KR20110099728A - Knitted fabric - Google Patents
Knitted fabric Download PDFInfo
- Publication number
- KR20110099728A KR20110099728A KR1020117015951A KR20117015951A KR20110099728A KR 20110099728 A KR20110099728 A KR 20110099728A KR 1020117015951 A KR1020117015951 A KR 1020117015951A KR 20117015951 A KR20117015951 A KR 20117015951A KR 20110099728 A KR20110099728 A KR 20110099728A
- Authority
- KR
- South Korea
- Prior art keywords
- staple
- fiber
- fibers
- knitted fabric
- staple fiber
- Prior art date
Abstract
본 발명은, 편직물 I로서, 이는 아라미드 스테이플 섬유를 포함하는 스테이플 섬유 성분 A 및 적어도 한가지 타입의 종자 섬유 또는 조류가 풍부한 라이오셀 섬유를 인열 또는 절단시켜 제조된 스테이플 섬유, 또는 적어도 한가지 타입의 종자 섬유와 조류가 풍부한 라이오셀 섬유를 인열 또는 절단시켜 제조된 스테이플 섬유와의 혼합물을 포함하는 스테이플 섬유 성분 B로 제조되고, 여기서 상기 A 및 B는 A와 B의 균질 혼합물로부터 제조되는 혼방 스테이플 섬유 얀 AB를 형성하며, 상기 혼방 스테이플 섬유 얀 AB 중 적어도 2개가 가연되어 연사 ZAB를 형성하고, 상기 연사 ZAB 중 적어도 1개가 편직물 I로 가공된, 편직물 I에 관한 것이다.
또한, 본 발명은, 편직물 II로서, 이는 아라미드 스테이플 섬유 및/또는 폴리올레핀 스테이플 섬유를 포함하는 스테이플 섬유 성분 A 및 적어도 한가지 타입의 종자 섬유 또는 조류가 풍부한 라이오셀 섬유를 인열 또는 절단시켜 제조된 스테이플 섬유, 또는 적어도 한가지 타입의 종자 섬유와 조류가 풍부한 라이오셀 섬유를 인열 또는 절단시켜 제조된 스테이플 섬유와의 혼합물을 포함하는 스테이플 섬유 성분 B로 제조되고, 여기서, 상기 A는 오로지 A로부터 제조되는 순수 스테이플 섬유 얀 RA를 형성하고, 상기 B는 오로지 B로부터 제조되는 순수 스테이플 섬유 얀 RB를 형성하며, 상기 순수 스테이플 섬유 얀 RA 중 적어도 2개가 가연되어 연사 ZA를 형성하고, 상기 순수 스테이플 섬유 얀 RB 중 적어도 2개가 가연되어 연사 ZB를 형성하며, 상기 편직물 II는 적어도 1개의 연사 ZA와 적어도 1개의 연사 ZB가 플레이팅되어 제조된, 편직물 II에 관한 것이다.The present invention relates to knitted fabric I, which is a staple fiber component A comprising aramid staple fibers and staple fibers prepared by tearing or cutting at least one type of seed fiber or algae-rich lyocell fibers, or at least one type of seed fiber And blended staple fiber yarns AB made from a staple fiber component B comprising a mixture of staple fibers prepared by tearing or cutting algae rich lyocell fibers, wherein A and B are made from a homogeneous mixture of A and B Forming a yarn ZAB, wherein at least two of the blended staple fiber yarns AB are combustible to form twisted yarn ZAB, and at least one of the twisted yarn ZAB is processed into knit fabric I.
The present invention also relates to knitted fabric II, which is a staple fiber prepared by tearing or cutting staple fiber component A, including aramid staple fibers and / or polyolefin staple fibers, and at least one type of seed fiber or algae-rich lyocell fibers. Or staple fiber component B comprising a mixture of at least one type of seed fiber and staple fibers prepared by tearing or cutting algae rich lyocell fibers, wherein A is a pure staple prepared solely from A Forming fiber yarns RA, wherein B forms pure staple fiber yarns RB made solely from B, at least two of the pure staple fiber yarns RA are combustible to form twisted yarn ZA, and at least of the pure staple fiber yarns RB Two are combustible to form twisted yarn ZB, the knitted fabric II being red At least one twisted yarn ZA and at least one twisted yarn ZB are made of plated fabric II.
Description
본 발명은 편직물, 특히 절단(cutting) 손상에 대해 착용자를 보호하고, 양호한 착용 쾌적성(wear comfort)을 갖는 의류의 일부(a piece)인 편직물에 관한 것이다.The present invention relates to knit fabrics, in particular knit fabrics which are a piece of clothing which protects the wearer against cutting damage and has good wear comfort.
예를 들면, 글로브(glove)의 형태인 이러한 타입의 편직물이 제WO 2008/017400호에 기술되어 있다. 상기 기술된 편직물, 특히 글로브는 통상 피부에 직접 착용하며, 착용 쾌적성의 한 측면을 나타내고, 착용자가 작고 섬세한 부품을 조심스럽게 다루어야 한다면 특히 바람직한, 양호한 절단 보호와 높은 촉감이 조합되어 있다. 보다 거친 활동 도중, 편직물의 착용자에게 조절된, 착용 쾌적성은 착용자가 처한 육체적 활동에 대해 상당히 좌우된다.For example, a knitted fabric of this type in the form of a glove is described in WO 2008/017400. The knitted fabrics described above, in particular gloves, are usually worn directly on the skin, exhibit a aspect of wearing comfort, and combine a good cut protection with a high hand feel, which is particularly desirable if the wearer has to handle small and delicate parts carefully. During rougher activities, the comfort comfort adjusted to the wearer of the knitwear is highly dependent on the physical activity of the wearer.
착용자가 단순히 적절한 수준의 육체적 활동을 하고, 그 동안 땀이 거의 나지 않으면, 생성된 땀은 피부의 한선관(sweat duct) 내에서 이미 증발되어, 결과적으로 피부 표면과 편직물 내부 표면 사이에 미기후(microclimate)의 증가된 수증기 부분압을 생성하지만, 액체 물은 축적되지 않음으로써, 착용자는 피부 표면과 편직물 내부 표면 사이의 미기후에서 수증기가 물로 응축되지 않는 한 착용 쾌적성의 상당한 감소를 감지하지 못하게 된다.If the wearer simply performs an adequate level of physical activity and little sweat occurs during this time, the resulting sweat already evaporates within the skin's sweat duct, resulting in a microclimate between the skin surface and the inner surface of the knit fabric. Although it produces an increased water vapor partial pressure of), the liquid water does not accumulate, the wearer does not perceive a significant decrease in wear comfort unless water vapor condenses into water in the microclimate between the skin surface and the knit inner surface.
이와 대조적으로, 착용자가 상당량의 땀을 유발하는, 연속적이고 격렬한 육체적 활동에 놓인다면, 액체 물은 피부 표면에 축적되며, 이는 착용 쾌적성에 이롭지 못하게 된다.In contrast, if the wearer is subjected to continuous and intense physical activity, which causes a significant amount of sweat, the liquid water accumulates on the skin surface, which is not beneficial to wearing comfort.
따라서, 본 발명의 목적은 선행 기술 분야에 기술된 편직물과 동일하게 양호한 만큼 내절단성(cut resistance)을 갖지만, 착용 쾌적성은 증가된 편직물을 제공하는 것이다.It is therefore an object of the present invention to provide a knitted fabric that has cut resistance as good as the knitted fabrics described in the prior art, but with increased wearing comfort.
