KR200423174Y1 - Board for gloss furniture - Google Patents

Board for gloss furniture Download PDF

Info

Publication number
KR200423174Y1
KR200423174Y1 KR2020060012921U KR20060012921U KR200423174Y1 KR 200423174 Y1 KR200423174 Y1 KR 200423174Y1 KR 2020060012921 U KR2020060012921 U KR 2020060012921U KR 20060012921 U KR20060012921 U KR 20060012921U KR 200423174 Y1 KR200423174 Y1 KR 200423174Y1
Authority
KR
South Korea
Prior art keywords
furniture
high gloss
undercoat
plate
mixed
Prior art date
Application number
KR2020060012921U
Other languages
Korean (ko)
Inventor
심재웅
Original Assignee
주식회사 위드퍼
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=41771795&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=KR200423174(Y1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by 주식회사 위드퍼 filed Critical 주식회사 위드퍼
Priority to KR2020060012921U priority Critical patent/KR200423174Y1/en
Application granted granted Critical
Publication of KR200423174Y1 publication Critical patent/KR200423174Y1/en

Abstract

본 고안은 고광택 가구용 판재에 관한 것으로, 보다 상세하게는 첨가제가 배합된 폴리에스테를 수지에 일정한 비율로 펄(pearl)을 혼합하여 고광택을 갖도록 함과 아울러 도료의 색상이 그대로 유지되는 고광택 가구용 판재에 관한 것이다.The present invention relates to a high gloss furniture sheet, and more specifically, to a high gloss furniture sheet, in which a polyester blended with an additive is mixed with a resin in a predetermined ratio to have a high gloss and the color of the paint is maintained as it is. It is about.

본 고안은 가구용 판재와, 상기 가구용 판재의 표면에 특정한 색상을 고착하여 형성된 하도층과, 상기 하도층의 경화된 상부에 형성되며, 분상입자의 펄을 포함하는 혼합코팅층으로 이루어진 것을 특징으로 한다.The present invention is characterized in that the plate made of a furniture, the undercoat layer formed by fixing a specific color on the surface of the plate for furniture, and a mixed coating layer formed on the cured upper portion of the undercoat, containing pearl of powder particles.

본 고안은 가구용 판재에 색상을 갖는 하도층과 상기 하도층의 상부에 혼합코팅층을 형성하여 작업공정이 단축될 뿐만 아니라, 표면 평탄도가 양호하면서 고광택을 갖는 효과가 있다.The present invention not only shortens the work process by forming a mixed coat layer having a color on the furniture plate and the upper layer of the undercoat, but also has a good surface flatness and high gloss effect.

가구용 판재, 폴리에스테르, 펄입자, 고광택 Furniture board, polyester, pearl particle, high gloss

Description

고광택 가구용 판재{BOARD FOR GLOSS FURNITURE}High gloss furniture board {BOARD FOR GLOSS FURNITURE}

도 1a와 도 1b는 본 고안의 바람직한 실시예로 형성된 고광택 가구용 판재를 도시한 단면도.Figure 1a and Figure 1b is a cross-sectional view showing a high gloss furniture plate formed as a preferred embodiment of the present invention.

**<도면의 주요 부분에 대한 부호의 설명>**** <Description of the symbols for the main parts of the drawings> **

10 : 가구용 판재 20 : 하도층10: furniture plate 20: undercoat

30 : 혼합코팅층 31 : 펄30: mixed coating layer 31: pearl

40 : 롤러 50 : 이형필름40: roller 50: release film

본 고안은 고광택 가구용 판재에 관한 것으로, 보다 상세하게는 첨가제가 배합된 폴리에스테를 수지에 일정한 비율로 펄(pearl)을 혼합하여 고광택을 갖도록 함과 아울러 도료의 색상이 그대로 유지되는 고광택 가구용 판재에 관한 것이다.The present invention relates to a high gloss furniture sheet, and more specifically, to a high gloss furniture sheet, in which a polyester blended with an additive is mixed with a resin in a predetermined ratio to have a high gloss and the color of the paint is maintained as it is. It is about.

