KR20070026745A - Cosmetic Sponges Containing Ocher and Manufacturing Method Thereof - Google Patents
Cosmetic Sponges Containing Ocher and Manufacturing Method Thereof Download PDFInfo
- Publication number
- KR20070026745A KR20070026745A KR1020070015120A KR20070015120A KR20070026745A KR 20070026745 A KR20070026745 A KR 20070026745A KR 1020070015120 A KR1020070015120 A KR 1020070015120A KR 20070015120 A KR20070015120 A KR 20070015120A KR 20070026745 A KR20070026745 A KR 20070026745A
- Authority
- KR
- South Korea
- Prior art keywords
- ocher
- mixing
- weight
- sponge
- mold
- Prior art date
Abstract
Description
도 1은 본 발명의 실시예에 의한 황토를 함유한 화장용 스폰지의 제조방법을 설명하는 순서도,1 is a flow chart illustrating a method of manufacturing a cosmetic sponge containing ocher according to an embodiment of the present invention,
도 2는 본 발명의 실시예에 의한 황토를 함유한 화장용 스폰지의 원적외선 시험성적을 도시한 그래프로서, 원적외선 파장에 대한 방사에너지의 그래프,Figure 2 is a graph showing the far-infrared test results of the ocher-containing cosmetic sponge according to an embodiment of the present invention, a graph of the radiation energy with respect to the far infrared wavelength,
도 3은 본 발명의 실시예에 의한 황토를 함유한 화장용 스폰지의 원적외선 시험성적을 도시한 그래프로서, 원적외선 파장에 대한 방사율의 그래프이다.Figure 3 is a graph showing the far-infrared test results of the ocher-containing cosmetic sponge according to an embodiment of the present invention, a graph of the emissivity with respect to the far infrared wavelength.
본 발명은 황토를 함유한 화장용 스폰지 및 그 제조방법에 관한 것으로서, 특히 황토에서 원적외선을 방사하여 항균 및 살균작용이 있고, 다공이 균일하게 형성되어 있음과 동시에, 화장품의 사용감도를 증대시킬 수 있는 황토를 함유한 화장용 스폰지 및 그 제조방법에 관한 것이다.The present invention relates to a cosmetic sponge containing ocher and a method for manufacturing the same, in particular, it has antibacterial and bactericidal action by radiating far-infrared rays from ocher, and evenly forms pores and can increase the usability of cosmetics. The present invention relates to a cosmetic sponge containing loess and a method for producing the same.
일반적으로 황토는 인체와 환경에 유익한 미생물이 다량 포함되어 있어 집안의 곰팡이 등의 서식을 억제시켜 쾌적한 주거환경을 제공함은 물론이고, 각종 병균의 살균작용에 의해 병균의 전염을 방지하며, 강한 원적외선의 방사열과 침투력에 의해 인체의 말초 모세혈관의 운동이 활발해지면서 혈액순환을 순조롭게 촉진시켜 건강한 생활을 영위할 수 있는 작용을 한다.In general, ocher contains a large amount of microorganisms that are beneficial to the human body and the environment, providing a pleasant living environment by suppressing the molds of the house, as well as preventing the spread of germs by sterilizing various germs. Radiation heat and penetrating power of the body's peripheral capillary movement is active, and promotes blood circulation smoothly to function to lead a healthy life.
상술한 바와 같이 황토가 인체에 매우 유용한 작용을 함에 따라 황토의 이용이 급속도를 늘어나고 있는데, 최근에는 건축물에서부터 일반생활용품, 화장품, 찜질방, 침구류 등에 널리 사용되고 있다.As described above, the use of ocher is rapidly increasing as the ocher has a very useful effect on the human body. Recently, it has been widely used in buildings, general household goods, cosmetics, jjimjilbang, beddings, and the like.
그런데, 황토가 인체에 유익함에도 불구하고, 화장용 스폰지에 황토의 기능성을 부여한 화장용 스폰지는 개발되어 있지 않다.By the way, although ocher is beneficial to a human body, the cosmetic sponge which provided the functionality of ocher to a cosmetic sponge has not been developed.
