KR20130034235A - Method and apparatus for reforming metal pattern - Google Patents

Method and apparatus for reforming metal pattern Download PDF

Info

Publication number
KR20130034235A
KR20130034235A KR1020110098133A KR20110098133A KR20130034235A KR 20130034235 A KR20130034235 A KR 20130034235A KR 1020110098133 A KR1020110098133 A KR 1020110098133A KR 20110098133 A KR20110098133 A KR 20110098133A KR 20130034235 A KR20130034235 A KR 20130034235A
Authority
KR
South Korea
Prior art keywords
pair
welding
plating
plating layer
welding line
Prior art date
Application number
KR1020110098133A
Other languages
Korean (ko)
Inventor
이창용
육완
Original Assignee
현대제철 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 현대제철 주식회사 filed Critical 현대제철 주식회사
Priority to KR1020110098133A priority Critical patent/KR20130034235A/en
Publication of KR20130034235A publication Critical patent/KR20130034235A/en

Abstract

PURPOSE: A plating layer reshaping apparatus of the steel sheet and method thereof are provided to reshape a plating layer on a welding line for connecting two steel sheets, thereby preventing the surface oxidation and surface layer decarburization phenomenon of a welded part caused by mechanical abrasion. CONSTITUTION: A plating layer reshaping apparatus of a steel sheet includes a tool slide, a pair of abrasive members(200,200'), a welding machine(300) and a pair of sprays(400,400'). The tool slide transfers two steel sheets(10,10') wherein plating on the upper and the lower side is completed. A pair of pressure rollers pressurizes respectively the upper and the lower parts of two steel sheets. The pair of abrasive members removes the plating layer formed on the weld line of two steel sheets transferred through the pair of pressure rollers. The welding machine welds the weld line in which the plating layer is removed by the abrasive member. The sprays spray plating liquid on the surface of the weld line welded by the welding machine, whereby alloying by welding heat reshapes a plating layer.

Description

강판의 도금층 재형성 장치 및 그 방법{METHOD AND APPARATUS FOR REFORMING METAL PATTERN}Plating layer reforming apparatus of steel sheet and method thereof {METHOD AND APPARATUS FOR REFORMING METAL PATTERN}

본 발명은 강판의 용접부 도금층 재형성 방법에 관한 것으로, 더욱 상세하게는 도금층이 제거된 용접라인의 표면에 도금층을 재형성시킴으로써, 용접부의 기폐적 연마에 의한 표면 산화 및 표층 탈탄 현상을 방지할 수 있는 강판의 도금층 재형성 방법에 관한 것이다.
The present invention relates to a method for reforming a weld plated layer of a steel sheet, and more particularly, by reforming a plated layer on a surface of a weld line from which a plated layer has been removed, thereby preventing surface oxidation and surface layer decarburization due to the mechanical polishing of the weld. It relates to a plated layer reforming method of a steel sheet.

일반적으로, 한장의 판넬 상태에서 프레스 성형이 가능하도록 두께나 강도가 다른 두 장의 강판을 레이저 용접하는 공법을 TWB (Tailor Welded Blank)라 한다.In general, a method of laser welding two sheets of steel sheets having different thicknesses or strengths to enable press molding in a single panel state is called TWB (Tailor Welded Blank).

또한, 블랭크를 특정온도 이상 가열 후 프레스 성형과 동시에 냉각하여 성형 전 낮은 강도에서 성형을 용이하게 하고, 성형 후 고강도를 갖게 하는 두 가지 이점을 동시에 취하는 기술을 HPF(Hot Press Forming) 공법이라 한다.In addition, a technology that simultaneously takes two advantages of heating the blank at a certain temperature and simultaneously cooling it with press molding to facilitate molding at low strength before molding and having high strength after molding is called HPF (Hot Press Forming).

HPF 용 강판은, 높은 온도에서 가열되는 공정을 거치게 되는데 이때 강판 표면의 산화를 방지하는 목적으로 도금층을 입히게 되는데, 가장 일반적인 도금 성분은 Al-Si으로 이루어진다.The steel sheet for HPF is subjected to a heating process at a high temperature, in which a coating layer is coated for the purpose of preventing oxidation of the surface of the steel sheet. The most common plating component is Al-Si.

