KR20050014464A - 스테인리스강의 제조방법 - Google Patents
스테인리스강의 제조방법Info
- Publication number
- KR20050014464A KR20050014464A KR1020030053108A KR20030053108A KR20050014464A KR 20050014464 A KR20050014464 A KR 20050014464A KR 1020030053108 A KR1020030053108 A KR 1020030053108A KR 20030053108 A KR20030053108 A KR 20030053108A KR 20050014464 A KR20050014464 A KR 20050014464A
- Authority
- KR
- South Korea
- Prior art keywords
- silicon
- amount
- reduction
- content
- stainless steel
- Prior art date
Abstract
Description
Claims (3)
- 희석가스 탈산용 정련로에 장입되는 용강의 탄소 함유량(중량%)이 1.00 ~ 2.50 이고 실리콘의 함유량(중량%)이 0.01 ~ 0.50 이며, 최종 제품에 함유된 탄소의 함유량(중량%)이 0.02~0.13, 실리콘의 함유량(중량%)이 0.3~0.8 그리고 크롬의 함유량(중량%)이 16.5~19이고 잔부가 철이며 기타 불가피한 불순물이 포함된 스테인레스 강을 제조하는 방법에 있어서,상기 스테인레스 강의 정련공정 중에서 탈탄완료 후의 환원단계에서 환원용 실리콘의 첨가량 결정을 정련시 필요한 조업 인자인 원료 장입시 탄소 함유량[C]%과, 원료 장입시 실리콘의 함유량[Si]%과, 정련공정인 탈탄 1단계 이 후 분석되는 1단계 탄소 함유량[C]%과, 탈탄 종료 후 환원과 탈류시에 계산되는 금속산화 산소량과, 아르곤 가스의 린싱유량과, 정련로에 장입되는 용강의 전장입량 그리고 생석회 사용량을 이용하여 결정하는 것을 특징으로 하는 스테인레스강의 제조방법.
- 제1항에서,상기 환원용 실리콘 첨가량은 다음의 실험식에 의하여 결정되는 것을 특징으로 하는 스테인레스 강의 제조방법.환원용 실리콘 첨가량(kg) = C1 - C2×장입[C]% - C3×장입[Si]% - C4×1단계[C]% + C5×전장입량(kg) - C6×린싱유량(Nm3) + C7×금속산화산소량(Nm3) + C8×생석회사용량(kg)여기서 C1 및C2, C3, C4, C5, C6, C7, C8 상수이며, 각 상수는 C4 ≥ C1 ≥ C3 ≥ C2 ≥ C7 ≥ C5 ≥ C6 ≥ C8의 조건을 만족한다.
- 제2항에서,상기 환원용 실리콘 첨가량을 결정하는 실험식에서 상기 상수는 C1:675~ 475, C2:225~25, C3:335~135, C4:956~756, C5:0.378~0.178, C6:0.223~ 0.023, C7:0.912~0.712, C8:0.145~0.001 의 조건을 만족하는 것을 특징으로 하는 스테인레스 강의 제조방법.