이 목적은,This purpose,
편직물 I로서, 이는As knitted fabric I, which
- 아라미드 스테이플 섬유를 포함하는 스테이플 섬유 성분 A 및Staple fiber component A comprising aramid staple fibers and
- 적어도 한가지 타입의 종자 섬유(seed fiber) 또는 조류(algae)가 풍부한 라이오셀(lyocell) 섬유를 인열 또는 절단시켜 제조된 스테이플 섬유, 또는 적어도 한가지 타입의 종자 섬유와 조류가 풍부한 라이오셀 섬유를 인열 또는 절단시켜 제조된 스테이플 섬유와의 혼합물을 포함하는 스테이플 섬유 성분 B로 제조되고,Tearing staple fibers made by tearing or cutting at least one type of seed fiber or algae-rich lyocell fiber, or tearing at least one type of seed fiber and algae-rich lyocell fiber Or staple fiber component B comprising a mixture with staple fibers prepared by cutting,
여기서, 상기 A 및 B는 A와 B의 균질 혼합물로부터 제조되는 혼방 스테이플 섬유 얀(mixed staple fiber yarn) AB를 형성하며, 상기 혼방 스테이플 섬유 얀 AB 중 적어도 2개가 가연되어 연사(twisted thread) ZAB를 형성하고, 상기 연사 ZAB 중 적어도 1개가 편직물 I로 가공된, 편직물 I에 의해 성취된다.Wherein A and B form a mixed staple fiber yarn AB made from a homogeneous mixture of A and B, wherein at least two of the blended staple fiber yarns AB are combustible to form twisted thread ZAB And at least one of the twisted yarns ZAB is achieved by knitted fabric I, which has been processed into knitted fabric I.
놀랍게도, 동일하게 양호한 내절단성을 갖는 본 발명의 편직물 I은 얀(yarn) 및 이의 연사가 단지 스테이플 섬유 성분 A만을 갖고 스테이플 섬유 성분 B는 함유하지 않는다는 점에서만, 본 발명의 편직물 I과 상이한 비교용 편직물과 비교시, 보다 낮은 수증기 유동 저항의 형태로 보다 높은 착용 쾌적성을 나타낸다. 물질의 수증기 유동 저항이 낮을수록, 수증기를 투과시킬 수 있는 이의 능력은 더 높아진다. 수증기를 투과시킬 수 있는 물질의 능력은 또한 물질의 "통기성(breathability)"으로서 나타낸다. 따라서, 본 발명의 편직물 I은 상응하는 비교용 편직물보다 높은 통기성을 갖는다.Surprisingly, the knitted fabric I of the present invention with equally good cut resistance differs from the knitted fabric I of the present invention only in that yarn and its twisted yarns contain only staple fiber component A and do not contain staple fiber component B. Compared with the woven fabric, it shows higher wearing comfort in the form of lower water vapor flow resistance. The lower the water vapor flow resistance of a material, the higher its ability to permeate water vapor. The ability of a material to permeate water vapor is also referred to as the "breathability" of the material. Accordingly, knitted fabric I of the present invention has higher breathability than the corresponding comparative knitted fabric.
본 발명의 편직물 I의 놀랍게도 증가된 통기성은 착용자의 단지 적절한 육체적 활동 도중, 피부의 한선관으로부터 배출되는 수증기가 비교용 편직물에 의해서 보다는 본 발명의 편직물 I에 의해서 보다 신속히 없어져서, 피부 표면과 본 발명의 편직물 I 내부 면 사이에 미기후의 수증기 부분압이 비교용 편직물을 착용할 때 보다 낮아진다. 그 결과, 본 발명의 편직물 I은 이의 착용자가 비교용 편직물의 착용자보다 피부에 대해 더 뽀송뽀송하게(dry) 느껴서 보다 쾌적한 느낌을 갖게 되는 효과를 갖는다.The surprisingly increased breathability of the knitted fabric I of the present invention, during only the proper physical activity of the wearer, the water vapor discharged from the cold tube of the skin disappears more quickly by the knitted fabric I of the present invention than by the comparative knitted fabric, thus the skin surface and the present invention. The partial vapor pressure of the microclimate between the inner surfaces of knitted fabric I is lower than when wearing the comparative knitted fabric. As a result, the knitted fabric I of the present invention has the effect that its wearer feels more dry to the skin than the wearer of the comparative knitted fabric, thereby making it feel more comfortable.
착용자가 연속적이고 격렬한 육체적 활동에 노출된다면, 본 발명의 편직물 I은 또한 확실히 착용자의 발한을 상당히 방지할 수 없어서, 액체 물이 피부 표면에 축적되게 된다. 그러나, 본 발명의 편직물 I의 놀랍게도 증가된 통기성은, 격렬함에서 적절한 육체적 활동으로 전환 후, 피부에 축적된 액체 땀이 비교용 편직물에 의해서 보다 본 발명의 편직물 I에 의해서 보다 신속히 없어지므로써, 본 발명의 편직물 I의 착용자는 비교용 편직물의 착용자보다 신속히 건조한 피부 표면 상태에, 즉 증가된 착용 쾌적성에 이르게 되는 효과를 갖는다.If the wearer is exposed to continuous and vigorous physical activity, the knitted fabric I of the present invention also certainly cannot significantly prevent the wearer's sweating, causing liquid water to accumulate on the skin surface. However, the surprisingly increased breathability of the knitted fabric I of the present invention, after switching from strenuous to proper physical activity, the liquid sweat accumulated in the skin is more quickly lost by the knitted fabric I of the present invention than by the comparative knitted fabric, thereby the present invention. The wearer of knitted fabric I has an effect that leads to a faster dry skin surface state, that is, increased wearing comfort, than the wearer of the comparative knitted fabric.
따라서, 본 발명의 편직물 I은 놀랍게도 동일한 내절단성에서 착용 쾌적성의 증가를 갖는다.Thus, knitted fabric I of the present invention surprisingly has an increase in wear comfort at the same cut resistance.
본 발명의 편직물 I의 스테이플 섬유 성분 A는 아라미드 스테이플 섬유를 포함한다. 바람직하게는, 본 발명의 편직물 I의 스테이플 섬유 성분 A는 아라미드 스테이플 섬유로 제조된다.Staple fiber component A of knitted fabric I of the present invention comprises aramid staple fibers. Preferably, the staple fiber component A of the knitted fabric I of the present invention is made of aramid staple fibers.
본 발명의 문맥 내에서, 용어 "아라미드 스테이플 섬유"는 아라미드 필라멘트 얀, 즉 이의 필라멘트 형성 중합체가 아라미드, 즉 방향족 폴리아미드이며, 이때 아미드 결합(-CO-NH-)의 85% 이상은 2개의 방향족 환에 직접 결합되는 필라멘트 얀을 인열 또는 절단에 의해 제조한 스테이플 섬유를 의미한다.Within the context of the present invention, the term “aramid staple fiber” refers to aramid filament yarns, ie its filament forming polymers are aramids, ie aromatic polyamides, wherein at least 85% of the amide bonds (—CO—NH—) are two aromatic By staple fibers produced by tearing or cutting a filament yarn bonded directly to the ring.
