KR20150142635A - Composition of natural adhesion for natural leather of vehicle and method thereof - Google Patents
Composition of natural adhesion for natural leather of vehicle and method thereof Download PDFInfo
- Publication number
- KR20150142635A KR20150142635A KR1020150082837A KR20150082837A KR20150142635A KR 20150142635 A KR20150142635 A KR 20150142635A KR 1020150082837 A KR1020150082837 A KR 1020150082837A KR 20150082837 A KR20150082837 A KR 20150082837A KR 20150142635 A KR20150142635 A KR 20150142635A
- Authority
- KR
- South Korea
- Prior art keywords
- natural
- water
- adhesive composition
- solution
- formulation
- Prior art date
Abstract
Description
본 발명은 피혁을 접착하기 위한 접착제 조성물에 관한 것으로, 특히 차량용 천연가죽을 접착하기 위해 사용되는 접착제 조성물에 관한 것이다.
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an adhesive composition for adhering leather, and more particularly to an adhesive composition used for adhering natural leather for automobiles.
일상에서 피혁을 가공하여 생산한 제품을 쉽게 찾아 볼 수 있으며, 대표적으로는 가방, 구두, 지갑, 핸드폰 케이스, 의류, 벨트 등의 피혁 제품이 있다. 이러한 피혁 제품은 생산시 바느질을 하거나 접착제를 이용하거나 또는 접착제와 바느질을 이용하여 두 개의 피혁을 서로 고정시킨다.It is easy to find products produced by processing leather in everyday life. Typical examples are leather products such as bags, shoes, wallets, cell phone cases, clothes, and belts. These leather products are fixed to each other by sewing, using an adhesive, or by using an adhesive and stitching.
한편, 자동차 내부에는 차량용 천연가죽을 이용한 제품(예; 시트 커버, 스티어링 휠 커버, 대쉬보드 커버 등)이 사용되고 있다. 여기서 차량용 천연가죽은 자동차 내장재에 사용되는 천연 가죽을 의미하며, 주행시 주어지는 다양한 환경을 감안한 많은 요구 조건들을 만족시킬 수 있도록 제조한 고도의 물성을 지닌 견고하고 튼튼한 가죽을 말한다.On the other hand, products using natural leather for automobiles (eg, seat covers, steering wheel covers, dashboard covers, etc.) are used in automobiles. Here, natural leather for automobiles refers to natural leather used in automobile interiors, and refers to a solid and durable leather having a high degree of physical properties, which is manufactured so as to satisfy many requirements in consideration of various environment given when driving.
이러한 차량용 천연가죽은 빈번한 사용성에 대비하여 기능적인 특성을 부여하기 위한 일련의 작업과정을 통해 만들어지는데, 원피에서 제품까지 약 1000 여번의 손길을 거치며 150 여일만에 만들어진다.These natural leather for cars are made through a series of work processes to give functional characteristics in preparation for frequent use. They are made in about 150 days after about 1000 touches from raw hides to products.
이러한 특성을 가진 차량용 천연가죽은 내부에 크롬 등의 화학제가 가미되어 있어서 현재 시중에서 판매되고 있는 접착제로는 차량용 천연가죽을 서로 접착시키는 것이 용이하지 않다. 이런 이유로 현재 사용되는 차량용 천연가죽을 서로 고정시키는 형태는 강한 화공성분의 접착제를 가죽재 사이에서 자체 응고되도록 하여 가죽을 잡아주는 형태이거나, 양면 테이프를 이용하여 가죽 사이를 임시로 접착하도록 하여 이용하는 형태이다.Since natural leather for automobiles having such characteristics has a chemical substance such as chrome incorporated therein, it is not easy to adhere natural leather for automobiles to adhesives sold on the market at present. For this reason, the currently used natural leather for automobiles is fixed to each other. In this case, it is a form in which a strong chemical compound adhesive is self-solidified between leather materials to hold the leather, or a form in which the leather is temporarily adhered by using double- to be.
그런데 강한 화공성분의 접착제를 이용하는 형태에서는 화공성분의 접착제가 오래지 않아 응고가 되고 응고된 부분이 돌출되어 미관상 및 사용상의 문제가 발생하고, 그 접착력 또한 오래 지속되지 않아 제품의 수명을 단축시키는 요인이 된다. 그리고 양면 테이프를 이용하는 형태는 차량용 천연가죽을 고정시키는 임시적인 처방일 뿐 근본적인 방법이 아니다.
