Abstract

PURPOSE: Provided is a cell-activating and toxicity-eliminating agent which inhibits cell aging, as well as has antibacterial effect on harmful bacteria and detoxification effect. Therefore, it prevents and treats various kinds of diseases when administered into an animal, and promotes plant growth as well as increases immunity when administered into a plant. CONSTITUTION: A cell-activating and toxicity-eliminating agent is characterized by mixing 75.8 wt.% of SiO2, 1.31 wt.% of Fe2O3, 0.01 wt.% of TiO2, 12.4 wt.% of Al2O3, 2.68 wt.% of CaO, 0.12 wt.% of MgO, 4.08 wt.% of K2O, 3.36 wt.% of Na2O, 0.01 wt.% of MnO and 0.23 wt.% of Ge; and 50-60 wt.% of mixture with 40-50 wt.% of water.

Description

Cell-activating and toxicity-eliminating agent

The present invention relates to a cell activity and detoxifying agent that inhibits the rate of progress of aging animals and plants, has antibacterial activity against harmful bacteria, and can remove various toxicities.

Matter and sunlight, which make up the earth, each releases bioelectricity to cells of all living things to activate the cells and lead them to healthy life, and prevent bacteria, fungi, viruses, etc. from invading them to combat disease And also regenerate damaged cells.

Such bioelectrics are presumed to be caused by the movement of electrons and intermolecular movements around the nucleus, and these bioelectrics activate the cells and influence the growth of life.

However, among the materials present on the earth, the majority of the materials that emit too much bioelectricity, and the ones that emit weakly, and very few materials that emit enough bioelectricity suitable for life.

Excessive bioelectricity of substances may play a deadly role in living organisms. For example, excessive bioelectricity, such as radioactive substances, may destroy all cells, and a small bioelectric material that emits little influence on life.

Far infrared rays are commonly known as such bioelectrics. Far infrared rays are emitted from all objects, and materials that emit far infrared rays absorb the heat of the human body when it comes into contact with the human body and radiate the absorbed heat into the far infrared rays, so that the cells absorb the far infrared rays and activate the cells by resonance resonance absorption of resonance. do.

This far infrared ray is also a kind of bioelectric generated by the electron motion of the atoms constituting the material. As such, techniques for activating cells by radiating far infrared rays to the human body have been known.

However, conventionally, in obtaining a far-infrared radiation material, it has been selectively obtained from materials existing in nature, or manufactured by mixing and sintering specific materials.

However, it is not easy to select and acquire far-infrared radioactive materials present in nature, and these materials have the disadvantage of having a relatively low far-infrared emissivity. Thus, conventionally, far-infrared radiation ceramics have been manufactured and used by mixing and sintering specific materials.

However, when the sintered far-infrared radiation material is formed by sintering, gas and crystal water, such as carbon dioxide gas, are separated from the far-infrared radiation material, and the property of the material itself is changed.

However, bioelectrics radiated from any substance are not limited to far infrared rays, and many other types of bioelectrics are generated.

The present invention can not identify (deleting) any of these bioelectrics, but it seems to be a kind of far-infrared, if it is not far-infrared, bioelectrics that are understood as unknown bioelectrics to activate the cells Of course, it is an object of the present invention to provide a substance that eliminates various toxicities.

The present invention is a silicon oxide (SiO₂) 75.8% by weight, iron oxide (Fe₂O₃) 1.31% by weight, titanium oxide (TiO₂) 0.01% by weight, aluminum oxide (Al₂O₃) 12.4% by weight, calcium oxide (CaO) 2.68% by weight, magnesium oxide ( 50% to 60% by weight of a mixture of 0.12% by weight of MgO), 4.08% by weight of potassium oxide (K₂O), 3.36% by weight of sodium oxide (Na₂O), 0.01% by weight of manganese monoxide (MnO), and 0.23% by weight of germanium (Ge) It is mixed with 40-50 weight% of water.

Such bioelectricity emitted by the cell activity and detoxifying agent of the present invention activates the cells of animals or plants to enhance the health of living organisms, and neutralizes and removes various toxicity.

In other words, applying the cell activation and detoxifying agent of the present invention to the human body will activate the cells of the skin and make the skin healthy, beautiful and clear, as well as remove various toxic substances present in the skin to maintain healthy skin. It can be done.

And oral administration of the cell activity and detoxifying agent of the present invention to the animal activates the cells of the intestines and removes the toxicity in the body, the intestines are healthy and effective in the prevention and treatment of various diseases, when administered to plants, the growth of plants This was promoted and increased immunity was found.

As described above, a method of preparing the above-mentioned material for activating cells and removing toxicity by releasing bioelectricity is as follows.

