KR20050062473A - Jellied pack contained yellow soil. - Google Patents

Abstract

The present invention relates to a manufacturing method of a gel-type pack containing ocher, and more particularly, a surface of a gel-form suspended by mixing pine needle essential oil, a moisturizer, a nutrient preservative, and the like with ocher. The present invention relates to a method for manufacturing a nonwoven fabric pack containing ocher, which has a cosmetic effect by cutting a sheet formed by pouring a gel into a thin sheet (sheet) or a nonwoven fabric and forming a gel by attaching it to a face. .

For this purpose, ocher sedimentation process is obtained by suspending ocher in water to separate sediment, and cosmetics such as pine needle essential oil and moisturizer, nutrients surfactant, whitening agent, antioxidant, preservative, fragrance, coloring agent etc. In addition to the mixing process, the powder dissolving step of heating and dissolving the mixture such as kappa-carrageenan, locust bean gum, reaction inhibitor, solubilizer and gel-forming agent by heating and heating, and cooling the stomach gelling agent to a certain temperature and then mixing the cosmetic agent A gelling agent mixing step of adding ocher to the gelling agent, a gelling agent preparation step of adding calcium compound directly involved in gel formation, a gel forming step of gelling a gelling agent on a flat cotton or nonwoven fabric, and a gel sheet or gel Mask cutting process that forms a mask shape by drilling holes in the parts of eyes and nose on the nonwoven fabric with sheet It consists of a packaging process in a polyethylene derephthalate bag, which gels the loess containing the moisturizing nutrient, etc., so that it does not flow down like a conventional pack, but eliminates the inconvenience of having to wash the face with muddy water like a conventional ocher pack. There is an effect of doubling the sorry effect by using the pack contained.

Description

Gel pack with ocher and its manufacturing method. {Jellied pack contained yellow soil.}

The present invention relates to a method of manufacturing a gel-pack (pack) with ocher added, and more particularly, gel formed by suspending ocher mixed with a moisturizer, nutrient preservative, etc. on a flat surface to form a gel. It is to provide a method for producing a gel-packed pack with ocher added to the face by cutting a mask formed by pouring a gel formed on a thin sheet (sheet) or non-woven surface to give a cosmetic effect.

Conventionally, the conditions required for the pack should be easy to apply with a suitable viscosity when used, should be easily peeled off while at the same time giving tension to the skin while drying in a suitable time, and a soft and moist texture should be maintained after use.

In addition to the usual method of applying a thin plate of vegetables or fruits to the face, the pack is coated with a transparent or translucent gel-type pack material to absorb the peel off type and beauty material that peels off the film formed on the skin after drying. Nonwoven fabric packs that are put on the face and the wash off type (wash off type) to wash with water after drying, such as clay or jelly form.

The flaking method of vegetables and fruits is one of the hassle of having to be blown one by one and the flaw that falls when moving, and the peel-off type has the hassle of peeling off over time, and the non-woven type has a cloth infiltrating essence or lotion. (浸潤) There is a limit to the amount of cosmetic materials absorbed by the cloth and there is a inconvenience to flow down if you absorb a large amount.

In recent years, attempts to obtain cosmetic effects by applying clay or ocher from Getul are spreading like fashion, and pack materials using clay or ocher have been released.

In general, the chemical composition of ocher contains a small amount of iron oxide, calcium, magnesium, etc. in addition to silicon dioxide and aluminum oxide. Plasticity is shown together with the viscosity.

Also, it is known that ocher is known to prevent aging of skin and decompose and destroy cancer and abnormal cells by neutralizing dilution of oxidative lipids such as catalase and protease, which release and contain a large amount of far infrared rays. Demand is increasing rapidly.

However, the wash-off type using ocher or clay has the inconvenience of washing off after drying and muddy water gets into your eyes or clothes.

