KR20110024083A - Execution method for coating in a bathroom - Google Patents

Abstract

PURPOSE: A construction method for the coating process of a bathroom is provided to obtain a smooth surface by implementing a fine surface processing operation. CONSTITUTION: The surface of tiles is ground. A putty operation is implemented to the surface of the tiles. The surface of the tiles is cleaned. Damaged parts of the surface are filled using putty. Special epoxy paint is coated on the cleaned surface of the tiles. The surface of the tile is processed with sandpaper. The epoxy paint or urethane paint is coated on the surface of the tiles. An antibiotic silicon caulking operation is implemented.

Description

Coating method inside the bathroom {Execution method for coating in a bathroom}

The present invention relates to a bathroom coating method, and more particularly, to a bathroom coating method to have a stable and high strength through the coating process several times in the bathroom wall tiles, bathtub, wash basin, toilet bowl and the like.

Bathroom coating is the most economical method of bathroom construction that is more advanced than bathroom reform. It is a method that transforms existing bathroom into a different bathroom in a short time, and color is changed from "color coating" to the addition of pearl so that various colors can be formed. These can be categorized as much softer "pearl coatings" or "screen coatings" that make the most of their points with deco-transfers.

Therefore, the coating of wall tiles, bathtubs, toilets or washbasins in the bathroom (hereinafter referred to as 'tiles') can be done by color-coating an old or unfavorable color, moldy bathtub with a color-coated bath. It is possible with the bathroom remodeling construction method to make.

The present invention relates to a construction method for coating a wall tile, a bath, a toilet or a wash basin (hereinafter referred to as a 'tile') in a bathroom, and the conventional washroom equipment or a bathtub is replaced when it is contaminated with water moss, scale, etc. due to aging of the surface. In the case of treatment with the conventional coating method, there is a problem that the physical properties such as waterproofness, surface strength, gloss, etc. do not match, or the process is complicated and the construction time is long.

Korean Patent Registration No. 144210 (April 16, 1998) has registered the contents of a non-slip sheet for bathroom floors, in which a mineral crushed product is added to the polyurethane binder as an aggregate and printed with a disperse dye.

U.S. Patent No. 4,195,010 (1980.5.25) describes coating compositions, such as ethylenically unsaturated polyesters, sand, quartz, etc. that coat the decorative surfaces of bricks or tiles.

In addition, U.S. Patent No. 3,673,148 (1972.6.27) describes a coating composition composed of an acrylic graft copolymer, polyester, and the like with a glass fiber reinforcement agent.

In the above-described document, treatment conditions do not match with direct construction in buildings such as general homes, bathrooms, buildings, etc. according to the present invention with high temperature treatment, energy irradiation treatment (ultraviolet ray, etc.) or high pressure treatment during curing.

In addition, there is a problem that is inappropriate to be dedicated to the construction of various colors, coloring according to the various coloring, consumer needs and tastes according to the present invention.

The present invention has been made to solve the above problems, such as the problem of excessively complicated construction costs such as the increase in the size of the existing coating, the input of expensive equipment and the demand of professional personnel and the provision of high-quality construction properties It is an object of the present invention to provide a coating treatment method in an interior of a bathroom for improved characteristics not achieved.

The present invention relates to a coating treatment construction method inside a bathroom, and more particularly, in a construction method of coating a wall tile, a bath, a toilet, or a sink (hereinafter, referred to as a 'tile') in a bathroom, a tile using a sander Polishing the surface, tile surface putty work for smoothing nail marks or cracks on the polished tile surface, replacing the damaged tiles with tiles of the same size, diatomaceous earth, super cleansing agent ( PB-1), the step of cleaning the tile surface by mixing water, the step of filling the incontinence or damaged portion of the joint between the tile and the tile with the cleaning polished tile using a putty, and specially Performing the primary coating by the cross-spray method using an epoxy paint, and drying at room temperature for 8 hours, sanding the surface of the primary coated tile using sandpaper. Steps to perform secondary coating by cross-spray method using special epoxy paint or urethane paint on sandpaper finished tiles, and pearl powder on high quality transparent urethane paint on the second coated tile surface Performing a third coating by mixing, performing a fourth coating in a cross-spray method using urethane paint on the third coated tile surface, and using a hot air dryer after the fourth coating with hot air at 80 ° C. After drying for 30 minutes, the step of performing a caulking operation on the tile is completed using antibacterial silicone is characterized in that it is performed sequentially.

As described above, the present invention enables the construction of various colors and colors according to various colorings, consumer demands and tastes, and enables the coating to be smooth and finished with high-precision surface processing, and the processing time is simple and construction time. This will shorten the effect.

With reference to the accompanying drawings, the coating treatment construction method inside the bathroom of the present invention to achieve the above objects and effects to be described in more detail with reference to the accompanying drawings.

1 is a schematic block diagram of a construction method according to the present invention, and relates to a coating method applied to a wall tile, a bath, a toilet, or a sink (hereinafter, referred to as a tile) in a bathroom. The description is as follows.

First step: polishing the tile surface using a sander.

The reason for using the sander is that by using an orbital sander for general woodworking, compared to a sanding disc made of a flap disc made of a conventional industrial scrubber with a 4 inch hand grinder spin wheel, a more dense surface can be obtained.

Step 2: A tile surface putty working step is performed to smooth the nail marks or cracks on the polished tile surface.

Putty work is a kind of crack filling work, which is a paste-like binder made by putting putty, calcium carbonate powder, stone powder, zinc oxide, etc., into a colorant such as oil, oiliness varnish, and lacquer. Putty, usually made of oily varnish or lacquer, is used to smooth the conjunctiva or base surface of the wood prior to painting.

