KR20090130921A - Plastic multi color electrodeposition coating method and multi color electrodeposition coating layers using the method - Google Patents

Plastic multi color electrodeposition coating method and multi color electrodeposition coating layers using the method Download PDF

Info

Publication number
KR20090130921A
KR20090130921A KR1020080056639A KR20080056639A KR20090130921A KR 20090130921 A KR20090130921 A KR 20090130921A KR 1020080056639 A KR1020080056639 A KR 1020080056639A KR 20080056639 A KR20080056639 A KR 20080056639A KR 20090130921 A KR20090130921 A KR 20090130921A
Authority
KR
South Korea
Prior art keywords
layer
electrodeposition
color
plastic
electrodeposition coating
Prior art date
Application number
KR1020080056639A
Other languages
Korean (ko)
Inventor
전수민
강성민
Original Assignee
삼광공업(주)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 삼광공업(주) filed Critical 삼광공업(주)
Priority to KR1020080056639A priority Critical patent/KR20090130921A/en
Publication of KR20090130921A publication Critical patent/KR20090130921A/en

Abstract

PURPOSE: A plastic multicolor electrodeposition coating method is provided to implement design about various characters or patterns on the plastic surface through a simple process, and to increase productivity of a process. CONSTITUTION: A plastic multicolor electrodeposition coating method includes the following steps of: treating and plating the surface of a plastic base material(S110); generating a first deposition layer by depositing a first color on a plated layer(S120); etching a part of the first deposition layer by irradiating a laser on the part of the first deposition layer(S130); generating a second deposition layer by depositing a second color on a first etched groove of the first deposition layer etched by irradiation of the laser(S140); and generating a third deposition layer(S150).

Description

플라스틱 다중컬러 전착코팅방법 및 그를 이용한 다중컬러 전착코팅층{Plastic multi color electrodeposition coating method and multi color electrodeposition coating layers using the method}Plastic multicolor electrodeposition coating method and multicolor electrodeposition coating layer using the same {Plastic multi color electrodeposition coating method and multi color electrodeposition coating layers using the method}

본 발명은 플라스틱 다중컬러 전착코팅방법 및 그를 이용한 다중컬러 전착코팅층에 관한 것으로서, 더욱 상세하게는 플라스틱 모재의 표면에 동일평면상에서 다양한 문양 및 컬러가 구현될 수 있도록 한 플라스틱 다중컬러 전착코팅방법 및 그를 이용한 다중컬러 전착코팅층에 관한 것이다.The present invention relates to a plastic multicolor electrodeposition coating method and a multicolor electrodeposition coating layer using the same, and more particularly, to a plastic multicolor electrodeposition coating method to realize various patterns and colors on the same plane on the surface of a plastic base material. It relates to a multi-color electrodeposition coating layer used.

일반적으로 전화기, 이동통신단말기 등의 전자제품은 외형이 플라스틱 재질로 제조되고 있으며, 제품의 내구성 및 고급화를 위하여 플라스틱 본체의 표면에 다양한 코팅층을 형성하여 제조되고 있다.In general, electronic products such as telephones and mobile communication terminals are manufactured from plastic materials, and are manufactured by forming various coating layers on the surface of the plastic body for durability and quality of products.

여기서, 플라스틱 재질의 표면에 코팅되는 코팅층은 통상 투명한 화학성분의 코팅막 처리를 하고 있다.Here, the coating layer coated on the surface of the plastic material is usually treated with a coating film of a transparent chemical component.

또한, 플라스틱 제품을 플라스틱 제품이 아닌 금속재질로 보일 수 있도록 표면을 도금처리하여 소정의 두께를 갖는 도금층을 형성하기도 하였다.In addition, the surface is plated to form a plating layer having a predetermined thickness so that the plastic product may be viewed as a metal material rather than a plastic product.

상기와 같은 플라스틱 제품의 표면처리는 플라스틱 제품이 강도가 강하게 보 이거나 외관상 고급스러움이 느껴질 수 있도록 다양한 도금층을 적용하고 있다.Surface treatment of the plastic product as described above is applying a variety of plating layers so that the plastic product can be seen as a strong strength or luxury in appearance.

이때, 도금층은 니켈, 크롬 등의 금속이 함유된 도금층 등으로 형성되며, 이러한 도금층이 형성된 플라스틱 제품은 일반적인 플라스틱 제품의 외관과 달리 제품이 금속으로 제조된 것으로 표현되어 고급스럽고, 미려한 느낌을 갖게 한다.In this case, the plating layer is formed of a plating layer containing a metal such as nickel, chromium, etc., and the plastic product having such a plating layer is expressed as being made of metal, unlike the appearance of a general plastic product, to have a luxurious and beautiful feeling. .

