KR20080076596A - Manufacturing method for a gold nano coating hemp cloth - Google Patents
Manufacturing method for a gold nano coating hemp cloth Download PDFInfo
- Publication number
- KR20080076596A KR20080076596A KR1020070016739A KR20070016739A KR20080076596A KR 20080076596 A KR20080076596 A KR 20080076596A KR 1020070016739 A KR1020070016739 A KR 1020070016739A KR 20070016739 A KR20070016739 A KR 20070016739A KR 20080076596 A KR20080076596 A KR 20080076596A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- fabric
- hemp cloth
- parts
- burlap
- Prior art date
Abstract
Description
도 1은 본 발명에 의한 금나노로 코팅된 삼베원단의 제조방법을 보인 개략적인 공정도,1 is a schematic process diagram showing a manufacturing method of burlap fabric coated with gold nano according to the present invention,
도 2는 본 발명에 의한 삼베원단의 가공과정을 보인 개략적인 상태도.Figure 2 is a schematic state diagram showing the processing of burlap fabric according to the present invention.
< 도면의 주요 부분에 대한 부호의 설명 ><Description of Symbols for Main Parts of Drawings>
10: 압착롤러 20: 건조기10: pressing roller 20: dryer
22: 이동롤러22: moving roller
본 발명은 금나노로 코팅된 삼베원단의 제조방법에 관한 것으로, 보다 상세하게는 금나노 또는 은나노를 삼베원단에 분사방식으로 코팅시켜 유해파로부터의 접근을 차단하도록 하는 금나노로 코팅된 삼베원단의 제조방법에 관한 것이다.The present invention relates to a method of manufacturing a burlap fabric coated with gold nano, and more specifically, to the burlap fabric coated with gold nano or silver nano to the burlap fabric to block access from harmful waves It relates to a manufacturing method.
일반적으로 삼베(안동포)는 재배와 수확을 거쳐 삶기, 삼껍질 벗기기, 속껍질 분리, 삼째기, 삼삼기, 베나르기, 베메기, 꾸리베기, 베짜기, 세탁하기, 색내기, 마무리의 공정을 거쳐서 삼베를 완성하게 된다.In general, burlap (Andongpo) is cultivated and harvested through boiling, peeling, peeling, trimming, trimming, cutting, weaving, weaving, weaving, weaving, washing, coloring and finishing You will complete the burlap.
그리고 상기의 공정을 거쳐 완성된 삼베는 통상 의류와, 죽은 사람의 시신에 입히는 수의로 널리 사용되고 있다.And hemp, which has been completed through the above process, is commonly used for clothing and veterinary coating on the dead body.
또한, 삼베(안동포)는 섬유 자체에 항균 항독성을 갖고 있으므로 인하여 곰팡이와 벌레가 생기지 않고 잘 썩어서 흙으로 빨리 돌아갈 수 있는 것으로 알려져 있다. 더욱이, 상기 삼베는 예로부터 시신이 잘 유기되어 고인의 유골이 변색되지 않고 황골이 되어 동기감응(同氣感應)식으로 조상의 기가 후손에 전해짐으로써 후손들에게 번영과 평안을 이룰 수 있다고 전함에 따라 그 사용이 점차 증가하고 있는 추세이다.In addition, because burlap (Andongpo) has antimicrobial anti-toxicity to the fiber itself, it is known to be able to return to the soil quickly due to rotting without mold and insects. Moreover, since the burlap has been well-organized since ancient times, the bones of the deceased are not discolored, but become bones. Its use is gradually increasing.
상기와 같이 삼베로 만들어진 수의는 수분 흡수력과 항균기능이 있으나, 미생물 등에 의한 유골의 부패와 유해파의 침투로 인하여 유골이 변질되는 등 고인의 유골을 손쉽게 훼손시키게 되는 문제점이 있었다.Veterinary made of burlap as described above has the ability to absorb moisture and antibacterial, but there is a problem that the bones of the deceased easily deteriorated due to decay of the ashes and infiltration of harmful waves by microorganisms.