본 발명의 편직물 I의 아라미드 스테이플 섬유는 바람직하게는 p-아라미드 스테이플 섬유, 특히 바람직하게는 폴리(p-페닐렌 테레프탈아미드) 스테이플 섬유이므로, 이의 필라멘트 형성 중합체가 p-페닐렌 디아민 및 테레프탈로일 디클로라이드의 몰-대-몰(mole-for-mole) 중합으로부터 생성되는 필라멘트 얀으로부터 제조된 스테이플 섬유이다. 또한, p-아라미드 스테이플 섬유는 이의 필라멘트-형성 중합체가 p-페닐렌 디아민 및 테레프탈로일 디클로라이드 이외에, 중합체 쇄에 함침된 소량의 다른 디아민 및/또는 다른 디카복실산 클로라이드를 함유하는 공중합체인, 필라멘트 얀으로부터 제조되는 본 발명의 편직물 I에 적합하다. 일반적으로, p-페닐렌 디아민 및 테레프탈로일 디클로라이드와 관련하여, 다른 디아민 및/또는 디카복실산 클로라이드는 10mole% 이하의 양으로 중합체 쇄에 혼입될 수 있음을 이해해야 한다.The aramid staple fibers of knitted fabric I of the present invention are preferably p-aramid staple fibers, particularly preferably poly (p-phenylene terephthalamide) staple fibers, so that the filament forming polymers thereof are p-phenylene diamine and terephthaloyl Staple fibers made from filament yarns resulting from mole-for-mole polymerization of dichloride. In addition, p-aramid staple fibers are filaments whose filament-forming polymers are copolymers containing small amounts of other diamines and / or other dicarboxylic acid chlorides impregnated in the polymer chain, in addition to p-phenylene diamine and terephthaloyl dichloride. It is suitable for knitted fabric I of the present invention made from yarn. In general, with respect to p-phenylene diamine and terephthaloyl dichloride, it should be understood that other diamine and / or dicarboxylic acid chlorides may be incorporated into the polymer chain in amounts of up to 10 mole%.
본 발명의 편직물 I의 스테이플 섬유 성분 A의 아라미드 스테이플 섬유의 길이는 바람직하게는 20 내지 180㎜의 범위, 특히 바람직하게는 30 내지 120㎜의 범위 및 보다 특히 바람직하게는 30 내지 100㎜의 범위이다.The length of the aramid staple fibers of the staple fiber component A of the knitted fabric I of the present invention is preferably in the range of 20 to 180 mm, particularly preferably in the range of 30 to 120 mm and more particularly preferably in the range of 30 to 100 mm. .
본 발명의 편직물의 스테이플 섬유 성분 B는 한가지 타입의 종자 섬유 또는 조류가 풍부한 라이오셀 섬유를 인열 또는 절단시켜 제조된 적어도 스테이플 섬유, 또는 적어도 한가지 타입의 종자 섬유와 조류가 풍부한 라이오셀 섬유를 인열 또는 절단시켜 제조된 스테이플 섬유와의 혼합물을 포함한다.The staple fiber component B of the knitted fabric of the present invention tears at least staple fibers prepared by tearing or cutting one type of seed fiber or algae-rich lyocell fiber, or at least one type of seed fiber and algae-rich lyocell fiber or And mixtures with staple fibers made by cutting.
본 발명의 편직물 I의 바람직한 양태로, 적어도 한가지 타입의 종자 섬유는 케이폭 섬유, 면 섬유, 아콘 섬유 또는 상기 언급한 종자 섬유들 중 2개 또는 3개의 혼합물, 특히 케이폭 섬유와 면 섬유의 혼합물(여기서, 상기 케이폭 섬유:면 섬유의 중량비는 바람직하게는 50:50 내지 5:95의 범위이며, 특히 바람직하게는 30:70 내지 5:95의 범위이다)을 포함한다.In a preferred embodiment of knitted fabric I of the present invention, at least one type of seed fiber is a kapok fiber, cotton fiber, acorn fiber or a mixture of two or three of the aforementioned seed fibers, in particular a mixture of kapok fiber and cotton fiber, The kapok fiber: cotton fiber weight ratio is preferably in the range of 50:50 to 5:95, particularly preferably in the range of 30:70 to 5:95).
케이폭 나무로부터 수득되는 케이폭 섬유는 대략 15㎜의 섬유 길이로부터 대략 40㎜의 섬유 길이로 연장된 길이 분포를 갖는 셀룰로즈 중공 섬유이다. Kapok fibers obtained from kapok trees are cellulose hollow fibers with a length distribution extending from a fiber length of approximately 15 mm to a fiber length of approximately 40 mm.
면 섬유는 재배된 고시피움 타입(Gossypium type)으로부터의 종자모(seed hair)이며, 이때 섬유는 길이 분포를 갖고, 길이 분포는 대략 10㎜의 섬유 길이로부터 대략 55㎜의 섬유 길이로 연장된다.Cotton fibers are seed hair from the cultivated Gossypium type, wherein the fibers have a length distribution, the length distribution extending from a fiber length of approximately 10 mm to a fiber length of approximately 55 mm.
아콘 섬유는 박주가리과(Asclepiadaceae) 및 협죽도과(Apocynaceae)로부터의 종자모이며, 이때 섬유는 길이 분포를 갖고, 길이 분포는 대략 10㎜의 섬유 길이로부터 대략 30㎜의 섬유 길이로, 종종 마찬가지로 대략 40㎜의 섬유 길이 미만으로 연장된다.Acorn fibers are seed hairs from Asclepiadaceae and Apocynaceae, wherein the fibers have a length distribution, the length distribution from about 10 mm of fiber length to about 30 mm of fiber length, often likewise of about 40 mm Extends below the fiber length.
한 양태로, 본 발명의 편직물 I은 스테이플 섬유 성분 B에, 조류가 풍부한 라이오셀 섬유를 인열 또는 절단시켜 제조된 스테이플 섬유를 포함한다. 이러한 타입의 스테이플 섬유는 상표명 Seacell®(제조원: SeaCell GmbH, Rudolstadt, Germany)으로 입수할 수 있다.In one embodiment, knitted fabric I of the present invention comprises staple fibers prepared by tearing or cutting algae-rich lyocell fibers in staple fiber component B. Staple fibers of this type are available under the trade name Seacell ® (SeaCell GmbH, Rudolstadt, Germany).
라이오셀 섬유는 유기 용매에 용해된 셀룰로즈를 섬유 형태로 재생시켜 제조된 셀룰로즈 합성 섬유이다(참조: MAN-MADE FIBE YEAR BOOK, September 1997, Fiber Tables according to P.-A. KOCH, "Lyocell Fibers", pages 41-47). Seacell® 스테이플 섬유의 다공성 구조는 본 발명의 편직물 I에서 이의 통기성에 기여하며, 피부에 대한 Seacell® 스테이플 섬유에 함유된 유더믹(eudermic) 조류 성분, 예를 들면, 칼슘염 및 마그네슘염과 같은 무기 염 및 비타민 E와 같은 비타민의 방출을 촉진시켜, Seacell® 스테이플 섬유를 포함하는 본 발명의 편직물 I이 피부 영양(skin nourshing) 및 피부 치료 효과를 나타냄으로써, 긍정적인 효과가 피부 질환(예:건선 및 신경성 피부염)에 대해 성취됨을 의미한다. 또한, Seacell® 스테이플 섬유 고유의 큰 유연성(softness)은 Seacell® 스테이플 섬유를 포함하는 본 발명의 편직물 I이 착용자에 대해 피부에 매우 쾌적한 느낌을 부여하도록 기여한다. 그 결과, Seacell® 스테이플 섬유를 포함하는 본 발명의 편직물 I은 고도의 착용 쾌적성을 나타낸다.Lyocell fibers are cellulose synthetic fibers prepared by regenerating cellulose dissolved in organic solvents in the form of fibers (see MAN-MADE FIBE YEAR BOOK, September 1997, Fiber Tables according to P.-A. KOCH, "Lyocell Fibers"). , pages 41-47). The porous structure of Seacell ® staple fibers contributes to its breathability in knitted fabric I of the present invention and is an inorganic like algae component such as calcium salts and magnesium salts contained in Seacell ® staple fibers for skin. By promoting the release of vitamins such as salts and vitamin E, the knitted fabric I of the present invention comprising Seacell ® staple fibers exhibits skin nourshing and skin healing effects, such that the positive effect is a skin disease (eg psoriasis) And neurodermatitis). In addition, the flexibility (softness) of Seacell ® staple fibers unique contributes to the knitted fabric (I) of the present invention, including staple fibers Seacell ® give a very pleasant feeling to the skin for the wearer. As a result, a knitted fabric (I) of the present invention comprising a Seacell ® staple fibers shows a high degree of wearing comfort.
