KR20140089917A - 착색 감광성 수지 조성물 - Google Patents

착색 감광성 수지 조성물 Download PDF

Info

Publication number
KR20140089917A
KR20140089917A KR1020130001980A KR20130001980A KR20140089917A KR 20140089917 A KR20140089917 A KR 20140089917A KR 1020130001980 A KR1020130001980 A KR 1020130001980A KR 20130001980 A KR20130001980 A KR 20130001980A KR 20140089917 A KR20140089917 A KR 20140089917A
Authority
KR
South Korea
Prior art keywords
photosensitive resin
resin composition
colored photosensitive
composition according
pigment
Prior art date
Application number
KR1020130001980A
Other languages
English (en)
Other versions
KR101961219B1 (ko
Inventor
이헌희
윤현진
Original Assignee
동우 화인켐 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 동우 화인켐 주식회사 filed Critical 동우 화인켐 주식회사
Priority to KR1020130001980A priority Critical patent/KR101961219B1/ko
Priority to CN201310669772.XA priority patent/CN103913949A/zh
Publication of KR20140089917A publication Critical patent/KR20140089917A/ko
Application granted granted Critical
Publication of KR101961219B1 publication Critical patent/KR101961219B1/ko

Abstract

본 발명은 착색 감광성 수지 조성물에 관한 것으로, 보다 상세하게는 N-벤질말레이미드를 포함하여 중합된 알칼리 가용성 수지 및 하기 화학식 1로 표시되는 광중합 개시제를 포함함으로써, 휘도가 우수하고 잔사 발생을 최소화하며, 표면 평활성이 우수하여, 후공정을 거쳐도 표면 불량이 발생하지 않아 도막의 신뢰도를 개선하는 착색 감광성 수지 조성물에 관한 것이다.

Description

착색 감광성 수지 조성물 {A COLORED PHOTOSENSITIVE RESIN COMPOSITION}
본 발명은 착색 감광성 수지 조성물에 관한 것이다.
컬러필터는 촬상(撮像)소자, 액정표시장치(LCD) 등에 널리 이용되는 것으로, 그 응용 범위가 급속히 확대되고 있다.
컬러 액정표시장치나 촬상소자 등에 사용되는 컬러필터는 통상 블랙 매트릭스가 패턴 형성된 기판상에 적색, 녹색 및 청색의 각 색에 상당하는 안료를 함유하는 착색 감광성 수지 조성물을 스핀 코팅에 의해 균일하게 도포한 후, 가열 건조(이하, 예비 소성이라고 하는 경우도 있음)하여 형성된 도막을 노광, 현상하고, 필요에 따라 더 가열 경화(이하, 후 소성이라고 하는 경우도 있음)하는 조작을 색마다 반복하여 각 색의 화소를 형성함으로써 제조되고 있다. 이후, 액정표시장치용 컬러필터는 표면에 ITO 전극을 형성하는 공정이 이루어지고, 이 공정에서는 약 200℃ 이상의 고온에 노출된다. 또 배향막 형성시에도 200℃ 이상의 고온에 노출된다.
상기와 같은 용도에 사용되는 착색 감광성 수지 조성물로서 내용제성이 우수하고, 색 변화가 적은 수지로서 측쇄에 카르복실기를 함유하는 아크릴계 수지 및 안료, 다관능 아크릴레이트의 조성을 통하여 얻은 착색 수지 조성물은 이미, 개시되어 있다. 또한, 한국공개특허 제1995-9350호에는 잔사 및 밀착성 등을 높이기 위해 친수성을 가지는 알코올성 히드록시기 골격을 함유하는 아크릴계 수지를 사용한 감광성 수지 조성물이 개시되어 있다.
그러나, 상기와 같은 종래기술을 그대로 도입하면 고농도의 착색 재료가 도입되는 조성에서 안료와의 상용성 문제로, 후 공정(ITO 전극의 형성이나 배향막 형성 등의 고온의 프로세스) 후에 패턴의 표면에 홀(Hole) 및 엠보싱 현상이 발생하거나, 휘도 저하 및 표면불량의 원인이 되는 문제점이 있고, 고온의 프로세스 후 감광성 수지 조성물이 분해되어 생기는 아웃가스(OUTGAS)에 의해 잔상이 발생하는 문제점이 있다.
또한, 최근에는 공정상 시간을 단축하기 위하여 적은 노광량에도 동등한 감도와 밀착성을 갖는 착색 감광성 수지 조성물이 요구되고 있으나 종래 기술을 통해서는 감도 및 밀착성이 부족하므로 요구되는 성능을 만족하는 착색 감광성 수지 조성물을 제공할 수 없다는 문제점이 있다.
한국공개특허 제1995-9350호
본 발명은 휘도가 우수하며 잔사 발생을 최소화하는 착색 감광성 수지 조성물을 제공하는 것을 목적으로 한다.
본 발명은 후공정을 거쳐도 표면 불량이 발생하지 않는 착색 감광성 수지 조성물을 제공하는 것을 목적으로 한다.
1. N-벤질말레이미드를 포함하여 중합된 알칼리 가용성 수지 및 하기 화학식 1로 표시되는 광중합 개시제를 포함하는 착색 감광성 수지 조성물:
[화학식 1]
Figure pat00001
(식 중, R1은 -H, -OH, -COOH, 탄소수 1 내지 6의 알킬기 또는
Figure pat00002
이고; R2는 -O-, -S-, -NH-, -OCO- 또는 -COO-이며; R3는 탄소수 1 내지 10의 알킬기, 탄소수 4 내지 10의 시클로알킬기, 탄소수 6 내지 10의 아릴기로 치환 또는 비치환된 탄소수 1 내지 20의 알킬렌기, 탄소수 6 내지 30의 아릴렌기 또는 탄소수 7 내지 30의 아릴알킬렌기이고, 상기 알킬렌은 각각 -O-, -S-, -COO- 또는 -OCO-에 의해 0 내지 5회 중단될 수 있으며; R4는 -OH 또는 -COOH이고, n은 1 내지 3의 정수임).
2. 위 1에 있어서, 상기 N-벤질말레이미드는 2 내지 50몰% 포함되어 중합되는 착색 감광성 수지 조성물.
3. 위 1에 있어서, 상기 알칼리 가용성 수지의 산가는 20 내지 200(KOH mg/g)인 착색 감광성 수지 조성물.
4. 위 1에 있어서, 상기 알칼리 가용성 수지는 고형분 기준으로 조성물 총 중량 중 10 내지 80중량%로 포함되는 착색 감광성 수지 조성물.
5. 위 1에 있어서, 아세토페논계, 벤조인계, 벤조페논계, 티옥산톤계, 트리아진계, 옥심계, 오늄염계, 니트로벤질토실레이트계 및 벤조인토실레이트계로 이루어진 군에서 선택된 적어도 1종의 광중합 개시제를 더 포함하는 착색 감광성 수지 조성물.
6. 위 1에 있어서, 상기 광중합 개시제는 고형분 기준으로 조성물 총 중량 중 0.1 내지 30중량%로 포함되는 착색 감광성 수지 조성물.
7. 위 1에 있어서, 착색제 및 용제를 더 포함하는 착색 감광성 수지 조성물.
8. 위 7에 있어서, 상기 착색제는 고형분 기준으로 조성물 총 중량 중 10 내지 70중량%로 포함되는 착색 감광성 수지 조성물.
9. 위 7에 있어서, 상기 용제는 에테르류, 방향족 탄화수소류, 케톤류, 알콜류, 에스테르류 및 아미드류로 이루어진 군에서 선택되는 착색 감광성 수지 조성물.
10. 위 7에 있어서, 상기 용제는 조성물 총 중량 중 10 내지 90중량%로 포함되는 착색 감광성 수지 조성물.
11. 위 1에 있어서, 광중합성 화합물 및 광중합 개시 보조제를 더 포함하는 착색 감광성 수지 조성물.
12. 위 11에 있어서, 광중합성 화합물을 고형분 기준으로 조성물 총 중량 중 5 내지 50중량%, 광중합 개시 보조제를 광중합 개시제 1 몰당 0.01 내지 10몰로 포함하는 착색 감광성 수지 조성물.
13. 위 1 내지 12 중 어느 한 항의 착색 감광성 수지 조성물로 형성된 컬러필터.
