KR20050077216A - Method manufacturing porcelain jade tile and porcelain tile glaze - Google Patents
Method manufacturing porcelain jade tile and porcelain tile glaze Download PDFInfo
- Publication number
- KR20050077216A KR20050077216A KR1020040005173A KR20040005173A KR20050077216A KR 20050077216 A KR20050077216 A KR 20050077216A KR 1020040005173 A KR1020040005173 A KR 1020040005173A KR 20040005173 A KR20040005173 A KR 20040005173A KR 20050077216 A KR20050077216 A KR 20050077216A
- Authority
- KR
- South Korea
- Prior art keywords
- jade
- tile
- glaze
- weight
- ceramic
- Prior art date
Abstract
본 발명은 도기질 옥 타일 제조방법 및 도기질 타일 유약에 관한 것으로, 본 발명은 타일의 표면을 이루고 있는 유약 조성에 후리트 72∼87중량%, 카오린 5∼10중량%, 옥 7∼15중량%, 슈퍼 음이온 1∼3중량%의 천연 원료를 주로하는 도기질 타일의 생유약 제조시 분쇄 공정의 습식 분쇄기인 볼밀에 경도와 비중이 높은 옥을 미분쇄하기 위하여 옥과 카오린을 먼저 투입하고 물 투입량의 절반만 투입, 먼저 분쇄하여 325메쉬를 완전히 통과할 때까지 분쇄한 후, 나머지 원료인 후리트, 슈퍼 음이온, 물 등을 투입하여 유약을 제조하고, 이것을 성형 건조 또는 1차 소성된 타일 위에 표면처리하고 1050∼1200℃로 소성하여 되는 기능성 옥타일 제품을 제공한다. 이러한 본 발명에 의한 기능성 도기질 옥 타일은 실내의 바닥 또는 벽면에 시공하면 옥 타일의 표면인 유약층에서 원적외선과 음이온이 방사되어 사용자의 건강증진에 큰 효과를 줄 수 있으며, 항균, 탈취 작용으로 각종 세균을 제거하고 그 배양을 방지해 주며, 각종 악취와 그 주변의 공기까지 정화시켜 실내 환경을 보다 쾌적하고 아름다운 주거 환경을 만들 수 있는 이점과 효과가 있다.The present invention relates to a method for producing a ceramic jade tile and a ceramic tile glaze, the present invention relates to 72 to 87% by weight frit, 5 to 10% by weight of kaolin, 7 to 15% by weight of glaze composition forming the surface of the tile In order to finely grind jade with high hardness and specific gravity in the ball mill, which is a wet grinder in the grinding process, in the manufacture of raw glaze of ceramic tiles mainly containing 1% to 3% by weight of super anion, jade and kaolin are added first. Only half of the mixture is pulverized first, and then pulverized until it completely passes through the 325 mesh. Then, the remaining raw materials, such as frit, super anion, and water, are added to prepare glaze, and the surface is formed on a molded or primary fired tile. The present invention provides a functional octale product which is treated and calcined at 1050 to 1200 ° C. When the functional ceramic jade tile according to the present invention is installed on the floor or wall of the room, far infrared rays and negative ions are radiated from the glaze layer, which is the surface of the jade tile, which can greatly enhance the health of the user. It removes various germs and prevents its culture, and purifies various odors and surrounding air to make indoor environment more comfortable and beautiful.
Description
본 발명은 도기질 옥 타일 제조방법 및 도기질 타일 유약에 관한 것으로, 더욱 상세하게는 옥과 슈퍼 음이온을 함유하는 도기질 옥 타일 유약을 제조하고, 이 도기질 옥 타일 유약을 건축용 타일에 표면처리하여 기능성 도기질 옥 타일을 제조함으로써 인체에 유익한 옥에서 방사되는 원적외선과 항균, 탈취 작용을 이용하고, 슈퍼 음이온으로부터 발생되는 음이온은 오염되어 가는 주변 환경을 개선하여 인체 건강의 균형을 유지 회복시켜 줄 수 있는 효과를 최대한 이용하기 위한 것이고, 이를 얻기 위하여 경도와 비중이 높은 옥을 완전히 습식 미분쇄하는 공정을 적용하여 유약을 제조하고, 이 유약으로 표면 처리한 후, 소성하여 고 단가의 옥을 적은 량으로 타일 표면에 균일하게 분산시켜 기능성 효과를 증대할 수 있는 옥 타일을 제공하기 위한 도기질 옥 타일 제조방법 및 도기질 타일 유약에 관한 것이다.The present invention relates to a method for producing a ceramic jade tile and a ceramic tile glaze, and more particularly, to prepare a ceramic jade tile glaze containing jade and super anion, and to surface-treat the ceramic jade tile glaze on a building tile By producing functional ceramic jade tile, it utilizes far-infrared radiation, antibacterial and deodorizing effect emitted from jade that is beneficial to human body, and negative ions generated from super anions can improve the environment of polluting and maintain the balance of human health. In order to make the most of the effect, the glaze is manufactured by applying a process of completely wet pulverization of jade having high hardness and specific gravity, and after the surface treatment with the glaze, it is calcined to produce a small amount of high unit price jade. Pottery to provide jade tiles that can be distributed evenly on the tile surface to increase functional effects The present invention relates to a nitric jade tile manufacturing method and a ceramic tile glaze.
