KR20050044990A - Two-component type water-soluble adhesive composition for floor - Google Patents
Two-component type water-soluble adhesive composition for floor Download PDFInfo
- Publication number
- KR20050044990A KR20050044990A KR1020030079057A KR20030079057A KR20050044990A KR 20050044990 A KR20050044990 A KR 20050044990A KR 1020030079057 A KR1020030079057 A KR 1020030079057A KR 20030079057 A KR20030079057 A KR 20030079057A KR 20050044990 A KR20050044990 A KR 20050044990A
- Authority
- KR
- South Korea
- Prior art keywords
- water
- adhesive composition
- flooring
- aqueous adhesive
- resin
- Prior art date
Abstract
본 발명은 바닥재용 2액형 수성접착제 조성물에 관한 것으로, 특히 수용성 에폭시 수지, 무기충진제 및 물을 함유하는 주제와, 수용성 에폭시 경화제 수지, 경화촉진제, 무기충진제 및 물을 함유하는 경화제를 포함하는 바닥재용 2액형 수성접착제 조성물에 관한 것이다.The present invention relates to a two-component aqueous adhesive composition for flooring, and in particular, for a flooring comprising a water-soluble epoxy resin, an inorganic filler and a water-containing epoxy resin, a water-soluble epoxy curing agent resin, a curing accelerator, an inorganic filler and a curing agent containing water. A two-component aqueous adhesive composition.
본 발명의 바닥재용 2액형 수성접착제 조성물은 종래 유기용제를 사용하여 야기되던 독성 방출, 오존 고갈, 가연성, 함불소 화합물 발생 등의 문제로 인한 환경파괴를 해결하여 환경친화적일 뿐만 아니라, 시공시 또는 시공 후 심한 약품냄새의 발생을 억제하여 별도의 환기를 시키지 않고도 작업자가 작업하기에 용이하고, 입주자가 시공한 건물에 입주하였을 경우 코끝을 찌르는 듯한 불쾌취를 느끼지 않고 편안하게 생활할 수 있는 바닥재용 2액형 수성접착제 조성물에 관한 것이다.The two-component aqueous adhesive composition for flooring according to the present invention solves environmental degradation due to problems such as toxic emission, ozone depletion, flammability, fluorine-containing compounds, etc. caused by conventional organic solvents. It is easy for workers to work without restraining the occurrence of severe chemical smell after construction, and when living in the building where the tenant is constructed, the flooring material can live comfortably without feeling the discomfort like piercing the nose. A two-component aqueous adhesive composition.
Description
본 발명은 바닥재용 2액형 수성접착제 조성물에 관한 것으로, 더욱 상세하게는 종래 유기용제를 사용하여 야기되던 독성 방출, 오존 고갈, 가연성, 함불소 화합물 발생 등의 문제로 인한 환경파괴를 해결하여 환경친화적일 뿐만 아니라, 시공시 또는 시공 후 심한 약품냄새의 발생을 억제하여 작업자가 작업하기에 용이하고, 입주자가 시공한 건물에 입주하였을 경우 코끝을 찌르는 듯한 불쾌취를 느끼지 않고 편안하게 생활할 수 있는 바닥재용 2액형 수성접착제 조성물에 관한 것이다.The present invention relates to a two-component aqueous adhesive composition for flooring, and more particularly, it is environmentally friendly by solving environmental degradation due to problems such as toxic emission, ozone depletion, flammability, fluorine-containing compounds, etc. caused by conventional organic solvents. In addition, it is easy for workers to work by suppressing the occurrence of severe chemical odor at the time of construction or after construction, and the flooring material which can live comfortably without feeling the discomfort like pricking the tip of the nose when the tenant moves into the constructed building. It relates to a two-component aqueous adhesive composition for use.
건축내장재는 나날이 고급화되고 있는 실정이며, 이에 따라 실내의 바닥면에 온돌마루판이 널리 시공되고 있다. 특히, 상기 온돌마루판을 시멘트 몰탈 처리된 온돌바닥에 부착하기 위하여 에폭시계 접착제가 주로 이용되어 왔다.Building interior materials are becoming more and more advanced day by day, according to which the flooring floor is widely installed on the floor of the interior. In particular, epoxy adhesives have been mainly used to attach the ondol floor to cement mortar-treated ondol floors.
상기 에폭시계 접착제는 에폭시 수지를 주제로, 폴리아미드, 아민(amine) 등을 경화제로 포함하는 2액형 접착제이나, 시멘트 몰탈 등으로 이루어진 무기계 하지면에 유기계 접착제를 사용함으로써 재료의 이질감에서 오는 시공상의 문제는 물론, 독성 방출, 오존 고갈, 가연성, 함불소 화합물 발생 등의 문제로 인하여 환경 규제의 대상이 되는 등 여러 문제가 대두되었다.The epoxy adhesive is composed of epoxy resin, a two-component adhesive containing polyamide, amine, or the like as a curing agent, or an organic adhesive on an inorganic base surface made of cement mortar or the like. As well as problems, toxic emissions, ozone depletion, flammability, fluorine-containing compounds, etc. have caused a number of problems, such as being subject to environmental regulations.
즉, 상기 유기계 접착제는 벤젠, 톨루엔, 자일렌 등의 유독성 유기용제를 사용함으로써 작업시 심한 약품 냄새로 인하여 작업자의 두통이나 호흡곤란 등의 문제를 초래한다는 문제점이 있다. That is, the organic adhesive has a problem of causing a headache or difficulty in breathing due to a bad smell of the drug during the work by using a toxic organic solvent such as benzene, toluene, xylene.