본 발명의 편직물 I의 양태에 사용되는, 조류가 풍부한 라이오셀 섬유를 인열 또는 절단시켜 제조된 스테이플 섬유(Seacell® 스테이플 섬유)는 바람직하게는 20 내지 180㎜의 범위, 특히 바람직하게는 30 내지 120㎜의 범위 및 보다 특히 바람직하게는 30 내지 100㎜의 범위인 길이를 갖는다.The staple fibers (Seacell ® Staple Fibers) prepared by tearing or cutting algae rich lyocell fibers, which are used in the aspect of knitted fabric I of the present invention, are preferably in the range of 20 to 180 mm, particularly preferably 30 to 120 mm. It has a length in the range of mm and more particularly preferably in the range of 30 to 100 mm.
본 발명의 편직물 I의 바람직한 양태로, 적어도 한가지 타입의 종자 섬유와 조류가 풍부한 라이오셀 섬유를 인열 또는 절단시켜 제조된 스테이플 섬유와의 혼합물은, 면 섬유와 조류가 풍부한 라이오셀 섬유를 인열 또는 절단시켜 제조된 스테이플 섬유와의 혼합물을 포함한다.In a preferred embodiment of knitted fabric I of the present invention, a mixture of at least one type of seed fiber and staple fibers prepared by tearing or cutting algae-rich lyocell fibers tears or cuts cotton fibers and algae-rich lyocell fibers. It includes a mixture with the staple fibers produced by the.
본 발명의 편직물 I의 추가의 바람직한 양태로, 면 섬유와, 조류가 풍부한 라이오셀 섬유를 인열 또는 절단시켜 제조된 스테이플 섬유와의 혼합물에서 중량비는 5:95 내지 95:5의 범위, 특히 바람직하게는 20:80 내지 80:20의 범위이다.In a further preferred embodiment of knitted fabric I of the invention, the weight ratio in the mixture of cotton fibers and staple fibers prepared by tearing or cutting algae-rich lyocell fibers ranges from 5:95 to 95: 5, particularly preferably Is in the range of 20:80 to 80:20.
본 발명의 편직물 I은 바람직하게는 99:1 내지 50:50의 범위, 보다 바람직하게는 97:3 내지 60:40의 범위 및 보다 특히 바람직하게는 95:5 내지 70:30의 범위인 A:B의 중량비로 스테이플 섬유 성분 A 및 스테이플 섬유 성분 B를 함유한다. 이 경우에, 스테이플 섬유 성분 A의 아라미드 스테이플 섬유는 새로이 제조된 아라미드 스테이플 섬유 100중량%로 이루어질 수 있다. 또는, 스테이플 섬유 성분 A의 아라미드 스테이플 섬유는 재생 아라미드 스테이플 섬유 100중량%로 이루어질 수 있다. 또한, 스테이플 섬유 성분 A의 아라미드 스테이플 섬유는 새로이 제조되고 재생된 아라미드 스테이플 섬유의 혼합물로 이루어질 수 있다.Knitted fabrics I of the invention are preferably in the range of 99: 1 to 50:50, more preferably in the range of 97: 3 to 60:40 and more particularly preferably in the range of 95: 5 to 70:30. It contains staple fiber component A and staple fiber component B in a weight ratio of B. In this case, the aramid staple fiber of the staple fiber component A may consist of 100% by weight of the newly produced aramid staple fiber. Alternatively, the aramid staple fiber of the staple fiber component A may consist of 100% by weight of regenerated aramid staple fiber. The aramid staple fibers of staple fiber component A may also consist of a mixture of freshly prepared and recycled aramid staple fibers.
본 발명의 편직물 I에서, 연사 ZAB는 적어도 2개의 혼방 스테이플 섬유 얀 AB로부터 제조되며, 이때 혼방 스테이플 섬유 얀 AB는 각각 A와 B의 균질한 혼합물로부터 제조된다. 이 경우에, 표현 "균질한 혼합물"은 필수적으로 A와 B의 혼합물의 각 용적 요소 - 및 결과적으로 또한 균질한 혼합물로부터 제조된 혼방 스테이플 섬유 얀 AB의 각 용적 요소에서 - A:B의 기술된 혼합물 비가 존재함을 의미한다.In knitted fabric I of the invention, the twisted yarn ZAB is made from at least two blended staple fiber yarns AB, wherein the blended staple fiber yarns AB are made from a homogeneous mixture of A and B, respectively. In this case, the expression “homogeneous mixture” essentially refers to each volumetric element of the mixture of A and B—and consequently also in each volumetric element of the blended staple fiber yarn AB made from a homogeneous mixture—described in A: B. It means that a mixture ratio is present.
본 발명의 편직물 I의 바람직한 양태에서, 혼방 스테이플 섬유 얀 AB의 선밀도(linear density)는 10 내지 1000tex의 범위, 특히 바람직하게는 12 내지 500tex의 범위이고, 보다 특히 바람직하게는 14 내지 100tex의 범위이다.In a preferred embodiment of knitted fabric I of the present invention, the linear density of the blended staple fiber yarns AB is in the range of 10 to 1000 tex, particularly preferably in the range of 12 to 500 tex, more particularly preferably in the range of 14 to 100 tex. .
또한, 본 발명의 편직물 I의 양태에서, 혼합 스테이플 섬유 얀 AB 중 바람직하게는 2 내지 10개 및 특히 바람직하게는 2 내지 8개가 가연되어 연사 ZAB를 형성한다.In addition, in the aspect of knitted fabric I of the present invention, preferably 2 to 10 and particularly preferably 2 to 8 of the mixed staple fiber yarns AB are twisted to form twisted yarn ZAB.
또한, 본 발명의 편직물 I의 양태에서, 연사 ZAB 중 바람직하게는 1 내지 10개 및 특히 바람직하게는 1 내지 8개가 본 발명의 편직물 I로 가공된다.In addition, in the aspect of the knitted fabric I of the present invention, preferably 1 to 10 and particularly preferably 1 to 8 of the twisted yarn ZAB are processed into the knitted fabric I of the present invention.
본 발명의 편직물 I의 추가의 바람직한 양태에서, 편직물 I은 니들 게이지 gg로 편직하며, 이때 니들 게이지는 바람직하게는 5 내지 18gg의 범위 및 특히 바람직하게는 7 내지 18gg의 범위에 놓인다.In a further preferred embodiment of the knitted fabric I of the present invention, the knitted fabric I is knitted with a needle gauge gg, wherein the needle gauge is preferably in the range of 5 to 18 gg and particularly preferably in the range of 7 to 18 gg.
본 발명의 편직물 I의 추가의 바람직한 양태에서, 편직물 I은 코스의 메시 밀도(mesh density), MiR로 편직하며, 이때 MiR은 바람직하게는 2 내지 15의 범위 및 특히 바람직하게는 3 내지 12의 범위에 놓인다.In a further preferred embodiment of the knitted fabric I of the present invention, the knitted fabric I is knitted with the mesh density of the course, MiR, wherein MiR is preferably in the range of 2 to 15 and particularly preferably in the range of 3 to 12. Is placed on.
본 발명의 편직물 I의 추가의 바람직한 양태에서, 편직물 I은 웨일즈의 메시 밀도, MiS로 편직하며, 이때 MiS는 바람직하게는 2 내지 15의 범위 및 특히 바람직하게는 3 내지 12의 범위에 놓인다.In a further preferred embodiment of the knitted fabric I of the present invention, the knitted fabric I is knitted with the mesh density of Wales, MiS, wherein the MiS is preferably in the range of 2 to 15 and particularly preferably in the range of 3 to 12.
