Abstract

PURPOSE: A manufacturing method of a reusable and removable silicon adhesive is provided to have excellent adhesion and to prevent stickiness for long time. CONSTITUTION: A manufacturing method of a reusable and removable silicon adhesive comprises a step of mixing 40.5-54.5 weight% of a polymethyl vinyl siloxane silica, 40.5-54.5 weight% of a polymethyl vinyl and polymethyl hydrogen O siloxane and obtaining a first mixture; and a step of mixing 3-7 weight% of a polymethyl dimethyl siloxane adhesive into the first mixture solution and manufacturing a mixture solution; and a step of mixing the mixture solution for 3-5 minutes at room temperature. [Reference numerals] (AA) Manufacturing first mixed liquid by mixing polymethyl vinyl siloxane silica, polymethyl vinyl, and polymethyl hydrogen O siloxane; (BB) Manufacturing mixed liquid by mixing the first mixed liquid with polymethyl dimethyl siloxane additive; (CC) Manufacturing an attachable-detachable type silicon adhesive by mixing the mixed liquid; (DD) Separating on a base for a wig using artificial leather strings; (EE) Applying a material such as silicon on the separated area; (FF) Applying the attachable-detachable silicon adhesive on a silicon coating part; (GG) Forming an attachable-detachable silicon adhesive layer by repeating a drying process at 70-200 deg. C for 1-5 hours 2-5 times;

Description

Manufacturing method of detachable silicone adhesive and detachable silicone adhesive and wig to which the detachable silicone adhesive is applied {wiggery}

본 발명은 탈·부착식 실리콘 점착제와 탈·부착식 실리콘 점착제의 제조방법 및 상기 탈·부착식 실리콘 점착제가 적용된 가발에 관한 것으로, 상세하게는 폴리 메틸 비닐 실록산 실리카(Poly methyl vinyl siloxanes Silica) 40.5~54.5중량%와 폴리 메틸 비닐 앤 폴리 메틸 하이드로겐O 실록산(Poly methyl vinyl and Poly methyl hydrogen O siloxanes) 40.5~54.5중량% 및 폴리 메틸 디메틸 실록산 애디시브(Poly methyl dimethyl siloxanes adhessive)를 3~7중량%를 혼합하여 혼합액을 제조하고, 상기의 혼합액이 안정되도록 10~30c의 상온에서 기포가 생기지 않도록 3~5분간 천천히 저어주면서 탈·부착식 실리콘 점착제를 제조하고, 상기의 탈·부착식 실리콘 점착제를 가발용 베이스에 레자 끈을 접착하여 구획으로 분리시킨 후 실리콘과 같은 물질을 도포하면서 매끄럽게 형성한 부위에 0.2～0.5mm의 두께로 도포 후 70～200c에서 1～5시간 건조하는 과정을 2~5회 반복하여 전체 두께 1～3mm의 탈·부착식 실리콘 점착제층을 형성하도록 함으로써 물이나 땀에 쉽게 떨어지지 않아 접착력이 우수하며, 장기간 부착하여도 끈적이지 않고, 재사용이 가능하여 필요에 따라 탈부착 가능하며, 인체에 무해한 가발용 탈·부착식 실리콘 점착제를 제조하는 방법과 이 방법으로 제조된 탈·부착식 실리콘 점착제 및 상기 탈·부착식 실리콘 점착제가 적용된 가발에 관한 것이다.The present invention relates to a detachable silicone adhesive, a method for preparing a detachable silicone adhesive, and a wig to which the detachable silicone adhesive is applied. Specifically, poly methyl vinyl siloxanes Silica 40.5 ~ 54.5% by weight, 40.5 ~ 54.5% by weight of poly methyl vinyl and Poly methyl hydrogen O siloxanes, and 3-7% by weight of poly methyl dimethyl siloxane adhessive % By mixing% to prepare a mixed solution, and stir slowly for 3 to 5 minutes to avoid bubbles at room temperature of 10 ~ 30c so that the mixture is stabilized, to prepare a detachable silicone adhesive, wherein the removable silicone adhesive 0.2 ~ 0.5mm thickness on the part formed by smoothly attaching the leather string to the base for the wig and separating it into compartments and applying a material such as silicone. After the coating process, the process of drying 1-5 hours at 70 ~ 200c is repeated 2 ~ 5 times to form a detachable silicone adhesive layer with a total thickness of 1 ~ 3mm. It is non-sticky even after long-term adhesion, and it is reusable, so that it can be attached and detached if necessary, and a method for producing a detachable silicone adhesive for wigs that is harmless to the human body, and a detachable silicone adhesive prepared by this method and the detachable The present invention relates to a wig to which an adhesive silicone adhesive is applied.