However, in the case of using an adhesive having a strong chemical component, the adhesive of the chemical component is not solidified, and the solidified portion is protruded to cause a problem in appearance and use, and the adhesive strength is not maintained for a long time, do. And the way of using double-sided tape is not a fundamental method but a temporary prescription for fixing natural leather for automobiles.
본 발명이 이루고자 하는 기술적 과제는 차량용 천연가죽을 서로 접착시킬 수 있는 차량용 천연가죽을 위한 접착제 조성물을 제공하는 것이다. 또한 본 발명이 이루고자 하는 기술적 과제는 제품의 외형이 보존되면서 접착 수명이 긴 차량용 천연가죽을 위한 접착제 조성물을 제공하는 것이다.
Disclosure of Invention Technical Problem [8] The present invention provides an adhesive composition for natural leather for automobiles capable of bonding natural leather for automobiles to each other. Another object of the present invention is to provide an adhesive composition for natural leather for automobiles having a long adhesive life, while preserving the appearance of the product.
본 발명의 일 특징에 따른 차량용 천연가죽을 위한 접착제 조성물 제조방법은 용기에 물을 넣고 가열하는 단계, 물이 가열에 의해 최초 끓는점 이상의 온도로 올라가서 끓기 시작하면, 가열 온도를 70℃ 내지 90℃로 낮춘 후 천연 타르 용액을 상기 용기에 넣고 계속해서 가열하는 단계, 계속된 가열에 의해 상기 천연 타르 용액이 물에 섞여 퍼질 때에 천연 라텍스 용액을 상기 용기에 투입하여 상기 물, 상기 천연 타르 용액 및 상기 천연 라텍스 용액으로 구성된 배합물을 만드는 단계, 상기 배합물을 중탕하여 응고형 접착성분을 만드는 단계, 그리고 상기 응고형 접착성분을 상온에서 식혀 반 응고형 배합물인 접착제 조성물을 만드는 단계를 포함한다.A method for manufacturing an adhesive composition for a leather for a vehicle according to one aspect of the present invention comprises the steps of placing water in a container and heating the water; heating the water to a temperature higher than the initial boiling point by heating to start boiling; The natural tar solution and the natural tar solution are introduced into the vessel and then heated, and when the natural tar solution is dispersed in the water by continuous heating, the natural latex solution is introduced into the vessel, Preparing a formulation comprising a latex solution, boiling the formulation to make a coagulated adhesive component, and cooling the coagulated adhesive component at room temperature to form an adhesive composition that is an anticoagulated formulation.
상기에서 배합물의 중량%가 100 중량%인 경우에, 상기 배합물의 물은 10 내지 25 중량%이고, 상기 배합물의 천연 라텍스 용액은 15 내지 50 중량%이며, 상기 배합물의 천연 타르 용액은 15 내지 35 중량%이다.Wherein the water content of the formulation is from 10 to 25% by weight, the natural latex solution of the formulation is from 15 to 50% by weight, and the natural tar solution of the formulation comprises from 15 to 35% Weight%.
상기에서 배합물을 중탕하는 단계는 상기 배합물을 95℃ 내지 100℃의 온도에서 20분 내지 40분간 1차 가열하는 단계, 그리고 상기 1차 가열 후 가열 온도를 40℃ 내지 60℃의 온도로 낮추고 15분 내지 30분간 2차 가열을 하는 단계를 포함한다.Wherein the step of boiling the formulation comprises the steps of first heating the formulation at a temperature of 95 ° C to 100 ° C for 20 minutes to 40 minutes and then lowering the heating temperature to a temperature of 40 ° C to 60 ° C for 15 minutes Followed by secondary heating for 30 minutes.
본 발명의 다른 특징에 따른 차량용 천연가죽을 위한 접착제 조성물은 고무나무에서 추출된 천연 라텍스 용액, 자작나무에서 추출된 천연 타르 용액, 그리고 용매인 물을 포함한다.According to another aspect of the present invention, an adhesive composition for a leather for a vehicle includes a natural latex solution extracted from a rubber tree, a natural tar solution extracted from a birch, and water as a solvent.