한편, 근래에 들어서면서 전자제품의 디자인은 날로 화려하고 고급스럽게 표면처리되고 있다.On the other hand, in recent years, the design of electronic products has been surface-treated with gorgeous and luxurious.

따라서, 이에 걸맞게 플라스틱 재질로 제조되는 전자제품의 표면에 대하여 다양한 문자 및 문양 등을 구현하는 것이 중요하게 요구되는 실정이다.Therefore, according to this situation it is important to implement a variety of characters and patterns on the surface of the electronic product made of a plastic material.

그러나, 전술한 바와 같은 종래의 플라스틱 제품에서의 표면처리는 플라스틱 표면에 다양한 문자나 형상 등을 구현할 수 없다는 문제점이 있었다.However, the surface treatment in the conventional plastic product as described above has a problem that it is not possible to implement a variety of characters, shapes, and the like on the plastic surface.

따라서, 플라스틱 표면에 다양한 문자나 형상 등에 대하여 다양한 컬러로 구현시킬 수도 없었다.Therefore, the plastic surface could not be embodied in various colors for various characters or shapes.

상기와 같은 문제점을 해결하기 위하여, 본 발명은 플라스틱 다중컬러 전착코팅방법 및 그를 이용한 다중컬러 전착코팅층에 관한 것으로서, 더욱 상세하게는 플라스틱 모재의 표면에 동일평면상에서 다양한 문양 및 컬러가 구현될 수 있도록 한 플라스틱 다중컬러 전착코팅방법을 제공하는 것을 목적으로 한다.In order to solve the above problems, the present invention relates to a plastic multi-color electrodeposition coating method and a multi-color electrodeposition coating layer using the same, more specifically, so that various patterns and colors can be implemented on the same plane on the surface of the plastic base material It is an object to provide a plastic multicolor electrodeposition coating method.

또한, 본 발명의 다른 목적은 플라스틱 모재의 표면에 1차적으로 형성된 도금층 상면에서 다양한 문양 및 컬러가 동일한 두께의 층으로 구현될 수 있도록 한 플라스틱 다중컬러 전착코팅방법을 이용한 다중컬러 전착코팅층을 제공하는데 있다.In addition, another object of the present invention to provide a multi-color electrodeposition coating layer using a plastic multi-color electrodeposition coating method to enable a variety of patterns and colors to be implemented in a layer of the same thickness on the upper surface of the plating layer formed primarily on the surface of the plastic base material. have.

상기 목적을 달성하기 위하여, 본 발명의 바람직한 실시예에 따른 플라스틱 다중컬러 전착코팅방법은 플라스틱 모재의 표면을 도금처리하는 제1 단계; 상기 플라스틱 모재의 도금처리된 도금층에 제1 컬러를 전착시켜 제1 전착층을 생성하는 제2 단계; 상기 제1 전착층의 일부분에 레이저를 조사하여 상기 제1 전착층의 일부분을 식각하는 제3 단계; 그리고 상기 레이저 조사에 의해 식각된 제1 전착층의 제1 식각홈에 제2 컬러를 전착시켜 제2 전착층을 생성하는 제4 단계를 포함하여 이루어진다.In order to achieve the above object, the plastic multicolor electrodeposition coating method according to a preferred embodiment of the present invention comprises a first step of plating the surface of the plastic base material; A second step of electrodepositing a first color on the plated plating layer of the plastic base material to generate a first electrodeposition layer; Irradiating a portion of the first electrodeposition layer with a laser to etch a portion of the first electrodeposition layer; And a fourth step of generating a second electrodeposition layer by electrodepositing a second color on the first etching groove of the first electrodeposition layer etched by the laser irradiation.

여기서, 상기 제1 전착층에 대하여 일부분이 재차 레이저를 이용한 식각처리가 되며, 식각처리된 상기 제1 전착층의 제2 식각홈에 제3의 컬러를 전착시켜 제3 의 전착층을 생성하는 제5 단계를 더 포함하여 이루어짐이 바람직하다.Here, a part of the first electrodeposition layer is subjected to an etching process again by using a laser, and a third color electrodeposits a third color on the second etching groove of the first electrodeposition layer which is etched to generate a third electrodeposition layer. It is preferred to further comprise five steps.