일반적인 세라믹 타일의 경우 도기질 유약 조성은 중량율로 후리트 94중량%, 카오린 6중량%로 조성되고, 이들을 배합하여 동시에 볼밀에 분쇄한 후 성형 건조 또는 1차 소성 타일 위에 표면 처리하여 소성한다.In the case of a general ceramic tile, the ceramic glaze composition is composed of 94% by weight of frit and 6% by weight of kaolin in a weight ratio, which are blended and pulverized in a ball mill at the same time, and then fired by surface treatment on a molded dry or primary fired tile.
특허 제10-0382777호에는 옥 타일의 조성물이 옥과 함께 소지에 이루어져 성형, 소성 제조하는 방법에 관한 것이 기재되어 있고, 실용신안 제20-0274078호에는 옥돌과 옥 입자 및 옥 분말을 바인더인 시멘트와 혼합하여 형성한 옥을 주성분으로 한 타일이 기재되어 있으며, 실용신안 제20-0184902호에는 옥돌판을 가공하여 장식적이고 시각적인 옥돌 내장타일이 기재되어 있다.Patent No. 10-0382777 discloses a method of forming and calcining a composition of an jade tile together with jade, and Utility Model No. 20-0274078 discloses jade stones, jade particles, and jade powder as a binder. Tiles composed mainly of jade formed by mixing are described, and Utility Model No. 20-0184902 describes a decorative and visual jade stone interior tile by processing an jade stone plate.
상기 종래 기술은 시공 후 원적외선을 방출하나 인체에 유익한 음이온과 타일 표면에서 환경 정화에 뛰어난 항균, 탈취 효과를 동시에 얻을 수 없는 문제점이 있는 것이었다.The prior art emits far-infrared rays after construction, but there is a problem in that it is possible to simultaneously obtain an antibacterial and deodorizing effect that is excellent for environmental purification on the anion and tile surfaces beneficial to the human body.
본 발명은 상기한 바와 같은 종래의 문제점 및 결함을 해소하기 위하여 창안한 것으로, 옥과 슈퍼 음이온을 함유하는 도기질 옥 타일 유약을 제조하고, 이 도기질 옥 타일 유약을 건축용 타일에 표면처리하여 기능성 도기질 옥 타일을 제조함으로써 인체에 유익한 옥에서 방사되는 원적외선과 항균, 탈취 작용을 이용하고, 슈퍼 음이온으로부터 발생되는 음이온은 오염되어 가는 주변 환경을 개선하여 인체 건강의 균형을 유지 회복시켜 줄 수 있는 효과를 최대한 이용할 수 있게 되는 도기질 옥 타일 제조방법 및 도기질 타일 유약을 제공하고자 함에 목적이 있다.The present invention has been made to solve the above problems and defects as described above, to prepare a ceramic jade tile glaze containing jade and super anion, and to surface-treated the ceramic jade tile glaze on a building tile functional ceramic By producing nitrous jade tile, it uses far-infrared rays, antibacterial and deodorizing effect emitted from jade, which is beneficial to human body, and negative ions generated from super anion improve the polluted environment and maintain the balance of human health. The purpose is to provide a ceramic jade tile manufacturing method and ceramic tile glaze that can be used to the maximum.