본 발명의 편직물 I에서 내절단성 및 착용 쾌적성의 유용한 조합이 모든 타입의 옷에서 주목할 만하며, 이때 본 발명의 편직물 I은 신체에 대해 착용된다. 바람직하게는, 본 발명의 편직물 I은 글로브, 보호 슬리브(protective sleeve), 후드(hood) 또는 셔츠로서 형성되는 의류 제품이다.Useful combinations of cut resistance and wear comfort in knitted fabric I of the present invention are noteworthy in all types of clothes, where knitted fabric I of the present invention is worn against the body. Preferably, knitted fabric I of the present invention is an article of clothing formed as a glove, protective sleeve, hood or shirt.
본 발명의 근본적인 목적은, 추가로The fundamental object of the present invention is further
편직물 II로서, 이는As knit II, which
- 아라미드 스테이플 섬유 및/또는 폴리올레핀 스테이플 섬유를 포함하는 스테이플 섬유 성분 A 및Staple fiber component A comprising aramid staple fibers and / or polyolefin staple fibers and
- 적어도 한가지 타입의 종자 섬유 또는 조류가 풍부한 라이오셀 섬유를 인열 또는 절단시켜 제조된 스테이플 섬유, 또는 적어도 한가지 타입의 종자 섬유와 조류가 풍부한 라이오셀 섬유를 인열 또는 절단시켜 제조된 스테이플 섬유와의 혼합물을 포함하는 스테이플 섬유 성분 B로 제조되고,Staple fibers prepared by tearing or cutting at least one type of seed fiber or algae-rich lyocell fibers, or a mixture of at least one type of seed fibers and staple fibers made by tearing or cutting algae-rich lyocell fibers It is made of a staple fiber component B comprising a,
여기서, 상기 A는 오로지 A로부터 제조되는 순수 스테이플 섬유 얀 RA를 형성하고, 상기 B는 오로지 B로부터 제조되는 순수 스테이플 섬유 얀 RB를 형성하며, 상기 순수 스테이플 섬유 얀 RA 중 적어도 2개가 가연되어 연사 ZA를 형성하고, 상기 순수 스테이플 섬유 얀 RB 중 적어도 2개가 가연되어 연사 ZB를 형성하며, 상기 편직물 II는 상기 연사 ZA 중 적어도 1개와 상기 연사 ZB 중 적어도 1개가 플레이팅(plaiting)되어 제조된, 편직물 II에 의해 성취된다.Wherein A forms pure staple fiber yarns RA produced solely from A, and B forms pure staple fiber yarns RB manufactured solely from B, wherein at least two of the pure staple fiber yarns RA are combusted and twisted yarn ZA And at least two of the pure staple fiber yarns RB are combustible to form twisted yarn ZB, and the knitted fabric II is a knitted fabric prepared by plating at least one of the twisted yarn ZA and at least one of the twisted yarn ZB. Achieved by II.
놀랍게도, 동일하게 양호한 내절단성을 갖는 본 발명의 편직물 II는 얀 및 이의 연사가 단지 스테이플 섬유 성분 A만을 갖고 스테이플 섬유 성분 B는 함유하지 않는다는 점에서만, 본 발명의 편직물 II와 상이한 비교용 편직물과 비교시, 보다 낮은 수증기 유동 저항의 형태로 보다 높은 착용 쾌적성을 나타낸다. 이 경우에, 용어 "아라미드 스테이플 섬유", "종자 섬유" 및 "조류가 풍부한 라이오셀 섬유를 인열 또는 절단시켜 제조된 스테이플 섬유"는 본 발명의 편직물 I의 기술에서 이미 설명한 것과 동일한 의미를 갖는다.Surprisingly, knitted fabric II of the present invention with equally good cut resistance differs from comparative knitted fabrics different from knitted fabric II of the present invention only in that the yarn and its twisted yarns contain only staple fiber component A and do not contain staple fiber component B. In comparison, it exhibits higher wearing comfort in the form of lower water vapor flow resistance. In this case, the terms "aramid staple fibers", "seed fibers" and "staple fibers made by tearing or cutting algae-rich lyocell fibers" have the same meaning as already described in the art of knitted fabric I of the present invention.
본 발명의 설명 내에서, 용어 "폴리올레핀 스테이플 섬유"는 폴리올레핀 필라멘트 얀, 즉 이의 필라멘트-형성 중합체가 폴리올레핀, 바람직하게는 폴리프로필렌 및 특히 바람직하게는 폴리에틸렌인 필라멘트 얀을 인열 또는 절단시켜 제조된 스테이플 섬유를 의미한다. 그 결과, 본 발명의 편직물 II의 폴리올레핀 스테이플 섬유는 바람직하게는 폴리프로필렌 스테이플 섬유이며, 특히 바람직하게는 폴리에틸렌 스테이플 섬유이다. 이에 의해, 본 발명의 문맥에 있어서, 폴리에틸렌은 분자량이 바람직하게는 백만보다 큰 실질적으로 선형 폴리에틸렌 물질인 것으로 이해되며, 소량의 쇄 분지(chain branching) 또는 공단량체를 포함할 수 있고, 이때 소량은 주쇄에서 100개의 탄소 원자마다, 5개 이하의 쇄 분지 또는 공단량체가 존재함을 의미하는 것으로 이해한다. 선형 폴리에틸렌 물질은 50중량% 이하의 하나 이상의 중합체 첨가제(예: 알켄-1 중합체, 특히 저압 폴리에틸렌 등) 또는, 일반적으로 혼입되는 저분자 첨가제(예: 산화방지제, UV 흡수제 및 염료 등)를 추가로 함유할 수 있다. 이러한 타입의 폴리에틸렌 물질은 표시 "연장된 쇄 폴리에틸렌(ECPE: extended chain polyethylene)"으로 공지되어 있다. 본 발명의 문맥 내에서, 폴리프로필렌은 분자량이 바람직하게는 백만보다 큰, 실질적으로 선형인 폴리프로필렌 물질인 것으로 이해한다.Within the description of the present invention, the term "polyolefin staple fiber" refers to staple fibers made by tearing or cutting polyolefin filament yarns, ie filament yarns whose filament-forming polymers are polyolefins, preferably polypropylene and particularly preferably polyethylene. Means. As a result, the polyolefin staple fibers of knitted fabric II of the present invention are preferably polypropylene staple fibers, particularly preferably polyethylene staple fibers. Thereby, in the context of the present invention, polyethylene is understood to be a substantially linear polyethylene material having a molecular weight, preferably greater than one million, which may comprise small amounts of chain branching or comonomers, where the small amount It is understood that for every 100 carbon atoms in the main chain, up to 5 chain branches or comonomers are present. The linear polyethylene material further contains up to 50% by weight of one or more polymer additives (e.g. alkene-1 polymers, in particular low pressure polyethylene, etc.) or generally incorporated low molecular weight additives (e.g. antioxidants, UV absorbers and dyes, etc.). can do. Polyethylene materials of this type are known as the indication "extended chain polyethylene" (ECPE). Within the context of the present invention, polypropylene is understood to be a substantially linear polypropylene material, preferably having a molecular weight greater than one million.
본 발명의 편직물 II의 스테이플 섬유 성분 A 중 폴리올레핀 스테이플 섬유의 길이는 바람직하게는 20 내지 180㎜의 범위, 특히 바람직하게는 30 내지 120㎜의 범위이며, 보다 특히 바람직하게는 30 내지 100㎜의 범위이다.The length of the polyolefin staple fibers in the staple fiber component A of the knitted fabric II of the present invention is preferably in the range of 20 to 180 mm, particularly preferably in the range of 30 to 120 mm, more particularly preferably in the range of 30 to 100 mm. to be.
