KR20080004184A - Antibacterial artificial marble composition having good sanding property - Google Patents
Antibacterial artificial marble composition having good sanding property Download PDFInfo
- Publication number
- KR20080004184A KR20080004184A KR1020060062876A KR20060062876A KR20080004184A KR 20080004184 A KR20080004184 A KR 20080004184A KR 1020060062876 A KR1020060062876 A KR 1020060062876A KR 20060062876 A KR20060062876 A KR 20060062876A KR 20080004184 A KR20080004184 A KR 20080004184A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- composition
- artificial marble
- size
- Prior art date
Abstract
Description
제1도는 비교실시예 1에 따라 제조된 인조대리석 제품의 사진을 나타낸 사진이다.1 is a photograph showing a photograph of the artificial marble product prepared according to Comparative Example 1.
제2도는 실시예 1에 따라 제조된 인조대리석 제품의 사진을 나타낸 사진이다.2 is a photograph showing a photograph of the artificial marble product prepared according to Example 1.
발명의 분야Field of invention
본 발명은 항균성 및 샌딩성이 우수한 인조대리석용 조성물에 관한 것이다. 보다 구체적으로, 본 발명은 아크릴계 인조대리석용 슬러리에 특정 크기의 자수정 분말을 첨가시킴으로써, 독특한 외관을 가질뿐만 아니라, 항균성 및 상온 원적외선 발산 효과가 우수하고 샌딩성이 향상된 인조 대리석 조성물에 관한 것이다. The present invention relates to a composition for artificial marble excellent in antibacterial and sanding properties. More specifically, the present invention relates to an artificial marble composition having a unique appearance by adding a specific size of amethyst powder to an acrylic artificial marble slurry, as well as having excellent antibacterial and room temperature far-infrared radiating effect and improved sanding properties.
발명의 배경Background of the Invention
인조대리석은 최근 건축 내장재로 많이 사용되고 있으며, 그 사용되는 베이스 레진(Base resin)에 따라 크게 아크릴계와 불포화 폴리에스터계의 두 가지 종류로 구분된다. 이 중 아크릴계 인조 대리석은 수지 자체의 은은한 투명성과 고급스러운 질감 및 우수한 내후성 등의 장점으로 인해 여러 가지 용도로 사용되고 있으며, 그 수요가 계속 증가하고 있다.Artificial marble is widely used as a building interior material in recent years, depending on the base resin (base resin) used is largely divided into two types of acrylic and unsaturated polyester. Among them, acrylic artificial marble is used for various purposes due to its soft transparency, luxurious texture, and excellent weather resistance, and its demand is continuously increasing.
예를 들면, 씽크대 상판, 세면 화장대의 상판, 은행 및 일반 매장의 접수대 등 각종 카운터의 상판, 내벽재, 각종 인테리어 조형물 등의 소재로서 그 사용이 확대되고 있다.For example, its use is being expanded as a material for counter tops, interior walls, various interior sculptures, such as sink tops, vanity tops, banks and reception desks in general stores.
그러나, 지금까지 개발되어온 인조대리석 소재는 천연 대리석에 가까운 질감을 내는 데에만 치중하였을 뿐, 건강 기능을 부여하는 것과는 무관하였다. However, the artificial marble material that has been developed so far has focused only on the texture of natural marble, and has been irrelevant to imparting a health function.
따라서 인조대리석 조성물에 황토나 옥 등을 첨가하여 건강 기능을 향상시키는 방법이 개발되었으며, 본 발명자는 국내특허출원 제2004-103498호 및 제2005-118547호로 출원한 바 있다. 그러나, 황토나 옥 등을 첨가할 경우, 상온에서 원적외선 발산 효과가 미약한 단점이 있다. Therefore, a method of improving the health function has been developed by adding ocher or jade to the artificial marble composition, and the present inventors have filed in Korean Patent Application Nos. 2004-103498 and 2005-118547. However, when adding ocher or jade, there is a disadvantage that the far-infrared divergence effect at room temperature is weak.