최근 차체 경량화 및 안전강화 기준충족을 위해 TWB와 HPF의 하이브리드 공법이 개발된 TWB와 HPF의 하이브리드 공법은, HPF 공정 전에 TWB 공정을 실시하여, 블랭크의 용도에 맞게 강판 두께 및 강판 강도의 조합을 가능하게 하는 것이다.The hybrid method of TWB and HPF, which was developed recently to meet the weight reduction and safety standards of the vehicle body, is a TWB and HPF hybrid method.The TWB process is performed before the HPF process. It is to make it.

그러나, 종래의 TWB와 HPF의 하이브리드 공법은, TWB 공정 시 Al-Si 도금층이 용접부에 침투하게 되어 용접효율이 급격하게 떨어지는 단점이 있다.However, the conventional hybrid method of TWB and HPF has a disadvantage in that the Al-Si plating layer penetrates into the welding part during the TWB process and thus the welding efficiency is sharply decreased.

이러한 문제점을 해결하기 위해, 근래에는 레이저 용접전에 용접부위에 존재하는 도금층을 기계적으로 제거한 후 TWB 라인에 투입하여 도금층의 용접부 침투를 최소화한다. In order to solve this problem, recently, before the laser welding, the plating layer existing on the welding site is mechanically removed, and then injected into the TWB line to minimize penetration of the welding layer.

그러나, TWB와 HPF의 하이브리드 공법은 용접부 강도 유지는 가능하나, 표면에 도금층이 제거된 상태이므로, 후공정인 HPF 공정 동안 표면의 산화 및 표층 탈탄 등이 발생할 수 있었다.However, in the hybrid method of TWB and HPF, the weld strength can be maintained, but since the plating layer is removed from the surface, surface oxidation and surface decarburization may occur during the later HPF process.

본 발명과 관련된 문헌으로는 대한민국 공개특허 10-2006-0075686(2006년07월04일)가 있으며, 상기 문헌에는 맞춤 재단 용접 설비의 용접부 산화 방지 장치가 개시되어 있다.
Literature related to the present invention is Korean Patent Application Publication No. 10-2006-0075686 (July 04, 2006), which discloses an apparatus for preventing oxidation of a welding part of a customized cutting welding facility.

본 발명의 목적은 연마부재에 의해 도금층이 제거된 후에, 용접이 이루어진 용접하인에 스프레이를 이용해 도금층을 재형성시킴으로써, 용접부의 기폐적 연마에 의한 표면 산화 및 표층 탈탄 현상을 방지할 수 있는 강판의 도금층 재형성 장치 및 그 방법을 제공하는데 있다.
An object of the present invention is to re-form a plated layer using a spray on a welder's weld weld after the plated layer is removed by the polishing member, thereby to prevent surface oxidation and surface layer decarburization due to the mechanical polishing of the welded part. The present invention provides a plating layer reforming apparatus and a method thereof.

본 발명에 따른 강판의 도금층 재형성 장치는 상·하부 면에 도금이 완료된 두 장의 강판을 함께 이송시키기 위한 이송대와, 상기 이송대 상에 회전가능하게 상하에 각각 설치되며, 상기 두 장의 강판의 상 하부를 각각 가압하는 한 쌍의 가압롤러와, 상기 이송대의 상·하부에 회전 및 승강 가능하게 설치되며, 상기 한 쌍의 가압롤러를 통해 이송되는 상기 두 장의 강판의 용접라인에 형성된 도금층을 제거하기 위한 한 쌍의 연마부재와, 상기 연마부재에 의해 도금층이 제거된 용접 라인을 용접하기 위한 용접기와, 상기 이송대의 상 하부에 설치되며, 상기 용접기에 의해 용접된 상기 용접라인 표면에 도금액을 분사하여, 용접 열에 의해 도금층을 재형성되도록 하는 한 쌍의 스프레이를 포함하는 것을 특징으로 한다.The plated layer reforming apparatus of the steel sheet according to the present invention is a transport table for transporting the two plated steel sheets together on the upper and lower surfaces together, rotatably installed on the transport table in the upper and lower sides, respectively, A pair of pressure rollers pressurizing the upper and lower portions respectively, and the upper and lower portions of the transfer table are rotatably installed and lifted, and the plating layer formed on the welding line of the two sheets of steel sheet conveyed through the pair of pressure rollers is removed. A pair of polishing members for welding, a welding machine for welding a welding line from which the plating layer has been removed by the polishing member, and a plating solution sprayed onto the surface of the welding line welded by the welding machine, which is installed on the upper and lower portions of the conveyer. And a pair of sprays for reforming the plating layer by the welding heat.