이때, 상기 제5 단계는 베이스 컬러로써 상기 도금층의 상면에 전체적으로 형성된 상기 제1 전착층과 동일평면상에 다양한 문양 및 컬러가 표현될 수 있도록 상기 제2 전착층의 제2 컬러 외에 추가로 전착코팅하고자하는 컬러 수에 대응되어 다수 번 반복될 수 있다.In this case, the fifth step is an electrodeposition coating in addition to the second color of the second electrodeposition layer so that various patterns and colors can be expressed on the same plane as the first electrodeposition layer formed on the upper surface of the plating layer as a base color. It may be repeated many times corresponding to the number of colors to be desired.

한편, 본 발명에 따른 플라스틱 다중컬러 전착코팅방법을 통한 플라스틱 다중컬러 전착코팅층은 플라스틱 모재의 표면을 도금처리하여 형성된 도금층; 상기 도금층의 상면 전체에 걸쳐 베이스 컬러인 제1 컬러로 전착되는 제1 전착층; 그리고 상기 제1 전착층의 소정의 면적에 대하여 레이저로 식각되며, 식각처리되어 형성된 제1 식각홈에 제2 컬러로 전착코팅되는 제2 전착층을 포함하여 이루어진다.On the other hand, the plastic multi-color electrodeposition coating layer by the plastic multi-color electrodeposition coating method according to the present invention is a plating layer formed by plating the surface of the plastic base material; A first electrodeposition layer electrodeposited to a first color which is a base color over the entire upper surface of the plating layer; And a second electrodeposition layer which is etched with a laser with respect to a predetermined area of the first electrodeposition layer, and is electrodeposited and coated with a second color on the first etching groove formed by etching.

여기서, 상기 제1 전착층의 소정의 면적에 대하여 재차 레이저로 식각되며, 식각처리된 제2 식각홈에 제3의 컬러로 전착코팅되는 제3의 전착층을 더 포함하여 이루어짐이 바람직하다.Here, it is preferable that the third electrodeposition layer is etched with a laser again with respect to a predetermined area of the first electrodeposition layer, and the third electrodeposition layer is electrodeposited and coated with a third color on the etched second etching groove.

상기에서 설명한 본 발명에 따른 플라스틱 다중컬러 전착코팅방법 및 그를 이용한 다중컬러 전착코팅층의 효과를 설명하면 다음과 같다.When explaining the plastic multi-color electrodeposition coating method and the multi-color electrodeposition coating layer using the same according to the present invention described above are as follows.

첫째, 레이저를 이용한 식각처리로 형성된 식각홈에 다양한 컬러를 전착코팅시킴으로써 플라스틱 모재의 도금층 상면에 다양한 문양 및 컬러가 동일한 두께의 층으로 동일평면상에서 구현될 수 있다.First, various patterns and colors may be implemented on the same plane as layers having the same thickness on the upper surface of the plating layer of the plastic base material by electrodeposition coating various colors on the etching grooves formed by the etching process using a laser.

둘째, 플라스틱 표면에 다양한 문자나 형상 등의 문양에 대한 디자인을 간단 한 공정을 통하여 용이하게 구현시킬 수 있으며, 아울러 다양한 문자나 형상에 대하여 다양한 컬러로 구현시킬 수 있다.Second, the design of patterns such as various characters or shapes on the plastic surface can be easily implemented through a simple process, and also in various colors for various characters or shapes.

셋째, 레이저를 이용한 식각처리로 형성된 식각홈에 다양한 컬러를 전착코팅시키는 공정을 통하여 간단한 반복공정에 의한 다중컬러의 전착코팅이 가능하며, 이에 따라 생산성을 증대시킬 수 있다.Third, multi-color electrodeposition coating by a simple iterative process is possible through the process of electrodeposition coating various colors in the etching groove formed by the etching process using a laser, thereby increasing the productivity.

이하, 첨부된 도면을 참조하여 본 발명에 따른 의 바람직한 실시예를 상세히 설명한다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings.

도 1은 본 발명에 따른 플라스틱 다중컬러 전착코팅방법의 단계별 공정을 나타낸 블록도이다.1 is a block diagram showing the step-by-step process of the plastic multi-color electrodeposition coating method according to the present invention.

도 2는 본 발명에 따른 플라스틱 다중컬러 전착코팅방법의 단계별 공정을 통하여 플라스틱 모재의 일면에 도금층 및 전착층이 형성되는 상태를 나타낸 단면도이다.2 is a cross-sectional view showing a state in which a plating layer and an electrodeposition layer are formed on one surface of a plastic base material through a step-by-step process of the plastic multicolor electrodeposition coating method according to the present invention.

