CN1331967C - Granite imitating paint and its prepn process and imitation granite making process - Google Patents
Granite imitating paint and its prepn process and imitation granite making process Download PDFInfo
- Publication number
- CN1331967C CN1331967C CNB2005100572726A CN200510057272A CN1331967C CN 1331967 C CN1331967 C CN 1331967C CN B2005100572726 A CNB2005100572726 A CN B2005100572726A CN 200510057272 A CN200510057272 A CN 200510057272A CN 1331967 C CN1331967 C CN 1331967C
- Authority
- CN
- China
- Prior art keywords
- granite
- pending
- paint
- treated side
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention discloses granite simulated paint for building decoration, a method for preparing the paint and a method for utilizing the paint to manufacture simulated granite. The granite simulated paint is mainly composed of 35 to 40 weight shares of white cement, 10 to 15 weight shares of marble powder, 15 to 20 weight shares of adhesives and 5 to 7 weight shares of acrylic acid emulsion. After the constituents are mixed and stirred uniformly in proportion, the adhesives and the acrylic acid emulsion are added to be uniformly stirred to obtain the paint. Simulated granite obtained by spraying the paint to a surface to be treated has the advantages of hardness, compactness, uniform whole body and smooth hand feeling which is similar to that of natural granite (marble), and the cost of simulated granite is one third to a quarter of that of natural granite. Besides, the service life is long, and the outdoor life of minimum durability can reach more than fifteen years, and the simulated granite is widely suitable for the decoration of walls and ground surfaces in building industry and decorative industry and the renewing treatment of old wall surfaces.
Description
Technical field
The present invention relates to a kind of architectural decoration granite-simulating paint, also relate to the preparation method of this granite-simulating paint, and the method for making artificial grantie with this granite-simulating paint.
Background technology
In the prior art, the inner, external wall of buildings and ground are decorated when handling, usually adopted: the first, at wall, ground daub; The second, at wall, ground tiling or granite (marble).Inner, external wall and ground daub at buildings belong to the simplest processing, and time one is long, and the coating of smearing can variable color, ftracture, come off, and also cannot stand for a long time at the exterior wall daub and to expose to the sun and rain; At wall, ground tiling or granite (marble),, can increase following shortcoming: not corrosion-resistant, easily aging though can remedy the deficiency of daub to a certain extent, there is aberration, easy to change, intensity is low, easy to crack, broken, poor adhesion, easily peels off, and assortment are single; When adopting natural granite (marble) when decorating, also there is the big phenomenon of radiation, therefore, injury to human body is big, and along with the variation of climate, the buck phenomenon also can appear oozing in the seam crossing between natural granite (marble), add its difficulty of construction big, cost an arm and a leg, the cost height, therefore limited the use of natural granite (marble).
Summary of the invention
The object of the present invention is to provide and a kind ofly be used for wall and the intensity height of processing, the granite-simulating paint that adhesivity is good, corrosion-resistant, radiationless are decorated in ground.
Another object of the present invention is to provide the preparation method of above-mentioned granite-simulating paint.
A further object of the present invention is to provide the method that adopts above-mentioned coating to make artificial grantie.
The object of the present invention is achieved like this: a kind of granite-simulating paint is characterized in that: mainly be made up of white cement 35-40 part, marble flour 10-15 part, binding agent 15-20 part, ACRYLIC EMULSION 5-7 part, in parts by weight.
Also have whitening powder in the above-mentioned granite-simulating paint or/and chemical paste or/and toning agent, its amount is: whitening powder 0-45 part, chemical paste 0-10 part, toning agent 0-30 part, in parts by weight.
Above-mentioned marble flour is the white jade stone flour; Described binding agent is 107 glue or 108 glue; Described whitening powder is titanium dioxide or dry powder.
Another object of the present invention is achieved in that a kind of preparation method of granite-simulating paint, it is characterized in that: after according to the above ratio white cement and marble flour being mixed, stir, add binding agent again, ACRYLIC EMULSION stirs and promptly gets coating.
For reaching better effect, after the present invention earlier mixes white cement, marble flour, stir according to the above ratio, add binding agent, ACRYLIC EMULSION, whitening powder more according to the above ratio or/and chemical paste or/and toning agent stir coating.
A further object of the present invention is achieved in that a kind of method that adopts above-mentioned coating to make artificial grantie, and it is characterized in that: it is that prepared coating is sprayed onto the artificial grantie that obtains in pending.