이에 따라, 대한민국 특허출원 제2001-0052292호는 수경성 폴리머 시멘트를 주성분으로 하여 유해가스 방출을 억제할 수 있는 수경성 무기계 접착제에 대하여 개시하고 있다. 그러나, 상기 접착제는 여전히 약품 냄새를 방출하여 작업이 어려울 뿐만 아니라, 120 ℃ 이상의 고온에서만 경화한다는 문제점이 있다.Accordingly, Korean Patent Application No. 2001-0052292 discloses a hydraulic inorganic adhesive that can suppress the emission of harmful gases mainly based on hydraulic polymer cement. However, the adhesive still emits a chemical smell and is difficult to work with, and has a problem of curing only at a high temperature of 120 ° C. or higher.
따라서, 시공시 또는 시공 후 심한 약품냄새의 발생을 억제하여 작업자가 작업하기에 용이하며 환경친화적일 뿐만 아니라, 상온에서 경화가능한 마루판용 수성접착제에 대한 연구가 더욱 필요한 실정이다.Therefore, it is necessary to study the water-based adhesive for floorboards that can be easily and environmentally friendly and harden at room temperature by suppressing the occurrence of severe chemical smell during or after construction.
상기와 같은 종래기술의 문제점을 해결하고자, 본 발명은 시공시 또는 시공 후 심한 약품냄새의 발생을 억제하여 별도의 환기를 시키지 않고도 작업자가 작업하기에 용이하고, 입주자가 시공한 건물에 입주하였을 경우 코끝을 찌르는 듯한 불쾌취를 느끼지 않고 편안하게 생활할 수 있으며, 상온에서 경화가 가능한 바닥재용 2액형 수성접착제 조성물을 제공하는 것을 목적으로 한다.In order to solve the problems of the prior art as described above, the present invention is easy for the worker to work without additional ventilation by suppressing the occurrence of severe chemical smell during construction or after construction, when the occupant moved into the building It is an object of the present invention to provide a two-component aqueous adhesive composition for flooring that can be comfortably lived without feeling an unpleasant odor, such as a stab nose.
본 발명의 다른 목적은 종래 유기용제를 사용하여 야기되던 독성 방출, 오존 고갈, 가연성, 함불소 화합물 발생 등의 문제로 인한 환경파괴를 해결하여 환경친화적인 바닥재용 2액형 수성접착제 조성물을 제공하는 것이다. Another object of the present invention is to provide an environmentally friendly two-component aqueous adhesive composition for flooring by solving environmental damage caused by problems such as toxic emission, ozone depletion, flammability, fluorine-containing compounds generated by using conventional organic solvents. .
본 발명의 또다른 목적은 시공시 또는 시공 후 심한 약품 냄새의 방출이 억제하고, 독성 방출, 오존 고갈, 가연성, 함불소 화합물 발생 등의 문제를 해결하여 환경친화적일 뿐만 아니라, 동시에 상온경화가 가능하여 상온에서의 마루판과 시멘트 바닥의 접착이 용이하고, 접착 후 온열에 쉽게 견딜 수 있으며, 보온성 및 접착성이 우수한 바닥재용 2액형 수성접착제 조성물을 제공하는 것이다.Another object of the present invention is to suppress the release of severe chemical odor during or after construction, and to solve the problems of toxic release, ozone depletion, flammability, fluorine-containing compounds, such as environmentally friendly, at the same time can be cured at room temperature It is to provide a two-component aqueous adhesive composition for the flooring material is easy to adhere the floorboard and the cement floor at room temperature, can easily withstand the heat after the adhesion, and excellent insulation and adhesiveness.
상기 목적을 달성하기 위하여, 본 발명은 바닥재용 2액형 수성접착제 조성물에 있어서,In order to achieve the above object, the present invention is a two-component aqueous adhesive composition for flooring,
a)ⅰ) 수용성 에폭시 수지;a) i) water soluble epoxy resin;
ⅱ) 무기충진제; 및 Ii) inorganic fillers; And
ⅲ) 물 Iii) water
을 포함하는 주제; 및 A subject comprising a; And
b)ⅰ) 수용성 에폭시 경화제 수지;b) iii) a water soluble epoxy curing agent resin;
ⅱ) 경화촉진제; Ii) curing accelerators;
ⅲ) 무기충진제; 및 Iii) inorganic fillers; And
ⅳ) 물 Iii) water
을 포함하는 경화제 Curing agent comprising
를 포함하는 바닥재용 2액형 수성접착제 조성물을 제공한다. It provides a two-component aqueous adhesive composition for flooring comprising a.
바람직하기로 상기 바닥재용 2액형 수성접착제 조성물은Preferably the two-component aqueous adhesive composition for flooring is
a)ⅰ) 수용성 에폭시 수지 1 내지 80 중량%;a) i) 1 to 80% by weight of a water soluble epoxy resin;
ⅱ) 무기충진제 1 내지 80 중량%; 및 Ii) 1 to 80% by weight of an inorganic filler; And
ⅲ) 잔량의 물 Iii) remaining water
을 포함하는 주제; 및 A subject comprising a; And
b)ⅰ) 수용성 에폭시 경화제 수지 1 내지 80 중량%;b) i) 1 to 80% by weight of a water soluble epoxy curing agent resin;
ⅱ) 경화촉진제 0.01 내지 50 중량%; Ii) 0.01 to 50% by weight of a curing accelerator;
ⅲ) 무기충진제 10 내지 90 중량%; 및 V) 10 to 90% by weight of inorganic filler; And
ⅳ) 잔량의 물 Iii) remaining water
을 포함하는 경화제 Curing agent comprising
를 1 : 1의 중량비로 포함한다.It is included in the weight ratio of 1: 1.