The present invention uses a mask made of a sheet gelled by suspending ocher mixed with a cosmetic agent in a gelling agent such as kappa-carrageenan to improve the defects of the prior art as a pack to remove or wash as conventionally An object of the present invention is to provide a gel-packed pack and a method of manufacturing the same.

In addition, kappa-carrageenan used in the ocher-added gel pack of the present invention is brittle because of its brittleness due to elongation when calcium ions are added. In order to remove defects and adhere to the face to enhance the aesthetic effect, the locust bean gum is added to increase the flexibility, and the gel shrinks even after a long time, and the gel pack containing the ocher that contains water-containing components does not separate and provides a method of manufacturing the same. For another purpose.

The ocher-added gel pack of the present invention is a loess line process in which ocher is suspended in water to separate ocher obtained by separating the earth and sand, and pine needle essential oil, moisturizer, nutrient, surfactant, whitening agent, and oxidation A process for mixing cosmetic ingredients that adds an inhibitor, a preservative, a fragrance, a pigment, and the like, and a gelling agent dissolving process in which water is added to a mixture of a kappa-carrageenan and locust bean gum by adding water to a mixture containing a reaction inhibitor and a dissolving agent. After cooling the gelling agent to a certain temperature, the ocher absorbing the cosmetic agent is suspended in the gelling agent, and a gelling agent preparation step of adding a coagulant directly involved in gel formation such as calcium sulfate, calcium lactate, calcium gluconate, and the flat side Gel forming process to form a gel sheet by pouring a gel agent on the nonwoven fabric or to form a gel on the nonwoven fabric surface. It consists of a mask cutting process for cutting in the form of a scrub, a packaging process for putting aluminum foil-coated polyethylene, a derephthalate into a bag, and the like.

Hereinafter, a gel-pack containing the loess of the present invention and a manufacturing method thereof will be described according to processes based on the accompanying drawings.

1 is a process diagram schematically showing a pack using the loess of the present invention and a method of manufacturing the same.

(a) refers to the ocher from which the epidermis is removed. ) It is a process of loess sedimentation, which separates soil fines and separates only fine particles of ocher and grinds them with a wet grinding machine. (S110)

(b) is a cosmetic material mixing process of adding essential oils, moisturizers, nutrients whitening agents, antioxidants, surfactants, preservatives, fragrances, and pigments to the stomach loess. (S120)

Essential oils obtained by steam distillation of pine needles include alpha-pinene, beta-pinene, dl-limonene, beta-phellandrene, and camphor (( In addition to cam-phene, bornylacetate and polyporenic acid, it contains many active ingredients and is effective in sedation, dizziness, shortness of breath, diuresis, hypoglycemia, and health. Research meeting)

Beauty agents include moisturizers and nutrients. Moisturizers include propylene glycol, sorbitol, dipropylene glycol, butylene glycol, and hydrated sodium hyaluronate. , P, methyl, glucoside, glycerin, etc., and emulsions include Squalane, Liquid paraffin, Olive oil, Castor oil ( Castor oil, Stearic acid, Cetyl alcohol, etc.As the active agent, POE (12) nonyl phenyl ether, Polysorbate 60, Potassium stearate (Potassium stearate), and other active ingredients and nutrients include Allantoin, DL-Panthenol, Methyl parabene, Propyl parabene as preservatives and others. Fragrance PH regulator.

(c) adds sodium hexaphosphate, a condensed phosphate, as a reaction inhibitor, and delta lactone gluconate as a solubilizer, to a mixture of 0.2 to 0.8% kappa-carrageenan and 0.3 to 0.7% locust bean as a gelling agent, followed by heating with water. It is a gelling agent dissolution process. (S130)

(d) is a gelling agent preparation step in which the loess which mixed the cosmetic material of step (b) is added to the gelling agent of step (c) above, and calcium calcium lactate, calcium gluconate, calcium sulfate and the like are added as a gel forming agent. (S140)

(e) is a gel forming process in which the gelling agent prepared in (d) above is poured on a flat bottom to form a gel sheet or on a nonwoven fabric to produce a gel. (S150)

(f) is a mask cutting process which cuts the gel sheet containing the loess of the process (e) or the gel sheet with a nonwoven fabric in the form of a mask. (S160)

(g) is a packaging process in which the finished pack is put into a polyethylene derephthalate bag covered with aluminum foil and vacuum packed.