여기서, 상기 이송대의 상부에는 상기 용접기가 상기 용접라인을 용접할 때 발생하는 스패터(spatter)를 흡입하여 제거하기 위한 스패터 흡입기가 더 구비되며, 상기 스패터 흡입기는 상기 용접기와 상기 한 쌍의 스프레이 사이 구간에 위치될 수 있다.Here, the upper portion of the feeder is further provided with a spatter inhaler for sucking and removing the spatter generated when the welder welds the welding line, the spatter inhaler is a pair of the welder and the pair It can be located in the interval between sprays.

또한, 상기 용접기는 레이저 빔을 사용하는 레이저 빔 용접기를 사용할 수 있다.In addition, the welder may use a laser beam welder using a laser beam.

또한, 상기 한 쌍의 스프레이를 통해 분사되는 도금액은, 알루미늄(Al), 실리콘(Si) 성분을 가질 수 있다,In addition, the plating liquid injected through the pair of sprays may have aluminum (Al) and silicon (Si) components.

한편, 본 발명에 따른 강판의 도금층 재형성 방법은 상·하부 면의 도금이 완료된 두 장의 강판의 일단이 인접하도록 이송대에 위치시키는 제1단계와, 상기 이송대에 위치된 상기 두 장의 강판의 상·하부 면을 한 쌍의 가압롤러로 가압하면서 이송시키는 제2단계와, 상기 용접라인의 상·하부 면에 형성된 도금층을 한 쌍의 연마부재로 제거하는 제3단계와, 도금층이 제거된 상기 용접라인을 용접기로 용접하여 연결시키는 제4단계와, 상기 용접기에 의해 용접된 용접라인에 용접라인 표면에 도금액을 분사하여 용접 열에 의해 도금층을 재형성되도록 하는 제5단계를 포함하는 것을 특징으로 한다.On the other hand, the method for reforming the plated layer of the steel sheet according to the present invention comprises the first step of placing the one end of the two sheets of the upper and lower surfaces of the plate is adjacent to the transfer table, and the two sheets of steel sheet located on the A second step of transferring the upper and lower surfaces while pressing the pair of pressure rollers; and a third step of removing the plating layers formed on the upper and lower surfaces of the welding line with a pair of polishing members, and the plating layers removed. And a fourth step of connecting the welding line by welding with a welder, and a fifth step of spraying a plating solution on the surface of the welding line on the welding line welded by the welder to form the plating layer by the welding heat. .

여기서, 상기 제4단계의 이후에는 상기 용접기가 상기 용접라인을 용접할 때 발생하는 스패터(spatter)를 흡입하여 제거시키는 단계가 더 포함될 수 있다.Here, after the fourth step, a step of sucking and removing a spatter generated when the welder welds the welding line may be further included.

또한, 상기 제5단계에서는 상기 한 쌍의 스프레이에서 알루미늄(Al), 실리콘(Si) 성분의 도금액을 상기 용접라인의 상·하부 면에 분사할 수 있다.
Further, in the fifth step, the plating liquid of aluminum (Al) and silicon (Si) components may be sprayed on the upper and lower surfaces of the welding line by the pair of sprays.

본 발명은 두 장의 강판을 연결하기 위해 용접된 용접라인에 도금층을 재형성시킴으로써, 용접부의 기폐적 연마에 의한 표면 산화 및 표층 탈탄 현상을 방지할 수 있으며, 이로 인해 도금층의 손실이 없고, 내식성이 우수한 HPF용 강판을 제조할 수 있는 효과를 갖는다.
The present invention can prevent the surface oxidation and surface decarburization due to the mechanical polishing of the welded portion by reforming the plated layer in the weld line welded to connect the two sheets of steel plate, so there is no loss of the plated layer, corrosion resistance Has the effect of producing an excellent steel sheet for HPF.