이하 본 발명을 상세하게 설명한다. Hereinafter, the present invention will be described in detail.
본 발명자들은 시공시 또는 시공 후 심한 약품냄새의 발생을 억제하여 작업자가 작업하기에 용이하고, 환경친화적이며, 상온경화가 가능한 마루판용 수성접착제에 대하여 연구하던 중, 종래 접착제 조성물에 사용되던 용매인 유기용제를 대신하여 물을 사용하여 수성접착제를 제조한 결과, 종래 유기계 접착제와 대등한 정도의 성능을 지니면서도 시공시 또는 시공 후 심한 약품냄새의 발생을 억제하여 작업자가 작업하기에 용이하고, 입주자가 시공한 건물에 입주하였을 경우 코끝을 찌르는 듯한 불쾌취를 느끼지 않고 편안하게 생활할 수 있음을 확인하고, 이를 토대로 본 발명을 완성하게 되었다.The inventors of the present invention, while studying a water-based adhesive for floorboards that are easy for the operator to work with, and which are easy to work for the workers by suppressing the occurrence of severe chemical smell during or after construction, are solvents that have been used in conventional adhesive compositions. As a result of manufacturing an aqueous adhesive using water instead of an organic solvent, it has a performance comparable to that of a conventional organic adhesive, and it is easy for an operator to work by suppressing the occurrence of severe chemical smell during or after construction. When moving into the building was confirmed that it is possible to live comfortably without feeling the discomfort like poking the tip of the nose, to complete the present invention based on this.
본 발명의 2액형 수성접착제 조성물은 주제로 수용성 에폭시 수지, 무기충진제 및 물을 함유하며, 경화제로 수용성 에폭시 경화제 수지, 경화촉진제, 무기충진제 및 물을 함유하는 2액형인 것을 특징으로 한다.The two-component aqueous adhesive composition of the present invention contains a water-soluble epoxy resin, an inorganic filler, and water as a main ingredient, and is a two-component type containing a water-soluble epoxy curing agent resin, a curing accelerator, an inorganic filler, and water as a curing agent.
본 발명의 2액형 수성접착제 조성물에 주제로 사용되는 상기 a)ⅰ)의 수용성 에폭시 수지는 통상 사용되는 수용성 에폭시 수지면 크게 제한되지 않는다. 특히 상기 수용성 에폭시 수지는 비스페놀 A형 에폭시 수지, 브롬화 비스페놀 A형 에폭시 수지, 페놀 에폭시 수지, ο-크레졸 노볼락 에폭시 수지, 또는 분자내 2 개 이상의 에폭시기를 갖는 수용성 에폭시 수지를 사용할 수 있으며, 특히 비스페놀 A형 에폭시 수지를 사용하는 것이 바람직하다.The water-soluble epoxy resin of a) iii) used as a subject in the two-part aqueous adhesive composition of the present invention is not particularly limited. In particular, the water-soluble epoxy resin may be a bisphenol A epoxy resin, a brominated bisphenol A epoxy resin, a phenol epoxy resin, ο-cresol novolac epoxy resin, or a water-soluble epoxy resin having two or more epoxy groups in the molecule, in particular bisphenol It is preferable to use an A type epoxy resin.
상기 수용성 에폭시 수지는 주제에 1 내지 80 중량%로 포함되는 것이 바람직하며, 더욱 바람직하게는 10 내지 60 중량%로 포함되는 것이며, 가장 바람직하게는 35 내지 35 중량%로 포함되는 것이다. 그 함량이 상기 범위일 경우에는 접착제 조성물이 적정범위의 강도를 유지하도록 하여 작업도중 발생할 수 있는 마루판의 휨 현상을 방지하여 작업성이 향상되는 효과가 있다.The water-soluble epoxy resin is preferably contained in 1 to 80% by weight, more preferably included in 10 to 60% by weight, most preferably in the 35 to 35% by weight. When the content is in the above range, the adhesive composition maintains an appropriate range of strength, thereby preventing warpage of floorboards that may occur during operation, thereby improving workability.
본 발명의 2액형 수성접착제 조성물에 주제로 사용되는 상기 a)ⅱ)의 무기충진제는 접착제의 점도를 조절하여 경화시 수축을 감소시켜 작업성을 보완하고, 비용을 절감시키며, 접착제의 내열성 및 내구성을 향상시키는 작용을 한다.The inorganic filler of a) ii), which is used as a subject in the two-part aqueous adhesive composition of the present invention, adjusts the viscosity of the adhesive to reduce shrinkage during curing to compensate for workability, reduce costs, and improve the heat resistance and durability of the adhesive. It works to improve.
상기 무기충진제는 바닥재의 재질 또는 사용하는 수지의 종류와 양에 따라 그 종류와 양을 변화시켜 사용할 수 있으며, 특히 탄산칼슘(CaCO3), 황화칼슘, 또는 황화바륨 등과 같은 경탄류, 백클레이, 딕스클레이, 또는 황클레이 등과 같은 클레이류, 회분과 같은 규조토류, 또는 실리카(silica) 등을 사용할 수 있고, 바람직하게는 탄산칼슘(CaCO3), 황화칼슘, 또는 황화바륨 등과 같은 경탄류를 사용하는 것이다.The inorganic filler may be used by changing the type and amount according to the type and amount of the flooring material or the resin used, in particular, light coals such as calcium carbonate (CaCO 3 ), calcium sulfide, or barium sulfide, back clay, Clays such as Dixclay or sulfur clay, diatomaceous earth such as ash, or silica may be used, and light coals such as calcium carbonate (CaCO 3 ), calcium sulfide, or barium sulfide may be used. It is.