본 발명은 상기한 문제점을 해결하기 위하여 안출된 것으로, 본 발명의 목적은 음이온의 방출 및 항균, 탈취, 정화작용으로 유해물질을 외부로 방출함과 아울러 유해파의 차단으로 인체의 건강증진을 도모할 수 있으며, 수의로 제작하여 고인에게 입힌 경우 미생물 및 유해파의 접근을 미연에 차단하여 유골을 완벽하게 황골로 변색시킬 수 있는 금나노로 코팅된 삼베원단의 제조방법을 제공하는 데 있다.The present invention has been made to solve the above problems, the object of the present invention is to release the harmful substances to the outside by the release of negative ions and antibacterial, deodorant, purifying action and to promote the health of the human body by blocking harmful waves. It is possible to provide a method of manufacturing a burlap fabric coated with gold nanotubes that can completely discolor the ashes to the sternum by blocking the access of microorganisms and harmful waves in advance.
상기의 목적을 달성하기 위한 본 발명의 삼베원단은 물 100중량부에 밀가루 10~30중량부와 금색도료 1~5중량부를 투입한 후 균일하게 혼합시키면서 가열하여 풀을 제조하는 풀제조공정과; 물 100중량부에 금나노 1~5중량부 또는 은나노 1~10 중량부를 투입한 후 균일하게 혼합시켜 코팅물을 제조하는 코팅물 제조공정과; 일정 면적을 갖는 용기에 상기 밀가루풀을 투입한 후 일정 길이 및 폭을 갖는 삼베원단을 상기 용기에 침지시키면서 상기 풀을 삼베원단에 접착시켜 금색을 띄는 삼베원단으로 제조하는 원단착색공정과; 상기 공정에서 접착된 풀이 삼베원단의 표면에서 흐르거나 결집되지 않고 균일하게 도포되도록 롤링시켜 압착하는 제1가압공정과; 상기 가압공정을 통해 인출되는 삼베원단을 이송시키면서 50~60℃의 온도로 건조시키는 건조공정과; 상기 공정 후 풀의 결착력을 증대시키도록 재차 롤링시켜 압착하는 제2가압공정과; 상기 제2가압공정을 거친 가공된 원단에 상기 코팅물을 분무기를 이용하여 분사시켜 상기 원단의 표면에 도포시키는 코팅물 도포공정과; 상기 공정을 통해 코팅된 원단을 자연 건조시키는 건조공정을 통해 이루어지는 것을 특징으로 한다.The burlap fabric of the present invention for achieving the above object is a pool manufacturing process for producing a paste by heating 10 to 30 parts by weight of wheat flour and 1 to 5 parts by weight of gold paint to uniformly mixed with water; A coating preparation process of preparing a coating by uniformly mixing 1-5 parts by weight or 1-10 parts by weight of silver nano with 100 parts by weight of water; Putting the flour paste into a container having a predetermined area and then bonding the paste to the burlap fabric while immersing the burlap fabric having a predetermined length and width in the container to produce a burlap fabric having gold color; A first pressing step of rolling and compressing the glued glue in the process so that the glue is uniformly applied without flowing or gathering on the surface of the burlap fabric; A drying step of drying at a temperature of 50 to 60 ° C. while transferring the hemp fabric drawn out through the pressing step; A second pressing step of rolling and pressing again to increase the binding force of the pool after the step; A coating material coating process of spraying the coating material on the fabric subjected to the second pressing process by using a sprayer to apply the surface to the surface of the fabric; Characterized in that it is made through a drying process for naturally drying the coated fabric through the process.
이하, 첨부된 도면을 참조하여 본 발명의 금나노로 코팅된 삼베원단의 제조방법을 상세히 설명한다.Hereinafter, with reference to the accompanying drawings will be described in detail a manufacturing method of burlap fabric coated with gold nano of the present invention.
도1은 본 발명에 의한 금나노로 코팅된 삼베원단의 제조방법을 보인 개략적인 공정도이고, 도 2는 본 발명에 의한 삼베원단의 가공과정을 보인 개략적인 상태도이다.Figure 1 is a schematic process diagram showing a manufacturing method of burlap fabric coated with gold nano according to the present invention, Figure 2 is a schematic state diagram showing a processing process of burlap fabric according to the present invention.
상기 도면에 도시된 바와 같이, 본 발명의 바람직한 실시예에 의한 금나노로 코팅된 삼베원단의 제조방법은 물과, 물 100중량부 대비 밀가루 10~30중량부와 금색도료 1~5중량부를 투입한 후 균일하게 혼합시킨 후 가열하면서 밀가루풀을 제조 한다.As shown in the drawings, the manufacturing method of the burlap fabric coated with gold nano according to a preferred embodiment of the present invention is 10 to 30 parts by weight of flour and 1 to 5 parts by weight of gold paint relative to 100 parts by weight of water and water. After the homogeneous mixing, the flour paste is prepared while heating.