따라서, 본 발명은 황토의 기능성을 화장용 스폰지에 접목시키기 위하여 이루어진 것으로서, 본 발명의 목적은 원적외선 방사와 항균, 살균작용이 있는 황토를 함유한 화장용 스폰지 및 그 제조방법을 제공하는데 있다.Accordingly, the present invention has been made in order to combine the functionality of the loess to the cosmetic sponge, an object of the present invention is to provide a cosmetic sponge containing loess having far-infrared radiation, antibacterial, bactericidal action and a method for producing the same.
본 발명의 다른 목적은 오일 성분을 흡수하지 않는 내유성의 스폰지(NBR - Nitrile Butadiene Rubb)에 황토를 함유한 화장용 스폰지 및 그 제조방법을 제공하는데 있다.Another object of the present invention is to provide a cosmetic sponge containing ocher in an oil resistant sponge (NBR-Nitrile Butadiene Rubb) that does not absorb oil components, and a method of manufacturing the same.
본 발명의 또 다른 목적은 다공이 균일하게 형성되어 있는 황토를 함유한 화장용 스폰지 및 그 제조방법을 제공하는데 있다.Still another object of the present invention is to provide a cosmetic sponge containing ocher in which the pores are uniformly formed, and a manufacturing method thereof.
본 발명의 또 다른 목적은 화장품이 피부에 잘 도포되어 화장품의 사용감도를 증대시킬 수 있는 황토를 함유한 화장용 스폰지 및 그 제조방법을 제공하는데 있다.Still another object of the present invention is to provide a cosmetic sponge containing ocher which can be applied to the skin well and increase the usability of the cosmetic, and a manufacturing method thereof.
본 발명의 또 다른 목적은 황토의 기능을 그대로 발휘할 수 있는 황토를 함 유한 화장용 스폰지 및 그 제조방법을 제공하는데 있다.It is still another object of the present invention to provide a cosmetic sponge containing ocher capable of exhibiting the function of ocher as it is and a method of manufacturing the same.
상기의 목적을 달성하기 위하여 본 발명의 황토를 함유한 화장용 스폰지 제조방법은 82중량% 내지 88.9중량%의 라텍스와, 3.1중량% 내지 4.8중량%의 유황분산액과, 2.9중량% 내지 4.2중량%의 아연산분산액과, 0.7 내지 1중량%의 기포안정제와, 0.6중량% 내지 1중량%의 황토를 교반기에서 20시간 내지 30시간동안 교반하여 균등하게 혼합하는 혼합공정과, 상기 혼합공정에서 균등하게 혼합된 혼합물과 3.8중량%의 응고제를 24℃ 내지 35℃ 의 온도로 가열된 발포기에 투입하여 1시간 동안 유지하면서 발포하는 발포공정과, 상기 발포공정에서 발포된 액상 발포물을 몰드에 주입하여 특정형상으로 성형하는 성형공정과, 상기 성형공정에서 몰드에 주입된 특정형상의 성형물을 90℃ 내지 100℃의 스팀을 40분 내지 80분 동안 가열하여 응고시키는 응고공정과, 상기 응고공정에서 응고된 황토함유 스폰지를 특정두께로 재단하는 재단공정과, 상기 재단공정에서 특정두께로 재단된 황토함유 스폰지의 가장자리를 라운드되게 연마하는 연마공정을 포함하는 것을 특징으로 한다.In order to achieve the above object, the method for producing a cosmetic sponge containing loess of the present invention comprises 82 wt% to 88.9 wt% of latex, 3.1 wt% to 4.8 wt% of sulfur dispersion, and 2.9 wt% to 4.2 wt% Mixing step of uniformly mixing the zinc acid dispersion of the mixture, 0.7 to 1% by weight of the bubble stabilizer, 0.6% to 1% by weight of the yellow soil in a stirrer for 20 to 30 hours and mixing it evenly The mixed mixture and the 3.8% by weight of the coagulant are introduced into a foamer heated to a temperature of 24 ° C. to 35 ° C. and maintained for 1 hour. A molding step of molding into a shape, and a solidification step of heating a specific shaped article injected into the mold in the molding step by heating steam at 90 ° C. to 100 ° C. for 40 to 80 minutes; It characterized by including the step of grinding the solidified sponge from the group comprising yellow soil solidification process to be polished round the cutting step and the cutting edge of an ocher-containing sponge cut to a specific thickness at the cutting step of a specific thickness.