Treat earlier specifically that treated side cleans, smooth processing; Then described coating is sprayed onto in pending; When pending drying reaches 75%-80%, roughly grind, fine grinding; With the full batch processing face of cloud stone glue, add water behind pending the complete drying and carry out wet-milling, make treated side smooth, smooth; Further clean face is again at its surperficial sprayed surface resin paint; After pending the drying, carry out wet-milling once more, waxing polishing is carried out to treated side in the dry back of cleaning, gets final product with glass cement sealing side seam crack, circle then.
More particularly, it is undertaken by following step:
(1) cleaning, smooth pending: mark needed frame bar at pending face, mixed and back batch processing face 1-2 time of stirring makes treated side smooth, after pending face is dried slightly with white cement and 107 glue or 108 glue, on the frame bar that marks, stick adhesive tape, treated side is divided into bulk;
(2) spraying is or/and spray artificial grantie decorative pattern: described spraying is to spray water smoke moist curing face with water pistol to treated side earlier, after pending face is dried slightly, spray 1-7 all over the described granite-simulating paint of the white for preparing or the colored described granite-simulating paint of required pattern to treated side with dual nozzle spray gun; Or/and described spray artificial grantie decorative pattern: after pending the drying, transfer the nozzle bore of big dual nozzle spray gun, spray the multiple colored described granite-simulating paint of required pattern to treated side, make colored described granite-simulating paint form block coarse groove at treated side, after treating surface drying, with cylinder with block coarse groove embossing moulding;
(3) corase grind: when pending surperficial drying reaches 75%-80%, will be sprayed with earlier the treated side dry grinding, smooth of granite-simulating paint, and add water again and carry out wet-milling with sander with sander;
(4) fine grinding: the lip-deep aperture of treated side, slit are mended with corresponding granite-simulating paint flat, treat complete drying after, with waterproof abrasive paper with surface finish, smooth;
(5) with the full batch processing face of cloud stone glue, add water with sander behind pending the surperficial complete drying and carry out wet-milling, make treated side surfacing, smooth;
(6) coat with lacquer at its surperficial spray epoxy with dual nozzle spray gun on clean face surface;
(7) after pending drying, add water with sander and carry out wet-milling, the dry back of cleaning is carried out waxing polishing with polishing machine to treated side, then with getting final product behind the glass cement sealing frame bar slit.
Be with marble flour and white cement base-material in described granite-simulating paint as granite-simulating paint; The effect of binding agent is to make the mixed mutually back of marble flour and white cement good with the adhesion of handling metope or ground; The effect of ACRYLIC EMULSION is to use caking ability, hardness, intensity, the fastness to rubbing of the artificial grantie of granite-simulating paint spray to reach requirement, and can make surface finish smooth; The effect that adds chemical paste is to use the hardness of the artificial grantie of granite-simulating paint spray, the requirement that pliability more can reach polishing; The effect of whitening powder is to increase the whiteness of granite-simulating paint so that toning; Toning agent adopts commercially available iron oxide red powder, iron oxide yellow powder, iron black powder, the green powder of iron, barba hispanica powder and various mill base, and its effect is that the needed shades of colour of granite-simulating paint furnishing is used during with the artificial grantie of the various patterns of spray (decorative pattern).
Making with granite-simulating paint in the method for artificial grantie: the effect of used cloud stone glue is the hardness that increases artificial grantie, and plays the protective layer effect; The effect of the epoxy resin-based paint that is adopted is that the surperficial spray with artificial grantie becomes to have natural granite effects such as Gao Guang, half inferior light, inferior light.
Granite-simulating paint of the present invention, it is wide that it makes material source, preparation technology is simple and easy to do, can be made into the required versicolor granite-simulating paint of client, the artificial grantie that adopts the method for the invention to make, hard and compact, whole evenly, be smooth to the touch, exactly like natural granite (marble), and the following advantage of tool:
One, pattern is varied, can make the artificial grantie (marble) of various patterns, decorative pattern and its color and luster is all permanent lasting according to requirement of client;
Two, anti-aging, acid-alkali-corrosive-resisting, gasproof marquis change, soaking-resistant, the antifouling ability of keeping a public place clean is strong;
Three, wear-resisting, shock resistance, do not ftracture the intensity height;
Four, good with the adhesivity of handling body of wall or ground, do not peel off, come off;
Five, UV resistant, radiationless pollution;
Six, easily construction, cost are low, and its cost is 1/3rd to 1/4th of a natural granite; And its long service life, the outdoor quality guaranteed period can reach more than 15 years.
