Abstract

The present invention relates to a method for manufacturing ocher boards for furniture making and ocher boards manufactured by the above method, and more particularly, to mix and crush Hanji paper in water, and then add oak charcoal to it and mix and grind it with a blender. In the first step, the second step of kneading by mixing the ocher powder in water and stirring with a blender, by adding the mixed crushed Hanji and charcoal powder mixture in the first step to the kneaded ocher mixture of the second step again by a mixer A method of manufacturing ocher boards for furniture manufacturing by a process comprising a third step of mixing and kneading the ocher paste, and a fourth step of putting the paste of the third step into a molding mold and then naturally drying at room temperature; It relates to an ocher board produced by the method.

The ocher board for furniture manufacturing according to the present invention is harmless to the human body because it is made of only natural materials, and can be utilized as an environmentally friendly building interior material with far-infrared radiation effects due to the inherent ocher ingredients and deodorization and antibacterial effects due to the addition of charcoal powder. There is an advantage.

Description

A method for manufacturing ocher boards for manufacturing furniture and ocher boards manufactured by the above method

The present invention is made of only natural materials, so it is harmless to human body, and manufacturing method of ocher board for furniture making, which can be utilized as eco-friendly building interior material with far-infrared radiation effect according to inherent ocher ingredient and deodorization and antibacterial effect by addition of charcoal powder and It relates to an ocher board produced by the method.

As the interest in health has increased from a long time, health promotion mechanisms for various articles have been developed using far-infrared emitters, magnets, and natural jade. Recently, as the other effects on the charcoal firewood began to be revealed, various application articles using charcoal have been developed and marketed, and many application articles using ocher have been developed and marketed.

In general, the chemical composition of ocher contains a small amount of iron oxide, calcium, magnesium, etc. in addition to silicon dioxide and aluminum oxide. It shows plasticity with high viscosity.

In addition, ocher is known to prevent aging of skin by oxidative lipid neutralization dilution such as catalase and protease, which releases and contains a large amount of far infrared rays, and decomposes and destroys cancer and abnormal cells. Demand is also rising rapidly.

The use of such loess has been developed, such as household goods and painted wallpaper, jangpan, but the ocher embedded in the wallpaper or jangpan is a very small amount is not enough to get great efficacy and effects. In addition, it was difficult to manufacture the board by using only ocher, and it was difficult to manufacture it as a board, and the strength was low, and it was difficult to use it as a light weight interior material or finishing material that should be as easy to handle as possible.

Meanwhile, as charcoal is a porous body, it has been used in real life recently as it has excellent effects such as humidity control, deodorization, antibacterial, electromagnetic wave blocking, water purification, and air purification. Usually, at home or business, charcoal itself is left as it is or put in a water purifier or refrigerator to achieve water purification and deodorization effect.However, at home, it is not easy to choose a suitable place to raise charcoal and it is not good to look at. The use of charcoal for removal or air purification is still insufficient.

An object of the present invention is to provide a manufacturing method of the ocher board for furniture manufacturing having far-infrared radiation effect and the deodorization and antibacterial effect by the addition of charcoal powder inherent to the ocher component to manufacture environmentally friendly furniture products.

It is also an object of the present invention to provide an ocher board for making furniture manufactured by the above method.

In order to solve the above object, the manufacturing method of the ocher board for making furniture according to the present invention is called by mixing 0.2 to 10 parts by weight of Hanji paper with respect to 100 parts by weight of water, and then by adding 10 to 15 parts by weight of oak charcoal powder The first step of mixing and grinding with a blender, a second step of mixing by stirring 100 ~ 150 parts by weight of ocher powder with respect to 100 parts by weight of water and stirring with a blender, the first step to the mixture of kneaded water and ocher powder of the second step Mixed crushed water, Hanji paper and charcoal powder mixture in the third step of mixing and kneading with a blender for 20 to 30 minutes to prepare the ocher paste, and the ocher paste prepared in the third step into a molding mold and room temperature It characterized in that it is manufactured by a process comprising a fourth step of natural drying.

At this time, the ocher paste of the third step is characterized in that it is prepared by further comprising 2 to 10% by weight of straw straw compared to the total weight of the paste.

In addition, there is provided an ocher board for producing furniture manufactured by the above method.

The ocher board for making furniture according to the present invention is harmless to the human body because it is made of only natural materials, and it is possible to produce furniture having excellent deodorizing and antibacterial effects due to the far-infrared radiation effect and the addition of charcoal powder. There is an advantage that can also be used as environmentally friendly building materials.

Hereinafter, the present invention will be described in more detail.

1 is a process diagram schematically showing the process of the manufacturing method of the ocher board for manufacturing furniture according to the present invention, after the process of mixing water, Hanji paper and charcoal and the process of mixing water and ocher powder, the mixture The paste is prepared by mixing them into one, then molded into a board and dried.

The process of mixing the water, Hanji paper and charcoal powder is called by mixing 0.2 to 10 parts by weight of Hanji paper with respect to 100 parts by weight of water, and then added to 10 to 15 parts by weight of oak charcoal powder mixed and pulverized by a blender.