일반적으로 가발은 일시적 또는 영구적인 탈모현상이 발생된 부위를 커버하기 위하여 착용하는 용도로 주로 사용되는데, 최근 유전적인 요인 이외에도 환경이나 스트레스 등의 영향으로 젊은 층 및 남녀를 불문하고 탈모의 발생이 증대되고 있으며, 분장이나 장식, 헤어스타일을 다양하게 하기 위하여 착용하는 등 가발의 활용이 증대되고 있다.In general, wigs are mainly used to cover areas where temporary or permanent hair loss occurs. In addition to genetic factors, the occurrence of hair loss increases in both young and men due to environmental and stress effects. The use of wigs is increasing, such as wearing to make up a variety of makeup, decorations, hairstyles.

이러한 가발의 종류는 보통 부착방식에 따라 버튼식, 고정식 및 테이프식으로 분류될 수 있다. 버튼식은 부착력이 약하여 불안정하며, 고정식은 샤워나 운동 등에 강한 접착력을 갖는데 장기간 부착하다 보니 위생적이지 못하고, 장기간 부착하면서 끈적이고, 재사용이 불가능하며, 테이프식은 물과 땀에 쉽게 떨어지는 단점이 있으며,These types of wigs can be generally classified into button type, fixed type and tape type according to the attachment method. The button type is unstable due to the weak adhesive force, and the fixed type has strong adhesive strength in showers or sports, but it is not hygienic because it is attached for a long time, and is sticky and non-reusable while being attached for a long time.

한번 벗었다가 재사용하는 경우 테이프의 접착력이 저하되어 재사용할 수 없는 점이 있다.Once peeled off and reused, there is a point that the adhesive strength of the tape is lowered and cannot be reused.

따라서 운동, 샤워 등 일상생활함에 불편이 없는 접착력을 제공하면서, 장기간 부착하여도 끈적이지 않고, 재사용이 가능하여 필요에 따라 탈부착 가능한 가발용 접착부재 및 가발의 개발이 필요한 실정이다.Therefore, it is necessary to develop an adhesive member for a wig and a wig that can be attached and detached as necessary, without being sticky even after long-term attachment while providing adhesion without inconvenience to daily life such as exercise and showering.

그리하여 2009년 10월 26일자 특허출원 제10-2009-0101693호(가발용 접착부재와 그 제조방법 및 이를 적용한 가발)가 제안되었으며,Thus, Patent Application No. 10-2009-0101693 dated October 26, 2009 (Adhesive member for wig and its manufacturing method and wig applying the same) has been proposed,

이는, 실리콘과 폴리부텐을 혼합하는 제1단계;This includes a first step of mixing silicon and polybutene;

상기 제1단계에서 혼합된 혼합물에 열을 가하여 반응시키는 제2단계; 및A second step of reacting by applying heat to the mixture mixed in the first step; And

상기 제2단계에서 반응된 반응물에 반응 억제제를 투입하는 제3단계를 포함하여 구성하였다.It was configured to include a third step of adding a reaction inhibitor to the reaction reacted in the second step.

그리고 상기의 가발용 접착부재 제조방법에 의하여 가발용 접착부재를 제조하도록 하였으며, 상기의 가발용 접착부재를 포함하는 가발을 제조하도록 하였다.Then, the wig adhesive member was manufactured by the method for manufacturing the wig adhesive member, and the wig including the wig adhesive member was manufactured.

그리고 2006년 11월 07일자 특허출원 제10-2006-7023334호(양면 접착 테이프 및 이를 구비한 가발)가 제안되었으며,In addition, Patent Application No. 10-2006-7023334 (Double Sided Adhesive Tape and Wig With It) of November 7, 2006 was proposed.

