To provide a method.
위와 같은 기술적 과제를 해결하기 위하여 본 발명은 1) 소각 잔재 100 중량부에 대하여 코우크스 탈황 석고 5~200 중량부 및 고로슬래그 미분말 5~50 중량부를 포함하는 흡수성 고화재 조성물을 준비하는 단계; 2) 매몰 구덩이를 파는 단계; 3) 상기 매몰 구덩이의 바닥과 벽면을 두께 0.2㎜ 이상인 불침투성 재료로 덮는 단계; 4) 상기 매몰 구덩이의 바닥에 덮인 불침투성 재료 위에 상기 흡수성 고화재 조성물을 매몰대상 동물 사체 무게의 3배 이상의 양으로 포설한 후, 매몰대상 동물 사체를 투입하는 단계; 5) 상기 투입된 매몰대상 동물 사체 위에, 상기 흡수성 고화재 조성물을 매몰대상 동물 사체 무게의 1배 이상의 양으로 포설하는 단계; 및 6) 상기 5) 단계에서 포설된 흡수성 고화재 조성물 위에, 상기 흡수성 고화 조성물과 흙을 혼합하여 준비한 혼합토를 지표면에서 1.5m 이상의 높이가 되도록 복토 및 성토를 하는 단계를 포함하는 것을 특징으로 하는 흡수성 고화재 조성물을 사용한 긴급 살처분 가축 매몰 공법을 제공한다.SUMMARY OF THE INVENTION The present invention has been made in view of the above problems, and has an object to provide an absorbent hose composition which comprises: 1) preparing 5 to 200 parts by weight of cokesulfurized gypsum and 5 to 50 parts by weight of blast furnace slag powder per 100 parts by weight of incineration residue; 2) digging the burrows; 3) covering the bottom and the wall surface of the buried hole with an impermeable material having a thickness of 0.2 mm or more; 4) placing the absorbent fire-proofing composition on the impermeable material covered on the bottom of the buried hole in an amount of 3 times or more of the weight of the buried animal carcass, and then injecting the carcass of the burial animal; 5) placing the absorbent core composition on the buried animal carcass in an amount of at least 1 times the weight of the buried animal carcass; And 6) a step in which the mixed soil prepared by mixing the water absorbent solidifying composition and the soil on the waterproofing composition laid in the step 5) is covered with soil and covered so that the height of the soil is at least 1.5 m above the ground surface Provides emergency land-disposal cattle burial method using fire composition.
본 발명의 상기 흡수성 고화재 조성물에 있어서, 흡수성 분체로는 상기 언급한 재료들 이외에 제지슬러지 소각재, 시멘트 바이패스 더스트 등의 부산물로 발생하는 흡수성 분체들이 있으나, 이들 제지슬러지 소각재, 시멘트 바이패스 더스트는 그 재료에 함유된 염소이온의 농도가 1~3%에 달할 정도로 높아 대부분이 농경지 인근인 매몰지에 사용하기에는 적합하지 않다.In the absorbent core composition of the present invention, there are absorbent powders other than the above-mentioned materials, such as paper sludge incineration ash, cement bypass dust and the like, but these paper sludge incineration ashes, cement bypass dust, The concentration of chlorine ions contained in the material is so high as to reach 1 to 3% that most of them are not suitable for use in landfills near farmland.
또한 본발명에 따른 흡수성 고화재 조성물의 상기 재료들은 pH가 11.5 이상에 달할 만큼 강알칼리 물질이다. 일반적으로 강알칼리 환경에서는 거의 모든 세균이 사멸한다고 알려져 있다. 구제역 방역이나 가금류 인플루엔자(A I)방역제로 사용되고 있는 생석회 및 생석회 적정 소독액 역시 강알칼리라는 생석회의 성분을 활용하는 것이다. In addition, the above materials of the waterproofing composition according to the present invention are strong alkali materials having a pH of 11.5 or more. It is generally known that almost all bacteria are killed in a strong alkaline environment. The quicklime and quicklime proper disinfectant which is used as an anti-foot-and-mouth disease or poultry influenza (A I) protector also uses the ingredient of quicklime called strong alkali.