도 1은 본 발명에 따른 강판의 용접부 도금층 재형성 장치를 보여주기 위한 도면이다.
도 2는 본 발명에 따른 강판의 용접부 도금층 재형성 방법에 대한 각 단계를 보여주기 위한 블록도이다.
도 3은 본 발명에 따른 강판의 용접부 도금층 재형성 방법에서 각 단계들을 구체적으로 보여주기 위한 공정도이다.1 is a view for showing a weld plate plating layer reforming apparatus of a steel sheet according to the present invention.
Figure 2 is a block diagram for showing each step of the method for reforming the weld plated layer of the steel sheet according to the present invention.
Figure 3 is a process chart for showing each step in the weld plate plating layer reforming method of the steel sheet according to the present invention in detail.

이하 첨부된 도면을 참조하면서 본 발명에 따른 바람직한 실시 예를 상세히 설명하기로 한다.
Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings.

본 발명의 이점 및 특징, 그리고 그것을 달성하는 방법은 첨부된 도면과 함께 상세하게 후술되어 있는 실시예들을 참조하면 명확해질 것이다.BRIEF DESCRIPTION OF THE DRAWINGS The advantages and features of the present invention and the manner of achieving it will become apparent with reference to the embodiments described in detail below with reference to the accompanying drawings.

그러나 본 발명은 이하게 개시되는 실시예들에 의해 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 것이며, 단지 본 실시예들은 본 발명의 개시가 완전하도록 하며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이며, 본 발명은 청구항의 범주에 의해 정의될 뿐이다.However, the present invention is not limited to the embodiments disclosed herein, but may be embodied in various different forms, and the present embodiments only make the disclosure of the present invention complete, and those of ordinary skill in the art to which the present invention belongs. It is provided to fully inform the person having the scope of the invention, which is defined only by the scope of the claims.

또한, 본 발명을 설명함에 있어 관련된 공지 기술 등이 본 발명의 요지를 흐리게 할 수 있다고 판단되는 경우 그에 관한 자세한 설명은 생략하기로 한다.In the following description, well-known functions or constructions are not described in detail since they would obscure the invention in unnecessary detail.

이하, 도면을 참조로 본 발명에 따른 강판의 용접부 도금층 재형성 방법을 설명하면 다음과 같다.Hereinafter, a method for reforming a welded plated layer of a steel sheet according to the present invention will be described with reference to the accompanying drawings.

도 1은 본 발명에 따른 강판의 용접부 도금층 재형성 장치를 보여주기 위한 도면이다.1 is a view for showing a weld plate plating layer reforming apparatus of a steel sheet according to the present invention.

도시한 바와 같이, 본 발명에 따른 강판의 용접부 도금층 재형성 장치는 이송대(미도시)와, 한 쌍의 가압롤러(100, 100')와, 한 쌍의 연마부재(200, 200')와, 용접기(300)와, 한 쌍의 스프레이(400, 400')를 포함한다.As shown, the weld plate plating layer reforming apparatus of the steel sheet according to the present invention is a feed table (not shown), a pair of pressure rollers (100, 100 '), a pair of polishing members (200, 200') and , Welder 300, and a pair of sprays 400, 400 ′.

상기 이송대(100)는, 상·하부 면에 도금이 완료된 두 장의 강판(10, 10')을 함께 이송시킨다.The transfer table 100 transfers two sheets of steel sheets 10 and 10 'which have been plated together on the upper and lower surfaces thereof.

그리고, 상기 이송대(100)는 강판(10, 10')을 이송시키기 위해 길이를 갖는 테이블(미도시)과, 상기 테이블의 상부에 길이방향을 따라 다수의 이송롤러(미도시)가 배열될 수 있다.In addition, the transfer table 100 may have a table (not shown) having a length to transfer the steel sheets 10 and 10 ', and a plurality of transfer rollers (not shown) arranged along the length direction of the table. Can be.