위와 같은 목적을 달성하기 위하여 본 발명은 후리트, 카오린, 옥, 슈퍼 음이온으로 조성된 유약 조성물을 분쇄하는 공정에서 제품의 기능을 증가시키기 위하여 경도와 비중이 높은 옥을 잘 분쇄하기 위하여 옥을 카오린과 먼저 볼 밀에서 분쇄하여 325메쉬를 모두 균일하게 통과할 수 있게 한 후, 나머지 원료를 배합하여 제조한 옥이 잘 분산된 유약으로 표면처리하여 소성하므로 인체에 유익한 기능을 증가할 수 있게 되는 도기질 옥 타일 제조방법 및 도기질 타일 유약을 제공한다.In order to achieve the above object, the present invention provides kaolin for crushing jade with high hardness and specific gravity in order to increase the function of the product in the process of grinding the glaze composition composed of frit, kaolin, jade and super anion. And first pulverized in a ball mill to uniformly pass all the 325 mesh, and then jade prepared by mixing the remaining raw materials and surface treatment with a well-dispersed glaze firing ceramics that can increase the beneficial function to the human body Provided are jade tile manufacturing methods and ceramic tile glazes.
보다 구체적으로 본 발명에 의한 도기질 옥 타일 제조방법은 옥, 카오린, 물을 배합하는 1차 원료배합 단계와, 상기 배합된 원료를 습식으로 분쇄하는 1차 습식분쇄 단계와, 상기 분쇄된 원료에 후리트, 슈퍼 음이온, 물을 배합하는 2차 원료배합 단계와, 상기 배한된 원료를 습식으로 분쇄하는 2차 습식분쇄 단계를 행하여 유약을 제조하고, 상기 유약을 성형 건조 또는 1차 소성된 타일 위에 표면처리하는 표면처리 단계와, 1050∼1200℃로 소성하는 소성단계를 포함하여 구성된다.More specifically, the method for preparing a ceramic jade tile according to the present invention includes a primary raw material mixing step of combining jade, kaolin, and water, a primary wet grinding step of wet grinding the blended raw material, and the pulverized raw material. A secondary raw material blending step of blending frit, super anion, and water, and a secondary wet grinding step of wetly pulverizing the distributed raw material are used to prepare a glaze, and the glaze is formed on a mold dried or primary fired tile. It comprises a surface treatment step for surface treatment, and a firing step for firing at 1050 ~ 1200 ℃.
상기 1차 습식분쇄 단계에서는 관리기준 325메쉬를 전량 통과하도록 분쇄하며, 2차 습식분쇄 단계에서는 관리기준 325메쉬 잔량 1∼2중량% 이하가 되도록 분쇄한다.The first wet grinding step is pulverized so as to pass all the management standard 325 mesh, and in the second wet grinding step, the control standard 325 mesh is pulverized to 1 to 2% by weight or less.
본 발병의 도기질 옥 타일 유약은 후리트 72∼87중량%, 카오린 5∼10중량%, 옥 7∼15중량%, 슈퍼 음이온 1∼3중량%으로 조성된다.The ceramic jade tile glaze of the present invention is composed of 72 to 87% by weight of frit, 5 to 10% by weight of kaolin, 7 to 15% by weight of jade, and 1 to 3% by weight of super anion.
유약 조성에 옥을 넣으면 경도와 비중이 높기 때문에 일반 유약 원료보다 분쇄가 잘 되지 않는다. 그러므로 저장 시나 유약 표면처리 시에 침전이 생기며, 이로 인하여 균일한 표면처리를 할 수 없으므로 침전을 방지하기 위해서는 옥을 완전히 미분쇄하여야 하므로 옥과 카오린, 물 등을 같이 1차적으로 분쇄하여야 유약 조성 속 적은 량의 옥이 잘 분산되어 균질한 기능성 타일을 제조할 수 있다.When jade is added to the glaze composition, the hardness and specific gravity are high, which makes it harder to grind than ordinary glaze raw materials. Therefore, precipitation occurs during storage or surface treatment of glaze. Therefore, uniform surface treatment is not possible. Therefore, jade must be completely ground to prevent precipitation. Therefore, jade, kaolin, and water must be ground first. The amount of jade is well dispersed to produce a homogeneous functional tile.
단, 일반 유약의 제조방법인 타 원료들과 같이 경도가 높은 옥을 장시간 분쇄하였을 시 유약원료 성분 중 일부분의 알카리 성분이 물에 용출되어 제품의 표면에 영향을 주어 유면 갈라짐, 핀홀, 끓음, 탈색 등으로 품질을 저하시킨다.However, when the high hardness jade is pulverized for a long time like other raw materials for general glaze manufacturing, the alkali component of some of the glaze raw materials is eluted in water, affecting the surface of the product, resulting in cracking, pinholes, boiling, and discoloration of oil. The quality is lowered.