14. 위 13에 있어서, 표면 거칠기(Ra)가 3㎛ 이하인 컬러필터.
본 발명의 착색 감광성 수지 조성물로 형성된 컬러 필터는 휘도가 우수하며 잔사 발생을 최소화한다.
본 발명의 착색 감광성 수지 조성물로 형성된 컬러 필터는 표면 평활성이 우수하여, ITO 증착 등의 후공정을 거쳐도 표면 불량이 발생하지 않아 도막의 신뢰도를 개선한다.
본 발명은 N-벤질말레이미드를 포함하여 중합된 알칼리 가용성 수지 및 화학식 1로 표시되는 광중합 개시제를 포함함으로써, 휘도가 우수하고 잔사 발생을 최소화하며, 표면 평활성이 우수하여, 후공정을 거쳐도 표면 불량이 발생하지 않아 도막의 신뢰도를 개선하는 착색 감광성 수지 조성물에 관한 것이다.
이하 본 발명을 상세히 설명하기로 한다.
본 발명의 착색 감광성 수지 조성물은 N-벤질말레이미드를 포함하여 중합된 알칼리 가용성 수지 및 하기 화학식 1로 표시되는 광중합 개시제를 포함한다:
[화학식 1]
Figure pat00003
(식 중, R1은 -H, -OH, -COOH, 탄소수 1 내지 6의 알킬기 또는
Figure pat00004
이고; R2는 -O-, -S-, -NH-, -OCO- 또는 -COO-이며; R3는 탄소수 1 내지 10의 알킬기, 탄소수 4 내지 10의 시클로알킬기, 탄소수 6 내지 10의 아릴기로 치환 또는 비치환된 탄소수 1 내지 20의 알킬렌기, 탄소수 6 내지 30의 아릴렌기 또는 탄소수 7 내지 30의 아릴알킬렌기이고, 상기 알킬렌은 각각 -O-, -S-, -COO- 또는 -OCO-에 의해 0 내지 5회 중단될 수 있으며; R4는 -OH 또는 -COOH이고, n은 1 내지 3의 정수임).
종래 착색 감광성 수지 조성물은 이로부터 형성한 컬러필터의 휘도나 평활성을 요구되는 수준으로 만족시키는 것이 어렵다. 이에 따라 ITO 증착이나 배향막 형성 등의 후공정을 진행하고 나면 패턴의 표면에 홀 또는 엠보싱 등이 발생하여 도막의 신뢰도가 저하되는 문제가 있었다.
그러나 본 발명의 착색 감광성 수지 조성물은 N-벤질말레이미드를 포함하여 중합된 알칼리 가용성 수지 및 화학식 1로 표시되는 광중합 개시제를 포함함으로써, 그로부터 형성된 컬러필터의 휘도가 우수하고 잔사 발생이 억제되며 평활성이 향상되어, 후공정을 거쳐도 표면 불량이 발생하지 않는다는 점에 착안하였다.
알칼리 가용성 수지는 착색 감광성 수지 조성물에 통상적으로 사용되는 착색제에 대한 결합제 수지로서 작용한다.
본 발명에 따른 알칼리 가용성 수지는 N-벤질말레이미드를 포함하여 중합된다.
N-벤질말레이미드는 공중합되는 다른 모노머의 구체적인 종류 등에 따라 적절히 혼합될 수 있으므로 함량 및 혼합비는 특별히 한정되지 않으며, N-벤질말레이미드가 2 내지 50몰%로 포함되어 중합될 수 있고, 바람직하게는 3 내지 45몰% 포함되어 중합되는 것이 형성되는 컬러필터의 표면 평활성 개선의 측면에서 바람직하다.
본 발명에 따른 알칼리 가용성 수지는 N-벤질말레이미드와 공중합 가능한 적어도 1종의 다른 단량체를 더 포함하여 중합된 것일 수 있다. 예를 들면, 스티렌, α-메틸스티렌, o-비닐톨루엔, m-비닐톨루엔, p-비닐톨루엔, p-클로로스티렌, o-메톡시스티렌, m-메톡시스티렌, p-메톡시스티렌, o-비닐벤질메틸에테르, m-비닐벤질메틸에테르, p-비닐벤질메틸에테르, o-비닐벤질글리시딜에테르, m-비닐벤질글리시딜에테르, p-비닐벤질글리시딜에테르, 인덴 등의 방향족 비닐 화합물; 메틸아크릴레이트, 메틸메타크릴레이트, 에틸아크릴레이트, 에틸메타크릴레이트, n-프로필아크릴레이트, n-프로필메타크릴레이트, i-프로필아크릴레이트, i-프로필메타크릴레이트, n-부틸아크릴레이트, n-부틸메타크릴레이트, i-부틸아크릴레이트, i-부틸메타크릴레이트, sec-부틸아크릴레이트, sec-부틸메타크릴레이트, t-부틸아크릴레이트, t-부틸메타크릴레이트, 2-히드록시에틸아크릴레이트, 2-히드록시에틸메타크릴레이트, 2-히드록시프로필아크릴레이트, 2-히드록시프로필메타크릴레이트, 3-히드록시프로필아크릴레이트, 3-히드록시프로필메타크릴레이트, 2-히드록시부틸아크릴레이트, 2-히드록시부틸메타크릴레이트, 3-히드록시부틸아크릴레이트, 3-히드록시부틸메타크릴레이트, 4-히드록시부틸아크릴레이트, 4-히드록시부틸메타크릴레이트, 알릴아크릴레이트, 알릴메타크릴레이트, 벤질아크릴레이트, 벤질메타크릴레이트, 시클로헥실아크릴레이트, 시클로헥실메타크릴레이트, 페닐아크릴레이트, 페닐메타크릴레이트, 2-메톡시에틸아크릴레이트, 2-메톡시에틸메타크릴레이트, 2-페녹시에틸아크릴레이트, 2-페녹시에틸메타크릴레이트, 메톡시디에틸렌글리콜아크릴레이트, 메톡시디에틸렌글리콜메타크릴레이트, 메톡시트리에틸렌글리콜아크릴레이트, 메톡시트리에틸렌글리콜메타크릴레이트, 메톡시프로필렌글리콜아크릴레이트, 메톡시프로필렌글리콜메타크릴레이트, 메톡시디프로필렌글리콜아크릴레이트, 메톡시디프로필렌글리콜메타크릴레이트, 이소보르닐아크릴레이트, 이소보르닐메타크릴레이트, 디시클로펜타디에닐아크릴레이트, 디시클로펜타디에틸메타크릴레이트, 2-히드록시-3-페녹시프로필아크릴레이트, 2-히드록시-3-페녹시프로필메타크릴레이트, 글리세롤모노아크릴레이트, 글리세롤모노메타크릴레이트 등의 불포화 카르복실산 에스테르류; 2-아미노에틸아크릴레이트, 2-아미노에틸메타크릴레이트, 2-디메틸아미노에틸아크릴레이트, 2-디메틸아미노에틸메타크릴레이트, 2-아미노프로필아크릴레이트, 2-아미노프로필메타크릴레이트, 2-디메틸아미노프로필아크릴레이트, 2-디메틸아미노프로 필메타크릴레이트, 3-아미노프로필아크릴레이트, 3-아미노프로필메타크릴레이트, 3-디메틸아미노프로필아크릴레이트, 3-디메틸아미노프로필메타크릴레이트 등의 불포화 카르복실산 아미노알킬에스테르류; 글리시딜아크릴레이트, 글리시딜메타크릴레이트 등의 불포화 카르복실산 글리시딜에스테르류; 아세트산 비닐, 프로피온산 비닐, 부티르산 비닐, 벤조산 비닐 등의 카르복실산 비닐에스테르류; 비닐메틸에테르, 비닐에틸에테르, 알릴글리시딜에테르 등의 불포화 에테르류;아크릴로니트릴, 메타크릴로니트릴, α-클로로아크릴로니트릴, 시안화 비닐리덴 등의 시안화 비닐 화합물; 아크릴아미드, 메타크릴아미드, α-클로로아크릴아미드, N-2-히드록시에틸아크릴아미드, N-2-히드록시에틸메타크릴아미드 등의 불포화 아미드류; 1,3-부타디엔, 이소프렌, 클로로프렌 등의 지방족 공액 디엔류; 폴리스티렌, 폴리메틸아크릴레이트, 폴리메틸메타크릴레이트, 폴리-n-부틸아크릴레이트, 폴리-n-부틸메타크릴레이트, 폴리실록산 등의 중합체 분자쇄의 말단에 모노아크릴로일기 또는 모노메타크릴로일기를 갖는 거대 단량체류; 말레이미드; N-페닐말레이미드; N-시클로헥실말레이미드; 카르복실기 함유 단량체 등을 들 수 있다.