The method for preparing artificial grantie of the present invention, easy handling, be convenient to construction, be widely used in the inner, external wall of buildings and the decoration on ground, the extraneous adornment that also can be applicable to various ornamental buildingss such as multiple view, sculpture, Hua Tai, pond, garden column piece, abnormal member is handled.
The artificial grantie that spray is good is done tests such as water logging bubble, acid, caustic corrosion, heatproof, shock resistance, its result: water logging bubble artificial grantie is after 120 hours, and top coat has not had drum, cracking, peeling phenomenon, and surface color has only slight variation; With concentration is that 83% sodium hydroxide solution soaked artificial grantie after 120 hours, and top coat has not had drum, cracking, peeling phenomenon, and surface color has only slight variation; With concentration is that 98% sulphuric acid soln soaked artificial grantie after 120 hours, and top coat has not had drum, cracking, peeling phenomenon, and surface color has only slight variation; After 12 hours, top coat does not have efflorescence, cracking, peeling phenomenon with roasting lamp baking (temperature can reach 1200 ℃) artificial grantie surfaces of 2000 watts, and surface color has only slight variation; Behind water blast gun impact artificial grantie surface, top coat flawless, peeling phenomenon.
Embodiment
Embodiment 1: a kind of granite-simulating paint is characterized in that: mainly be made up of for 6 parts 35 parts of white cements, 15 parts of marble flours, 16 parts in 107 glue, ACRYLIC EMULSION, in parts by weight.
The white jade stone flour that above-mentioned marble flour adopts Nanyang City, Henan Province stone flour factory to produce,
Preparation method: after according to the above ratio white cement and white jade stone flour being mixed, stir, stir with 107 glue and ACRYLIC EMULSION again and promptly get coating.
Adopt the above-mentioned coating that makes, arbitrarily be sprayed onto pending metope, can obtain white artificial grantie metope.
Embodiment 2: a kind of granite-simulating paint is characterized in that: it is by 36 parts of white cements, 14 parts of white jade stone flours, 17 parts in 108 glue, 5 parts of ACRYLIC EMULSION, 45 parts of dry powders, in parts by weight.
The preparation method: earlier 36 parts of white cements, white jade stone flour are added in the stirred vessel for 14 parts, after stirring with stirrer, quantitatively add 17 parts in 108 glue, 5 parts of ACRYLIC EMULSION, 45 parts of dry powders again, with stirrer stir coating.
Adopt the treatment process of the above-mentioned coating that makes to metope: earlier to pending metope clean, smooth processing; Then described coating is sprayed onto in pending metope; When pending metope drying reaches 75%-80%, roughly grind, fine grinding; With the full batch processing metope of cloud stone glue, add water behind the pending metope complete drying and carry out wet-milling, make and handle wall surface levelling, smooth: further clean metope, again at its surperficial spray epoxy lacquer; After the pending metope drying, carry out wet-milling once more, waxing polishing is carried out to handling metope in the dry back of cleaning, gets final product with glass cement sealing side seam crack, circle then.
Embodiment 3: a kind of granite-simulating paint is characterized in that: it is made up of for 5 parts 37 parts of white cements, 13 parts of white jade stone flours, 18 parts in 107 glue, 7 parts of ACRYLIC EMULSION, chemical paste, in parts by weight.
The preparation method: earlier 37 parts of white cements, white jade stone flour are added in the stirred vessel for 13 parts, after stirring with stirrer, quantitatively add 18 parts in 107 glue, 7 parts of ACRYLIC EMULSION, 5 parts of chemical pastes again, with stirrer stir coating.
Adopt the treatment process of the above-mentioned coating that makes to metope: earlier to pending metope clean, smooth processing; Then described coating is sprayed onto in pending metope; When pending metope drying reaches 75%-80%, roughly grind, fine grinding; With the full batch processing metope of cloud stone glue, add water behind the pending metope complete drying and carry out wet-milling, make and handle wall surface levelling, smooth; Further the clean metope coats with lacquer at its surperficial spray epoxy again; After the pending metope drying, carry out wet-milling once more, waxing polishing is carried out to handling metope in the dry back of cleaning, gets final product with glass cement sealing side seam crack, circle then.