또한 본 발명의 상기 흡수성 고화재 조성물에서 각 구성 성분들은 산화칼슘 함량이 높은 것이 바람직하다. 산화칼슘은 생석회의 주성분인 CaO와 동일한 작용을 한다. 즉 수분과 접촉하면 약 100 에 달하는 발열과 흡수작용을 한다. 따라서 동물의 사체에서 발생하는 슬러지 및 침출수와 이들 재료가 반응하면서 발열에 의한 멸균 및 흡수작용을 해 슬러지와 침출수가 외부로 유출되지 않고 매몰지 내에서 구속되도록 한다. Further, it is preferable that each constituent component in the above-described water absorbent core composition of the present invention has a high calcium oxide content. Calcium oxide has the same effect as CaO, which is the main component of quicklime. In other words, when it comes into contact with water, it absorbs about 100 heat and absorption. Therefore, the sludge and leachate generated from the carcass of the animal react with these materials to sterilize and absorb by the heat, so that the sludge and leachate are confined in the buried land without being leaked to the outside.
또한 본 발명의 상기 흡수성 고화재 조성물에서 각 구성 성분들은 분체의 형태인 것이 바람직하고, 비표면적이 3,500㎠/g 이상일 정도로 미립자인 것이 바람직하다. 미립자는 상당히 많은 공극을 가지고 있고, 다른 부분과 혼합되면서 그 공극이 줄어드는 작용으로 부피가 감소하는 이점이 있다. 이러한 특성은 동물의 사체가 부패하면서 발생하는 가스에 의해 매몰지가 융기하는 현상을 방지할 수 있다.In the water absorbent core composition of the present invention, each of the constituent components is preferably in the form of powder, and it is preferable that the constituent components are fine particles having a specific surface area of 3,500 cm 2 / g or more. The fine particles have a considerable number of voids and have an advantage in that the volume decreases as the void decreases while being mixed with other portions. This characteristic can prevent the phenomenon that the burnt ground is raised by the gas generated by the decay of the carcass of the animal.
본 발명에 따르면, 가축의 유행성 질병 특히 구제역이나 조류 인플루엔자의 유행시 질병의 급속한 확산을 방지하기 위하여 부득이하게 가축을 긴급 살처분하여 땅에 매몰할 경우 살처분 매몰지에서 필연적으로 발생하는 사체 슬러지, 침출수 및 기타 유해 병원균의 유출을 막고 매몰지를 환경적이나 토질역학적으로도 안전하게 보호할 수 있는 긴급살처분 가축 매몰공법을 제공하는 효과가 있다. According to the present invention, there is provided a method for preventing the spread of disease in a livestock, particularly, in the case of foot-and-mouth disease or avian influenza, in the case of cattle sludge inevitably occurring in a land- There is an effect of providing an emergency cattle livestock burial method which can prevent leakage of leachate and other harmful pathogens and safely protect the buried land in environmental and soil mechanics.
또한, 석회석을 고온에서 하소하여 생산하는 생석회의 사용을 전면 대체하여 백두대간의 무분별한 석회석 채광을 방지할 수 있으며, 생석회 성분 및 석고 성분이 다량 들어있으며, 산업부산물로 발생하는 고로슬래그, 코우크스 탈황석고, 소각잔재 등을 재활용하여 환경을 보존하는 효과도 있다.In addition, it is possible to prevent undesirable limestone mining of Baekdudaegan by completely replacing the use of quicklime which is produced by calcining limestone at high temperature. It also contains a large amount of quicklime component and gypsum component, and is used as blast furnace slag, Gypsum, incineration residues, and so on.