일반적으로 가구용 판재의 표면에 화려한 미관상 고광택 부여하기 위해 판재의 표면에 펄, 메탈릭, 폴리에스테르 필름(이하 광택재로 칭하기로 함) 등을 사용하였다.In general, pearl, metallic, polyester film (hereinafter referred to as gloss material) and the like were used on the surface of the plate to impart a gorgeous aesthetic appearance high gloss on the surface of the plate for furniture.

종래의 고광택 가구용 판재 제조공정에 있어서, D/S 공법(DIRECT SHINNING) 또는 POLYURETILANE HIGH-GLOSSY) 제조공정에서는 제품을 한층 더 미려하게 하고 펄 층을 보호하기 위함을 목적으로 상도 작업시 광택재를 스프레이(SPRAY) 방법으로 표면에 도포한 후 이 상측에 별도의 코팅 도막을 형성시켜 제조하였다.In the conventional high gloss furniture plate manufacturing process, in the D / S manufacturing process (DIRECT SHINNING) or POLYURETILANE HIGH-GLOSSY (processing) manufacturing process, the polished material is sprayed during the top coat work for the purpose of making the product more beautiful and protecting the pearl layer. After applying to the surface by the (SPRAY) method was prepared by forming a separate coating film on the upper side.

이와 같이, 고광택 가구용 판재에 고광택을 갖기 위해서는 별도의 광택재를 스프레이 방법 또는 UV 커튼 방식으로 도포하는 공정이 추가하여야 하므로 작업공정이 복잡한 문제점이 있었다.As described above, in order to have a high gloss on the high-gloss furniture sheet, a separate coating material must be added by a spray method or a UV curtain method.

또한, 스프레이 작업공정에서 표면에 도포되는 두께가 일정하게 유지되지 않을 경우 펄 입자가 뭉쳐서 색상이색현상이 발생되어 제품의 불량이 발생하는 문제점이 있었다.In addition, when the thickness applied to the surface in the spray work process is not kept constant there is a problem that the color of the pearl particles agglomeration occurs, the product defects occur.

상기 문제점을 해결하기 위한 본 발명은 합판, MDF 등의 가구용 판재의 외관상 고광택 미관을 갖도록 함과 동시에 작업공정을 단축시키기 위한 고광택 가구용 판재를 제공함에 목적이 있다.The present invention for solving the above problems is to provide a high gloss furniture plate for shortening the work process and at the same time to have a high gloss aesthetic appearance of furniture plates such as plywood, MDF.

상기 목적을 달성하기 위한 본 고안은 가구용 판재와, 상기 가구용 판재의 표면에 특정한 색상을 고착하여 형성된 하도층과, 상기 하도층의 경화된 상부에 형성되며, 분상입자의 펄을 포함하는 혼합코팅층으로 이루어진 것을 특징으로 한다.The present invention for achieving the above object is a mixed coating layer comprising a plate for furniture, the undercoat layer formed by fixing a specific color on the surface of the furniture plate, and formed on the cured upper portion of the undercoat layer, and the pearl of powder particles Characterized in that made.

이하, 본 고안을 바람직한 실시예로 첨부된 도면을 참조하여 상세하게 설명하면 다음과 같다.Hereinafter, described in detail with reference to the accompanying drawings as a preferred embodiment of the present invention.

도 1a와 같이, 본 고안은 합판, MDF(중밀도 섬유판), P.B (파티클 보드) 등의 가구용 판재(10)의 상측에 도료가 도포되어 일정한 색상을 가지도록 하도층(20)이 형성되는데, 상기 도료는 불포화 폴리에스테르로서 무광 또는 유광을 선택적으로 사용할 수 있으며, 일반적으로 경화제 1.5중량%와 경화촉진제 0.5중량%로 첨가되어 두께가 0.01∼0.2㎜ 정도 되도록 형성된다.As shown in Figure 1a, the present invention is a paint coating is applied to the upper side of the furniture plate 10, such as plywood, MDF (medium density fiber board), PB (particle board) is formed to have a constant color 20, The paint may be selectively used matte or gloss as unsaturated polyester, and is generally added in an amount of 1.5% by weight of a curing agent and 0.5% by weight of a curing accelerator to form a thickness of about 0.01 to 0.2mm.