Embodiment 4: a kind of granite-simulating paint is characterized in that: it is made up of for 6 parts 38 parts of white cements, 12 parts of white jade stone flours, 19 parts in 108 glue, 5 parts of ACRYLIC EMULSION, 25 parts of titanium dioxides, chemical paste, in parts by weight.
Preparation method and using method are with embodiment 3, and different is that component and proportioning are different.
Embodiment 5: a kind of granite-simulating paint is characterized in that: it is made up of for 30 parts 39 parts of white cements, 11 parts of white jade stone flours, 20 parts in 107 glue, 7 parts of ACRYLIC EMULSION, 10 parts of titanium dioxides, 7 parts of chemical pastes, iron black powder, in parts by weight.
The preparation method is with embodiment 3, and different is selected component and proportioning difference.
Adopt the above-mentioned coating that makes to make the method for the artificial grantie of the black decorative pattern of white background:
(1) cleaning, smooth pending ground: mark needed frame bar on pending ground, mixed and the batch processing ground, back two times of stirring makes treated side smooth, after pending face is dried slightly with white cement and 107 glue, on the frame bar that marks, stick adhesive tape, treated side is divided into bulk;
(2) spraying and spray artificial grantie decorative pattern: described spraying is to spray the wetting ground of water smoke with water pistol to treated side earlier, after treating that ground is dried slightly, spray the described granite-simulating paint of the white for preparing by embodiment 1 for 5 times earthward with dual nozzle spray gun, after pending the drying, transfer the nozzle bore of big dual nozzle spray gun, spray the described granite-simulating paint of the black for preparing by present embodiment to treated side, make the described granite-simulating paint of black form block coarse groove at treated side, after treating surface drying, with cylinder with block coarse groove embossing moulding;
(3) corase grind: when pending surperficial drying reaches 75%-80%, will be sprayed with earlier the treated side dry grinding, smooth of granite-simulating paint, and add water again and carry out wet-milling with sander with sander;
(4) fine grinding: the aperture on the treated side, slit are mended with corresponding granite-simulating paint flat, treat complete drying after, with waterproof abrasive paper with surface finish, smooth;
(5) with the full batch processing face of cloud stone glue, add water with sander behind pending the surperficial complete drying and carry out wet-milling, make treated side surfacing, smooth;
(6) coat with lacquer at its surperficial spray epoxy with dual nozzle spray gun on clean face surface;
(7) after pending drying, add water with sander and carry out wet-milling, the dry back of cleaning is carried out waxing polishing with polishing machine to treated side, then with getting final product behind the glass cement sealing frame bar slit.
Embodiment 6: a kind of granite-simulating paint is characterized in that: it is made up of for 15 parts 40 parts of white cements, 10 parts of white jade stone flours, 15 parts in 108 glue, 6.5 parts of ACRYLIC EMULSION, 15 parts of dry powders, iron oxide red powder, in parts by weight.
The preparation method is component and proportioning difference with embodiment 3.
Adopt the above-mentioned coating that makes to make the method for the artificial grantie of black matrix safflower line:
(1) cleaning, smooth pending metope: mark needed frame bar at pending metope, mixed and the back batch processing metope one time of stirring makes treated side smooth, after pending face is dried slightly with white cement and 108 glue, on the frame bar that marks, stick adhesive tape, treated side is divided into bulk;
(2) spraying and spray artificial grantie decorative pattern: described spraying is to spray the wetting metope of water smoke with water pistol to treated side earlier, after treating that metope is dried slightly, the described granite-simulating paint of the black for preparing by embodiment 5 to metope spray 6 times with dual nozzle spray gun, after pending the drying, transfer the nozzle bore of big dual nozzle spray gun, spray the described granite-simulating paint of the redness for preparing by present embodiment to treated side, make red described granite-simulating paint form block coarse groove at treated side, after treating surface drying, with cylinder with block coarse groove embossing moulding;
(3) corase grind: when pending surperficial drying reaches 75%-80%, will be sprayed with earlier the treated side dry grinding, smooth of granite-simulating paint, and add water again and carry out wet-milling with sander with sander;
(4) fine grinding: the aperture on the treated side, slit are mended with corresponding granite-simulating paint flat, treat complete drying after, with waterproof abrasive paper with surface finish, smooth;
(5) with the full batch processing face of cloud stone glue, add water with sander behind pending the surperficial complete drying and carry out wet-milling, make treated side surfacing, smooth;
(6) coat with lacquer at its surperficial spray epoxy with dual nozzle spray gun on clean face surface;
(7) after pending drying, add water with sander and carry out wet-milling, the dry back of cleaning is carried out waxing polishing with polishing machine to treated side, then with getting final product behind the glass cement sealing frame bar slit.