이하, 본 발명의 황토를 함유한 화장용 스폰지 및 그 제조방법에 관하여 도 1을 참조하면서 실시예를 들어서 상세히 설명한다.Hereinafter, the cosmetic sponge containing the loess of the present invention and a manufacturing method thereof will be described in detail with reference to Examples.
도 1은 본 발명의 실시예에 의한 황토를 함유한 화장용 스폰지의 제조방법을 설명하는 순서도이다.1 is a flow chart illustrating a manufacturing method of a cosmetic sponge containing ocher according to an embodiment of the present invention.
실시예1Example 1
85중량%의 라텍스와, 4.0중량%의 유황분산액과, 3.5중량%의 아연산분산액 과, 0.9중량%의 기포안정제와, 0.8중량%의 황토를 교반기에서 20시간 내지 30시간동안 교반하여 균등하게 혼합하고(혼합공정), 상기 혼합공정에서 균등하게 혼합된 혼합물과 5.8중량%의 응고제를 24℃ 내지 35℃ 의 온도로 가열된 발포기에 투입하여 1시간 동안 유지하면서 발포하고(발포공정), 상기 발포공정에서 발포된 액상 발포물을 몰드에 주입하여 특정형상으로 성형하고(성형공정), 상기 성형공정에서 몰드에 주입된 특정형상의 성형물을 80℃ 내지 100℃의 스팀장치 내에서 40분 내지 80분 동안 가열하여 가류(액체를 스폰지로 성형)시키고(가류공정), 상기 가류공정에서 가류된 황토함유 스폰지를 몰드에서 꺼내서 특정두께로 재단하고(재단공정), 상기 재단공정에서 특정두께로 재단된 황토함유 스폰지의 가장자리를 라운드(둥굴게)되게 연마(연마공정)하여 본 발명의 황토를 함유한 화장용 스폰지를 제조하였다(도 1참조).85 wt% latex, 4.0 wt% sulfur dispersion, 3.5 wt% zinc dispersion, 0.9 wt% bubble stabilizer, and 0.8 wt% ocher were stirred in an stirrer for 20 to 30 hours Mixing (mixing step), and the mixture evenly mixed in the mixing step and 5.8% by weight of the coagulant is introduced into a foamer heated to a temperature of 24 ℃ to 35 ℃ and maintained for 1 hour (foaming step), the The liquid foam foamed in the foaming process is injected into a mold to be molded into a specific shape (molding process), and the molding of the specific shape injected into the mold in the molding process is carried out for 40 minutes to 80 in a steam apparatus at 80 ° C to 100 ° C. After heating for a minute, the vulcanization (liquid is formed into a sponge) (vulcanization step), the ocher-containing sponge vulcanized in the vulcanization step is taken out of the mold and cut to a specific thickness (cutting step), and The edges of the yellow soil foundation containing sponge was prepared in the round (round gulge) to be polished (polishing step) for the sponge containing a yellow soil of the present invention make-up (see FIG. 1).
