KR20060102235A - Manufacturing method of medical trocar - Google Patents

Manufacturing method of medical trocar Download PDF

Info

Publication number
KR20060102235A
KR20060102235A KR1020050024212A KR20050024212A KR20060102235A KR 20060102235 A KR20060102235 A KR 20060102235A KR 1020050024212 A KR1020050024212 A KR 1020050024212A KR 20050024212 A KR20050024212 A KR 20050024212A KR 20060102235 A KR20060102235 A KR 20060102235A
Authority
KR
South Korea
Prior art keywords
base material
trocar
passed
manufacturing
medical trocar
Prior art date
Application number
KR1020050024212A
Other languages
Korean (ko)
Inventor
이덕근
Original Assignee
이덕근
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이덕근 filed Critical 이덕근
Priority to KR1020050024212A priority Critical patent/KR20060102235A/en
Publication of KR20060102235A publication Critical patent/KR20060102235A/en

Abstract

의료용 트로카의 제조방법이 제공된다. 제공된, 트로카의 제조방법은 스테인레스봉을 소정길이로 절단하여 모재를 만든 후 이 모재의 전방에는 날카로운 형태의 삽입부를 절삭가공하고 그 후방에는 다수의 걸림턱을 가공하는 제 1단계와, 상기 제 1단계를 거친 모재의 센터리스 연삭작업을 수행하는 제 2단계와, 상기 제 2단계를 거친 모재의 전방부를 소정각도로 절곡하는 제 3단계와, 상기 제 3단계를 거친 모재의 표면을 연마하는 제 4단계와, 상기 제 4단계를 거친 모재를 열처리하는 제 5단계와, 상기 제 5단계를 거친 모재를 전해연마하는 제 6단계와, 상기 제 6단계를 거친 모재를 초음파세척하는 제 7단계와, 상기 제 7단계를 거친 모재에 가요성을 부여하기 위해 무산화열처리하는 제 8단계를 포함한다.Provided is a method of making a medical trocar. Provided, the manufacturing method of the trocar is a first step of cutting the stainless rod to a predetermined length to form a base material, and then cutting the insert of the sharp shape in the front of the base material and processing a plurality of locking jaws in the rear, and the second step A second step of performing a centerless grinding operation of the base material which has been subjected to the first step, a third step of bending the front part of the base material which has been subjected to the second step at a predetermined angle, and polishing a surface of the base material which has been subjected to the third step A fourth step, a fifth step of heat-treating the base material through the fourth step, a sixth step of electropolishing the base material through the fifth step, and a seventh step of ultrasonic cleaning of the base material through the sixth step And an eighth step of oxidation-free heat treatment to impart flexibility to the base material that has undergone the seventh step.

Description

의료용 트로카의 제조방법{omitted}Manufacturing method of medical trocar {omitted}

도 1은 기존의 의료용 트로카를 설명하기 위한 사시도이다.1 is a perspective view for explaining a conventional medical trocar.

도 2는 본 발명에 따른 의료용 트로카의 제조방법을 설명하기 위한 블럭도이다.2 is a block diagram illustrating a method of manufacturing a medical trocar according to the present invention.

도 3은 본 발명에 따른 제조방법을 통해 제조된 트로카의 형태변경상태를 보인 구성도이다.Figure 3 is a block diagram showing a form change state of the trocar manufactured by the manufacturing method according to the present invention.

본 발명은 의료용 트로카의 제조방법에 관한 것이다.The present invention relates to a method for producing a medical trocar.

일반적으로, 환부를 절개하는 수술을 시술할 때에는 절개부위를 꿰매는 과정에서 흡인관을 삽입하여 환부에 고여 있는 피고름 등을 흡인하는 과정을 거치게 된다. 이때, 흡인관은 연질의 합성수지재로 구성됨에 따라서 별도의 가이더를 이용하여 환부에 삽입되는데, 이러한 가이더의 대표적인 일례로는 의료용 트로카를 들 수 있다.In general, when performing surgery to incision the affected area is inserted into the suction tube in the process of sewing the incision to go through the process of sucking the pus stuck in the affected area. At this time, the suction tube is inserted into the affected part using a separate guider as it is composed of a soft synthetic resin material, a typical example of such a guider is a medical trocar.

도 1은 기존의 의료용 트로카를 설명하기 위한 사시도이다.1 is a perspective view for explaining a conventional medical trocar.