상기 무기충진제는 주제에 1 내지 80 중량%로 포함되는 것이 바람직하며, 더욱 바람직하게는 20 내지 80 중량%로 포함되는 것이며, 가장 바람직하게는 30 내지 50 중량%로 포함되는 것이다. 그 함량이 상기 범위일 경우에는 접착제의 점도를 효과적으로 조절하여 경화시 수축을 현저히 감소시킬 수 있으며, 접착제의 내열성 및 내구성을 현저히 향상시키는 효과가 있다.The inorganic filler is preferably included in 1 to 80% by weight, more preferably included in 20 to 80% by weight, most preferably 30 to 50% by weight. When the content is in the above range, it is possible to effectively control the viscosity of the adhesive to significantly reduce the shrinkage during curing, and has the effect of significantly improving the heat resistance and durability of the adhesive.
본 발명의 2액형 수성접착제 조성물에 주제로 사용되는 상기 a)ⅲ)의 물은 수용성 에폭시 수지 및 무기충진제 이외에 주제 잔량으로 포함된다.The water of a) iii), which is used as a main ingredient in the two-part aqueous adhesive composition of the present invention, is contained in the remaining amount of the main ingredient in addition to the water-soluble epoxy resin and the inorganic filler.
종래 접착제 조성물에 용매로 사용되던 유기 용제는 독성 방출, 오존 고갈, 가연성, 함불소 화합물 발생 등의 문제를 야기시킨다. 구체적으로, 고농도의 유기 용제를 흡입하였을 경우 코, 목을 자극하고, 두통, 현기증, 몸떨림, 졸음, 구토, 식욕부진, 마취작용 등을 일으키며, 심할 경우 중추신경억제를 나타내고 마취상태, 신경쇠약, 조혈계통 장애, 말초신경 장애를 일으킨다. 뿐만 아니라, 저농도의 유기 용제를 흡입하였을 경우 두통, 어지러움, 불안감 등의 자극증상을 일으킨다. 또한, 피부에 묻었을 경우 접촉부위를 자극하여 염증을 유발하며, 심할 경우 피부파열, 피부궤양 등을 일으키며 피부흡수를 통해 전신 독성을 나타낼 수 있고, 눈에 들어갔을 경우 점막을 자극하여 결막염을 일으킬 수 있다.Conventional organic solvents used as solvents in adhesive compositions cause problems such as toxic release, ozone depletion, flammability, and fluorine-containing compounds. Specifically, inhalation of high concentrations of organic solvents may irritate nose and throat, cause headache, dizziness, tremor, drowsiness, vomiting, anorexia, anesthesia, etc. , Causes hematopoietic disorders, peripheral nerve disorders. In addition, inhalation of low concentrations of organic solvents causes irritation symptoms such as headache, dizziness and anxiety. In case of contact with the skin, it irritates the contact area, causing inflammation, and in severe cases, it may cause skin rupture, skin ulceration, and systemic toxicity through skin absorption.If it gets into the eyes, it may irritate the mucous membranes and cause conjunctivitis. have.
상기 물은 2액형 수성접착제 조성물에 용매로 사용되며, 상기 물을 용제로 사용함으로써 유기용제의 사용으로 인하여 야기되던 환경파괴 문제를 해결하여 환경친화적일 뿐만 아니라, 시공시 또는 시공 후 심한 약품냄새의 발생을 억제하여 작업자의 작업능률을 향상시켜 작업성을 향상시킬 수 있으며, 입주자가 시공한 건물에 입주하였을 경우 코끝을 찌르는 듯한 불쾌취를 느끼지 않고 편안하게 생활할 수 있는 잇점이 있다.The water is used as a solvent in the two-component aqueous adhesive composition, and by using the water as a solvent to solve the environmental problems caused by the use of the organic solvent, not only environmentally friendly, but also a severe chemical smell during construction or after construction By suppressing the occurrence, the work efficiency of the worker can be improved, and the workability can be improved. When the tenant moves into the constructed building, there is an advantage of living comfortably without feeling the unpleasant odor of the nose.
상기와 같은 성분으로 이루어지는 a)의 주제는 필요에 따라 에멀젼 수지를 추가로 포함할 수 있다. The subject matter of a) consisting of such components may further comprise an emulsion resin, if necessary.
상기 에멀젼 수지는 물에 유화제를 첨가하여 유화중합시켜 물이 20∼60 % 함유된 유화상태로 물에 대한 용해성이 우수하다.The emulsion resin is excellent in solubility in water in the emulsion state containing 20 to 60% of water by emulsion polymerization by adding an emulsifier to water.
상기 에멀젼 수지는 수용성 아크릴 수지, 에틸렌 비닐 아세테이트(ethylene vinylacetate, EVA), 폴리비닐아세테이트(polyvinylacetate, PVAC), 또는 폴리우레탄(polyurethane, PU) 등을 사용할 수 있으며, 특히 수용성 아크릴 수지의 경우 응집력이 강하여 접착제 조성물의 강도를 일정하게 유지할 수 있어 더욱 효과적이다.The emulsion resin may be a water-soluble acrylic resin, ethylene vinyl acetate (ethylene vinylacetate, EVA), polyvinylacetate (PVAC), or polyurethane (polyurethane, PU), and the like, especially in the case of water-soluble acrylic resin has a strong cohesion The strength of the adhesive composition can be kept constant, which is more effective.