일반적으로 자수정은 몸에 좋은 원적외선이 상온에서도 다량 방출되어 미국, 일본, 독일 등 선진국 의학연구소에서도 이미 대체의학으로 활용되어 왔으며, 근래 웰빙화의 추세에 따라 자수정이 첨가된 제품에 대하여 선호도가 점점 증가하고 있다. In general, amethyst has a large amount of far-infrared rays, which are good for the body, and has been used as an alternative medicine in medical research centers in developed countries such as the US, Japan, and Germany. Doing.
따라서 상판, 내벽재, 각종 인테리어 조형물 등의 소재로 사용되고 있는 인조대리석에 자수정을 첨가시킬 경우, 보다 다양한 소비자의 욕구에 부응할 수 있을 것으로 기대되지만, 자수정과 수지 매트릭스와의 상용성, 공정 안정성 등으로 인해 인조대리석 본래의 샌딩성을 유지하는 제품의 개발은 아직까지 미미한 실정이다. Therefore, when amethyst is added to artificial marble, which is used for materials such as top plate, inner wall material, and various interior sculptures, it is expected to meet various consumer needs, but compatibility with amethyst and resin matrix, process stability, etc. Due to the development of a product that maintains the original sanding of artificial marble is still insignificant.
국내 공개특허 제2005-82279호에서는 자수정분말과 불포화폴리에스테르 수지를 혼합하여 형성된 자수정 욕조를 개시하고 있다. 그러나, 인조대리석 슬러리 수지 시럽에 자수정 분말을 첨가시킬 경우, 슬러리 점도의 급격한 변화로 공정 제어가 어렵고, 최종 제품에 있어서 페이퍼 샌딩이 안되는 문제점이 있다. 특히, 수지 시럽이 아크릴계 수지일 경우, 점도 변화 현상은 더욱 심각하다. Korean Patent Laid-Open Publication No. 2005-82279 discloses an amethyst bath formed by mixing an amethyst powder and an unsaturated polyester resin. However, when the amethyst powder is added to the artificial marble slurry resin syrup, it is difficult to control the process due to a sudden change in the viscosity of the slurry, and paper sanding is not possible in the final product. In particular, when the resin syrup is an acrylic resin, the viscosity change phenomenon is more serious.
따라서 본 발명자는 상기의 문제점을 해결하기 위하여 아크릴계 인조대리석용 조성물에 특정 크기의 자수정 분말을 특정한 함량으로 첨가시킴으로써, 원적외선 방출효과와 항균 및 탈취기능은 물론, 샌딩성이 뛰어난 인조대리석용 조성물을 개발하기에 이른 것이다. Therefore, the present inventors add a specific size of amethyst powder to the acrylic artificial marble composition in order to solve the above problems, to develop a composition for artificial marble excellent in the far-infrared emission effect and antibacterial and deodorizing function, as well as sanding properties It was early.
본 발명의 목적은 항균 및 탈취기능이 우수한 인조 대리석 조성물을 제공하기 위한 것이다.An object of the present invention is to provide an artificial marble composition excellent in antibacterial and deodorizing function.
본 발명의 다른 목적은 원적외선 방출효과가 우수한 인조 대리석 조성물을 제공하기 위한 것이다.Another object of the present invention is to provide an artificial marble composition having excellent far-infrared emission effect.
본 발명의 또 다른 목적은 샌딩성이 뛰어난 인조 대리석 조성물을 제공하기 위한 것이다.Another object of the present invention is to provide an artificial marble composition having excellent sanding properties.
본 발명의 또 다른 목적은 기계적 물성이 우수한 인조 대리석 조성물을 제공하기 위한 것이다.Still another object of the present invention is to provide an artificial marble composition having excellent mechanical properties.
본 발명의 또 다른 목적은 아크릴계 인조대리석의 투명성을 유지하면서 독특한 외관을 갖는 인조 대리석 조성물을 제공하기 위한 것이다.Another object of the present invention is to provide an artificial marble composition having a unique appearance while maintaining the transparency of acrylic artificial marble.
본 발명의 상기 목적 및 기타의 목적들은 하기 설명되는 본 발명에 의해 모두 달성될 수 있다. The above and other objects of the present invention can be achieved by the present invention described below.
이하, 본 발명의 내용을 하기에 상세히 설명한다.Hereinafter, the content of the present invention will be described in detail below.
