KR20150123885A - Optical pressure-sensitive adhesive composition, optical pressure-sensitive adhesive sheet, image display device, and input/output device - Google Patents
Optical pressure-sensitive adhesive composition, optical pressure-sensitive adhesive sheet, image display device, and input/output device Download PDFInfo
- Publication number
- KR20150123885A KR20150123885A KR1020157026550A KR20157026550A KR20150123885A KR 20150123885 A KR20150123885 A KR 20150123885A KR 1020157026550 A KR1020157026550 A KR 1020157026550A KR 20157026550 A KR20157026550 A KR 20157026550A KR 20150123885 A KR20150123885 A KR 20150123885A
- Authority
- KR
- South Korea
- Prior art keywords
- sensitive adhesive
- pressure
- mass
- adhesive composition
- component
- Prior art date
Abstract
광학용 점착제 조성물은, (A) 수소 첨가 블록 공중합체와, (B) 제 1 상용제와, (C) 제 2 상용제를 함유하는 광학용 점착제 조성물로서, 상기 (A) 수소 첨가 블록 공중합체는, 방향족 비닐 단량체의 중합체 성분으로 구성되는 하드 세그먼트와, 공액 디엔 단량체의 중합체 성분으로 구성되는 소프트 세그먼트를 갖고, 상기 (B) 제 1 상용제는, 상기 하드 세그먼트에 상용하는 성질을 갖고, 또한 연화점이 80 ℃ 이상이고, 상기 (C) 제 2 상용제는, 상기 소프트 세그먼트에 상용하는 성질을 갖고, 또한 상온 (23 ℃) 에 있어서 액체이고, 상기 광학용 점착제 조성물로부터 얻어지는 점착제층의 비유전율이 1 이상 3.5 이하이다.The optical pressure-sensitive adhesive composition for optical use is an optical pressure-sensitive adhesive composition for optical use containing (A) a hydrogenated block copolymer, (B) a first compatibilizing agent, and (C) a second compatibilizing agent, wherein the hydrogenated block copolymer Has a hard segment composed of a polymer component of an aromatic vinyl monomer and a soft segment composed of a polymer component of a conjugated diene monomer, wherein the first compatibilizing agent (B) has properties compatible with the hard segment, and Wherein the softener has a softening point of 80 DEG C or higher and the second softener (C) has properties compatible with the soft segment and is liquid at room temperature (23 DEG C), and the relative dielectric constant Is not less than 1 and not more than 3.5.
Description
본 발명은 광학용 점착제 조성물, 광학용 점착 시트, 화상 표시 장치 및 입출력 장치에 관한 것이다.The present invention relates to an optical pressure-sensitive adhesive composition, an optical pressure-sensitive adhesive sheet, an image display device, and an input / output device.
최근, 액정 표시 장치 등의 화상 표시 장치나, 화상 표시 장치와 조합하여 사용되는, 터치 패널 등의 입출력 장치가 널리 사용되게 되었다. 이들 화상 표시 장치나 입출력 장치의 제조에 있어서, 구성 부재를 첩합 (貼合) 할 때에 점착제 조성물이 사용되고 있다.2. Description of the Related Art In recent years, an input / output device such as a touch panel, which is used in combination with an image display device such as a liquid crystal display device or an image display device, has been widely used. In the production of these image display apparatuses and input / output apparatuses, a pressure-sensitive adhesive composition is used when the constituent members are bonded.
이들 화상 표시 장치나 입출력 장치를 구성하는 전자 부품의 미세화에 수반하여, 예를 들어 회로 중에서 발생하는 고주파 노이즈나, 구동시에 도전체에 끼워진 유전체의 차지에서 기인하여, 전자 부품에 포함되는 내부 회로에서 발생하는 노이즈에 의한 오작동이 무시할 수 없는 것이 되었다. 특히, 아크릴계 점착제를 주성분으로 하는 점착제 조성물로 형성된 점착제층에는 비유전율이 4 를 초과하는 것도 있으며, 이와 같은 비유전율을 갖는 점착제 조성물을 사용한 경우, 절연층으로서의 정전 용량이 높고, 고주파 노이즈에 의한 오작동이 발생하는 경우가 있다.With the miniaturization of electronic parts constituting these image display apparatuses and input / output devices, for example, in an internal circuit included in an electronic part due to high-frequency noise generated in a circuit and charge of a dielectric member sandwiched between conductors Malfunction due to generated noise can not be ignored. In particular, the pressure-sensitive adhesive layer formed from a pressure-sensitive adhesive composition containing an acrylic pressure-sensitive adhesive as a main component may have a relative dielectric constant exceeding 4, and when such a pressure-sensitive adhesive composition having a relative dielectric constant is used, the capacitance as an insulating layer is high, May occur.
예를 들어, 특허문헌 1 에는, 정전 용량 방식의 터치 패널식 입출력 장치의 오작동을 방지하는 것을 목적으로 하는 광학용 점착용 시트가 개시되어 있다.For example,
본 발명자들은 화상 표시 장치나 입출력 장치의 제조에 사용되는 점착제 조성물의 비유전율의 저감을 도모함으로써, 화상 표시 장치나 입출력 장치의 오작동을 방지하는 것에 대하여 예의 검토한 결과, 특정한 재료를 포함하는 점착제 조성물로 형성되는 점착제층이 낮은 비유전율을 갖고, 또한 우수한 내구성, 밀착성 및 내후성을 갖는 것을 알아냈다.As a result of intensive investigations to prevent malfunction of an image display apparatus and an input / output device by reducing the relative dielectric constant of the pressure-sensitive adhesive composition used in the manufacture of an image display apparatus and an input / output apparatus, the present inventors have found that a pressure- Has a low relative dielectric constant, and has excellent durability, adhesion, and weather resistance.
본 발명은 비유전율이 저감되고, 또한 내구성, 밀착성 및 내후성이 우수한 점착제층을 얻을 수 있는 광학용 점착제 조성물, 그 광학용 점착제 조성물을 사용하여 형성된 광학용 점착 시트, 그리고 그 광학용 점착제 조성물을 사용하여 형성된 점착제층을 포함하는 화상 표시 장치 및 입출력 장치를 제공한다.The present invention provides a pressure-sensitive adhesive composition for optical use which can obtain a pressure-sensitive adhesive layer having a reduced relative dielectric constant and excellent durability, adhesion and weather resistance, an optical pressure-sensitive adhesive sheet formed using the optical pressure-sensitive adhesive composition, and an optical pressure- And a pressure-sensitive adhesive layer formed on the pressure-sensitive adhesive layer.
1. 본 발명의 하나의 양태에 관련된 광학용 점착제 조성물은,1. A pressure-sensitive adhesive composition for optical use according to one embodiment of the present invention,
(A) 수첨 블록 공중합체와,(A) a hydrogenated block copolymer,
(B) 제 1 상용(相溶)제 와,(B) a first compatibilizing agent,
(C) 제 2 상용제를 함유하는, 광학용 점착제 조성물로서,(C) a second compatibilizing agent, wherein the pressure-
상기 (A) 수첨 블록 공중합체는, 방향족 비닐 단량체의 중합체 성분으로 구성되는 하드 세그먼트와, 공액 디엔 단량체의 중합체 성분으로 구성되는 소프트 세그먼트를 갖고,The hydrogenated block copolymer (A) has a hard segment composed of a polymer component of an aromatic vinyl monomer and a soft segment composed of a polymer component of a conjugated diene monomer,
상기 (B) 제 1 상용제는, 상기 하드 세그먼트에 상용하는 성질을 갖고, 또한 연화점이 80 ℃ 이상이고,The first compatibilizing agent (B) has properties compatible with the hard segment and has a softening point of 80 ° C or higher,
상기 (C) 제 2 상용제는, 상기 소프트 세그먼트에 상용하는 성질을 갖고, 또한 상온 (23 ℃) 에 있어서 액체이고,The second compatibilizing agent (C) has properties compatible with the soft segment and is liquid at room temperature (23 캜)
상기 광학용 점착제 조성물로부터 얻어지는 점착제층의 비유전율이 1 이상 3.5 이하이다.The relative dielectric constant of the pressure-sensitive adhesive layer obtained from the pressure-sensitive adhesive composition for optical use is not less than 1 and not more than 3.5.
2. 상기 1 에 기재된 광학용 점착제 조성물에 있어서, 상기 (A) 수첨 블록 공중합체에 있어서의 상기 하드 세그먼트의 함유량이 5 질량％ 이상 70 질량％ 이하일 수 있다.2. The optical pressure-sensitive adhesive composition for optical use according to 1 above, wherein the content of the hard segment in the hydrogenated block copolymer (A) is 5% by mass or more and 70% by mass or less.
3. 상기 1 또는 2 에 기재된 광학용 점착제 조성물에 있어서, 상기 (A) 수첨 블록 공중합체를 구성하는 공액 디엔 단량체의 중합체 성분에 함유되는 2 중 결합의 수첨률이 90 ％ 이상일 수 있다.3. The pressure-sensitive adhesive composition for optical use according to 1 or 2, wherein the number of double bonds contained in the polymer component of the conjugated diene monomer constituting the hydrogenated block copolymer (A) may be 90% or more.
4. 상기 1 내지 3 중 어느 하나에 기재된 광학용 점착제 조성물에 있어서, 상기 (B) 제 1 상용제는, 방향족계 점착 부여 수지일 수 있다.4. The pressure-sensitive adhesive composition for optical use according to any one of 1 to 3 above, wherein the first compatibilizing agent (B) may be an aromatic tackifying resin.
5. 상기 4 에 기재된 광학용 점착제 조성물에 있어서, 상기 방향족계 점착 부여 수지가, 방향족 석유 수지, 스티렌계 중합체, α-메틸스티렌계 중합체, 스티렌-(α-메틸스티렌)계 공중합체, 스티렌-지방족 탄화수소계 공중합체, 스티렌-(α-메틸스티렌)-지방족 탄화수소계 공중합체 및 스티렌-방향족 탄화수소계 공중합체로 이루어지는 군에서 선택되는 적어도 1 종일 수 있다.5. The pressure-sensitive adhesive composition for optical use according to 4 above, wherein the aromatic tackifier resin is at least one selected from the group consisting of an aromatic petroleum resin, a styrene polymer, an? -Methylstyrene polymer, a styrene- (? At least one member selected from the group consisting of aliphatic hydrocarbon-based copolymers, styrene- (? -Methylstyrene) -aliphatic hydrocarbon-based copolymers and styrene-aromatic hydrocarbon-based copolymers.
6. 상기 1 내지 5 중 어느 하나에 기재된 광학용 점착제 조성물에 있어서, 상기 (C) 제 2 상용제가, 폴리부텐계 화합물, 폴리이소부틸렌계 화합물 및 폴리이소프렌계 화합물로 이루어지는 군에서 선택되는 적어도 1 종일 수 있다.6. The optical pressure-sensitive adhesive composition for optical use according to any one of 1 to 5 above, wherein at least one (1) selected from the group consisting of the second compatibilizing agent (C), polybutene compound, polyisobutylene compound and polyisoprene compound It can be all day.
7. 상기 1 내지 6 중 어느 하나에 기재된 광학용 점착제 조성물에 있어서, 상기 광학용 점착재 조성물의 산가가 1 이하일 수 있다.7. The optical pressure-sensitive adhesive composition for optical use according to any one of 1 to 6 above, wherein the acid value of the optical pressure-sensitive adhesive composition is 1 or less.