도 3은 본 발명에 따른 플라스틱 다중컬러 전착코팅층의 일 예를 나타낸 단면도이고, 도 4는 본 발명에 따른 플라스틱 다중컬러 전착코팅층의 다른 예를 나타낸 단면도이다.3 is a cross-sectional view showing an example of a plastic multicolor electrodeposition coating layer according to the present invention, Figure 4 is a cross-sectional view showing another example of a plastic multicolor electrodeposition coating layer according to the present invention.

도 1 내지 4에서 보는 바와 같이, 본 발명의 바람직한 실시예에 따른 플라스틱 다중컬러 전착코팅방법은 플라스틱 모재를 도금처리하는 제1 단계(S110), 제1 전착층을 생성하는 제2 단계(S120), 레이저를 이용하여 식각처리하는 제3 단계(S130), 그리고 제2 전착층을 생성하는 제4 단계(S140)를 포함하여 이루어진다.As shown in Figures 1 to 4, the plastic multi-color electrodeposition coating method according to a preferred embodiment of the present invention is a first step (S110) for plating the plastic base material, a second step (S120) for generating a first electrodeposition layer , A third step (S130) of etching using a laser, and a fourth step (S140) of generating a second electrodeposition layer.

여기서, 상기 플라스틱 모재를 도금처리하는 제1 단계(S110)는 전자제품의 외형에 대한 모재가 되는 플라스틱 모재(100)의 표면에 대하여 도금처리하여 상기 플라스틱 모재(100)의 표면에 도금층(110)을 생성하는 단계로 이루어진다.Here, the first step (S110) of plating the plastic base material is plated on the surface of the plastic base material 100 by plating the surface of the plastic base material 100, which is a base material for the appearance of electronic products. It is made of a step.

이때, 상기 도금층(110)의 생성은 상기 플라스틱 모재(100)의 표면 전체적으로 생성됨이 바람직하다.At this time, the generation of the plating layer 110 is preferably generated on the entire surface of the plastic base material (100).

또한, 상기 제1 전착층을 생성하는 단계(S120)는 상기 플라스틱 모재(100)의 도금처리된 도금층(110)에 제1 컬러를 전착시켜 상기 도금층(110) 상면 전체에 걸쳐 제1 전착층(120)을 전착코팅시키는 단계로 이루어진다.In addition, the step of generating the first electrodeposition layer (S120) is electrodeposition the first color on the plated plating layer 110 of the plastic base material 100 to the first electrodeposition layer (over the entire surface of the plating layer 110) ( 120) the electrodeposition coating step.

여기서, 상기 제1 전착층(120)은 베이스 컬러로써 상기 플라스틱 모재(100)의 일면에 형성된 상기 도금층(110)의 상면에 전체적으로 형성됨이 바람직하다.Here, the first electrodeposition layer 120 is preferably formed on the entire upper surface of the plating layer 110 formed on one surface of the plastic base material 100 as a base color.

그리고, 상기 레이저를 이용하여 식각처리하는 제3 단계(S130)는 상기 제1 전착층(120)의 일부분에 레이저를 조사하여 상기 제1 전착층(120)의 일부분을 식각하는 단계로 이루어진다.In addition, the third step S130 of etching using the laser may be performed by etching a portion of the first electrodeposition layer 120 by irradiating a portion of the first electrodeposition layer 120 with the laser.

이때, 상기 레이저를 이용하여 식각처리하는 제3 단계(S130)를 통하여 상기 제1 전착층(120)의 일부분에는 소정의 형상을 갖는 제1 식각홈(123)이 형성된다.In this case, a first etching groove 123 having a predetermined shape is formed in a portion of the first electrodeposition layer 120 through a third step S130 of etching using the laser.

또한, 상기 제2 전착층을 생성하는 제4 단계(S140)는 레이저를 이용한 식각처리단계(S130)를 통하여 형성된 상기 제1 식각홈(123)에 제2 컬러를 전착시켜 상기 도금층(110) 상면에 제2 전착층(130)을 전착코팅시키는 단계로 이루어진다.In addition, in the fourth step S140 of generating the second electrodeposition layer, an upper surface of the plating layer 110 is electrodeposited by depositing a second color on the first etching groove 123 formed through an etching process step S130 using a laser. Electrodeposition of the second electrodeposition layer 130 is carried out.