카르복실기 함유 단량체로서는, 예를 들면 불포화 모노카르복실산, 불포화 디카르복실산, 불포화 트리카르복실산 등의 분자 중에 1개 이상의 카르복실기를 갖는 불포화 다가 카르복실산 등의 불포화 카르복실산 등을 들 수 있다.
불포화 모노카르복실산은, 예를 들면 아크릴산, 메타크릴산, 크로톤산, α-클로로아크릴산, 신남산 등을 들 수 있다. 불포화 디카르복실산은, 예를 들면 말레산, 푸마르산, 이타콘산, 시트라콘산, 메사콘산 등을 들 수 있다.
불포화 다가 카르복실산은 말레산 무수물, 이타콘산 무수물, 시트라콘산 무수물 등의 산무수물; 숙신산 모노(2-아크릴로일옥시에틸), 숙신산 모노(2-메타크릴로일옥시에틸), 프탈산모노(2-아크릴로일옥시에틸), 프탈산 모노(2-메타크릴로일옥시에틸) 등의 카르복시기를 갖는 모노(2-메타크릴로일옥시알킬)에스테르; ω-카르복시폴리카프로락톤 모노아크릴레이트, ω-카르복시폴리카프로락톤 모노메타크릴레이트 등의 양말단 디카르복시 중합체의 모노(메타)아크릴레이트일 수 있다.
알칼리 가용성 수지의 산가는 특별히 한정되지 않으며, 예를 들면 20 내지 200(KOH ㎎/g)일 수 있고, 바람직하게는 50 내지 150(KOH ㎎/g)일 수 있다. 산가가 상기 범위 내인 경우, 현상액 중의 용해성이 향상되어, 비-노출부가 쉽게 용해되고 감도가 증가하여, 결과적으로 노출부의 패턴이 현상시에 남아서 잔막률(film remaining ratio)을 개선할 수 있다.
산가란, 아크릴계중합체 1g을 중화하는 데 필요한 수산화칼륨의 양(mg)으로서 측정되는 값이며, 통상적으로 수산화칼륨 수용액으로 적정함으로써 구할 수 있다. 산가는 알칼리 가용성 수지에 포함되어 중합되는 아크릴계 단량체의 함량 또는 혼합비에 의해 조절 가능하다.
알칼리 가용성 수지의 분자량은 특별히 한정되지 않으며, 예를 들면 중량 평균 분자량이 3,000 내지 200,000일 수 있고, 바람직하게는 5,000 내지 100,000일 수 있다. 중량 평균 분자량이 상기 범위 내인 경우, 코팅 필름의 경도가 향상되어 잔막률이 높으며, 현상액 중의 비-노출부의 용해성이 탁월하고 해상도가 향상될 수 있다.
알칼리 가용성 수지의 함량은 특별히 한정되지 않으며, 예를 들면 고형분 기준으로 조성물 총 중량 중 10 내지 80중량%로 포함될 수 있고, 바람직하게는 20 내지 70중량%로 포함될 수 있다. 알칼리 가용성 수지의 함량이 상기 범위 내인 경우, 양호한 패턴을 형성할 수 있고, 해상도 및 잔막률이 향상될 수 있다.
본 발명의 착색 감광성 수지 조성물은 하기 화학식 1로 표시되는 광중합 개시제를 포함한다:
[화학식 1]
Figure pat00005
(식 중, R1은 -H, -OH, -COOH, 탄소수 1 내지 6의 알킬기 또는
Figure pat00006
이고; R2는 -O-, -S-, -NH-, -OCO- 또는 -COO-이며; R3는 탄소수 1 내지 10의 알킬기, 탄소수 4 내지 10의 시클로알킬기, 탄소수 6 내지 10의 아릴기로 치환 또는 비치환된 탄소수 1 내지 20의 알킬렌기, 탄소수 6 내지 30의 아릴렌기 또는 탄소수 7 내지 30의 아릴알킬렌기이고, 상기 알킬렌은 각각 -O-, -S-, -COO- 또는 -OCO-에 의해 0 내지 5회 중단될 수 있으며; R4는 -OH 또는 -COOH이고, n은 1 내지 3의 정수임).
본 발명의 착색 감광성 수지 조성물은 화학식 1로 표시되는 광중합 개시제 외에도 당 분야에서 통상적으로 사용되는 적어도 1종의 광중합 개시제를 더 포함할 수 있다. 예를 들면 아세토페논계, 벤조인계, 벤조페논계, 티옥산톤계, 트리아진계, 옥심계, 오늄염계, 니트로벤질토실레이트계, 벤조인토실레이트계 등을 들 수 있다.
아세토페논계는 예를 들면, 디에톡시아세토페논, 2-메틸-2-모르폴리노-1-(4-메틸티오페닐)프로판-1-온, 2-히드록시-2-메틸-1-페닐프로판-1-온, 벤질디메틸케탈, 2-히드록시-2-메틸-1-[4-(2-히드록시에톡시)페닐]프로판-1-온, 1-히드록시시클로헥실페닐케톤, 2-히드록시-2-메틸-1-[4-(1-메틸비닐)페닐]프로판-1-온의 올리고머 등을 들 수 있으며, 바람직하게는 2-메틸-2-모르폴리노-1-(4-메틸티오페닐)프로판-1-온일 수 있다. 또한, 복수의 아세토페논계 화합물 및 다른 광중합 개시제를 조합하여 사용할 수도 있다.
벤조인계는 예를 들면, 벤조인, 벤조인메틸에테르, 벤조인에틸에테르, 벤조인이소프로필에테르, 벤조인이소부틸에테르 등을 들 수 있다.
벤조페논계는 예를 들면, 벤조페논, o-벤조일벤조산메틸, 4-페닐벤조페논, 4-벤조일-4'-메틸디페닐설파이드, 3,3',4,4'-테트라(t-부틸퍼옥시카보닐)벤조페논, 2,4,6-트리메틸벤조페논 등을 들 수 있다.
티옥산톤계는 예를 들면, 2-이소프로필티옥산톤, 4-이소프로필티옥산톤, 2,4-디에틸티옥산톤, 2,4-디클로로티옥산톤, 1-클로로-4-프로폭시티옥산톤등을 들 수 있다.
트리아진계는, 예를 들면, 2,4-비스(트리클로로메틸)-6-(4-메톡시페닐)-1,3,5-트리아진, 2,4-비스(트리클로로메틸)-6-(4-메톡시나프틸)-1,3,5-트리아진, 2,4-비스(트리클로로메틸)-6-(4-메톡시스티릴)-1,3,5-트리아진, 2,4-비스(트리클로로메틸)-6-[2-(5-메틸퓨란-2-일)에테닐]-1,3,5-트리아진, 2,4-비스(트리클로로메틸)-6-[2-(퓨란-2-일)에테닐]-1,3,5-트리아진, 2,4-비스(트리클로로메틸)-6-[2-(4-디에틸아미노-2-메틸페닐)에테닐]-1,3,5-트리아진, 2,4-비스(트리클로로메틸)-6-[2-(3,4-디메톡시페닐)에테닐]-1,3,5-트리아진 등을 들 수 있다.
옥심계는 예를 들면, 2-(O-벤조일옥심)-1-[4-(페닐티오)페닐]-1,2-옥탄디온,1-(4-메틸술파닐-페닐)-부탄-1,2-부탄-2-옥심-O-아세테이트, 1-(4-메틸술파닐-페닐)-부탄-1-온옥심-O-아세테이트, 히드록시이미노-(4-메틸술파닐-페닐)-초산에틸에스테르-O-아세테이트, 히드록시이미노-(4-메틸술파닐-페닐)-초산에틸에스테르-O-벤조에이트 등을 들 수 있다.