8. 상기 1 내지 7 중 어느 하나에 기재된 광학용 점착제 조성물에 있어서, 상기 (B) 제 1 상용제의 함유량이, 상기 (A) 수첨 블록 공중합체 100 질량부에 대하여 5 질량부 이상 60 질량부 이하일 수 있다.(8) The pressure-sensitive adhesive composition for optical use according to any one of (1) to (7) above, wherein the content of the first compatibilizing agent (B) is 5 parts by mass or more and 60 parts by mass ≪ / RTI >
9. 상기 1 내지 8 중 어느 하나에 기재된 광학용 점착제 조성물에 있어서, 상기 (C) 제 2 상용제의 함유량이, 상기 (A) 수첨 블록 공중합체 100 질량부에 대하여 5 질량부 이상 60 질량부 이하일 수 있다.9. The pressure-sensitive adhesive composition for optical use according to any one of 1 to 8 above, wherein the content of the second compatibilizing agent (C) is 5 parts by mass or more and 60 parts by mass or less per 100 parts by mass of the hydrogenated block copolymer (A) ≪ / RTI >
10. 상기 1 내지 9 중 어느 하나에 기재된 광학용 점착제 조성물에 있어서, 상기 (B) 제 1 상용제 및 상기 (C) 제 2 상용제의 합계 함유량이, 상기 (A) 수첨 블록 공중합체 100 질량부에 대하여 10 질량부 이상 80 질량부 이하일 수 있다.10. The optical pressure-sensitive adhesive composition for optical use according to any one of 1 to 9 above, wherein the total content of the first compatibilizing agent (B) and the second compatibilizing agent (C) is 100 parts by mass of the hydrogenated block copolymer (A) And more preferably 10 parts by mass or more and 80 parts by mass or less.
11. 상기 1 내지 10 중 어느 하나에 기재된 광학용 점착제 조성물에 있어서, 상기 소프트 세그먼트에 상용하고, 또한 상온 (23 ℃) 에 있어서 고체인 (D) 제 3 상용제를 추가로 함유하고, 상기 (D) 제 3 상용제는, 로진계 점착 부여 수지, 테르펜계 점착 부여 수지, 또는 수첨 지환족 탄화수소 수지일 수 있다.(11) The pressure-sensitive adhesive composition for optical use according to any one of (1) to (10), further comprising (D) a third compatibilizing agent which is soluble in the soft segment and is solid at room temperature D) The third compatibilizing agent may be a rosin-based tackifying resin, a terpene-based tackifying resin, or a hydrogenated cycloaliphatic hydrocarbon resin.
12. 상기 1 내지 11 중 어느 하나에 기재된 광학용 점착제 조성물에 있어서, 상기 점착제층은, 주파수 1.0 × 106 ㎐ 에서의 비유전율이, 주파수 1.0 × 102 ㎐ 에서의 비유전율의 90 ％ 이상일 수 있다.12. The pressure-sensitive adhesive composition for optical use according to any one of 1 to 11 above, wherein the pressure-sensitive adhesive layer has a relative dielectric constant at a frequency of 1.0 × 10 6 Hz of 90% or more of a relative dielectric constant at a frequency of 1.0 × 10 2 Hz have.
13. 상기 1 내지 12 중 어느 하나에 기재된 광학용 점착제 조성물에 있어서, 터치 패널식 입출력 장치를 구성하는 부재의 첩합에 사용할 수 있다.13. The pressure-sensitive adhesive composition for optical use according to any one of 1 to 12 above, which can be used for bonding members constituting a touch panel type input / output device.
14. 본 발명의 다른 하나의 양태에 관련된 점착 시트는, 상기 1 내지 13 중 어느 하나에 기재된 광학용 점착제 조성물을 세퍼레이터의 표면에 도포하고, 건조시켜 얻어진다.14. A pressure-sensitive adhesive sheet according to another embodiment of the present invention is obtained by applying the pressure-sensitive adhesive composition for optical use according to any one of 1 to 13 above to the surface of a separator and drying it.
15. 본 발명의 다른 하나의 양태에 관련된 화상 표시 장치는, 상기 1 내지 13 중 어느 하나에 기재된 광학용 점착제 조성물을 사용하여 형성된 점착제층을 포함한다.15. An image display apparatus according to another aspect of the present invention comprises a pressure-sensitive adhesive layer formed using the optical pressure-sensitive adhesive composition according to any one of 1 to 13 above.
16. 본 발명의 다른 하나의 양태에 관련된 입출력 장치는, 상기 1 내지 13 중 어느 하나에 기재된 광학용 점착제 조성물을 사용하여 형성된 점착제층을 포함한다.16. An input / output device according to another aspect of the present invention comprises a pressure-sensitive adhesive layer formed using the optical pressure-sensitive adhesive composition according to any one of the above-mentioned 1 to 13. [
상기 광학용 점착제 조성물은, (A) 성분, (B) 성분 및 (C) 성분을 함유함으로써, 그 광학용 점착제 조성물로부터 얻어지는 점착제층의 비유전율이 1 이상 3.5 이하가 되기 때문에, 표시 장치에 포함되는 내부 회로에서 발생하는 노이즈에 의한 오작동이나, 도전체에 끼워진 유전체의 차지가 일으키는 오작동을 방지할 수 있고, 또한 내구성, 밀착성 및 내후성이 우수한 점착제층을 얻을 수 있다. 또, 상기 광학용 점착제 조성물을 사용한 상기 화상 표시 장치 및 입출력 장치는, 내구성, 밀착성 및 내후성이 우수한 점착제층을 갖고, 또한 내부 회로에서 발생하는 노이즈에 의한 오작동을 방지할 수 있다.Since the optical pressure-sensitive adhesive composition for optical use contains the component (A), the component (B) and the component (C), the relative dielectric constant of the pressure-sensitive adhesive layer obtained from the optical pressure- It is possible to prevent the malfunction caused by the noise generated in the internal circuit or the malfunction caused by the charge of the dielectric sandwiched by the conductor, and to obtain the pressure-sensitive adhesive layer having excellent durability, adhesion and weather resistance. The image display apparatus and the input / output device using the optical pressure-sensitive adhesive composition described above have a pressure-sensitive adhesive layer excellent in durability, adhesion, and weather resistance, and can prevent malfunction due to noise generated in the internal circuit.
도 1 은 본 발명의 실시예 1 에 관련된 점착제 조성물을 구성하는 (A) 성분 (수첨 블록 공중합체) 으로 형성된 점착제층의 비유전율과 주파수의 관계를 모식적으로 설명하는 도면이다.
도 2 는 본 발명의 일 실시형태에 관련된 출입력 장치 (터치 패널식 입출력 장치) 의 구성을 모식적으로 나타내는 단면도이다.
도 3 은 공지된 출입력 장치 (터치 패널식 입출력 장치) 의 구성을 모식적으로 나타내는 단면도이다.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a view for schematically explaining a relationship between a relative dielectric constant and a frequency of a pressure-sensitive adhesive layer formed of a component (A) (hydrogenated block copolymer) constituting the pressure-sensitive adhesive composition according to Example 1 of the present invention.
2 is a cross-sectional view schematically showing the configuration of an input / output device (touch panel type input / output device) according to an embodiment of the present invention.
3 is a cross-sectional view schematically showing the configuration of a known input / output device (touch panel type input / output device).
이하, 도면을 참조하면서 본 발명을 상세하게 설명한다. 또한, 본 발명에 있어서, 각별히 언급하지 않는 한,「부」는「질량부」를 의미하고,「％」는「질량％」를 의미한다.Hereinafter, the present invention will be described in detail with reference to the drawings. In the present invention, unless otherwise specified, "part" means "part by mass" and "%" means "% by mass".
1. 광학용 점착제 조성물1. Pressure-sensitive adhesive composition for optical use
본 발명의 일 실시형태에 관련된 광학용 점착제 조성물 (이하, 간단히「점착제 조성물」이라고 기재하는 경우도 있다.) 은, (A) 수첨 블록 공중합체 (이하, 간단히「(A) 성분」이라고 기재하는 경우도 있다.) 와, (B) 제 1 상용제 (이하, 간단히「(B) 성분」이라고 기재하는 경우도 있다.) 와, (C) 제 2 상용제 (이하, 간단히「(C) 성분」이라고 기재하는 경우도 있다.) 를 함유한다. 본 실시형태에 관련된 광학용 점착제 조성물로부터 얻어지는 점착제층의 비유전율은 1 이상 3.5 이하이다.The pressure-sensitive adhesive composition for optical use according to one embodiment of the present invention (hereinafter sometimes simply referred to as "pressure-sensitive adhesive composition") is a pressure-sensitive adhesive composition comprising a hydrogenated block copolymer (hereinafter, simply referred to as "component (A) (Hereinafter sometimes simply referred to as "component (B)"), (C) a second compatibilizing agent (hereinafter simply referred to as "component (C) Quot;) may be included. The relative dielectric constant of the pressure-sensitive adhesive layer obtained from the optical pressure-sensitive adhesive composition according to the present embodiment is 1 or more and 3.5 or less.
1.1. (A) 성분1.1. (A) Component
(A) 성분인 수첨 (수소 첨가 : hydrogenated) 블록 공중합체는, 방향족 비닐 단량체의 중합체 성분으로 구성되는 하드 세그먼트와, 공액 디엔 단량체의 중합체 성분으로 구성되는 소프트 세그먼트를 갖는 열가소성 엘라스토머이다. 여기서, 보다 구체적으로는, 방향족 비닐 화합물은 스티렌, α-메틸스티렌인 것이 바람직하고 (보다 바람직하게는 스티렌), 공액 (conjugate) 디엔 화합물은 부타디엔, 이소프렌인 것이 바람직하다.The hydrogenated block copolymer (A) is a thermoplastic elastomer having a hard segment composed of a polymer component of an aromatic vinyl monomer and a soft segment composed of a polymer component of a conjugated diene monomer. More specifically, the aromatic vinyl compound is preferably styrene,? -Methylstyrene (more preferably styrene), and the conjugated diene compound is preferably butadiene or isoprene.
(A) 성분을 함유하는 본 실시형태에 관련된 점착제 조성물을 사용하여 형성된 점착제층은, 아크릴계 폴리머를 함유하는 점착제 조성물로 형성되는 점착제층과 비교하여, 비유전율이 낮다는 특징을 갖는다 (예를 들어, 비유전율이 1 이상 3.5 이하).The pressure-sensitive adhesive layer formed using the pressure-sensitive adhesive composition according to the present embodiment containing the component (A) is characterized in that the relative dielectric constant is low as compared with the pressure-sensitive adhesive layer formed of the pressure-sensitive adhesive composition containing an acrylic polymer , And a relative dielectric constant of 1 or more and 3.5 or less).