한 쌍의 가압롤러(100, 100')는, 이송대(100) 상에 회전가능하게 상하에 각각 설치된다.The pair of pressure rollers 100 and 100 'are respectively installed on the conveyer 100 so as to be rotatable up and down.

상세하게는, 상기 한 쌍의 가압롤러(100, 100')는 이송대의 상부와 하부에 각각 대응되게 설치된 상태에서 두 장의 강판의 상·하부 면을 각각 가압한다.In detail, the pair of pressure rollers 100 and 100 'press each of the upper and lower surfaces of the two sheets of steel sheet in a state in which they are installed to correspond to the upper and lower portions of the transfer table, respectively.

한 쌍의 연마부재(300, 300')는, 이송대(100)의 상·하부에 회전 및 승강 가능하게 설치된다.The pair of abrasive members 300 and 300 'are rotatably and elevating the upper and lower portions of the conveyance table 100.

그리고, 상기 연마부재(300, 300')는 한 쌍의 가압롤러(100, 100'))를 통해 이송되는 두 장의 강판(10, 10')의 용접라인(11)에 형성된 도금층을 제거한다.The polishing members 300 and 300 'remove the plating layer formed on the welding line 11 of the two sheets of steel sheets 10 and 10' which are transferred through the pair of pressure rollers 100 and 100 '.

용접기(300)는, 한 쌍의 연마부재(300, 300')에 의해 상·하부 면의 도금층(12)이 제거된 용접라인(11)을 용접하여 상호 연결시킨다.The welder 300 welds and interconnects the welding line 11 from which the upper and lower plating layers 12 are removed by a pair of polishing members 300 and 300 '.

여기서, 상기 용접기(300)는 레이저 빔을 사용하는 레이저 빔 용접기를 사용할 수 있다.Here, the welder 300 may use a laser beam welder using a laser beam.

한 쌍의 스프레이(400, 400')는, 이송대(100)의 상 하부에 설치된다.The pair of sprays 400, 400 ′ are provided at the upper and lower portions of the transfer table 100.

그리고, 상기 한 쌍의 스프레이(400, 400')는 용접기(300)에 의해 용접된 용접라인(11)의 표면에 도금액을 분사하여, 용접 열에 의해 도금층(12)을 재형성되도록 한다.In addition, the pair of sprays 400 and 400 ′ inject a plating solution onto the surface of the welding line 11 welded by the welder 300, thereby reforming the plating layer 12 by welding heat.

또한, 상기 한 쌍의 스프레이(400, 400')를 통해 분사되는 도금액은, 알루미늄(Al), 실리콘(Si) 성분을 가질 수 있다,In addition, the plating liquid injected through the pair of sprays 400 and 400 ′ may have aluminum (Al) and silicon (Si) components.

한편, 전술한 이송대(100)의 상부에는 용접기(300)가 상기 용접라인을 용접할 때 스패터(spatter)가 발생하게 되는데, 이때 발생하는 스패터를 흡입하여 제거하기 위한 스패터 흡입기(500)가 더 구비된다.On the other hand, a spatter is generated when the welder 300 welds the welding line to the upper portion of the transfer table 100. A spatter inhaler 500 for sucking and removing the spatter generated at this time is generated. ) Is further provided.

여기서, 용접기(300)와 한 쌍의 스프레(500, 500')이 사이 구간에 위치될 수 있다. 그리고 스패터 흡입기(500)는, 공기를 흡입하여 스패너를 흡입하는 방식을 가질 수 있다. Here, the welder 300 and the pair of sprays 500 and 500 ′ may be located in a section between them. The spatter inhaler 500 may have a manner of sucking air and sucking the spanner.

이하, 도 2와 도 3을 참조로 본 발명에 따른 강판의 용접부 도금층 재형성방법에 대해 설명하면 다음과 같으며, 전술한 구성과 동일 구성에 대해서는 반복하여 설명하지 않도록 한다.Hereinafter, a method of reforming a welded plated layer of a steel sheet according to the present invention will be described with reference to FIGS. 2 and 3 as follows. The same configuration as the above-described configuration will not be repeated.