이와 같은 본 발병의 도기질 옥 타일 유약의 정량적 조성에서In this quantitative composition of the ceramic jade tile glaze of this outbreak
후리트가 72중량% 미만으로 배합되면 타일 품질이 요구하는 유약의 비중을 갖추기 어려워 품질이 떨어지고 생산량이 적어지며, 87중량%를 초과하면 습식 분쇄하기가 어렵고 단가가 상승한다, 카오린은 5중량% 미만이면 유약의 침전이 일어날 수 있고 점도 조절이 어렵우며, 10중량%를 초과하면 유약의 유동성이 떨어지고 표면의 발색이 떨어진다., 옥 7∼15중량%, 슈퍼 음이온 1∼3중량%으로 조성된다. 그리고, 상기 옥과 슈퍼 음이온은 가능한한 다량 첨가함이 좋으나 과량으로 첨가하면 단가 상승의 요인이 있다.If the frit is blended at less than 72% by weight, it is difficult to achieve the specific gravity of the glaze required by the tile quality, resulting in poor quality and low production.When it is more than 87% by weight, it is difficult to wet grind and the unit price increases. If less than it may cause precipitation of the glaze and difficult to control the viscosity, and if it exceeds 10% by weight, the fluidity of the glaze is reduced and the color of the surface is reduced, 7 to 15% by weight of jade, 1 to 3% by weight of super anion . In addition, the jade and the super anion may be added as much as possible, but when added in an excessive amount, there is a factor of an increase in unit cost.
본 발명에 사용되는 옥은 인체에 필요한 성분이 칼슘과 마그네슘을 함유하고 구성은 Mg6(OH)8Si4O10으로 되어 있으며, 엽록소의 구성 물질인 마그네슘이 40중량% 이상 함유하고 있어 인체 세포를 구성하고 있는 세포 역시 마그네슘으로 되어 있어 옥에서 나오는 기파동과 인체 세포의 기파동이 같은 파동이라 한다.The jade used in the present invention contains calcium and magnesium as components necessary for the human body, and the composition is composed of Mg 6 (OH) 8 Si 4 O 10 . The cells that make up are also made of magnesium, the same wave waves coming out of the jade and human cells are called waves.
또한 옥은 동의보감으로부터 인체의 열을 제거해 주고 편안하게 하며 비만을 방지해 주고, 미세한 가루를 먹으면 몸 속에 찌거기가 체외로 배출된다고 기재되어 있으며 본초강목에는 오장육부를 윤택하게 하고 체내의 노폐물을 완전히 배출시켜 주는 효과가 있으며, 위증의 열을 제거하여 소화 계통의 효과가 있고, 기관지 천식, 신열이 나고 가슴이 답답한 증상에 효과가 있으며, 빈혈증에 좋고, 갈증도 해소시키며, 폐장의 기능을 원활하게 하고, 성대의 발성을 도와주고, 인후에도 좋으며, 모발에 영향을 조고, 오장의 기능을 자양해 주며, 특히 스트레스등 신경성 질환을 가라앉히는 효과가 있다고 기재되어 있어 이미 건강에 유익하다는 것이 알려져 있다.In addition, jade removes heat from the body and comforts the body and prevents obesity, and when it is eaten, it is described that the trash is discharged to the outside of the body. It is effective in the digestive system by removing the heat of gastric juice. It is effective for bronchial asthma, fever and stuffy chest. It is good for anemia. It also relieves thirst. It is said to be beneficial for health because it is said to help the vocal cords, good for throat, affect hair, nourish the intestine, and reduce the nervous diseases such as stress.