(A) 성분의 구체예로는, 예를 들어, 스티렌-(에틸렌-프로필렌)-스티렌형 블록 공중합체 (SEPS) (스티렌-이소프렌-스티렌형 블록 공중합체 (SIS) 의 수소 첨가물), 스티렌-(부타디엔-부틸렌)-스티렌형 블록 공중합체 (SBBS) 의 수소 첨가물, 스티렌-(에틸렌-부틸렌)-스티렌형 블록 공중합체 (SEBS) (스티렌-부타디엔-스티렌형 블록 공중합체 (SBS) 의 수소 첨가물), 스티렌-(에틸렌-프로필렌)형 블록 공중합체 (SEP) (스티렌-이소프렌형 블록 공중합체 (SI) 의 수소 첨가물), 스티렌-(에틸렌-부틸렌)형 블록 공중합체 (SEB) (스티렌-부타디엔형 블록 공중합체 (SB) 의 수소 첨가물) 등을 들 수 있다. 그 중에서도, (B) 성분과의 상용성이 우수한 관점에서, (A) 성분은, 스티렌-(에틸렌-프로필렌)-스티렌형 블록 공중합체 (SEPS), 스티렌-(에틸렌-부틸렌)-스티렌형 블록 공중합체 (SEBS) 등의 ABA 형 수첨 블록 공중합체가 특히 바람직하다. 이것들은 단독으로 사용해도 되고, 또 2 종 이상을 혼합하여 사용해도 된다.Specific examples of the component (A) include styrene- (ethylene-propylene) -styrene type block copolymer (SEPS) (hydrogenated product of styrene-isoprene-styrene type block copolymer (SIS)), styrene- (Ethylene-butylene) styrene block copolymer (SEBS) (styrene-butadiene-styrene block copolymer (SBS)), a hydrogenated product of a styrene-butadiene-styrene block copolymer (Ethylene-propylene) block copolymer (SEP) (hydrogenated product of styrene-isoprene type block copolymer (SI)), styrene- (ethylene-butylene) type block copolymer (SEB) Styrene-butadiene type block copolymer (SB)), and the like. Among them, the component (A) is preferably a styrene- (ethylene-propylene) -styrene type block copolymer (SEPS), a styrene- (ethylene-butylene) -styrene type Block copolymers (SEBS) and the like are particularly preferred. These may be used alone or in combination of two or more.
본 발명에 있어서「상용성을 갖는다 (compatible)」또는「상용한다 (compatibilizing)」란, 상이한 2 개의 성분을 혼합하여 얻어지는 혼합물에 있어서, 탁함 또는 상분리가 육안으로 확인되지 않는 것을 말한다.In the present invention, " compatible " or " compatibilizing " means that turbidity or phase separation is not visually recognized in a mixture obtained by mixing two different components.
여기서, (B) 성분이 (A) 성분을 구성하는 하드 세그먼트에 상용하는지 여부는, (A) 성분의 하드 세그먼트에 상당하는 성분, 즉 방향족 비닐 단량체만으로부터 합성되는 중합체와, (B) 성분을 사용하여 평가하는 것으로 한다.Whether or not the component (B) is miscible with the hard segment constituting the component (A) depends on the component corresponding to the hard segment of the component (A), that is, the polymer synthesized from only the aromatic vinyl monomer, and the component And evaluated by using.
보다 구체적으로는, 방향족 비닐 단량체만으로부터 중합되는 중합체와 (B) 성분을, 필요에 따라 용매를 사용하여 혼합하여 얻어지는 혼합물에 있어서 탁함의 발생, 또는 그 중합체를 함유하는 상과 (B) 성분을 함유하는 상의 상분리가 육안으로 보이지 않는 경우에는, (B) 성분은 (A) 성분을 구성하는 하드 세그먼트에 상용하는 것으로 하고, 한편, 상기 서술한 탁함 또는 상분리가 육안으로 보이는 경우, (B) 성분은 (A) 성분을 구성하는 하드 세그먼트에 상용하지 않는 것으로 한다.More specifically, in the mixture obtained by mixing the polymer to be polymerized from the aromatic vinyl monomer alone and the component (B), if necessary, by using a solvent, turbidity is generated or the phase containing the polymer and the component (B) (B) is used in the hard segment constituting the component (A), and when the turbidity or the phase separation described above is visible to the naked eye, the component (B) Is not commonly used in the hard segment constituting the component (A).
(A) 성분으로는, 시판되는 수첨 블록 공중합체, 예를 들어, SEP 형의 셉톤 1001 및 1020, SEPS 형의 셉톤 2002, 2004, 2005, 2006, 2007, 2063 및 2104, SEBS 형의 셉톤 8004, 8006, 8007, 8076 및 8104 (상기의 셉톤 시리즈는 모두 쿠라레사 제조), SEBS 형의 터프텍 H1221, H1662, H1052, H1053, H1041, H1051, H1517, H1043, H1272 및 N504, SBBS 형의 터프텍 P1500, P2000 및 JT83X (상기의 터프텍 시리즈는 모두 아사히화성사 제조) 등을 사용할 수도 있다.SEP type Septtons 2002, 2004, 2005, 2006, 2007, 2063 and 2104, SEBS-type Septtop 8004, and SEP type SEPTON 8006. Examples of the component (A) include commercially available hydrogenated block copolymers such as SEP type septones 1001 and 1020, H1061, H1041, H1051, H1517, H1043, H1272 and N504 of the SEBS type, Tuftec P1500 of the SBBS type (trade name, manufactured by Sumitomo Chemical Co., Ltd.), 8006, 8007, 8076 and 8104 , P2000 and JT83X (all of the above-mentioned Tuftec series manufactured by Asahi Chemical Industry Co., Ltd.) may be used.
본 실시형태에 관련된 점착제 조성물에 내열성을 부여하는 관점에서, (A) 성분에 있어서의 하드 세그먼트 (예를 들어 스티렌) 의 함유율은 5 질량％ 이상 70 질량％ 이하인 것이 바람직하고, 10 질량％ 이상 60 질량％ 이하인 것이 보다 바람직하다. (A) 성분에 있어서의 하드 세그먼트의 함유율이 5 질량％ 미만이면 내열성이 열등하고, 한편 70 질량％ 를 초과하면, 점착제층이 지나치게 단단해져, 피착체와의 밀착성이 열등한 경우가 있다.The content of the hard segment (for example, styrene) in the component (A) is preferably 5% by mass or more and 70% by mass or less, more preferably 10% by mass or more and 60% or less by mass, from the viewpoint of imparting heat resistance to the pressure- And more preferably not more than 1 mass%. If the content of the hard segment in the component (A) is less than 5 mass%, the heat resistance is inferior. If the content of the hard segment exceeds 70 mass%, the pressure-sensitive adhesive layer becomes excessively hard and the adhesion with the adherend may be inferior.
또, (C) 성분과의 상용성이 우수한 관점에서, (A) 성분을 구성하는 공액 디엔 단량체의 중합체 성분에 함유되는 2 중 결합의 수첨률 (수소 첨가 비율) (이하, 간단히「수첨률」이라고도 한다.) 은 90 ％ 이상인 것이 바람직하고, 95 ％ 이상인 것이 보다 바람직하다 (또한, 수첨률은 100 ％ 인 것이 바람직하지만, 흔적량의 2 중 결합이 잔존해도 지장없다). 즉, 본 발명에 있어서, 공액 디엔 단량체의 중합체 성분에 함유되는 2 중 결합의 수첨률이란, 공액 디엔 단량체의 중합체 성분에 함유되는 2 중 결합 중, 수소 첨가에 의해 포화되어 있는 것의 비율을 말한다.From the viewpoint of excellent compatibility with the component (C), the number of double bonds (hydrogenation ratio) contained in the polymer component of the conjugated diene monomer constituting the component (A) (hereinafter simply referred to as " ) Is preferably not less than 90%, more preferably not less than 95% (more preferably 100%, but no trace of double bonds remain). That is, in the present invention, the hydroxyl number of the double bond contained in the polymer component of the conjugated diene monomer refers to the proportion of the double bonds contained in the polymer component of the conjugated diene monomer that are saturated by hydrogenation.
여기서, (C) 성분이 (A) 성분을 구성하는 소프트 세그먼트에 상용하는지 여부는, (A) 성분의 소프트 세그먼트에 상당하는 성분, 즉 공액 디엔 단량체만으로부터 합성되는 중합체와, (B) 성분을 사용하여 평가하는 것으로 한다.Whether or not the component (C) is miscible with the soft segment constituting the component (A) can be determined by using a component corresponding to the soft segment of the component (A), that is, a polymer synthesized from only the conjugated diene monomer, And evaluated by using.
보다 구체적으로는, 공액 디엔 단량체만으로부터 중합되는 중합체와 (C) 성분을, 필요에 따라 용매를 사용하여 혼합하여 얻어지는 혼합물에 있어서 탁함의 발생, 또는 그 중합 물체를 함유하는 상과 (C) 성분을 함유하는 상 사이에서 상분리의 발생이 육안으로 보이지 않는 경우에는, (C) 성분은 (A) 성분을 구성하는 소프트 세그먼트에 상용하는 것으로 하고, 한편 상기 서술한 탁함 또는 상분리가 육안으로 보이는 경우, (C) 성분은 (A) 성분을 구성하는 소프트 세그먼트에 상용하지 않는 것으로 한다.More specifically, occurrence of turbulence in the mixture obtained by mixing the polymer to be polymerized from only the conjugated diene monomer with the component (C) and, if necessary, a solvent, or a mixture of the phase containing the polymerized product and the component (C) (C) is compatible with the soft segment constituting the component (A). On the other hand, when the turbidity or phase separation described above is visible to the naked eye, (C) is not compatible with the soft segment constituting the component (A).
또한, 피착체의 부식을 방지할 수 있는 관점에서, 본 실시형태에 관련된 점착제 조성물의 산가는 1 이하인 것이 바람직하다.From the viewpoint of preventing corrosion of the adherend, the acid value of the pressure-sensitive adhesive composition according to the present embodiment is preferably 1 or less.
본 실시형태에 관련된 점착제 조성물에 있어서의 (A) 성분의 함유량은 50 질량％ 이상 90 질량％ 이하인 것이 바람직하고, 55 질량％ 이상 80 질량％ 이하인 것이 보다 바람직하다.The content of the component (A) in the pressure-sensitive adhesive composition according to the present embodiment is preferably 50 mass% or more and 90 mass% or less, more preferably 55 mass% or more and 80 mass% or less.
1.2. (B) 성분1.2. Component (B)
(B) 성분인 제 1 상용제는, (A) 성분을 구성하는 하드 세그먼트에 상용하는 성질을 갖고, 또한 연화점 (softening point) 이 80 ℃ 이상이다. 본 실시형태에 관련된 점착제 조성물이 (B) 성분을 함유함으로써, (B) 성분이 (A) 성분을 구성하는 하드 세그먼트에 상용하기 때문에, 그 점착제 조성물로 형성되는 점착제층에, 어느 정도의 경도를 부여하면서, 피착체에 대한 밀착성을 높일 수 있고, 또한 그 점착제층의 내열성을 높일 수 있다.The first compatibilizing agent which is a component (B) has properties compatible with the hard segment constituting the component (A) and has a softening point of 80 ° C or higher. Since the pressure-sensitive adhesive composition according to the present embodiment contains the component (B), since the component (B) is compatible with the hard segment constituting the component (A), the pressure-sensitive adhesive layer formed of the pressure- The adhesion to the adherend can be increased and the heat resistance of the pressure-sensitive adhesive layer can be increased.