본 발명의 편직물 II의 양태에서, 스테이플 섬유 성분 A는 아라미드 스테이플 섬유 및 폴리올레핀 스테이플 섬유를 포함하며, 여기서 상기 아라미드 스테이플 섬유:폴리올레핀 스테이플 섬유의 중량비는 95:5 내지 5:95의 범위, 특히 바람직하게는 80:20 내지 20:80의 범위이다.In an aspect of knitted fabric II of the present invention, staple fiber component A comprises aramid staple fibers and polyolefin staple fibers, wherein the weight ratio of aramid staple fibers: polyolefin staple fibers is in the range of 95: 5 to 5:95, particularly preferably Is in the range of 80:20 to 20:80.
본 발명의 편직물의 바람직한 양태로, 폴리올레핀 스테이플 섬유는 폴리에틸렌 스테이플 섬유이다.In a preferred embodiment of the knitted fabric of the present invention, the polyolefin staple fibers are polyethylene staple fibers.
본 발명의 편직물 II의 양태에서, 순수 스테이플 섬유 얀 RA의 선밀도는 바람직하게는 10 내지 1000tex의 범위, 특히 바람직하게는 12 내지 500tex의 범위이며, 보다 특히 바람직하게는 14 내지 100tex의 범위이다.In an embodiment of knitted fabric II of the present invention, the linear density of pure staple fiber yarn RA is preferably in the range of 10 to 1000 tex, particularly preferably in the range of 12 to 500 tex, more particularly preferably in the range of 14 to 100 tex.
또한, 본 발명의 편직물 II의 양태에서, 순수 스테이플 섬유 얀 RB의 선밀도는 바람직하게는 10 내지 1000tex의 범위, 특히 바람직하게는 12 내지 500tex의 범위이며, 보다 특히 바람직하게는 14 내지 100tex의 범위이다.Further, in the aspect of knitted fabric II of the present invention, the linear density of pure staple fiber yarn RB is preferably in the range of 10 to 1000 tex, particularly preferably in the range of 12 to 500 tex, and more particularly preferably in the range of 14 to 100 tex. .
또한, 본 발명의 편직물 II의 양태에서, 순수 스테이플 섬유 얀 RA 중 바람직하게는 2 내지 10개 및 특히 바람직하게는 2 내지 8개가 가연되어 연사 ZA를 형성한다.In addition, in the embodiment of knitted fabric II of the present invention, preferably 2 to 10 and particularly preferably 2 to 8 of the pure staple fiber yarn RA are twisted to form twisted yarn ZA.
또한, 본 발명의 편직물 II의 양태에서, 순수 스테이플 섬유 얀 RB 중 바람직하게는 2 내지 10개 및 특히 바람직하게는 2 내지 8개가 가연되어 연사 ZB를 형성한다. In addition, in the aspect of knitted fabric II of the present invention, preferably 2 to 10 and particularly preferably 2 to 8 of pure staple fiber yarn RB are twisted to form twisted yarn ZB.
또한, 한 양태로, 본 발명의 편직물 II는 바람직하게는 연사 ZA 중 1 내지 8개와 바람직하게는 연사 ZB 중 1 내지 8개가 플레이팅되어 제조되며, 이때 편직물 II는 연사 ZA 중 1 내지 6개와 바람직하게는 연사 ZB 중 1 내지 6개가 플레이팅되어 제조되는 것이 특히 바람직하다.Further, in one aspect, knitted fabric II of the present invention is preferably prepared by plating one to eight of the twisted yarn ZA and preferably one to eight of the twisted yarn ZB, wherein knitted fabric II is preferably one to six of the twisted yarn ZA. It is particularly preferred that 1 to 6 of the twisted yarn ZB are plated and made.
추가의 바람직한 양태로, 본 발명의 편직물 II는 니들 게이지 gg로 편직하며, 이때 gg는 바람직하게는 5 내지 18의 범위 및 특히 바람직하게는 7 내지 15의 범위이다.In a further preferred embodiment, knitted fabric II of the present invention is knitted with a needle gauge gg, wherein gg is preferably in the range of 5 to 18 and particularly preferably in the range of 7 to 15.
추가의 바람직한 양태로, 본 발명의 편직물 II는 코스의 메시 밀도, MiR로 편직하며, 이때 MiR는 바람직하게는 2 내지 15의 범위 및 특히 바람직하게는 3 내지 12의 범위에 놓인다.In a further preferred embodiment, knitted fabric II of the present invention is knitted with the mesh density of the course, MiR, wherein the MiR is preferably in the range from 2 to 15 and particularly preferably in the range from 3 to 12.
다른 바람직한 양태로, 본 발명의 편직물 II는 웨일즈의 메시 밀도, MiS로 편직하며, 이때 MiS는 바람직하게는 2 내지 15의 범위 및 특히 바람직하게는 3 내지 12의 범위에 놓인다.In another preferred embodiment, knitted fabric II of the present invention is knitted to the mesh density of Wales, MiS, wherein the MiS is preferably in the range of 2 to 15 and particularly preferably in the range of 3 to 12.
본 발명의 편직물 II에서 순수 스테이플 섬유 얀 RA를 순수 필라멘트 얀 RA'로 대체하는 것으로 변화시키는 경우, 마찬가지로 내절단성, 내마모성 및 착용 쾌적성의 매력적인 조합을 갖는, 플레이팅에 의해 제조되는 다른 동일한 구조의 편직물 II가 생성된다.In the case of changing the pure staple fiber yarn RA to replacing the pure filament yarn RA 'in knitted fabric II of the present invention, it is likewise of another identical structure made by plating, which has an attractive combination of cut resistance, wear resistance and wear comfort. Knit fabric II is produced.
본 발명의 편직물 II에서 내절단성 및 착용 쾌적성의 유용한 조합이 모든 타입의 옷에서 주목할 만하며, 이때 본 발명의 편직물 II는 신체에 대해 착용된다. 바람직하게는, 본 발명의 편직물 II는 글로브, 보호 슬리브, 후드 또는 셔츠로서 형성되는 의류 제품이다.A useful combination of cut resistance and wear comfort in knitted fabrics II of the present invention is noteworthy in all types of clothes, where knitted fabrics II of the present invention are worn against the body. Preferably, knitted fabric II of the present invention is an article of clothing formed as a glove, protective sleeve, hood or shirt.
본 발명은 하기의 실시예를 사용하여 보다 상세히 기술될 것이다.
The invention will be described in more detail using the following examples.
실시예 1Example 1
폴리-p-페닐렌 테레프탈아미드(Twaron 1070; 제조원: Teijin Aramid GmbH)로 제조된 40㎜ 길이의 스테이플 섬유가 스테이플 섬유 성분 A로서 사용된다. 대략 15㎜의 섬유 길이로부터 대략 40㎜의 섬유 길이로 연장된 길이 분포를 갖는 케이폭 섬유가 스테이플 섬유 성분 B로서 사용된다. 90중량%의 성분 A 및 10중량%의 성분 B로부터 균질한 스테이플 섬유 혼합물을 제조한다. 균질한 스테이플 섬유 혼합물로부터 선밀도가 Nm 28, 즉 36tex인 혼방 스테이플 섬유 얀 AB를 제조한다. 이들 혼방 스테이플 섬유 얀 AB 중 2개를 가연시켜 연사 ZAB를 형성한다. 이들 연사 ZAB 중 4개를 편직기로 평행하게 공급하고, 7gg의 니들 게이지, 3.5의 코스 메시 밀도, MiR 및 3.5의 웨일즈 메시 밀도 MiS로 글로브로 편직한다.A 40 mm long staple fiber made of poly-p-phenylene terephthalamide (Twaron 1070; Teijin Aramid GmbH) is used as staple fiber component A. A kapok fiber having a length distribution extending from a fiber length of approximately 15 mm to a fiber length of approximately 40 mm is used as staple fiber component B. A homogeneous staple fiber mixture is prepared from 90% by weight of component A and 10% by weight of component B. Blended staple fiber yarns AB having a linear density of Nm 28, ie 36 tex, are prepared from a homogeneous staple fiber mixture. Two of these blended staple fiber yarns AB are twisted to form twisted yarn ZAB. Four of these yarn ZABs are fed in parallel with a knitting machine and knitted into a glove with a needle gauge of 7gg, a coarse mesh density of 3.5, MiR and a Wales mesh density MiS of 3.5.