상기에서 접착제 조성물 제조시에 이용되는 용기에 담긴 상기 물, 상기 천연 라텍스 용액 및 상기 천연 타르 용액으로 구성된 배합물의 중량%를 100 중량%로 하는 경우에, 상기 접착제 조성물의 물은 0 내지 5 중량%이고, 상기 접착제 조성물의 천연 라텍스 용액은 15 내지 50 중량%이며, 상기 접착제 조성물의 천연 타르 용액은 15 내지 35 중량%이다. 이때 상기 배합물의 물은 10 내지 25 중량%이고, 상기 배합물의 천연 라텍스 용액은 15 내지 50 중량%이며, 상기 배합물의 천연 타르 용액은 15 내지 35 중량%이다.
When the weight percentage of the water, the natural latex solution and the natural tar solution contained in the container used for preparing the adhesive composition is set to 100 wt%, the water of the adhesive composition is 0 to 5 wt% , The natural latex solution of the adhesive composition is 15 to 50 wt%, and the natural tar solution of the adhesive composition is 15 to 35 wt%. Wherein the water content of the formulation is 10-25 wt%, the natural latex solution of the formulation is 15-50 wt%, and the natural tar solution of the formulation is 15-35 wt%.
본 발명의 실시 예에 따르면, 오랜 시간동안 응고가 되지 않으면서 차량용 천연가죽 간을 접착시킬 수 있게 하여 차량용 천연가죽 이외의 가죽이 사용되는 제품에 차량용 천연가죽이 이용될 수 있게 하는 효과가 있다. According to the embodiment of the present invention, natural leather for automobiles can be adhered without being solidified for a long period of time, thereby enabling natural leather for automobiles to be used for products other than automotive leather.
또한 본 발명의 실시 예에 따르면, 천연 성분으로 접착제를 구성하여 차량용 천연가죽을 이용한 가공품이 친환경적인 효과가 있다.Further, according to the embodiment of the present invention, there is an eco-friendly effect that a work made of a natural leather for a vehicle constituting an adhesive as a natural component.
또한 본 발명의 실시 예에 따르면, 제작공정상에서 환경 파괴적 요소가 미미하고, 접착 후에도 상온에서 유동성 연질 고착되어 사용성이 매우 뛰어난 효과가 있다.
Further, according to the embodiment of the present invention, environmental destructive elements are insignificant in the manufacturing process, and after bonding, they are fixed by fluidity and softness at room temperature, and the useability is extremely excellent.
도 1은 본 발명의 실시 예에 따른 차량용 천연가죽을 위한 접착제 조성물의 제조방법에 대한 순서도이다.
도 2는 본 발명의 실시 예에 따른 차량용 천연가죽을 위한 접착제 조성물의 제조방법에서 중탕 과정에 대한 순서도이다.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a flow chart of a method of manufacturing an adhesive composition for a leather for a vehicle according to an embodiment of the present invention. FIG.
2 is a flow chart for a bathing process in a method of manufacturing an adhesive composition for a leather for a vehicle according to an embodiment of the present invention.
본 발명은 다양한 변경을 가할 수 있고 여러 가지 실시예를 가질 수 있는 바, 특정 실시예들을 도면에 예시하고 상세한 설명에 상세하게 설명하고자 한다. 그러나, 이는 본 발명을 특정한 실시 형태에 대해 한정하려는 것이 아니며, 본 발명의 사상 및 기술 범위에 포함되는 모든 변경, 균등물 내지 대체물을 포함하는 것으로 이해되어야 한다.While the invention is susceptible to various modifications and alternative forms, specific embodiments thereof are shown by way of example in the drawings and will herein be described in detail. It should be understood, however, that the invention is not intended to be limited to the particular embodiments, but includes all modifications, equivalents, and alternatives falling within the spirit and scope of the invention.
각 도면을 설명하면서 유사한 참조부호를 유사한 구성요소에 대해 사용하였다. 본 발명을 설명함에 있어서 관련된 공지 기술에 대한 구체적인 설명이 본 발명의 요지를 흐릴 수 있다고 판단되는 경우 그 상세한 설명을 생략한다.Like reference numerals are used for like elements in describing each drawing. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.
제1, 제2 등의 용어는 다양한 구성 요소들을 설명하는데 사용될 수 있지만, 상기 구성 요소들은 상기 용어들에 의해 한정되어서는 안 된다. 상기 용어들은 하나의 구성요소를 다른 구성요소로부터 구별하는 목적으로만 사용된다.The terms first, second, etc. may be used to describe various components, but the components should not be limited by the terms. The terms are used only for the purpose of distinguishing one component from another.