오늄염계는 예를 들면, 4-히드록시페닐디메틸설포늄 p-톨루엔설포네이트, 4-히드록시페닐디메틸설포늄헥사플루오로안티모네이트, 4-아세톡시페닐디메틸설포늄 p-톨루엔설포네이트, 4-아세톡시페닐메틸 벤질설포늄헥사플루오로안티모네이트, 트리페닐설포늄 p-톨루엔설포네이트, 트리페닐설포늄헥사플루오로안티모네이트, 디페닐요오도늄 p-톨루엔설포네이트, 디페닐요오도늄헥사플루오로안티모네이트 등을 들 수 있다.
광중합 개시제의 함량은 특별히 한정되지 않으며, 예를 들면 고형분 기준으로 조성물 총 중량 중 0.1 내지 30중량%로 포함될 수 있고, 바람직하게는 0.5 내지 20중량%로 포함될 수 있다. 광중합 개시제의 함량이 상기 범위 내인 경우, 고감도화되어 노출시간이 단축되므로 생산성이 향상되며 높은 해상도를 유지할 수 있다.
본 발명의 착색 감광성 수지 조성물은 착색제 및 용제를 더 포함할 수 있다.
착색제는 색조가 한정되지 않으며, 얻어지는 컬러필터의 용도에 따라서 선정이 가능하다.
착색제는 안료, 염료, 천연 색소 또는 이들의 혼합물일 수 있다.
안료는 특별히 한정되지 않으며, 컬러 인덱스(The Society of Dyers and Colourists 출판)에서 피그먼트(Pigment)로 분류되어 있는 화합물이 사용될 수 있다.
예를 들면, C.I. 피그먼트옐로우 1, C.I. 피그먼트 옐로우 3, C.I. 피그먼트 옐로우 12, C.I. 피그먼트 옐로우 13, C.I. 피그먼트 옐로우 14, C.I. 피그먼트옐로우 15, C.I. 피그먼트 옐로우16, C.I. 피그먼트 옐로우 17, C.I. 피그먼트 옐로우 20, C.I. 피그먼트 옐로우24, C.I. 피그먼트 옐로우 31, C.I. 피그먼트 옐로우 53, C.I. 피그먼트 옐로우83, C.I. 피그먼트 옐로우 86, C.I. 피그먼트 옐로우 93, C.I. 피그먼트 옐로우94, C.I. 피그먼트 옐로우 109, C.I. 피그먼트 옐로우 110, C.I. 피그먼트 옐로우117, C.I. 피그먼트 옐로우 125, C.I. 피그먼트 옐로우 128, C.I. 피그먼트 옐로우137, C.I. 피그먼트 옐로우 138, C.I. 피그먼트 옐로우 139, C.I. 피그먼트 옐로우147, C.I. 피그먼트 옐로우 148, C.I. 피그먼트 옐로우 150, C.I. 피그먼트 옐로우153, C.I. 피그먼트 옐로우 154, C.I. 피그먼트 옐로우 166, C.I. 피그먼트 옐로우173, C.I. 피그먼트 옐로우 194, C.I. 피그먼트 옐로우 214 등의 황색 안료; C.I.피그먼트 오렌지 13, C.I. 피그먼트 오렌지 31, C.I. 피그먼트 오렌지 38, C.I. 피그먼트 오렌지 40, C.I. 피그먼트 오렌지 42, C.I. 피그먼트 오렌지 43, C.I. 피그먼트 오렌지 51, C.I. 피그먼트 오렌지 55, C.I. 피그먼트 오렌지 59, C.I. 피그먼트 오렌지 61, C.I. 피그먼트 오렌지 64, C.I. 피그먼트 오렌지 65, C.I. 피그먼트오렌지 71, C.I. 피그먼트 오렌지 73 등의 오렌지색 안료; C.I. 피그먼트 레드 9,C.I. 피그먼트 레드 97, C.I. 피그먼트 레드 105, C.I. 피그먼트 레드 122, C.I.피그먼트 레드 123, C.I. 피그먼트 레드 144, C.I. 피그먼트 레드 149, C.I. 피그먼트 레드 166, C.I. 피그먼트 레드 168, C.I. 피그먼트 레드 176, C.I. 피그먼트레드 177, C.I. 피그먼트 레드 180, C.I. 피그먼트 레드 192, C.I. 피그먼트 레드209, C.I. 피그먼트 레드 215, C.I. 피그먼트 레드 216, C.I. 피그먼트 레드 224,C.I. 피그먼트 레드 242, C.I. 피그먼트 레드 254, C.I. 피그먼트 레드 264, C.I.피그먼트 레드 265 등의 적색 안료; C.I. 피그먼트 블루 15, C.I. 피그먼트 블루15:3, C.I. 피그먼트 블루 15:4, C.I. 피그먼트 블루 15:6, C.I. 피그먼트 블루 60등의 청색 안료; C.I. 피그먼트 바이올렛 1, C.I. 피그먼트 바이올렛 19, C.I. 피그먼트 바이올렛 23, C.I. 피그먼트 바이올렛 29, C.I. 피그먼트 바이올렛 32,C.I. 피그먼트 바이올렛 36, C.I. 피그먼트 바이올렛 38 등의 바이올렛색 안료; C.I. 피그먼트 그린 7, C.I. 피그먼트 그린 36, C.I. 피그먼트 그린 58 등의 녹색 안료; C.I. 피그먼트 브라운 23, C.I. 피그먼트 브라운 25 등의 브라운색 안료; C.I. 피그먼트 블랙 1,C.I. 피그먼트 블랙 7 등의 흑색 안료 등을 들 수 있으며, 바람직하게는 C.I. 피그먼트 옐로우 138, C.I. 피그먼트 옐로우 139, C.I. 피그먼트 옐로우 150, C.I. 피그먼트 레드 177, C.I. 피그먼트 레드 209, C.I. 피그먼트 레드 254, C.I. 피그먼트 바이올렛 23, C.I. 피그먼트 블루 15:6, C.I. 피그먼트 그린 36 등 일 수 있다. 이들은 단독 또는 2종 이상 혼합하여 사용할 수 있다.
안료의 혼합 방식은 특별히 한정되지 않으며, 예를 들면, 적색 화소를 형성하기 위해 C.I. 피그먼트 레드 254 및 C.I. 피그먼트 옐로우 139를, 녹색 화소를 형성하기 위해 C.I. 피그먼트 그린 58, C.I. 피그먼트 옐로우 150 또는 C.I. 피그먼트 옐로우 138를, 청색 화소를 형성하기 위해 C.I. 피그먼트 블루 15:6을 포함할 수 있다.
염료의 종류는 용제에 대한 용해성을 가지면서 알칼리 현상액에 대한 용해성, 내열성, 내용제성 등의 신뢰성을 확보할 수 있는 것이라면 특별히 한정되지 않으며, 예를 들면 컬러 인덱스(The Society of Dyers and Colourists 출판)내에 염료로 분류되어 있는 화합물이나, 염색 노트(색염사)에 기재되어 있는 공지의 염료 중에서 설포닐기, 카르복시기 등의 산성기를 갖는 산성 염료 또는 이들의 설폰아미드체 등의 유도체; 산성 염료와 질소 함유 화합물의 염; 아조계, 크산텐계, 프탈로시아닌계의 산성염료 및 이들의 유도체 등을 들 수 있다.
구체적인 예로는, C.I. 솔벤트 염료로서, C.I. 솔벤트 옐로우 4, 14, 15, 21, 23, 24, 38, 62, 63, 68, 82, 94, 98, 99, 162 등의 황색 염료; C.I. 솔벤트 레드 8, 45, 49, 122, 125, 130 등의 적색 염료; C.I. 솔벤트 오렌지 2, 7, 11, 15, 26, 45, 56, 62 등의 오렌지색 염료; C.I. 솔벤트 블루 35, 37, 45, 59, 67 등의 청색 염료; C.I. 솔벤트 그린 1, 3, 4, 5, 7, 28, 29, 32, 33, 34, 35 등의 녹색 염료 등을 들 수 있다.