본 발명의 3개의 글로브 1a, 1b 및 1c를 이 방법으로 편직한다. 내절단성 N은 ISO 13997(August 1999)에 따라 본 발명의 글로브 1a, 1b 및 1c에 대해 측정한다.
Three gloves 1a, 1b and 1c of the present invention are knitted in this manner. Cut resistance N is measured for the globes 1a, 1b and 1c of the present invention according to ISO 13997 (August 1999).
실시예 2Example 2
폴리-p-페닐렌 테레프탈아미드(Twaron 1070; 제조원: Teijin Aramid GmbH)로 제조된 40㎜ 길이의 스테이플 섬유가 스테이플 섬유 성분 A로서 사용된다. 대략 15㎜의 섬유 길이로부터 대략 40㎜의 섬유 길이로 연장된 길이 분포를 갖는 케이폭 섬유가 스테이플 섬유 성분 B로서 사용된다. 90중량%의 성분 A 및 10중량%의 성분 B로부터 균질한 스테이플 섬유 혼합물을 제조한다. 균질한 스테이플 섬유 혼합물로부터 선밀도가 Nm 28, 즉 36tex인 혼방 스테이플 섬유 얀 AB를 제조한다. 이들 혼방 스테이플 섬유 얀 AB 중 2개를 가연시켜 연사 ZAB를 형성한다. 이들 연사 ZAB 중 1개를 편직기로 공급하고, 13gg의 니들 게이지, 6.0의 코스 메시 밀도, MiR 및 7.5의 웨일즈 메시 밀도 MiS로 글로브로 편직한다.A 40 mm long staple fiber made of poly-p-phenylene terephthalamide (Twaron 1070; Teijin Aramid GmbH) is used as staple fiber component A. A kapok fiber having a length distribution extending from a fiber length of approximately 15 mm to a fiber length of approximately 40 mm is used as staple fiber component B. A homogeneous staple fiber mixture is prepared from 90% by weight of component A and 10% by weight of component B. Blended staple fiber yarns AB having a linear density of Nm 28, ie 36 tex, are prepared from a homogeneous staple fiber mixture. Two of these blended staple fiber yarns AB are twisted to form twisted yarn ZAB. One of these twisted yarn ZABs is fed to a knitting machine and knitted into a glove with a needle gauge of 13 gg, a coarse mesh density of 6.0, a MiR and a Wales mesh density MiS of 7.5.
본 발명의 3개의 글로브 2a, 2b 및 2c를 이 방법으로 편직한다. 내절단성 N은 ISO 13997(August 1999)에 따라 본 발명의 글로브 2a, 2b 및 2c에 대해 측정한다.
Three gloves 2a, 2b and 2c of the present invention are knitted in this manner. Cut resistance N is measured for the globes 2a, 2b and 2c of the present invention according to ISO 13997 (August 1999).
비교 실시예 1Comparative Example 1
단지 스테이플 섬유 성분 A, 즉 폴리-p-페닐렌 테레프탈아미드(Twaron 1070; 제조원: Teijin Aramid GmbH)로 제조된 40㎜ 길이의 스테이플 섬유만을 사용한다. 100중량%의 성분 A로부터 선밀도가 Nm 28, 즉 36tex인 스테이플 섬유 얀을 제조한다. 이들 스테이플 섬유 얀 중 2개를 가연시켜 연사를 형성한다. 이들 연사 중 4개를 편직기로 평행하게 공급하고, 7gg의 니들 게이지, 3.5의 코스 메시 밀도, MiR 및 3.5의 웨일즈 메시 밀도 MiS로 글로브로 편직한다.Only staple fiber component A is used, i.e. 40 mm long staple fibers made of poly-p-phenylene terephthalamide (Twaron 1070; Teijin Aramid GmbH). Staple fiber yarns having a linear density of Nm 28, ie 36 tex, are prepared from 100% by weight of component A. Two of these staple fiber yarns are twisted to form twisted yarns. Four of these yarns are fed in parallel to a knitting machine and knitted into a glove with a needle gauge of 7 gg, cos mesh density of 3.5, MiR and Wales mesh density MiS of 3.5.
3개의 비교용 글로브 V1a, V1b 및 V1c를 이 방법으로 편직한다. 내절단성 N은 ISO 13997(August 1999)에 따라 비교용 글로브 V1a, V1b 및 V1c에 대해 측정한다.
Three comparative gloves V1a, V1b and V1c are knitted in this manner. Cut resistance N is measured for comparative gloves V1a, V1b and V1c according to ISO 13997 (August 1999).
비교 실시예 2Comparative Example 2
단지 스테이플 섬유 성분 A, 즉 폴리-p-페닐렌 테레프탈아미드(Twaron 1070; 제조원: Teijin Aramid GmbH)로 제조된 40㎜ 길이의 스테이플 섬유만을 사용한다. 100중량%의 성분 A로부터 선밀도가 Nm 28, 즉 36tex인 스테이플 섬유 얀을 제조한다. 이들 스테이플 섬유 얀 중 2개를 가연시켜 연사를 형성한다. 이 연사를 편직기로 공급하고, 13gg의 니들 게이지, 6.0의 코스 메시 밀도, MiR 및 8.0의 웨일즈 메시 밀도 MiS로 글로브로 편직한다.Only staple fiber component A is used, i.e. 40 mm long staple fibers made of poly-p-phenylene terephthalamide (Twaron 1070; Teijin Aramid GmbH). Staple fiber yarns having a linear density of Nm 28, ie 36 tex, are prepared from 100% by weight of component A. Two of these staple fiber yarns are twisted to form twisted yarns. This yarn is fed to a knitting machine and knitted into a glove with a needle gauge of 13 gg, coarse mesh density of 6.0, MiR and Wales mesh density MiS of 8.0.
3개의 비교용 글로브 V2a, V2b 및 V2c를 이 방법으로 편직한다. 내절단성 N은 ISO 13997(August 1999)에 따라 비교용 글로브 V2a, V2b 및 V2c에 대해 측정한다.Three comparative gloves V2a, V2b and V2c are knitted in this manner. Cut resistance N is measured for comparative gloves V2a, V2b and V2c according to ISO 13997 (August 1999).
결과가 표 1에 요약되어 있다.The results are summarized in Table 1.
본 발명의 글로브 1a 내지 1c와 비교용 글로브 V1a 내지 V1c의 비교는 본 발명의 글로브가 10중량%의 케이폭 섬유의 비에도 불구하고, 비교용 글로브 V1a 내지 V1c의 것과 동일한 단위 면적당 질량, 동일하게 양호한 내절단성 N을 가짐을 나타낸다.Comparison of the gloves 1a to 1c of the present invention and the comparative gloves V1a to V1c shows that the glove of the present invention has the same mass per unit area as that of the comparative gloves V1a to V1c, equally good, despite the ratio of 10% by weight of kapok fibers. It has a cut resistance N.