예를 들어, 본 발명의 권리 범위를 벗어나지 않으면서 제1 구성요소는 제2 구성요소로 명명될 수 있고, 유사하게 제2 구성요소도 제1 구성요소로 명명될 수 있다.For example, without departing from the scope of the present invention, the first component may be referred to as a second component, and similarly, the second component may also be referred to as a first component.
및/또는 이라는 용어는 복수의 관련된 기재된 항목들의 조합 또는 복수의 관련된 기재된 항목들 중의 어느 항목을 포함한다.And / or < / RTI > includes any combination of a plurality of related listed items or any of a plurality of related listed items.
어떤 구성요소가 다른 구성요소에 "연결되어" 있다거나 "접속되어" 있다고 언급된 때에는, 그 다른 구성요소에 직접적으로 연결되어 있거나 또는 접속되어 있을 수도 있지만, 중간에 다른 구성요소가 존재할 수도 있다고 이해되어야 할 것이다.It is to be understood that when an element is referred to as being "connected" or "connected" to another element, it may be directly connected or connected to the other element, .
반면에, 어떤 구성요소가 다른 구성요소에 "직접 연결되어" 있다거나 "직접 접속되어" 있다고 언급된 때에는, 중간에 다른 구성요소가 존재하지 않는 것으로 이해되어야 할 것이다.On the other hand, when an element is referred to as being "directly connected" or "directly connected" to another element, it should be understood that there are no other elements in between.
본 출원에서 사용한 용어는 단지 특정한 실시예를 설명하기 위해 사용된 것으로, 본 발명을 한정하려는 의도가 아니다.The terminology used in this application is used only to describe a specific embodiment and is not intended to limit the invention.
단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 본 출원에서, "포함하다" 또는 "가지다" 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.The singular expressions include plural expressions unless the context clearly dictates otherwise. In the present application, the terms "comprises" or "having" and the like are used to specify that there is a feature, a number, a step, an operation, an element, a component or a combination thereof described in the specification, But do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, or combinations thereof.
다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미를 가지고 있다.Unless defined otherwise, all terms used herein, including technical or scientific terms, have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs.
일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련 기술의 문맥상 가지는 의미와 일치하는 의미를 가지는 것으로 해석되어야 하며, 본 출원에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다.Terms such as those defined in commonly used dictionaries are to be interpreted as having a meaning consistent with the contextual meaning of the related art and are to be interpreted as either ideal or overly formal in the sense of the present application Do not.
이하, 첨부된 도면을 참조하여 본 발명의 실시 예에 따른 차량용 천연가죽을 위한 접착제 조성물 및 이의 제조방법에 대하여 설명한다. Hereinafter, an adhesive composition for a leather for a vehicle according to an embodiment of the present invention and a method of manufacturing the same will be described with reference to the accompanying drawings.
도 1은 본 발명의 실시 예에 따른 차량용 천연가죽을 위한 접착제 조성물의 제조방법에 대한 순서도이다.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a flow chart of a method of manufacturing an adhesive composition for a leather for a vehicle according to an embodiment of the present invention. FIG.
차량용 천연가죽을 위한 접착용 조성물을 제조하기 위해, 전체 배합물 100 중량%를 기준으로 하여 10 내지 25 중량%의 물, 원목(고무나무)에서 추출된 15 내지 50 중량%의 천연 라텍스(Latex) 용액, 그리고 건조된 자작나무에서 추출된 15 내지 35 중량%의 천연 타르(Tar) 용액을 준비한다.In order to prepare an adhesive composition for automotive leather, 10 to 25% by weight of water based on 100% by weight of the total formulation, 15 to 50% by weight of natural latex solution extracted from logs (rubber tree) , And 15 to 35 wt% of a natural tar (Tar) solution extracted from the dried birch.
모든 구성요소가 준비된 상태에서, 용기에 10 내지 25 중량%의 물을 넣고 가열한다(S101).In a state in which all the components are prepared, 10 to 25% by weight of water is added to the container and heated (S101).
그리고 물이 가열에 의해 최초 끓는점 이상의 온도로 올라가서 끓기 시작하면, 가열 온도를 70℃ ~ 90℃로 낮춘다(S102).Then, when the water rises to a temperature higher than the initial boiling point by heating and starts to boil, the heating temperature is lowered to 70 ° C to 90 ° C (S102).
가열 온도를 70℃ ~ 90℃로 낮추면, 이 상태에서 15 ~ 35 중량의 천연 타르 용액을 용기에 넣고 계속해서 가열한다(S103). When the heating temperature is lowered to 70 to 90 占 폚, 15 to 35 weight of the natural tar solution is put into the vessel and the heating is continued (S103).