먼저, 제1단계(S100)는 상·하부 면의 도금이 완료된 두 장의 강판(10, 10')의 일단이 인접하도록 이송대(100)의 상부로 공급한다.First, the first step (S100) is supplied to the upper portion of the transfer table 100 so that one end of the two sheets of steel sheets 10 and 10 ', the plating of the upper and lower surfaces is completed.

즉, 본 발명에서는 서로 분리된 두 장의 강판을 상호 용접에 의해 연결함과 동시에, 도금층(12)이 제거된 용접라인(11)의 표면에 도금층(12)을 재형성시키기 위한 것이다.That is, in the present invention, two sheets of steel sheets separated from each other are connected by mutual welding, and at the same time, the plating layer 12 is formed on the surface of the welding line 11 from which the plating layer 12 is removed.

다음으로, 제2단계(S200)는 이송대(100)의 상부에 위치된 두 장의 강판(10, 10')의 상·하부 면을 한 쌍의 가압롤러(100, 100')로 가압하면서 이송시킨다. 이때, 상기 두 장의 강판(10, 10')은 서로 다른 두께로 성형 될 수 있다.Next, the second step (S200) is conveyed while pressing the upper and lower surfaces of the two sheets of steel sheet (10, 10 ') located on the upper portion of the conveyance table 100 with a pair of pressure rollers (100, 100') Let's do it. In this case, the two sheets of steel sheet 10 and 10 'may be formed in different thicknesses.

다음으로, 제3단계(S300)는 용접라인(11)의 상·하부 면에 형성된 도금층(12)을 한 쌍의 연마부재(300, 300')로 제거한다.Next, in the third step S300, the plating layer 12 formed on the upper and lower surfaces of the welding line 11 is removed with a pair of polishing members 300 and 300 ′.

여기서, 상기 한 쌍의 연마부재(300, 300')는 상하 대응되게 회전되는 연마롤러로 구비될 수 있다.Here, the pair of polishing members 300 and 300 'may be provided with a polishing roller which rotates up and down correspondingly.

즉, 상기 연마롤러의 대응되는 회전에 의해 용접라인(11)의 상·하부 면에 형성된 도금층(12) 만이 제거될 수 있다.That is, only the plating layer 12 formed on the upper and lower surfaces of the welding line 11 may be removed by the corresponding rotation of the polishing roller.

이때, 도금층(12)이 제거된 용접라인(11)의 상·부 용접 면이 외부로 노출된다.At this time, the upper and lower welding surfaces of the welding line 11 from which the plating layer 12 is removed are exposed to the outside.

다음으로, 제4단계(S400)는 도금층(12)이 제거된 용접라인(11)을 용접기(300)로 용접하여 연결시킨다.Next, in the fourth step S400, the welding line 11 from which the plating layer 12 is removed is welded to the welding machine 300 to be connected.

여기서, 상기 제4단계(S400)의 이후에는 용접기(300)가 용접라인(11)을 용접할 때 발생하는 스패터(spatter)를 흡입하여 제거시키는 단계(S410)가 더 포함될 수 있다.Here, after the fourth step (S400) may further include a step (S410) of sucking and removing a spatter generated when the welder 300 welds the welding line (11).

즉, 용접기(300)에 의해 용접시에 발생하는 스패터가 한 쌍의 스패터 흡입기(500)에 의해 제거되므로, 용접라인(11)의 재도금 단계에서 불균일한 도금층이 형성되지 않게 된다.That is, since the spatter generated during welding by the welder 300 is removed by the pair of spatter inhalers 500, the non-uniform plating layer is not formed in the replating step of the welding line 11.

최종적으로, 제5단계(S500)는 용접기(300)에 의해 용접된 용접라인(11)의 표면에 도금액을 분사하여 용접 열에 의해 도금층(12)을 재형성되도록 한다.Finally, the fifth step (S500) is to spray the plating liquid on the surface of the welding line 11 welded by the welder 300 to form the plating layer 12 by the welding heat.

상기 제5단계(S500)에서는, 한 쌍의 스프레이(400, 400')에서 알루미늄(Al), 실리콘(Si) 성분의 도금액을 상기 용접라인의 상·하부 면에 분사할 수 있다.In the fifth step S500, a plating liquid of aluminum (Al) or silicon (Si) component may be sprayed on the upper and lower surfaces of the welding line by a pair of sprays 400 and 400 ′.