도 1을 참조하면, 의료용 트로카(10)는 소정길이를 갖는 봉형태로 구성되며, 그 구성재질로는 금속재, 예컨대 스테인레스재가 적용된다. 이와 같은 의료용 트로카(10)는 그 전방에 날카로운 삽입부(10a)가 가공되어 있고, 그 후방에는 흡인관(20)을 끼움고정하기 위한 걸림턱(10b)이 마련되어 있으며, 시술자가 환부에 용이하게 삽입할 수 있도록 소정각도, 예컨대 15°로 절곡된 구조를 갖는다. 이와같은 구성에 따르면, 시술자는 홉인관(20)이 끼움고정된 의료용 트로카(10)를 환부에 삽입하여 흡인관(20)에 마련된 흡인공(20a)이 환부에 위치되도록 한 상태에서 이 흡입관(20)과 연결되어 있는 별도의 흡인기(30)를 구동시켜서 환부에 고여 있는 피고름 등을 몸밖으로 흡인하게 된다. 이때, 의료용 트로카(10)는 절개부위의 형태, 즉 내과에서 수술할 때와 외과에서 수술할 때 등 각기 다른 형태의 절개부위에 따라 다양한 직경(3.2mm, 4.8mm, 6.4mm 등)으로 제조된다.Referring to Figure 1, the medical trocar 10 is configured in the form of a rod having a predetermined length, the material of the material is a metal material, for example, stainless steel is applied. Such a medical trocar 10 has a sharp insertion portion 10a in the front thereof, and a locking jaw 10b for fitting the suction tube 20 in the rear thereof is provided, and the operator can easily It has a structure that is bent at a predetermined angle, such as 15 °, so as to be inserted. According to such a configuration, the operator inserts the medical trocar 10, in which the hop-in tube 20 is fitted, into the affected part so that the suction hole 20a provided in the suction tube 20 is positioned in the affected part ( By driving a separate aspirator (30) connected to the 20) to suck out the pulp stuck in the affected part out of the body. At this time, the medical trocar 10 is manufactured in various diameters (3.2mm, 4.8mm, 6.4mm, etc.) according to different types of incisions, such as when incisions are performed in the internal medicine and surgery. do.

하지만, 기존의 의료용 트로카(10)는 수술시 절개부위의 형태에 대응하도록 재차 절곡해서 삽입해야 하는데, 스테인레스와 같은 금속재로 구성되는 기존의 의료용 트로카(10)는 상당한 직경을 지니고 있어 그 절곡작업에 상당한 어려움이 있다. 더욱이, 의료용 트로카(10)의 형태변경작업은 수술실 현장에서 직접수행되는데, 수술실에는 의료용 트로카(10)를 절곡하기 위한 별도의 도구가 불비되어 있어서, 단순히 사람의 힘에 의해 구부려야하므로 작업의 어려움이 가중되고 있다.However, the conventional medical trocar 10 should be inserted by bending again to correspond to the shape of the incision during surgery, the existing medical trocar 10 consisting of a metal material such as stainless steel has a considerable diameter There is considerable difficulty in the work. Moreover, the shape change operation of the medical trocar 10 is performed directly at the operating room site, and the operating room is equipped with a separate tool for bending the medical trocar 10, so the work must be bent simply by human force. Difficulties are increasing.

이에, 본 발명은 기존의 의료용 트로카가 갖는 제반적인 문제점을 해결하고자 창안된 것으로,Therefore, the present invention was devised to solve the general problems of the conventional medical trocar,

본 발명이 이루고자 하는 기술적 과제는 금속재로 구성되는 의료용 트로카의 형태를 원활하게 변경할 수 있도록 하여, 수술시 수행되는 트로카의 형태변경작업을 용이하게 수행할 수 있도록 한 의료용 트로카의 제조방법을 제공하는데 있다.The technical problem to be achieved by the present invention is to enable a smooth change of the shape of the medical trocar consisting of a metal material, to facilitate the shape change operation of the trocar performed during the operation of the medical trocar manufacturing method To provide.

상기한 기술적 과제를 해결하기 위한 본 발명의 구체적인 수단으로는;As a specific means of the present invention for solving the above technical problem;

스테인레스봉을 소정길이로 절단하여 모재를 만든 후, 이 모재의 전방에는 날카로운 형태의 삽입부를 절삭가공하고, 그 후방에는 다수의 걸림턱을 가공하는 제 1단계;After cutting the stainless rod to a predetermined length to make a base material, a first step of cutting the insert of the sharp shape in the front of the base material, and processing a plurality of locking jaws in the rear;

상기 제 1단계를 거친 모재의 센터리스 연삭작업을 수행하는 제 2단계;A second step of performing a centerless grinding operation of the base material passed through the first step;

상기 제 2단계를 거친 모재의 전방부를 소정각도로 절곡하는 제 3단계;A third step of bending the front part of the base material having passed through the second step at a predetermined angle;

상기 제 3단계를 거친 모재의 표면을 연마하는 제 4단계;A fourth step of polishing the surface of the base material having passed through the third step;

상기 제 4단계를 거친 모재를 열처리하는 제 5단계;A fifth step of heat-treating the base material having passed through the fourth step;

상기 제 5단계를 거친 모재를 전해연마하는 제 6단계; 및A sixth step of electropolishing the base material having undergone the fifth step; And

상기 제 6단계를 거친 모재를 초음파세척하는 제 7단계; 를 포함하며,A seventh step of ultrasonically cleaning the base material having passed through the sixth step; Including;

상기 제 7단계를 거친 모재에 가요성을 부여하기 위해 무산화열처리하는 제 8단계;를 포함하는 의료용 트로카의 제조방법을 구비한다.And an eighth step of non-oxidizing heat treatment to give flexibility to the base material having undergone the seventh step.