이하, 본 발명에 의한 흡수성 고화재 조성물을 사용한 긴급 살처분 가축 매몰공법에 대하여 구체적으로 설명한다. Hereinafter, the emergency burating cattle burial method using the waterproofing composition according to the present invention will be described in detail.
먼저, 본 발명에 의한 흡수성 고화재 조성물의 구성성분 및 작용을 설명한다.First, the constituent components and the action of the water absorbent core composition according to the present invention will be described.
본 발명에 의한 흡수성 고화재 조성물은 소각 잔재 100 중량부에 대하여 코우크스 탈황 석고 5~200 중량부(바람직하게는 50~200 중량부) 및 고로슬래그 미분말 5~50 중량부(바람직하게는 20~50 중량부)를 포함한다. The water absorbent composition according to the present invention comprises 5 to 200 parts by weight (preferably 50 to 200 parts by weight) of cokesulfurized gypsum and 5 to 50 parts by weight (preferably 20 to 50 parts by weight) of fine powder of blast furnace slag, 50 parts by weight).
상기 소각잔재는 노내 탈황 방식 석탄연소 보일러에서 발생하는 플라이애시인 것이 바람직하고, 산화칼슘 함량이 20% 이상인 고칼슘 플라이애시인 것이 특히 바람직하다. The incineration residue is preferably fly ash generated in an in-furnace desulfurization type coal combustion boiler, and particularly preferably is a high calcium fly ash having a calcium oxide content of 20% or more.
상기 고칼슘 플라이애시는 석탄에 포함된 황성분의 대기배출을 방지하기 위하여 석탄과 석회석을 혼합 연소하는 과정에서 발생된다. 이 플라이애시에 다량 함유된 산화칼슘은 물과 반응하여 흡수, 발열 하여 수산화칼슘이 되는데 이에 대한 반응식은 아래와 같다. The high-calcium fly ash is generated in a process of mixing coal and limestone to prevent the sulfur component contained in the coal from being discharged to the atmosphere. This fly ash contains a large amount of calcium oxide reacts with water to absorb and heat to become calcium hydroxide, the reaction formula is as follows.
CaO+ H2O->Ca(OH)2+15.6kcal mol-1 CaO + H 2 O-> Ca (OH) 2 + 15.6 kcal mol -1
상기 코우크스 탈황석고는 석탄계 코우크스 및 석유계 코우크스를 원료로 하는 보일러에서 노내 탈황을 위해 석회석을 혼소하는 과정에서 연료인 코우크스에 포함되어있는 황 성분과 석회석이 고온에서 탈탄산된 CaO 성분이 반응하여 생성된 분진과 같은 입자상 석고 물질로서 pH가 11.5이상의 강알칼리 물질이다. The coke desulfurization gypsum is produced by mixing a sulfur component contained in coke, which is a fuel, and a CaO component decarboxylated at high temperature, in a boiler using coal-based coke and petroleum coke as a raw material in the process of mixing limestone for desulfurization in the furnace And is a strong alkaline substance having a pH of 11.5 or higher as a particulate gypsum material such as dust produced by the reaction.
상기 코우크스 탈황석고 역시 수분과 반응하게 되면 이 석고에 포함된 CaO 성분이 발열과 흡수작용을 하게 되어 동물사체 슬러지 및 침출수를 외부로 유출되지 않도록 구속한다.When the cokes desulfurized gypsum reacts with moisture, the CaO component contained in the gypsum exotherms and absorbs the sludge so that the sludge and leachate are prevented from leaking to the outside.