(B) 성분은 예를 들어, 방향족계 점착 부여 수지 (tackifier resin) 일 수 있다. (B) 성분으로서 사용되는 방향족계 점착 부여 수지는, 상용성의 관점에서는 분자량 5,000 이하인 것이 바람직하다. (B) 성분으로서 사용 가능한 방향족계 점착 부여 수지로는, 예를 들어, 방향족 석유 수지, 스티렌계 중합체, α-메틸스티렌계 중합체, 스티렌-(α-메틸스티렌)계 공중합체, 스티렌-지방족 탄화수소계 공중합체, 스티렌-(α-메틸스티렌)-지방족 탄화수소계 공중합체, 스티렌-방향족 탄화수소계 공중합체 등을 들 수 있다. 보다 구체적으로는, 예를 들어 시판되는 스티렌-방향족 탄화수소계 공중합체로서의 FMR-0150 (연화점 145 ℃, 미츠이 화학사 제조), 스티렌-지방족 탄화수소계 공중합체로서의 FTR-6100 (연화점 100 ℃, 미츠이 화학사 제조), FTR-6110 (연화점 110 ℃, 미츠이 화학사 제조) 및 FTR-6125 (연화점 125 ℃, 미츠이 화학사 제조), 스티렌-(α-메틸스티렌)-지방족 탄화수소계 공중합체로서의 FTR-7100 (연화점 100 ℃, 미츠이 화학사 제조), 스티렌계 중합체로서의 FTR-8120 (연화점 120 ℃, 미츠이 화학사 제조) 및 SX-100 (연화점 100 ℃, 야스하라 케미컬사 제조), α-메틸스티렌계 중합체로서의 FTR-0100 (연화점 100 ℃, 미츠이 화학사 제조), 스티렌-(α-메틸스티렌)계 공중합체로서의 FTR-2120 (연화점 120 ℃, 미츠이 화학사 제조), FTR-2140 (연화점 145 ℃, 미츠이 화학사 제조), 크리스탈렉스 3100 (연화점 100 ℃, 이스트맨 케미컬사 제조), 크리스탈렉스 3085 (연화점 85 ℃, 이스트맨 케미컬사 제조), 크리스탈렉스 5140 (연화점 140 ℃, 이스트맨 케미컬사 제조), 크리스탈렉스 1120 (연화점 120 ℃, 이스트맨 케미컬사 제조), 크리스탈렉스 F85 (연화점 85 ℃, 이스트맨 케미컬사 제조), 크리스탈렉스 F100 (연화점 100 ℃, 이스트맨 케미컬사 제조) 및 크리스탈렉스 F115 (연화점 115 ℃, 이스트맨 케미컬사 제조), 등을 사용할 수도 있다.The component (B) may be, for example, an aromatic tackifier resin. The aromatic tackifying resin used as the component (B) preferably has a molecular weight of 5,000 or less from the viewpoint of compatibility. Examples of the aromatic tackifying resin that can be used as the component (B) include aromatic petroleum resins, styrene type polymers, alpha -methylstyrene type polymers, styrene- (alpha-methylstyrene) type copolymers, styrene-aliphatic hydrocarbons Based copolymer, a styrene- (? -Methylstyrene) -aliphatic hydrocarbon-based copolymer, and a styrene-aromatic hydrocarbon-based copolymer. More specifically, for example, FMR-0150 (softening point 145 ° C, manufactured by Mitsui Chemicals, Inc.) as a styrene-aromatic hydrocarbon copolymer commercially available, FTR-6100 (softening
본 실시형태에 관련된 점착제 조성물에 내구성을 부여하여, 피착체와의 밀착성을 높일 수 있고, 또한 내구성을 높일 수 있는 관점에서, (B) 성분의 연화점은 80 ℃ 이상일 수 있고, 95 ℃ 이상인 것이 바람직하고, 140 ℃ 초과인 것이 보다 바람직하다.The softening point of the component (B) may be 80 ° C or higher, preferably 95 ° C or higher, from the viewpoint of imparting durability to the pressure-sensitive adhesive composition according to the present embodiment and enhancing adhesion with an adherend and improving durability And more preferably more than 140 ° C.
본 실시형태에 관련된 점착제 조성물에 있어서의 (B) 성분의 함유량은 5 질량％ 이상 35 질량％ 이하인 것이 바람직하고, 10 질량％ 이상 30 질량％ 이하인 것이 보다 바람직하다. 또, (A) 성분과의 상용성을 높일 수 있는 관점에서, (B) 성분의 함유량은, (A) 성분 100 질량부에 대하여 5 질량부 이상 60 질량부 이하인 것이 바람직하고, 10 질량부 이상 55 질량부 이하인 것이 보다 바람직하다.The content of the component (B) in the pressure-sensitive adhesive composition according to the present embodiment is preferably 5 mass% or more and 35 mass% or less, more preferably 10 mass% or more and 30 mass% or less. The content of the component (B) is preferably 5 parts by mass or more and 60 parts by mass or less, more preferably 10 parts by mass or more, per 100 parts by mass of the component (A) from the viewpoint of enhancing compatibility with the component (A) More preferably 55 parts by mass or less.
1.3. (C) 성분1.3. (C) Component
(C) 성분인 제 2 상용제는, (A) 성분을 구성하는 소프트 세그먼트에 상용하는 성질을 갖고, 또한 상온 (23 ℃) 에 있어서 액체이다. 또한, 본 발명에서 말하는 바의「액체」란, 점조 (粘稠) 인 점탄성 (viscoelastic) 액체나, 그 외에 저점도의 액체도 포함하는 것이다. 본 실시형태에 관련된 점착제 조성물이 (C) 성분을 함유함으로써, (C) 성분이 (A) 성분을 구성하는 소프트 세그먼트에 상용하기 때문에, 그 점착제층의 젖음성 (wettability) 을 높이는 것에 의한 결과로서, 내구성을 높일 수 있다. (C) 성분은 예를 들어, 폴리부텐계 화합물, 폴리이소부틸렌계 화합물, 폴리이소프렌계 화합 등의 지방족 탄화수소를 함유하는 연화제일 수 있다. (C) 성분으로서 사용 가능한 연화제로는, 시판되는 연화제, 예를 들어 폴리부텐계 화합물로서 닛세키 폴리부텐 LV-7, LV-50, LV-100, HV-15, HV-35, HV-50, HV-100, HV-300, HV-1900 및 SV-7000 (모두 JX 닛코 닛세키 에너지사 제조), 폴리이소부틸렌계 화합물로서 테트락스 3T, 4T, 5T 및 6T, 하이몰 4H, 5H, 5.5H 및 6H (모두 JX 닛코 닛세키 에너지사 제조), 폴리이소프렌계 화합물로서 쿠라프렌 LIR-290 (쿠라레사 제조) 등을 사용할 수도 있다.The second compatibilizing agent which is the component (C) has properties compatible with the soft segment constituting the component (A) and is a liquid at room temperature (23 캜). The term " liquid " in the present invention includes a viscoelastic liquid which is viscous or a liquid having a low viscosity. As the pressure-sensitive adhesive composition according to the present embodiment contains the component (C), the component (C) is compatible with the soft segment constituting the component (A), and as a result of improving the wettability of the pressure- Durability can be increased. The component (C) may be, for example, a softener containing an aliphatic hydrocarbon such as a polybutene-based compound, a polyisobutylene-based compound, or a polyisoprene-based compound. LV-50, LV-100, HV-15, HV-35, HV-50 (manufactured by Nisseki Polybutene) as a softening agent that can be used as the component (C) , HV-100, HV-300, HV-1900 and SV-7000 (both manufactured by JX Nikkorieski Energy Co., Ltd.), tetrax 3T, 4T, 5T and 6T as polyisobutylene compounds, H and 6H (all manufactured by JX Nikkiso Co., Ltd.), and polyphenylene compound (manufactured by Kuraray Co., Ltd.) may be used.
본 실시형태에 관련된 점착제 조성물에 있어서의 (C) 성분의 함유량은 5 질량％ 이상 35 질량％ 이하인 것이 바람직하고, 10 질량％ 이상 30 질량％ 이하인 것이 보다 바람직하다. 또, (A) 성분과의 상용성을 높일 수 있는 관점에서, (C) 성분의 함유량은, (A) 성분 100 질량부에 대하여 5 질량부 이상 60 질량부 이하인 것이 바람직하고, 10 질량부 이상 55 질량부 이하인 것이 보다 바람직하다. 또한, (B) 성분 및 (C) 성분의 합계 함유량은, (A) 성분 100 질량부에 대하여 10 질량부 이상 80 질량부 이하인 것이 바람직하고, 15 질량부 이상 80 질량부 이하인 것이 보다 바람직하고, 20 질량부 이상 75 질량부 이하인 것이 더욱 바람직하다.The content of the component (C) in the pressure-sensitive adhesive composition according to the present embodiment is preferably 5 mass% or more and 35 mass% or less, more preferably 10 mass% or more and 30 mass% or less. From the viewpoint of enhancing compatibility with the component (A), the content of the component (C) is preferably 5 parts by mass or more and 60 parts by mass or less with respect to 100 parts by mass of the component (A), more preferably 10 parts by mass or more More preferably 55 parts by mass or less. The total content of the component (B) and the component (C) is preferably 10 parts by mass or more and 80 parts by mass or less, more preferably 15 parts by mass or more and 80 parts by mass or less, based on 100 parts by mass of the component (A) More preferably 20 parts by mass or more and 75 parts by mass or less.
1.4. 비유전율1.4. Relative dielectric constant
본 실시형태에 관련된 광학용 점착제 조성물로부터 얻어지는 점착제층의 비유전율은, 주파수가 1.0 × 102 ∼ 1.0 × 106 ㎐ 에 있어서 측정된 비유전율의 값이다. 본 실시형태에 관련된 광학용 점착제 조성물로부터 얻어지는 점착제층의 비유전율은 1 이상 3.5 이하이고, 1 이상 3.2 이하인 것이 바람직하고, 1 이상 2.8 이하인 것이 더욱 바람직하다. 본 실시형태에 관련된 광학용 점착제 조성물로부터 얻어지는 점착제층은, 주파수 1.0 × 106 ㎐ 에서의 비유전율이, 주파수 1.0 × 102 ㎐ 에서의 비유전율의 90 ％ 이상일 수 있고, 95 ％ 이상인 것이 바람직하다. 이와 같이, 점착제층은, 주파수 1.0 × 106 ㎐ 에서의 비유전율이, 주파수 1.0 × 102 ㎐ 에서의 비유전율의 90 ％ 이상인 것에 의해, 폭넓은 주파수 영역에 있어서 안정적인 비유전율을 갖기 때문에, 그 점착제층이 형성된 화상 표시 장치 또는 입출력 장치에 있어서, 고주파 펄스에 의한 오작동을 방지할 수 있다.The relative dielectric constant of the pressure-sensitive adhesive layer obtained from the optical pressure-sensitive adhesive composition according to the present embodiment is a value of a relative dielectric constant measured at a frequency of 1.0 × 10 2 to 1.0 × 10 6 Hz. The relative dielectric constant of the pressure-sensitive adhesive layer obtained from the optical pressure-sensitive adhesive composition related to this embodiment is preferably 1 or more and 3.5 or less, more preferably 1 or more and 3.2 or less, and further preferably 1 or more and 2.8 or less. The pressure-sensitive adhesive layer obtained from the pressure-sensitive adhesive composition for optical use according to the present embodiment may have a relative dielectric constant at a frequency of 1.0 × 10 6 Hz of 90% or more of a relative dielectric constant at a frequency of 1.0 × 10 2 Hz, and preferably 95% . As described above, since the pressure-sensitive adhesive layer has a relative dielectric constant at a frequency of 1.0 x 10 6 Hz and a relative dielectric constant of at least 90% of a relative dielectric constant at a frequency of 1.0 x 10 2 Hz, Malfunction due to high frequency pulses can be prevented in an image display apparatus or an input / output apparatus having a pressure-sensitive adhesive layer formed thereon.
본 발명에 있어서, 비유전율은, 후술하는 실시예에 기재된 방법으로 측정된 값이다.In the present invention, the relative dielectric constant is a value measured by the method described in the following embodiment.