상기 에멀젼 수지는 주제에 1 내지 50 중량%로 포함되는 것이 바람직하며, 더욱 바람직하게는 5 내지 40 중량%로 포함되는 것이며, 가장 바람직하게는 5 내지 30 중량%로 포함되는 것이다. 그 함량이 상기 범위일 경우에는 수용성 에폭시 수지의 부족한 응집력을 보완하여 점착제 조성물에 응집력을 부여함으로써 적정범위의 강도를 유지하여 작업도중 발생할 수 있는 마루판의 휨 현상을 방지할 수 있는 효과가 있다.The emulsion resin is preferably contained in 1 to 50% by weight, more preferably contained in 5 to 40% by weight, and most preferably included in 5 to 30% by weight. When the content is in the above range, the cohesive force of the water-soluble epoxy resin is compensated for and the cohesive force is applied to the pressure-sensitive adhesive composition, thereby maintaining the strength in an appropriate range, thereby preventing warpage of floorboards that may occur during operation.
본 발명의 2액형 수성접착제 조성물에 경화제로 사용되는 상기 b)ⅰ)의 수용성 에폭시 경화제 수지는 무취, 무용제 타입의 폴리아마이드계 또는 아민(amine)계 수용성 경화제 수지를 단독 또는 혼합하여 사용하는 것이 좋다.The water-soluble epoxy curing agent resin of b) iii), which is used as a curing agent in the two-component aqueous adhesive composition of the present invention, may be used alone or in combination of an odorless, solvent-free polyamide-based or amine-based water-soluble curing agent resin. .
상기 폴리아마이드계 수용성 경화제 수지는 폴리아민류와 중합식물류 지방산과 축중합 반응으로 생성된 수지로 점도(25 ℃에서 측정)가 3,000∼10,000 cps인 것이 바람직하다.The polyamide-based water-soluble curing agent resin is a resin produced by polycondensation reaction with polyamines and polymerized plant fatty acids, and preferably has a viscosity (measured at 25 ° C.) of 3,000 to 10,000 cps.
상기 수용성 에폭시 경화제 수지는 경화제에 1 내지 80 중량%로 포함되는 것이 바람직하며, 더욱 바람직하게는 10 내지 70 중량%로 포함되는 것이며, 가장 바람직하게는 20 내지 60 중량%로 포함되는 것이다. 그 함량이 상기 범위일 경우에 물에 대한 우수한 용해성으로 경화제가 주제에 균일하게 혼합되어 적당한 점도와 경도를 유지함으로써 경화시간을 단축할 수 있으며, 경화시 수축을 현저히 감소시킬 수 있는 효과가 있다.The water-soluble epoxy curing agent resin is preferably contained in 1 to 80% by weight of the curing agent, more preferably included in 10 to 70% by weight, most preferably in the 20 to 60% by weight. When the content is in the above range, the curing agent is uniformly mixed with the main body with excellent solubility in water to maintain a suitable viscosity and hardness, thereby shortening the curing time, and has an effect of significantly reducing shrinkage during curing.
본 발명의 2액형 수성접착제 조성물에 경화제로 사용되는 상기 b)ⅱ)의 경화촉진제는 접착제의 경화를 빠르게 하여 접착시간을 단축시키고, 강도를 증가시키는 작용을 한다.The curing accelerator of b) ii), which is used as a curing agent in the two-part aqueous adhesive composition of the present invention, serves to accelerate the curing of the adhesive, shorten the adhesion time, and increase strength.
상기 경화촉진제는 통상 사용되는 경화촉진제면 모두 사용할 수 있으며, 특히 노닐페놀 또는 리튬카보나이트계를 사용하는 것이 좋다.The curing accelerator may be used for all of the curing accelerators usually used, in particular, it is preferable to use nonylphenol or lithium carbonite.
상기 경화촉진제는 사용되는 경화제의 종류 및 양에 따라 사용량이 달라질 수 있으나, 특히 경화제에 0.01 내지 50 중량%로 포함되는 것이 좋으며, 바람직하게는 0.1 내지 5 중량%로 포함되는 것이다. 그 함량이 상기 범위일 경우 접착제의 경화시간을 현저히 단축시킬 수 있으며, 저온경화성을 현저히 향상시킬 수 있는 효과가 있다.The amount of the curing accelerator may vary depending on the type and amount of the curing agent used, in particular, the curing agent is preferably included in 0.01 to 50% by weight, preferably contained in 0.1 to 5% by weight. When the content is in the above range, it is possible to significantly shorten the curing time of the adhesive, it is possible to significantly improve the low temperature curing properties.
본 발명의 2액형 수성접착제 조성물의 경화제에 사용되는 상기 b)ⅲ)의 무기충진제는 상기 주제에 함유되는 무기충진제와 동일한 것을 사용할 수 있다. The inorganic filler of b) iii) used in the curing agent of the two-pack aqueous adhesive composition of the present invention may be the same as the inorganic filler contained in the subject.
상기 무기충진제는 경화제에 10 내지 90 중량%로 포함되는 것이 바람직하며, 더욱 바람직하게는 20 내지 80 중량%로 포함되는 것이며, 가장 바람직하게는 22 내지 55 중량%로 포함되는 것이다. 그 함량이 상기 범위일 경우에는 접착제의 점도를 효과적으로 조절하여 경화시 수축을 현저히 감소시킬 수 있으며, 접착제의 내열성 및 내구성을 현저히 향상시키는 효과가 있다.The inorganic filler is preferably contained in 10 to 90% by weight, more preferably 20 to 80% by weight, most preferably 22 to 55% by weight in the curing agent. When the content is in the above range, it is possible to effectively control the viscosity of the adhesive to significantly reduce the shrinkage during curing, and has the effect of significantly improving the heat resistance and durability of the adhesive.
본 발명의 2액형 수성접착제 조성물의 경화제에 상기 b)ⅳ)의 물은 상기 주제에 함유되는 물과 동일한 작용을 하며, 경화제에 잔량으로 포함된다.The water of b) iii) in the curing agent of the two-pack aqueous adhesive composition of the present invention has the same function as the water contained in the above-mentioned main ingredient, and is contained in the remaining amount in the curing agent.