그리고 슈퍼 음이온은 1cc당 31,000개에 달하는 음이온을 발산하며, 인체에 대한 효과로는 혈액의 정화 작용, 즉 음이온은 혈액 중에 미네랄 성분인 칼슘, 나트륨, 칼륨 등의 이온화 율을 상승시켜 알카리화의 진행을 통해 혈액을 정화시켜주고, 앤돌핀, 엔케피린이라는 물질을 발생시킴으로 인해 혈청 속에 칼슘과 나트륨의 이온화율의 상승으로 혈액정화, 피로회복, 체력의 회복 뿐 아니라 강한 통증이 있던 부분의 세포를 건강하게 활성화시켜 통증이 완화된다. 또 세포막에서의 전기적 물질교류로 혈액을 정화해 주기도 하고, TV, PC 이동전화를 포함한 각종 전자, 전기제품에서 방출되는 X선, R선, 전리방사선, 자외선 등은 높은 에너지를 갖고 있으며, 이것은 공기 중에서 양이온을 생성하는 원인이 되며, 양이온의 숫자가 많아지면 천식, 기관지염, 두통, 시각장애, 요통, 어깨 결림, 신경과민, 긴장고조, 생리불순, 무기력증, 우울증, 피부염, 기형아 출산 등과 같은 병을 유발할 수 있다.Super anions emit 31,000 anions per 1cc, and the effect on the human body is the purification of blood, that is, the anion increases the ionization rate of calcium, sodium, potassium, etc. It cleanses the blood and raises the ionization rate of calcium and sodium in the serum by generating substances such as androphine and enkepyrin, which not only cleanses blood, recovers fatigue, recovers stamina, but also restores the cells in the area of strong pain. It can be activated to relieve pain. It also purifies the blood through the exchange of electrical substances in cell membranes. X-rays, R-rays, ionizing radiation, and ultraviolet rays emitted from various electronics and electrical appliances, including TVs and PCs, have high energy. It causes the formation of cations in the liver, and if the number of cations increases, diseases such as asthma, bronchitis, headache, visual impairment, low back pain, stiff shoulder, nervousness, tension, dysmenorrhea, lethargy, depression, dermatitis, birth defects, etc. May cause
그러나 음이온은 (-)전하를 띤 공기의 요소로써 유해한 양이온을 중화시키고, 피를 맑게하며, 신경 안정과 피로회복, 식용증진, 세포의 활성화를 촉진시켜 생기있는 생활을 영위케하는 효과가 있으며 이외에도 저항력 증가 작용, 자율신경계 조절작용, 공기 정화작용, 살균 작용 등의 효과가 있다.Negative ions, however, are negatively charged air elements that neutralize harmful cations, clear blood, promote nerve stabilization, fatigue recovery, food intake, and cell activation. It has the effect of increasing resistance, autonomic nervous system control, air purification, sterilization.
본 발명에 의해 제조된 기능성 도기질 옥 타일을 실내의 바닥 또는 벽면에 시공하면 옥 타일의 표면인 유약층에서 원적외선과 음이온이 방사되어 사용자의 건강증진 효과를 얻고, 항균, 탈취 작용으로 각종 세균을 제거하며, 주위 공기를 정화시켜 실내 환경 개선하는 효과가 있다.When the functional ceramic jade tile prepared by the present invention is applied to the floor or wall of the room, far infrared rays and anions are radiated from the glaze layer, which is the surface of the jade tile, to obtain a health promoting effect of the user, and to prevent various bacteria by antibacterial and deodorizing action. It removes and purifies the surrounding air, thereby improving the indoor environment.
이하, 본 발명에 의한 도기질 옥 타일 제조방법 및 도기질 타일 유약에 관하여 실시예를 들어 보다 구체적으로 설명하면 다음과 같다.Hereinafter, the ceramic jade tile manufacturing method and the ceramic tile glaze according to the present invention will be described in more detail with reference to Examples.
본 발명에 의한 도기질 옥 타일 제조방법은 옥, 카오린, 물을 배합하는 1차 원료배합 단계와, 상기 배합된 원료를 습식으로 분쇄하는 1차 습식분쇄 단계와, 상기 분쇄된 원료에 후리트, 슈퍼 음이온, 물을 배합하는 2차 원료배합 단계와, 상기 배한된 원료를 습식으로 분쇄하는 2차 습식분쇄 단계를 행하여 유약을 제조하고, 상기 유약을 성형 건조 또는 1차 소성된 타일 위에 표면처리하는 표면처리 단계와, 1050∼1200℃로 소성하는 소성단계를 포함하여 기능성 옥타일 제품을 제조하는 것으로 되어 있다.The ceramic jade tile production method according to the present invention comprises a primary raw material mixing step of combining jade, kaolin, water, the first wet grinding step of wet grinding the blended raw materials, and the frit to the pulverized raw material, A secondary raw material blending step of combining super anion and water, and a secondary wet grinding step of wet grinding of the distributed raw material to produce a glaze, and the glaze is surface-treated on a molded dry or primary fired tile It is intended to produce a functional octale product, including a surface treatment step and a firing step of firing at 1050 to 1200 ° C.