In general, a gel is formed upon addition of calcium ions to the gelling agent. As a reaction inhibitor added to delay the reaction, condensed phosphates such as sodium hexametaphosphate are used, and these condensed phosphates block calcium ions of the added calcium salt. It changes to a colloidal insoluble calcium compound to block the reaction with the gelling agent.

In the above reaction, depending on the amount of condensation phosphate added, the gel formation time is shortened from a dozen hours to several minutes. As the gel formation time is longer, the gel strength is lowered. In the present invention, 0.16% to 0.24% by weight of hexametaphosphate is added. .

The percentages listed are in weight percent relative to the total gel fire prepared.

In addition, delta lactone gluconate added as a disintegrating agent decomposes into gluconic acid and lactone acid in the solution, converts the insoluble calcium compound in the colloidal state into a soluble salt, and proceeds with the gelling agent. It is shortened or lengthened and delta lactone gluconate is added at 0.20% to 0.50% by weight.

Coagulants that form a gel by reacting with a gelling agent include calcium lactate, calcium gluconate, calcium sulfate, and the like. In the present invention, 0.10% to 0.9% by weight of calcium sulfate is added and the gel formation time depends on the amount of calcium compound added. The strength of the gel is shortened or lengthened, and the strength of the gel is proportional to the amount added. If the strength of the gel is high, the elasticity of the gel is insufficient, resulting in the formation of a crushable or brittle gel, which is unsuitable for the pack material.

An embodiment of the present invention will be described in detail as follows.

Example 1

This embodiment relates to a pack and a method for producing the same, wherein the loess to which the hazel extract (Witch haze1 extract) having a convergence effect, prepared by the following mixing ratio, is suspended in a sol of kappa-carrageenan and locust bean gum and gelled Would

60% of water, ocher 20%, pine needle essential oil 0.4%, Ethanol 14.5%, Glycerine 1.0%, Butylene glycol 0.4%, Phenylsiloxane 0.2%, Hazel Witch hazel extract 1.1%, POE 60 hydrogenated castor oil (0.2%), Perfume (0.2%), methyl paraben (0.1%) and propyl paraben (prep) 0.01%, nutrient (DL-Panthenol) 0.16%, activator (Allantoin) 0.09gr and the like kappa-carrageenan 0.6%. 0.5% of locust bean gum was suspended in a colloidal solution dissolved by heating, and then uniformly mixed by adding 0.18% of hexameta phosphate and 0.16% of delta-lactone gluconate, followed by stirring with 0.20% of calcium sulfate, and then pouring into a flat or nonwoven surface. Pour it into gel and cut it into a mask.

The gel produced in this way has no crushing effect due to the elasticity and has the flexibility not to be crushed by excessive bending, so it adheres to the face, so that the absorption of beauty materials is easy and it contains various beauty materials. .

Example 2

This embodiment is the ocher added with phenyl siloxane (Phenyl siloxane) to give the flexibility and moisturizing effect prepared by the following mixing ratio and POE (60) hydrogenated castor oil (POE (60) hydrogenated castor oil) to disperse it The present invention relates to a pack prepared by suspending in a sol of kappa-carrageenan and locust bean gum and gelling.