1.5. (D) 성분1.5. (D) Component
(D) 성분인 제 3 상용제는, 적어도 (A) 성분을 구성하는 소프트 세그먼트에 상용하는 성질을 갖고, 또한 상온 (23 ℃) 에 있어서 고체이다. (D) 성분은, 로진계 점착 부여 수지, 테르펜계 점착 부여 수지, 또는 수첨 지환족 탄화수소 수지일 수 있다. (D) 성분으로는, 예를 들어, KE311 (담색 로진계 점착 부여 수지, 아라카와 화학사 제조), TH130 (테르펜 페놀형 점착 부여 수지, 야스하라 케미컬사 제조), P-100 (수첨 지환족 포화 탄화수소 수지, 아라카와 화학사 제조) 을 사용할 수 있다.The third compatibilizing agent as the component (D) has properties compatible with at least the soft segment constituting the component (A) and is a solid at room temperature (23 캜). The component (D) may be a rosin-based tackifying resin, a terpene-based tackifying resin, or a hydrogenated cycloaliphatic hydrocarbon resin. (Terpene phenol type tackifying resin, manufactured by Yasuhara Chemical Co., Ltd.), P-100 (a hydrogenated cycloaliphatic saturated hydrocarbon (trade name, manufactured by Yasuhara Chemical Co., Ltd.)), Resin, manufactured by Arakawa Chemical Industries, Ltd.) can be used.
본 실시형태에 관련된 점착제 조성물에 있어서의 (D) 성분의 함유량은 5 질량％ 이상 35 질량％ 이하인 것이 바람직하고, 10 질량％ 이상 30 질량％ 이하인 것이 보다 바람직하다. 또, (A) 성분과의 상용성을 높일 수 있는 관점에서, (D) 성분의 함유량은, (A) 성분 100 질량부에 대하여 5 질량부 이상 60 질량부 이하인 것이 바람직하고, 10 질량부 이상 55 질량부 이하인 것이 보다 바람직하다. 또한, (C) 성분 및 (D) 성분의 합계 함유량은, (A) 성분 100 질량부에 대하여 10 질량부 이상 80 질량부 이하인 것이 바람직하고, 15 질량부 이상 80 질량부 이하인 것이 보다 바람직하고, 20 질량부 이상 75 질량부 이하인 것이 더욱 바람직하다.The content of the component (D) in the pressure-sensitive adhesive composition according to the present embodiment is preferably 5 mass% or more and 35 mass% or less, more preferably 10 mass% or more and 30 mass% or less. From the viewpoint of enhancing compatibility with the component (A), the content of the component (D) is preferably 5 parts by mass or more and 60 parts by mass or less with respect to 100 parts by mass of the component (A), more preferably 10 parts by mass or more More preferably 55 parts by mass or less. The total content of the components (C) and (D) is preferably 10 parts by mass or more and 80 parts by mass or less, more preferably 15 parts by mass or more and 80 parts by mass or less, based on 100 parts by mass of the component (A) More preferably 20 parts by mass or more and 75 parts by mass or less.
1.6. 용도1.6. Usage
본 실시형태에 관련된 광학용 점착제 조성물은, 화상 표시 장치나 입출력 장치를 구성하는 부재의 첩합에 사용할 수 있다. 본 실시형태에 관련된 광학용 점착제 조성물을 사용한 첩합의 대상이 되는 부재는, 광학 부재 (예를 들어, 편광 필름, 위상차 필름, 타원 편광 필름, 반사 방지 필름, 휘도 향상 필름, 광확산 필름 및 하드 코트 필름으로 이루어지는 군에서 선택되는 광학 필름), ITO 층 등의 금속층, 또는 유리 또는 플라스틱으로 이루어지는 기재이어도 된다. 보다 구체적으로는, 본 실시형태에 관련된 광학용 점착제 조성물은, 터치 패널식 입출력 장치를 구성하는 부재의 첩합에 바람직하게 사용할 수 있다.The optical pressure-sensitive adhesive composition for use in the present embodiment can be used for bonding an image display apparatus and a member constituting an input / output apparatus. The member to be subjected to the cohesion using the optical pressure-sensitive adhesive composition according to the present embodiment may be an optical member (such as a polarizing film, a retardation film, an elliptically polarizing film, an antireflection film, a brightness improving film, Film), a metal layer such as an ITO layer, or a substrate made of glass or plastic. More specifically, the optical pressure-sensitive adhesive composition according to the present embodiment can be suitably used for bonding members constituting the touch panel type input / output device.
본 실시형태에 관련된 광학용 점착제 조성물을, 터치 패널식 출입력 장치를 구성하는 부재의 첩합에 사용한 예를, 도 2 를 참조하여 설명한다. 도 2 는, 본 발명의 일 실시형태에 관련된 출입력 장치 (터치 패널식 입출력 장치 (100)) 의 구성을 모식적으로 나타내는 단면도이다. 본 실시형태에 관련된 터치 패널식 출입력 장치 (100) 는, 액정 표시 장치 (LCD) (10) 와, 터치 패널부 (20) 와, LCD (10) 와, 터치 패널부 (20) 사이에 형성된 접착제층 (30) 을 포함한다. 접착제층 (30) 은 LCD (10) 와 터치 패널부 (20) 를 접착한다. 접착제층 (30) 은, 예를 들어, 본 실시형태에 관련된 광학용 점착제 조성물을 세퍼레이터 (도시 생략) 의 표면에 도포하고, 건조시켜 얻어진 접착 시트를 세퍼레이터로부터 박리하여, LCD (10) 와 터치 패널 (20) 사이에 설치한 것이다.An example in which the optical pressure-sensitive adhesive composition according to the present embodiment is used for joining members constituting the touch panel type input / output device will be described with reference to Fig. 2 is a cross-sectional view schematically showing the configuration of an input / output device (touch panel type input / output device 100) according to an embodiment of the present invention. The touch panel type input /
또, 도 2 에 나타내는 바와 같이, LCD (10) 는, 편광판 (11) 과, 점착제층 (12) 과, 액정 패널 (13) 과, 점착제층 (14) 과, 편광판 (15) 이 이 순서로 적층되어 구성되어 있다. 점착제층 (12) 은 편광판 (11) 과 액정 패널 (13) 을 접착하고, 점착제층 (14) 은 액정 패널 (13) 과 편광판 (15) 을 접착한다.2, the
또, 도 2 에 나타내는 바와 같이, 터치 패널부 (20) 는, 비산 방지 필름 (16) 과, 점착제층 (17) 과, ITO 층 (18) 과, 유리 패널 (19) 이 이 순서로 적층되어 구성되어 있다. 점착제층 (17) 은, 비산 방지 필름 (16) 과 ITO 층 (18) 을 접착한다.2, the
점착제층 (12, 14, 17) 은, 점착제층 (30) 과 동일하게, 본 실시형태에 관련된 광학용 점착제 조성물을 세퍼레이터 (도시 생략) 의 표면에 도포하고, 건조시켜 얻어진 접착 시트를 세퍼레이터로부터 박리하여 설치한 것이다.The pressure-sensitive adhesive layers 12, 14, and 17 are formed by applying the optical pressure-sensitive adhesive composition according to this embodiment to the surface of a separator (not shown), drying the same, Respectively.
1.7. 작용 효과1.7. Action effect
본 실시형태에 관련된 광학용 점착제 조성물은, (A) 성분, (B) 성분 및 (C) 성분을 함유함으로써, 그 광학용 점착제 조성물로부터 얻어지는 점착제층의 비유전율이 1 이상 3.5 이하인, 저비유전율의 점착제층을 얻을 수 있기 때문에, 표시 장치에 포함되는 내부 회로에서 발생하는 노이즈에 의한 오작동을 방지할 수 있다.The optical pressure-sensitive adhesive composition for an optical system according to the present embodiment contains the component (A), the component (B) and the component (C) so that the pressure-sensitive adhesive layer obtained from the optical pressure- A pressure-sensitive adhesive layer can be obtained, so that it is possible to prevent malfunction due to noise generated in the internal circuit included in the display device.
또, 본 실시형태에 관련된 광학용 점착제 조성물에 있어서, (B) 성분이 (A) 성분을 구성하는 하드 세그먼트에 상용하고, (C) 성분이 (A) 성분을 구성하는 소프트 세그먼트에 상용함으로써, 피착체에 대한 젖음성을 높이는 것에 의해 내구성을 높일 수 있다. 또한, 본 실시형태에 관련된 광학용 점착제 조성물이, 연화점이 80 ℃ 이상인 (B) 성분을 함유함으로써, 내구성 (내열성) 을 높일 수 있다.In the optical pressure-sensitive adhesive composition for an optical element according to the present embodiment, the component (B) is commonly used for the hard segment constituting the component (A) and the component (C) is used for the soft segment constituting the component (A) Durability can be improved by increasing the wettability to the adherend. In addition, durability (heat resistance) can be enhanced by containing the component (B) having a softening point of 80 캜 or higher in the optical pressure-sensitive adhesive composition relating to the present embodiment.
보다 구체적으로는, (C) 성분에서 기인하는, (A) 성분을 구성하는 소프트 세그먼트에 대한 상용에 의한 피착체에 대한 젖음성의 향상과, (B) 성분에서 기인하는, 연화점이 높은 성분에 의한 내열성의 향상의 2 개의 상호 작용에 의해, 점착제층의 내구성을 높일 수 있다. 이것에 의해, 내구성, 밀착성 및 내후성이 우수한 점착제층을 얻을 수 있다.More specifically, it is preferable to improve the wettability of the soft segment constituting the component (A) due to the component (C) to the adherend by commercial application, and to improve the wettability of the adherend due to the component having a high softening point The durability of the pressure-sensitive adhesive layer can be enhanced by the two interactions of improving heat resistance. As a result, a pressure-sensitive adhesive layer having excellent durability, adhesion, and weather resistance can be obtained.
또, 본 실시형태에 관련된 광학용 점착제 조성물을 사용한 화상 표시 장치 및 입출력 장치는, 액정 셀 등의 피착체에 적당한 점착력으로 첩착 (貼着) 되어, 우수한 내구성을 발휘하고, 또한 내부 회로에서 발생하는 노이즈에 의한 오작동을 방지할 수 있다.The image display device and the input / output device using the optical pressure-sensitive adhesive composition according to the present embodiment are bonded (adhered) to an adherend such as a liquid crystal cell with an appropriate adhesive force to exhibit excellent durability, Malfunction due to noise can be prevented.
특히, 본 실시형태에 관련된 광학용 점착제 조성물은, 터치 패널식 입출력 장치를 구성하는 부재의 첩합에 바람직하게 사용할 수 있다.Particularly, the optical pressure-sensitive adhesive composition for use in the present embodiment can be preferably used for bonding members constituting the touch panel type input / output device.