여기서 가열하지 않는 물(즉, 상온 중의 물)에 천연 타르 용액을 넣으면 천연 타르 용액은 타르 용액 내의 기름 성분으로 인해 물과 섞이지 않고 물 위에 위치한다. 그러나 물을 가열하는 중에 천연 타르 용액을 넣으면 일반적인 기름과 같이 천연 타르 용액은 물과 섞이게 되어 용기 전체로 퍼진다.When a natural tar solution is placed in unheated water (ie, water at normal temperature), the natural tar solution is placed on the water without mixing with water due to the oil component in the tar solution. However, if you add a natural tar solution while heating the water, the natural tar solution, like common oil, will mix with water and spread throughout the container.
이와 같은 일반적인 원리에 따라 가열 중인 물에 투입된 천연 타르 용액은 시간이 지남에 따라 물과 따로 뭉쳐져 있다가 물과 섞여서 퍼진다. 이렇게 천연 타르 용액이 물에 섞여 퍼질 때에 15 ~ 50 중량%의 천연 라텍스 용액을 용기에 투입한다(S104).According to this general principle, the natural tar solution put into the heating water is separated from the water over time and spread by being mixed with the water. When the natural tar solution is dispersed in water, 15 to 50% by weight of the natural latex solution is put into the container (S104).
여기서 서로 섞이는 중인 물과 천연 타르의 배합물에 천연 라텍스 용액을 투입하면, 용기 내의 천연 타르 용액은 라텍스 입자와 결합하여 응고형 접착성분으로 재조직된다. 이때 물은 천연 라텍스 입자와 천연 타르 입자간의 결합을 도와서 천연 라텍스 입자와 천연 타르 입자가 보다 단단히 결속되게 하는 기능을 한다.Here, when a natural latex solution is added to a mixture of water and natural tar mixed with each other, the natural tar solution in the container is combined with the latex particles and reorganized into a coagulated adhesive component. In this case, water helps bond between natural latex particles and natural tar particles, so that natural latex particles and natural tar particles are tightly bound together.
한편 천연 라텍스 용액을 용기에 투입함에 따라 용기의 배합물은 천연 라텍스 용액, 천연 타르 용액 및 용매인 물로 이루어진다. 이런 상태에서 배합물이 든 용기를 중탕기에 넣고 중탕 작업을 수행하여 응고형 접착성분을 얻는다(S105).On the other hand, as the natural latex solution is put into the container, the combination of the container is made of a natural latex solution, a natural tar solution and water as a solvent. In this state, the container containing the compound is placed in a hot water bath and a hot water bath is performed to obtain a coagulated adhesive component (S105).
그리고 응고형 접착성분을 중탕기에서 꺼내 상온에 두어 시간을 두고 식히는 냉각 과정을 수행한다(S106). 이러한 상온에서의 냉각에 의해 응고형 접착성분은 배합물의 조직이 보다 안정적이고 견고해지며, 점차적으로 젤리(jelly)와 같이 반 응고형 배합물(즉, 반 응고형 접착물)이 된다(S107).Then, the coagulation-type adhesive component is taken out from the boiling water, cooled at room temperature, and cooled for a time (S106). By such cooling at room temperature, the coagulated adhesive component becomes more stable and firm in texture of the formulation, and gradually becomes an anticoagulant (e. G., An anticoagulated adhesive) such as a jelly (S107).
반 응고형 배합물은 본 발명의 실시 예에 따른 접착제 조성물이며, 천연 라텍스, 천연 타르 및 물로 구성된다.The anticoagulant formulation is an adhesive composition according to an embodiment of the present invention and consists of natural latex, natural tar and water.
상기의 접착제 조성물을 제조하는 과정에서, 천연 타르 용액이 설정된 대상 중량비를 초과하면 상온에서 응고되지 않고 계속 액화상태로 유지되어 접착 기능을 가지지 않게 되며, 천연 라텍스 용액이 50 중량%를 초과하면 접착제 조성물이 완연한 연질의 고체화가 되어 도포가 불가하다. 그리고 천연 라텍스 용액이 15 중량% 미만이면 상온에서 응고되지 않고 계속 액화상태로 유지되어 접착 기능을 가지지 않게 된다.When the natural tar solution exceeds the set target weight ratio, it does not solidify at room temperature and is kept in a liquefied state to have no adhesive function. When the natural latex solution exceeds 50 wt%, the adhesive composition It is solidified and the application is impossible. If the natural latex solution is less than 15% by weight, it does not solidify at room temperature and remains in a liquefied state, so that it does not have an adhesive function.