발명의 요약Summary of the Invention
본 발명의 항균성 및 샌딩성이 우수한 인조대리석용 조성물은 (a) 아크릴 수지 시럽 100 중량부; (b) 5∼90 ㎛ 입자 크기를 갖는 자수정 분말 1 내지 20 중량부; (c) 무기 충전물 100 내지 200 중량부; 및 (d) 중합 개시제 0.1 내지 10 중량부로 이루어진다. The composition for artificial marble having excellent antibacterial and sanding properties of the present invention comprises: (a) 100 parts by weight of an acrylic resin syrup; (b) 1 to 20 parts by weight of amethyst powder having a particle size of 5 to 90 μm; (c) 100 to 200 parts by weight of the inorganic filler; And (d) 0.1 to 10 parts by weight of the polymerization initiator.
본 발명의 하나의 구체예에서는 상기 조성물은 0.1∼5 mm 크기의 인조대리석 분쇄물 0.1 내지 150 중량부를 더 포함할 수 있다.In one embodiment of the present invention, the composition may further comprise 0.1 to 150 parts by weight of artificial marble crushed to the size of 0.1 to 5 mm.
본 발명의 다른 구체예에서는 상기 조성물은 실란계 커플링제 1 내지 30 중량부를 더 포함할 수 있다.In another embodiment of the present invention, the composition may further include 1 to 30 parts by weight of the silane coupling agent.
본 발명의 또 다른 구체예에서는 상기 조성물은 나노 입자 크기의 은 항균제 0.01 내지 5 중량부를 더 포함할 수 있다.In another embodiment of the present invention, the composition may further comprise 0.01 to 5 parts by weight of the silver antimicrobial agent of the nanoparticle size.
본 발명의 또 다른 구체예에서는 상기 조성물은 폴리헥실메틸렌 구아니딘 포스파이트 0.01 내지 3 중량부를 더 포함할 수 있다.In another embodiment of the present invention the composition may further comprise 0.01 to 3 parts by weight of polyhexylmethylene guanidine phosphite.
본 발명의 또 다른 구체예에서는 상기 조성물은 에틸렌글리콜디메타아크릴레이트, 프로필렌글리콜디메타아크릴레이트, 글리세롤트리메타아크릴레이트, 디펜타에리트리롤헥사메타아크릴레이트, 트리메틸올프로판 트리메타아크릴레이트 및 이들의 혼합물로 이루어진 군으로부터 선택되는 아크릴계 다관능성 모노머를 0.1 내지 30 중량부 더 포함할 수 있다.In another embodiment of the present invention the composition is ethylene glycol dimethacrylate, propylene glycol dimethacrylate, glycerol trimethacrylate, dipentaerythrol hexamethacrylate, trimethylolpropane trimethacrylate and these It may further comprise 0.1 to 30 parts by weight of an acrylic polyfunctional monomer selected from the group consisting of a mixture.
본 발명의 항균성 및 샌딩성이 우수한 인조대리석은 아크릴 수지 시럽, 무기 충전물 및 중합 개시제로 이루어진 슬러리에 5∼90 ㎛ 크기의 자수정 분말을 혼합하고; 그리고 상기 자수정 분말이 혼합된 혼합물을 경화시키는 단계로 제조된다. The artificial marble having excellent antibacterial and sanding properties of the present invention is mixed with an amethyst powder having a size of 5 to 90 μm in a slurry composed of an acrylic resin syrup, an inorganic filler and a polymerization initiator; And it is prepared by the step of curing the mixture in which the amethyst powder is mixed.
이하, 본 발명의 각 성분을 하기에 상세히 설명한다. Hereinafter, each component of this invention is demonstrated in detail below.
(a) 아크릴 수지 시럽 (a) acrylic resin syrup
본 발명에 사용되는 아크릴 수지 시럽은 아크릴계 단량체와 이들의 중합물인 폴리아크릴레이트가 용해되어 있는 수지 시럽이다. The acrylic resin syrup used in the present invention is a resin syrup in which an acrylic monomer and a polyacrylate which is a polymer thereof are dissolved.