Embodiment 7: a kind of granite-simulating paint is characterized in that: it is made up of for 20 parts 35 parts of white cements, 12 parts of white jade stone flours, 17 parts in 107 glue, 5 parts of ACRYLIC EMULSION, 10 parts of chemical pastes, barba hispanica powder, in parts by weight.
The preparation method is component and proportioning difference with embodiment 3.
Adopt the above-mentioned coating that makes to make the method for the artificial grantie of the blue decorative pattern of white background:
(1) cleaning, smooth pending metope: mark needed frame bar at pending metope, mixed and the back batch processing metope two times of stirring makes treated side smooth, after pending face is dried slightly with white cement and 107 glue, on the frame bar that marks, stick adhesive tape, treated side is divided into bulk;
(2) spraying and spray artificial grantie decorative pattern: described spraying is to spray the wetting metope of water smoke with water pistol to treated side earlier, after treating that metope is dried slightly, the described granite-simulating paint of the white for preparing by embodiment 2 to metope spray 4 times with dual nozzle spray gun, after pending the drying, transfer the nozzle bore of big dual nozzle spray gun, spray the described granite-simulating paint of the blueness for preparing by present embodiment to treated side, make blue described granite-simulating paint form block coarse groove at treated side, after treating surface drying, with cylinder with block coarse groove embossing moulding;
(3) corase grind: when pending surperficial drying reaches 75%-80%, will be sprayed with earlier the treated side dry grinding, smooth of granite-simulating paint, and add water again and carry out wet-milling with sander with sander;
(4) fine grinding: the aperture on the treated side, slit are mended with corresponding granite-simulating paint flat, treat complete drying after, with waterproof abrasive paper with surface finish, smooth;
(5) with the full batch processing face of cloud stone glue, add water with sander behind pending the surperficial complete drying and carry out wet-milling, make treated side surfacing, smooth;
(6) coat with lacquer at its surperficial spray epoxy with dual nozzle spray gun on clean face surface;
(7) after pending drying, add water with sander and carry out wet-milling, the dry back of cleaning is carried out waxing polishing with polishing machine to treated side, then with getting final product behind the glass cement sealing frame bar slit.
Embodiment 8: a kind of granite-simulating paint is characterized in that: it is made up of for 30 parts 37 parts of white cements, 13 parts of white jade stone flours, 19 parts in 108 glue, 7 parts of ACRYLIC EMULSION, iron oxide yellow powder, in parts by weight.
The preparation method is component and proportioning difference with embodiment 3.
Adopt the above-mentioned coating that makes to make the method for the artificial grantie of the alternate decorative pattern of red end champac:
(1) cleaning, smooth pending metope: mark needed frame bar at pending metope, mixed and the back batch processing metope two times of stirring makes treated side smooth, after pending face is dried slightly with white cement and 108 glue, on the frame bar that marks, stick adhesive tape, treated side is divided into bulk;
(2) spraying and spray artificial grantie decorative pattern: described spraying is to spray the wetting metope of water smoke with water pistol to treated side earlier, after treating that metope is dried slightly, the described granite-simulating paint of the redness for preparing by embodiment 6 to metope spray 7 times with dual nozzle spray gun, after pending the drying, transfer the nozzle bore of big dual nozzle spray gun, spray the described granite-simulating paint of xanchromatic for preparing by present embodiment to treated side earlier, and then the described granite-simulating paint of the blueness for preparing by embodiment 7 to treated side spraying, make yellow, blue described granite-simulating paint forms block coarse groove at treated side, after treating surface drying, with cylinder with block coarse groove embossing moulding;
(3) corase grind: when pending surperficial drying reaches 75%-80%, will be sprayed with earlier the treated side dry grinding, smooth of granite-simulating paint, and add water again and carry out wet-milling with sander with sander;
(4) fine grinding: the aperture on the treated side, slit are mended with corresponding granite-simulating paint flat, treat complete drying after, with waterproof abrasive paper with surface finish, smooth;
(5) with the full batch processing face of cloud stone glue, add water with sander behind pending the surperficial complete drying and carry out wet-milling, make treated side surfacing, smooth;
(6) coat with lacquer at its surperficial spray epoxy with dual nozzle spray gun on clean face surface;
(7) after pending drying, add water with sander and carry out wet-milling, the dry back of cleaning is carried out waxing polishing with polishing machine to treated side, then with getting final product behind the glass cement sealing frame bar slit.