또한 코우크스 탈황석고의 주성분인 황산염과 높은 pH가 황산염자극 및 pH에 따른 알칼리 자극을 고로슬래그 미분말에 가하게 되면 고로슬래그 미분말이 조기에 활성화되어 잠재 수경성 반응을 개시하여 고결강도를 발현한다. 이 탈황석고가 소각잔재 100중량부에 대하여 5~200 중량부 혼입된다. 5중량부 미만 혼입될 경우 함께 포함되는 고로슬래그 미분말을 충분히 자극하지 못하여 소정의 강도를 발현할 수 없으며, 200중량부 초과 혼입될 경우 석고의 수분접촉에 의한 자경성 때문에 너무 높은 고결강도가 발생하여 향후 매몰지를 폐쇄하고 그 토지를 재활용 하는데 장애가 될 수 있다.In addition, when sulfate, which is the main component of coke desulfurization gypsum, and high pH are added to the blast furnace slag powder by the stimulation of sulphate and alkali by pH, the blast furnace slag powder is activated early to initiate the latent hydraulic reaction to develop the cemented strength. 5 to 200 parts by weight of the desulfurized gypsum is mixed with 100 parts by weight of the incineration residue. If less than 5 parts by weight is incorporated, the blast furnace slag powder contained together can not be sufficiently stimulated to exhibit a predetermined strength, and if it is incorporated in an amount exceeding 200 parts by weight, too high cementation strength occurs due to self- In the future, it may become an obstacle to closing the burial site and recycling the land.
또한 상기 고로슬래그 미분말은 제철공정에서 발생하는 고로 수쇄 슬래그를 건조하고 분쇄하여 생산된다. 고로슬래그 미분말은 수분과 접촉하면 그 표면에 산화피막이 형성되어 스스로 경화되지는 않는 물질이다. 그러나 알칼리 및 황산염 자극에 의해 산성피막이 깨지게 되면서 경화하는 반응이 발생하는데 이를 잠재수경성의 발현이라 한다. 본 발명의 매몰지 특성상 동물의 사체에서 나오는 슬러지와 침출수를 외부로 유출되지 않도록 구속하고 외부의 토질역학적 응력변화에 대응하기 위하여는 큰 고결강도를 요구하지 않는다. 고로슬래그 미분말은 상기 소각잔재 100중량부에 대하여 5~50중량부 혼입되는데 5중량부 미만이면 잠재수경성 발현 물질이 너무 적어 소요의 강도를 발현할 수 없으며, 50중량부 초과이면 너무 높은 고결강도를 발현하여 향후 매몰지를 폐쇄하고 그 토지를 재활용 하는데 장애가 될 수 있다. 상기 고로슬래그 미분말의 분말도(비표면적)는 3,500~8,000㎠/g인 것이 바람직하고, 4,000~8,000㎠/g인 것이 더 바람직하다The blast furnace slag fine powder is produced by drying and pulverizing blast furnace slag generated in a steel making process. Blast furnace slag powder is a material that does not harden itself when an oxide film is formed on its surface when it comes into contact with water. However, as the acidic coating is broken by alkali and sulfate stimulation, a curing reaction occurs, which is referred to as latent hydration. The sludge and leachate coming from the carcass of the animal are prevented from leaking to the outside and the large cementation strength is not required in order to cope with changes in the external soil dynamic stress. The blast furnace slag powder is mixed in an amount of 5 to 50 parts by weight with respect to 100 parts by weight of the incineration residue. If the blast furnace slag powder is less than 5 parts by weight, the latent hydraulic powder is too small to exhibit the required strength. And it may become an obstacle to closing the burial site and recycling the land in the future. The powder blend (specific surface area) of the blast furnace slag powder is preferably 3,500 to 8,000 cm 2 / g, more preferably 4,000 to 8,000 cm 2 / g
이하 본 발명에 따른 매몰공법에 대하여 자세히 설명한다.Hereinafter, the buried technique according to the present invention will be described in detail.