또한 C.I. 애시드 염료로서, C.I.애시드 옐로우 1, 3, 7, 9, 11, 17, 23, 25, 29, 34, 36, 38, 40, 42, 54, 65, 72, 73, 76, 79, 98, 99, 111, 112, 113, 114, 116, 119, 123, 128, 134, 135, 138, 139, 140, 144, 150, 155, 157, 160, 161, 163, 168, 169, 172, 177, 178, 179, 184, 190, 193, 196, 197, 199, 202, 203, 204, 205, 207, 212, 214, 220, 221, 228, 230, 232, 235, 238, 240, 242, 243, 251 등의 황색 염료; C.I.애시드 레드 1, 4, 8, 14, 17, 18, 26, 27, 29, 31, 34, 35, 37, 42, 44, 50, 51, 52, 57, 66, 73, 80, 87, 88, 91, 92, 94, 97, 103, 111, 114, 129, 133, 134, 138, 143, 145, 150, 151, 158, 176, 182, 183, 198, 206, 211, 215, 216, 217, 227, 228, 249, 252, 257, 258, 260, 261, 266, 268, 270, 274, 277, 280, 281, 195, 308, 312, 315, 316, 339, 341, 345, 346, 349, 382, 383, 394, 401, 412, 417, 418, 422, 426 등의 적색 염료; C.I.애시드 오렌지 6, 7, 8, 10, 12, 26, 50, 51, 52, 56, 62, 63, 64, 74, 75, 94, 95, 107, 108, 169, 173 등의 오렌지색 염료; C.I.애시드 블루 1, 7, 9, 15, 18, 23, 25, 27, 29, 40, 42, 45, 51, 62, 70, 74, 80, 83, 86, 87, 90, 92, 96, 103, 112, 113, 120, 129, 138, 147, 150, 158, 171, 182, 192, 210, 242, 243, 256, 259, 267, 278, 280, 285, 290, 296, 315, 324:1, 335, 340 등의 청색 염료; C.I.애시드 바이올렛 6B, 7, 9, 17, 19 등의 바이올렛색 염료; C.I.애시드 그린 1, 3, 5, 9, 16, 25, 27, 50, 58, 63, 65, 80, 104, 105, 106, 109등의 녹색 염료 등을 들 수 있다.
또한 C.I.다이렉트 염료로서, C.I.다이렉트 옐로우 2, 33, 34, 35, 38, 39, 43, 47, 50, 54, 58, 68, 69, 70, 71, 86, 93, 94, 95, 98, 102, 108, 109, 129, 136, 138, 141 등의 황색 염료; C.I.다이렉트 레드 79, 82, 83, 84, 91, 92, 96, 97, 98, 99, 105, 106, 107, 172, 173, 176, 177, 179, 181, 182, 184, 204, 207, 211, 213, 218, 220, 221, 222, 232, 233, 234, 241, 243, 246, 250 등의 적색 염료; C.I.다이렉트 오렌지 34, 39, 41, 46, 50, 52, 56, 57, 61, 64, 65, 68, 70, 96, 97, 106, 107 등의 오렌지색 염료; C.I.다이렉트 블루 38, 44, 57, 70, 77, 80, 81, 84, 85, 86, 90, 93, 94, 95, 97, 98, 99, 100, 101, 106, 107, 108, 109, 113, 114, 115, 117, 119, 137, 149, 150, 153, 155, 156, 158, 159, 160, 161, 162, 163, 164, 166, 167, 170, 171, 172, 173, 188, 189, 190, 192, 193, 194, 196, 198, 199, 200, 207, 209, 210, 212, 213, 214, 222, 228, 229, 237, 238, 242, 243, 244, 245, 247, 248, 250, 251, 252, 256, 257, 259, 260, 268, 274, 275, 293 등의 청색 염료; C.I.다이렉트 바이올렛 47, 52, 54, 59, 60, 65, 66, 79, 80, 81, 82, 84, 89, 90, 93, 95, 96, 103, 104 등의 바이올렛색 염료; C.I.다이렉트 그린 25, 27, 31, 32, 34, 37, 63, 65, 66, 67, 68, 69, 72, 77, 79, 82 등의 녹색 염료 등을 들 수 있다.
또한, C.I. 모단토 염료로서, C.I.모단토 옐로우 5, 8, 10, 16, 20, 26, 30, 31, 33, 42, 43, 45, 56, 61, 62, 65 등의 황색 염료; C.I.모단토 레드1, 2, 3, 4, 9, 11, 12, 14, 17, 18, 19, 22, 23, 24, 25, 26, 30, 32, 33, 36, 37, 38, 39, 41, 43, 45, 46, 48, 53, 56, 63, 71, 74, 85, 86, 88, 90, 94, 95 등의 적색 염료; C.I.모단토 오렌지 3, 4, 5, 8, 12, 13, 14, 20, 21, 23, 24, 28, 29, 32, 34, 35, 36, 37, 42, 43, 47, 48 등의 오렌지색 염료; C.I.모단토 블루 1, 2, 3, 7, 8, 9, 12, 13, 15, 16, 19, 20, 21, 22, 23, 24, 26, 30, 31, 32, 39, 40, 41, 43, 44, 48, 49, 53, 61, 74, 77, 83, 84 등의 청색 염료; C.I.모단토 바이올렛 1, 2, 4, 5, 7, 14, 22, 24, 30, 31, 32, 37, 40, 41, 44, 45, 47, 48, 53, 58 등의 바이올렛색 염료; C.I.모단토 그린 1, 3, 4, 5, 10, 15, 19, 26, 29, 33, 34, 35, 41, 43, 53 등의 녹색 염료 등을 들 수 있다.
착색제의 함량은 특별히 한정되지 않으며, 예를 들면 고형분 기준으로 조성물 총 중량 중 10 내지 70중량%로 포함될 수 있고, 바람직하게는 20 내지 60중량%로 포함될 수 있다. 착색제의 함량이 상기 범위 내인 경우, 컬러필터로 만들어졌을 때의 컬러 농도가 충분하고, 착색제 이외의 성분이 적절량 함유될 수 있어 기계적 강도가 충분한 패턴을 형성할 수 있다.
용제의 종류는 상기 성분을 충분히 분산시키고 용해할 수 있는 것이라면 특별히 한정되지 않으며, 예를 들면 에테르류, 방향족 탄화수소류, 케톤류, 알콜류, 에스테르류, 아미드류 등을 들 수 있다. 이들은 단독 또는 2종 이상 혼합하여 사용할 수 있다.
에테르류는 특별히 한정되지 않으며, 예를 들면 테트라히드로퓨란, 테트라히드로피란, 1,4-디옥산, 에틸렌글리콜모노메틸에테르, 에틸렌글리콜모노에틸에테르, 에틸렌글리콜모노프로필에테르, 에틸렌글리콜모노부틸에테르, 디에틸렌글리콜모노메틸에테르, 디에틸렌글리콜모노에틸에테르, 디에틸렌글리콜모노부틸에테르, 디에틸렌글리콜디메틸에테르, 디에틸렌글리콜디에틸에테르, 디에틸렌글리콜디프로필에테르, 디에틸렌글리콜디부틸에테르, 프로필렌글리콜메틸에테르, 프로필렌글리콜모노메틸에테르아세테이트, 프로필렌글리콜모노에틸에테르아세테이트, 프로필렌글리콜모노프로필에테르아세테이트, 메틸셀로솔브아세테이트, 에틸셀로솔브아세테이트, 에틸카비톨아세테이트, 부틸카비톨아세테이트, 프로필렌글리콜메틸에테르아세테이트, 메톡시부틸아세테이트, 메톡시펜틸아세테이트, 아니솔, 페네톨 또는 메틸아니솔 등을 들 수있다.
방향족 탄화수소류는 특별히 한정되지 않으며, 예를 들면 벤젠, 톨루엔, 크실렌, 메시틸렌 등을 들 수 있다.
케톤류는 특별히 한정되지 않으며, 예를 들면 아세톤, 2-부탄온, 2-헵탄온, 3-헵탄온, 4-헵탄온,4-메틸-2-펜탄온, 시클로펜탄온, 시클로헥산온 등을 들 수 있다.
알콜류는 특별히 한정되지 않으며, 예를 들면 메탄올, 에탄올, 프로판올, 부탄올, 헥산올, 시클로헥산올, 에틸렌글리콜, 글리세린 등을 들 수 있다.