이 과정으로 얻어지는 천연 접착제는 차량용천연가죽과 사용될 때 최적의 사용성을 할휘하기 위함으로, 차량용 천연가죽의 내마모성, 방수성 등의 사용성 기준 특수물성을 극대화하기 위해 봉재 부위나 접착부, 가죽마감부에 도포되어 제품화 되었을 경우에 연질이 유지되면서도 내부에 삽입된 전기기기나 카드, 개인 소품 등을 보호할 수 있는 완전한 방수성과 마모성 등을 유지할 수 있게 한다.
The natural adhesives obtained by this process are applied to the bar parts, adhesive parts and leather finish parts in order to maximize the special properties of usability criteria such as abrasion resistance and water resistance of the natural leather for automobile, When it is commercialized, it maintains softness and maintains the waterproofness and abrasion that can protect the electric devices, cards, and personal items inserted inside.
이하에서는 도 2를 참조로 하여 상기 배합물의 중탕 과정을 설명한다. 도 2는 본 발명의 실시 예에 따른 차량용 천연가죽을 위한 접착제 조성물의 제조방법에서 중탕 과정에 대한 순서도이다.Hereinafter, the bathing process of the combination will be described with reference to FIG. 2 is a flow chart for a bathing process in a method of manufacturing an adhesive composition for a leather for a vehicle according to an embodiment of the present invention.
물, 천연 라텍스 용액 및 천연 타르 용액으로 이루어진 배합물이 담긴 용기를 중탕기에 투입하고(S201), 95℃ 내지 100℃의 온도에서 20분 내지 40분간 1차 가열한다(S202). A container containing a mixture of water, a natural latex solution and a natural tar solution is introduced into a boiling water reactor (S201) and then heated at a temperature of 95 to 100 ° C for 20 to 40 minutes (S202).
그리고 1차 가열 후 가열 온도를 40℃ 내지 60℃의 온도로 낮추고 15분 내지 30분간 2차 가열을 하고(S203), 그 결과로 천연 라텍스와 천연 타르의 결합 조직이 보다 안정적이고 견고해진 응고형 접착성분을 얻는다(S204).After the first heating, the heating temperature is lowered to a temperature of 40 to 60 ° C and the secondary heating is performed for 15 to 30 minutes (S203). As a result, the bonding structure of the natural latex and natural tar becomes more stable and solidified An adhesive component is obtained (S204).
이러한 중탕 과정에서 천연 라텍스 입자와 천연 타르 입자는 물의 도움으로 상호 결합하게 되고, 중탕 과정이 끝나는 시점에서는 모든 천연 라텍스 입자와 천연 타르 입자가 상호 결합되어 응고형 접착성분이 된다.In this bath process, natural latex particles and natural tar particles are combined with the help of water, and at the end of the boiling process, all the natural latex particles and natural tar particles are combined with each other to form a coagulated adhesive component.
한편 배합물 중 물은 일부가 1차 가열 및 2차 가열 시에 수증기로 기화하여 공기중으로 날아가 버리게 되고, 그에 따라 중탕의 결과로 얻어진 응고형 접착성분 내의 물의 중량%는 최초 용기에 투입된 10 내지 25 중량%보다 적은 중량%를 가진다. 구체적으로 응고형 접착성분 내의 물의 중량%는 최초 용기에 투입된 10 내지 25 중량%에서 기화하고 남은 0 내지 5 중량%를 가진다.
On the other hand, the water in the formulation is vaporized by water vapor in part during the first heating and the second heating, and is blown into the air, so that the weight percentage of water in the coagulated adhesive component obtained as a result of the water bath is 10 to 25 wt% % ≪ / RTI > by weight. Specifically, the weight percentage of water in the coagulable adhesive component is 0 to 5% by weight, which is vaporized at 10 to 25% by weight of the initial vessel.
이하에서는 본 발명의 실시 예에 따른 차량용 천연가죽을 위한 접착제 조성물 제조방법에 의해 제조된 접착제 조성물에 대하여 설명한다.Hereinafter, an adhesive composition prepared by a method for manufacturing an adhesive composition for a leather for a vehicle according to an embodiment of the present invention will be described.