여기서, 상기 도료는 액상으로써 첨가제를 넣고, 젤화 또는 일정한 점도를 가진 상태에서 가구용 판재(10)의 표면에 도포한 후, 그 위에 이형필름(50)을 부착시키고, 롤러(40) 등에 의해 가구용 판재(10)에 소정두께를 갖는 도막이 형성되도록 이루어진다.Here, the paint is added to the additive as a liquid, and applied to the surface of the furniture plate 10 in the state of gelation or a certain viscosity, and then attach the release film 50 thereon, the furniture plate by the roller 40 or the like A coating film having a predetermined thickness is formed at (10).

상기 하도층(20)의 형성이 끝단 후에는 이형필름(50)을 제거하고, 상기 하도층(20)과 혼합코팅층(30)의 부착을 견고히 하기 위해 샌딩 또는 사포 등을 이용하여 표면처리한다.After the formation of the undercoat layer 20 is finished, the release film 50 is removed, and the surface treatment is performed using sanding or sandpaper or the like to firmly adhere the undercoat layer 20 and the mixed coating layer 30.

도 1b에 도시된 바와 같이, 하도층(20)의 표면에는 혼합코팅층(30)이 형성되는데, 상기 혼합코팅층(30)에는 투명 폴리에스테르 수지에 첨가제와 광택재가 배합된다.As shown in FIG. 1B, a mixed coating layer 30 is formed on the surface of the undercoat layer 20, and the mixed coating layer 30 is blended with an additive and a varnish to the transparent polyester resin.

상기 광택재는 첨가제가 혼합된 폴리에스테르 수지에 분상의 입자 50∼200㎛크기를 가지며 0.1∼0.9중량%의 펄(31)이 배합된다. 또한, 상기 광택재는 펄(31) 뿐만 아니라 홀로그램, 메탈틱(METALLIC) 또는 합성수지 필름(POLYESTER FILM) 등을 광택재로서 혼합하여 사용할 수 있는 것이다.The gloss material has a particle size of 50-200 μm in powdery polyester resin mixed with additives, and 0.1-0.9% by weight of pearl 31 is blended. In addition, the gloss material may be used by mixing not only the pearl 31, but also a hologram, a metaltic (METALLIC) or a synthetic film (POLYESTER FILM) as a gloss material.

이와 같이 배합하면, 혼합코팅층(30)의 표면 평탄도가 양호화게 형성될 수 있는 것이다.When blended in this way, the surface flatness of the mixed coating layer 30 can be formed to be good.

상기 첨가제는 기포를 방지하는 소포제 0.15중량%, 경화제 0.4중량%, 경화촉진제 0.3중량%가 포함되는데, 상기 첨가제는 사용상에 따라 다소 변경실시 될 수 있는 것이다.The additives include 0.15% by weight of antifoaming agent, 0.4% by weight of curing agent, 0.3% by weight of curing accelerator, and the additive may be changed somewhat depending on use.

이와 같이 혼합코팅층(30)은 젤화 또는 일정한 점도를 가진 상태에서 하도층(20)에 도포하고 그 위에 이형필름(50)을 부착시키며, 이어서 롤러(40)코팅 등을 이용하여 표면에 일정한 도막을 형성하는 공정으로 이루어 진다.In this way, the mixed coating layer 30 is applied to the undercoat layer 20 in a state of gelling or having a constant viscosity, and attaches the release film 50 thereon, and then uses a roller 40 coating or the like to apply a constant coating film to the surface. It consists of the process of forming.

상기와 같은 혼합코팅층(30) 형성공정 과정에서 표면상에 돌출된 펄(31) 입자는 롤러(40)에 의해 이형필름(50)과 같이 압착되어 상기 혼합코팅층(30)의 내부로 밀려지면서 혼합코팅층(30)의 일부가 덮어져 펄(31) 입자가 표면상으로 돌출되지 않으며, 이때 상기 롤러(40)코팅에 의해 도막을 형성하면서 혼합코팅층(30)에 내재된 기포가 외부로 배출되면서 표면이 자연스럽게 코팅된 상태가 된다.In the process of forming the mixed coating layer 30 as described above, the pearl 31 particles protruding on the surface are compressed together with the release film 50 by the roller 40 and are pushed into the mixed coating layer 30 to be mixed. Part of the coating layer 30 is covered so that the particles of pearl 31 do not protrude onto the surface. At this time, bubbles formed in the mixed coating layer 30 are discharged to the outside while the coating film is formed by the roller 40 coating. This is a naturally coated state.