이는, 가발을 두부에 피착시키기 위한 양면 접착 테이프로서,This is a double-sided adhesive tape for attaching a wig to the head,

코어 부재 양측의 점착층 중 적어도 한쪽 점착층의 표면을, 미소 요철형으로 성형함으로써 광택제거 처리하는 동시에, 한쪽 점착층을 가발 베이스의 네트 부재로 이용하는 필라멘트 선 직경의 적어도 과반을 매몰시키는 두께로 형성함으로써, 가발의 이면에서 한쪽 점착층을 네트 부재의 그물코에 침입하게 하여 네트 부재에 접착하는 동시에, 점착층에 의해서 필라멘트를 면형으로 접착하고, 다른 쪽의 점착층을 두부에 접착하도록 구성하였다.The surface of at least one of the adhesive layers on both sides of the core member is formed into a micro uneven shape to remove the gloss and at the same time to at least half of the filament wire diameter using the one adhesive layer as the net member of the wig base. Thus, one adhesive layer was made to penetrate into the mesh of the net member on the back side of the wig, the adhesive was adhered to the net member, the filament was adhered in a planar shape by the adhesive layer, and the other adhesive layer was configured to adhere to the head.

또한 2006년 11월 13일자 특허출원 제10-2006-0111795호(우레탄 접착테잎이 구비된 가발)이 제안되었고,In addition, Patent Application No. 10-2006-0111795 dated November 13, 2006 (wig with a polyurethane adhesive tape) was proposed,

이는, 망사 형태로서 다수 개의 통풍홀이 형성되어 있고, 다수 개의 머리카락이 고정 가능하도록 된 머리카락 고정체와;It is a mesh form is formed with a plurality of ventilation holes, the hair fixture to be fixed to a plurality of hairs;

머리카락 고정체에 고정되어 있는 다수 개의 머리카락과;A plurality of hairs fixed to the hair fixture;

머리카락 고정체가 구겨지는 것을 방지하는 동시에 안쪽이 볼록하게 솟은 형태를 유지하도록 머리카락 고정체의 가장자리를 따라 부착되어 있는 스트립과;A strip attached along the edge of the hair fixture to prevent the hair fixture from being crumpled and to maintain a convexly raised shape therein;

유연하고 다수의 공극이 형성된 천에 접착성 우레탄을 코팅하되 코팅된 접착성 우레탄이 밀리지 않는 두께로 얇게 코팅한 것으로서 상기 머리카락 고정체의 하부에 고정되어 있어 착용자의 머리 부분 피부에 부착되도록 되어 있는 우레탄 접착테잎;을 포함하여 구성하였다.The urethane is coated on the flexible, multi-pore fabric with adhesive urethane, but the coating adhesive urethane is thinly coated to a thickness that does not push. It was configured to include an adhesive tape.

그러나 상기와 같은 종래의 가발용 접착제는 사람이 머리에 착용하였을 때 땀과 먼지 등으로 인해 점착성이 약화 됨은 물론, 한 번 분리시킨 후에는 그 점착성이 매우 낮아 다시 착용하는데 무리가 따르게 되는 등의 문제점이 있었다.However, the conventional wig adhesives as described above have a weakening of adhesiveness due to sweat and dust when a person wears them on the head, and after being separated once, the adhesiveness is very low, so that it is difficult to wear again. There was this.

이에 본 발명은 상기와 같은 종래의 문제점을 해소하기 위한 것으로, 폴리 메틸 비닐 실록산 실리카와 폴리 메틸 비닐 앤 폴리 메틸 하이드로겐O 실록산 및 폴리 메틸 디메틸 실록산 애디시브를 혼합한 혼합액을 상온에서 3~5분간 천천히 저으면서 혼합하여 탈·부착식 실리콘 점착제를 제조하도록 함을 그 목적으로 한다.Accordingly, the present invention is to solve the conventional problems as described above, the mixture of polymethyl vinyl siloxane silica, poly methyl vinyl and poly methyl hydrogen O siloxane and poly methyl dimethyl siloxane additive at room temperature for 3 to 5 minutes It is aimed to prepare a detachable silicone adhesive by mixing while stirring slowly.