In performing the putty work step, it is preferable to replace the tiles with the same size because the tiles with severe breakage may be difficult or inefficient.

The replacement method is to cut the joint of the tile with a 4 inch hand grinder, and then remove the damaged tile using a hammer or chisel.

Then, after applying a repair adhesive to the cement mass inside the removed tiles, the same size tiles are attached, and the cut joints are filled with poly putty.

Third step: Perform a work step of cleaning the tile surface by mixing diatomaceous earth, PB-1 (super cleaner) and water.

As the main component of PB-1, in order to increase the cleaning effect, it is preferable to use natural fatty acid, bio-based surfactant, proteolytic agent, orange oil, dispersant and the like.

Fourth step: performing a step of filling the joint between the cleaning polished tile and the tile with a putty by using a putty.

Step 5: A cross spraying primary coating step is performed using a special epoxy paint on the cleaned tiles.

The special epoxy paint used in the above five steps of the present invention is different from a general epoxy paint or a conventional special epoxy paint, and a two-component tile repair paint mainly containing a special epoxy resin and a hardener is used.

In addition, the literature meaning of the cross-spray method described in the present invention is redefined to mean a method of spraying and coating the surface of the coating target in the horizontal and vertical directions using an airless spray.

In addition, the cross-spray method is characterized in that it comprises a step of spraying and coating the paint over the entire object in the transverse direction, and the process of spraying and coating the paint more densely than in the transverse direction in the longitudinal direction.

Step 6: After drying for 8 hours at room temperature, performing a sanding operation using sandpaper on the surface of the first coated tile.

Drying at room temperature for 8 hours may include the purpose of solving the problem of peeling or discoloration occurring at a short time of drying at high temperature, and enhancing affinity with the bottom surface.

Step 7: The second coating is performed by cross-spraying using a special epoxy paint or urethane paint on the sandpaper finished tiles.

By performing the secondary coating through the cross injection method, it is possible to increase the durability of the coating film, each step of performing the cross injection method is preferably made of a coating operation over several or several times.

Eighth step: The third coating is performed by mixing pearl powder with high quality transparent urethane paint on the second coated tile surface.

The high-quality transparent urethane paint used in the eighth step is a two-component acrylic urethane transparent paint, which has a higher solid content than the general transparent urethane paint used in the conventional coating, which is excellent in workability, reinforces scratch resistance and chemical resistance, It has a paint characteristic that shortens the drying time by using a fast drying type curing agent.

9th step: The 4th coating step is performed by the cross spraying method using the urethane paint on the 3rd coated tile surface.

Step 10: After the fourth coating and dried for 30 minutes by hot air dryer at 80 ℃ using a hot air dryer, performing a caulking operation on the coated tile using the antimicrobial silicone to inhibit mold.

The caulking operation is to fill a small gap created by seams or cracks of each material and to compress them in a watertight and airtight manner, and has a wide elastic range, flexibility, and adhesion. It is preferable to use this rich material.

1 is a schematic block diagram showing the concept of a coating treatment construction method according to the present invention.

Claims (6)

A method of coating a wall tile, a bath, a toilet or a wash basin (hereinafter referred to as a 'tile') in a bathroom; Polishing the tile surface using a sander; A tile surface putty working step for smoothing nail marks or cracks on the polished tile surface; Replacing the badly damaged tiles with tiles of the same size; Cleaning the tile surface by mixing diatomaceous earth, super strong detergent (PB-1) and water; Filling the joint between the cleaned and polished tile with a tile by using a putty; Performing a primary coating in a cross spray method using a special epoxy paint on the cleaned tile; After drying for 8 hours at room temperature, performing a sanding operation using sandpaper on the surface of the first coated tile; Performing a secondary coating in a cross-spray method using a special epoxy paint or urethane paint on the sanding finished tiles; Performing a tertiary coating by mixing pearl (pearl) powder with a high quality transparent urethane paint on the secondary coated tile surface; Performing a fourth coating in a cross spraying manner using a urethane paint on the third coated tile surface; After the fourth coating and dried for 30 minutes in hot air of 80 ℃ using a hot air dryer, performing a coking operation on the tile is completed using antibacterial silicone; Coating treatment construction method inside the bathroom comprising a. The method according to claim 1; The tile replacement step, Cutting the joint of the tile with a 4 inch hand grinder and removing the damaged tile using a hammer and a chisel; Applying a repair adhesive to the cement mass inside the removed tile and then attaching tiles of the same size; Filling the cut joints with a polymorphism; Coating treatment construction method inside the bathroom, characterized in that consisting of. The method according to claim 1; The super strong detergent (PB-1), Method of coating treatment inside the bathroom, characterized in that consisting of natural fatty acids, biosurfactants, proteolytic agents, orange oil, dispersant. The method according to claim 1; The special epoxy coating is a coating treatment construction method in the bathroom, characterized in that for use as a two-component tile repair paint mainly composed of a special epoxy resin and a curing agent. The method according to claim 1; The cross-spray method is a method of spraying, coating in the horizontal, vertical direction on the surface of the coating object using an airless spray, Spraying and coating the paint horizontally on the entire object; Spraying and coating the paint more densely than in the transverse direction; Coating treatment construction method inside the bathroom, characterized in that consisting of. The method according to claim 1; The high-quality transparent urethane paint has a higher solid content than a general transparent urethane paint, which is excellent in workability, reinforces scratch resistance and chemical resistance, and uses a two-component acrylic urethane transparent paint to shorten the drying time by using a fast-drying curing agent. Coating treatment construction method in the bathroom, characterized in that used.