상기 아크릴계 단량체로는 메틸 메타아크릴레이트, 에틸 메타아크릴레이트, 이소 프로필 메타아크릴레이트, n-부틸 메타아크릴레이트, 2-에틸 헥실 메타아크릴레이트 등이 있다. The acrylic monomers include methyl methacrylate, ethyl methacrylate, isopropyl methacrylate, n-butyl methacrylate, 2-ethyl hexyl methacrylate, and the like.
본 발명의 아크릴 수지 시럽은 아크릴 단량체의 함량이 65 내지 99 중량%, 폴리아크릴레이트 함량이 1 내지 35 중량%인 것이 바람직하다.The acrylic resin syrup of the present invention preferably has an acrylic monomer content of 65 to 99% by weight and a polyacrylate content of 1 to 35% by weight.
(b) 자수정 분말(b) amethyst powder
본 발명의 인조대리석 조성물은 특정 크기의 자수정 분말을 첨가시킴으로써, 항균성 및 원적외선 발산효과와 함께 샌딩성을 향상시킨다. Artificial marble composition of the present invention by adding a specific size of the amethyst powder, to improve the sanding properties with antibacterial and far-infrared divergence effect.
일반적으로 자수정은 동의보감에 "마음을 안정시키고 피부를 곱게하고 아기를 잉태하지 못하는 것을 다스린다"라고 기재되어 있으며, 몸에 좋은 원적외선이 다량 방출되어 대체의학으로 활용되어 왔다. 따라서, 건축내외장재나 인테리어 소재로 다양하게 활용되고 있는 인조대리석용 조성물에 자수정 분말을 첨가사킬 경우, 건강 증진에 효과적일 것이다. In general, amethyst is described in the synonym as "stable mind, fine skin, and govern the inability to conceive a baby," and has been used as an alternative medicine because a large amount of far-infrared rays are released to the body. Therefore, when amethyst powder is added to the composition for artificial marble, which is widely used as a building interior or exterior material or interior material, it will be effective in promoting health.
그런데, 상기 자수정 분말이 아크릴계 인조대리석 슬러리에 첨가될 경우, 슬러리 점도에 급격한 변화를 일으켜 공정 제어에 문제점이 있고, 최종 제품의 샌딩성에 있어서도 샌딩이 잘 안되는 단점이 있다. 따라서 본 발명에서는 자수정 분말의 입자 크기를 약 5∼90 ㎛ 로 제한한다. 만일 입자 크기가 5 ㎛ 미만일 경우, 슬러리 점도가 지나치게 상승하여 공정에 어려움이 있고, 90 ㎛를 초과할 경우, 슬러리 점도가 저하되어 공정 제어가 어렵고 최종 제품의 샌딩성을 저하와 함께 기계적 물성을 떨어뜨린다. However, when the amethyst powder is added to the acrylic artificial marble slurry, there is a problem in controlling the process by causing a sudden change in the slurry viscosity, and there is a disadvantage in that sanding is not good even in sanding properties of the final product. Therefore, in the present invention, the particle size of the amethyst powder is limited to about 5 to 90 μm. If the particle size is less than 5 μm, the slurry viscosity is excessively increased, so that the process is difficult. If the particle size is more than 90 μm, the slurry viscosity is lowered, making it difficult to control the process. Drop.
본 발명에서 자수정 분말의 바람직한 함량은 아크릴 수지 시럽 100 중량부에 대하여 약 1 내지 20 중량부로 사용되며, 보다 바람직하게는 약 5∼15 중량부로 사용한다. In the present invention, the preferred amount of amethyst powder is used in an amount of about 1 to 20 parts by weight, and more preferably about 5 to 15 parts by weight, based on 100 parts by weight of the acrylic resin syrup.
자수정 분말이 20 중량부를 초과할 경우, 대리석의 기계적 물성이 저하되며, 1 중량부 미만으로 사용할 경우, 원적외선 방출 및 항균 효과가 미미하다.If the amethyst powder is more than 20 parts by weight, the mechanical properties of the marble is lowered, and when used less than 1 part by weight, the far-infrared emission and antibacterial effect is insignificant.