62% water, 22% fine ocher, 0.4% pine needle essential oil, 6.5% ethanol, glycerin 3.0%, butylene glycol 3.0%, phenyl siloxane 0.5%, POE ( 60) hydrogenated castor oil (POE (60) hydrogenated castor 0.26%, Perfume 0.3%, preservative (Methyl paraben) 0.1%, preservative (Propyl paraben) 0.02% and the like kappa-carrageenan 0.7%. Was suspended in a colloidal solution dissolved in heat and then mixed evenly by adding 0.20% of hexameta phosphate and 0.18% of delta lactone gluconate, followed by stirring with addition of 0.24% of calcium sulfate, followed by pouring onto a flat surface or pouring into a nonwoven fabric. After cutting, cut into a mask form.

The gel produced in this way is a pack material having no flexibility due to the swelling property and does not bend in excess of bending, having suitable gel properties and containing various cosmetic materials, thereby having excellent cosmetic effects.

Example 3

This embodiment relates to a pack of a nonwoven fabric using kappa-carrageenan and locust bean gum to which citric acid, which has a weakly acidic effect produced by the following formulation ratio, is added, and a manufacturing method thereof.

61% of water, ocher 24%, pine needle essential oil 0.4%, ethanol 5.5%, glycerin 2.5%, butylene glycol 3.7%, POE (20) cetyl oleate (POE (20) ) cetyl oleate) 0.52%, Perfume 0.2%, Preservative (Methyl paraben) 0.09%, Preservative (Propyl paraben) 0.01%, Citric acid (0.01%), DL-Panthenol (0.2%), Allantoin 0.24%, kappa-carrageenan 0.5%. 0.5% of locust bean gum was suspended in a colloidal solution dissolved in heat, and mixed uniformly by adding 0.21% of hexameta phosphate and 0.19% of delta lactone gluconate, followed by stirring by adding 0.23% of calcium sulfate, or pouring into a non-woven surface Pour it into gel and cut it into a mask.

The gel produced in this way has no brittleness due to the elasticity and is in close contact with the face because of its flexibility, thus facilitating the absorption of beauty materials and containing various beauty materials.

As described above, the gel pack of the present invention to which ocher of the present invention is added, in particular, the gelation agent of kappa-carrageenan and locust bean gum, in which ocher containing a cosmetic agent is suspended, is gelled with soluble calcium salt. There is no crushing effect due to the excellent flexibility and because it does not break when put on the face closes the beauty effect.

In addition, the conventional nonwoven pack is limited in the amount of moisturizers or nutrients absorbed in a single nonwoven fabric, but the content of the active ingredient of the gel pack containing the loess of the present invention is controlled by the thickness of the gel, so its effectiveness is very high.

1 is a process chart showing a manufacturing method of a gel pack to which ocher of the present invention is added.

* Explanation of Signs of Major Parts of Drawings "

100. Yellow ocher 200. Ocher mixed with beauty ingredients

300. Dissolved gelling agent 400. Prepared gelling agent

500. Gel Sheet 600. Cut Mask

Claims (1)

(a) the loess from which the epidermis is removed is called with water. Ocherous sedimentation process for separating and grinding only the fine particles of ocher after sedimentation; (S110) (b) a cosmetic material mixing process of adding pine needle essential oil, moisturizer, nutrient whitening agent, antioxidant, surfactant, preservative, fragrance, pigment, etc. to the yellow loess; (S120) (c) a gelling agent dissolving step of adding sodium hexa phosphate and delta lactone gluconate to a mixture of 0.2 to 0.8% kappa-carrageenan and 0.3 to 0.7% locust bean gum as a gelling agent, followed by heating with water; (S130) (d) a gelling agent preparation step of suspending ocher mixed with the cosmetic material of step (b) to the gelling agent of step (c) and adding 0.10% to 0.9% by weight of calcium antioxidant; (S140) (e) a gel forming step of producing a gel by pouring the gelling agent of step (d) on a flat bottom to form a gel sheet or by pouring on a nonwoven fabric; (S150) (f) a pack of ocher-added gel form comprising a mask cutting process (S160) for cutting a gel sheet containing ocher in step (e) or a gel sheet with nonwoven fabric in the form of a mask; Its manufacturing method.