본 발명에 따른 매몰공법은 가축전염병 예방법 시행규칙 별표 5에 따른 매몰기준을 근거로 하였으며, 매몰공정에서 사용되는 매립재인 흙과 생석회를 흡수성 고화재로 대체하여 시공하는 공법을 제시하는 것이다. 본 발명에 따른 매몰공법은 1) 소각 잔재 100 중량부에 대하여 코우크스 탈황 석고 5~200 중량부 및 고로슬래그 미분말 5~50 중량부를 포함하는 흡수성 고화재 조성물을 준비하는 단계; 2) 매몰 구덩이를 파는 단계; 3) 상기 매몰 구덩이의 바닥과 벽면을 두께 0.2㎜ 이상인 불침투성 재료로 덮는 단계; 4) 상기 매몰 구덩이의 바닥에 덮인 불침투성 재료 위에 상기 흡수성 고화재 조성물을 매몰대상 동물 사체 무게의 3배 이상의 양으로 포설한 후, 매몰대상 동물 사체를 투입하는 단계; 5) 상기 투입된 매몰대상 동물 사체 위에, 상기 흡수성 고화재 조성물을 매몰대상 동물 사체 무게의 1배 이상의 양으로 포설하는 단계; 및 6) 상기 5) 단계에서 포설된 흡수성 고화재 조성물 위에, 상기 흡수성 고화 조성물과 흙을 혼합하여 준비한 혼합토를 지표면에서 1.5m 이상의 높이가 되도록 복토 및 성토를 하는 단계를 포함하는 것을 특징으로 한다.The burial method according to the present invention is based on the burial criterion according to Table 5 of the Enforcement Regulation of Livestock Epidemic Disease Prevention Act and suggests a construction method in which the soil and quicklime used in the burial process are replaced with an absorbent fire. The burial method according to the present invention comprises the steps of 1) preparing an absorbent horticulture composition comprising 5 to 200 parts by weight of kaolin-desulfurized gypsum and 5 to 50 parts by weight of a blast furnace slag powder per 100 parts by weight of incineration residue; 2) digging the burrows; 3) covering the bottom and the wall surface of the buried hole with an impermeable material having a thickness of 0.2 mm or more; 4) placing the absorbent fire-proofing composition on the impermeable material covered on the bottom of the buried hole in an amount of 3 times or more of the weight of the buried animal carcass, and then injecting the carcass of the burial animal; 5) placing the absorbent core composition on the buried animal carcass in an amount of at least 1 times the weight of the buried animal carcass; And 6) a step in which the mixed soil prepared by mixing the water-absorbing and solidifying composition and soil on the water-repellent composition disposed in step 5) has a height of 1.5 m or more on the surface of the earth.
상기 4) 단계는, 예를 들어, 비닐을 사용하여 일정 두께 이상의 불투수층을 구성한 후(상기 '3) 단계'), 바닥으로부터 매몰대상 동물 사체 무게의 3배 이상의 흡수성 고화재 조성물을 매몰구덩이에 포설하고 그 위에 동물의 사체를 매몰하는 단계이다. 이때 동물사체 무게 3배 이상의 고화재 조성물이 포설되지 않으면 동물의 체액과 각종 유기물이 슬러지나 침출수화 되어서 사체 밖으로 이탈될 때 이를 흡수하는 충분한 고화재 량이 되지 않아 소정의 목적을 달성할 수 없다. In the step 4), for example, a water impermeable layer having a thickness of at least a certain thickness is formed by using vinyl (step 3), and then an absorbent fire retardant composition of three times or more the weight of the burial animal carcass is laid And buried the carcass of animals on it. If the fire extinguishing composition having a weight of three times or more the weight of the animal carcass is not installed, the body fluid and various organic substances of the animal can not reach the predetermined purpose because the sludge or leach water is not sufficiently absorbed when it is taken out from the body.
일반적으로 동물의 몸체는 약 70% 이상의 수분으로 구성되어 있다고 알려져 있다. 따라서 적정한 흡수성 고화재의 중량은 사체무게의 약 1.5배 이면 적당하나, 외부로 부터의 응력변화요인 등을 고려하여 안전율을 200%로 설정하였다.It is generally known that the animal body is composed of at least about 70% moisture. Therefore, it is appropriate that the weight of proper absorbent and fireproof is about 1.5 times the weight of carcass, but the safety factor is set to 200% considering factors of external stress.