바람직한 실시예로써, 상기 제 8단계에서 수행되는 무산화 열처리는 모재를 진공상태에서 3～5분 가열한 후 냉각한다.In a preferred embodiment, the oxidation-free heat treatment carried out in the eighth step is cooled after heating the base material in a vacuum for 3 to 5 minutes.

이하, 본 발명의 바람직한 실시예를 첨부도면에 의거 상세히 설명하기로 한다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.

도 2는 본 발명에 따른 의료용 트로카의 제조방법을 설명하기 위한 블럭도이 고, 도 3은 본 발명에 따른 제조방법을 통해 제조된 트로카의 형태변경상태를 보인 구성도이다.Figure 2 is a block diagram for explaining a method for manufacturing a medical trocar according to the present invention, Figure 3 is a block diagram showing a shape change state of the trocar manufactured through the manufacturing method according to the present invention.

도 2를 참조하면, 본 발명의 의료용 트로카의 제조방법은 모재의 성형단계인 제 1단계와, 모재의 센터리스작업을 수행하는 제 2단계와, 모재를 소정각도로 절곡하는 제 3단계와, 모재를 연마하는 제 4단계와, 모재를 열처리하는 제 5단계와, 모재를 전해연마하는 제 6단계와, 모재를 초음파세척하는 제 7단계와, 모재를 무산화 열처리하는 제 8단계로 나뉘어진다.2, the method of manufacturing a medical trocar of the present invention includes a first step of forming a base material, a second step of performing a centerless work of the base material, and a third step of bending the base material at a predetermined angle; It is divided into a fourth step of grinding the base material, a fifth step of heat treatment of the base material, a sixth step of electropolishing the base material, a seventh step of ultrasonic cleaning the base material, and an eighth step of anodizing the base material. Lose.

상기 제 1단계에서는 스테인레스봉, 예컨대 3.2mm, 4.8mm, 6.4mm 등의 직경을 가지며, sus304 반강인 스테인레스봉을 소정길이로 절단하여 모재를 만들고, 이 모재의 전방에 날카로운 형태의 삽입부를 절삭가공함과 아울러 그 후방에 다수의 걸림턱을 가공하므로써 트로카의 외형을 성형한다.In the first step, a stainless rod, for example, 3.2 mm, 4.8 mm, 6.4 mm, and the like, is cut to a predetermined length by sus304 semi-steel stainless rod to make a base material, and a cutting insert is formed at the front of the base material. In addition, by forming a plurality of locking jaws in the rear portion of the trocar shape.

상기 제 2단계에서는 모재의 센터리스 연삭작업을 수행하는데, 이와 같은 센터리스 연삭작업은 통상의 센터리스 연삭기를 이용하여 모재의 정확한 센터를 맞춘다.In the second step, the centerless grinding work of the base material is performed. The centerless grinding work is performed to adjust the center of the base material accurately using a conventional centerless grinding machine.

상기 제 3단계에서는 모재의 전방부를 소정각도, 예컨대 15°의 각도로 절곡하는 작업이 수행되고, 상기 제 4단계에서는 모재의 표면을 통상의 연삭기에 의해 연마한다.In the third step, an operation of bending the front part of the base material at a predetermined angle, for example, 15 °, is performed. In the fourth step, the surface of the base material is polished by a conventional grinding machine.

상기 제 5단계에서는 모재를 열처리(담금질)하고, 상기 제 6단계를 거친 모재를 전해연마, 즉 인산 65～75％, 황산 15～12％, 무수크롬산 15～12％ 비중 1.74 또는 인산 40～45％, 황산 37～34％, 무수크롬산 3～4％ 비중 1.65으로 전해조건 35～50A/dm2, 온도 70～85℃, 시간 10～15분의 환경에서 전해연마를 수행하고, 상기 제 7단계에서는 모재를 초음파세척한다.In the fifth step, the base material is heat treated (quenched), and the base material passed through the sixth step is electropolished, that is, 65 to 75% phosphoric acid, 15 to 12% sulfuric acid, 15 to 12% chromic anhydride, 1.74 or 40 to 45 phosphoric acid. %, Sulfuric acid 37-34%, chromic anhydride 3-4% specific gravity 1.65, electrolytic polishing was carried out in an environment of 35-50 A / dm 2 electrolysis conditions, temperature 70-85 ° C., time 10-15 minutes, and in the seventh step Ultrasonic cleaning of the base material.