결과적으로, 본 발명은 두 장의 강판(10, 10')을 연결하기 위해 용접된 용접라인(11)에 도금층(12)을 재형성시킴으로써, 용접부의 기폐적 연마에 의한 표면 산화 및 표층 탈탄 현상을 방지할 수 있으며, 이로 인해 도금층의 손실이 없고, 내식성이 우수한 HPF용 강판을 제조할 수 있다.As a result, the present invention reforms the surface layer and surface decarburization by the mechanical polishing of the weld by reforming the plating layer 12 in the weld line 11 welded to connect the two steel sheets 10 and 10 '. It is possible to prevent, and thereby there is no loss of the plating layer, it is possible to manufacture a steel sheet for HPF excellent in corrosion resistance.

지금까지 본 발명의 강판의 도금층 재형성 장치 및 그 방법에 관한 구체적인 실시예에 관하여 설명하였으나, 본 발명의 범위에서 벗어나지 않는 한도 내에서는 여러 가지 실시 변형이 가능함은 자명하다.Although the specific examples regarding the plated layer reforming apparatus and method thereof of the steel sheet of the present invention have been described so far, it is obvious that various implementation modifications are possible without departing from the scope of the present invention.

그러므로 본 발명의 범위에는 설명된 실시예에 국한되어 전해져서는 안 되며, 후술하는 특허청구범위뿐만 아니라 이 특허청구범위와 균등한 것들에 의해 정해져야 한다.Therefore, the scope of the present invention should not be limited to the above-described embodiments, but should be determined by the scope of the appended claims and equivalents thereof.

즉, 전술된 실시예는 모든 면에서 예시적인 것이며, 한정적인 것이 아닌 것으로 이해되어야 하며, 본 발명의 범위는 상세한 설명보다는 후술될 특허청구범위에 의하여 나타내어지며, 그 특허청구범위의 의미 및 범위 그리고 그 등가 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.
It is to be understood that the foregoing embodiments are illustrative and not restrictive in all respects and that the scope of the present invention is indicated by the appended claims rather than the foregoing description, It is intended that all changes and modifications derived from the equivalent concept be included within the scope of the present invention.

10, 10‘: 강판 11: 용접라인
12: 도금층 100, 100': 가압롤러
200, 200‘: 연마부재 300: 용접기
400, 400‘: 스프레이 500: 스패터 흡입기10, 10 ': steel plate 11: welding line
12: plating layer 100, 100 ': pressure roller
200, 200 ': abrasive member 300: welder
400, 400 ': Spray 500: Spatter inhaler

Claims (7)