Claims (10)
1, a kind of granite-simulating paint is characterized in that: mainly be made up of for 5～7 parts 35～40 parts of white cements, 10～15 parts of marble flours, 15～20 parts of binding agents, ACRYLIC EMULSION, in parts by weight; Wherein said binding agent is 107 glue or 108 glue.
2, granite-simulating paint as claimed in claim 1 is characterized in that: it also have whitening powder or/and chemical paste or/and toning agent, its amount is: 0～45 part of whitening powder, 0～10 part of chemical paste, 0～30 part of toning agent, in parts by weight.
3, granite-simulating paint as claimed in claim 1 is characterized in that: described marble flour is the white jade stone flour.
4, granite-simulating paint as claimed in claim 2 is characterized in that: described whitening powder is titanium dioxide or dry powder.
5, the preparation method of granite-simulating paint as claimed in claim 1 is characterized in that: after in proportion white cement and marble flour being mixed, stir, add binding agent again, ACRYLIC EMULSION stirs and promptly gets coating.
6, the preparation method of granite-simulating paint as claimed in claim 2, it is characterized in that: after earlier white cement, marble flour being mixed, stir in proportion, add binding agent, ACRYLIC EMULSION, whitening powder again or/and chemical paste or/and toning agent stir coating.
7, as claim 1～4 arbitrary as described in the using method of coating, it is characterized in that: prepared coating is sprayed onto in pending.
8, as the using method of coating as described in the claim 7, it is characterized in that: treat earlier that treated side cleans, smooth processing; Then described coating is sprayed onto in pending; Pending drying reaches at 75%～80% o'clock, roughly grinds, fine grinding; With the full batch processing face of cloud stone glue, add water behind pending the complete drying and carry out wet-milling, make treated side smooth, smooth; Further clean face is again at its surperficial sprayed surface resin paint; After pending the drying, carry out wet-milling once more, waxing polishing is carried out to treated side in the dry back of cleaning, gets final product with glass cement sealing side seam crack, circle then.
9, as the using method of coating as described in the claim 8, it is characterized in that: described surface resin lacquer is epoxy resin-based paint.
10, as the using method of coating as described in the claim 8, it is characterized in that:
(1) cleaning, smooth pending: mark needed frame bar at pending face, mixed and the back batch processing face 1～2 time of stirring with white cement and 107 glue or 108 glue, make treated side smooth, after pending face is dried slightly, on the frame bar that marks, stick adhesive tape, treated side is divided into bulk;
(2) spraying is or/and spray artificial grantie decorative pattern: described spraying is to spray water smoke moist curing face with water pistol to treated side earlier, after pending face is dried slightly, spray the described granite-simulating paint of the white for preparing for 1～7 time or the colored described granite-simulating paint of required pattern to treated side with dual nozzle spray gun; Or/and described spray artificial grantie decorative pattern: after pending the drying, transfer the nozzle bore of big dual nozzle spray gun, spray the multiple colored described granite-simulating paint of required pattern to treated side, make colored described granite-simulating paint form block coarse groove at treated side, after treating surface drying, with cylinder with block coarse groove embossing moulding;
(3) corase grind: pending surperficial drying reaches at 75%～80% o'clock, will be sprayed with earlier the treated side dry grinding, smooth of granite-simulating paint with sander, adds water again and carries out wet-milling with sander;
(4) fine grinding: the lip-deep aperture of treated side, slit are mended with corresponding granite-simulating paint flat, treat complete drying after, with waterproof abrasive paper with surface finish, smooth;
(5) with the full batch processing face of cloud stone glue, add water with sander behind pending the surperficial complete drying and carry out wet-milling, make treated side surfacing, smooth;
(6) coat with lacquer at its surperficial spray epoxy with dual nozzle spray gun on clean face surface;
(7) after pending drying, add water with sander and carry out wet-milling, the dry back of cleaning is carried out waxing polishing with polishing machine to treated side, then with getting final product behind the glass cement sealing frame bar slit.