또한, 상기 5) 단계는 상기 투입된 매몰대상 동물 사체 위에, 매몰대상 동물사체 무게 1배의 이상의 상기 흡수성 고화재 조성물을 매몰대상 동물 사체위에 포설하는 단계이다. 모든 물질은 위치에너지가 낮은 곳으로 이동하기 때문에 사체에서 발생한 슬러지나 침출수는 대부분 하층으로 이동하여 사체 아래쪽에 포설된 흡수성 고화재와 반응하게 되리라 예상하지만 혹시 발생할 수 있는 지표수나 지하수의 유입에 대처하기 위해 사체 무게와 동일중량의 고화재를 매몰 사체 위에 포설해야한다. In addition, the step 5) is a step of laying on the carcass of the animal subject to be buried, the carcass of the carcass of an animal to be buried at least one time by weight of the carcass. Since all the materials move to a place with low potential energy, it is expected that the sludge or leachate from the dead body will move to the lower layer and react with the absorptive solidifying fire that is placed under the carcass, but cope with the possible inflow of surface water or groundwater A fire of the same weight as the carcass weight must be laid on the buried carcass.
만일 동물 사체 동일 중량 이상의 고화재가 동물의 사체위에 포설되지 않으면 지표수나 지하수의 유입을 완전히 방지하지 못할 위험이 있다. There is a risk that the inflow of surface water or groundwater can not be completely prevented unless a fire of the same weight or more is placed on the carcass of the animal.
또한, 상기 6) 단계는 상기 5) 단계에서 포설된 흡수성 고화재 조성물 위에, 상기 흡수성 고화 조성물과 흙을 혼합하여 준비한 혼합토를 지표면에서 1.5m 이상의 높이가 되도록 복토 및 성토를 하는 단계이다. 상기 흡수성 고화재 조성물과 흙은 1:1의 중량비로 혼합되는 것이 바람직하다. In the step 6), the mixed soil prepared by mixing the water-absorbing and solidifying composition and the soil on the water-repellent composite composition laid in the step 5) is covered with soil and filler to a height of 1.5 m or more from the ground surface. It is preferable that the water absorbent composition and the soil are mixed at a weight ratio of 1: 1.
기존 공법에서는 흙을 주원료로 하여 성토하고 생석회를 뿌려 마무리하는 것으로 되어있으나, 우천이나 지표수의 유동이 있을 경우, 상부로부터의 물 유입을 예방하기 위하여 고화재와 흙을 혼합하여 투수가 어려운 특성을 가진 지반으로 개량할 필요가 있다.However, in the case of rain or surface water flow, it is difficult to mix water with high fire and soil to prevent water inflow from the upper part. It needs to be improved to the ground.
본 발명의 상기 긴급 살처분 가축 매몰 방법은 필요한 경우, 하기 A) 내지 C) 단계 중 하나 이상을 추가로 더 포함할 수 있다: A) 사체의 부패에 의한 가스발생에 따른 가스배출관의 설치하는 단계; B) 비닐 덮개, 및/또는 빗물 배수로와 집수로를 설치하는 단계, 및 C) 침출수 배출관 및 저류조를 설치하고 상기 저류조를 소독하는 단계.
The method of the present invention may further comprise at least one of the following steps A) to C), if necessary: A) the step of installing a gas discharge pipe according to the generation of gas by corruption of the corpse ; B) installing a vinyl cover, and / or a rainwater drainage and collection channel, and C) installing a drainage water discharge pipe and reservoir and disinfecting the reservoir.
본 발명에 따른 방법에 있어서 상기 흡수성 고화재 조성물의 특성을 보다 구체적으로 살펴보기 위해 다음과 같은 시험을 실시하였다.In order to examine the characteristics of the water absorbent composition in the method according to the present invention in more detail, the following tests were conducted.