실시예2Example 2
82중량%의 라텍스와, 4.8중량%의 유황분산액과, 4.2중량%의 아연산분산액과, 1중량%의 기포안정제와, 1중량%의 황토를 교반기에서 20시간 내지 30시간동안 교반하여 균등하게 혼합하고(혼합공정), 상기 혼합공정에서 균등하게 혼합된 혼합물과 7중량%의 응고제를 24℃ 내지 35℃ 의 온도로 가열된 발포기에서 1시간 동안 유지하면서 발포하고(발포공정), 상기 발포공정에서 발포된 액상 발포물을 몰드에 주입하여 특정형상으로 성형하고(성형공정), 상기 성형공정에서 몰드에 주입된 특정형상의 성형물을 80℃ 내지 100℃의 스팀장치 내에서 40분 내지 80분 동안 가열하여 가류시키고(가류공정), 상기 가류공정에서 가류된 황토함유 스폰지를 몰드 에서 꺼내서 특정두께로 재단하고(재단공정), 상기 재단공정에서 특정두께로 재단된 황토함유 스폰지의 가장자리를 라운드(둥굴게)되게 연마(연마공정)하여 본 발명의 황토를 함유한 화장용 스폰지를 제조하였다(도 1 참조).82 weight percent latex, 4.8 weight percent sulfur dispersion, 4.2 weight percent zinc dispersion, 1 weight percent bubble stabilizer, and 1 weight percent loess were stirred in an stirrer for 20 to 30 hours Mixing (mixing step), and the mixture evenly mixed in the mixing step and 7% by weight of the coagulant is foamed while maintaining for 1 hour in a foamer heated to a temperature of 24 ℃ to 35 ℃ (foaming step), the foaming The liquid foam foamed in the process is injected into a mold and molded into a specific shape (molding process), and the molding of the specific shape injected into the mold in the molding process is 40 to 80 minutes in a steam apparatus of 80 ° C to 100 ° C. Heated to vulcanize (vulcanization step), take out the loess-containing sponge vulcanized in the vulcanization step and cut it to a specific thickness (cutting step), and add the loess-containing sponge cut to a specific thickness in the cutting step. Place to prepare a round (round gulge) to be polished (polishing step) for the sponge containing a yellow soil of the present invention make-up (see Fig. 1).
실시예3Example 3
88.9중량%의 라텍스와, 3.1중량%의 유황분산액과, 2.9중량%의 아연산분산액과, 0.7중량%의 기포안정제와, 0.6중량%의 황토를 교반기에서 20시간 내지 30시간동안 교반하여 균등하게 혼합하고(혼합공정), 상기 혼합공정에서 균등하게 혼합된 혼합물과 3.8중량%의 응고제를 24℃ 내지 35℃ 의 온도로 가열된 발포기에 투입하여 1시간 동안 유지하면서 발포하고(발포공정), 상기 발포공정에서 발포된 액상 발포물을 몰드에 주입하여 특정형상으로 성형하고(성형공정), 상기 성형공정에서 몰드에 주입된 특정형상의 성형물을 90℃ 내지 100℃의 스팀장치 내에서 40분 내지 80분 동안 가열하여 가류시키고(가류공정), 상기 가류공정에서 가류된 황토함유 스폰지를 몰드에서 꺼내서 특정두께로 재단하고(재단공정), 상기 가류공정에서 가류된 황토함유 스폰지를 특정두께로 재단하고(재단공정), 상기 재단공정에서 특정두께로 재단된 황토함유 스폰지의 가장자리를 라운드(둥굴게)되게 연마(연마공정)하여 본 발명의 황토를 함유한 화장용 스폰지를 제조하였다(도 1 참조).88.9 wt% latex, 3.1 wt% sulfur dispersion, 2.9 wt% zinc dispersion, 0.7 wt% bubble stabilizer, and 0.6 wt% ocher were stirred in an stirrer for 20 to 30 hours Mixing (mixing step), and the mixture evenly mixed in the mixing step and 3.8% by weight of the coagulant is introduced into a foamer heated to a temperature of 24 ℃ to 35 ℃ and maintained for 1 hour (foaming step), the The liquid foam foamed in the foaming process is injected into a mold to be molded into a specific shape (molding process), and the molding of the specific shape injected into the mold in the molding process is carried out in a steam apparatus at 90 ° C. to 100 ° C. for 40 minutes to 80 minutes. After heating for vulcanization (vulcanization step), the loess-containing sponge vulcanized in the vulcanization step is removed from the mold and cut to a specific thickness (cutting step), and the loess-containing sponge vulcanized in the vulcanization step Cut to the thickness (cutting step), the edge of the ocher-containing sponge cut to a specific thickness in the cutting step was polished (rounded) to prepare a cosmetic sponge containing the loess of the present invention ( See FIG. 1).