또한, 일정 크기의 용기에 물과, 물 100중량부 대비 금나노 1~5중량부 또는 은나노 1~10중량부를 투입한 후 균일하게 혼합시켜 코팅물을 제조한다.In addition, water and 1 to 5 parts by weight of gold nano or 1 to 10 parts by weight of silver nano to 100 parts by weight of water are added to a container of a predetermined size, and then uniformly mixed to prepare a coating.
이 후, 상기 밀가루풀을 일정 면적을 갖는 용기에 담은 후 일정 길이 및 폭을 갖는 삼베원단의 양면에 상기 밀가루풀이 접착되도록 일측에서 이송시켜 상기 용기에 침지시키면서 타측으로 이송시켜 상기 밀가루풀에 혼합된 금색도료가 상기 삼베원단에 접착되어 금색을 띄도록 제조한다. 그런 다음 이송된 삼베원단을 압착롤러(10)를 이용하여 압착하여 삼베원단의 표면에서 상기 밀가루풀이 흐르거나 결집되지 않고 균일하게 도포되게 한 후 건조기(20)로 이송시켜 50~60℃의 온도로 건조시킨다.Thereafter, the flour paste is contained in a container having a predetermined area and then transferred from one side to be bonded to both sides of the burlap fabric having a predetermined length and width so as to be immersed in the container and mixed with the flour pool. Gold paint is manufactured to adhere to the burlap fabric to have a gold color. Then, the transferred burlap fabric is compressed using a
상기 건조기(20)는 통상 섬유 등 직물지를 건조시키도록 내부에 상,하측으로 다수개의 이동롤러(22)가 구비된 것으로, 상기 이동롤러의 내부에 내장된 열선 또는 금속봉으로부터 발산되는 열에 의해 상기 삼베원단을 건조시키게 된다.The
상기 건조기(20)를 통해 건조되어 외부로 이송되면 상기 밀가루풀의 결착력을 증대시키도록 재차 롤링시켜 압착하면 된다.When it is dried through the
이 후, 가공된 상기 삼베원단에 상기 코팅물을 분무기를 이용하여 분사시키면서 상기 원단의 표면에 균일하게 도포시킨 다음 자연 건조시키면 된다.Thereafter, the coating is uniformly applied to the surface of the fabric while spraying the coating on the processed burlap fabric using an atomizer, and then naturally dried.
상기 금나노 또는 은나노는 수맥파의 차단효과가 우수할 뿐만 아니라 인체에 흡수된 노폐물을 제거하는 해독 작용과 피부정화 및 인체의 신진대사를 활성화시켜 에너지를 채워주는 것으로 알려져 있다.The gold nano or silver nano is known to fill energy by activating the detoxification and skin cleansing and metabolism of the human body as well as the blocking effect of the water wave, as well as to remove the waste absorbed by the human body.
[ [ 실시예Example ] ]
풀 및 Pool and 코팅물Coating 제조공정 Manufacture process
물과, 물 100중량부 대비 밀가루 10~30중량부와 금색도료 1~5중량부를 투입한 후 5~10분 동안 균일하게 혼합시킨 후 가열하면서 밀가루풀을 제조한다.Water and 10 to 30 parts by weight of wheat flour and 1 to 5 parts by weight of gold paint are added to 100 parts by weight of water, and then uniformly mixed for 5 to 10 minutes to prepare a flour paste while heating.
상기 밀가루풀의 제조시에는 온도가 너무 높지 않는 30~50℃의 낮은 온도에서 풀을 쑤도록 한다.When the flour paste is prepared, the paste is soaked at a low temperature of 30-50 ° C., the temperature of which is not too high.
또한, 코팅물은 일정 크기의 용기에 물과, 물 100중량부 대비 금나노 1~5중량부 또는 은나노 1~10중량부를 투입한 후 균일하게 혼합시켜 제조한다.In addition, the coating is prepared by uniformly mixing water and 1 to 5 parts by weight of gold nano or 1 to 10 parts by weight of silver nano to 100 parts by weight of water in a container of a predetermined size.
원단착색공정Fabric coloring process
일정 면적을 갖는 용기에 상기 밀가루풀을 투입시킨 상태에서 일정 길이 및 폭을 갖는 삼베원단을 상기 용기에 침지시키면서 상기 풀을 삼베원단에 접착시켜 금색을 띄는 삼베원단으로 제조한다.While the flour paste is put into a container having a predetermined area, the hemp fabric having a predetermined length and width is immersed in the container, and the paste is bonded to the hemp fabric to produce a gold burlap fabric.