1.7.1. 공지된 출입력 장치의 구성1.7.1. Configuration of the known input / output device
본 실시형태에 관련된 광학용 점착제 조성물의 작용 효과를 보다 구체적으로 설명함에 있어서, 공지된 출입력 장치의 구성에 대하여 설명한다. 도 3 은, 공지된 출입력 장치 (터치 패널식 입출력 장치 (200)) 의 구성을 모식적으로 나타내는 단면도이다. 터치 패널식 입출력 장치 (200) 는, 액정 표시 장치 (LCD) (110) 와 터치 패널부 (120) 를 포함한다. LCD (110) 와 터치 패널부 (120) 사이의 단부에 갭제층 (130) 이 형성되어 있기 때문에, 양단의 갭제층 (130) 사이에는 공극 (140) 이 발생한다.In explaining the function and effect of the optical pressure-sensitive adhesive composition relating to the present embodiment in more detail, the structure of a known input / output device will be described. 3 is a cross-sectional view schematically showing the configuration of a known input / output device (touch panel type input / output device 200). The touch panel type input /
최근, 터치 패널식 입출력 장치의 디스플레이의 고콘스트라스트화가 요구되고 있다. 고콘스트라스트화의 실현을 위하여, 예를 들어, 이전에는 공극이었던 화상 표시부와 터치 센서의 간극 (도 3 에 있어서의 공극 (140)) 을 점착제 등의 투명 재료로 충전하는 수단이 취해지게 되었다. 이것에 의해, 각 계면 간에서의 광의 반사나 굴절이 억제되어, 결과적으로 고콘스트라스트화를 달성할 수 있다.In recent years, there has been a demand for high-contrast display of a display of a touch panel type input / output device. A means for filling the space (the
그러나, 도 3 의 공극 (140) 에 점착제 등을 충전하여 부재를 첩합하는 경우, 장치의 내부 회로로부터 발생하는 고주파 노이즈나 부재의 차지가 원인이 되어, 터치 센서에 오작동을 발생시키는 경우가 있다. 화상 표시부와 터치 센서 (특히 정전 용량 방식의 터치 센서) 의 간극에 공극이 발생한 터치 패널식 입출력 장치에서는, 공극의 공기층의 비유전율이 1 이기 때문에, 이 공기층으로 이루어지는 공극에 의해 노이즈가 차단되므로 오작동의 발생이 방지된다. 한편, 화상 표시부와 터치 센서의 간극을 메우기 위하여, 투명 수지 (예를 들어, 비유전율이 4 이상인 아크릴계 점착제) 를 충전제로서 사용한 경우, 고주파 노이즈가 터치 센서에 전파되어, 결과적으로 오작동을 발생시키는 경우가 있다. 구동의 주파수나 노이즈의 주파수는 상이하고, 넓은 주파수역에 있어서 오작동을 방지하는 것이 요구되지만, 아크릴계 점착제를 사용하여 형성된 점착제층의 비유전율은, 주파수 의존성을 갖는 경향이 있다.However, when the
이와 같은 경위에서, 터치 패널식 출입력 장치에 있어서는, 폭넓은 주파수 대역에 있어서 비유전율이 낮은 점착제층을 사용하여, 화상 표시부와 터치 센서의 간극을 메우는 것이 요망되고 있다.In such a case, it is desired to fill the gap between the image display section and the touch sensor by using a pressure sensitive adhesive layer having a low relative dielectric constant in a wide frequency band in the touch panel type input / output device.
1.7.2. 본 발명의 작용 효과1.7.2. Action and effect of the present invention
이것에 대하여, 본 실시형태에 관련된 광학용 점착제 조성물에 의하면, 그 광학용 점착제 조성물을 사용하여, 폭넓은 주파수 대역에 있어서 비유전율이 낮은 (비유전율의 주파수 의존성이 낮은) 점착제층을 얻을 수 있기 때문에, 점착제층의 높은 비유전율에서 기인하는 터치 센서의 오작동을 방지할 수 있다. 즉, 본 실시형태에 관련된 광학용 점착제 조성물을 사용하여 도 3 의 공극 (140) 을 충전하고, 비유전율이 1 이상 3.5 이하인 점착제층을 공극 (140) 에 형성함으로써, 터치 센서의 오작동을 방지할 수 있다.On the other hand, with the optical pressure-sensitive adhesive composition according to the present embodiment, it is possible to obtain a pressure-sensitive adhesive layer having a low dielectric constant (low relative frequency dependency of relative dielectric constant) in a wide frequency band by using the optical pressure- Therefore, it is possible to prevent the malfunction of the touch sensor caused by the high relative dielectric constant of the pressure-sensitive adhesive layer. That is, by using the optical pressure-sensitive adhesive composition according to the present embodiment to fill the
예를 들어, 도 2 에 나타내는 본 실시형태에 관련된 터치 패널식 출입력 장치 (100) 에서는, LCD (10) 와 터치 패널부 (20) 사이에 점착제층 (30) 이 형성되고, 이 점착제층 (30) 은 본 실시형태에 관련된 광학용 점착제 조성물로 형성된 것이기 때문에, 비유전율이 1 이상 3.5 이하로 낮은 점에서, 점착제층의 높은 비유전율에서 기인하는 터치 센서의 오작동을 방지할 수 있다.For example, in the touch panel type input /
또, (A) 성분인 수첨 블록 공중합체가, 방향족 비닐 단량체의 중합체 성분으로 구성되는 하드 세그먼트와, 공액 디엔 단량체의 중합체 성분으로 구성되는 소프트 세그먼트를 갖는 열가소성 엘라스토머인 것에 의해, 그 하드 세그먼트에서 기인하여 내열성이 우수한 데다가, (A) 성분이 수소 첨가물이기 때문에, 착색이나 자외선 등의 영향에 의한 변색 및 변성을 방지할 수 있고, 그 결과, 내후성이 우수하다. 이 때문에, 과혹 조건하에서 피착체로부터 발생하는 가스 (수증기나 피착체 유래의 휘발성 성분) 에 의한 들뜸이나 벗겨짐을 억제할 수 있다. 이것에 의해, 고품질이고 또한 내구성이 우수한 터치 패널식 출입 출력 장치를 얻을 수 있다.Further, since the hydrogenated block copolymer as the component (A) is a thermoplastic elastomer having a hard segment composed of a polymer component of an aromatic vinyl monomer and a soft segment composed of a polymer component of a conjugated diene monomer, And the component (A) is a hydrogenated product, it is possible to prevent discoloration and denaturation due to coloration and ultraviolet rays, and as a result, it is excellent in weather resistance. Therefore, it is possible to suppress lifting or peeling off of the gas (volatile component derived from steam or adherend) generated from the adherend under severe conditions. Thus, it is possible to obtain a touch panel type input / output device having high quality and excellent durability.
1.8. 다른 실시형태1.8. Other embodiments
본 발명의 다른 일 실시형태에 관련된 광학용 점착제 조성물은, (ⅰ) 수첨 블록 공중합체와, (ⅱ) 제 1 상용제와, (ⅲ) 제 2 상용제를 함유하는, 광학용 점착제 조성물로서, 상기 (ⅰ) 수첨 블록 공중합체는, 방향족 비닐 단량체의 중합체 성분으로 구성되는 하드 세그먼트와, 공액 디엔 단량체의 중합체 성분으로 구성되는 소프트 세그먼트를 갖고, 상기 (ⅱ) 제 1 상용제는, 상기 하드 세그먼트에 상용하는 성질을 갖고, 상기 (ⅲ) 제 2 상용제는, 상기 소프트 세그먼트에 상용하는 성질을 갖고, 상기 광학용 점착제 조성물로부터 얻어지는 점착제층의 비유전율이 1 이상 3.5 이하이다. 여기서, 상기 (ⅰ) 수첨 블록 공중합체로는, 예를 들어, 상기 서술한 (A) 성분을 사용할 수 있고, 상기 (ⅱ) 제 1 상용제로는, 예를 들어, 상기 서술한 (B) 성분을 사용할 수 있고, 상기 (ⅲ) 제 2 상용제로는, 예를 들어, 상기 서술한 (C) 성분 및 (D) 성분 (즉, 상온에서 고체 또는 액체의 상용제) 을 사용할 수 있다.A pressure-sensitive adhesive composition for optical use according to another embodiment of the present invention is an optical pressure-sensitive adhesive composition for optical use which comprises (i) a hydrogenated block copolymer, (ii) a first compatibilizing agent, and (iii) (I) the hydrogenated block copolymer has a hard segment composed of a polymer component of an aromatic vinyl monomer and a soft segment composed of a polymer component of a conjugated diene monomer, and (ii) the first compatibilizing agent has a hard segment (Iii) the second compatibilizing agent has a property of being compatible with the soft segment, and the relative dielectric constant of the pressure-sensitive adhesive layer obtained from the optical pressure-sensitive adhesive composition is not less than 1 and not more than 3.5. For example, the above-mentioned component (A) can be used as the (i) hydrogenated block copolymer, and (ii) the first commercial component can be, for example, (C) and the component (D) described above (that is, a compatibilizing agent of a solid or a liquid at room temperature) may be used as the second commercial zeros (iii).
상기 광학용 점착제 조성물은, (ⅰ) 성분, (ⅱ) 성분 및 (ⅲ) 성분을 함유함으로써, 그 광학용 점착제 조성물로부터 얻어지는 점착제층의 비유전율이 1 이상 3.5 이하가 되기 때문에, 표시 장치에 포함되는 내부 회로에서 발생하는 노이즈에 의한 오작동이나, 도전체에 끼워진 유전체의 차지가 일으키는 오작동을 방지할 수 있고, 또한 내구성, 밀착성 및 내후성이 우수한 점착제층을 얻을 수 있다.Since the optical pressure-sensitive adhesive composition for optical use contains the component (i), the component (ii) and the component (iii), the relative dielectric constant of the pressure-sensitive adhesive layer obtained from the optical pressure- It is possible to prevent the malfunction caused by the noise generated in the internal circuit or the malfunction caused by the charge of the dielectric sandwiched by the conductor, and to obtain the pressure-sensitive adhesive layer having excellent durability, adhesion and weather resistance.
2. 점착 시트2. Adhesive sheet
본 실시형태에 관련된 점착 시트는, 본 실시형태에 관련된 광학용 점착제 조성물을 세퍼레이터의 표면에 도포하고, 건조시켜 얻어진다. 보다 구체적으로는, 기재 상에, 본 실시형태에 관련된 점착제 조성물을 그라비어 코터, 메이어 바 코터, 에어 나이프 코터, 롤 코터 등에 의해 도포하고, 도포된 그 점착제 조성물을 상온 또는 가열에 의해 건조시켜, 본 실시형태에 관련된 점착 시트를 제조해도 된다. 또, 점착 시트의 두께는, 통상은 10 ㎛ 이하 500 ㎛ 이하, 바람직하게는 20 ㎛ 이상 300 ㎛ 이하의 범위의 정도이다.The pressure-sensitive adhesive sheet according to the present embodiment is obtained by applying the optical pressure-sensitive adhesive composition according to the present embodiment on the surface of a separator and drying it. More specifically, the pressure-sensitive adhesive composition according to the present embodiment is coated on a substrate by a gravure coater, a Meyer bar coater, an air knife coater, a roll coater or the like, and the applied pressure-sensitive adhesive composition is dried at room temperature or by heating, The pressure-sensitive adhesive sheet according to the embodiment may be produced. The thickness of the pressure-sensitive adhesive sheet is usually in the range of 10 占 퐉 to 500 占 퐉, preferably 20 占 퐉 to 300 占 퐉.
3. 화상 표시 장치 및 입출력 장치3. Image display device and input / output device
본 발명의 다른 실시형태에 관련된 화상 표시 장치는, 본 실시형태에 관련된 광학용 점착제 조성물을 사용하여 형성된 점착제층을 포함한다. 본 실시형태에 관련된 화상 표시 장치로는, 예를 들어, 액정 표시 장치를 들 수 있다.The image display apparatus according to another embodiment of the present invention includes a pressure-sensitive adhesive layer formed using the optical pressure-sensitive adhesive composition according to the present embodiment. The image display apparatus according to the present embodiment is, for example, a liquid crystal display apparatus.
또, 본 발명의 다른 실시형태에 관련된 입출력 장치는, 본 실시형태에 관련된 광학용 점착제 조성물을 사용하여 형성된 점착제층을 포함한다. 이 경우, 입출력 장치로는, 예를 들어, 정전 용량 방식의 터치 패널식 출입력 장치를 들 수 있다.The input / output device according to another embodiment of the present invention includes a pressure-sensitive adhesive layer formed using the optical pressure-sensitive adhesive composition according to the present embodiment. In this case, the input / output device is, for example, a capacitive touch panel type input / output device.