본 발명의 실시 예에 따른 차량용 천연가죽을 위한 접착제 조성물은 천연 타르, 천연 라텍스 및 물로 구성되며, 젤리 형태 즉, 반 응고형태를 나타낸다.The adhesive composition for a leather for a vehicle according to an embodiment of the present invention is composed of natural tar, natural latex and water, and exhibits a jelly form, that is, an anticoagulant form.
천연 타르는 자작나무에서 추출된 액상의 천연 타르 용액을 원(original) 성분으로 하며 환경 친화적 접착 기능을 가지고 있다. 그리고 천연 라텍스는 고무나무에서 추출된 액상의 천연 라텍스 용액을 원(original) 성분으로 하며 환경 친화적 접착 기능을 가지고 있다.Natural tar is made from natural tar solution extracted from birch as original ingredient and has environmentally friendly adhesive function. And natural latex is made of natural latex solution extracted from rubber tree as original ingredient and has environment friendly adhesive function.
그리고 물은 천연 라텍스의 성분과 천연 타르의 성분을 결합시키는 용매의 역할을 한다.And water acts as a solvent to combine the ingredients of natural latex with the ingredients of natural tar.
이러한 천연 타르, 천연 라텍스 및 물의 조성비를 접착제 조성물 제조시에 사용된 배합물의 100 중량%를 기준으로 설명하면 다음과 같다.The composition ratio of the natural tar, natural latex and water will be described based on 100% by weight of the blend used in the production of the adhesive composition.
접착제 조성물 제조시에 물, 천연 타르 용액 및 천연 라텍스 용액으로 구성된 배합물의 100 중량%를 기준으로, 배합물의 물은 10 내지 25 중량%이고, 천연 타르 용액은 15 내지 35 중량%이며, 천연 라텍스 용액은 15 내지 50 중량%이다.The water content of the formulation is 10 to 25% by weight, the natural tar solution is 15 to 35% by weight, based on 100% by weight of the formulation consisting of water, natural tar solution and natural latex solution in preparing the adhesive composition, Is 15 to 50% by weight.
이를 기반으로, 접착제 조성물 제조 결과물인 접착제 조성물은 천연 타르 15 내지 35 중량%, 천연 라텍스 15 내지 50 중량% 그리고 물 0 내지 5 중량 %로 구성된다. 결국 접착제 조성물의 총 중량%는 접착제 조성물 제조시에 사용된 배합물의 100 중량%에서 수증기로 증발한 물의 중량%만큼이 적으며, 배합물의 중량% 대비 최대 90 중량%를 가진다.Based on this, the adhesive composition resulting from the production of the adhesive composition comprises 15 to 35% by weight of natural tar, 15 to 50% by weight of natural latex and 0 to 5% by weight of water. Ultimately, the total weight percent of the adhesive composition is less than the weight percent of water vaporized with water vapor at 100 weight percent of the formulation used in the preparation of the adhesive composition, and up to 90 weight percent relative to the weight percent of the formulation.
이상에서 설명한 본 발명의 실시예는 장치 및 방법을 통해서만 구현이 되는 것은 아니며, 본 발명의 실시예의 구성에 대응하는 기능을 실현하는 프로그램 또는 그 프로그램이 기록된 기록 매체를 통해 구현될 수도 있으며, 이러한 구현은 앞서 설명한 실시예의 기재로부터 본 발명이 속하는 기술분야의 전문가라면 쉽게 구현할 수 있는 것이다. The embodiments of the present invention described above are not only implemented by the apparatus and method but may be implemented through a program for realizing the function corresponding to the configuration of the embodiment of the present invention or a recording medium on which the program is recorded, The embodiments can be easily implemented by those skilled in the art from the description of the embodiments described above.
이상에서 본 발명의 실시예에 대하여 상세하게 설명하였지만 본 발명의 권리범위는 이에 한정되는 것은 아니고 다음의 청구범위에서 정의하고 있는 본 발명의 기본 개념을 이용한 당업자의 여러 변형 및 개량 형태 또한 본 발명의 권리범위에 속하는 것이다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed exemplary embodiments, It belongs to the scope of right.