비교예Comparative example
89.5중량%의 라텍스와, 3.1중량%의 유황분산액과, 2.9중량%의 아연산분산액과, 0.7중량%의 기포안정제를 교반기에서 20시간 내지 30시간동안 교반하여 균등하게 혼합하고(혼합공정), 상기 혼합공정에서 균등하게 혼합된 혼합물과 3.8중량 %의 응고제를 24℃ 내지 35℃ 의 온도로 가열된 발포기에 투입하여 1시간 동안 유지하면서 발포하고(발포공정), 상기 발포공정에서 발포된 액상 발포물을 몰드에 주입하여 특정형상으로 성형하고(성형공정), 상기 성형공정에서 몰드에 주입된 특정형상의 성형물을 90℃ 내지 100℃의 스팀을 40분 내지 80분 동안 가열하여 응고시키고(응고공정), 상기 응고공정에서 응고된 황토함유 스폰지를 특정두께로 재단하고(재단공정), 상기 재단공정에서 특정두께로 재단된 황토함유 스폰지의 가장자리를 라운드(둥굴게)되게 연마(연마공정)하여 본 발명의 황토를 함유한 화장용 스폰지를 제조하였다.89.5% by weight of latex, 3.1% by weight of sulfur dispersion, 2.9% by weight of zinc dispersion and 0.7% by weight of bubble stabilizer were stirred and stirred for 20 to 30 hours in a stirrer and mixed evenly (mixing step), The mixture evenly mixed in the mixing process and 3.8% by weight of a coagulant are introduced into a foamer heated to a temperature of 24 ° C to 35 ° C and maintained for 1 hour (foaming step), and the liquid foaming foamed in the foaming step Water is injected into a mold to form a specific shape (molding step), and the specific shape molded product injected into the mold in the molding step is solidified by heating steam at 90 ° C. to 100 ° C. for 40 to 80 minutes. ), And cut the ocher-containing sponge solidified in the solidification process to a specific thickness (cutting step), and polish the edges of the ocher-containing sponge rounded (rounded) to a specific thickness in the cutting process ( Polishing process) to prepare a cosmetic sponge containing the loess of the present invention.
상기 설명에 있어서, 상기 유황분산액은 가류촉진제로서 50중량%의 유황과 물과 TAMOL N(미국의 BSAF사 상표명 ; 희석제)을 1:1 로 혼합한 분산제 50중량%를 교반기에서 48시간 동안 혼합한 것을 사용하는 것이 바람직하고, 상기 아연산분산액은 스폰지의 탄성을 유지시키기 위해 50중량%의 산화아연과 50중량%의 분산제를 24시간 동안 교반기에서 교반한 것을 사용하는 것이 바람직하고, 상기 기포안정제는 트리멘 베이스(TRIMENE BASE ; 미국의 CROMPTON사 상표명)를 사용하는 것이 바람직하다.In the above description, the sulfur dispersion is 50% by weight of sulfur and 50% by weight of the dispersant mixed with water and TAMOL N (trade name; diluent) in a stirrer for 48 hours in a stirrer as a vulcanization accelerator Preferably, the zinc acid dispersion is a mixture of 50% by weight of zinc oxide and 50% by weight of a dispersant in a stirrer for 24 hours to maintain the elasticity of the sponge, and the bubble stabilizer It is preferable to use TRIMENE BASE (trade name of CROMPTON Corporation of the United States).
상기 응고제는 규불화소다와 밴드나이트를 10:1로 혼합한 혼합물 20 내지 25중량%와 물과 TAMOL N 을 1:1로 혼합한 혼합물 75 내지 80중량%를 혼합한 것을 사용하는 것이 바람직하다.The coagulant is preferably used by mixing 20 to 25% by weight of a mixture of sodium silicate and bandite in 10: 1 and 75 to 80% by weight of a mixture of water and TAMOL N in a 1: 1 ratio.