4. 실시예4. Example
이하, 본 발명을 하기 실시예에 기초하여 설명하지만, 본 발명은 실시예에 한정되지 않는다.Hereinafter, the present invention will be described based on the following examples, but the present invention is not limited to the examples.
4.1. 점착제 조성물의 조제4.1. Preparation of pressure-sensitive adhesive composition
표 1 및 표 2 에 나타내는 배합으로 각 성분을 혼합하여, 실시예 1 내지 21 및 비교예 1 내지 18 의 점착제 조성물을 각각 조제하였다. 또한, 후술하는 평가 방법에서 사용되는, 두께 50 ㎛ 의 점착 시트는, 각 점착제 조성물을 세퍼레이터의 표면에 도포하고, 건조시켜 얻어졌다.The pressure-sensitive adhesive compositions of Examples 1 to 21 and Comparative Examples 1 to 18 were prepared by mixing the components in the formulations shown in Tables 1 and 2, respectively. The pressure-sensitive adhesive sheet having a thickness of 50 占 퐉 used in the evaluation method described later was obtained by applying each pressure-sensitive adhesive composition to the surface of the separator and drying it.
4.2. 평가 방법4.2. Assessment Methods
4.2.1. 비유전율4.2.1. Relative dielectric constant
두께 100 ㎛ 의 동박에, 두께 50 ㎛ 의 점착 시트를 첩부하고, 추가로 두께 100 ㎛ 의 동박에 첩부하여 측정 샘플로 하였다. 토요 테크니카 제조 LCR 미터 6440B 를 사용하여 동박에 접속하여, 23 ℃ 65 ％RH 의 조건하에서 비유전율을 산출하였다. 또한, 실시예 1 의 점착제 조성물을 구성하는 수첨 블록 공중합체에 대하여, 측정 주파수를 변경하여 비유전율을 측정한 결과를 도 1 에 나타낸다. 또한, 비교 대상으로서, 비교예 13 및 17 의 점착제 조성물을 구성하는 아크릴계 폴리머에 대해서도 동일한 측정을 실시하였다.A pressure sensitive adhesive sheet having a thickness of 50 占 퐉 was attached to a copper foil having a thickness of 100 占 퐉 and further attached to a copper foil having a thickness of 100 占 퐉 to obtain a measurement sample. The relative dielectric constant was calculated under the conditions of 23 deg. C and 65% RH by connecting to a copper foil using an LCR meter 6440B manufactured by Toyotecnica. 1 shows the results of measuring the relative dielectric constant of the hydrogenated block copolymer constituting the pressure-sensitive adhesive composition of Example 1 by changing the measurement frequency. As comparative objects, the same measurements were also performed on the acrylic polymer constituting the pressure-sensitive adhesive composition of Comparative Examples 13 and 17.
4.2.2. 내열발포성4.2.2. Heat-Resistant Foaming
두께 100 ㎛ 의 PET 에 두께 50 ㎛ 의 점착 시트를 전사하고, 미츠비시 수지 제조 폴리카보네이트 MR-58 에 첩부하여 85 ℃ 의 85 ％RH 의 환경하에서 가만히 정지시켰다. 점착 시트의 외관을 이하의 기준으로 육안으로 평가하였다.A pressure-sensitive adhesive sheet having a thickness of 50 占 퐉 was transferred to PET having a thickness of 100 占 퐉 and attached to Polycarbonate MR-58 manufactured by Mitsubishi Resin Co., Ltd., and was stopped still under an 85% RH environment at 85 占 폚. The appearance of the pressure-sensitive adhesive sheet was visually evaluated based on the following criteria.
(평가)(evaluation)
◎ : 외관 이상이 관찰되지 않는다&Amp; cir &: Appearance abnormality is not observed
○ : 1 ㎠ 당 직경 0.1 ㎜ 이하의 기포가 1 개 이하 관찰되었다&Amp; cir &: no more than one bubbles having a diameter of 0.1 mm or less per 1 cm < 2 &
△ : 1 ㎠ 당 직경 0.1 ㎜ 이하의 기포가 2 ∼ 5 개 관찰되었거나, 혹은 직경 0.1 ㎜ 초과 1.0 ㎜ 이하의 기포가 관찰되었다?: 2 to 5 bubbles having a diameter of 0.1 mm or less were observed per 1
× : 1 ㎠ 당 기포가 6 개 이상 관찰되었거나, 혹은 직경 1.0 초과의 기포가 관찰되었다X: 6 or more bubbles were observed per 1
4.2.3. 습열백화성4.2.3. Wet heat whitening
두께 100 ㎛ 의 PET 에 두께 50 ㎛ 의 점착 시트를 전사하고, 이것을 유리판에 첩부하여, 60 ℃ 95 ％RH 환경하에서 가만히 정지시켰다. 헤이즈미터로 습열백화성을 측정하였다.A pressure-sensitive adhesive sheet having a thickness of 50 占 퐉 was transferred to PET having a thickness of 100 占 퐉, and the pressure-sensitive adhesive sheet was attached to a glass plate and stopped still under an environment of 60 占 폚 and 95% RH. The wet heat flux was measured with a haze meter.
4.2.4. 점착력의 평가4.2.4. Evaluation of cohesion
점착층 두께 50 ㎛ 의 점착 시트를 폭 20 ㎜ 의 단책상(短冊狀)으로 잘라내고, 세퍼레이터를 박리하여 유리 기판에 붙여 2 ㎏ 의 롤러로 3 왕복 압착하였다. 20 분 후, 박리 속도 0.3 m/분, 박리 각도 180˚로 박리하고, 그 때의 점착력을 측정하였다 (단위 : N/20 ㎜).A pressure sensitive adhesive sheet having an adhesive layer thickness of 50 占 퐉 was cut into short strips having a width of 20 mm and the separator was peeled off and attached to a glass substrate and subjected to three rounds of pressure bonding with a roller of 2 kg. After 20 minutes, the peel was peeled off at a peeling speed of 0.3 m / min and a peel angle of 180 占 (unit: N / 20 mm).
4.2.5. 내후성4.2.5. Weatherability
크세논 웨더 미터를 사용하여 블랙 패널 온도 63 ± 3 ℃ 에서 명암 사이클 연속 점등으로 시험 전후의 색상을 비교 측정하였다.The color before and after the test was measured comparatively by using a xenon weatherometer at a black panel temperature of 63 3 deg.
(평가)(evaluation)
◎ : 색차 ΔE* 가 3.2 이하?: Color difference? E * is 3.2 or less
○ : 색차 ΔE* 가 3.2 초과 6.5 이하?: Color difference? E * is more than 3.2 and less than 6.5
△ : 색차 ΔE* 가 6.5 초과 13.0 이하?: Color difference? E * is more than 6.5 but not more than 13.0
× : 색차 ΔE* 가 13.0 초과X: color difference? E * exceeded 13.0
또한, 표 1 및 표 2 에 있어서의 약어의 의미는 이하와 같다.The meanings of abbreviations in Tables 1 and 2 are as follows.
SEPS1 : 스티렌/에틸렌-프로필렌/스티렌형 블록 공중합체 (스티렌-이소프렌-스티렌형 블록 폴리머의 수소 첨가물 ; 스티렌 함유율 13 ％)SEPS1: styrene / ethylene-propylene / styrene block copolymer (hydrogenated styrene-isoprene-styrene block polymer; styrene content: 13%)
SEPS2 : 스티렌/에틸렌-프로필렌/스티렌형 블록 공중합체 (스티렌-이소프렌-스티렌형 블록 폴리머의 수소 첨가물 ; 스티렌 함유율 20 ％)SEPS 2: Styrene / ethylene-propylene / styrene block copolymer (hydrogenated product of styrene-isoprene-styrene block polymer; styrene content: 20%)
SEPS3 : 스티렌/에틸렌-프로필렌/스티렌형 블록 공중합체 (스티렌-이소프렌-스티렌형 블록 폴리머의 수소 첨가물 ; 스티렌 함유율 65 ％)SEPS3: Styrene / ethylene-propylene / styrene block copolymer (hydrogenation product of styrene-isoprene-styrene block polymer; styrene content 65%)
SEBS : 스티렌/에틸렌-부틸렌/스티렌형 블록 폴리머 (스티렌 함유율 30 ％) (또한, 상기 SEPS1, SEPS2 및 SESP3 및 SEBS 는, 모두 수첨률 90 ％ 이상이다)SEBS: styrene / ethylene-butylene / styrene type block polymer (
SIS : 스티렌-이소프렌-스티렌형 블록 폴리머SIS: Styrene-isoprene-styrene type block polymer
SBS : 스티렌-부타디엔-스티렌형 블록 폴리머SBS: Styrene-butadiene-styrene type block polymer
아크릴계 폴리머 1 : n-부틸아크릴레이트/메틸아크릴레이트/2-하이드록시에틸아크릴레이트 ＝ 60/30/10 (질량비)Acrylic polymer 1: n-butyl acrylate / methyl acrylate / 2-hydroxyethyl acrylate = 60/30/10 (by mass ratio)
아크릴계 폴리머 2 : 2-에틸헥실아크릴레이트/메틸아크릴레이트/2-하이드록시에틸아크릴레이트 ＝ 60/30/10 (질량비)Acrylic polymer 2: 2-ethylhexyl acrylate / methyl acrylate / 2-hydroxyethyl acrylate = 60/30/10 (mass ratio)
아크릴계 폴리머 3 : 메틸메타크릴레이트/n-부틸아크릴레이트 ＝ 6.5/87/6.5 (질량비) 의 ABA 형 트리 블록 폴리머Acrylic polymer 3: ABA type triblock polymer of methyl methacrylate / n-butyl acrylate = 6.5 / 87 / 6.5 (mass ratio)
FMR-0150 : 연화점 145 ℃ 의 방향족계 점착 부여 수지 (미츠이 화학사 제조)FMR-0150: aromatic tackifier resin having a softening point of 145 占 폚 (manufactured by Mitsui Chemicals)
FTR-6100 : 연화점 100 ℃ 의 방향족계 점착 부여 수지 (미츠이 화학사 제조)FTR-6100: aromatic tackifier resin having a softening point of 100 占 폚 (manufactured by Mitsui Chemicals)
크리스탈렉스 3100 : 연화점 100 ℃ 의 방향족계 점착 부여 수지 (이스트맨 케미컬사 제조)Crystallex 3100: aromatic tackifier resin having a softening point of 100 占 폚 (manufactured by Eastman Chemical Company)
피콜라스틱 A5 : 연화점 5 ℃ 의 방향족계 점착 부여 수지 (이스트맨 케미컬사 제조)Picolastic A5: aromatic tackifying resin having a softening point of 5 DEG C (manufactured by Eastman Chemical Co., Ltd.)
DOP : 프탈산디옥틸 (이스트맨 케미컬사 제조)DOP: dioctyl phthalate (manufactured by Eastman Chemical Company)
KE311 : 담색 로진계 점착 부여 수지 (아라카와 화학사 제조)KE311: Pale rosin-based tackifying resin (manufactured by Arakawa Chemical Industries, Ltd.)
TH130 : 테르펜 페놀형 점착 부여 수지 (야스하라 케미컬사 제조)TH130: terpene phenol type tackifier resin (manufactured by Yasuhara Chemical Co., Ltd.)
P-100 : 수첨 지환족 포화 탄화수소 수지 (아라카와 화학사 제조)P-100: Hydrogenated alicyclic saturated hydrocarbon resin (Arakawa Chemical Industries, Ltd.)