At this time, the water may be used a conventional purified water, the paper is a conventional paper made of paper mulberry. Korea's traditional Korean paper is made from perennial vegetation, Dak tree, which has long been the mainstream of paper products in our lives, but since its high productivity, Yangji has been limited to its application in western paper or window paper, despite its excellent performance. there was. In the present invention, in the manufacture of the ocher board using a Hanji paper, it serves to reduce the weight of the board and increase the strength to prevent the occurrence of cracks.

The Hanji paper is mixed with 0.2 to 10 parts by weight with respect to the amount of 100 parts by weight of water, when the addition of 0.2 parts by weight or less occurs a lot of cracks occur in the drying process of the ocher board, when 10 parts by weight or more is called a soaking process Does not contain enough water, and the hardness of the whole ocher board is lowered.

In the present invention, the charcoal is used oak charcoal powder, it is preferable to use the pulverized in 200 mesh (mesh) or more. In the present invention, the charcoal powder is added to the mixture of water and Hanji paper, and then mixed and pulverized with a blender to mix evenly.

In the present invention, the process of mixing the water and the ocher powder is a process of mixing 100 to 150 parts by weight of the ocher powder with respect to 100 parts by weight of water, stirring and kneading with a blender. In order to knead the paste, the amount of water and the amount of ocher powder must be properly mixed. Specifically, when the ocher powder is 100 parts by weight or less, the amount of water increases and moldability decreases, and a lot of cracks are generated during the manufacture of the board. When the ocher powder is 150 parts by weight or more, the weight of the product is excessively increased, so 100 parts by weight of water is used. It is preferable that 100 to 150 parts by weight of the contrast ocher powder is mixed.

In the present invention, the ocher paste manufacturing process comprises mixing the water, Hanji paper and charcoal powder mixture and water and ocher powder mixture in a ratio of 1: 3 to 5, and then mixing and kneading with a blender for 20 to 30 minutes to prepare the ocher paste. It is a process to do it. After producing the said ocher paste, it is preferable to perform the shaping | molding process in the following shaping | molding die as a continuous process.

At this time, in preparing the ocher paste, when the rice straw powder of 2 to 10% by weight relative to the total weight of the ocher paste is added, the strength can be further increased while minimizing the weight of the ocher board.

In the present invention, the molding process can be produced in a thickness of 1 ~ 2cm put into a plate-shaped molding frame, when used as a building interior, etc. can be produced in a thickness of 2cm or more. However, when used as a loess board for making furniture, it is preferable to produce a thickness of 1.5 ~ 1.8cm. Too thin will increase the incidence of cracking, and too thick will make it less practical due to the weight of the product.

After the molding process, it is possible to complete the ocher board according to the present invention through natural drying. High temperature drying is also possible to shorten the drying time, but at 100 ° C. or more, cracking occurs during the drying process.

Figure 2 is an embodiment of the cabinet made by using the ocher board manufactured through the above process, when adding a special waterproof and coating treatment to the surface of the furniture produced furniture exhibits a variety of patterns and excellent practicality Production is possible.

The ocher board for making furniture of the present invention is harmless to the human body because it is made of only natural materials, and it is possible to produce furniture having excellent deodorizing and antibacterial effects due to the far-infrared radiation effect and the addition of charcoal powder, and the strength is excellent. There is an advantage that can be utilized as a building interior materials.

Although the present invention has been described above, the technical scope of the present invention is not limited to the contents described in the above-described embodiments, and equivalent configurations modified or changed by those skilled in the art may be described. Obviously, it is not beyond the scope of thought.

1 is a flow chart listing step by step the manufacturing method of the ocher board for manufacturing furniture according to the present invention,

Figure 2 is a picture of one embodiment of a cabinet manufactured using the ocher board manufactured by the method of the present invention.

Claims

A first step of mixing 0.2 to 10 parts by weight of Hanji paper with respect to 100 parts by weight of water, and then mixing 10 to 15 parts by weight of oak charcoal powder and mixing and pulverizing with a blender;

A second step of mixing 100 to 150 parts by weight of ocher powder with respect to 100 parts by weight of water and stirring the mixture with a mixer;

Mixing and pulverizing water, Hanji paper and charcoal powder mixture in the first step and the kneaded water and ocher powder mixture of the second step in a ratio of 1: 3 to 5, and then mixed and kneaded with a blender for 20 to 30 minutes A third step of preparing an ocher paste; And

After the ocher paste prepared in the third step in the molding die and the manufacturing method of the ocher board for furniture manufacturing is manufactured by a process comprising a fourth step of natural drying at room temperature.

The method of claim 1, wherein the third step of the ocher paste,

The ocher board manufacturing method for furniture making, characterized in that it further comprises rice straw of 2 to 10% by weight relative to the total weight of the ocher paste.

A loess board for manufacturing furniture manufactured by the method of claim 1.