상기와 같은 a)의 주제와 b)의 경화제는 상기의 성분 이외에 필요에 따라 통상의 접착제 조성물에 사용되는 기능성 충진제, 분산제, 소포제, 안정제, 레벨링제, 가스흡수제, 습기흡수제, 점착부여제, 또는 촉매 등의 첨가제를 추가로 포함할 수 있다.The subject matter of a) and the curing agent of b) are functional fillers, dispersants, antifoaming agents, stabilizers, leveling agents, gas absorbers, moisture absorbents, tackifiers, or the like, which are used in conventional adhesive compositions as necessary in addition to the above components. Additives such as a catalyst may be further included.
상기 a)의 주제와 b)의 경화제는 1 : 1의 중량비로 혼합하는 것이 바람직하다. 상기 주제와 경화제는 동시에 두가지 성분을 혼합하여 사용할 수도 있으며, 상기 b)의 경화제에 a)의 주제를 소량으로 1차 첨가하여 반응시킨 후, 상기 반응물에 나머지량의 주제를 첨가하여 혼합하는 어덕트 타입(adduct type)으로도 사용할 수 있다.It is preferable to mix the said main ingredient of a) and the hardening | curing agent of b) in the weight ratio of 1: 1. The main ingredient and the curing agent may be used by mixing two components at the same time. After admixing the main ingredient of a) in a small amount to the curing agent of b), the adduct is mixed by adding the remaining amount of the main ingredient to the reactant. It can also be used as an adduct type.
본 발명의 수성접착제는 목재, 복합상재 등의 통상 마루판 자재에 모두 적용할 수 있으며, 상기 수성접착제를 시멘트 바닥에 최소 2 ㎜의 두께가 되도록 도포 즉시∼3 시간 이후 사이에 마루판을 조립 접착하는 방법으로 시공할 수 있다.The water-based adhesive agent of the present invention can be applied to all conventional floorboard materials such as wood, composite materials, and the method of assembling and bonding the floorboards between immediately and 3 hours after applying the aqueous adhesive to a cement floor of at least 2 mm. Can be installed by
본 발명에 따른 2액형 수성접착제 조성물은 종래 유기용제를 사용하여 야기되던 독성 방출, 오존 고갈, 가연성, 함불소 화합물 발생 등의 문제로 인한 환경파괴를 해결하여 환경친화적일 뿐만 아니라, 시공시 또는 시공 후 심한 약품냄새의 발생을 억제하여 별도의 환기를 시키지 않고도 작업자가 작업하기에 용이하고, 입주자가 시공한 건물에 입주하였을 경우 코끝을 찌르는 듯한 불쾌취를 느끼지 않고 편안하게 생활할 수 있으며, 유기용제 또는 가소제(디부틸프탈레이트 등의 프탈레이트계, 포르말린 등)를 사용하지 않고도 종래 유기계 에폭시 접착제와 비교하여 대등한 정도의 성능을 나타낼 수 있는 우수한 효과가 있다.The two-component aqueous adhesive composition according to the present invention solves environmental degradation due to problems such as toxic release, ozone depletion, flammability, and fluorine-containing compounds, which are caused by using conventional organic solvents. It is easy for workers to work without restraining the occurrence of severe chemical odor afterwards, and when the tenants move in to the building constructed by the tenant, they can live comfortably without feeling the unpleasant smell of the tip of their nose. Or there is an excellent effect that can exhibit a comparable degree of performance compared to conventional organic epoxy adhesives without using a plasticizer (phthalate, such as dibutyl phthalate, formalin, etc.).
또한 상기 2액형 수성접착제 조성물은 경도 및 강도가 우수하여 마루판의 움직임이 없게 하고, 이에 따라 마루판의 휨 현상이 발생하지 않으며, 상온경화가 가능하여 상온에서의 마루판과 시멘트 바닥의 접착이 용이하고, 접착 후 온열에 쉽게 견딜 수 있을 뿐만 아니라, 용이하게 마루판을 제거시킬 수 있어 보수 및 재시공이 쉬우며, 시멘트 바닥에 붙어 있는 접착제도 쉽게 제거될 수 있도록 하여 작업 효율성이 우수하다. 뿐만 아니라, 과습과 과건조에 의해 변형이 된 마루판의 초기 경화시간 및 점착력을 향상시켜 작업도중 마루판과 바닥면과의 밀착성을 개선시킴과 동시에 경화시간을 앞당겨 작업도중 발생할 수 있는 마루판의 휨현상으로 바닥면과 떨어진 채 경화되어 접착이 제대로 되지 않는 문제를 완전히 해결할 수 있다.In addition, the two-component aqueous adhesive composition is excellent in hardness and strength, so that the floorboard does not move, and thus warp of the floorboard does not occur, and at room temperature curing is possible, so that the floorboard is easily bonded to the cement floor at room temperature, Not only can it easily withstand the heat after gluing, but also the floorboard can be easily removed, so it is easy to repair and re-install, and the adhesive on the cement floor can be easily removed, so the work efficiency is excellent. In addition, by improving the initial curing time and adhesion of floorboards deformed by over-humidity and overdrying, it improves the adhesion between floorboards and flooring during work and at the same time the flooring due to warpage of floorboards that can occur during work It hardens away from the surface and can completely solve the problem of poor adhesion.
이하, 본 발명의 이해를 돕기 위하여 바람직한 실시예를 제시하나, 하기 실시예는 본 발명을 예시하는 것일 뿐 본 발명의 범위가 하기 실시예에 한정되는 것은 아니다.Hereinafter, preferred examples are provided to help understanding of the present invention, but the following examples are merely to illustrate the present invention, and the scope of the present invention is not limited to the following examples.