4.3. 평가 결과4.3. Evaluation results
표 1 의 결과로부터, 본원 실시예 1 내지 21 의 점착제 조성물은, (A) 성분, (B) 성분 및 (C) 성분을 함유함으로써, 그 점착제 조성물로부터 얻어지는 점착제층의 비유전율을 1 이상 3.5 이하로 할 수 있고, 또한 내구성 (내열발포성 및 습열백화성) 및 내후성이 우수한 점착제층을 얻을 수 있다.From the results shown in Table 1, the pressure-sensitive adhesive compositions of Examples 1 to 21 of the present application contain the component (A), the component (B) and the component (C) so that the relative dielectric constant of the pressure-sensitive adhesive layer obtained from the pressure- , And a pressure-sensitive adhesive layer excellent in durability (heat-expandable foaming property and wet heat whitening property) and weather resistance can be obtained.
이것에 대하여, 표 2 에 나타내는 바와 같이, 본원 비교예 1 내지 5 의 조성물은 (B) 성분을 함유하고 있지 않기 때문에, 내구성 (내열발포성) 이 열등한 것을 이해할 수 있다. 특히, 본원 비교예 1 에서는, (B) 성분인 연화점이 80 ℃ 이상인 제 1 상용제 대신에, 연화점이 80 ℃ 미만인 방향족계 점착 부여 수지를 사용했기 때문에, 내열성이 열등한 것을 이해할 수 있다.On the contrary, as shown in Table 2, it can be understood that the composition of Comparative Examples 1 to 5 of the present invention does not contain the component (B), and therefore the durability (heat-resistant foamability) is inferior. In particular, in Comparative Example 1 of the present invention, it is understood that the heat resistance is inferior because an aromatic tackifier resin having a softening point of less than 80 캜 is used in place of the first compatibilizer having a softening point of 80 캜 or higher, which is the component (B).
또, 본원 비교예 6 내지 8 의 조성물은, (C) 성분을 함유하고 있지 않기 때문에, 내구성 (내열발포성) 이 열등한 것을 이해할 수 있다. 또한, 본원 비교예 9 내지 11 의 조성물에서는, (A) 성분 대신에, 수첨되어 있지 않은 블록 공중합체를 사용했기 때문에, 내후성이 열등한 것을 이해할 수 있다. 덧붙여, 본원 비교예 12 내지 15, 17 및 18 의 조성물에서는, (A) 성분 대신에 아크릴계 폴리머를 사용했기 때문에, 비유전율이 높은 점착제층이 얻어진 것을 이해할 수 있다. 또한, 본원 비교예 16 의 조성물에서는, (C) 성분 대신에, DOP (프탈산디옥틸) 를 사용했기 때문에, 내열성이 열등한 것을 이해할 수 있다.In addition, since the compositions of Comparative Examples 6 to 8 do not contain the component (C), it is understood that the durability (heat-resistant foamability) is inferior. Further, in the compositions of Comparative Examples 9 to 11 of the present invention, it is understood that since the block copolymer which is not hydrogenated is used in place of the component (A), the weather resistance is inferior. In addition, it can be understood that in the compositions of Comparative Examples 12 to 15, 17 and 18 of the present invention, since an acrylic polymer was used in place of the component (A), a pressure-sensitive adhesive layer having a high dielectric constant was obtained. Further, since the composition of Comparative Example 16 of the present invention uses DOP (dioctyl phthalate) instead of the component (C), it can be understood that the heat resistance is inferior.
또, 도 1 에 의하면, 실시예 1 의 점착제 조성물로 형성된 점착제층은, 폭넓은 주파수 대역에 있어서 안정적인 비유전율을 갖는다. 이것에 대하여, 비교예 13 및 17 의 점착제 조성물로 형성된 점착제층은, 주파수에 의해 비유전율이 크게 변동되고 있다. 이 결과로부터, 본 발명의 점착제 조성물을 사용함으로써, 비유전율이 1 이상 3.5 이하로 낮고, 또한 비유전율의 주파수 의존성이 낮은 점착제층이 얻어지는 것을 이해할 수 있다.1, the pressure-sensitive adhesive layer formed from the pressure-sensitive adhesive composition of Example 1 has a stable relative dielectric constant in a wide frequency band. On the other hand, in the pressure-sensitive adhesive layer formed of the pressure-sensitive adhesive compositions of Comparative Examples 13 and 17, the relative dielectric constant largely fluctuated depending on the frequency. From this result, it can be understood that by using the pressure-sensitive adhesive composition of the present invention, a pressure-sensitive adhesive layer having a relative dielectric constant as low as not less than 1 and not more than 3.5 and a low frequency dependence of relative dielectric constant can be obtained.
Claims (16)
(B) 제 1 상용(相溶)제와,
(C) 제 2 상용제를 함유하는, 광학용 점착제 조성물로서,
상기 (A) 수소 첨가 블록 공중합체는, 방향족 비닐 단량체의 중합체 성분으로 구성되는 하드 세그먼트와, 공액 디엔 단량체의 중합체 성분으로 구성되는 소프트 세그먼트를 갖고,
상기 (B) 제 1 상용제는, 상기 하드 세그먼트에 상용하는 성질을 갖고, 또한 연화점이 80 ℃ 이상이고,
상기 (C) 제 2 상용제는, 상기 소프트 세그먼트에 상용하는 성질을 갖고, 또한 상온 (23 ℃) 에 있어서 액체이고,
상기 광학용 점착제 조성물로부터 얻어지는 점착제층의 비유전율이 1 이상 3.5 이하인 광학용 점착제 조성물.(A) a hydrogenated block copolymer,
(B) a first compatibilizing agent,
(C) a second compatibilizing agent, wherein the pressure-
The hydrogenated block copolymer (A) has a hard segment composed of a polymer component of an aromatic vinyl monomer and a soft segment composed of a polymer component of a conjugated diene monomer,
The first compatibilizing agent (B) has properties compatible with the hard segment and has a softening point of 80 ° C or higher,
The second compatibilizing agent (C) has properties compatible with the soft segment and is liquid at room temperature (23 캜)
Wherein the pressure-sensitive adhesive layer obtained from the optical pressure-sensitive adhesive composition has a relative dielectric constant of from 1 to 3.5.
상기 (A) 수소 첨가 블록 공중합체에 있어서의 상기 하드 세그먼트의 함유량이 5 질량％ 이상 70 질량％ 이하인 광학용 점착제 조성물.The method according to claim 1,
Wherein the content of the hard segment in the hydrogenated block copolymer (A) is 5% by mass or more and 70% by mass or less.
상기 (A) 수소 첨가 블록 공중합체를 구성하는 공액 디엔 단량체의 중합체 성분에 함유되는 2 중 결합의 수소 첨가률이 90 ％ 이상인 광학용 점착제 조성물.3. The method according to claim 1 or 2,
Wherein the hydrogenation ratio of the double bonds contained in the polymer component of the conjugated diene monomer constituting the hydrogenated block copolymer (A) is 90% or more.
상기 (B) 제 1 상용제는 방향족계 점착 부여 수지인 광학용 점착제 조성물.4. The method according to any one of claims 1 to 3,
The first pressure-sensitive adhesive composition (B) is an aromatic pressure-sensitive adhesive resin.
상기 방향족계 점착 부여 수지가 방향족 석유 수지, 스티렌계 중합체, α-메틸스티렌계 중합체, 스티렌-(α-메틸스티렌)계 공중합체, 스티렌-지방족 탄화수소계 공중합체, 스티렌-(α-메틸스티렌)-지방족 탄화수소계 공중합체 및 스티렌-방향족 탄화수소계 공중합체로 이루어지는 군에서 선택되는 적어도 1 종인 광학용 점착제 조성물.5. The method of claim 4,
Wherein the aromatic tackifying resin is selected from the group consisting of an aromatic petroleum resin, a styrene type polymer, an? -Methylstyrene type polymer, a styrene- (? -Methylstyrene) type copolymer, a styrene-aliphatic hydrocarbon type copolymer, - aliphatic hydrocarbon-based copolymer and styrene-aromatic hydrocarbon-based copolymer.
상기 (C) 제 2 상용제가 폴리부텐계 화합물, 폴리이소부틸렌계 화합물 및 폴리이소프렌계 화합물로 이루어지는 군에서 선택되는 적어도 1 종인 광학용 점착제 조성물.6. The method according to any one of claims 1 to 5,
Wherein the second compatibilizing agent (C) is at least one selected from the group consisting of a polybutene compound, a polyisobutylene compound, and a polyisoprene compound.
상기 광학용 점착제 조성물의 산가가 1 이하인 광학용 점착제 조성물.7. The method according to any one of claims 1 to 6,
Wherein the acid value of said optical pressure-sensitive adhesive composition is 1 or less.
상기 (B) 제 1 상용제의 함유량이, 상기 (A) 수소 첨가 블록 공중합체 100 질량부에 대하여 5 질량부 이상 60 질량부 이하인 광학용 점착제 조성물.8. The method according to any one of claims 1 to 7,
Wherein the content of the first compatibilizing agent (B) is 5 parts by mass or more and 60 parts by mass or less based on 100 parts by mass of the hydrogenated block copolymer (A).
상기 (C) 제 2 상용제의 함유량이, 상기 (A) 수소 첨가 블록 공중합체 100 질량부에 대하여 5 질량부 이상 60 질량부 이하인 광학용 점착제 조성물.9. The method according to any one of claims 1 to 8,
Wherein the content of the second compatibilizing agent (C) is 5 parts by mass or more and 60 parts by mass or less based on 100 parts by mass of the hydrogenated block copolymer (A).
상기 (B) 제 1 상용제 및 상기 (C) 제 2 상용제의 합계 함유량이, 상기 (A) 수소 첨가 블록 공중합체 100 질량부에 대하여 10 질량부 이상 80 질량부 이하인 광학용 점착제 조성물.10. The method according to any one of claims 1 to 9,
Wherein the total content of the first compatibilizing agent (B) and the second compatibilizing agent (C) is 10 parts by mass or more and 80 parts by mass or less based on 100 parts by mass of the hydrogenated block copolymer (A).
상기 소프트 세그먼트에 상용하고, 또한 상온 (23 ℃) 에 있어서 고체인 (D) 제 3 상용제를 추가로 함유하고,
상기 (D) 제 3 상용제는 로진계 점착 부여 수지, 테르펜계 점착 부여 수지, 또는 수소 첨가 지환족 탄화수소 수지인 광학용 점착제 조성물.11. The method according to any one of claims 1 to 10,
(D) a third compatibilizing agent which is soluble in said soft segment and which is solid at room temperature (23 DEG C)
The third pressure-sensitive adhesive composition (D) is a rosin-based pressure-sensitive adhesive resin, a terpene-based pressure-sensitive adhesive resin, or a hydrogenated alicyclic hydrocarbon resin.
상기 점착제층은 주파수 1.0 × 106 ㎐ 에서의 비유전율이, 주파수 1.0 × 102 ㎐ 에서의 비유전율의 90 ％ 이상인 광학용 점착제 조성물.12. The method according to any one of claims 1 to 11,
Wherein the pressure-sensitive adhesive layer has a relative dielectric constant at a frequency of 1.0 x 10 6 Hz of 90% or more of a relative dielectric constant at a frequency of 1.0 x 10 2 Hz.
터치 패널식 입출력 장치를 구성하는 부재의 첩합(貼合)에 사용되는 광학용 점착제 조성물.13. The method according to any one of claims 1 to 12,
A pressure-sensitive adhesive composition for optical use to be used for bonding members constituting a touch panel type input / output device.