그리고 본 발명은 상기의 제조한 탈·부착식 실리콘 점착제를, 가발용 베이스에 레자 끈으로 분리시켜 매끄럽게 형성한 부위에 0.2～0.5mm의 두께로 도포 후 70～200c에서 1～5시간 건조하는 과정을 2~5회 반복하여 전체 두께 1～3mm의 탈·부착식 실리콘 점착제층을 형성하도록 한 탈·부착식 실리콘 점착제를 구비한 가발을 제공하는 것을 다른 목적으로 한다.And the present invention is a process of drying for 1 to 5 hours at 70 ~ 200c after applying the detachable silicone adhesive prepared above, the thickness of 0.2 ~ 0.5mm to a smoothly formed site by separating the leather strap on the base for the wig Another object of the present invention is to provide a wig having a detachable silicone adhesive having a thickness of 1 to 3 mm to form a detachable silicone adhesive layer having a total thickness of 1 to 3 mm.

상기 목적을 달성하기 위한 본 발명의 탈·부착식 실리콘 점착제와 탈·부착식 실리콘 점착제의 제조방법 및 상기 탈·부착식 실리콘 점착제가 적용된 가발은,The wig to which the detachable silicone adhesive and the detachable silicone adhesive of the present invention and the detachable silicone adhesive are applied to achieve the above object,

폴리 메틸 비닐 실록산 실리카 40.5~54.5중량%와 폴리 메틸 비닐 앤 폴리 메틸 하이드로겐O 실록산 40.5~54.5중량%를 혼합하여 1차 혼합액을 제조하고,40.5-54.5 weight% of polymethyl vinyl siloxane silica, and 40.5-54.5 weight% of polymethyl vinyl- and polymethyl-hydrogen O siloxanes are mixed, and the primary liquid mixture is prepared,

상기 1차 혼합액 93~97중량%에 혼합물의 성능을 높이기 위해 폴리 메틸 디메틸 실록산 애디시브를 3~7중량%를 혼합하여 혼합액을 제조하고,In order to increase the performance of the mixture to 93 to 97% by weight of the primary mixed solution, 3 to 7% by weight of polymethyl dimethyl siloxane additive was mixed to prepare a mixed solution,

상기의 혼합액이 안정되도록 10~30c의 상온에서 기포가 생기지 않도록 3~5분간 조심스럽고 천천히 저어주면서 혼합하여 탈·부착식 실리콘 점착제를 제조하고,Prepare a detachable silicone pressure-sensitive adhesive by mixing carefully and slowly stirring for 3-5 minutes to avoid bubbles at room temperature of 10 ~ 30c so that the mixture is stable,

상기의 탈·부착식 실리콘 점착제를 가발용 베이스에 레자 끈을 접착하여 구획으로 분리시킨 후 실리콘과 같은 물질을 도포하면서 매끄럽게 형성한 부위에 0.2～0.5mm의 두께로 도포 후 70~200c에서 1～5시간 건조하는 과정을 2~5회 반복하여 전체 두께 1～3mm의 탈·부착식 실리콘 점착제층을 형성하도록 함으로써 물이나 땀에 쉽게 떨어지지 않아 접착력이 우수하며, 장기간 부착하여도 끈적이지 않고, 접착테이프를 바꾸지 않고도 재사용이 가능하여 필요에 따라 탈부착 가능하며, 인체에 무해하도록 구성함을 특징으로 한다.The detachable silicone adhesive is attached to the base of the wig by a leather strap and separated into sections, and then applied to a smoothly formed portion while applying a material such as silicone to a thickness of 0.2 to 0.5 mm and then 1 to 70 to 200c. Repeat the drying process for 5 hours 2 ~ 5 times to form a detachable silicone adhesive layer with a total thickness of 1 ~ 3mm, so it does not easily fall on water or sweat, so it has excellent adhesion and is not sticky even after long-term adhesion. It can be reused without changing the tape, so it can be attached and detached as needed, and is configured to be harmless to the human body.