먼저, 다음의 표1과 같이 생후 약 7일가량 경과한 병아리(개체당 평균 무게 60g) 시험체를 플라스틱 밀폐용기에 넣고 병아리 그 자체, 흙과 생석회를 이용한 매립 및 본 발명에 따른 고화재를 이용한 매립 시험체를 구성하고 섭씨 25도의 수조에 항온조건으로 촉진시험을 수행하였다. 이때 사용한 흡수성 고화재의 조성은 산화칼슘 함량이 43%인 고칼슘 플라이애시 100 중량부에 대하여 코우크스 탈황 석고 100 중량부 및 분말도(비표면적)가 4,000~6,000㎠/g인 고로슬래그 미분말 25 중량부를 혼합물이다. First, as shown in the following Table 1, the chicks (average weight per individual 60g) aged about 7 days after birth were placed in a plastic sealed container, and the chicks themselves, the landfill using soil and quicklime, and the landfill using the fire according to the present invention The test specimens were constructed and the accelerated test was carried out under constant temperature conditions in a water bath at 25 ° C. The composition of the water-absorbing sludge used herein was 100 parts by weight of coke-desulfurized gypsum and 100 parts by weight of high-calcium fly ash having a calcium oxide content of 43% and 25 parts by weight of blast furnace slag powder having a powdery degree (specific surface area) of 4,000 to 6,000 cm & Part is a mixture.
아래의 표 1 에서와 같이 병아리 사체만 용기에 넣어 보관한 경우 15일 부터 침출수가 발생하여 45일 경과후에는 고체와 액체가 거의 완전히 분리되었다. 반면 기존의 매몰공법에 따른 흙과 생석회를 이용하여 매립한 시료에서는 15일 경과시 까지 침출수가 어느정도 흙과 생석회에 흡수되어 침출수 발생이 없었으나, 30일 과 45일 시간이 경과할수록 침출수가 많이 발생하였으며, 매립상태에서의 침하가 상당히 발생하였다. 그러나 본 발명의 흡수성 고화재를 이용한 매립공법에 따른 시험체는 동일한 시험기간이 경과하였음에도 침출수나 지반의 침하가 발생하지 않았다. 이는 고화재속에 다량 함유되어 있는 생석회성분에 의한 흡수작용과 높은 분말도의 분체로 구성된 고화재의 공극에 수분이 포함되는 동시에 수분과 생석회성분이 반응하여 생성되는 수산화칼슘이 고로슬래그 분말을 자극하여 잠재수경성이 발현되면서 강도를 발현하는 안정적인 고결체로 전이된 결과로 판단된다.As shown in Table 1 below, when only the chick carcass was stored in the container, the leachate was generated from the 15th day, and after 45 days, the solid and the liquid were almost completely separated. On the other hand, in the samples buried with soil and quicklime according to the existing burial method, the leachate was absorbed to soil and lime by 15 days until the elapse of 15 days, And settlement in the landfilled state occurred considerably. However, even though the same test period has passed, the settling of the leachate and the ground did not occur. This is because the water content is contained in the pores of the high fire which is composed of the powder of the powdery powder and the absorption action of the quicklime component contained in a large amount in the fire, and the calcium hydroxide produced by the reaction of the water and the quicklime component stimulates the blast furnace slag powder It is considered to be the result of transferring into stable solid body expressing strength with manifestation of hydraulicity.