(c) 무기 충전물(c) inorganic filler
본 발명의 무기 충전물은 탄산칼슘, 수산화 알루미늄, 실리카, 알루미나, 유산바륨, 수산화 마그네슘과 같이 당 분야에서 통상적으로 사용되는 무기 분말 중 어느 것도 사용 가능하며, 약 1 내지 100 ㎛의 크기를 갖는 것이 바람직하다. The inorganic filler of the present invention may be any of inorganic powders commonly used in the art, such as calcium carbonate, aluminum hydroxide, silica, alumina, barium lactate, magnesium hydroxide, and preferably has a size of about 1 to 100 μm. Do.
상기 무기 분말 중 특히, 수산화 알루미늄은 투명하고 미려한 대리석 형상의 외관을 갖는 인조대리석을 제조 할 수 있다는 점에서 바람직하다.Among the inorganic powders, aluminum hydroxide is particularly preferable in that it can produce artificial marble having a transparent and beautiful marble appearance.
본 발명의 무기 충전물의 혼합비는 아크릴 수지 시럽 100 중량부를 기준으로 무기 충전물이 약 100∼200 중량부, 더욱 바람직하기로는 약 120∼160 중량부로 첨가되는 것이 바람직하다. 만일 무기충전물의 함량이 200 중량부를 초과할 경우, 투명성이 저하되고 슬러리 비중이 증가하여 공정에 문제점이 있다. 또한 100 중량부 미만으로 사용될 경우, 인조대리석 분쇄물 등의 침강현상이 발생된다. The mixing ratio of the inorganic filler of the present invention is preferably about 100 to 200 parts by weight, more preferably about 120 to 160 parts by weight, based on 100 parts by weight of the acrylic resin syrup. If the content of the inorganic filler exceeds 200 parts by weight, transparency is reduced and the specific gravity of the slurry is increased, there is a problem in the process. In addition, when used in less than 100 parts by weight, sedimentation of artificial marble pulverization occurs.
(d) 중합 개시제(d) polymerization initiator
본 발명의 중합 개시제로는 벤조일 퍼옥사이드, 라우로일 퍼옥사이드, 부틸 하이드로 퍼옥사이드, 큐밀 하이드로 퍼옥사이드 등의 과산화물 또는 아조비스이소부틸로니트릴과 같은 아조 화합물을 사용한다.As the polymerization initiator of the present invention, peroxides such as benzoyl peroxide, lauroyl peroxide, butyl hydroperoxide, cumyl hydroperoxide, or azo compounds such as azobisisobutylonitrile are used.
상기 중합개시제의 함량은 아크릴 수지 시럽 100 중량부 기준으로 약 0.1∼ 10 중량부가 바람직하다. 상기 범위를 벗어날 경우, 경화가 되지 않거나 급격한 반응으로 경화되어 판재상태에 굴곡이 생기는 문제점이 있다. The content of the polymerization initiator is preferably about 0.1 to 10 parts by weight based on 100 parts by weight of the acrylic resin syrup. If it is out of the above range, there is a problem that the curvature is not cured or cured by a rapid reaction occurs in the plate state.
인조대리석 분쇄물Artificial Marble Crush
본 발명에서는 다양한 색상을 갖는 인조대리석 분쇄물을 선택적으로 첨가할 수 있다. 상기 인조대리석 분쇄물은 약 0.1∼10 mm의 크기를 가지며, 통상의 방법으로 제조된다. 예컨대, 아크릴 수지 시럽 100 중량부에 대하여, 무기 충전물 약 120 내지 200 중량부, 가교제 약 0.1 내지 10 중량부 및 개시제 약 0.1 내지 10 중량부를 혼합, 경화한 다음, 이를 파쇄하여 제조된다. In the present invention, artificial marble pulverized powder having various colors may be selectively added. The artificial marble pulverized product has a size of about 0.1 to 10 mm, and is manufactured by a conventional method. For example, based on 100 parts by weight of the acrylic resin syrup, about 120 to 200 parts by weight of the inorganic filler, about 0.1 to 10 parts by weight of the crosslinking agent and about 0.1 to 10 parts by weight of the initiator are mixed and cured, and then crushed.
상기 인조대리석 분쇄물의 혼합비는 아크릴 수지 시럽 100 중량부를 기준으로 약 0.1∼150 중량부가 사용되며, 다양한 패턴을 구현할 수 있다. The mixing ratio of the artificial marble crushed is about 0.1 to 150 parts by weight based on 100 parts by weight of the acrylic resin syrup, it can implement a variety of patterns.