상기 설명에 있어서, 상기 라텍스를 88.9중량% 이상 함유하면 라텍스가 경화되고, 기공이 너무 조밀하게 형성되어 부드럽지 못해서 바람직하지 못하고, 상기 라텍스를 82중량% 이하 함유하면 기공이 크게 발생될 뿐만 아니라, 기공이 크고 불규칙적으로 형성되어 화장품이 불규칙적으로 묻지 않아서 화장을 자연스럽게 할 수 없어서 바람직하지 못하고, 유황분산액을 4.8중량% 이상 함유하면 가류가 과도하게 일어나서 기공이 거칠게 형성되어 바람직하지 못하고, 유황분산액을 3.1중량%이하 함유하면 가류가 불규칙하게 일어나서 기공이 크게 발생되어 바람직하지 못하다.In the above description, when the latex is contained 88.9% by weight or more, the latex is cured, the pores are too densely formed and not smooth, and when the latex is contained by 82% by weight or less, not only pores are greatly generated. The pores are large and irregularly formed, which is not desirable because cosmetics are not irregularly applied, and makeup is not natural, and if 4.8 wt% or more of sulfur dispersion is contained, excessive vulcanization occurs and rough pores are formed, which is undesirable. If the content is less than or equal to% by weight, vulcanization occurs irregularly and pores are largely generated, which is not preferable.
또한, 상기 아연산분산액을 4.2중량% 이상 함유하면, 경화 되어 바람직하지 못하고, 상기 아연산분산액을 2.9중량% 이하 함유하면, 탄성저하로 바람직하지 못하고, 황토를 1중량% 이상 함유하면 다른 성분이 부족하여 발포가 불규칙적으로 발생하고 원적외선은 많이 방사하여 항균 및 살균작용은 높아지나, 다른 성분이 부족하여 바람직하지 못하고, 황토를 0.6중량% 이하 함유하면 원적외선 방사량이 너무 적어서 항균 및 살균작용이 약해져서 바람직하지 못하고, 상기 기포안정제를 1중량% 이상 함유하면 유동성이 떨어져서 너무 신속하게 응고되어 기공이 불규칙적으로 발생하여 바람직하지 못하고, 상기 기포안정제를 0.6중량% 이하 함유하면 유동성이 너무 커서 발포할 수 없으므로 바람직하지 못하다.If the content of the zinc acid dispersion is 4.2% by weight or more, curing is not preferable. If the content of the zinc acid dispersion is 2.9% by weight or less, it is not preferable to reduce elasticity. Insufficient foaming occurs irregularly, and far infrared rays are radiated a lot to increase antibacterial and bactericidal action, but it is not desirable due to lack of other ingredients, and containing less than 0.6 wt. If the bubble stabilizer is contained in an amount of 1 wt% or more, the fluidity is poor and solidifies too quickly, causing irregularities in pores. I can't.
이와 같이 제조한 본 발명의 황토를 함유한 화장용 스폰지를 사단법인 한국원적외선협회의 한국원적외선 응용평가연구원에 원적외선 방사율과 방사에너지의 시험을 의뢰하였다.The cosmetic sponge containing the loess of the present invention prepared as described above was commissioned to the far-infrared emissivity and radiation energy test by the Korea Far Infrared Applied Evaluation Institute of Korea Far Infrared Association.
도 2는 본 발명의 실시예에 의한 황토를 함유한 화장용 스폰지의 원적외선 시험성적을 도시한 그래프로서, 원적외선 파장에 대한 방사에너지의 그래프이고, 도 3은 본 발명의 실시예에 의한 황토를 함유한 화장용 스폰지의 원적외선 시험성적을 도시한 그래프로서, 원적외선 파장에 대한 방사율의 그래프이다.Figure 2 is a graph showing the far-infrared test results of the cosmetic sponge containing ocher according to an embodiment of the present invention, a graph of the radiation energy with respect to the far infrared wavelength, Figure 3 contains the loess according to an embodiment of the present invention A graph showing the far-infrared test performance of a cosmetic sponge, which is a graph of emissivity versus far-infrared wavelength.