한편, 상기 제2 전착층을 생성하는 제4 단계(S140) 후에는 제3의 전착층을 생성하는 제5 단계(S150)가 더 이루어짐이 바람직하다.Meanwhile, after the fourth step S140 of generating the second electrodeposition layer, a fifth step S150 of generating the third electrodeposition layer is further preferably performed.

여기서, 상기 제3의 전착층을 생성하는 제5 단계(S150)는 상기 제1 전착층(120)의 일부분이 재차 레이저를 이용한 식각처리가 되며, 식각처리에 의해 형성된 상기 제1 전착층(120)의 제2 식각홈(124)에 제3의 컬러를 전착시켜 상기 도금층(110) 상면에 제3의 전착층(140)을 전착코팅시키는 단계로 이루어진다.Here, in the fifth step S150 of generating the third electrodeposited layer, a portion of the first electrodeposited layer 120 is subjected to an etching process using a laser again, and the first electrodeposited layer 120 formed by the etching process is performed. Electrodepositing a third color on the second etching groove 124 of the electrode), followed by electrodeposition coating of the third electrodeposition layer 140 on the upper surface of the plating layer 110.

이때, 상기 제3의 전착층을 생성하는 제5단계(S150)는 상기 제2 전착층의 제2 컬러 외에 추가로 전착코팅하고자 하는 컬러 수에 대응되어 다수 번 반복될 수 있다.In this case, the fifth step S150 of generating the third electrodeposition layer may be repeated a plurality of times corresponding to the number of colors to be electrodeposited in addition to the second color of the second electrodeposition layer.

이와 같이, 상기 제3의 전착층을 생성하는 제5단계(S150)가 추가되되, 전착코팅하고자 하는 컬러 수에 대응되어 반복됨으로써 베이스 컬러로써 상기 도금층(110)의 상면에 전체적으로 형성된 상기 제1 전착층(120)과 동일평면상에 다양한 문양 및 컬러가 표현될 수 있다.As such, a fifth step (S150) of generating the third electrodeposition layer is added, and the first electrodeposition is formed on the entire surface of the plating layer 110 as a base color by repeating corresponding to the number of colors to be electrodeposition coated. Various patterns and colors may be represented on the same plane as the layer 120.

한편, 전술한 바와 같은 본 발명에 따른 플라스틱 다중컬러 전착코팅방법은 공정순서에 따라 순차적으로 살펴보면 다음과 같다.On the other hand, the plastic multi-color electrodeposition coating method according to the present invention as described above will be described in sequence according to the process sequence.

먼저, 플라스틱 모재(100)의 표면에 도금층(110)을 형성하는 도금처리단계가 진행되고, 이후 상기 도금층(110)의 상면 전체에 걸쳐 제1 컬러가 전착되어 제1 전착층(120)이 전착코팅된다.First, a plating treatment step of forming the plating layer 110 on the surface of the plastic base material 100 is performed. After that, the first color is electrodeposited on the entire upper surface of the plating layer 110, and the first electrodeposition layer 120 is electrodeposited. Coated.

그리고, 상기 제1 전착층(120)의 소정의 면적에 해당하는 부분에 레이저를 조사하여 식각처리하여 제1 식각홈(123)을 형성한다.In addition, a laser beam is irradiated to a portion corresponding to a predetermined area of the first electrodeposition layer 120 to be etched to form a first etching groove 123.

이후, 상기 제1 식각홈(123)에 제2 컬러를 전착시켜 상기 제1 전착층(120)과 동일평면상에 동일한 두께로 제2 전착층(130)이 전착코팅된다.Thereafter, the second electrodeposition layer 130 is electrodeposited and coated on the same plane as the first electrodeposition layer 120 by electrodepositing a second color on the first etching groove 123.

상기 제2 전착층(130)이 전착코팅된 후, 제3의 컬러로 전착코팅이 요구되면 제3의 전착층(140)을 상기 제1 전착층(120)과 동일한 두께로 동일평면상에 전착코팅시킨다.After electrodeposition coating of the second electrodeposition layer 130, if electrodeposition coating is required in a third color, the third electrodeposition layer 140 is electrodeposited on the same plane with the same thickness as the first electrodeposition layer 120. Coating.