상기의 본 발명에 따른 탈·부착식 실리콘 점착제와 탈·부착식 실리콘 점착제의 제조방법 및 상기 탈·부착식 실리콘 점착제가 적용된 가발에 의하여서는 폴리 메틸 비닐 실록산 실리카(Poly methyl vinyl siloxanes Silica) 40.5~54.5중량%와 폴리 메틸 비닐 앤 폴리 메틸 하이드로겐O 실록산(Poly methyl vinyl and Poly methyl hydrogen O siloxanes) 40.5~54.5중량% 및 폴리 메틸 디메틸 실록산 애디시브(Poly methyl dimethyl siloxanes adhessive)를 3~7중량%를 혼합하여 혼합액을 제조하고, 상기의 혼합액이 안정되도록 10~30c의 상온에서 기포가 생기지 않도록 3~5분간 천천히 저어주면서 탈·부착식 실리콘 점착제를 제조하고, 상기의 탈·부착식 실리콘 점착제를 가발용 베이스에 레자 끈을 접착하여 구획으로 분리시킨 후 실리콘과 같은 물질을 도포하면서 매끄럽게 형성한 부위에 0.2～0.5mm의 두께로 도포 후 70～200c에서 1～5시간 건조하는 과정을 2~5회 반복하여 전체 두께 1～3mm의 탈·부착식 실리콘 점착제층을 형성하도록 함으로써 물이나 땀에 쉽게 떨어지지 않아 접착력이 우수하며, 장기간 부착하여도 끈적이지 않고, 재사용이 가능하여 필요에 따라 탈부착 가능하며, 인체에 무해한 탈·부착식 실리콘 점착제층을 형성하도록 함으로써 물이나 땀에 쉽게 떨어지지 않아 접착력이 우수하며, 장기간 부착하여도 끈적이지 않고, 접착테이프를 바꾸지 않고도 재사용이 가능하여 필요에 따라 탈부착 가능하며, 인체에 무해하도록 한 효과가 있다.Polymethyl vinyl siloxanes (Poly methyl vinyl siloxanes Silica) 40.5 ~ by the method of manufacturing a removable silicone adhesive and a removable silicone adhesive according to the present invention and the wig to which the removable silicone adhesive is applied 54.5% by weight, 40.5-54.5% by weight of poly methyl vinyl and Poly methyl hydrogen O siloxanes and 3-7% by weight of poly methyl dimethyl siloxane adhessive To prepare a mixed solution, and stir slowly for 3 to 5 minutes to prevent bubbles from forming at room temperature of 10 ~ 30c so that the mixed solution is stabilized to prepare a detachable silicone adhesive, wherein the detachable silicone adhesive 0.2 ~ 0.5mm thickness on the part formed by smoothly attaching the leather string to the base for wig and separating it into compartments and applying a material such as silicone. Repeat the process of drying for 1 ~ 5 hours at 70 ~ 200c after coating for 2 ~ 5 times to form detachable silicone adhesive layer with total thickness of 1 ~ 3mm. It is not sticky even if it is attached, and it is reusable, so it can be attached and detached as needed.It is easy to fall off from water or sweat by forming a removable / adhesive silicone adhesive layer that is harmless to human body. It is possible to reuse without changing the adhesive tape, and can be attached and detached as needed, there is an effect that is harmless to the human body.

도 1은 본 발명의 제조 과정을 도시한 계통도.
도 2는 본 발명의 결합상태를 상세히 도시한 일부 측단면도.1 is a schematic diagram illustrating a manufacturing process of the present invention.
Figure 2 is a partial side cross-sectional view showing in detail the coupling state of the present invention.

이하, 첨부된 도면을 참조하여 본 발명의 바람직한 실시예를 설명하면 다음과 같다.Hereinafter, preferred embodiments of the present invention will be described with reference to the accompanying drawings.

본 발명에 따른 탈·부착식 실리콘 점착제와 탈·부착식 실리콘 점착제의 제조방법 및 상기 탈·부착식 실리콘 점착제가 적용된 가발은,The wig to which the detachable silicone adhesive and the detachable silicone adhesive according to the present invention and the detachable silicone adhesive are applied,

폴리 메틸 비닐 실록산 실리카(Poly methyl vinyl siloxanes Silica) 40.5~54.5중량%와 폴리 메틸 비닐 앤 폴리 메틸 하이드로겐O 실록산(Poly methyl vinyl and Poly methyl hydrogen O siloxanes) 40.5~54.5중량%를 혼합하여 1차 혼합액을 제조하는 과정과,Primary mixture by mixing 40.5-54.5 wt% of poly methyl vinyl siloxanes silica and 40.5-54.5 wt% of poly methyl vinyl and poly methyl hydrogen O siloxanes Manufacturing process,

상기 1차 혼합액 93~97중량%에 혼합물의 성능을 높이기 위해 폴리 메틸 디메틸 실록산 애디시브(Poly methyl dimethyl siloxanes adhessive)를 3~7중량%를 혼합하여 혼합액을 제조하는 과정과,Preparing a mixture by mixing 3-7 wt% of poly methyl dimethyl siloxane adhessive in order to increase the performance of the mixture in 93-97 wt% of the primary mixed solution;

상기의 혼합액이 안정되도록 10~30c의 상온에서 기포가 생기지 않도록 3~5분간 조심스럽고 천천히 저어주면서 혼합하는 과정에 의해 탈·부착식 실리콘 점착제를 제조하도록 구성한 것이다.It is configured to prepare a removable silicone adhesive by a process of stirring carefully and slowly stirring for 3 to 5 minutes so that bubbles do not occur at room temperature of 10 ~ 30c so that the mixed solution is stable.