[실시예]EXAMPLE
실시예 1Example 1
수용성 에폭시 수지로 KEM-128-70(국도화학) 35중량%, 무기충진제로 탄산칼슘(OM-2, OMYA KOREA) 50 중량%, 및 잔량의 물을 균일하게 혼합하여 주제를 준비하였다. 그 다음 수용성 에폭시 경화제 수지로 KH-700(국도화학) 30 중량%, 경화촉진제로 노닐페닐(국도화학) 및 K-54(국도화학) 1.5 중량%, 무기충진제로 탄산칼슘(OM-2, OMYA KOREA) 50 중량%, 및 잔량의 물을 균일하게 혼합하여 경화제를 준비하였다. 상기 준비된 주제와 경화제를 1 : 1의 비율로 균일하게 혼합하여 2액형 수성접착제 조성물을 제조하였다.The subject was prepared by uniformly mixing 35% by weight of KEM-128-70 (Kukdo Chemical) with a water-soluble epoxy resin, 50% by weight of calcium carbonate (OM-2, OMYA KOREA) with an inorganic filler, and remaining water. Then, 30% by weight of KH-700 (Kukdo Chemical) with water-soluble epoxy curing agent resin, 1.5% by weight of Nonylphenyl (Kukdo Chemical) and K-54 (Kukdo Chemical) as curing accelerator, Calcium Carbonate (OM-2, OMYA) as inorganic filler KOREA) 50% by weight, and the balance of water was uniformly mixed to prepare a curing agent. The prepared main ingredient and the curing agent were uniformly mixed in a ratio of 1: 1 to prepare a two-part aqueous adhesive composition.
실시예 2∼4Examples 2-4
상기 실시예 1에서 하기 표 1에 나타낸 성분과 조성비로 사용한 것을 제외하고는 상기 실시예 1과 동일한 방법으로 실시하여 2액형 수성접착제 조성물을 제조하였다. 이때 표 1의 단위는 중량%이다.A two-component aqueous adhesive composition was prepared in the same manner as in Example 1, except that Example 1 was used as the component and the composition ratio shown in Table 1 below. At this time, the unit of Table 1 is weight%.
비교예 1Comparative Example 1
비스페놀 A형 에폭시 수지 35 중량%, 에멀젼 수지 13 중량%, 탄산칼슘 40 중량%, 아세톤 8 중량%, 및 가소제로 디부틸프탈레이트 8 중량%을 균일하게 혼합하여 주제를 준비하였다. 그 다음 폴리아마이드 아민 수지 47 중량%, 탄산칼슘 47 중량%, 메틸알콜 4 중량%, 및 가소제로 디부틸프탈레이트 4 중량%를 균일하게 혼합하여 경화제를 준비하였다. 상기 준비된 주제에 경화제를 균일하게 혼합하여 유성접착제 조성물을 제조하였다.The subject was prepared by uniformly mixing 35% by weight of bisphenol A type epoxy resin, 13% by weight of emulsion resin, 40% by weight of calcium carbonate, 8% by weight of acetone, and 8% by weight of dibutylphthalate with a plasticizer. Then, a curing agent was prepared by uniformly mixing 47% by weight of polyamide amine resin, 47% by weight of calcium carbonate, 4% by weight of methyl alcohol, and 4% by weight of dibutylphthalate with a plasticizer. The oil-based adhesive composition was prepared by uniformly mixing a curing agent on the prepared subject.
비교예 2Comparative Example 2
시중에 판매되는 EP-920((주)오공)을 사용하였다.A commercially available EP-920 Co., Ltd. was used.
비교예 3Comparative Example 3
상기 실시예 1에서 주제 및 경화제에 사용된 물을 대신하여 아세톤을 사용한 것을 제외하고는 상기 실시예 1과 동일한 방법으로 실시하여 접착제 조성물을 제조하였다.An adhesive composition was prepared in the same manner as in Example 1, except that acetone was used instead of water used in the main material and the curing agent in Example 1.
비교예 4Comparative Example 4
상기 실시예 1에서 주제 및 경화제에 가소제로 디부틸프탈레이트 3 중량%를 추가로 사용한 것을 제외하고는 상기 실시예 1과 동일한 방법으로 실시하여 접착제 조성물을 제조하였다.An adhesive composition was prepared in the same manner as in Example 1, except that 3 wt% of dibutyl phthalate was used as a plasticizer in the main body and the curing agent.
상기 실시예 1 내지 4 및 비교예 1 내지 4에서 제조한 접착제 조성물을 목재 및 복합상재에 각각 적용하여 시멘트 몰탈 처리된 온돌바닥에 부착한 결과, 목재 및 복합상재에서 모두 종래 유기 접착제인 비교예 1 내지 4와 대등한 정도의 전단강도를 나타내면서도 시공시 또는 시공후 발생하는 독한 약품냄새를 현저히 줄여 냄새가 거의 발생하지 않았다. 이로부터 본 발명에 따른 실시예 1 내지 4의 접착제 조성물은 시공시 또는 시공 후 심한 약품냄새의 발생을 억제하여 별도의 환기를 시키지 않고도 작업자가 작업하기에 용이하고, 입주자가 시공한 건물에 입주하였을 경우 코끝을 찌르는 듯한 불쾌취를 느끼지 않고 편안하게 생활할 수 있음을 알 수 있었다.As a result of applying the adhesive composition prepared in Examples 1 to 4 and Comparative Examples 1 to 4 to the cement mortar-treated ondol floor by applying to the wood and the composite material, respectively, Comparative Example 1 is a conventional organic adhesive in both wood and composite material Although the shear strength was comparable to 4 to 4, the odor was hardly generated by significantly reducing the odor of the chemicals generated during or after construction. From this, the adhesive composition of Examples 1 to 4 according to the present invention is easy for the worker to work without additional ventilation by suppressing the occurrence of severe chemical smell during construction or after construction, and occupied by the occupant in the building In this case, it was found that they could live comfortably without feeling the discomfort of piercing the nose.