여기서, 상기 제3의 전착층(140)이 상기 도금층(110) 상면에 전착코팅되는 공정은 상기 제1 전착층(120)의 일부분에 재차 레이저를 이용한 식각처리가 된 후, 식각처리에 의해 형성된 상기 제1 전착층(120)의 제2 식각홈(124)에 제3의 컬러를 전착시켜 상기 도금층(110) 상면에 제3의 전착층(140)을 전착코팅시키는 공정으로 이루어진다.Here, the process of electrodeposition coating the third electrodeposition layer 140 on the upper surface of the plating layer 110 is subjected to an etching process using a laser on a portion of the first electrodeposition layer 120 again, and then formed by etching Electrodepositing the third color on the second etching groove 124 of the first electrodeposition layer 120 is electrodeposition coating the third electrodeposition layer 140 on the upper surface of the plating layer (110).

이때, 상기 제3의 컬러가 다수 개로 요구될 경우에 상기 제3의 전착층(140)을 전착코팅시키는 공정은 요구되는 컬러의 수에 대응되어 반복공정으로 진행된다.In this case, when a plurality of the third colors are required, the process of electrodeposition coating the third electrodeposition layer 140 proceeds to a repetitive process corresponding to the required number of colors.

한편, 상기 제3의 컬러로 전착코팅이 요구되지 않을 경우에는 상기 제2 전착층(140)이 전착코팅된 후, 플라스틱 모재(100)의 다중컬러 전착 코팅공정이 종료된다.On the other hand, when the electrodeposition coating is not required in the third color, after the electrodeposition coating of the second electrodeposition layer 140, the multi-color electrodeposition coating process of the plastic base material 100 is completed.

전술한 바와 같이, 본 발명에 따른 플라스틱 모재(100)의 다중컬러 전착코팅방법은 레이저를 이용한 식각처리로 형성된 식각홈(123, 124)에 다양한 컬러를 전착코팅시킴으로써 플라스틱 모재(100)의 도금층 상면에 다양한 문양 및 컬러가 동일한 두께의 층으로 동일평면상에서 구현시킬 수 있다.As described above, in the multi-color electrodeposition coating method of the plastic base material 100 according to the present invention, the plating layer upper surface of the plastic base material 100 is electrodeposited by coating various colors on the etching grooves 123 and 124 formed by an etching process using a laser. Various patterns and colors can be implemented on the same plane as layers of the same thickness.

또한, 플라스틱 표면에 다양한 문자나 형상 등의 문양에 대한 디자인을 간단한 공정을 통하여 용이하게 구현시킬 수 있으며, 아울러 다양한 문자나 형상에 대하여 다양한 컬러로 구현시킬 수 있다.In addition, it is possible to easily implement a design for a pattern, such as a variety of letters or shapes on the plastic surface through a simple process, and can also be implemented in a variety of colors for a variety of letters or shapes.

더욱이, 레이저를 이용한 식각처리로 형성된 식각홈(123, 124)에 다양한 컬러를 전착코팅시키는 공정을 통하여 간단한 반복공정에 의한 다중컬러의 전착코팅이 가능하며, 이에 따라 생산성을 증대시킬 수 있다.Furthermore, electrodeposition coating of multiple colors by a simple iterative process is possible through electrodeposition coating various colors on the etching grooves 123 and 124 formed by the etching process using a laser, thereby increasing productivity.

한편, 도 3 및 도 4를 참조하면, 본 발명에 따른 플라스틱 다중컬러 전착코팅방법을 이용한 플라스틱 다중컬러 전착코팅층은 도금층(110), 제1 전착층(120) 및 제2 전착층(130)을 포함하여 이루어진다.Meanwhile, referring to FIGS. 3 and 4, the plastic multicolor electrodeposition coating layer using the plastic multicolor electrodeposition coating method according to the present invention may include a plating layer 110, a first electrodeposition layer 120, and a second electrodeposition layer 130. It is made to include.

여기서, 상기 도금층(110)은 플라스틱 모재(100)의 표면을 도금처리하여 상기 플라스틱 모재(100)의 일면에 전체적으로 형성된다.Here, the plating layer 110 is formed on the entire surface of the plastic base material 100 by plating the surface of the plastic base material 100.

또한, 상기 제1 전착층(120)은 상기 도금층(110)의 상면 전체에 걸쳐 베이스 컬러인 제1 컬러로 전착코팅됨이 바람직하다.In addition, the first electrodeposition layer 120 is preferably electrodeposited with a first color of the base color over the entire upper surface of the plating layer (110).