실란계 커플링제Silane Coupling Agent
본 발명에서 실란계 커플링제는 수지와 자수정간 화학적 결합을 발생시켜 기계적 강도의 향상 효과를 기대할 수 있다. In the present invention, the silane coupling agent may generate a chemical bond between the resin and the amethyst, thereby improving the mechanical strength.
상기 실란계 커플링제로는 3-(트리메톡시실릴)프로필메타아크릴레이트, 비닐트리메톡시실란, 비닐트리에톡시실란 등이 사용될 수 있다. As the silane coupling agent, 3- (trimethoxysilyl) propylmethacrylate, vinyltrimethoxysilane, vinyltriethoxysilane, or the like may be used.
상기 실란계 커플링제는 아크릴 수지 시럽 100 중량부를 기준으로 하여 약 1-30 중량부로 사용된다. The silane coupling agent is used at about 1-30 parts by weight based on 100 parts by weight of the acrylic resin syrup.
나노 입자 크기의 은 항균제Nanoparticle sized silver antimicrobial
본 발명에서 나노 입자 크기의 은 항균제는 90% 이상의 은으로 이루어진 물질이며 더욱 바람직하게는 95%이상 은으로 이루어진 물질로, 나노 입자 크기로 이루어져 있다. 본 발명의 은 항균제의 입자 크기는 약 1∼200 nm 이다.Silver antimicrobial agent of the nanoparticle size in the present invention is a material consisting of more than 90% silver and more preferably made of a material consisting of more than 95% silver, nanoparticle size. The particle size of the silver antibacterial agent of the present invention is about 1 to 200 nm.
본 발명에서는 나노 입자 크기의 은 항균제를 사용함으로써, 항세균성을 더욱 강화하는 것과 동시에 수지의 물성 저하 현상을 크게 개선할 수 있다.In the present invention, by using the silver particle antimicrobial agent of the nanoparticle size, it is possible to further enhance the antibacterial properties, and to significantly improve the physical property degradation of the resin.
본 발명에서 상기 나노 입자 크기의 은 항균제는 전체 수지 조성물 100 중량부에 대하여 약 0.01 내지 5 중량부로 사용된다.In the present invention, the nanoparticle sized silver antimicrobial agent is used at about 0.01 to 5 parts by weight based on 100 parts by weight of the total resin composition.
폴리헥실메틸렌 구아니딘 포스파이트Polyhexylmethylene guanidine phosphite
상기 폴리헥실메틸렌 구아니딘 포스파이트는 항균 효과를 더욱 향상시키기 위하여 더 첨가할 수 있다. 본 발명에서는 상기 폴리헥실메틸렌 구아니딘 포스파이트는 아크릴 수지 시럽 100 중량부에 대하여 약 0.01 내지 3 중량부의 범위에서 사용된다. 만일 3 중량부를 초과할 경우, 인조대리석 경화시 변색이 일어날 수 있다. The polyhexylmethylene guanidine phosphite may be further added to further improve the antibacterial effect. In the present invention, the polyhexylmethylene guanidine phosphite is used in the range of about 0.01 to 3 parts by weight based on 100 parts by weight of the acrylic resin syrup. If it exceeds 3 parts by weight, discoloration may occur during hardening of artificial marble.
아크릴계 다관능성 모노머Acrylic Polyfunctional Monomer
본 발명의 아크릴계 다관능성 모노머의 구체적인 예로는 에틸렌글리콜디메타아크릴레이트, 프로필렌글리콜디메타아크릴레이트, 글리세롤트리메타아크릴레이트, 디펜타에리트리롤헥사메타아크릴레이트, 트리메틸올프로판 트리메타아크릴레이트 등을 들 수 있다. 상기 아크릴계 다관능성 모노머는 2종 이상 혼합하여 사용할 수 있다. Specific examples of the acrylic polyfunctional monomer of the present invention include ethylene glycol dimethacrylate, propylene glycol dimethacrylate, glycerol trimethacrylate, dipentaerythrol hexamethacrylate, trimethylolpropane trimethacrylate, and the like. Can be mentioned. Two or more types of said acryl-type polyfunctional monomer can be used in mixture.