에스테르류는 특별히 한정되지 않으며, 예를 들면 아세트산에틸, 아세트산-n-부틸, 아세트산이소부틸, 포름산아밀, 아세트산이소아밀, 아세트산이소부틸, 프로피온산부틸, 부티르산이소프로필, 부티르산에틸, 부티르산부틸, 알킬에스테르류, 락트산메틸, 락트산에틸, 옥시아세트산메틸, 옥시아세트산에틸, 옥시아세트산부틸, 메톡시아세트산메틸, 메톡시아세트산에틸, 메톡시아세트산부틸, 에톡시아세트산메틸, 에톡시아세트산에틸, 3-옥시프로피온산메틸, 3-옥시프로피온산에틸, 3-메톡시프로피온산메틸,3-메톡시프로피온산에틸, 3-에톡시프로피온산메틸, 3-에톡시프로피온산에틸, 2-옥시프로피온산메틸, 2-옥시프로피온산에틸, 2-옥시프로피온산프로필, 2-메톡시프로피온산메틸, 2-메톡시프로피온산에틸, 2-메톡시프로피온산프로필, 2-에톡시프로피온산메틸, 2-에톡시프로피온산에틸, 2-옥시-2-메틸프로피온산메틸, 2-옥시-2-메틸프로피온산에틸, 2-메톡시-2-메틸프로피온산메틸, 2-에톡시-2-메틸프로피온산에틸,피루브산메틸, 피루브산에틸, 피루브산프로필, 아세토아세트산메틸, 아세토아세트산에틸, 2-옥소부탄산메틸, 2-옥소부탄산에틸, 3-메톡시부틸아세테이트, 3-메틸-3-메톡시부틸아세테이트, γ-부티로락톤 등을 들 수 있다.
아미드류는 특별히 한정되지 않으며, 예를 들면 N,N-디메틸포름아미드 또는 N,N-디메틸아세트아미드 등을 들 수 있다.
상기 용제 외에도 N-메틸피롤리돈, 디메틸설폭시드 또는 이들의 혼합물을 더 혼합하여 사용할 수 있다.
용제의 함량은 특별히 한정되지 않으며, 예를 들면 감광성 수지 조성물 총 중량 중 10 내지 90중량% 포함될 수 있고, 바람직하게는 60 내지 90중량% 포함될 수 있다. 용제의 함량이 상기 범위 내인 경우, 도포시의 평활성이 양호하고, 컬러필터를 형성했을 때 색농도가 충분하여 표시 특성이 양호할 수 있다.
본 발명의 착색 감광성 수지 조성물은 필요에 따라 광중합성 화합물 및 광중합 개시 보조제를 더 포함할 수 있다.
광중합성 화합물은 패턴의 강도를 강화시키기 위한 성분으로서, 1 내지 6관능성 단량체를 들 수 있다. 구체적인 예로는 노닐페닐카비톨아크릴레이트, 2-히드록시-3-페녹시프로필아크릴레이트, 2-에틸헥실카비톨아크릴레이트, 2-히드록시에틸아크릴레이트, N-비닐피롤리돈 등의 1관능성 단량체; 1,6-헥산디올디(메타)아크릴레이트, 에틸렌글리콜디(메타)아크릴레이트, 네오펜틸글리콜디(메타)아크릴레이트, 트리에틸렌글리콜디(메타)아크릴레이트, 비스페놀 A의 비스(아크릴로일옥시에틸)에테르, 3-메틸펜탄디올디(메타)아크릴레이트, 3-(아크릴로일옥시)-2-하이드록시 프로필 메타 크릴레이트 등의 2관능성 단량체; 트리메틸올프로판트리(메타)아크릴레이트, 펜타에리트리톨트리(메타)아크릴레이트 등의 3관능성 단량체; 펜타에리트리톨테트라(메타)아크릴레이트 등의 4관능성 단량체; 디펜타에리트리톨펜타(메타)아크릴레이트 등의 5관능성 단량체; 디펜타에리트리톨헥사(메타)아크릴레이트 등의 6관능성 단량체 등을 들 수 있다. 이들은 단독 또는 2종 이상 혼합하여 사용할 수 있다.
광중합성 화합물은 패턴 강도 강화 및 평활성 개선의 측면에서 바람직하게는 2관능 이상의 다관능성 단량체일 수 있고, 보다 바람직하게는 5관능 이상의 다관능성 단량체일 수 있다.
광중합성 화합물의 함량은 특별히 한정되지 않으며, 예를 들면 고형분 기준으로 조성물 총 중량 중 5 내지 50중량%로 포함될 수 있고, 바람직하게는 7 내지 45중량%로 포함될 수 있다. 광중합성 화합물이 함량이 상기 범위 내인 경우, 화소부의 강도나 평활성이 양호할 수 있다.
광중합 개시 보조제는 광중합 개시제에 의해 중합이 개시된 광중합성 화합물의 중합을 촉진시킨다.
광중합 개시 보조제의 종류는 특별히 한정되지 않으며, 예를 들면 아민계 화합물, 알콕시안트라센계 화합물, 티옥산톤계 화합물 등을 들 수 있다. 이들은 단독 또는 2종 이상 혼합하여 사용할 수 있다.
아민계 화합물은 특별히 한정되지 않으며, 예를 들면 트리에탄올아민, 메틸디에탄올아민, 트리이소프로판올아민, 4-디메틸아미노벤조산메틸, 4-디메틸아미노벤조산에틸, 4-디메틸아미노벤조산이소아밀, 벤조산 2-디메틸아미노에틸, 4-디메틸아미노벤조산 2-에틸헥실, N,N-디메틸파라톨루이딘, 4,4'-비스(디메틸아미노)벤조페논, 4,4'-비스(디에틸아미노)벤조페논, 4,4'-비스(에틸메틸아미노)벤조페논 등을 들 수 있으며, 바람직하게는 4,4'-비스(디에틸아미노)벤조페논일 수 있다.
알콕시안트라센계 화합물은 특별히 한정되지 않으며, 예를 들면 9,10-디메톡시안트라센, 2-에틸-9,10-디메톡시안트라센, 9,10-디에톡시안트라센, 2-에틸-9,10-디에톡시안트라센 등을 들 수 있다.
티옥산톤계 화합물은 특별히 한정되지 않으며, 예를 들면 2-이소프로필티옥산톤, 4-이소프로필티옥산톤, 2,4-디에틸티옥산톤, 2,4-디클로로티옥산톤, 1-클로로-4-프로폭시티옥산톤등을 들 수 있다.
시판되는 광중합 개시 보조제로는, 예를 들면 EAB-F(호도가 야가가쿠고교가부시키가이샤 제품) 등이 있다.
사용 가능한 광중합 개시제/광중합 개시 보조제의 조합은 특별히 한정되지 않으며, 예를 들면 디에톡시아세토페논/4,4'-비스(디에틸아미노)벤조페논; 2-메틸-2-모르폴리노-1-(4-메틸티오페닐)프로판-1-온/4,4'-비스(디에틸아미노)벤조페논; 2-히드록시-2-메틸-페닐프로판-1-온/4,4'-비스(디에틸아미노)벤조페논; 2-히드록시-2-메틸-1-[4-(2-히드록시에톡시)페닐]프로판-1-온/4,4'-비스(디에틸아미노)벤조페논; 1-히드록시시클로헥실페닐케톤/4,4'-비스(디에틸아미노)벤조페논; 2-히드록시-2-메틸-1-[4-(1-메틸비닐)페닐]프로판-1-온의 올리고머/4,4'-비스(디에틸아미노)벤조페논; 2-벤질-2-디메틸아미노-1-(4-모르폴리노페닐)부탄-1-온/4,4'-비스(디에틸아미노)벤조페논의 조합 등을 들 수 있으며, 바람직하게는 2-메틸-2-모르폴리노-1-(4-메틸티오페닐)프로판-1-온/4,4'-비스(디에틸아미노)벤조페논의 조합일 수 있다.
광중합 개시 보조제의 함량은 특별히 한정되지 않으며, 예를 들면 광중합 개시제 1몰당 0.01 내지 10몰일 수 있으며, 바람직하게는 광중합 개시제 1몰당 0.01 내지 5몰일 수 있다. 광중합 개시 보조제의 함량이 상기 범위 내인 경우 중합 반응 촉진 효과가 극대화 될 수 있다.
본 발명의 착색 감광성 수지 조성물은 필요에 따라 충전제, 안료분산제, 계면활성제, 밀착성 증진제, 항산화제, 자외선 흡수제, 응집 방지제 등의 첨가제를 더 포함할 수 있다. 이들은 단독 또는 2종 이상 혼합하여 사용할 수 있다.
이들 첨가제는 조성물 총 중량에 대하여 0.001 내지 15중량%의 범위로 포함될 수 있다.
충전제의 종류는 특별히 한정되지 않으며, 예를 들면 유리, 산화알루미늄 등을 들 수 있다.