이와 같이 혼합코팅층(30) 형성공정이 끝난 후 상온에서 1시간 정도 자연 건조한 후 이형필름(50)을 제거하면 고광택 가구용 판재가 제조되는 것이다.As such, after the mixing coating layer 30 is formed, the natural film is dried for about 1 hour at room temperature, and then the release film 50 is removed.

상기에서 설명한 바와 같이 가구용 판재(10)에 색상을 갖는 하도층(20)을 형성하고, 상기 하도층(20)의 표면에 혼합코팅층(30)을 도포하고 롤러(40)코팅에 의해 일정한 두께로 도막을 형성하는 형성공정으로 이루어져, 종래에 작업공정보다 단축되고, 고광택을 갖을 수 있는 고광택 가구용 판재가 형성된다.As described above, a color undercoat 20 having a color is formed on the furniture plate 10, the mixed coating layer 30 is applied to the surface of the undercoat 20, and the roller 40 is coated to a predetermined thickness. It consists of the forming process of forming a coating film, The board | substrate for high gloss furniture which is shorter than the conventional work process and can have high gloss is formed.

또한, 상기 하도층(20)의 색상과 혼합코팅층(30)이 분리되어 하도층(20)의 색상이 그대로 전달됨과 동시에 색상이 변색되지 않을 뿐만 아니라, 상기 혼합코팅층(30)의 두께에 따라 입체감을 갖도록 펄(31) 입자가 배열되어 다양한 각도로 빛을 반사하여 미관상 미려함을 향상시킬 수 있는 것이다.In addition, the color of the undercoat layer 20 and the mixed coating layer 30 is separated, the color of the undercoat layer 20 is transmitted as it is, and the color is not discolored, as well as the three-dimensional effect according to the thickness of the mixed coating layer 30 Pearl 31 particles are arranged so as to reflect the light at various angles to improve the aesthetic appearance.

상기 구성에 따른 본 고안은 가구용 판재에 색상을 갖는 하도층과 상기 하도층의 상부에 혼합코팅층을 형성하여 작업공정이 단축될 뿐만 아니라, 표면 평탄도가 양호하면서 고광택을 갖는 효과가 있다.The present invention according to the above configuration is to form a mixed coating layer on the upper surface of the undercoat layer having a color on the furniture plate material, not only shorten the work process, but also has an excellent surface flatness and high gloss.

Claims (3)

가구용 판재(10)와, 상기 가구용 판재(10)의 표면에 특정한 색상을 고착하여 형성된 하도층(20)과, 상기 하도층(20)의 경화된 상부에 형성되며, 분상입자의 펄(31)을 포함하는 혼합코팅층(30)으로 이루어진 것을 특징으로 하는 고광택 가구용 판재.The plate 10 for furniture, the undercoat layer 20 formed by fixing a specific color on the surface of the plate 10 for furniture, and formed on the cured upper portion of the undercoat 20, pearl 31 of powdered particles High gloss furniture sheet, characterized in that consisting of a mixed coating layer 30 comprising a. 제 1항에 있어서,The method of claim 1, 상기 분상입자의 펄(31)은 50∼200㎛ 입자크기를 가지며, 0.1∼0.9중량%로서 배합된 것을 특징으로 하는 고광택 가구용 판재.The pearl 31 of the powdered particles has a particle size of 50 ~ 200㎛, high-gloss furniture sheet, characterized in that blended as 0.1 to 0.9% by weight. 제 2항에 있어서,The method of claim 2, 상기 혼합코팅층(30)은 첨가제가 첨가된 폴리에스테르 수지를 롤러(40)코팅의 방법으로 도막을 형성한 것이며, 상기 첨가제는 기포를 방지하는 소포제 0.15중량%, 경화제 0.4중량%, 경화촉진제 0.3중량%를 포함하는 것을 특징으로 하는 고광택 가구용 판재.The mixed coating layer 30 is to form a coating film of a polyester resin to which the additive is added by the method of coating the roller 40, the additive is 0.15% by weight antifoaming agent, 0.4% by weight curing agent, 0.3% by curing accelerator High gloss furniture sheet, characterized in that it comprises%.
KR2020060012921U 2006-05-15 2006-05-15 Board for gloss furniture KR200423174Y1 (en)