사단법인 한국원적외선협회의 한국원적외선 응용평가연구원(KIFA)에서 FT-IR 스펙트로미터를 사용하여 BLACK BODY대비 측정한 결과, 원적외선 방사율이 5 내지 20 μm 파장대가 90%였고, 37℃에서 방사에너지가 3.47×102(W/m2·μm, 37℃)였다(도 2 및 도 3 참조).The FT-IR spectrometer measured the black body at KIFA of the Korea Far Infrared Association (KIFA), and compared it with the BLACK BODY. It was * 10 <2> (W / m <2> micrometer, 37 degreeC) (refer FIG. 2 and FIG. 3).
본 발명의 황토를 함유한 화장용 스폰지를 사용하여 20회 화장을 한 샘플을 산업 환경 연구센터에 의뢰하여 대장균의 항균성시험을 행한 결과(KATRI NO BS04-00002121), 초기균수가 0.9×104개/mL가 존재하였으나, 24시간 경과 후에 100개 이하로 줄었다.As a result of conducting an antimicrobial test of Escherichia coli by applying a sample of 20 makeups using the cosmetic sponge containing ocher of the present invention to the Industrial Environment Research Center (KATRI NO BS04-00002121), the initial bacterial count was 0.9 × 10 4 / mL was present but was reduced to less than 100 after 24 hours.
따라서, 본 발명의 황토를 함유한 화장용 스폰지는 대장균에 대한 항균력이 있음을 실험 결과 확인하였다.Therefore, it was confirmed that the cosmetic sponge containing the loess of the present invention has an antibacterial activity against Escherichia coli.
한편, 산업 환경 연구센터에서 KS M 0146(2003)의 규정에 의해 대조편을 대장균의 항균성시험을 행한 결과, 초기균수가 0.9×104개/mL가 존재하였으나, 24시간 경과 후에 1.4×108개/mL가 존재하였으며, 대조편(비교예에 의해 제조한 스폰지)은 대장균에 대한 항균력이 없음을 실험결과 확인되었다.On the other hand, the antibacterial test of Escherichia coli was carried out in the Industrial Environment Research Center according to the provisions of KS M 0146 (2003). As a result, the initial bacterial count was 0.9 × 10 4 / mL, but after 24 hours, 1.4 × 10 8 The dog / mL was present, and the control piece (sponge prepared by the comparative example) was confirmed that the antimicrobial activity against E. coli.
따라서, 본 발명의 황토를 함유한 화장용 스폰지는 황토에서 원적외선을 방사하여 항균 및 살균작용이 있고, 다공이 균일하게 형성되어 있어 화장품이 스폰지 에 균등하게 부착되어 화장품을 피부에 균등하게 도포할 수 있다.Therefore, the cosmetic sponge containing ocher of the present invention has antimicrobial and bactericidal action by emitting far infrared rays from ocher, and the pores are formed uniformly so that the cosmetics are evenly attached to the sponge and the cosmetics can be evenly applied to the skin. have.
상기 설명에 있어서, 특정 실시예를 들어서 도시하고 설명하였으나, 본 발명은 이에 한정되는 것은 아니며, 예를 들면 본 발명의 개념을 이탈하지 않는 범위내에서 이 기술 분야의 통상의 지식을 가진 자에 의해 여러가지로 설계변경할 수 있음은 물론이다.In the above description, the specific embodiments have been shown and described, but the present invention is not limited thereto, for example, by those skilled in the art without departing from the concept of the present invention. Of course, the design can be changed in various ways.
앞에서 설명한 바와 같이 본 발명의 황토를 함유한 화장용 스폰지 및 그 제조방법에 의하면, 황토에서 원적외선을 방사하여 항균 및 살균작용이 있고, 다공이 균일하게 형성되어 있음과 동시에, 화장품이 피부에 잘 도포되어 화장품의 사용감도를 증대시킬 수 있고, 황토의 기능을 그대로 발휘할 수 있다는 효과가 있다.As described above, according to the cosmetic sponge containing the loess of the present invention and its manufacturing method, it has antibacterial and bactericidal action by emitting far-infrared rays from loess, and the pores are uniformly formed, and cosmetics are well applied to the skin. It is possible to increase the usability of the cosmetics, there is an effect that the function of the loess can be exhibited as it is.
Claims (5)