Silicon oxide (SiO₂) 75.8 wt%, iron oxide (Fe₂O₃) 1.31 wt%, titanium oxide (TiO₂) 0.01 wt%, aluminum oxide (Al₂O₃) 12.4 wt%, calcium oxide (CaO) 2.68 wt%, magnesium oxide (MgO) 0.12 Weigh%, potassium oxide (K₂O) 4.08% by weight, sodium oxide (Na₂O) 3.36% by weight, manganese monoxide (MnO) 0.01% by weight, germanium (Ge) 0.23% by weight to crush the particles to 10mm or less, It was immersed in 7-10% aqueous solution of organic acid (preferably 7-10% aqueous solution) and heated for 24 to 200 hours at a temperature of 80 ℃ ~ 100 ℃ to produce an activated mixture with active ion exchange, electron and molecular motion. do.

The mixture thus prepared is immersed in clean hot water at about 60 ° C to 80 ° C for 20 to 24 hours, followed by washing with water, followed by washing with water 5 to 8 times in the same manner to produce a secondary product having a pH of 6 to 7 do.

Then, 40 to 50% by weight of water and 50 to 60% by weight of the mixture are mixed and ground by a ball mill for 72 to 120 hours to produce a finished product of small particles of 10 microns, which passes through 365 meshes.

The reason for the grinding by the ball mill is that the piezoelectric phenomenon occurs during the grinding, which makes the activation even more, and the moisture is adsorbed around the activated fine particles to change into cations (H) and anions (OH), thereby increasing the ion exchange function.

One embodiment is described below to explain in detail the method for producing the cell activator of the present invention.

EXAMPLE

Silicon Oxide (SiO₂) 75.8g

Iron oxide (Fe₂O₃) 1.31 g

0.01g titanium oxide (TiO₂)

Aluminum Oxide (Al₂O₃) 12.4g

Calcium Oxide (CaO) 2.68

Magnesium Oxide (MgO) 0.12g

Potassium oxide (K₂O) 4.08 g

Sodium oxide (Na₂O) 3.36 g

Manganese Monoxide (MnO) 0.01g

Germanium (Ge) 0.23 g

After mixing, the particles were crushed to have a diameter of 10 mm or less, immersed in 7-10% aqueous solution of organic acid (preferably 7-10% aqueous solution), and heated at a temperature of 100 ° C. for 190 hours to mix the powdery mixture. Produced.

The mixture thus prepared was immersed in clean hot water at 70 ° C. for 24 hours and washed with water seven times by removing water to prepare a second product, so that the acidity of the mixture was pH7.

Then, the water and the mixture was mixed in a 1: 1 (weight ratio) and pulverized with a ball mill for about 100 hours to produce a liquid finished product consisting of particles having a size that passes through 365 mesh.

In order to investigate the acute toxicity of the cellular activity and detoxifying agents prepared by the method of the present invention, oral single doses were administered to male and female SD rats (rats) to observe death, general symptoms, changes in body weight, and necropsy findings.

As a result of this test, no dead animals were observed in the 625 ~ 5000mg / kg dose group, no abnormal symptoms due to the administration of test substance were observed in the general symptoms, and the effect of the test substance on the change of body weight and macroscopic autopsy findings. No symptoms were observed, indicating no toxic symptoms caused by the test substance.

As the above toxic symptoms by acute oral administration were not found, the LD50 value was shown to be 5000 mg / kg (Acute Oral Toxicity Test of Biogene Liquid Rats). In the case of human, the cell activator of the present invention prepared by the above example can be administered orally up to 300g. However, the preferred daily dose of the cell activity and detoxicant of the present invention is considered to be 22.5 g based on solids.

Massage by the method of applying the cell activity and detoxifying agent of the present invention as described above to the skin (Massage) to activate the cells of the skin to prevent aging, the elasticity of the skin is increased, the skin is soft, of course, the skin It is effective in removing various toxic substances remaining in the body, and oral administration to animals activates the cells of the intestines and removes the toxicity in the body, which makes the intestines healthy and effective in the prevention and treatment of various diseases. It is effective in promoting plant growth and increasing immunity.

Claims (1)

Silicon oxide (SiO₂) 75.8 wt%, iron oxide (Fe₂O₃) 1.31 wt%, titanium oxide (TiO₂) 0.01 wt%, aluminum oxide (Al₂O₃) 12.4 wt%, calcium oxide (CaO) 2.68 wt%, magnesium oxide (MgO) 0.12 50% to 60% by weight of a mixture of 4% by weight, 4.08% by weight of potassium oxide (K₂O), 3.36% by weight of sodium oxide (Na₂O), 0.01% by weight of manganese monoxide (MnO), and 0.23% by weight of germanium (Ge). Cellular activity and detoxifying agent, characterized in that mixed with 50% by weight