이때, 상기 삼베원단은 롤러에 권취시킨 상태로 상기 용기의 일측에서 이송시켜 삼베원단의 양면에 상기 밀가루풀이 전체적으로 접착되도록 침지시킨 후 타측으로 이송시키면 되며, 이때 침지시간은 1~3초면 충분하다.At this time, the burlap fabric is transported from one side of the container in a wound state on the roller, so as to immerse the flour paste on both sides of the burlap fabric as a whole, and then transfer to the other side, the immersion time is enough 1 to 3 seconds.
제1가압공정1st pressure process
상기 밀가루풀이 접착된 후 삼베원단의 표면에서 흘러 내리거나 일측으로 결집되지 않고 균일하게 도포되도록 한쌍의 1차적으로 한쌍의 롤러를 이용하여 밀가루풀이 일정 두께로 접착되게 한 후, 2차적으로 가압하여 밀가루풀이 삼베원단의 표면에 압착되게 한다.After the flour paste is bonded, the flour paste is bonded to a certain thickness by using a pair of firstly a pair of rollers so as to be uniformly applied without flowing down from the surface of the burlap fabric or gathering to one side, and then pressurizing the flour secondly. The grass is pressed against the surface of the burlap fabric.
건조공정Drying process
가압된 삼베원단을 건조기 내부로 이송시켜 50~60℃의 온도로 건조시킨다.The pressurized burlap fabric is transferred to a dryer and dried to a temperature of 50 ~ 60 ℃.
이때, 상기 건조기 내부에는 내부에 열을 발산하도록 열선 또는 금속봉이 장착된 다수개의 이동롤러가 상,하측에 순차적으로 위치하고 있어 상기 삼베원단은 상기 이동롤러에 의해 상,하측으로 이송되면서 건조되게 된다.At this time, inside the dryer, a plurality of moving rollers equipped with a heating wire or a metal rod are sequentially positioned on the upper and lower sides so as to dissipate heat therein, and the burlap fabric is dried while being transported to the upper and lower sides by the moving roller.
여기서, 상기 열선 또는 금속봉은 외부에 구비된 열장치에 의해 동작되도록 연결되어 있다.Here, the heating wire or the metal rod is connected to be operated by a heat device provided outside.
제2가압공정Second press process
삼베원단의 표면에 접착된 밀가루풀의 결착력을 증대시키도록 재차 롤링시켜 압착한 후 타측에 구비된 롤러에 권취시킨다.Rolling and pressing again to increase the binding force of the flour paste adhered to the surface of the burlap fabric, it is wound on a roller provided on the other side.
코팅물Coating 도포 및 건조공정 Application and drying process
롤러에 권취된 가공된 삼베원단을 다시 권출시키면서 분무기를 이용하여 상기 코팅물을 상기 가공된 원단의 표면에 균일하게 도포시킨다.The coating is uniformly applied to the surface of the processed fabric using a sprayer while again unwinding the processed burlap fabric wound on a roller.
이 후, 코팅된 원단을 자연 건조시켜 삼베원단을 완성한다.Thereafter, the coated fabric is naturally dried to complete the burlap fabric.
상기와 같이 구성된 본 발명에 따르면, 저비용으로 단시간에 대량생산이 가능할 뿐만 아니라 적용분야가 광범위하여 제품 경쟁력을 향상시킬 수 있으며, 더욱이 인체에 흡수된 유해물질을 외부로 방출함과 동시에 수맥파 등의 유해파의 악영향으로부터 인체를 보호하여 심신을 안정시키고 인체의 건강을 증진시킬 수 있으며, 수의로 제작하여 고인에게 입힌 경우 미생물 및 유해파의 접근을 미연에 차단 하여 유골을 완벽하게 황골로 변색시킬 수 있는 장점이 있다.According to the present invention configured as described above, not only mass production can be performed in a short time at low cost, but also a wide range of applications can improve product competitiveness, and furthermore release harmful substances absorbed by the human body to the outside and at the same time harmful waves such as water wave It protects the human body from the bad effects of the body and stabilizes the mind and body and promotes the health of the human body.If it is manufactured by the veterinarian and it is applied to the deceased person, it can completely discolor the ashes by blocking the access of microorganisms and harmful waves. have.
Claims (1)