상기 습식분쇄는 통상의 볼밀을 이용하여 하며, 1차 습식분쇄 단계에서는 관리기준 325메쉬를 전량 통과하도록 분쇄하며, 2차 습식분쇄 단계에서는 관리기준 325메쉬 잔량 1∼2중량%가 되도록 분쇄하여 도기질 옥 타일 유약을 제조한다.The wet grinding is performed using a conventional ball mill, and in the first wet grinding step, pulverizes to pass the entire management standard 325 mesh, and in the second wet grinding step, the grinding standard is pulverized to 1 to 2% by weight of the control standard 325 mesh. Manufactures quality jade tile glazes.
위와 같은 과정으로 제조된 본 발명에 의한 도기질 옥 타일 유약은 후리트 72∼87중량%, 카오린 5∼10중량%, 옥 7∼15중량%, 슈퍼 음이온 1∼3중량%으로 조성된다.Ceramic pottery glaze according to the present invention prepared by the above process is composed of 72 to 87% by weight of frit, 5 to 10% by weight of kaolin, 7 to 15% by weight of jade, 1 to 3% by weight of super anion.
상기한 과정으로 제조된 유약은 적정한 장소에 보관하고 필요에 따라 사용하며, 이 도기질 옥 타일 유약을 성형 건조 또는 1차 소성된 타일 위에 표면처리하고 1050∼1200℃로 소성하여 기능성 옥타일 제품을 제조한다.The glaze prepared by the above process is stored in an appropriate place and used as necessary.The ceramic octane glaze is surface-treated on a mold dried or primary fired tile and calcined at 1050-1200 ° C. to produce a functional octale product. Manufacture.
유약 조성에 옥을 넣으면 경도와 비중이 높기 때문에 일반 유약 원료보다 분쇄가 잘 되지 않는다. 그러므로 저장 시나 유약 표면처리 시에 침전이 생기며, 이로 인하여 균일한 표면처리를 할 수 없으므로 침전을 방지하기 위해서는 옥을 완전히 미분쇄하여야 하므로 옥과 카오린, 물 등을 같이 1차적으로 분쇄하여야 유약 조성 속 적은 량의 옥이 잘 분산되어 균질한 기능성 타일을 제조할 수 있다.When jade is added to the glaze composition, the hardness and specific gravity are high, which makes it harder to grind than ordinary glaze raw materials. Therefore, precipitation occurs during storage or surface treatment of glaze. Therefore, uniform surface treatment is not possible. Therefore, jade must be completely ground to prevent precipitation. Therefore, jade, kaolin, and water must be ground first. The amount of jade is well dispersed to produce a homogeneous functional tile.
상기 슈퍼 음이온은 (주)환경 코리아에서 제조되고, 모나자이트를 함유한 Ce, La, Nd, Th와 PO4의 화합물으로서 음이온 발생 물질인 KN-100을 사용하는 것이 바람직하나, 다른 제품도 사용할 수 있다.The super anion is manufactured by Environment Korea Co., Ltd. It is preferable to use an anion generating material KN-100 as a compound of Ce, La, Nd, Th and PO 4 containing monazite, but other products can also be used. .
상기 도기질 옥 타일 유약에 사용된 옥 분말의 성분은 다음과 같다.The components of the jade powder used in the ceramic jade tile glaze are as follows.
옥 분말의 성분Ingredients of jade powder
참고로, 상기 분석은 요업기술원의 분석결과이며, 상기 분석에 사용된 KP-OES는 PERKIN-ELMER의 OPTIMA 3300DV이다.For reference, the analysis is an analysis result of the Korea Institute of Industrial Technology, KP-OES used in the analysis is OPTIMA 3300DV of PERKIN-ELMER.
이와 같은 본 발명에 의한 도기질 옥 타일 제조방법의 실시예를 종래의 비교예와 구체적으로 비교 설명하면 다음과 같다.When explaining the embodiment of the ceramic jade tile manufacturing method according to the present invention in detail compared with the conventional comparative example as follows.
상기 실시예의 도기질 옥 타일 유약은 본 발명에 따라 옥, 카오린, 물을 1차로 배합하고, 습식분쇄한 후, 분쇄된 원료에 후리트, 슈퍼 음이온, 물을 2차로 배합하여 습식분쇄하는 과정으로 제조한 것이다.According to the present invention, the ceramic jade tile glaze according to the present invention is primarily a combination of jade, kaolin, and water, followed by wet milling, followed by wet blending of frits, super anions, and water in the milled raw material by secondary blending. It is manufactured.