안료분산제는 착색제로 안료를 사용할 경우에, 용제에서 안료가 잘 분산될 수 있도록 한다. 안료분산제의 종류는 특별히 한정되지 않으며, 예를 들면 폴리에스테르계 중합체 분산제, 아크릴계 중합체 분산제, 폴리우레탄계 중합체 분산제, 양이온계 계면활성제, 음이온계 계면활성제, 비이온계 계면활성제 등을 들 수 있다. 안료 분산제의 함량은 특별히 한정되지 않으며, 예를 들면 착색제 1중량부 당 1중량부 이하로 포함될 수 있고, 바람직하게는 0.05 내지 0.5중량부로 포함될 수 있다. 안료 분산제의 함량이 상기 범위 내인 경우, 균일한 분산 상태의 안료를 얻을 수 있다.
밀착성 증진제의 종류는 특별히 한정되지 않으며, 예를 들면 비닐트리메톡시실란, 비닐트리에톡시실란, 비닐트리스 (2-메톡시에톡시)실란, N-(2-아미노에틸)-3-아미노프로필메틸디메톡시실란, N-(2-아미노에틸)-3-아미노프로필트리메톡시실란, 3-아미노프로필트리에톡시실란, 3-글리시독시프로필트리메톡시실란, 3-글리시독시프로필메틸디메톡시실란, 2-(3, 4-에폭시시클로헥실)에틸트리메톡시실란, 3-클로로프로필메틸디메톡시실란, 3-클로로프로필트리메톡시실란, 3-메타크릴옥시프로필트리메톡시실란, 3-머캅토프로필트리메톡시실란 등을 들 수 있다.
항산화제의 종류는 특별히 한정되지 않으며, 예를 들면 2,2-티오비스 (4-메틸-6-t-부틸페놀), 2,6-디-t-부틸페놀 등을 들 수 있다.
자외선 흡수제의 종류는 특별히 한정되지 않으며, 예를 들면 2-(3-t-부틸-5-메틸-2-히드록시페닐)-5-클로로벤조트리아졸을 들 수 있다.
응집 방지제의 종류는 특별히 한정되지 않으며, 예를 들면 나트륨 폴리아크릴레이트를 들 수 있다.
본 발명의 착색 감광성 수지 조성물은 다음과 같은 방법에 의해 제조할 수 있다.
착색제를 미리 용제와 혼합하여 착색 재료의 평균 입경이 0.2㎛ 이하 정도가 될 때까지 비드 밀 등을 이용하여 분산시킨다. 이 때, 필요에 따라 안료 분산제가 사용되고, 알칼리 가용성 수지의 일부 또는 전부가 배합되는 경우도 있다. 얻어진 분산액에 알칼리 가용성 수지의 나머지, 광중합 개시제, 필요에 따라 사용되는 그 밖의 성분, 필요에 따라 추가의 용제를 소정의 농도가 되도록 더 첨가하여 목적하는 착색 감광성 수지 조성물을 얻을 수 있다.
또한, 본 발명은 상기 착색 감광성 수지 조성물로 제조된 컬러필터를 제공한다.
컬러필터는 기판 및 상기 기판의 상부에 형성된 컬러층을 포함한다.
기판은 컬러필터 자체 기판일 수 있으며, 또는 디스플레이 장치 등에 컬러필터가 위치되는 부위일 수도 있는 것으로, 특별히 제한되지 않는다. 상기 기판은 유리, 실리콘(Si), 실리콘 산화물(SiOx) 또는 고분자 기판일 수 있으며, 상기 고분자 기판은 폴리에테르설폰(polyethersulfone, PES) 또는 폴리카보네이트(polycarbonate, PC) 등일 수 있다.
컬러층은 본 발명의 착색 감광성 수지 조성물을 포함하는 층으로, 상기 착색 감광성 수지 조성물을 도포하고 소정의 패턴으로 노광, 현상 및 열경화하여 형성된 층일 수 있다.
상기와 같은 기판 및 컬러층을 포함하는 컬러필터는, 각 착색패턴 사이에 형성된 격벽을 더 포함할 수 있으며, 블랙 매트릭스를 더 포함할 수도 있다. 또한, 컬러필터의 컬러층 상부에 형성된 보호막을 더 포함할 수도 있다.
본 발명의 착색 감광성 수지 조성물로 형성된 컬러필터는 표면 거칠기(Ra)가 3㎛ 이하일 수 있으며, 바람직하게는 2.9㎛ 이하일 수 있다. 컬러필터의 표면 거칠기가 상기 범위 내인 경우 표면 평활성이 우수하여 후공정을 진행하여도 표면 불량이 발생하지 않아 도막의 신뢰성이 향상된다.
또한 본 발명은 상기 컬러필터를 구비한 액정표시장치에 관한 것이다.
본 발명의 액정표시장치는 상기 컬러필터를 구비한 것을 제외하고는 본 발명의 기술분야에서 당업자에게 알려진 구성을 포함할 수 있고, 본 발명에서 특별히 제한하지 않는다.
이하, 본 발명의 이해를 돕기 위하여 바람직한 실시예를 제시하나, 이들 실시예는 본 발명을 예시하는 것일 뿐 첨부된 특허청구범위를 제한하는 것이 아니며, 본 발명의 범주 및 기술사상 범위 내에서 실시예에 대한 다양한 변경 및 수정이 가능함은 당업자에게 있어서 명백한 것이며, 이러한 변형 및 수정이 첨부된 특허청구범위에 속하는 것도 당연한 것이다.
실시예 1.
착색제로 안료인 C.I. 피그먼트 레드 254를 3.35중량부 및 C.I. 피그먼트 레드 177을 2.75중량부; 알칼리 가용성 수지로 N-벤질말레이미드 5몰%, 비닐톨루엔 65몰%, 아크릴산 15몰% 및 3-(아크릴로일옥시)-2-하이드록시 프로필 메타 크릴레이트 15몰%의 공중합체(고형분 산가는 100mgKOH/g, 폴리스티렌 환산 중량 평균 분자량은 10,000)를 4.07중량부; 광중합성 화합물로 디펜타에리트리톨헥사아크릴레이트(DPHA, 일본화약)를 1.83중량부; 광중합 개시제로 하기 화학식 2로 표시되는 화합물을 0.91중량부;
[화학식 2]
Figure pat00007
광중합 개시 보조제로 2,4-디에틸티옥산톤을 0.3중량부; 용제로 프로필렌글리콜모노메틸에테르아세테이트를 84중량부; 첨가제로 안료분산제(폴리에스테르계, 폴리아크릴계)를 2.64중량부, 계면활성제로 다우코닝 도레이 실리콘사의 SH8400를 0.02중량부; 밀착성 증진제로 메타아크릴록시프로필트리메톡시실란을 0.13중량부를 혼합 및 분산하여 착색 감광성수지 조성물을 제조하였다.
실시예 2.
알칼리 가용성 수지로 N-벤질말레이미드 25몰%, 비닐톨루엔 45몰%, 아크릴산 15몰% 및 3-(아크릴로일옥시)-2-하이드록시 프로필 메타 크릴레이트 15몰%의 공중합체(고형분 산가는 100mgKOH/g, 폴리스티렌 환산 중량 평균 분자량은 10,000)를 4.07중량부로 첨가한 것을 제외하고는 실시예 1과 동일한 방법으로 착색 감광성 수지 조성물을 제조하였다.
실시예 3.
알칼리 가용성 수지로 N-벤질말레이미드 45몰%, 비닐톨루엔 25몰%, 아크릴산 15몰% 및 3-(아크릴로일옥시)-2-하이드록시 프로필 메타 크릴레이트 15몰%의 공중합체(고형분 산가는 100mgKOH/g, 폴리스티렌 환산 중량 평균 분자량은 10,000)를 4.07 중량부로 첨가한 것을 제외하고는 실시예 1과 동일한 방법으로 착색 감광성 수지 조성물을 제조하였다.
실시예 4.
알칼리 가용성 수지로 N-벤질말레이미드 55몰%, 비닐톨루엔 15몰%, 아크릴산 15몰% 및 3-(아크릴로일옥시)-2-하이드록시 프로필 메타 크릴레이트 15몰% 의 공중합체(고형분 산가는 100mgKOH/g, 폴리스티렌 환산 중량 평균 분자량은 10,000)를 4.07 중량부로 첨가한 것을 제외하고는 실시예 1과 동일한 방법으로 착색 감광성 수지 조성물을 제조하였다.