상기 아크릴계 다관능성 모노머는 아크릴 수지 시럽 100 중량부를 기준으로 약 0.1 내지 30 중량부로 첨가한다. 만일 30 중량부를 초과할 경우, 최종 대리석 제품에 크랙이 쉽게 발생하는 문제점이 있다.The acrylic polyfunctional monomer is added at about 0.1 to 30 parts by weight based on 100 parts by weight of the acrylic resin syrup. If it exceeds 30 parts by weight, there is a problem that cracks easily occur in the final marble product.
본 발명에서는 상기 구성성분 외에도 난연제, 대전방지제, 안료 및 또는 염료를 더 포함할 수 있다. In addition to the above components, the present invention may further include a flame retardant, an antistatic agent, a pigment, and / or a dye.
본 발명의 인조 대리석은 아크릴 수지 시럽, 무기 충전물 및 중합 개시제로 이루어진 슬러리에 5∼90 ㎛ 크기의 자수정 분말을 혼합하고; 그리고 상기 자수정 분말이 혼합된 혼합물을 경화시키는 단계로 제조된다. The artificial marble of the present invention is mixed with an amethyst powder having a size of 5 to 90 μm in a slurry composed of an acrylic resin syrup, an inorganic filler and a polymerization initiator; And it is prepared by the step of curing the mixture in which the amethyst powder is mixed.
본 발명은 하기의 실시예에 의하여 보다 더 잘 이해될 수 있으며, 하기의 실시예는 본 발명의 예시 목적을 위한 것이며 첨부된 특허 청구 범위에 의하여 한정되는 보호범위를 제한하고자 하는 것은 아니다.The invention can be better understood by the following examples, which are intended for the purpose of illustration of the invention and are not intended to limit the scope of protection defined by the appended claims.
실시예 1Example 1
30 %의 폴리메틸 메타아크릴레이트와 70 %의 메틸메타아크릴레이트의 혼합물로 이루어진 메틸메타아크릴레이트 시럽(이하, 수지 시럽으로 칭함) 100 중량부, 수산화 알루미늄 150 중량부 및 벤조일 퍼옥사이드 2 중량부에 10 ㎛크기의 자수정 분말 10 중량부를 혼합하여 인조대리석 슬러리를 제조하였다. 상기 슬러리를 300×600×15 ㎜의 유리 성형 셀에 뿌린 후 45 ℃ 열풍오븐에 넣고, 단계적으로 오븐의 온도를 100 ℃ 까지 올려 경화를 시켰다. 경화가 완료된 후 상온까지 냉각하여 평판상의 인조대리석판을 얻었다. 제조된 인조대리석판에 대하여 원적외선 방출량, 항균성, 충격강도, 투명성 및 샌딩성에 대하여 측정하였으며 최종 제품의 사진은 도 2에 나타내었다. 100 parts by weight of methylmethacrylate syrup (hereinafter referred to as resin syrup) consisting of a mixture of 30% polymethyl methacrylate and 70% methylmethacrylate, 150 parts by weight of aluminum hydroxide and 2 parts by weight of benzoyl peroxide An artificial marble slurry was prepared by mixing 10 parts by weight of a 10 μm-sized amethyst powder. The slurry was sprayed into a glass molding cell of 300 × 600 × 15 mm and then placed in a 45 ° C. hot air oven, and the oven temperature was raised to 100 ° C. in step to cure. After curing was completed, the mixture was cooled to room temperature to obtain a plate-like artificial marble plate. Far-infrared emission, antimicrobial activity, impact strength, transparency and sanding properties of the manufactured artificial slabs were measured and the photographs of the final products are shown in FIG. 2.
실시예 2Example 2
80 ㎛크기의 자수정 분말을 20 중량부 사용하고 비닐트리메톡시실란 5 중량부를 첨가한 것을 제외하고는 상기 실시예 1과 동일하게 수행하였다. The same procedure as in Example 1 was carried out except that 20 parts by weight of 80 μm-size amethyst powder was used and 5 parts by weight of vinyltrimethoxysilane was added.
실시예 3Example 3
100 nm의 은나노 입자 5 중량부를 더 첨가한 것을 제외하고는 상기 실시예 1과 동일하게 수행하였다. The same process as in Example 1 was performed except that 5 parts by weight of silver nanoparticles having a thickness of 100 nm was further added.