본 발명의 실시예에서 사용된 표면처리 방법은 분무 시유를 하였고, 유약 비중은 1.70으로 하고, 유약 무게는 200X250mm 타일에 40g을 하였다. 또, 실시예별로 유약을 만들고, 완전히 건조된 타일 또는 1차 소성된 타일 위에 표면처리하여 연속롤러가마에서 1080℃∼1175℃로 소성하여 제품화하였다.The surface treatment method used in the embodiment of the present invention was sprayed oil, the specific gravity of the glaze was 1.70, the weight of the glaze was 40g to 200X250mm tile. In addition, glazes were made for each embodiment, and surface-treated on a completely dried tile or a first calcined tile, and then fired at 1080 ° C. to 1175 ° C. in a continuous roller kiln to produce a product.
또한, 본 발명에 의해 제조된 기능성 옥타일을 유약 조성만 시험한 결과 옥은 15g 내에서 많이 사용하면 좋으나, 가격이 고가이므로 최소한으로 사용하고, 슈퍼 음이온도 1g 내에서 사용함으로써 원가절감의 효과를 볼 수 있는 결과를 얻었다.In addition, as a result of testing only the glaze composition of the functional octale produced according to the present invention, jade is good to use a lot within 15g, but because the price is expensive, use it at a minimum, and also use super anion within 1g to reduce the cost A visible result was obtained.
그리고, 시험에 따른 분석은 사단법인 한국원적외선협의회의 한국원적외선 응용평가연구원의 측정결과이다.The analysis according to the test is the result of the Korea Far Infrared Applied Evaluation Institute of Korea Far Infrared Council.
실시예(본 발명)Example (Invention)
실시예의 시험분석결과Test Analysis Result of Example
비교예(종래 타일)Comparative example (conventional tile)
비교예의 시험분석 결과Test Analysis Result of Comparative Example
위 분석의 비교 결과 종래의 타일 보다 본 발명에 의한 타일이 원적외선, 음이온, 항균감소, 탈취작용 기능성의 효과가 향상됨이 확인되었다.As a result of the comparison of the above analysis, it was confirmed that the tile according to the present invention improves the effect of far-infrared rays, anions, antibacterial and deodorizing functions than the conventional tiles.
이상에서 설명한 바와 같은 본 발명에 의한 기능성 자기질 옥 타일은 실내의 바닥 또는 벽면에 시공하면 옥 타일의 표면인 유약층에서 원적외선과 음이온이 방사되어 사용자의 건강증진에 큰 효과를 줄 수 있으며, 항균, 탈취 작용으로 각종 세균을 제거하고 그 배양을 방지해 주며, 각종 악취와 그 주변의 공기까지 정화시켜 실내 환경을 보다 쾌적하고 아름다운 주거 환경을 만들 수 있는 이점과 효과가 있다. Functional magnetic jade tile according to the present invention as described above can be far-infrared and negative ions are radiated from the glaze layer that is the surface of the jade tile when installed on the floor or wall of the room can have a great effect on the health of the user, antibacterial, The deodorizing action removes various germs and prevents their culture, and cleans up various odors and the air around them to make the indoor environment more comfortable and beautiful.
이상에서 설명한 바와 같은 본 발명에 의한 기능성 도기질 옥 타일은 실내의 바닥 또는 벽면에 시공하면 옥 타일의 표면인 유약층에서 원적외선과 음이온이 방사되어 사용자의 건강증진에 큰 효과를 줄 수 있으며, 항균, 탈취 작용으로 각종 세균을 제거하고 그 배양을 방지해 주며, 각종 악취와 그 주변의 공기까지 정화시켜 실내 환경을 보다 쾌적하고 아름다운 주거 환경을 만들 수 있는 이점과 효과가 있다.Functional ceramic jade tile according to the present invention as described above can be far-infrared and negative ions are radiated from the glaze layer that is the surface of the jade tile when installed on the floor or wall of the room can have a great effect on the health of the user, antibacterial By deodorizing action, it removes various germs and prevents its cultivation, and also cleans various odors and the surrounding air and has the advantage and effect to make indoor environment more comfortable and beautiful living environment.
Claims (3)