그리고, 상기 제2 전착층(130)은 상기 제1 전착층(120)의 소정의 면적에 대하여 레이저로 식각되며, 식각처리에 의해 형성된 제1 식각홈(123)에 제2 컬러로 전착코팅된다.In addition, the second electrodeposition layer 130 is etched with a laser with respect to a predetermined area of the first electrodeposition layer 120, and is electrodeposited and coated with a second color on the first etching groove 123 formed by an etching process. .

전술한 바와 같이, 상기 제2 전착층(130)은 식각처리에 의한 식각홈 형성공정 및 식각홈에 컬러를 전착코팅시키는 전착코팅공정을 통하여 형성됨이 바람직하다.As described above, the second electrodeposition layer 130 is preferably formed through an etching groove forming process by an etching process and an electrodeposition coating process for electrodeposition coating color on the etching groove.

한편, 상기 제2 전착층(130)의 제2 컬러 외에 추가로 전착코팅하고자하는 컬러 수에 대응되어 상기 제1 전착층의 소정의 면적에 대하여 재차 레이저로 식각된 후, 식각처리된 제2 식각홈(124)에 상기 제1 전착층과 동일평면상에 동일한 두께로 형성되는 제3의 전착층(140)이 더 형성될 수 있다.Meanwhile, in addition to the second color of the second electrodeposition layer 130, the second etching process is performed after the laser is etched again with respect to a predetermined area of the first electrodeposition layer, corresponding to the number of colors to be electrodeposition coated. A third electrodeposition layer 140 may be further formed in the groove 124 to have the same thickness on the same plane as the first electrodeposition layer.

이때, 상기 제3의 전착층(140)은 상기 제2 전착층(130)의 제2 컬러 외에 추가로 요구되는 제3의 컬러의 수에 대응되어 식각처리에 의한 식각홈 형성공정 및 식각홈에 컬러를 전착코팅시키는 전착코팅공정의 반복공정에 의해 형성됨이 바람직하다.In this case, the third electrodeposition layer 140 corresponds to the number of third colors required in addition to the second color of the second electrodeposition layer 130 to the etching groove forming process and the etching groove by the etching process. It is preferably formed by a repeating process of the electrodeposition coating process of electrodeposition coating the color.

상기와 같이, 플라스틱 모재(100)에 전착코팅하고자하는 컬러의 수에 대응되도록 식각처리에 의한 식각홈 형성공정 및 식각홈에 컬러를 전착코팅시키는 전착코팅공정이 반복공정으로 이루어짐으로써 플라스틱 표면에 음각이나 양각이 아닌 동일평면상에서의 다양한 문양과 컬러가 구현될 수 있도록 다중컬러 전착코팅층을 형성시킬 수 있다.As described above, the etching groove forming process by etching treatment and the electrodeposition coating process of electrodeposition coating the color on the etching grooves are repeated so as to correspond to the number of colors to be electrodeposition coated on the plastic base material 100, thereby engraving the plastic surface. It is possible to form a multi-color electrodeposition coating layer so that a variety of patterns and colors on the same plane rather than embossed.

이상에서 본 발명의 구체적인 실시예를 상세히 설명하였으나, 본 발명은 이에 한정되는 것은 아니며, 이 분야의 통상의 지식을 가진 자라면 본 발명의 기술적 사상을 바탕으로 다양한 변경과 수정이 가능할 것이다.Although specific embodiments of the present invention have been described in detail above, the present invention is not limited thereto, and those skilled in the art may make various changes and modifications based on the technical idea of the present invention.

도 1은 본 발명에 따른 플라스틱 다중컬러 전착코팅방법의 단계별 공정을 나타낸 블록도.1 is a block diagram showing the step-by-step process of the plastic multi-color electrodeposition coating method according to the invention.

도 2는 본 발명에 따른 플라스틱 다중컬러 전착코팅방법의 단계별 공정을 통하여 플라스틱 모재의 일면에 도금층 및 전착층이 형성되는 상태를 나타낸 단면도.Figure 2 is a cross-sectional view showing a state in which the plating layer and the electrodeposition layer is formed on one surface of the plastic base material through a step-by-step process of the plastic multi-color electrodeposition coating method according to the present invention.

도 3은 본 발명에 따른 플라스틱 다중컬러 전착코팅층의 일 예를 나타낸 단면도.Figure 3 is a cross-sectional view showing an example of the plastic multi-color electrodeposition coating layer according to the present invention.

도 4는 본 발명에 따른 플라스틱 다중컬러 전착코팅층의 다른 예를 나타낸 단면도.Figure 4 is a cross-sectional view showing another example of a plastic multi-color electrodeposition coating layer according to the present invention.