상·하부 면에 도금이 완료된 두 장의 강판을 함께 이송시키기 위한 이송대와, 상기 이송대 상에 회전가능하게 상하에 각각 설치되며, 상기 두 장의 강판의 상 하부를 각각 가압하는 한 쌍의 가압롤러와, 상기 이송대의 상·하부에 회전 및 승강 가능하게 설치되며, 상기 한 쌍의 가압롤러를 통해 이송되는 상기 두 장의 강판의 용접라인에 형성된 도금층을 제거하기 위한 한 쌍의 연마부재와, 상기 연마부재에 의해 도금층이 제거된 용접 라인을 용접하기 위한 용접기와, 상기 이송대의 상 하부에 설치되며, 상기 용접기에 의해 용접된 상기 용접라인 표면에 도금액을 분사하여, 용접 열에 의해 도금층을 재형성되도록 하는 한 쌍의 스프레이를 포함하는 것을 특징으로 하는 강판의 도금층 재형성 장치.
A feeder for transporting the two plated steel sheets together on the upper and lower surfaces thereof, and a pair of pressure rollers respectively installed on the feeder so as to be rotatable, and pressurizing the upper and lower portions of the two steel sheets respectively. And a pair of abrasive members installed on upper and lower portions of the transfer table so as to be rotatable and liftable, for removing a plated layer formed on a welding line of the two sheets of steel sheet conveyed through the pair of pressure rollers. A welding machine for welding the welding line from which the plating layer has been removed by the member, and a plating solution disposed on the upper and lower portions of the conveyance table, and spraying a plating solution onto the surface of the welding line welded by the welding machine, thereby reforming the plating layer by welding heat. An apparatus for reforming a plated layer of a steel sheet, comprising a pair of sprays.
제1항에 있어서,
상기 이송대의 상부에는,
상기 용접기가 상기 용접라인을 용접할 때 발생하는 스패터(spatter)를 흡입하여 제거하기 위한 스패터 흡입기가 더 구비되며,
상기 스패터 흡입기는,
상기 용접기와 상기 한 쌍의 스프레이 사이 구간에 위치되는 것을 특징으로 하는 강판의 도금층 재형성 장치.
The method of claim 1,
In the upper portion of the transfer tray,
A spatter inhaler is further provided to suck and remove a spatter generated when the welder welds the welding line.
The spatter inhaler,
The plated layer reforming apparatus of the steel sheet, characterized in that located in the interval between the welder and the pair of spray.
제1항에 있어서,
상기 용접기는,
레이저 빔을 사용하는 레이저 빔 용접기를 사용하는 것을 특징으로 하는 강판의 도금층 재형성 장치.
The method of claim 1,
The welder,
A plated layer reforming apparatus for steel sheets, characterized by using a laser beam welder using a laser beam.
제1항에 있어서,
상기 한 쌍의 스프레이를 통해 분사되는 도금액은,
알루미늄(Al), 실리콘(Si) 성분을 가지는 것을 특징으로 하는 강판의 도금층 재형성 장치.
The method of claim 1,
The plating liquid sprayed through the pair of sprays,
The plated layer reforming apparatus of the steel plate which has aluminum (Al) and silicon (Si) component.
상·하부 면의 도금이 완료된 두 장의 강판의 일단이 인접하도록 이송대에 위치시키는 제1단계;
상기 이송대에 위치된 상기 두 장의 강판의 상·하부 면을 한 쌍의 가압롤러로 가압하면서 이송시키는 제2단계;
상기 용접라인의 상·하부 면에 형성된 도금층을 한 쌍의 연마부재로 제거하는 제3단계;
도금층이 제거된 상기 용접라인을 용접기로 용접하여 연결시키는 제4단계;
상기 용접기에 의해 용접된 용접라인에 용접라인 표면에 도금액을 분사하여 용접 열에 의해 도금층을 재형성되도록 하는 제5단계;를 포함하는 것을 특징으로 하는 강판의 도금층 재형성 방법.
A first step of placing one end of the two sheets of steel plate on which the upper and lower surfaces are plated to be adjacent to the transfer table;
A second step of transferring the upper and lower surfaces of the two sheets of steel sheets positioned on the conveyer while pressing the pair of pressure rollers;
A third step of removing the plating layers formed on the upper and lower surfaces of the welding line with a pair of abrasive members;
A fourth step of connecting the welding line from which the plating layer is removed by welding with a welder;
And a fifth step of spraying a plating solution on the surface of the welding line to the welding line welded by the welder to reform the plating layer by welding heat.
제5항에 있어서,
상기 제4단계의 이후에는,
상기 용접기가 상기 용접라인을 용접할 때 발생하는 스패터(spatter)를 흡입하여 제거시키는 단계가 더 포함하는 것을 특징으로 하는 강판의 도금층 재형성 방법.
The method of claim 5,
After the fourth step,
And removing and removing a spatter generated when the welder welds the welding line.
제5항에 있어서,
상기 제5단계에서는,
상기 한 쌍의 스프레이에서 알루미늄(Al), 실리콘(Si) 성분의 도금액을 상기 용접라인의 상·하부 면에 분사하는 것을 특징으로 하는 강판의 도금층 재형성 방법.

The method of claim 5,
In the fifth step,
The plating layer reforming method of the steel sheet, characterized in that for spraying the plating liquid of aluminum (Al), silicon (Si) component on the upper and lower surfaces of the welding line by the pair of sprays.

KR1020110098133A 2011-09-28 2011-09-28 Method and apparatus for reforming metal pattern KR20130034235A (en)