마지막으로, 상기 제 8단계에서는 모재에 가요성을 부여하기 위해 무산화 열처리작업을 수행하는데, 이와 같은 무산화 열처리작업은 모재를 진공상태에서 3～5분 가열한 후 냉각하므로써 구현된다.Lastly, in the eighth step, an anodizing heat treatment is performed to give flexibility to the base material. Such an annealing heat treatment is performed by heating the base material in a vacuum for 3 to 5 minutes and then cooling it.

이에, 상기와 같은 단계를 갖는 본 발명에 따른 의료용 트로카의 제조방법은 제 8단계에서 무산화 열처리작업을 수행하여 트로카에 가요성, 즉 소정의 탄성이 부여함에 따라서, 도 3에서와 같이 별도의 도구없이도 단순한 수작업을 통해 원하는 형태로 변형이 가능하다. 이에 따라서. 수술시 절개부위의 형태에 대응하도록 재차 절곡하는 작업을 용이하게 수행할 수 있는 것이다.(도면 부호 1은 의료용 트로카를 가리킨다.)Thus, according to the method of manufacturing a medical trocar according to the present invention having the above steps, the trocar is flexible, that is, given a predetermined elasticity by performing an anodizing heat treatment operation in the eighth step, as shown in FIG. 3. It can be transformed into the desired shape through simple manual work without any tools. Accordingly. It is easy to perform the operation of bending again to correspond to the shape of the incision site during surgery (reference numeral 1 indicates a medical trocar).

이상과 같이, 본 발명에 따른 의료용 트로카의 제조방법은 금속재(스테인레스재)로 구성되는 의료용 트로카의 제조시 무산화 열처리단계를 수행함으로써, 트로카자체에 가요성을 부여하여 그 형태를 원활하게 변경할 수 있는 장점이 있다. 이에 따라서, 수술시 수행되는 트로카의 형태변경작업을 용이하게 수행할 수 있어 편리하게 사용할 수 있는 효과가 있다.As described above, the method for manufacturing a medical trocar according to the present invention performs an anodizing annealing step in the manufacture of a medical trocar consisting of a metal material (stainless material), thereby giving flexibility to the trocar body and smoothing its shape. There is an advantage that can be changed. Accordingly, it is possible to easily perform the shape change operation of the trocar to be performed during surgery has the effect that can be conveniently used.

Claims (2)

스테인레스봉을 소정길이로 절단하여 모재를 만든 후, 이 모재의 전방에는 날카로운 형태의 삽입부를 절삭가공하고, 그 후방에는 다수의 걸림턱을 가공하는 제 1단계;After cutting the stainless rod to a predetermined length to make a base material, a first step of cutting the insert of the sharp shape in the front of the base material, and processing a plurality of locking jaws in the rear; 상기 제 1단계를 거친 모재의 센터리스 연삭작업을 수행하는 제 2단계;A second step of performing a centerless grinding operation of the base material passed through the first step; 상기 제 2단계를 거친 모재의 전방부를 소정각도로 절곡하는 제 3단계;A third step of bending the front part of the base material having passed through the second step at a predetermined angle; 상기 제 3단계를 거친 모재의 표면을 연마하는 제 4단계;A fourth step of polishing the surface of the base material having passed through the third step; 상기 제 4단계를 거친 모재를 열처리하는 제 5단계;A fifth step of heat-treating the base material having passed through the fourth step; 상기 제 5단계를 거친 모재를 전해연마하는 제 6단계; 및A sixth step of electropolishing the base material having undergone the fifth step; And 상기 제 6단계를 거친 모재를 초음파세척하는 제 7단계; 를 포함하며,A seventh step of ultrasonically cleaning the base material having passed through the sixth step; Including; 상기 제 7단계를 거친 모재의 가요성을 부여하기 위해 무산화열처리하는 제 8단계;를 포함하는 의료용 트로카의 제조방법.And an eighth step of non-oxidizing heat treatment in order to give flexibility of the seventh step of the base material. 제 1항에 있어서,The method of claim 1, 상기 제 8단계에서 수행되는 무산화 열처리는 모재를 진공상태에서 3～5분 가열한 후 냉각하는 작업이 수행되는 것을 특징으로 하는 의료용 트로카의 제조방법.The non-oxidation heat treatment carried out in the eighth step is a method for manufacturing a medical trocar, characterized in that the cooling is performed after heating the base material in a vacuum for 3 to 5 minutes.
KR1020050024212A 2005-03-23 2005-03-23 Manufacturing method of medical trocar KR20060102235A (en)