그리고 본 발명은 And the present invention

폴리 메틸 비닐 실록산 실리카(Poly methyl vinyl siloxanes Silica) 40.5~54.5중량%와 폴리 메틸 비닐 앤 폴리 메틸 하이드로겐O 실록산(Poly methyl vinyl and Poly methyl hydrogen O siloxanes) 40.5~54.5중량%를 혼합하여 1차 혼합액을 제조하고,Primary mixture by mixing 40.5-54.5 wt% of poly methyl vinyl siloxanes silica and 40.5-54.5 wt% of poly methyl vinyl and poly methyl hydrogen O siloxanes Manufacturing the

상기 1차 혼합액 93~97중량%에 혼합물의 성능을 높이기 위해 폴리 메틸 디메틸 실록산 애디시브(Poly methyl dimethyl siloxanes adhessive)를 3~7중량%를 혼합하여 혼합액을 제조하고,In order to increase the performance of the mixture to 93 to 97% by weight of the primary mixture, polymethyl dimethyl siloxane adjuvant (Poly methyl dimethyl siloxanes adhessive) was prepared by mixing 3 to 7% by weight,

상기의 탈·부착식 실리콘 점착제를 가발용 베이스(1)에 레자 끈(2)을 접착하여 구획으로 분리시킨 후 실리콘과 같은 물질(3)을 도포하면서 매끄럽게 형성한 부위(4)에 0.2～0.5mm의 두께로 도포 후 70~200c에서 1～5시간 건조하는 과정을 2~5회 반복하여 전체 두께 1～3mm의 탈·부착식 실리콘 점착제층(5)을 형성하도록 구성한 것이다.The detachable silicone adhesive is attached to the base 1 for the wig and the leather strap 2 is separated into sections, and then 0.2 to 0.5 is applied to the smoothly formed part 4 while applying a material such as silicone 3. After coating to a thickness of mm is repeated 2-5 times the process of drying for 1-5 hours at 70 ~ 200c is configured to form a removable silicone adhesive layer (5) having a total thickness of 1-3mm.

상기의 혼합액이 안정되도록 10~30c의 상온에서 기포가 생기지 않도록 3~5분간 조심스럽고 천천히 저어주면서 혼합하여 탈·부착식 실리콘 점착제를 제조한다.Carefully and slowly stir for 3 to 5 minutes to avoid bubbles at room temperature of 10 ~ 30c so that the mixed solution is stable to prepare a removable silicone adhesive.

그러므로 뛰어난 점착성이 지속할 뿐 아니라 점착성이 존재하는 동안 떼었다가 다시 붙일 수 있게 된다.Therefore, not only does the stickiness last, but it can be released and reattached while the stickiness is present.

그리고 상기의 탈·부착식 실리콘 점착제를 가발용 베이스(1)에 레자 끈(2)을 접착하여 구획으로 분리시킨 후 실리콘과 같은 물질(3)을 도포하면서 매끄럽게 형성한 부위(4)에 0.2～0.5mm의 두께로 도포 후 70~200c에서 1～5시간 건조하는 과정을 2~5회 반복하여 전체 두께 1～3mm의 탈·부착식 실리콘 점착제층(5)을 형성하도록 한다.And the detachable silicone adhesive is bonded to the leather strap 2 on the base 1 for the wig and separated into compartments, and then 0.2 to the smoothly formed part 4 while applying a material such as silicone 3 to 0.2 ~. After the coating to a thickness of 0.5mm to repeat the process of drying for 1-5 hours at 70 ~ 200c 2-5 times to form a removable silicone adhesive layer (5) of a total thickness of 1 ~ 3mm.

