KR20000049399A - Amult-Fuaction A Box laying method dya loess - Google Patents

Abstract

PURPOSE: A method for preparing a cinerary urn using loess and hardwood charcoal is provided which prevents the cracking of a cinerary urn and the decomposition of cinereous bodies and reduces the cost of production. CONSTITUTION: A mixture of 70% by weight of loess, 10% by weight of clay or kaolin, 13% by weight of pulp, fiber or straw, 2% by weight of leaves of a ginkgo, a pine needle, a mugwort, and starch, and the balance being a material is blended with above 100% by weight of water, heat treated at 250°C for 20 to 30 min, dried at 60 to 90°C for 24 hr, dried naturally, and coated with a graze to give a solid, beautiful funerary urn. The product has high impact strength two times that of pottery and a smell of the mugwort.

Description

Manufacture of multipurpose crypts using loess {Amult-Fuaction A Box laying method dya loess}

The present invention relates to a method for manufacturing multipurpose crypts using ocher and charcoal, and more particularly, to facilitate its molding without baking the crypts molded using ocher and charcoal, and at the same time, the impact is greatly strengthened to cause cracks or crumbs. The present invention relates to a method for producing multipurpose crypts using ocher and char as a mixed method of preventing.

In general, ocher absorbs moisture when it is wet and discharges water when it is dry, so it is not only excellent in humidity control but also has various beneficial and antibacterial ingredients. Charcoal is also known for its excellent efficacy as a dehumidifying and deodorizing and disinfectant.

It is a large object of the present invention to bind the above-mentioned loess, charcoal and use the compound for multi-purpose.

Until now, the reason why it was not possible to manufacture the ossuary using ocher is because it is difficult to manufacture it without baking because the cracks or cracks occur when the ocher is dried due to the lack of adhesion of the ocher.

Therefore, the present invention invented in view of the problems as described above, and the direct contact with the antimicrobial properties due to the decay of oak, charcoal, and charcoal can be mixed with charcoal to remove moisture and odor removal and kaolin, clay mixed It provides firmness, and combines pine needle starch, which gives cohesive strength to pulp, fiber, straw, and styrofoam with scent, and scented mugwort to produce urine box. It is an object of the present invention to provide a method for manufacturing a multi-purpose coarse bin which can greatly reduce energy saving in a solar drying manufacturing process.

In addition, the present invention is to classify and shape the body and the lid as described above to attach the surface to the surface of the lid of a predetermined size with jade, stainless, glass, wood, etc., or smooth the surface by a heat treatment process of 500 ℃ with emulsion coating or urethane, etc. The purpose of the present invention is to provide a multi-purpose manufacturing method using ocher charcoal that can be applied to smooth and display the beauty.

The present invention for achieving the above object is a predetermined size after mixing 70% ocher weight, 5% charcoal weight, 10% kaolin weight, pulp, fiber, straw 13% by weight of pine needles, mugwort starch 2% After molding to the molding die of the heat treatment step and drying step is characterized in that carried out for a predetermined temperature and time.

The present invention is also mixed with more than 100% of moisture in the process of heat treatment and drying the molded crypt and then heat-treated at 250 ℃ for 20-30 minutes in the heat treatment process and dried for 24 hours at 60 ~ 90 ℃ in the drying process Complete after drying for 48 hours in drying.

In addition, the present invention can change the various colors by coating the outside, the inside has the characteristics of giving the efficacy of ocher antibacterial and true charcoal as raw ocher.

Hereinafter, the manufacturing method according to the present invention will be described.

First, ocher and charcoal are the main ingredients, and pulp, fiber, straw, and styrofoam are mixed at a predetermined ratio. -Pulp, fiber, straw, and styrofoam play a role of preventing cracks or chipping. Pine needles, starch, and ginkgo leaves give cohesion, wormwood gives fragrance, and kaolin, clay gives firmness and impact. Will give an effect.

Then, the mold is sprayed according to a predetermined amount with a water sprayer and simultaneously sprayed evenly according to a predetermined amount to a predetermined stirrer. On the other hand, the reason for heating the water is to facilitate the mixing of pulp, straw, fibers and the like and other residues.

After the mixture is uniformly mixed as described above, the mixture is placed in a mold and molded in a predetermined box, followed by heat treatment at 250 ° C. for 20 minutes in the first heat treatment step, followed by drying at 60-90 ° C. for 24 hours in a drying step, Dry for 48 hours.

Then, the dried ossuary is coated by heat-treating the outer surface with latex coating or coated with lacquer and urethane, and the glass is attached to the glass, stainless steel, wood, stone, etc. to show the beauty.

Example

70% cotton bottom loess, 5% charcoal weight, kaolin. 10% clay weight, pulp. fiber. straw. 13% weight of styrofoam, mugwort. Starch. 2% by weight of ginkgo biloba is mixed with water and then mixed uniformly in a stirrer.

Then, put the mixture into the mold, and put the mixture of the predetermined shape into the mold to prepare a box of the predetermined shape, heat-treated for 20 minutes at 250 ℃ in the heat treatment process, and dried for 24 hours at 60 ~ 90 ℃ in the drying process 48 Drying was completed for time.

At this time, the instantaneous surface frictional heat coating in the drying process.

Therefore, the present invention is a baking method by producing a mixture of ocher and charcoal, and kaolin to improve the firmness, clay, pulp, fiber, straw, styrofoam, styrofoam, pine needles, ginkgo leaves, starch, wormwood to give cohesion Energy saving, waste prevention from bacteria and insects encroachment, and the impact effect is more than twice as strong as ceramics, it is very useful to increase the demand of ossuary sugar, which increases day by day.

The present invention is not limited to the preferred embodiments of the above-described characteristics, and various modifications can be made by those skilled in the art without departing from the gist of the present invention as claimed above. And such changes will fall within the scope of the claims.

Claims (4)

70% ocher weight, 10% clay, kaolin weight, lump, fiber, straw, styrofoam 13% weight, uniformly add and mix ginkgo biloba, pine needles, mugwort, starch, etc. It is characterized in that the drying process is carried out for a predetermined temperature and time. The method of claim 1 After applying the latex to the surface of the dried brick, heat-treated and coated with 500 ℃, urethane, lacquer, etc., the oak, charcoal manufacturing method characterized in that using the ocher, charcoal The method of claim 1 Method for producing multipurpose crypts using ocher and charcoal with a thermal friction coating of 300 ° C. on a dried surface. The method of claim 1 A method for manufacturing multipurpose crypts using ocher and charcoal, characterized by attaching any one of stainless steel, glass, wood, and stone to the dried crypts surface.