비고
Remarks
-
-
-
-
-
-
병아리 세 마리(180g)만 용기에 투입No buried material,
Only three chicks (180g) are put into the container
발생 없음
No occurrence
침출수 발생
Leachate generation
침출수 다량 발생
Large amount of leachate
발생
없음
Occur
none
침하
발생
subsidence
Occur
침하 많이 발생
A lot of settlement occurred
없음Occur
none
없음Occur
none
Claims (5)
2) 매몰 구덩이를 파는 단계;
3) 상기 매몰 구덩이의 바닥과 벽면을 두께 0.2㎜ 이상인 불침투성 재료로 덮는 단계;
4) 상기 매몰 구덩이의 바닥에 덮인 불침투성 재료 위에 상기 흡수성 고화재 조성물을 매몰대상 동물 사체 무게의 3배 이상의 양으로 매몰 구덩이에 포설한 후, 매몰대상 동물 사체를 투입하는 단계;
5) 상기 투입된 매몰대상 동물 사체 위에, 상기 흡수성 고화재 조성물을 매몰대상 동물 사체 무게의 1 배 이상의 양으로 포설하는 단계; 및
6) 상기 5) 단계에서 포설된 흡수성 고화재 조성물 위에, 상기 흡수성 고화재 조성물과 흙을 혼합하여 준비한 혼합토를 지표면에서 1.5m 이상의 높이가 되도록 복토 및 성토를 하는 단계포함하는 흡수성 고화재 조성물을 사용한 긴급 살처분 가축 매몰공법.1) preparing an absorbent antioxidant composition comprising 5 to 200 parts by weight of a cokes desulfurization gypsum and 5 to 50 parts by weight of a blast furnace slag fine powder in 100 parts by weight of incineration residue;
2) digging the burrows;
3) covering the bottom and the wall surface of the buried hole with an impermeable material having a thickness of 0.2 mm or more;
4) placing the absorbent fire-proof composition on the impermeable material covered on the bottom of the buried hole in the buried pore in an amount of three times or more the weight of the buried animal carcass, and then injecting the burial target animal carcass;
5) placing the absorbent core composition on the buried animal carcass in an amount of at least 1 times the weight of the buried animal carcass; And
6) An absorbent fire-resistant composition comprising the step of covering the soil and the embankment so that the mixture soil prepared by mixing the water-absorbing fire-fighting composition and the soil is at least 1.5 m above the ground surface on the water- Emergency Cattle Disposal Method.
하기 A) 내지 C) 단계 중 하나 이상을 추가로 더 포함하는 것을 특징으로 하는 흡수성 고화재 조성물을 사용한 긴급 살처분 가축 매몰 공법:
A) 사체의 부패에 의한 가스발생에 따른 가스배출관의 설치하는 단계;
B) 비닐 덮개, 및/또는 빗물 배수로와 집수로를 설치하는 단계; 및
C) 침출수 배출관 및 저류조 설치하고, 상기 저류조를 소독 하는 단계. The method according to claim 1,
Further comprising at least one of the following steps A) to C): < tb > ______________________________________ < tb > ______________________________________ <
A) a step of installing a gas discharge pipe according to the generation of gas by corruption of the body;
B) installing a vinyl cover, and / or rainwater drainage and collection channels; And
C) installing a leachate discharge pipe and a storage tank, and disinfecting the storage tank.
상기 소각 잔재가 산화칼슘 함량이 20% 이상인 고칼슘 플라이애시인 것을 특징으로 하는 흡수성 고화재 조성물을 사용한 긴급 살처분 가축 매몰 공법.The method according to claim 1,
Wherein the incineration residue is high calcium fly ash having a calcium oxide content of 20% or more.
상기 고로슬래그 미분말의 분말도(비표면적)가 3,500~8,000㎠/g인 것을 특징으로 하는 흡수성 고화재 조성물을 사용한 긴급 살처분 가축 매몰 공법.The method according to claim 1,
Wherein the blast furnace slag fine powder has a specific surface area (specific surface area) of 3,500 to 8,000 cm < 2 > / g.
상기 6) 단계에서 흡수성 고화재 조성물과 흙이 1:1의 중량비로 혼합되는 것을 특징으로 하는 흡수성 고화재 조성물을 사용한 긴급 살처분 가축 매몰 공법.The method according to claim 1,
Wherein the water absorbent composition and the soil are mixed at a weight ratio of 1: 1 in the step 6).