<도면 주요부분에 대한 부호의 설명><Description of Symbols for Main Parts of Drawing>

100: 플라스틱 모재 110: 도금층100: plastic base material 110: plating layer

120: 제1 전착층 130: 제2 전착층120: first electrodeposition layer 130: second electrodeposition layer

140: 제3의 전착층140: third electrodeposition layer

Claims (5)

플라스틱 모재의 표면을 도금처리하는 제1 단계; A first step of plating the surface of the plastic base material; 상기 플라스틱 모재의 도금처리된 도금층에 제1 컬러를 전착시켜 제1 전착층을 생성하는 제2 단계; A second step of electrodepositing a first color on the plated plating layer of the plastic base material to generate a first electrodeposition layer; 상기 제1 전착층의 일부분에 레이저를 조사하여 상기 제1 전착층의 일부분을 식각하는 제3 단계; 그리고 Irradiating a portion of the first electrodeposition layer with a laser to etch a portion of the first electrodeposition layer; And 상기 레이저 조사에 의해 식각된 제1 전착층의 제1 식각홈에 제2 컬러를 전착시켜 제2 전착층을 생성하는 제4 단계를 포함하여 이루어진 플라스틱 다중컬러 전착코팅방법.And a fourth step of depositing a second color on the first etching groove of the first electrodeposition layer etched by the laser irradiation to generate a second electrodeposition layer. 제1항에 있어서, The method of claim 1, 상기 제1 전착층에 대하여 일부분이 재차 레이저를 이용한 식각처리가 되며, 식각처리된 상기 제1 전착층의 제2 식각홈에 제3의 컬러를 전착시켜 제3의 전착층을 생성하는 제5 단계를 더 포함하여 이루어짐을 특징으로 하는 플라스틱 다중컬러 전착코팅방법.A fifth step of partially etching the first electrodeposition layer using a laser, and electrodepositing a third color into a second etching groove of the first electrodeposition layer that has been etched to generate a third electrodeposition layer Plastic multi-color electrodeposition coating method characterized in that it further comprises a. 제2항에 있어서, The method of claim 2, 상기 제5 단계는 베이스 컬러로써 상기 도금층의 상면에 전체적으로 형성된 상기 제1 전착층과 동일평면상에 다양한 문양 및 컬러가 표현될 수 있도록 상기 제 2 전착층의 제2 컬러 외에 추가로 전착코팅하고자하는 컬러 수에 대응되어 다수 번 반복됨을 특징으로 하는 플라스틱 다중컬러 전착코팅방법.The fifth step is to be electrodeposition coating in addition to the second color of the second electrodeposition layer so that various patterns and colors can be expressed on the same plane as the first electrodeposition layer formed on the upper surface of the plating layer as a base color. Plastic multi-color electrodeposition coating method characterized in that repeated multiple times corresponding to the number of colors. 플라스틱 모재의 표면을 도금처리하여 형성된 도금층; A plating layer formed by plating the surface of the plastic base material; 상기 도금층의 상면 전체에 걸쳐 베이스 컬러인 제1 컬러로 전착되는 제1 전착층; 그리고 A first electrodeposition layer electrodeposited to a first color which is a base color over the entire upper surface of the plating layer; And 상기 제1 전착층의 소정의 면적에 대하여 레이저로 식각되며, 식각처리되어 형성된 제1 식각홈에 제2 컬러로 전착코팅되는 제2 전착층을 포함하여 이루어진 플라스틱 다중컬러 전착코팅층.A plastic multicolor electrodeposition coating layer comprising a second electrodeposition layer which is etched by a laser with respect to a predetermined area of the first electrodeposition layer and is electrodeposited and coated in a second color on a first etching groove formed by etching. 제4항에 있어서, The method of claim 4, wherein 상기 제1 전착층의 소정의 면적에 대하여 재차 레이저로 식각되며, 식각처리된 제2 식각홈에 제3의 컬러로 전착코팅되는 제3의 전착층을 더 포함하여 이루어짐을 특징으로 하는 플라스틱 다중컬러 전착코팅층.Plastic multi-colored, characterized in that further comprising a third electrodeposition layer which is etched again with a laser for the predetermined area of the first electrodeposition layer, the electrodeposition layer is electrodeposited and coated in a third color to the etched second etching groove. Electrodeposition coating layer.
KR1020080056639A 2008-06-17 2008-06-17 Plastic multi color electrodeposition coating method and multi color electrodeposition coating layers using the method KR20090130921A (en)