본 발명의 글로브 2a 내지 2c와 비교용 글로브 V2a 내지 V2c의 비교는 본 발명의 글로브가 10중량%의 케이폭 섬유의 비에도 불구하고, 그리고 단위 면적당 다소 작은 질량에도 불구하고, 비교용 글로브 V2a 내지 V2c의 것보다 실제로 다소 양호한 내절단성 N을 가짐을 나타낸다.Comparison of the gloves 2a to 2c of the present invention with the comparative gloves V2a to V2c shows that the gloves of the present invention are used for the comparative gloves V2a to V2c, despite the ratio of 10% by weight of kapok fibers and somewhat smaller mass per unit area. Actually has a rather good cut resistance N than.
다른 본 발명의 글로브 1d는 글로브 1a 내지 1c와 동일한 조건을 사용하여 제조한다. DIN EN 31 092(February 1994) 또는 ISO 11092(15 October 1993)에 따라, 수증기 유동 저항 Ret를 본 발명의 글로브 1d에 대해 측정한다. 인용된 표준에 따라, Ret는 수증기 부분압 구배를 따라 생성되는 단위 면적당 증발열 유동으로 나눈, 글로브의 두 표면 사이, 즉 글로브의 내면 및 외면 사이의 수증기 부분압 차를 의미한다.Another glove 1d of the present invention is produced using the same conditions as the gloves 1a to 1c. According to DIN EN 31 092 (February 1994) or ISO 11092 (15 October 1993), the water vapor flow resistance R et is measured for the glove 1d of the present invention. According to the cited standard, R et means the steam partial pressure difference between two surfaces of the glove, ie between the inner and outer surfaces of the glove, divided by the evaporative heat flow per unit area produced along the steam partial pressure gradient.
추가의 비교용 글로브 V1d는 비교용 글로브 V1a 내지 V1c와 동일한 조건을 사용하여 제조한다. DIN EN 31 092(February 1994) 또는 ISO 11092(15 October 1993)에 따라, 수증기 유동 저항 Ret를 비교용 글로브 V1d에 대해 측정한다. Further comparative gloves V1d are prepared using the same conditions as comparative gloves V1a to V1c. In accordance with DIN EN 31 092 (February 1994) or ISO 11092 (15 October 1993), the water vapor flow resistance R et is measured against a comparative globe V1d.
Ret 측정 결과는 표 2에 제시되어 있다.R et measurement results are shown in Table 2.
본 발명의 글로브 1d와 비교용 글로브 V1d의 비교는 본 발명의 글로브 1d의 수증기 유동 저항 Ret이 비교용 글로브 V1d의 수증기 유동 저항 Ret의 것보다 21% 낮은 것으로 나타났다. 그 결과, 본 발명의 글로브 1d의 통기성이 비교용 글로브 V1d의 통기성보다 26% 더 크다.Comparison of the glove 1d and Comparative V1d glove of the present invention showed 21% lower than that of the water vapor resistance R et flow of the glove V1d for vapor flow resistance R et a comparison of the glove 1d of the present invention. As a result, the breathability of the glove 1d of the present invention is 26% greater than that of the comparative glove V1d.
따라서, 적절한 육체적 활동을 시뮬레이팅한 DIN EN 31 092(February 1994) 또는 ISO 11092(15 October 1993)의 조건하에, 본 발명의 글로브 1d는 동일한 내절단성에서 비교용 글로브 V1d보다 더 큰 착용 쾌적성을 나타낸다.Thus, under the conditions of DIN EN 31 092 (February 1994) or ISO 11092 (15 October 1993), which simulates proper physical activity, the glove 1d of the present invention has greater wear comfort than the comparative glove V1d at the same cut resistance. Indicates.
착용자의 육체적 활동 없이 착용 시험에서, 본 발명의 글로브 1d는 또한 비교용 글로브 V1d의 착용 쾌적성보다 더 쾌적한 것으로 착용자가 기술한 착용 쾌적성을 나타낸다.
In the wear test without the physical activity of the wearer, the glove 1d of the present invention also exhibits the wear comfort described by the wearer as being more comfortable than the wearing comfort of the comparative glove V1d.
Claims (18)
- 아라미드 스테이플 섬유를 포함하는 스테이플 섬유 성분 A 및
- 적어도 한가지 타입의 종자 섬유(seed fiber) 또는 조류(algae)가 풍부한 라이오셀(lyocell) 섬유를 인열 또는 절단시켜 제조된 스테이플 섬유, 또는 적어도 한가지 타입의 종자 섬유와 조류가 풍부한 라이오셀 섬유를 인열 또는 절단시켜 제조된 스테이플 섬유와의 혼합물을 포함하는 스테이플 섬유 성분 B로 제조되고,
여기서, 상기 A 및 B는 A와 B의 균질 혼합물로부터 제조되는 혼방 스테이플 섬유 얀(mixed staple fiber yarn) AB를 형성하며, 상기 혼방 스테이플 섬유 얀 AB 중 적어도 2개가 가연되어 연사(twisted thread) ZAB를 형성하고, 상기 연사 ZAB 중 적어도 1개가 편직물 I로 가공된, 편직물 I.As knitted fabric I, which
Staple fiber component A comprising aramid staple fibers and
Tearing staple fibers made by tearing or cutting at least one type of seed fiber or algae-rich lyocell fiber, or tearing at least one type of seed fiber and algae-rich lyocell fiber Or staple fiber component B comprising a mixture with staple fibers prepared by cutting,
Wherein A and B form a mixed staple fiber yarn AB made from a homogeneous mixture of A and B, wherein at least two of the blended staple fiber yarns AB are combustible to form twisted thread ZAB Knitted fabric I, wherein at least one of the twisted yarns ZAB has been processed into knitted fabric I.
- 아라미드 스테이플 섬유 및/또는 폴리올레핀 스테이플 섬유를 포함하는 스테이플 섬유 성분 A 및
- 적어도 한가지 타입의 종자 섬유 또는 조류가 풍부한 라이오셀 섬유를 인열 또는 절단시켜 제조된 스테이플, 또는 적어도 한가지 타입의 종자 섬유와 조류가 풍부한 라이오셀 섬유를 인열 또는 절단시켜 제조된 스테이플 섬유와의 혼합물을 포함하는 스테이플 섬유 성분 B로 제조되고,
여기서, 상기 A는 오로지 A로부터 제조되는 순수 스테이플 섬유 얀 RA를 형성하고, B는 오로지 B로부터 제조되는 순수 스테이플 섬유 얀 RB를 형성하며, 상기 순수 스테이플 섬유 얀 RA 중 적어도 2개가 가연되어 연사 ZA를 형성하고, 상기 순수 스테이플 섬유 얀 RB 중 적어도 2개가 가연되어 연사 ZB를 형성하며, 상기 편직물 II는 상기 연사 ZA 중 적어도 1개와 상기 연사 ZB 중 적어도 1개가 플레이팅(plaiting)되어 제조된, 편직물 II.As knit II, which
Staple fiber component A comprising aramid staple fibers and / or polyolefin staple fibers and
Staples made by tearing or cutting at least one type of seed fiber or algae-rich lyocell fiber, or a mixture of at least one type of seed fiber and staple fiber made by tearing or cutting algae-rich lyocell fiber; It is made of a staple fiber component B comprising,
Wherein A forms pure staple fiber yarns RA produced solely from A, B forms pure staple fiber yarns RB manufactured solely from B, and at least two of the pure staple fiber yarns RA are combustible to form twisted yarn ZA Forming, wherein at least two of the pure staple fiber yarns RB are combusted to form twisted yarn ZB, and the knit fabric II is fabricated by fabricating at least one of the twisted yarn ZA and at least one of the twisted yarn ZB plated. .
16. Knitted fabric II according to any one of the preceding claims, characterized in that it is an article of clothing formed as a glove, protective sleeve, hood or shirt.