실시예 4Example 4
에틸렌글리콜디메타아크릴레이트 5 중량부를 더 첨가한 것을 제외하고는 상기 실시예 1과 동일하게 수행하였다. The same procedure as in Example 1 was carried out except that 5 parts by weight of ethylene glycol dimethacrylate was further added.
실시예 5Example 5
폴리헥실메틸렌 구아니딘 포스파이트 3 중량부를 더 첨가한 것을 제외하고는 상기 실시예 1과 동일하게 수행하였다. The same procedure as in Example 1 was repeated except that 3 parts by weight of polyhexylmethylene guanidine phosphite was added.
비교실시예 1Comparative Example 1
자수정 분말을 사용하지 않은 것을 제외하고는 상기 실시예 1과 동일하게 수행하였다. 최종 제품의 사진은 도 1에 나타내었다. The same procedure as in Example 1 was conducted except that no amethyst powder was used. A photograph of the final product is shown in FIG. 1.
비교실시예 2Comparative Example 2
자수정 분말을 사용하지 않고 폴리헥실메틸렌 구아니딘 포스파이트 3 중량부를 첨가한 것을 제외하고는 상기 실시예 1과 동일하게 수행하였다. The same procedure as in Example 1 was performed except that 3 parts by weight of polyhexylmethylene guanidine phosphite was added without using an amethyst powder.
비교실시예 3Comparative Example 3
100 ㎛ 크기의 자수정 분말을 사용한 것을 제외하고는 상기 실시예 1와 동일하게 수행하였다. The same procedure as in Example 1 was carried out except for the use of an amethyst powder having a size of 100 μm.
비교실시예 4Comparative Example 4
1 mm 크기의 자수정 분말을 사용한 것을 제외하고는 상기 실시예 1와 동일하게 수행하였다.The same procedure as in Example 1 was conducted except that a 1 mm size amethyst powder was used.
상기 제조된 제품에 대한 물성 평가는 하기의 방법으로 수행하였다. Evaluation of physical properties of the prepared product was performed by the following method.
(1) 원적외선 방출량: 상온에서 FT-IR Spectrometer기기를 이용하여 측정하였으며, BLACK BODY 대비하여 평가하였다.(1) Far-infrared emission amount: Measured using an FT-IR Spectrometer at room temperature, and evaluated in comparison with the BLACK BODY.
(2) 항균성 : KFIA-FI-1003방법에 의해 측정하였다.(2) Antibacterial: Measured by KFIA-FI-1003 method.
(3) 충격강도: ASTM D-256에 따라 IZOD 충격강도를 측정하였다. (3) Impact strength: IZOD impact strength was measured according to ASTM D-256.
(4) 투명성 : 일반제품 대비 육안으로 평가하였다.(4) Transparency: Evaluated visually compared to general products.
(5) 샌딩성 : 샌드페이퍼를 이용하여 작업성으로 평가하였다.(5) Sanding property: Workability was evaluated using the sand paper.
본 발명의 특정 입경 크기의 자수정 분말을 함유한 인조 대리석은 항균 및 탈취기능과 원적외선 방출효과가 우수하고, 샌딩성이 뛰어나며, 기계적 물성이 우수하고, 아크릴계 인조대리석의 투명성을 유지하면서 독특한 외관을 갖는 인조 대리석 조성물을 제공하는 발명의 효과를 갖는다.Artificial marble containing amethyst powder of specific particle size of the present invention has excellent antibacterial and deodorizing function and far-infrared ray emission effect, excellent sanding property, excellent mechanical properties, and having a unique appearance while maintaining the transparency of acrylic artificial marble. It has the effect of providing the artificial marble composition.
본 발명의 단순한 변형 내지 변경은 이 분야의 통상의 지식을 가진 자에 의하여 용이하게 실시될 수 있으며, 이러한 변형이나 변경은 모두 본 발명의 영역에 포함되는 것으로 볼 수 있다.Simple modifications or changes of the present invention can be easily carried out by those skilled in the art, and all such modifications or changes can be seen to be included in the scope of the present invention.
Claims (7)