그러므로 물이나 땀에 쉽게 떨어지지 않아 접착력이 우수하며, 장기간 부착하여도 끈적이지 않고, 접착테이프를 바꾸지 않고도 재사용이 가능하여 필요에 따라 탈부착 가능하며, 인체에 무해한 상태에서 가발을 착용할 수 있게 된다.Therefore, it does not fall easily on water or sweat, so it has excellent adhesion, and it is not sticky even after long-term attachment, and it can be reused without changing the adhesive tape.

그리고 1개월 내지 2개월 정도 착용하다가 점착성이 덜어지게 되면 레자 끈(2)으로 구획된 부위(3)의 물질(4) 위에 도포된 탈·부착식 실리콘 점착제층을 분리시킨 후 다시 새로운 탈·부착식 실리콘 점착제층을 도포하여줌으로써 가발을 반영구적으로 착용할 수 있게 된다.If the adhesive becomes less used after being worn for 1 month or 2 months, the detachable silicone adhesive layer applied on the material 4 of the part 3 separated by the leather string 2 is separated, and then the new detachable adhesive layer is detached. By applying the formula silicone pressure-sensitive adhesive layer can be worn semi-permanently.

이상에서는 본 발명의 바람직한 실시예에 대하여 도시하고 또한 설명하였으나, 본 발명은 상기한 실시예에 한정되지 아니하며, 청구범위에서 청구하는 본 발명의 요지를 벗어남이 없이 당해 본 발명이 속하는 분야에서 통상의 지식을 가진 자라면 누구든지 다양한 변형 실시 가능한 것은 물론이고, 그와 같은 변경은 기재된 청구범위 내에 있게 된다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed exemplary embodiments, but many variations and modifications may be made without departing from the scope of the invention. It will be understood by those skilled in the art that various changes and modifications may be made without departing from the spirit and scope of the invention as defined by the appended claims.

1 : 베이스 2 : 레자 끈
3 : 물질 4 : 매끄러운 부위1: base 2: leather strap
3: substance 4: smooth part

Claims

Primary mixture by mixing 40.5-54.5 wt% of poly methyl vinyl siloxanes silica and 40.5-54.5 wt% of poly methyl vinyl and poly methyl hydrogen O siloxanes Manufacturing process,
Preparing a mixture by mixing 3-7 wt% of poly methyl dimethyl siloxane adhessive in order to increase the performance of the mixture in 93-97 wt% of the primary mixed solution;
Method for producing a detachable silicone adhesive, characterized in that the mixture is composed of a process of stirring carefully and slowly stirring for 3 to 5 minutes so that bubbles do not occur at room temperature of 10 ~ 30c to stabilize the mixture.

Primary mixture by mixing 40.5-54.5 wt% of poly methyl vinyl siloxanes silica and 40.5-54.5 wt% of poly methyl vinyl and poly methyl hydrogen O siloxanes Manufacturing the
In order to increase the performance of the mixture to 93 to 97% by weight of the primary mixture, polymethyl dimethyl siloxane adjuvant (Poly methyl dimethyl siloxanes adhessive) was prepared by mixing 3 to 7% by weight,
Detachable silicone pressure-sensitive adhesive, characterized in that the mixed solution is prepared by mixing while stirring carefully and slowly for 3 to 5 minutes so that bubbles do not occur at room temperature of 10 ~ 30c.

Primary mixture by mixing 40.5-54.5 wt% of poly methyl vinyl siloxanes silica and 40.5-54.5 wt% of poly methyl vinyl and poly methyl hydrogen O siloxanes Manufacturing the
In order to increase the performance of the mixture to 93 to 97% by weight of the primary mixture, polymethyl dimethyl siloxane adjuvant (Poly methyl dimethyl siloxanes adhessive) was prepared by mixing 3 to 7% by weight,
Prepare a detachable silicone pressure-sensitive adhesive by mixing carefully and slowly stirring for 3-5 minutes to avoid bubbles at room temperature of 10 ~ 30c so that the mixture is stable,
The detachable silicone adhesive is attached to the base 1 for the wig and the leather strap 2 is separated into sections, and then 0.2 to 0.5 is applied to the smoothly formed part 4 while applying a material such as silicone 3. Detachable silicone, characterized in that it is configured to form a detachable silicone adhesive layer having a total thickness of 1 to 3 mm by repeating the process of drying for 1 to 5 hours at 70-200c after application to a thickness of mm mm Wig with adhesive.