Claims (6)
물이 가열에 의해 최초 끓는점 이상의 온도로 올라가서 끓기 시작하면, 가열 온도를 70℃ 내지 90℃로 낮춘 후 천연 타르 용액을 상기 용기에 넣고 계속해서 가열하는 단계,
계속된 가열에 의해 상기 천연 타르 용액이 물에 섞여 퍼질 때에 천연 라텍스 용액을 상기 용기에 투입하여 상기 물, 상기 천연 타르 용액 및 상기 천연 라텍스 용액으로 구성된 배합물을 만드는 단계,
상기 배합물을 중탕하여 응고형 접착성분을 만드는 단계, 그리고
상기 응고형 접착성분을 상온에서 식혀 반 응고형 배합물인 접착제 조성물을 만드는 단계
를 포함하는 차량용 천연가죽을 위한 접착제 조성물 제조방법.Placing the vessel in water and heating,
When the water is heated to a temperature higher than the initial boiling point and starts to boil, the heating temperature is lowered to 70 to 90 DEG C, then the natural tar solution is placed in the vessel and then heated,
Introducing a natural latex solution into the vessel when the natural tar solution is dispersed in water by subsequent heating to form a blend comprising the water, the natural tar solution and the natural latex solution;
Boiling the formulation to form a coagulated adhesive component, and
The above-mentioned coagulation-type adhesive component is cooled at room temperature to produce an adhesive composition which is an anti-coagulation formulation
≪ / RTI > wherein the adhesive composition comprises at least one of the following.
상기 배합물의 중량%가 100 중량%인 경우에,
상기 배합물의 물은 10 내지 25 중량%이고,
상기 배합물의 천연 라텍스 용액은 15 내지 50 중량%이며,
상기 배합물의 천연 타르 용액은 15 내지 35 중량%인
차량용 천연가죽을 위한 접착제 조성물 제조방법.The method of claim 1,
When the weight percentage of the formulation is 100% by weight,
The water of the formulation is from 10 to 25% by weight,
The natural latex solution of the formulation comprises 15 to 50% by weight,
The natural tar solution of the formulation comprises 15 to 35 wt%
A method for manufacturing an adhesive composition for natural leather for automobiles.
상기 배합물을 중탕하는 단계는
상기 배합물을 95℃ 내지 100℃의 온도에서 20분 내지 40분간 1차 가열하는 단계, 그리고
상기 1차 가열 후 가열 온도를 40℃ 내지 60℃의 온도로 낮추고 15분 내지 30분간 2차 가열을 하는 단계
를 포함하는 차량용 천연가죽을 위한 접착제 조성물 제조방법.3. The method according to claim 1 or 2,
The step of soaking the formulation
Heating the formulation at a temperature of from 95 캜 to 100 캜 for 20 minutes to 40 minutes, and
Lowering the heating temperature after the primary heating to a temperature of 40 ° C to 60 ° C, and performing secondary heating for 15 minutes to 30 minutes
≪ / RTI > wherein the adhesive composition comprises at least one of the following.
자작나무에서 추출된 천연 타르 용액, 그리고
용매인 물
을 포함하는 차량용 천연가죽을 위한 접착제 조성물.Natural latex solution extracted from rubber tree,
Natural tar solution extracted from birch, and
The solvent, water
≪ / RTI >
접착제 조성물 제조시에 이용되는 용기에 담긴 상기 물, 상기 천연 라텍스 용액 및 상기 천연 타르 용액으로 구성된 배합물의 중량%를 100 중량%로 하는 경우에,
상기 접착제 조성물의 물은 0 내지 5 중량%이고,
상기 접착제 조성물의 천연 라텍스 용액은 15 내지 50 중량%이며,
상기 접착제 조성물의 천연 타르 용액은 15 내지 35 중량%인
차량용 천연가죽을 위한 접착제 조성물.5. The method of claim 4,
When the weight percentage of the water, the natural latex solution and the mixture composed of the natural tar solution contained in the container used in the production of the adhesive composition is 100% by weight,
The water of the adhesive composition is 0 to 5% by weight,
The natural latex solution of the adhesive composition is 15 to 50 wt%
The natural tar solution of the adhesive composition comprises 15 to 35 wt%
An adhesive composition for natural leather for automobiles.
상기 배합물의 물은 10 내지 25 중량%이고,
상기 배합물의 천연 라텍스 용액은 15 내지 50 중량%이며,
상기 배합물의 천연 타르 용액은 15 내지 35 중량%인
차량용 천연가죽을 위한 접착제 조성물.
6. The method of claim 5,
The water of the formulation is from 10 to 25% by weight,
The natural latex solution of the formulation comprises 15 to 50% by weight,
The natural tar solution of the formulation comprises 15 to 35 wt%
An adhesive composition for natural leather for automobiles.