비교예 1.
알칼리 가용성 수지로 비닐톨루엔 70몰%, 아크릴산 15몰% 및 3-(아크릴로일옥시)-2-하이드록시 프로필 메타 크릴레이트 15몰%의 공중합체(고형분 산가는 100mgKOH/g, 폴리스티렌 환산 중량 평균 분자량은 10,000)를 4.07 중량부로 첨가한 것을 제외하고는 실시예 1과 동일한 방법으로 착색 감광성 수지 조성물을 제조하였다.
비교예 2.
광중합 개시제로 Irgacure OXE-02를 0.91중량부로 첨가한 것을 제외하고는 실시예 1과 동일한 방법으로 착색 감광성 수지 조성물을 제조하였다.
실험예 .
실시예 및 비교예에서 제조된 착색 감광성 수지 조성물을 스핀 코팅법으로 유리 기판 위에 도포한 다음, 가열판 위에 놓고 100℃의 온도에서 3분간 유지하여 박막을 형성시켰다. 이어서 박막 위에 1 내지 50㎛의 라인/스페이스 패턴을 갖는 시험 포토마스크를 올려놓고 시험 포토마스크와의 간격을 100㎛로 하여 자외선을 조사하였다. 이때, 자외선 광원은 g, h, i 선을 모두 함유하는 1KW의 고압 수은등을 사용하여 100mJ/cm2의 조도로 조사하였다. 자외선이 조사된 박막을 pH 10.5의 KOH 수용액 현상 용액에 1분 동안 담구어 현상하였다. 박막이 입혀진 유리판을 증류수를 사용하여 세척한 다음, 질소 가스를 불어서 건조하고, 220℃의 가열 오븐에서 1시간 동안 가열하여 컬러필터를 제조하였다. 상기에서 제조된 컬러필터의 필름 두께는 2.4㎛이었다.
제조된 컬러필터 도막에 20분간 140℃, 감압(10-7torr)조건에서 ITO를 증착 한 후 30분간 220℃에서 어닐링 하여 ITO 도막을 제조하였다. 상기에서 제조된 ITO 도막의 두께는 1500Å이었다.
(1) 휘도( 색특성 ) 평가
휘도는 RED 색좌표 Ry = 0.64에서의 RY (휘도) 색특성 값을 OSP-SP200 (Olympus社)로 측정하였다. 측정 결과는 하기 표 1에 나타내었다.
(2) 현상잔사 평가
기판상 현상잔사가 없는 경우는 '○'으로, 기판상 현상잔사가 약하게 나타나는 경우는 '△'으로, 기판상 현상잔사가 심하게 나타난 경우는 '×'로 나타내었다. 평가 결과는 하기 표 1에 나타내었다.
(3) 컬러필터 표면 평활성 평가
AFM((PSIA XE-100)장비를 사용해 NonContact mode 건으로 측정한 Ra 값으로 나타내었다. 측정 결과는 하기 표 1에 나타내었다.
(4) ITO 도막 특성 평가
ITO 도막의 특성을 육안으로 평가하여 도막에 홀 또는 엠보싱 현상이 발생하지 않은 경우는 ○, 미약하게 발생하는 경우는 △, 심하게 발생하는 경우는 X로 나타내었다. 평가 결과는 하기 표 2에 나타내었다.
구분 실시예 1 실시예 2 실시예 3 실시예 4 비교예 1 비교예 2
휘도
(RY 색특성 값)		 19.56 19.55 19.55 19.55 19.56 19.19
현상잔사 ○ ○ ○ ○ △ X
표면평활성
(㎛)		 2.8 2.5 2.9 3.5 4.8 5.7
ITO 도막특성 ○ ○ ○ △ X X
상기 표 1을 참조하면, 실시예 1 내지 3의 착색 감광성 수지 조성물로 형성한 컬러필터는 휘도가 높고, 현상잔사가 발생하지 않았다. 또한, 표면 거칠기가 2.5 내지 2.9㎛로 표면 평활성이 우수하여 ITO 도막 표면에 홀 또는 엠보싱 등이 발생하지 않았다.
실시예 4의 착색 감광성 수지 조성물은 알칼리 가용성 수지가 N-벤질말레이미드를 과량으로 포함하여 ITO 도막 표면에 미약하게 엠보싱이 발생하였다.
그러나 비교예 1 및 2의 감광성 수지 조성물로 형성한 컬러필터는 휘도는 우수하였으나, 현상잔사가 발생하고, 표면 거칠기가 높아 ITO 도막 표면에 홀과 엠보싱이 심하게 발생하였다.

Claims (14)

  1. N-벤질말레이미드를 포함하여 중합된 알칼리 가용성 수지 및
    하기 화학식 1로 표시되는 광중합 개시제를 포함하는 착색 감광성 수지 조성물:
    [화학식 1]
    Figure pat00008

    (식 중, R1은 -H, -OH, -COOH, 탄소수 1 내지 6의 알킬기 또는
    Figure pat00009
    이고;
    R2는 -O-, -S-, -NH-, -OCO- 또는 -COO-이며;
    R3는 탄소수 1 내지 10의 알킬기, 탄소수 4 내지 10의 시클로알킬기, 탄소수 6 내지 10의 아릴기로 치환 또는 비치환된 탄소수 1 내지 20의 알킬렌기, 탄소수 6 내지 30의 아릴렌기 또는 탄소수 7 내지 30의 아릴알킬렌기이고, 상기 알킬렌은 각각 -O-, -S-, -COO- 또는 -OCO-에 의해 0 내지 5회 중단될 수 있으며;
    R4는 -OH 또는 -COOH이고, n은 1 내지 3의 정수임).
  2. 청구항 1에 있어서, 상기 N-벤질말레이미드는 2 내지 50몰% 포함되어 중합되는 착색 감광성 수지 조성물.
  3. 청구항 1에 있어서, 상기 알칼리 가용성 수지의 산가는 20 내지 200(KOH mg/g)인 착색 감광성 수지 조성물.
  4. 청구항 1에 있어서, 상기 알칼리 가용성 수지는 고형분 기준으로 조성물 총 중량 중 10 내지 80중량%로 포함되는 착색 감광성 수지 조성물.
  5. 청구항 1에 있어서, 아세토페논계, 벤조인계, 벤조페논계, 티옥산톤계, 트리아진계, 옥심계, 오늄염계, 니트로벤질토실레이트계 및 벤조인토실레이트계로 이루어진 군에서 선택된 적어도 1종의 광중합 개시제를 더 포함하는 착색 감광성 수지 조성물.
  6. 청구항 1에 있어서, 상기 광중합 개시제는 고형분 기준으로 조성물 총 중량 중 0.1 내지 30중량%로 포함되는 착색 감광성 수지 조성물.
  7. 청구항 1에 있어서, 착색제 및 용제를 더 포함하는 착색 감광성 수지 조성물.
  8. 청구항 7에 있어서, 상기 착색제는 고형분 기준으로 조성물 총 중량 중 10 내지 70중량%로 포함되는 착색 감광성 수지 조성물.
  9. 청구항 7에 있어서, 상기 용제는 에테르류, 방향족 탄화수소류, 케톤류, 알콜류, 에스테르류 및 아미드류로 이루어진 군에서 선택되는 착색 감광성 수지 조성물.
  10. 청구항 7에 있어서, 상기 용제는 조성물 총 중량 중 10 내지 90중량%로 포함되는 착색 감광성 수지 조성물.
  11. 청구항 1에 있어서, 광중합성 화합물 및 광중합 개시 보조제를 더 포함하는 착색 감광성 수지 조성물.
  12. 청구항 11에 있어서, 광중합성 화합물을 고형분 기준으로 조성물 총 중량 중 5 내지 50중량%, 광중합 개시 보조제를 광중합 개시제 1 몰당 0.01 내지 10몰로 포함하는 착색 감광성 수지 조성물.
  13. 청구항 1 내지 12 중 어느 한 항의 착색 감광성 수지 조성물로 형성된 컬러필터.
  14. 청구항 13에 있어서, 표면 거칠기(Ra)가 3㎛ 이하인 컬러필터.
KR1020130001980A 2013-01-08 2013-01-08 착색 감광성 수지 조성물 KR101961219B1 (ko)