또한, 상기 실시예 1 및 비교예 2의 접착제 조성물을 사용하여 냄새, 가사시간, 및 전단강도를 통상의 접착제 물성 평가방법으로 측정하고, 그 결과를 하기 표 2에 나타내었다. 이때, 전단강도는 25 ㎜ × 25 ㎜의 시편에 상기 실시예 1 및 비교예 2의 접착제 조성물을 부착한 후 5 시간, 24 시간, 72 시간이 지난 후에 측정하였다. 또한, 냄새가 전혀 없는 것을 5점, 약간 나는 것을 3점, 심하게 나는 것을 1점으로 하여 10 회 반복하여 평균치를 기재하였다.In addition, using the adhesive composition of Example 1 and Comparative Example 2, the smell, pot life, and shear strength were measured by a conventional adhesive property evaluation method, the results are shown in Table 2 below. In this case, the shear strength was measured after 5 hours, 24 hours, and 72 hours after attaching the adhesive compositions of Example 1 and Comparative Example 2 to the specimens of 25 mm × 25 mm. In addition, the average value was repeated 10 times, making five points, the one which has a little smell, three points, and the one which makes a bad smell one point at all.
상기 표 2를 통하여, 본 발명에 따른 실시예 1의 접착제 조성물은 종래 유기 용제를 용매로 사용한 유기 접착제와 비교하여 대등한 정도의 접착력을 나타내면서도 독한 약품냄새를 현저히 저하시켜 작업자의 시공 및 입주자가 입주하였을 때 불쾌취를 느끼지 않고 편안하게 작업하고 생활할 수 있음을 알 수 있었다.Through the above Table 2, the adhesive composition of Example 1 according to the present invention exhibits a similar degree of adhesive strength compared to the organic adhesive using a conventional organic solvent as a solvent, while significantly reducing the toxic chemical smell, the construction and occupants of the worker When I moved in, I could know that I could work and live comfortably without feeling discomfort.
본 발명에 따른 바닥재용 2액형 수성접착제 조성물은 종래 유기용제를 사용하여 야기되던 독성 방출, 오존 고갈, 가연성, 함불소 화합물 발생 등의 문제로 인한 환경파괴를 해결하여 환경친화적일 뿐만 아니라, 시공시 또는 시공 후 심한 약품냄새의 발생을 억제하여 별도의 환기를 시키지 않고도 작업자가 작업하기에 용이하고, 입주자가 시공한 건물에 입주하였을 경우 코끝을 찌르는 듯한 불쾌취를 느끼지 않고 편안하게 생활할 수 있으며, 유기용제 또는 가소제(디부틸프탈레이트 등의 프탈레이트계, 포르말린 등)를 사용하지 않고도 종래 유기계 에폭시 접착제와 비교하여 대등한 정도의 성능을 나타낼 수 있는 우수한 효과가 있다. 또한 본 발명의 2액형 수성접착제 조성물은 경도 및 강도가 우수하여 마루판의 움직임이 없게 하고, 이에 따라 마루판의 휨 현상이 발생하지 않으며, 상온경화가 가능하여 상온에서의 마루판과 시멘트 바닥의 접착이 용이하고, 접착 후 온열에 쉽게 견딜 수 있을 뿐만 아니라, 용이하게 마루판을 제거시킬 수 있어 보수 및 재시공이 쉬우며, 시멘트 바닥에 붙어 있는 접착제도 쉽게 제거될 수 있도록 하여 작업 효율성이 우수하다. 뿐만 아니라, 과습과 과건조에 의해 변형이 된 마루판의 초기 경화시간 및 점착력을 향상시켜 작업도중 마루판과 바닥면과의 밀착성을 개선시킴과 동시에 경화시간을 앞당겨 작업도중 발생할 수 있는 마루판의 휨현상으로 바닥면과 떨어진 채 경화되어 접착이 제대로 되지 않는 문제를 완전히 해결할 수 있는 효과가 있다.The two-component aqueous adhesive composition for flooring according to the present invention is not only environmentally friendly by solving environmental damage due to problems such as toxic emission, ozone depletion, flammability, fluorine-containing compounds, etc., which were caused by conventional organic solvents. Or, it is easy for workers to work without restraining the occurrence of severe chemical smell after construction, and when the tenants move into the building, they can live comfortably without feeling the unpleasant smell of the tip of their nose. There is an excellent effect that can exhibit a comparable degree of performance compared to the conventional organic epoxy adhesive without using an organic solvent or a plasticizer (phthalate, such as dibutyl phthalate, formalin, etc.). In addition, the two-component aqueous adhesive composition of the present invention is excellent in hardness and strength so that the floorboard does not move, and thus warp of the floorboard does not occur. In addition, it can easily withstand the heat after adhesion, and can easily remove the floorboard, so that it is easy to repair and rebuild, and that the adhesive adhered to the cement floor can be easily removed, thereby improving work efficiency. In addition, by improving the initial curing time and adhesion of floorboards deformed by over-humidity and overdrying, it improves the adhesion between floorboards and flooring during work and at the same time the flooring due to warpage of floorboards that can occur during work It hardens away from the surface, so it can completely solve the problem of poor adhesion.
Claims (9)